Slurry Preparation and Hot Tearing Susceptibility of A201 Aluminum Alloy in Rheological Die Casting

Article Preview

Abstract:

A201 alloy is the strongest cast aluminum alloy, but it is considered one of the most difficult aluminum alloys to cast due to its susceptibility to hot tearing during solidification. Semi-solid casting, which characterizes fine near-globular or non-dendritic grains and relatively narrow solidification range, is potential to reduce hot cracking tendency of alloys. In this present work, semi-solid slurries of A201 alloy were prepared using Swirled Enthalpy Equilibrium Device (SEED) technique and then injected into a self-designed high pressure hot tearing mold. The microstructures of A201 semi-solid slurries with different pouring temperatures were examined. Effects of different casting pressures on the hot tearing sensitivity of A201 have been investigated. This study finds that SEED is capable of producing satisfying A201 semi-solid slurries. Lower pouring temperatures produce A201 semi-solid slurries with finer and rounder grains as well as more uniform microstructure distribution. Increasing the intensification pressure significantly decreases the hot treating tendency of A201 alloy. When the pressure reaches to 90 MPa and the mold temperature of about 250 °C, the hot tearing susceptibility (HTS) index value is nearly zero, which means almost no surface cracks are found in the semi-solid A201 die casting parts.

You might also be interested in these eBooks

Info:

Periodical:

Solid State Phenomena (Volume 285)

Pages:

311-317

Citation:

Online since:

January 2019

Export:

Price:

* - Corresponding Author

[1] Z. Fan, Semisolid metal processing, Int. Mater. Rev. 47 (2002) 49-85.

Google Scholar

[2] Q. Zhu, S. Midson, Semi-solid moulding: Competition to cast and machine from forging in making automotive complex components, Trans. Nonferrous Met. Soc. China 20 (2010) 1042-1047.

DOI: 10.1016/s1003-6326(10)60628-0

Google Scholar

[3] G. Wallace, A.P. Jackson, S.P. Midson, Q. Zhu, High-quality aluminum turbocharger impellers produced by thixocasting, Trans. Nonferrous Met. Soc. China. 20 (2010) 1786-1791.

DOI: 10.1016/s1003-6326(09)60375-7

Google Scholar

[4] E.J. Zoqui, 5.09 - Alloys for semisolid processing, in: S. Hashmi, G. F. Batalha, C. J. Van Tyne and B. Yilbas (Eds.), Comprehensive Materials Processing, Elsevier, Oxford, 2014, pp.163-164.

DOI: 10.1016/b978-0-08-096532-1.00520-3

Google Scholar

[5] L. Wang, M. Makhlouf, D. Apelian, Aluminium die casting alloys: alloy composition, microstructure, and properties-performance relationships, Metall. Rev. 40 (1995) 221-238.

DOI: 10.1179/imr.1995.40.6.221

Google Scholar

[6] D. Liu, H.V. Atkinson, H. Jones, Thermodynamic prediction of thixoformability in alloys based on the Al–Si–Cu and Al–Si–Cu–Mg systems, Acta. Mater. 53 (2005) 3807-3819.

DOI: 10.1016/j.actamat.2005.04.028

Google Scholar

[7] H. Möller, U.A. Curle, E.P. Masuku, Characterization of surface liquid segregation in SSM-HPDC aluminium alloys 7075,2024,6082 and A201, Trans. Nonferrous Met. Soc. China. 20 (2010) 847-851.

DOI: 10.1016/s1003-6326(10)60593-6

Google Scholar

[8] B. Zhou, Y.L. Kang, G.M. Zhu, J.Z. Gao, M.F. Qi, H.H. Zhang, Forced convection rheoforming process for preparation of 7075 aluminum alloy semisolid slurry and its numerical simulation, Trans. Nonferrous Met. Soc. China. 24 (2014) 1109-1116.

DOI: 10.1016/s1003-6326(14)63169-1

Google Scholar

[9] A. Bolouri, Q.F. Zhao, P. Côté, X.G. Chen, Microstructure and rheological properties of semi-solid 7075 slurries using SEED rheocasting process, Solid. State. Phenom. 256 (2016) 288-293.

DOI: 10.4028/www.scientific.net/ssp.256.288

Google Scholar

[10] Q. Zhu, S. Midson, C.W. Ming, H.V. Atkinson, Casting and heat treatment of turbocharger impellers thixocast from Alloy 201, Solid. State. Phenom. 192-193 (2013) 556-561.

DOI: 10.4028/www.scientific.net/ssp.192-193.556

Google Scholar

[11] J.E. Hatch, Aluminum: properties and physical metallurgy, ASM International, Ohio, 1984, p.323.

Google Scholar

[12] J.Z. Gao, Q. Zhu, D.Q. Li, Y. L. Kang, Microstructural changes and thermal stability of A201, 319s and 2618 aluminum alloys during thermal exposure, Mater. Sci. Forum. 913 (2018) 55-62.

DOI: 10.4028/www.scientific.net/msf.913.55

Google Scholar

[13] S. Lin, C. Aliravci, M.O. Pekguleryuz, Hot-Tear Susceptibility of Aluminum Wrought Alloys and the Effect of Grain Refining, Metall. Mater. Trans. A. 38 (2007) 1056-1068.

DOI: 10.1007/s11661-007-9132-7

Google Scholar

[14] S. Li, D. Apelian, Hot tearing of aluminum alloys a critical literature review, Int. J. Metalcast. 5 (2011) 23-40.

DOI: 10.1007/bf03355505

Google Scholar

[15] P. Côté, M.È. Larouche, X.G. Chen, New developments with the SEED technology, Solid. State. Phenom. 192-193 (2013) 373-378.

DOI: 10.4028/www.scientific.net/ssp.192-193.373

Google Scholar

[16] S.N. Dubey, Design and evaluation of an enhanced constrained rod casting mold for experimental characterization of hot tearing in aluminum casting alloys, Int. J. Cast Met. Res. 30 (2017) 201-216.

DOI: 10.1080/13640461.2017.1286553

Google Scholar