Title:Mechanisms of Elevated Temperature Galling in Hardfacings
View PDF HTML (experimental)Abstract:The galling mechanism of Tristelle 5183, an Fe-based hardfacing alloy, was investigated at elevated temperature. The test was performed using a bespoke galling rig. Adhesive transfer and galling were found to occur, as a result of shear at the adhesion boundary and the activation of an internal shear plane within one of the tribosurfaces. During deformation, carbides were observed to have fractured, as a result of the shear train they were exposed to and their lack of ductility. In the case of niobium carbides, their fracture resulted in the formation of voids, which were found to coalesce and led to cracking and adhesive transfer. A tribologically affected zone (TAZ) was found to form, which contained nanocrystalline austenite, as a result of the shear exerted within 30{\mu}m of the adhesion boundaries. The galling of Tristelle 5183 initiated from the formation of an adhesive boundary, followed by sub-surface shear in only one tribosurface, Following further sub-surface shear, an internal shear plane is activated. internal shear and shear at the adhesion boundary continues until fracture occur, resulting in adhesive transfer.
Submission history
From: Samuel Rogers Ph.D. [view email][v1] Tue, 12 Mar 2024 15:10:43 UTC (21,043 KB)
Current browse context:
physics.app-ph
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.