Hygroscopic analysis and tribo-mechanical characterization of biocompatible PP/PA6/Boron sesquioxide composite

The purpose of this study is to look into the hygroscopic and tribo-mechanical properties of a polypropylene/polyamide-6 (PP/PA6) blend and a PP/PA6/Boron sesquioxide composite.

The hygroscopic behaviour of the PP/PA6 blend and PP/PA6/Boron sesquioxide composite was studied using a water contact angle goniometer in this study. To validate the hygroscopic behaviour of the blend and composite, water contact angles and surface energy of the materials were investigated. Tensile strength and hardness tests were used to determine mechanical characteristics, and tribological experiments on a pin-on-disc tribometer were used to demonstrate the friction and wear rates of dry and water-conditioned blends and composites. The melting temperature of dry and water-conditioned composites was determined using DSC analysis.

The hygroscopic effect of the PP/PA6 blend was found to be minimal in the experiment, while it was relatively dominating in the PP/PA6/Boron sesquioxide composite. Tensile strength was found to be somewhat lower in blend and composite compared to virgin PP, whereas hardness was found to be higher in both blend and composite. The composite’s tribological testing findings were fairly outstanding, with the coefficient of friction (COF) and wear rates significantly reduced due to boron sesquioxide reinforcement. The reaction between boron sesquioxide and water molecules produced boric acid, which increased the tribological characteristics of the composite even further. Following 30 days of water conditioning, the weight of the blend increased by 3.64% and the weight of the composite increased by 6.45% as compared to the dry materials. After water conditioning, tensile strength reduced by 0.8% for the blend and 14.16% for the composite. Hardness was determined to be the same in the dry state and after water-conditioning for blend but dropped 1% for composite. As compared to blend, the COF and wear resistance of composite were 15.52% and 25.16% higher, respectively. After absorbing some water, the results increased to 28.57% and 34.9%, respectively.

The mechanical and thermal behaviour of polymer composites (particularly polyamide composites) vary depending on the surrounding environment. Tests were carried out to explore the effect of water treatment on the tribo-mechanical and thermal characteristics of PP/PA6/Boron sesquioxide composite. Water treatment caused polyamides to bind with water molecules, resulting in voids in the material. The interaction between boron sesquioxide and water molecules produced boric acid, which increased the tribological characteristics of the composite.