In order to develop thermostable Raney-type catalysts for the methanation of carbon mono xide, the method of pieparing the Raney-type nickel catalysts was examined. The thermal stabilities of the Ni-Al2O3 catalysts depend remarkably on their pretreatment. The thermal stability decreased in the following order: (calcined in air at 550°C)>(calcined in N2 at 460°C)>(without pretreatment) (Fig.2). For the Ni-Cr2O3Al2O3 catalysts, the extent of the increase in the Ni crystallite size and the decrease in the amount of H2 chemisorption during a thermal stability test were found smaller than those by the Ni-Al2O3 catalysts (Table 1). The Ni-Cr2O3Al2O3 catalyst calcined at 550°C was found to be most thermostable of the catalysts tested in this study.