Influence of V doping on the microstructure, chemical stability, mechanical and tribological properties of MoS₂ coatings

This study aims to investigate the effect of V doping on the microstructure, chemical stability, mechanical and vacuum tribological behavior of sputtered MoS₂ coatings.

The MoS₂-V coatings are fabricated via tuning V target current by magnetron sputtering technique. The structural characteristic and elemental content of the coatings are measured by field emission scanning electron microscopy, X-ray diffractometer, electron probe X-ray micro-analyzer, Raman, X-ray photoelectron spectroscopy, high resolution transmission electron microscope and energy dispersive spectrometer. The hardness of the deposited coatings are tested by a nanoindentation technique. The vacuum tribological properties of MoS₂-V coatings are studied by a ball-on-disc tribometer.

Introducing V into the MoS₂ coatings results in a more compact microstructure. The hardness of the coatings increases with the doping of V. The MoS₂-V coating deposited at a current of 0.2 A obtains the lowest friction coefficient (0.043) under vacuum. As the amount of V doping increases, the wear rate of the coating decreases first and then increases, among which the coating deposited at a current of 0.5 A has the lowest wear rate of 2.2 × 10–6 mm³/N·m.

This work elucidates the role of V doping on the lubrication mechanism of MoS₂ coatings in a vacuum environment, and the MoS₂-V coating is expected to be applied as a solid lubricant in space environment.