Preparation and Characterization of Cu-Coated Nano SiC Composite Particles

Sheng Zhu; Chao Li; Jian Hua Du; Wen Zheng Han

doi:10.4028/www.scientific.net/KEM.373-374.674

Paper Titles

A Novel Thermo-Sensitive Polymer Film and its Imaging Properties
p.658

Study on Preparation and Properties of a Room Temperature Fast Curing Epoxy Resin Nano-Adhesive
p.662

Preparation of TiC/ Fe Surface Composite by a Casting–SHS Process
p.666

Surface Modification of Nano-Copper and its Dispersive Behavior in Water
p.670

Preparation and Characterization of Cu-Coated Nano SiC Composite Particles
p.674

The Synthesis and Phase Behavior of a Novel Discoticnematic Triphenylene Mesogen and its Application to an Optically Anisotropic Film
p.678

The Insulated Effect of New Inorganic Coatings on the Surface of Fiber Paper
p.682

A Photometric Method for Measuring Photoacid Generator Efficiencies Using Rhodamine B as Acid Sensor in Thin Polymer Films
p.686

Superficial Optimization of Microcapsule
p.690

HomeKey Engineering MaterialsKey Engineering Materials Vols. 373-374Preparation and Characterization of Cu-Coated Nano...

Preparation and Characterization of Cu-Coated Nano SiC Composite Particles

Abstract:

The Cu-coated nano SiC composite particles were prepared by heterogeneous nucleation method. For the heterogeneous nucleation process, the dispered nano SiC particles and the active Cu2O precipitation were both prefabricated. The composite particles were characterized by means of XRD, SEM, EDS, TEM and ED analysis technics. It is found that Cu layers are coated on the nano SiC particles, which are continuous and dense, and partly oxidized to Cu2O, and the oxidation rate can be reduced by improving experimental processes. The investigation on reaction mechanism shows the disproportionating reaction speed of Cu+ can be controlled by adjusting the pH value of reaction solution, which makes the degree of supersaturation of Cu crystallites accord with the conditions of heterogeneous nucleation.