Effects of Si Addition on the Microstructure and Properties of Cr-Al alloy for High Temperature Coating

고온 코팅용 Cr-Al합금의 미세조직 및 특성에 미치는 Si 첨가의 영향

Jeong-Min Kim1†
,
Il-Hyun Kim2
,
Hyun-Gil Kim2
김 정민1†
,
김 일현2
,
김 현길2
1Department of Materials Science and Engineering, Hanbat National University, Daejeon 34158, Republic of Korea
2Light Water Reactor Fuel Technology Division, Korea Atomic Energy Research Institute, Daejeon 34057, Republic of Korea
1한밭대학교
2한국원자력연구원
†Corresponding author E-Mail : jmk7475@hanbat.ac.kr (J.-M. Kim, Hanbat Nat’l
January 2019. pp. 7-10
PDF XML Citation
Abstract

Cr-Al alloys are attracting attention as oxidation resistant coating materials for high temperature metallic materials due to their excellent high temperature stability. However, the mechanical properties and oxidation resistance of Cr-Al alloys can be further enhanced, and such attempts are made in this study. To improve the properties of Cr-Al alloys, Si is added up to 5 wt%. Casting specimens with different amounts of Si content are prepared by a vacuum arc remelting method and isothermally heated under steam conditions at 1,100°C for 1 hour. The as-cast microstructure of low Si alloys is mainly composed of only a Cr phase, while Al8Cr5 and Cr3Si phases are also observed in the 5% Si alloy. In the high Si alloy, only Cr and Cr3Si phases remain after the isothermal heating at 1,100°C. It is found that Si additions slightly decrease the oxidation resistance of the Cr-Al alloy. However, the microhardness of the Cr-Al alloy is observed to increase with an increasing Si content.

Keywords
Cr-Al alloy
oxidation resistance
microhardness
microstructure
References
1.
W. Zhong, P. A. Mouche and B. J. Heuser, J. Nucl. Mater., 498, 137 (2018). 10.1016/j.jnucmat.2017.10.021
2.
T. K. Sawarn, S. Banerjee, A. Samanta, B. N. Rath and S. Kumar, J. Nucl. Mater., 467, 820 (2015). 10.1016/j.jnucmat.2015.10.012
3.
H. G. Kim, I. H. Kim, Y. I. Jung, D. J. Park and J. Y. Park, J. Nucl. Mater., 465, 531 (2015). 10.1016/j.jnucmat.2015.06.030
4.
A. S. Kuprin, V. A. Belous, V. N. Voyevodin, V. V. Bryk, R. L. Vasilenko, V. D. Ovcharenko, E. N. Reshetnyak, G. N. Tolmachova and P. N. V’yugov, J. Nucl. Mater., 465, 400 (2015). 10.1016/j.jnucmat.2015.06.016
5.
J. M. Kim, J. C. Lee, I. H. Kim and H. G. Kim, Korean J. Mater. Res., 27, 563 (2017).
6.
J. M. Kim, T. H. Ha, I. H. Kim and H. G. Kim, Metals, 7, 59 (2017).
7.
C. Chen, J. Zhang, C. Duan, X. Feng and Y. Shen, J. Alloy. Compd., 660, 208 (2016). 10.1016/j.jallcom.2015.11.094
8.
S. Cui and I. H. Jung, J. Alloy. Compd., 708, 887 (2017). 10.1016/j.jallcom.2017.03.042
9.
Y. Liang, C. Guo, C. Li and Z. Du, JPEDAV, 30, 462 (2009). 10.1007/s11669-009-9572-4
10.
R. Yang, Q. Wu, S. Li and S. Gong, Procedia Eng., 27, 976 (2012).
11.
N. Birks, G. H. Meier and F. S. Pettit, Introduction to the high-temperature oxidation of metals, p. 101, Cambridge Univ. Press, Cambridge, UK (2006). 10.1017/CBO9781139163903.007
12.
I. Rosales and H. Martinez, J. Mater. Sci. Chem. Eng., 2, 64 (2014).
13.
J. Newkirk and J. A. Hawk, Wear, 251, 1361 (2001). 10.1016/S0043-1648(01)00768-2
Information
  • Publisher :Materials Research Society of Korea
  • Publisher(Ko) :한국재료학회
  • Journal Title :Korean Journal of Materials Research
  • Journal Title(Ko) :한국재료학회지
  • Volume : 29
  • No :1
  • Pages :7-10
  • Received Date : 2018-09-28
  • Revised Date : 2018-09-28
  • Accepted Date : 2018-10-23
  • DOI :https://doi.org/10.3740/MRSK.2019.29.1.7
Journal Informaiton Korean Journal of Materials Research Korean Journal of Materials Research
Online Submission
  • scopus
  • NRF
  • KOFST
  • crossref crossmark
  • crossref cited-by
  • crosscheck
  • open access
  • ccl
Journal Informaiton Journal Informaiton - close