Abstract
Wear protection plays an important role for highly loaded components. Therefore, PVD hard coatings with very high hardness have become well established in industrial applications for steel components in the automotive industry. As an alternative to steels, efforts are currently being focused on cast irons for components because of their reduced requirements for superior properties in machining, their lower weight, and lower costs. However, due to the insufficient load-bearing support of this soft base material and/or of their individual microstructural constituents (graphite), the use of hard coatings on cast irons for wear protection has remained limited. The present contribution deals with the possibilities with respect to using electron beam (EB) solid phase treatment (hardening) and liquid phase surface treatments with Ni-based additives (alloying) and without additives (remelting), to improve the conditions for deposition and the load-bearing support of the thin PVD hard coatings. Apart from the hardness of the EB-treated layer, the toughness of the specific microstructural constituents influences the properties of the composite layer substantially. Comparative studies of different single treatments and duplex treatments (EB treated and, subsequently, PVD hard-coated) were carried out by means of unlubricated pin-on-disc wear tests and potentiodynamic corrosion measurements in a 5% NaCl solution. The investigations proved that it is possible to use PVD hard coatings (with all their outstanding properties) for cast iron components by utilising duplex surface treatment technologies.
Kurzfassung
Der Verschleißschutz spielt insbesondere für hochbelastete Bauteile eine wichtige Rolle. Für Bauteile aus Stahl haben sich aufgrund der hohen Härte vor allem PVD-Hartstoffschichten in der industriellen Praxis etabliert. Alternativ zum Stahl zielen aktuelle Bestrebungen darauf ab, die Bauteile aus Gusseisen zu fertigen, weil dieser Werkstoff einfacher zu bearbeiten und kostengünstiger ist sowie ein geringeres Gewicht aufweist. Die Nutzung von PVD-Hartstoffschichten auf Gusseisen zum Zweck des Verschleißschutzes ist jedoch stark eingeschränkt. Ursache hierfür ist die unzureichende Abstützung durch das weiche Gefüge und/oder der einzelnen Gefügebestandteile (Graphit) des Gusseisens. Der vorliegende Beitrag behandelt die Möglichkeiten von Elektronenstrahl (EB)-Festphasenprozessen (EB-Härten) und Flüssigphasenprozessen ohne/mit Zusatzstoff (EB-Umschmelzen, EB-Legieren) sowohl zur Verbesserung der Bedingungen zur Schichtabscheidung als auch der Stützwirkung für dünne PVD-Hartstoffschichten. Neben der erreichten Schichthärte beeinflusst die Zähigkeit der einzelnen Gefügebestandteile die Eigenschaften des Randschichtverbundes entscheidend. Es wurden vergleichende Untersuchungen an verschiedenen Einzel- und Duplexbehandlungen (EB-Randschichtbehandlung und nachfolgende PVD-Beschichtung) zum Verschleiß- (ungeschmierte Stift-Scheibe-Tests) und Korrosionsverhalten (potentiodynamische Messungen in 5 %iger NaCl-Lösung) durchgeführt. Die Ergebnisse belegen, dass es möglich ist, durch eine vorherige EB-Randschichtbehandlung die hervorragenden Eigenschaften von PVD-Hartstoffschichten auch für Gusseisen nutzbar zu machen.
References
1. Schwarz, H.: Schadensanalyse von PVD-TiN beschichteten Bauteilen und Werkzeugen. Prakt. Metallographie30 (1993) 10, pp. 496–506Schwarz, H.: Schadensanalyse von PVD-TiN beschichteten Bauteilen und Werkzeugen. Prakt. Metallographie30 (1993) 10, pp. 496–506Search in Google Scholar
2. Holmberg, K.; Matthews, A.: Coating Tribology; Properties, Techniques and Applications in Surface Engineering. Tribology Series 28, Elsevier, Amsterdam, 1994Holmberg, K.; Matthews, A.: Coating Tribology; Properties, Techniques and Applications in Surface Engineering. Tribology Series 28, Elsevier, Amsterdam, 199410.1016/S0167-8922(08)70748-XSearch in Google Scholar
3. Zenker, R.: Beitrag zur Entwicklung neuer Wärmebehandlungstechnologien in Verbindung mit hohen Erwärmungsgeschwindigkeiten. Habilitation, TU Bergakademie Freiberg, 1986Zenker, R.: Beitrag zur Entwicklung neuer Wärmebehandlungstechnologien in Verbindung mit hohen Erwärmungsgeschwindigkeiten. Habilitation, TU Bergakademie Freiberg, 1986Search in Google Scholar
4. Keßler, O.: Kombinationsverfahren zur Randschichtbehandlung von Stählen – Stoffeigenschaftändernde und Beschichtungsverfahren. Habilitation, University Bremen, Shaker, Aachen, 2003Keßler, O.: Kombinationsverfahren zur Randschichtbehandlung von Stählen – Stoffeigenschaftändernde und Beschichtungsverfahren. Habilitation, University Bremen, Shaker, Aachen, 2003Search in Google Scholar
5. Zenker, R.; Sacher, G.; Buchwalder, A.; Liebich, J.; Reiter, A.; Häßler, R.: Hybrid technology hard coating – electron beam surface hardening. Surf. Coat. Technol.202 (2007), pp. 804–808, 10.1016/j.surfcoat.2007.05.089Zenker, R.; Sacher, G.; Buchwalder, A.; Liebich, J.; Reiter, A.; Häßler, R.: Hybrid technology hard coating – electron beam surface hardening. Surf. Coat. Technol.202 (2007), pp. 804–808, 10.1016/j.surfcoat.2007.05.089Search in Google Scholar
6. Grumbt, G.; Zenker, R.; Biermann, H.; Weigel, K.; Bewilogua, K.; Bräuer, G.: Electron beam hardening of PVD-coated steels – improved load-supporting capacity for Ti1-xAlxN layers. Surf. Coat. Technol.283 (2015), pp. 201–209, 10.1016/j.surfcoat.2015.10.077Grumbt, G.; Zenker, R.; Biermann, H.; Weigel, K.; Bewilogua, K.; Bräuer, G.: Electron beam hardening of PVD-coated steels – improved load-supporting capacity for Ti1-xAlxN layers. Surf. Coat. Technol.283 (2015), pp. 201–209, 10.1016/j.surfcoat.2015.10.077Search in Google Scholar
7. Buchwalder, A.; Jung, A.; Zenker, R.; Steudtner, M.; Engelmann, M.; Gleißner, F.; Schwab, R.: Electron beam liquid phase surface treatments – facilitating the use of PVD hard coatings as surface protection for cast irons. Proc. Europ. Conf. on Heat Treatment & 22nd IFHTSE Congr., 20–22.05.15, Venice/Italy, AIM, Milano/Italy, 2015, on CD: 038Buchwalder, A.; Jung, A.; Zenker, R.; Steudtner, M.; Engelmann, M.; Gleißner, F.; Schwab, R.: Electron beam liquid phase surface treatments – facilitating the use of PVD hard coatings as surface protection for cast irons. Proc. Europ. Conf. on Heat Treatment & 22nd IFHTSE Congr., 20–22.05.15, Venice/Italy, AIM, Milano/Italy, 2015, on CD: 038Search in Google Scholar
8. Buchwalder, A.; Zenker, R.; Fritzsch, K.; Rüthrich, K.; Nagel, K.; Griesbach, W.: Potenziale von ausgewählten Randschichtbehandlungsverfahren sowie deren Kombinationen zur Verbesserung des Verschleiß- und Korrosionsverhaltens von Gusseisenwerkstoffen. Mat.-Wiss. u. Werkstofftech.46 (2015) 6, pp. 550–562, 10.1002/mawe.201500392Buchwalder, A.; Zenker, R.; Fritzsch, K.; Rüthrich, K.; Nagel, K.; Griesbach, W.: Potenziale von ausgewählten Randschichtbehandlungsverfahren sowie deren Kombinationen zur Verbesserung des Verschleiß- und Korrosionsverhaltens von Gusseisenwerkstoffen. Mat.-Wiss. u. Werkstofftech.46 (2015) 6, pp. 550–562, 10.1002/mawe.201500392Search in Google Scholar
9. Schiller, S.; Heisig, U.; Panzer, S.: Electron Beam Technology. Verlag Technik GmbH, Berlin, 1995Schiller, S.; Heisig, U.; Panzer, S.: Electron Beam Technology. Verlag Technik GmbH, Berlin, 1995Search in Google Scholar
© 2016, Carl Hanser Verlag, München