Thermal Cycling Effect on Mechanical Properties, Grain Size and Residual Stress in Alumina and Yttria-Stabilized Tetragonal Zirconia

Article Preview

Abstract:

Alumina and zirconia are important materials for energy and optical applications. In this study, the effect of thermal cycling on grain size and residual stress was reported. Residual stress was measured using X-ray diffraction (XRD) sin2ψ method for the as-received and the samples after thermal cycling up to 900 cycles. For alumina, the measured residual stress is approximately 96 MPa in tensile for the as-received material, and increases to its highest value of 480 MPa after 650 thermal cycles. The residual stress decreases from 480 MPa to 96 MPa in tensile with increased thermal cycling from 650 to 900 cycles. The crystallized grain size calculated from the diffraction pattern shows that the mean crystallized grain size is about 93 nm for the as-received and increases to 232 nm after 650 thermal cycles. This result is consistent with the enlarged grain size observed by scanning electron microscopy for the alumina after 650 thermal cycles reported earlier. With continued thermal cycling up to 900 cycles, the crystallized grain size is greatly reduced to 104 nm. It suggests that evolution of the crystallized grain size is correlated with the residual stress. For yttria-stabilized tetragonal zirconia (Y-TZP), the mechanical properties at room temperature, are consistent with the property values provided by the manufacturer. The Young’s modulus of shows a non-linear inverse relationship with increasing temperature. The degradation of the Young’s modulus mostly occurs prior to 400 °C and to a less extent in the temperature range of 400 °C up to 850 °C. The Vickers hardness number for the as-received Y-TZP material decreases to a very small extent after 560 thermal cycles and increases approximately 2%, after 1200 thermal cycles. This is consistent with the trend of the Young’s modulus for thermal-cycled specimens.

You might also be interested in these eBooks

Info:

Periodical:

Advanced Materials Research (Volumes 875-877)

Pages:

1642-1646

Citation:

Online since:

February 2014

Authors:

Export:

Price:

[1] Zhang, J. and S. Bandopadhyay, DOE Annual Report - Novel Dense Membranes for Hydrogen Separation for Energy Applications, (2010).

Google Scholar

[2] Prevey, P.S., A Method Of Determining The Elastic Properties Of Alloys In Selected Crystallographic Directions For X-Ray Diffraction Residual Stress Measurement. Advances in X-Ray Analysis, Vol. 20, Plenum Press, New York, NY, 1977: pp.345-354.

DOI: 10.1007/978-1-4613-9981-0_30

Google Scholar

[3] Prevey, P.S., X-ray Diffraction Residual Stress Techniques. American Society for Metals, 1986: pp.380-392.

DOI: 10.31399/asm.hb.v10.a0001761

Google Scholar

[4] Pecharsky, V.K. and P.Y. Zavalij, Fundamentals of Powder Diffraction and Structural Characterization of Materials (2nd Version). 2005: p.172.

Google Scholar

[5] Bobet, J.L., et al., Thermal residual stresses in ceramic matrix composites-II. Experimental results for model materials. Acta Metallurgica et Materialia, 1995. 43(6): pp.2255-2268.

DOI: 10.1016/0956-7151(94)00430-7

Google Scholar

[6] Motohashi, Y., T. Sekigami, and N. Sugeno, Variation in some mechanical properties of Y-TZP caused by superplastic compressive deformation. Journal of Materials Processing Technology, 1997. 68(3): pp.229-235.

DOI: 10.1016/s0924-0136(96)00106-9

Google Scholar

[7] Tanaka, K., et al., Phase stability after aging and its influence on pin-on-disk wear properties of Ce-TZP/Al2O3 nanocomposite and conventional Y-TZP. Journal of Biomedical Materials Research Part A, 2003. 67A(1): pp.200-207.

DOI: 10.1002/jbm.a.10006

Google Scholar