Physico-chemical characterization of Fe3O4 nanoparticles by XPS / HAXPES / SEM

Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”.

Fe₃O₄ nanoparticles were provided by Promethean Particles (EMR identifier in the project: ERM00000409).

Prior to the measurements, the samples were prepared from the solution as drop cast on Si wafers.  First SEM and EDS measurements were performed, followed by XPS and HAXPES measurements on the same samples. Here at first survey spectra were recorded followed by high resolution spectra. For XPS / HAXPES several Si-wafers were mounted together on one platen. The platen was left in the intro chamber of the instrument for several hours before the measurement started.

Equipment:

SEM images were acquired with a Supra 40 (Zeiss) SEM equipped with a Quantax 400 (Bruker) SDD EDS spectrometer.

For X-ray spectroscopy experiments, a combined XPS / HAXPES spectrometer (Quantes from ULVAC-PHI) was used, where XPS is measured at 1486.6 eV (monochromatic Al Kα source) and HAXPES at 5414.9 eV (monochromatic Cr Kα source). Here it is possible to perform the measurements at the exact same position.

Data:

For SEM, the data are given in .tif format. For XPS / HAXPES the raw data are given as .spe (PHI format) and .npl (VAMAS format) files. The measurement conditions are given in the data files.

Naming of data:

SEM: sample_treatment (n), with n a consecutive number.

XPS / HAXPES:    For the .spe and for the corresponding .npl files Pn.m.o.sample_treatment, with Pn: platen-number, m: spectrum number (order of the measurements); o: point-number, of the position on the sample, sample_treatment with "p" for pristine.

The authors thank Sigrid Benemann, who performed the SEM measurements.