Decoration of Ti / TiO 2 Nanotubes with Pt Nanoparticles for Enhanced UV-Vis Light Absorption in Photoelectrocatalytic Process

Nanotubos de TiO2 (TiO2NTs) foram decorados com nanopartículas de Pt via deposição catódica. Estas nanopartículas foram uniformemente distribuídas, altamente separadas e espaçadas sobre toda a superfície do TiO2NT para o menor tempo de deposição, com os tamanhos das partículas de Pt proporcionais às cargas aplicadas. O fotoeletrodo de Pt/TiO2NTs apresentou intenso pico de absorção na região do visível com significativo deslocamento para vermelho induzido pela platina depositada na superfície do TiO2NTs, diminuindo a energia do band gap de 3,21 eV para 2,87 eV. O fotoeletrodo de Pt/TiO2NTs foi testado na oxidação fotoeletrocatalítica do corante Vermelho Ácido 29 com grande sucesso. Descoloração total e 92% de remoção do carbono orgânico total foram obtidos após 120 min de tratamento empregando o fotoeletrodo de Pt/TiO2NTs, o qual apresentou valores superiores aos do não-decorado (87% e 68%, respectivamente), devido ao melhor uso da radiação e da minimização da recombinação de carga.


Introduction
The exponential increase of industrial activities and the high demand for manufactured products have caused a considerable impact on the environment.2][3][4][5] Among the different techniques employed for contaminant removal, electrochemical advanced oxidation processes (EAOPs) have aroused a great interest for degradation/mineralization of organic pollutants due to their potential environmental compatibility, 6 since it rears no generation of secondary pollution, and allows the use of biologically inert materials and of low cost The doping or band gap engineering of TiO 2 has been made in order to shift the absorption spectra to longer wavelengths.This is obtained by the incorporation of metal ions into the lattice, such as Pt, 18,19 non-metals such as C and N 20,21 and composites of semiconductors such as WO 3 /TiO 2 . 221][32] The decrease in electron density within the TiO 2 NTs causes the holes which freely diffuse to the surface where oxidation of organic compounds can occur.
Park et al. 33 deposited Pt nanoparticles on the TiO 2 NT structure by photoreduction method and their physicochemical properties were investigated.In this work, Pt decorated photoelectrode exhibited higher photocatalytic performance than the undecorated one on the photodegradation of Methylene Blue dye.Pt/TiO 2 NT photoelectrodes prepared by platinum deposition-precipitation method were also studied by Zhu et al. 34 and their photocatalytic performance was evaluated by the degradation rates of Methyl Orange solution under UV-vis light irradiation.Using stable TiO 2 NTs, An et al. 35 studied the Pt nanoparticle deposition on nanotubular TiO 2 surface via photodeposition process and the photocatalytic performance was also evaluated by the photodegradation of Methyl Orange under UV light irradiation.According to these authors, Pt/TiO 2 NTs exhibited higher photocatalytic activity than the undecorated one.Hosseini and Momeni 36 recently evaluated the performance of Pt/TiO 2 NT electrodes for electrochemical oxidation of formic acid.Nevertheless, the literature does not explore the increase of electrical conductivity of Pt/TiO 2 NTs to evaluate its performance in the photoelectrocatalytic oxidation of an organic pollutant.
In this context, the present work reports the preparation of Pt/TiO 2 NT photoelectrodes by galvanostatic electrodeposition of Pt nanoparticles on TiO 2 NT surface.The influence of Pt introduction onto TiO 2 NT surface was evaluated by systematic characterization of the morphology and photoactivity response when irradiated by UV-Vis light.In order to assess the photoelectrocatalytic (PEC) performance of the Pt/TiO 2 NT photoelectrode, this material was applied to the degradation of the azo dye Acid Red 29 (AR29) (see formula in Figure 1).This textile dye was chosen as model compound due to its wide applicability and because 70% of the dyes usually consumed in the world are based on azo dyes, characterized by the presence of one or more azo groups (-N=N-). 3,37Percentages of color removal and changes of total organic carbon (TOC) of AR29 dye solutions were monitored as responses.Decay kinetics for AR29 dye was followed by high-performance liquid chromatography (HPLC) during the dye mineralization.All results are compared with TiO 2 NTs without modification.

Experimental
Preparation of TiO 2 NT and Pt/TiO 2 NT photoelectrodes TiO 2 NT electrodes were produced by anodization according to described in the literature. 2,38For this, titanium sheets (99.9%,Sigma Aldrich) were previously cut (2.0 cm × 2.5 cm) and mechanically polished with different sandpapers, ultrasonically degreased in isopropyl alcohol, acetone and ultrapure water, successively for 15 min each one and drying in nitrogen flow.The TiO 2 NT photoelectrodes were prepared by anodization using two-electrode cell configuration, with Ti foils as anode and ruthenium foil (2.0 cm × 2.0 cm) as a cathode.Ethylene glycol solution containing 0.25 wt.% NH 4 F and 10 vol.% ultrapure water was used as electrolyte.The anodization consisted of a potential ramp from 0 to 30 V (sweep rate of 1.0 V min -1 ) maintained at a constant potential of 30 V for 50 h.Immediately after the anodization the obtained electrodes were fired at 450 °C during 30 min in a muffle furnace to transform amorphous TiO 2 into crystalline anatase phase.
Finally, Pt/TiO 2 NT photoelectrodes were prepared by Pt nanoparticle deposition on TiO 2 NT surface by using a procedure adapted from Hosseini et al.. 39 A conventional three-electrode electrochemical cell with a platinum gauze (auxiliary electrode) and Ag/AgCl (reference electrode) was used for deposition of Pt nanoparticles on TiO 2 NTs.All the Pt electrodeposition assays were performed at cathodic current density of 10 mA cm -2 in 10 mmol L -1 chloroplatinic acid (≥ 99.9% purity, Sigma Aldrich) of ethanolic solution and at room temperature.In this electrochemical method, deposition times of 15, 20, 30 and 40 min were studied and a potentiostat/galvanostat (AUTOLAB Model PGSTAT 302) controlled by GPES software was used during the electro deposition experiments.
Characterization of the Pt/TiO 2 NT photoelectrodes TiO 2 NT (undecorated) and Pt/TiO 2 NT photoelectrodes were characterized according to their physical structure by means of X-ray diffraction (XRD) on a Siemens D 5000 using radiation in the 4 to 70° range.The structures and morphologies were characterized by field emission gun scanning electron microscopy (FEG-SEM), Zeiss Supra 35, coupled to an energy dispersive X-ray (EDX).The photochemical properties were analyzed by diffuse reflectance spectroscopy (DRS), by using an UV/Vis/NIR spectrophotometer (PerkinElmer Lambda 1050) equipped with a 150 mm Integrating Sphere and a high sensitivity Gridless-PMT detector operating between 200 and 800 nm.The UV/Vis/NIR spectrophotometer was calibrated with a Spectralon standard (Labsphere USRS-99-020).
Photocurrent measurements of both photoelectrodes were performed with a Potentiostat/Galvanostat Model 263 (EG&G Princeton Applied Research Co., USA), by using a conventional three-electrode cell with a double jacket where external thermostated water recirculated to maintain the solution temperature at 25 o C. A Philips high-pressure Hg lamp (I = 9.2 W m -2 and 125 W) without glass protection (inserted in a quartz cylinder) was immersed in 250 mL of 0.100 mol L -1 aqueous sodium sulfate (Na 2 SO 4 ).A platinum wire and an Ag/AgCl (KCl, 3.0 mol L -1 ) were employed as counter and reference electrodes, respectively.The linear sweeps were carried out using a scan rate of 10 mV s -1 , in the range potential of -0.5 to 2.0 V under and without lamp exposure, separated from the photoanode by a distance of 2.0 cm.

Evaluation of the photoelectrocatalytic activities of TiO 2 NT and Pt/TiO 2 NT photoelectrodes
Photoelectrocatalytic experiments were performed by using a conventional three-electrode electrochemical cell with cylindrical cell of 500 mL capacity with a double jacket, where the temperature was maintained at 25 °C via external water recirculation by using a thermostat.TiO 2 NT (undecorated) and Pt/TiO 2 NT photoelectrodes were used as anodes, platinum gauze as a cathode (auxiliary electrode) and Ag/AgCl (KCl, 3.0 mol L -1 ) as the reference electrode.The geometric areas of the photoanodes were 5.0 cm 2 , whereas the platinum gauze cathode was 4.0 cm 2 .For all PEC experiments, photoanode and platinum gauze cathode were arranged around a high-pressure mercury lamp (125 W) without the bulb.The gap between photoanodes and Hg lamp was ca.2.0 cm.The PEC assay experiments were performed with a TECTROL R3/AS1 power supply and under potentiostatic mode.The cell potentials were monitored with a MINIPA ET-2042D digital multimeter connected in parallel to the electrochemical cell.
Comparative PEC treatments (by using TiO 2 NT and Pt/TiO 2 NT photoelectrodes) of 500 mL of 85.4 mg L -1 AR29 solution (35 mg L -1 TOC) in 0.05 mol L -1 Na 2 SO 4 were conducted at potential of 2.0 V vs. Ag/AgCl (KCl, 3.0 mol L -1 ) in the range of pH from 3.0 to 6.0 and under continuous stirring with a magnetic bar to provide the transport of species towards the electrodes.Samples were withdrawn from the cell at regular time intervals.The color removal of AR29 solutions was monitored from the absorbance decay at the wavelength of 508 nm (corresponding to maximum absorption) using a Hewlett Packard 8453 UV-Vis spectrophotometer operating in the range of 190-900 nm and the efficiency of dye decolorization was calculated as: where A 0 and A t are the maximum absorbance (l = 508 nm) before and after irradiation, respectively.The degradation of AR29 solutions was monitored from the abatement of their TOC, determined on a Shimadzu TOC-V CPN analyzer and reproducible TOC values with an accuracy of ± 2% were always found by injecting 800 µL samples to the TOC analyzer.Decay kinetics of AR 29 were followed by reversed-phase HPLC using a Shimadzu 10 Avp LC fitted with a Spherisorb ODS2 (5 µm, 150 mm × 4.6 mm i.d.) column and coupled with photodiode array detectors at l = 508 nm.The mobile phase used in isocratic mode was 75:25 (v/v) acetonitrile/phosphate buffer (pH = 3.5) with a flow rate of 0.6 mL min −1 at 25 °C.

Results and Discussion
Characterization of TiO 2 NT and Pt/TiO 2 NT photoelectrodes Figures 2a-2e illustrate the morphologies of TiO 2 NT photoelectrodes produced via anodization of Ti sheets before (Figure 2a) and after (Figures 2b-e) modification with Pt nanoparticles by electrodeposition methodology using different deposition times.The results indicate that the adopted methodology promoted the formation/ growth of highly ordered and structured nanotubes, with mean inner diameters varying from 104 to 124 nm and with thickness of about 13 nm (see Figures 2a and 2b).The synthesized TiO 2 NTs were remarkably well-aligned (vertically to the Ti substrate) with nanotube layers of up to 1.20 µm length, as shown in the inset of Figure 2a.
The Pt/TiO 2 NT photoelectrodes prepared by electrochemical Pt deposition employing a cathodic current density of 10 mA cm -2 during 15, 20, 30 and 40 min (Figures 2b, c, d and e, respectively) show that the time of electrochemical reduction of chloroplatinic acid affects directly the Pt nanoparticles formation.By using 15 min of cathodic deposition the TiO 2 NT surface is decorated with uniformly distributed Pt nanoparticles with diameter of 2-5 nm (Figure 2b), which were confirmed as Pt atoms by EDX measurements.The cross-sectional view illustrated at the inset of Figure 2b shows that the Pt nanoparticles were also uniformly deposited on TiO 2 NT walls without any sign of aggregation, with nanoparticle sizes similar to those described above (2-5 nm). Figure 2c shows that Pt/TiO 2 NT photoelectrode prepared employing 20 min of electrolysis presents deposits with bigger and more irregularly distributed Pt nanoparticles, with Pt deposits reaching up to 30 nm.Figures 2d and 2e   clusters, when compared with the electrodes produced in shorter times (see Figure 2e).Therefore, we can verify that Pt particles sizes were proportional to the applied charge for electrodeposition, i.e., more aggregation of Pt nanoparticles was observed at longer deposition times.The results indicate that Pt deposition by electrochemical reduction on TiO 2 NTs is very efficient for obtaining Pt nanoparticles regularly distributed on TiO 2 NT surface, i.e., highly separated and spaced over all electrode surface, and short deposit times, such as 15 min can promote small particle formation and more efficient coating.Although EDX analysis has been used for all TiO 2 NT photoelectrodes to confirm the formation and presence of platinum, for simplicity only EDX spectrum of Pt/TiO 2 NT photoelectrode obtained during 15 min electrolysis is depicted, as can be seen in Figure 2f.
Figure 3 compares the X-ray diffraction patterns of the TiO 2 NT and the Pt/TiO 2 NT photoelectrodes (deposits of 15 min).As can be seen, the shape of X-ray diffraction peaks of Pt/TiO 2 NT photoelectrode was similar to the undecorated one, due to the small Pt concentration in relation to the TiO 2 NTs and to the detection limit of the equipment employed.All the diffraction peaks identified and located at 25.5, 38.1, 48.1, 54.8 and 62,7° are indexed as anatase TiO 2 (JCPDS card No. 21-1272) corresponding to reflections of (1 0 1), (0 0 4), (2 0 0), (1 0 5) and (2 0 4) planes, respectively. 35otocurrent-potential curves in dark conditions (curve a) and under UV-Vis illumination by using TiO 2 NT and Pt/TiO 2 NT (Pt electrodeposition times of 15, 20, 30 and 40 min) photoelectrodes in 0.100 mol L -1 Na 2 SO 4 are compared in Figure 4.All photocurrents generated for Pt/TiO 2 NT (decorated) photoelectrodes (curves b-e, Figure 4) are higher than the undecorated one (Figure 4, Curve f), and gradually reaches current plateaus (saturated states) at positive potentials near 1.0 V under UV-Vis lamp exposure, with insignificant current response in the dark in the potential range of -0.5 to 2.0 V. Taking into consideration that the irradiation source includes UV and visible light content, it seems that the Pt introduction could be improving the light absorption in relation to TiO 2 NTs (undecorated) that is activated only at wavelengths lower than 380 nm.
Nevertheless, comparing the effect of Pt nanoparticle size deposit on TiO 2 NT surface it is possible to observe that the photocurrents generated were inversely proportional to the electrodeposition time.The maximum photocurrent densities for Pt/TiO 2 NTs is obtained for Pt electrodeposition times of 15 min, approximately 41% higher than obtained for electrodeposition carried out on 40 min.The respective values of photocurrent (taken at 1.5 V) for all Pt/TiO 2 NT (decorated in different times) photoelectrodes are shown in Table 1.This behavior can be simply explained by the formation of smaller and more uniformly distributed Pt nanoparticles which serve as efficient electron traps (i.e., Schottky barriers) to avoid the electro-hole recombination. 40n the other hand, superfluous Pt content and/or a large particle size distribution on the TiO 2 NT surfaces would block the transferring of electrons to the Pt nanoparticles to some extent, increasing the electron-hole recombination. 41n short, the modification of TiO 2 with Pt smaller nanoparticles promotes efficient light absorption and reduction on the recombination of the photogenerated electron-hole pairs generated under UV-Vis light.These photogenerated holes can be trapped in the photoanode surface by H 2 O/OH -species, giving rise to • OH radicals, which could improve the mineralization of organic compounds in favorable conditions. 5 The other effect observed for photocurrent-potential curves by using TiO 2 NT and Pt/TiO 2 NT (Pt electrodeposition times of 15, 20, 30 and 40 min) photoelectrodes in 0.100 mol L -1 Na 2 SO 4 (Figure 4) is the shift on flat-band potentials (E fb ).This corresponds to the situation in which there is no charge accumulation at semiconductors and that at n-type semiconductors photoanodic currents only flow at potentials more positive than E fb . 42The flat-band potentials for TiO 2 NT (undecorated) and for all Pt/TiO 2 NT photoelectrodes were calculated using the Butler equation, 5,43 and their values are exhibited in Table 1.From similar plots, the introduction of Pt nanoparticles promotes a shift of 167 mV in the flat-band potentials to less positive potential when TiO 2 NTs are decorated with smaller Pt nanoparticles (electrochemical deposition during 15 min).This could be indicative of a better band bending and of a consequent improvement in the charge separation. 44hese results are confirmed by comparing the UV-Vis diffuse reflectance spectra of TiO 2 NTs (undecorated) and Pt/TiO 2 NTs (electrodeposits of 15 min), as shown in Figure 5.The spectra indicates a strong light absorption in the UV region, ascribed to the charge transfer from the valence band (2p orbital of TiO 2 NTs) to the conduction band (3d orbital of the Ti 4+ ) for both photoelectrodes. 45ut, marked peaks around 650 nm (absorption in the visible region) were observed for Pt/TiO 2 NT materials.The increase in the absorption peak intensity in the visible region with the addition of platinum can possibly be related to surface plasmon resonance (SPR) effect of electrons in the Pt nanoparticles. 46,47Additionally, it is observed a significant red shift induced by platinum deposited on TiO 2 NTs probably due to the formation of an intra-gap energy level inside the band gap of TiO 2 NTs. 46igure 6 shows the estimated band gap values (obtained by extrapolating the linear region to (αhν) 1/2 = 0) for TiO 2 NT and Pt/TiO 2 NT photoelectrodes, calculated with the Kubelka-Munk function (equation 2): 48 where α is the extinction coefficient, h is Planck's constant (J s), v is the incident light frequency (s -1 ), A is the absorption constant, E g is the band gap (eV) and n is the absorption coefficient.An n value of 1 was chosen for all the samples, indicating a direct allowed optical transition. 49The band gap of TiO 2 NT (undecorated) and Pt/TiO 2 NT photoelectrodes were estimated to be 3.21 and 2.87 eV, respectively (Figure 6).Thus, the results indicate that Pt deposition on TiO 2 NT photoelectrode results in an increase in the visible-light response, i.e., that the deposition of Pt nanoparticles effectively extends the absorption from UV to a visible region by the reduction of the band gap value. 32Taking into account that the irradiation system adopted as source promotes irradiation in UV and visible light, an improvement in the photodegradation of pollutants is expected when TiO 2 NTs are decorated with Pt nanoparticles.Further studies were carried out comparing the degradation of AR29 dye by using both electrodes.

Degradation of AR29 dye at TiO 2 NT and Pt/TiO 2 NT photoelectrodes
In order to test the photoelectrocatalytic activities of TiO 2 NT (undecorated) and Pt/TiO 2 NT (decorated with Pt by electrochemical method during 15 min) photoelectrodes, PEC assays were conducted for 85.4 mg L -1 AR29 solutions (35 mg L -1 TOC) in 0.05 mol L -1 Na 2 SO 4 (pH 6.0) at bias potential of 2.0 V vs. Ag/AgCl by using UV-Vis irradiation.Figure 7 compares the percentage of color removal and the TOC abatement obtained using TiO 2 NT (undecorated) and Pt/TiO 2 NT photoelectrodes.The percentage of decolorization was obtained by monitoring the absorbance at l = 508 nm, where azo group is acting as chromophore. 3s can be seen at Figure 7, PEC assays conducted by using Pt/TiO 2 NT photoelectrode were more efficient than the undecorated one for both responses, i.e., for efficiency of decolorization and TOC abatement.
Then, the effect of pH was studied by monitoring the dye decolorization in 0.05 mol L -1 Na 2 SO 4 at pH 3.0, 4.5 and 6.0, and bias potential of 2.0 V vs. Ag/AgCl by using UV-Vis irradiation.For all degradation experiments, slight pH decreases with prolonging electrolysis time up to 120 min were observed.This drop of pH can be related to the formation of aliphatic carboxylic acids as found for treatment of other dyes. 3,50Taking into account that at acidic conditions there is no need of pH correction, all the experiments were done in acidic medium.The percentages of color removal calculated from equation 1 and for three pH values are plotted in Figure 8 for both photoelectrodes.Total color removal of the AR29 solutions was obtained by using the Pt/TiO 2 NT (decorated) photoelectrode at pH values of 3.0 and 4.5 after 60 min of electrolysis.On the other hand, at pH 6.0 partial color removal (87%) was obtained for the same time of electrolysis.A similar tendency was observed while using TiO 2 NT (undecorated) photoelectrodes, with maximum decolorization efficiencies at pH values of 3.0 and 4.5.However, decolorization efficiencies obtained by using the undecorated material were slightly lower compared to the decorated one for 60 min of electrolysis.
The adsorption process of ionic form of the AR29 dye (AR29 2-) onto Pt/TiO 2 NT and TiO 2 NT surfaces is probably the first step in the process of AR29 oxidation. 51o, the effect of pH on photoelectrocatalytic oxidation of AR29 may be securely explained by the relation/ interaction between the surface charge of TiO 2 surface and the acid dissociation constant (pK a = -3.08 at 25 °C) of AR29.Charge on TiO 2 NT surface is formed by either protonation (Ti-OH + H + → Ti-OH 2 + ) or deprotonation (Ti-OH + OH -→ Ti-O -+ H 2 O) of the Ti-OH bonds. 52It is known from literature that the isoelectric point (IEP) for TiO 2 varies between 5.2 and 5.5. 53The IEP (or point of zero charge, PZC) is the pH at which the surface charge is electrically neutral.On the other hand, the surface is positively charged at a pH < IEP and negatively charged at pH > IEP. 52The anionic form of the AR29 (AR29 2-) predominates above its pK a value.Therefore, the pH range from -3.08 to 5.5 (i.e., at pH between the pK a and the IEP) which may be the optimum condition for the adsorption of AR29 2-onto Pt/TiO 2 NT and TiO 2 NT surfaces, explains why the kinetics of the AR29 oxidation was favored at more acid conditions.For pH values above 5.5 the TiO 2 NT surface is negatively charged and the adsorption process of AR29 2-is not favored.
Better results shown by the Pt/TiO 2 NT photoelectrode compared with the undecorated one can be explained by  the fact that when coupling metallic Pt with TiO 2 NTs, photogenerated electrons can flow from the semiconductor to the metallic Pt forming the Schottky barrier on the metal-semiconductor interface 33,35,54,55 due to the higher energy of conduction band of the TiO 2 NTs (undecorated) compared with the new formed Fermi level of Pt/TiO 2 NTs.So the electrons on the Pt surface can be transferred to adsorbed O 2 to form O 2 •− , while holes accumulated at the valence band of TiO 2 NTs led to the additional production of the strong and non-selective radical • OH.Finally, the hydroxyl radical formed reacts with the AR29 dye until their total mineralization, i.e., conversion into carbon dioxide, water and inorganic ions.In other words, Pt nanoparticles deposited on the TiO 2 NT surface act as electron scavengers, promoting a better separation of electron-hole pairs.Consequently, more • OH radicals were generated, enhancing the photocatalytic activity of TiO 2 NTs and the decolorization and degradation rates.Moreover, Pt/TiO 2 NT photoelectrodes have shown a stronger light absorption both in UV and visible regions than that of undecorated ones (see Figure 8), which coincides with the absorption lines in the regions (i.e., at l = 254, 373, 410, 441, 542 and 572 nm) obtained for the employed Hg lamp.Therefore, more photons with specific wavelength can be absorbed, thus enhancing the photoelectrocatalytic activity.Furthermore, AR29 solutions were exposed directly to the same high-pressure Hg lamp during 30 min and significant changes in the absorbance (at l max = 508 nm) were not observed, indicating that this dye is not directly photolyzed.
The mineralization of AR29 solutions by PEC process was monitored as a function of the TOC abatement.Figure 9 shows the TOC-time plots obtained for the degradation of the 85.4 mg L -1 AR29 solution by using TiO 2 NT (undecorated) and Pt/TiO 2 NT photoelectrodes at pH values of 3.0, 4.5 and 6.0.It can be observed that TOC decayed more rapidly for the Pt/TiO 2 NT photoelectrode when compared to the undecorated one, after 120 min of degradation.At this time, TOC reductions of 92%, 89% and 80% were obtained for pH values of 3.0, 4.5 and 6.0, respectively.On the other hand, at the same time and by using the TiO 2 NT (undecorated) photoelectrode only 66%, 67% and 61% of TOC abatement (after 120 min electrolysis) were found for pH values of 3.0, 4.5 and 6.0, respectively.These results corroborate the findings of photocurrent and decolorization obtained in this work (Figures 4 and 8, respectively), due to the better adsorption of ionic form of the AR29 dye (AR29 2-) onto Pt/TiO 2 NT and TiO 2 NT surfaces at more acid conditions (as explained above).As expected, higher efficiency on the dye mineralization was obtained by using the Pt/TiO 2 NT material probably due to the better separation of electron-hole pairs generating additional • OH radicals, which accelerate the oxidation process, as it has been explained above.Furthermore, the TOC content in AR29 solutions did not vary when exposed to Hg lamp source during 120 min, confirming that the direct photolysis of this dye can be neglected.Although the decorated photoelectrode has yielded 92% TOC removal of dye solution, the formation of recalcitrant products (i.e., products hardly destroyed by photogenerated • OH radicals) may have prevented their total mineralization. 7e kinetics of degradation of 85.4 mg L -1 AR29 in 0.05 mol L -1 Na 2 SO 4 by • OH radicals formed at Pt/TiO 2 NT and TiO 2 NT (undecorated) photoanode surfaces were also followed by reverse-phase HPLC coupled to diode array detector (see Figure 10).The chromatograms obtained for AR29 dye displayed a well-defined peak at retention time  (t R ) of 8.35 min.Direct photolysis of the AR29 dye was discarded because its content in solution remained constant after 120 min under UV lamp exposure and without potential application by the photoelectrochemical cell.
Figure 10 highlights the quick and almost total degradation of the 85.4 mg L -1 AR29 solution in 0.05 mol L -1 Na 2 SO 4 at pH 3.0 by using Pt/TiO 2 NTs (decorated) applying 2.0 V vs. Ag/AgCl and under UV-Vis irradiation exposure during 30 min.Similar concentration decay was observed using the TiO 2 NT (undecorated) photoelectrode under the same experimental conditions.As can be seen in the inset in Figure 10, the concentration decays fitted well with equation expected for pseudo first-order kinetics.From this analysis, pseudo first-order constants (k 1 ) of 3.0 × 10 -3 s -1 (R 2 = 0.996) and 1.36 × 10 -3 s -1 (R 2 = 0.987) were obtained for Pt/TiO 2 NT (decorated) and TiO 2 NT photoelectrodes, respectively.The fastest AR29 dye degradation promoted by the Pt/TiO 2 NT photoelectrode can be ascribed to Pt nanoparticles deposited on the TiO 2 NT surface, which act as electron sinks promoting a better separation of electron-hole pairs, generating more • OH radicals, 32 and consequently also promoting a better light absorption than TiO 2 NT (undecorated) photoelectrode.
These results are in agreement with TOC abatement illustrated in Figure 9, indicating that the use of Pt/TiO 2 NT photoelectrodes in the photoelectrocatalytic oxidation of dye are not only more efficient in decolorization of dye solutions, but also for TOC mineralization when compared to the undecorated one.

Conclusions
In this work, Pt decorated TiO 2 NT photoelectrodes were prepared using different deposition times under galvanostatic condition.Platinum nanoparticles were more uniformly distributed, highly separated and spaced over the entire TiO 2 NT surface in shorter deposition times.Additionally, it has been verified that Pt particle sizes were proportional to the applied charge, i.e., more aggregation (clusters) of Pt particles were observed at longer deposition times.Similarly, the higher photocurrent response was obtained by applying the Pt/TiO 2 NT photoelectrode which presented a better Pt nanoparticle distribution on TiO 2 NT surface.The band gap of this Pt/TiO 2 NT photoelectrode was red shifted to the visible region in comparison with the undecorated one, and their band gap were estimated (by using Kubelka-Munk function) to be 3.21 and 2.87 eV, respectively.
The decolorization and mineralization rate of AR29 dye solutions were studied employing TiO 2 NT (undecorated) and Pt/TiO 2 NT photoelectrodes and at different pH values (3.0, 4.5 and 6.0).Although the total color removal of AR29 dye solutions has been achieved by using the Pt/TiO 2 NT photoelectrode at pH values of 3.0 and 4.5 (i.e., pH values which are between the pK a of AR29 and the IEP for TiO 2 ) after 60 min of electrolysis, at pH 6.0, only partial color removal (87%) was achieved at the same time.Similar tendency was observed for the undecorated photoelectrode, even if less efficient than the decorated one.Furthermore, TOC reductions of 66 and 92% were obtained at pH 3.0 (the optimum pH value) and after 120 min electrolysis by using TiO 2 NT and Pt/TiO 2 NT photoelectrodes, respectively.For both materials, the AR29 decay followed pseudo first-order kinetics with similar constant rates, which is double than with the Pt/TiO 2 NTs electrode.This difference on TOC reductions showed that platinum nanoparticles improves the light absorption composed of UV and visible irradiation in relation to TiO 2 NTs (undecorated) that is activated only by UV irradiation and, in addition, it can accelerate the dye mineralization due to the better separation of electronhole pairs, generating additional • OH radicals, i.e., due to the higher photocatalytic activity of the Pt/TiO 2 NT photoelectrode compared to the undecorated one.Finally, our results revealed that platinum modification of TiO 2 NTs by using a simple method is a promising and an attractive way to develop photoelectrodes with high photocatalytic activity and capacity for dye oxidation improving the light absorption in a situation close to solar radiation.
(for 30 and 40 min of Pt deposition, respectively) indicated that the Pt deposits are deeply irregular with cluster formation, which compromises the deposits' quality.Furthermore, Pt/TiO 2 NT electrodes obtained for 40 min of electrolysis showed Pt nanoparticles with varying sizes and poorly distributed Pt

Figure 7 .
Figure 7. Percentage of color removal and TOC abatement vs. degradation time of 500 mL of a 85.4 mg L -1 Acid Red (AR29) solution in 0.05 mol L -1 Na 2 SO 4 by the PEC process and applying 2.0 V vs. Ag/AgCl for: () TiO 2 NT (undecorated) and () Pt/TiO 2 NT (for 15 minutes of Pt electrochemical deposition) photoelectrodes.Applied pH: 6.0.

Table 1 .
Comparison of the results of photocurrent densities (I ph ) and Flat-band potentials (E fb ) for TiO 2 NTs (undecorated) and Pt/TiO 2 NTs (decorated in different times) in 0.100 mol L -1 Na 2 SO 4 under UV irradiation exposure supplied by using a high-pressure mercury lamp (125 W) without the bulb Ag/AgCl; b flat-band potential vs. Ag/AgCl (KCl, 3.0 mol L -1 ).
a At 1.5 V vs.