Residual Stress and Wear Characteristics of Ni3Al Coating Layer

Article Preview

Abstract:

The Ni3Al intermetallic compound is of great interest because of its oxidation, corrosion-resistance, and high melting point. The low-temperature hot press + thermal diffusion process method is a technique that uses the thermal reactive diffusions between the elements that compose the intermetallic compound. In this method the powder mixture is heated and be able to generate the diffusions of the powder elements by keeping the heating temperature comparatively lower temperature with other technique. The authors evaluated the preparation conditions and joining quality in Ni3Al coating layer of particular interest is the residual stress due to the different mechanical properties of the coating and the substrate and its effect on the interface joining quality. It is known that residual stresses were generated by the difference in the coefficient of thermal expansion (CTE) of coating and substrate during cooling process. Such a residual stress caused by the differences of mechanical properties has strong influence on composite material strength. X-ray stress measurement techniques has been developed for experimental determination of residual stresses. In this paper, the Ni3Al intermetallic compound was coated on spheroidal graphite cast iron and austenite stainless steel using the reactive sintering method. Wear characteristics and residual stress on these intermetallic compound layers were investigated to evaluate the effect of substrate materials on coating layer properties.

You might also be interested in these eBooks

Info:

Periodical:

Materials Science Forum (Volumes 490-491)

Pages:

619-624

Citation:

Online since:

July 2005

Export:

Price:

[1] A. Ikenaga, Y. Gotoh, M. Kawamoto, K. Kobayashi and K. Uenishi : J. JFS 68 (1996), p.417.

Google Scholar

[2] T. Murotani, T. Taguchi, A. Ikenaga and Y. Hirose : J. JFS 74 (2002), p.429.

Google Scholar

[3] X-ray stress measurement, (Society of materials science, Youkendo, Japan 1990), p.54.

Google Scholar

[4] T. Sasaki, T. Gotoh, H. Tabata and Y. Hirose : J. Journal of the society of materials science 46 (1997), p.756.

Google Scholar

[5] B. D. Cullity : Ellements of X-ray diffraction, (Agune, Japan 1992), p.259.

Google Scholar

[6] W. H. Hall : The journal of the institute of metals 77 (1950), p.601.

Google Scholar

[7] M. Kawamoto, M. Adachi and K. Okabayashi : J. JFS 50 (1978), p.32.

Google Scholar

[8] M. Kawamoto, T. Sone and K. Okabayashi: J. Jpn. Inst. Met. 37 (1973), p.357.

Google Scholar

[9] M. Kawamoto, S. Shintani, T. Sone and K. Okabayashi: J. Jpn. Inst. Met. 37 (1973), p.1236.

Google Scholar

[10] S.W.E. Earles and M.G. Hayler: Wear 20(1972), p.51.

Google Scholar

[11] L.M. Zhang, J. Liu, R.Z. Yuan, T. Hirai: Materials Science & Engineering 203 (1995), p.272.

Google Scholar

[12] National Astronomical Observatory: Chronological ScientificTables1998, (Maruzen, Japan 1998), p.474.

Google Scholar

[13] N. Mori, T. Endoh and M. Kawakami : J. Journal of the society of materials science 34(1985), p.384.

Google Scholar

[14] A. Ikenaga, Y. Gotoh, Y. Nitta, M. Kawamoto, K. Kobayashi and K. Araki : J. JFS 68 (1996), p.852.

Google Scholar