Korean Journal of Materials Research ISSN:1225-0562(Print) 2287-7258(Online) 한국재료학회지

In this study, we investigated the overpotential of precipitation related to the catalytic activity of electrodes on the initial process of electrodeposition of Co and Co-Ni alloys on polycrystalline Cu substrates. In the case of Co electrodeposition, the surface morphology and the magnetic property change depending on the film thickness, and the relationship with the electrode potential fluctuation was shown. Initially, the deposition potential(−170 mV) of the Cu electrode as a substrate was shown, the electrode potential(E_dep) at the T_on of electrodeposition and the deposition potential(−600 mV) of the surface of the electrodeposited Co film after T_off and when the pulse current was completed were shown. No significant change in the electrode potential value was observed when the pulse current was energized. However, in a range of number of pulses up to 5, there was a small fluctuation in the values of E_dep and E_imm. In addition, in the Co-Ni alloy electrodeposition, the deposition potential(−280 mV) of the Cu electrode as the substrate exhibited the deposition potential(−615 mV) of the electrodeposited Co-Ni alloy after pulsed current application, the E_dep of electrodeposition at the T_on of each pulse and the E_imm at the T_off varied greatly each time the pulse current was applied. From 20 % to less than 90% of the Co content of the thin film was continuously changed, and the value was constant at a pulse number of 100 or more. In any case, it was found that the shape of the substrate had a great influence.