0.72Pb(Zr0.47Ti0.53)O3-0.28Pb[(Zn0.45Ni0.55)1/3Nb2/3]O3 (0.72PZT-0.28PZNN) thick films were prepared by using a tape casting method to develop new materials with high energy-density applicable to energy-harvesting devices. The piezoelectric strain constant (d 33), dielectric constant (ɛ T33 /ɛ 0), piezoelectric voltage constant (g 33) and transduction coefficient (d 33·g 33) of the films were affected by the sintering temperature. These results could be attributed to the crystal structure, microstructures and secondary phases. However, the dielectric loss (tanδ) of the films was not changed remarkably with increasing sintering temperature. Typically, a d 33 of 452 pC/N, ɛ T33 /ɛ 0 of 1444, d 33·g 33 of 20,340 × 10−15 m2/N and tanδ of 0.15% were obtained for the films sintered at 1050 °C for 1 h. The power generation performance of the piezoelectric unimorph cantilever was assessed to demonstrate the feasibility of the 0.72PZT-0.28PZNN piezoelectric thick film. Also, theoretical models were employed to predict the resonance frequency of the unimorph cantilever generator, and the predicted values were compared with experimental data.
Similar content being viewed by others
References
Y.-J. Cha, I.-T. Seo, I.-Y. Kang, S.-B. Shin, J.-H. Choi, S. Nahm, T.-H. Seung and J.-H. Paik, J. Appl. Phys. 110, 084111 (2011).
I.-T. Seo, Y.-J. Cha, I.-Y. Kang, J.-H. Choi, S. Nahm, T.-H. Seung and J.-H. Paik, J. Am. Ceram. Soc. 94, 3629 (2011).
R. A. Islam and S. Priya, J. Am. Ceram. Soc. 89, 3147 (2006).
S. Priya, IEEE Trans. Ultrason. Ferroelectr. Freq. Control 57, 2610 (2010).
K. Carl and K. H. Härdtl,, Phys. Stat. Sol. A 8, 87 (1971).
S. Roundy, P. K. Wright and J. Rabaey, Computer Commun. 26, 1131 (2003).
S. Roundy, P. K. Wright and J. M. Rabaey, Energy Scavenging for Wireless Sensor Networks: With Special Focus on Vibrations (Kluwer Academic Publishers, Boston, 2004).
H. Shen, J. Qiu and M. Balsi, Sens. Actuators A 169, 178 (2011).
X. Dai, Y. Wen, P. Li, J. Yang and M. Li, Sens. Actuators A 166, 94 (2011).
V. R. Challa, M. G. Prasad, Y. Shi and F. T. Fisher, Smart Mater. Struct. 17, 015035 (2008).
R. Ly, M. Rguiti, S. D’Astorg, A. Hajjaji, C. Courtois and A. Leriche, Sens. Actuators A 168, 95 (2011).
I.-H. Kim, H.-J. Jung, B. M. Lee and S.-J. Jang, Appl. Phys. Lett. 98, 214102 (2011).
X. Gao, W.-H. Shih and W. Y. Shih, Appl. Phys. Lett. 97, 233503 (2010).
J.-S. Park, H.-D. Park and S.-G. Kang, Sens. Actuators A 117, 1 (2005).
J. V. Shanahan, E. H. Kisi, J. S. Forrester, H. J. Goodshaw, J. S. Zobec and D. Phelan, J. Am. Ceram. Soc. 93, 3902 (2010).
Z. L. Wang, J. J. Li, Z. H. Sun, Y. L. Li, Q. Luo, C. Z. Gu and Z. Cui, Appl. Phys. Lett. 90, 133118 (2007).
K. V. R. Prasad, A. R. Raju and K. B. R. Varma, J. Mater. Sci. 29, 2691 (1994).
X.-G. Tang and H. L.-W. Chan, J. Appl. Phys. 97, 034109 (2005).
P. Moetakef and Z. A. Nemati, Sens. Actuators A 141, 463 (2008).
D. M. Stein, M. R. Suchomel and P. K. Davies, Appl. Phys. Lett. 89, 132907 (2006).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Jeon, C.J., Hwang, H.N., Jeong, Y.H. et al. High energy-density 0.72Pb(Zr0.47Ti0.53)O3-0.28Pb[(Zn0.45Ni0.55)1/3Nb2/3]O3 thick films fabricated by tape casting for energy-harvesting-device applications. Journal of the Korean Physical Society 63, 1772–1776 (2013). https://doi.org/10.3938/jkps.63.1772
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.3938/jkps.63.1772