Effect of Physical Parameters on Fatigue Life of Materials and Alloys: A Critical Review

: Fatigue refers to the progressive and localized structural damage that occurs when a material is subjected to repeated loading and unloading, typically at levels below its ultimate strength. Several failure mechanisms have been observed in practical scenarios, encompassing high-cycle, low-cycle, thermal, surface, corrosion, and fretting fatigue. Fatigue, connected to the failure of numerous engineered products, stands out as a prevalent cause of structural failure in service. Conducting research on the advancement and application of fatigue analysis technologies is crucial because fatigue analysis plays a critical role in determining the service life of components and mitigating the risk of failure. This study compiles data from a wide range of sources and offers a thorough summary of the state of fatigue analysis. It focuses on the effects of different parameters, including hardness, temperature, residual stresses, and hardfacing, on the fatigue life of different materials and their alloys. The fatigue life of alloys is typically high at low temperatures, but it is significantly reduced at high temperatures or under high-stress conditions. One of the main causes of lower fatigue life is residual stress. High-temperature conditions and hardfacing processes cause the development of tensile residual stresses, which in turn decreases fatigue life. But, if the hardness of the material significantly increases due to hardfacing, then the fatigue life also increases. This manuscript focuses on reviewing the research on fatigue-life prediction methods, shortcomings, and recommendations.


Introduction
Fatigue is defined as a type of failure caused by a repeated load that does not exceed the point of failure in a single occurrence [1].The way materials react and break down when subjected to repetitive stresses, such as mechanical or thermal loads, is communicated using engineering language.Fatigue damage is identified by the nucleation, coalescence, and stable propagation of cracks that can result in the material either yielding or fracturing in a brittle manner.Fatigue also refers to the development and propagation of cracks in a material caused by cyclic loading.With each cycle of loading, an expanding fatigue crack frequently leaves striations on particular areas of the fracture surface [2].Fatigue damage holds a dominant status as a life-limiting issue for most structural components subjected to varying stress in service situations [3].Defects arise in structural components during the manufacturing, fabrication, assembly, repair, and maintenance stages.Fatigue is predicted to account for at least half of all mechanical failures [2].A bolt fatigue failure caused by repeated unidirectional bending is illustrated in Figure 1.The failure began at the thread root at A, spread throughout the cross-section as indicated by beach markings at B, and ended in the final fracture part as shown by C [4].Crack spreading with a constant-amplitude load occurs very rarely in real applications for cyclic structures.To describe the rate of fracture propagation under conditions of constant-amplitude loading, a number of crack propagation models have been created, including the Paris law and the Forman/Mettu crack growth equation [5].Variable-amplitude loading frequently results in load sequence effects compared to constant-amplitude loading, which may accelerate, retard, or stop crack propagation [6].Small fatigue cracking is also a cause of crack growth [7].In addition to the fact that the propagation of small fatigue fractures consumes a significant percentage of the overall fatigue life, the behavior of small fatigue cracks is crucial because it determines which fatigue regimes are safe and which are potentially dangerous.The probability of small cracks being elastic-plastic, as opposed to linear elastic, is greater due to the significantly high ratio of fatigue strength to yield strength.Thus, the ratio between the length of the plastic zone and the fracture length increases [8].
A fullyreversed cyclic axial loading condition is used to primarily examine the fatigue life utilizing cylindrical specimens [9].A considerable amount of research has been devoted to predicting the onset and propagation of fatigue cracks to estimate the approximate number of cycles until specimen failure.Fatigue life has two stages: the initiation phase when a minor fracture first appears, and the propagation phase when the crack expands to a critical size and causes specimen failure.The growth prediction method establishes a correlation between fatigue damage and the number of cycles with respect to fatigue life [10].Figure 2 depicts the progress of damage from the beginning of a crack to eventual failure.The length of each of these stages is affected by a variety of parameters, including the load, surroundings, and stress concentration [11].Crack spreading with a constant-amplitude load occurs very rarely in real applications for cyclic structures.To describe the rate of fracture propagation under conditions of constant-amplitude loading, a number of crack propagation models have been created, including the Paris law and the Forman/Mettu crack growth equation [5].Variable-amplitude loading frequently results in load sequence effects compared to constant-amplitude loading, which may accelerate, retard, or stop crack propagation [6].Small fatigue cracking is also a cause of crack growth [7].In addition to the fact that the propagation of small fatigue fractures consumes a significant percentage of the overall fatigue life, the behavior of small fatigue cracks is crucial because it determines which fatigue regimes are safe and which are potentially dangerous.The probability of small cracks being elastic-plastic, as opposed to linear elastic, is greater due to the significantly high ratio of fatigue strength to yield strength.Thus, the ratio between the length of the plastic zone and the fracture length increases [8].
A fullyreversed cyclic axial loading condition is used to primarily examine the fatigue life utilizing cylindrical specimens [9].A considerable amount of research has been devoted to predicting the onset and propagation of fatigue cracks to estimate the approximate number of cycles until specimen failure.Fatigue life has two stages: the initiation phase when a minor fracture first appears, and the propagation phase when the crack expands to a critical size and causes specimen failure.The growth prediction method establishes a correlation between fatigue damage and the number of cycles with respect to fatigue life [10].Figure 2 depicts the progress of damage from the beginning of a crack to eventual failure.The length of each of these stages is affected by a variety of parameters, including the load, surroundings, and stress concentration [11].
Structural failure caused by fatigue is a prevalent reason for malfunction in various mechanical parts.Understanding the factors that affect the fatigue life of a component is essential to designing reliable and safe structures.This paper discusses some of the key factors that affect the fatigue life of a component [12].

Comprehensive Overview of Fatigue Analysis
In the realm of engineering, fatigue analysis emerges as an essential discipline for ensuring the reliability and safety of numerous structures and components exposed to cyclic loading.The consequences of fatigue failure are severe, encompassing financial setbacks, infrastructure deterioration, and potential harm to individuals or loss of life.Hence, fatigue analysis assumes paramount importance in safeguarding the longevity and structural integrity of diverse engineering components and structures.Fundamental ideas regulating the behavior of materials under cyclic loading are at the core of fatigue analysis.The S-N curve, fatigue life, fatigue crack initiation and propagation, and stress concentration constitute major roles in fatigue analysis.Differences in microstructure, composition, loading conditions, and environmental factors all influence the fatigue characteristics of materials.The metals mainly link to the microstructural features, including grain boundaries, defects, and metallurgical phases.In the present scenario, fatigue analysis is character-ized by analytical and experimental methods like finite element analysis, strain life and stress life tests, rotary bending tests, non-destructive testing such as ultrasonic testing, and magnetic particle inspection that monitors fatigue damage.Fatigue analysis is crucial for enhancing engineering systems' safety, reliability, and longevity amidst challenges posed by cyclic loading.It achieves this by advancing our comprehension of fatigue mechanisms, developing predictive models, and implementing effective mitigation strategies.
Technologies 2024, 12, x FOR PEER REVIEW 3 Figure 2. Stages of failure in terms of crack length versus time/cycles of service [11].
Structural failure caused by fatigue is a prevalent reason for malfunction in va mechanical parts.Understanding the factors that affect the fatigue life of a compone essential to designing reliable and safe structures.This paper discusses some of the factors that affect the fatigue life of a component [12].

Comprehensive Overview of Fatigue Analysis
In the realm of engineering, fatigue analysis emerges as an essential disciplin ensuring the reliability and safety of numerous structures and components expose cyclic loading.The consequences of fatigue failure are severe, encompassing fina setbacks, infrastructure deterioration, and potential harm to individuals or loss of Hence, fatigue analysis assumes paramount importance in safeguarding the long and structural integrity of diverse engineering components and structures.Fundam ideas regulating the behavior of materials under cyclic loading are at the core of fa analysis.The S-N curve, fatigue life, fatigue crack initiation and propagation, and s concentration constitute major roles in fatigue analysis.Differences in microstruc composition, loading conditions, and environmental factors all influence the fa characteristics of materials.The metals mainly link to the microstructural features cluding grain boundaries, defects, and metallurgical phases.In the present scenario tigue analysis is characterized by analytical and experimental methods like finite elem analysis, strain life and stress life tests, rotary bending tests, non-destructive testing as ultrasonic testing, and magnetic particle inspection that monitors fatigue damage tigue analysis is crucial for enhancing engineering systems' safety, reliability, and gevity amidst challenges posed by cyclic loading.It achieves this by advancing comprehension of fatigue mechanisms, developing predictive models, and implemen effective mitigation strategies.
In this paper, an extensive review of fatigue life analysis of mechanical and s tural components has been presented.Particular emphasis will be given to the effec In this paper, an extensive review of fatigue life analysis of mechanical and structural components has been presented.Particular emphasis will be given to the effects of temperature, residual stress, hardness, hardfacing, and different mechanical properties.This paper also discusses crack initiation and propagation that lead to the failure of components.The subsequent sections of the article are organized as follows.In Section 1, an introduction to fatigue life and a comprehensive overview of fatigue analysis are presented.Section 2 concerns problems related to fatigue.Section 3 emphasizes the effect of different parameters on fatigue life.Section 4 presents the effect of mechanical properties on the fatigue life of structural components.Section 5 presents the evaluation and development of fatigue life from the early 1990s to 2024.Section 6 delves into recent research focal points and prospective future development in fatigue analysis, while Section 7 provides a summary of conclusions.

Problems Related to Fatigue
Failures caused by fatigue can lead to significant consequences, ranging from minor malfunctions to devastating accidents [2].According to certain authors, two distinct types of materials are identified: the first type is fatigue cracks that initiate from the surface due to slip bands across the entire fatigue range and lack inclusions or internal imperfections, while the second type demonstrates fatigue behavior in the very highcycle fatigue regime characterized by internal crack initiations induced by any form of volume imperfections [13].Metallurgical flaws are introduced during manufacturing operations such as forging, machining, cladding, and heat treatment.Micro cracks are mainly induced and propagated via cyclic loading, which leads to failure.Material flaws such as inclusions, voids, and porosities act as starting points for fatigue cracks to develop.In aluminum alloys, it is widely recognized that fatigue cracks predominantly originate from inclusions [4,6].High and variable temperatures are also a reason for material flaws.At high temperatures, AA6061 is not preferable for automobile components.Wear loss is high at low temperatures due to low contact stresses [14].The surface condition significantly influences the fatigue life of parts.Elevated surface roughness results in the formation of intermittent small gaps, leading to stress concentration and consequently shortening fatigue life [15,16].High-stress concentrations such as notches, fillets, and sharp corners are also prone to fatigue failure.Residual stresses created during manufacturing processes accelerate the beginning and propagation of fatigue cracks.Residual stresses introduce complex stress states in materials, which can lead to unpredictable fatigue behavior.Stress corrosion cracking and hydrogen embrittlement exemplify environmentally assisted cracking mechanisms that can be exacerbated by residual tensile stresses.These mechanisms can lead to diminished fatigue life and accelerate fatigue crack propagation, particularly in severe environments [17][18][19][20].The interaction between applied stresses and residual stresses can result in stress concentrations, multiaxial loading conditions, and non-uniform stress distributions, making fatigue life prediction challenging.Hardfacing has both positive and negative effects on fatigue life [15,21].Significant residual stresses are often imparted onto the component during the application of hardfacing materials, such as through thermal spraying or welding [22].These residual stresses can act as potential sites for the initiation and propagation of cracks, thereby reducing the fatigue life of the component.Stress concentration sites can emerge at the interface between the hardfacing layer and the underlying material.These localized areas of elevated stress, stemming from the stress concentration, heighten the component's vulnerability to the initiation and propagation of fatigue cracks [23][24][25][26].An uneven distribution of carbon in the parent structure during the carburization of steel can result in the hardening of its surface and the development of small cracks [7,27].Failures in shafts almost always start on the surface, usually at locations where mechanical or metallurgical stress concentrations increase local strains [28,29].The aforementioned factors are primary contributors, but there are numerous others that can also diminish the fatigue life and lead to component failure.

Effect of Temperature
In general, when temperature rises, a material's fatigue life is reduced [23].Various metallic components in the shape of cylinders, such as pressure vessels and pipes, which are utilized in the construction of aircraft, are exposed to temperatures ranging from −60 • C (213 • K) to 250 • C (523 • K).Due to these temperatures, it is essential to examine the impact of fatigue on surface cracks under diverse climatic conditions, particularly in specific technical applications.
The impact of temperature on the fatigue life behavior of the aluminum alloy AA 6061 was investigated using an analytical technique [30].Temperature had a substantial influence on the number of cycles until failure in fatigue life research at high temperatures.The aluminum alloy AA6061 is beneficial in circumstances with high ambient temperatures due to its lower weight, excellent mechanical properties, and improved corrosion resistance.When fatigue life was compared at 300 • C to that at ambient temperature, the number of cycles until failure decreased by up to 99%.The reduction was primarily caused by the acceleration of oxidation at high temperatures and the deterioration of the mechanical properties with increasing temperatures.As a result, the aluminum alloy AA6061 cannot be utilized for high-temperature applications because of the significant reduction in cycles until failure rendering it unsuitable for use in engine parts in automobiles.Therefore, this research confirms that the use of AA6061 in high-temperature conditions should be avoided [14].
The influence of temperature on the fatigue life of materials in nuclear reactor main bolts was investigated.The Ni-Cr-Mo-V alloy is used as an experimental material for the main bolt of the pressure vessel in a pressurized water reactor.The range of stress during high temperatures had a significant impact on the bolt's fatigue life.There was a clear temperature effect, and it was evident that the fatigue life of the bolt material rapidly decreased with a constant temperature rise.When a fatigue specimen's temperature is elevated from room temperature to 200 • C, the material's fatigue life decreases significantly.However, the decrease in the material's fatigue life is only marginal when the temperature is raised from 200 • C to 360 • C. At an ambient temperature, the fatigue limit of the smooth specimen is 845.0MPa, which decreases to 790.0 MPa and 770.0 MPa when the temperature is raised to 200 • C and 360 • C, respectively [24].When the samples of Alloy 617 were evaluated at 25 • C, 800 • C, and 850 • C, distinct cyclic hardness, saturation, and softening were seen.The samples underwent up to 100 cycles of hardening before continuously softening at a temperature of 25 • C. Due to decreased strain, consistent cyclic hardening was seen for the majority of cycles at 800 • C. In a few initial cycles at 850 • C, there was significant cyclic hardening.From the first cycle at 900 • C, the specimens become softer.At 950 • C, there was a similar cyclic softening behavior, with the exception of an abrupt decrease in the magnitudes of the maximum and minimum stresses observed during the initial cycles.At high temperatures, the material became more brittle, which is why the material showed softening between 800 and 950 • C. The specimens that were tested at 25 • C, 800 • C, and 850 • C underwent cyclic hardening, whereas those that were examined above 900 • C underwent cyclic softening from the first cycle, meaning that their fatigue life was shortened at high temperatures as a result of a loss of strength.The fatigue life is much longer at 25 • C than it is between 800 and 950 • C.This occurs due to a loss of strength at high temperatures.It is interesting to note that in the 800-950 • C temperature range, the fatigue life is not significantly impacted by temperature [25].An analytical approach was employed to investigate how temperature influences the fatigue behavior of the aluminum alloy AA6061.The fatigue life analysis conducted at elevated temperatures revealed a significant impact of temperature on the number of cycles until failure.Due to its lighter weight, superior mechanical properties, and enhanced corrosion resistance, aluminum alloy AA6061 proves to be a valuable material in applications with ambient temperature conditions [31].When comparing the fatigue life at 300 • C to that at an ambient temperature, a substantial 99% decrease in the number of cycles until failure was observed.Consequently, the use of aluminum alloy AA6061 in high-temperature environments is not advisable due to this notable reduction in the number of cycles until failure.In high-temperature conditions, most moving components within an automobile engine are susceptible to fatigue.Therefore, the findings of this study underscore the inadvisability of using aluminum alloy AA6061 for automotive engine parts exposed to high temperatures [26,31].
Fatigue tests were carried out on specimens composed of two different types of aluminum wrought alloy, namely AA6061-T6 and AA7075-T6 [30].The ASTM E466-07 guidelines were followed to determine the dimensions of the dumbbell-shaped specimens, which were machined from solid wrought bars.In total, 38 specimens were subjected to fatigue testing, as shown in Figure 3.For both aluminum alloys, the loading sequence from hightolow and the constant-amplitude loading (CAL) resulted in the lowest number of cycles until failure [32], whereas the low-to-high loading sequence yielded the highest number of cycles.Under the low-to-high loading sequence, the number of cycles for AA6061 was 56% greater than that for CAL, while the difference between these loading sequences was 84% for AA7075.This observed difference can be attributed to the distinct properties of the two alloys, suggesting that AA7075 experienced loading sequences with greater intensity compared to AA6061. Figure 4a,b depicts the influence of elevated temperatures on the fatigue life for each type of loading sequence.It is worth noting that, as temperature increased, the number of cycles until failure for both alloys decreased exponentially [33].Previous authors investigated the stress-life methodology to predict the fatigue life of aluminum alloy wheels utilizing simulation techniques.Their investigations revealed that at a temperature of 250 • C, the AA6110 aluminum alloy experiences a significant 96% de-crease in fatigue life [30].Similarly, the AA6061 aluminum alloy has been found to show an 80% reduction in fatigue life under the same elevated-temperature conditions [33,34].When fatigue occurs at higher temperatures, it results in substantial strain deformation, facilitates the initiation of cracks, and accelerates the rate at which cracks propagate.At elevated temperatures, crack initiation occurs at an earlier stage, and the rates of crack growth are markedly higher when compared to what is observed at standard ambient temperatures [26,30].
enced loading sequences with greater intensity compared to AA6061. Figure 4a,b depicts the influence of elevated temperatures on the fatigue life for each type of loading sequence.It is worth noting that, as temperature increased, the number of cycles until failure for both alloys decreased exponentially [33].Previous authors investigated the stress-life methodology to predict the fatigue life of aluminum alloy wheels utilizing simulation techniques.Their investigations revealed that at a temperature of 250 °C, the AA6110 aluminum alloy experiences a significant 96% decrease in fatigue life [30].Similarly, the AA6061 aluminum alloy has been found to show an 80% reduction in fatigue life under the same elevated-temperature conditions [33,34].When fatigue occurs at higher temperatures, it results in substantial strain deformation, facilitates the initiation of cracks, and accelerates the rate at which cracks propagate.At elevated temperatures, crack initiation occurs at an earlier stage, and the rates of crack growth are markedly higher when compared to what is observed at standard ambient temperatures [26,30].The deformation characteristics and dislocation behaviors of metal alloys are simultaneously influenced by temperature and strain rate.Investigations into the effect of temperature on cyclic stress-strain rates were conducted on copper and 304 stainless steel.These studies found that tests at high strain rates remained unaffected by temperature.However, the mechanism of the time-dependent fracture was predominantly observed at high temperatures and low strain rates.In this experiment, strain rates ranged from 2 × 10 −2 to 4 × 10 −1 per second, while temperatures varied from −75 °C to 760 °C.The stress responses of both stainless-steel and copper specimens decreased with increases in The deformation characteristics and dislocation behaviors of metal alloys are simultaneously influenced by temperature and strain rate.Investigations into the effect of temperature on cyclic stress-strain rates were conducted on copper and 304 stainless steel.These studies found that tests at high strain rates remained unaffected by temperature.However, the mechanism of the time-dependent fracture was predominantly observed at high temperatures and low strain rates.In this experiment, strain rates ranged from 2 × 10 −2 to 4 × 10 −1 per second, while temperatures varied from −75 • C to 760 • C. The stress responses of both stainless-steel and copper specimens decreased with increases in temperature, as illustrated in Figure 5.Moreover, the material exhibited increased strain rate sensitivity with rising temperatures.In the testing environment, the monotonic flow stress and strain hardening exponent decreased with the elevation of the ambient temperature.Consequently, at high temperatures, this led to a narrow stress-strain curve with a minimal slope.Notably, there exists a negative linear relationship between the strain hardening exponent and temperature in face-centered cubic (FCC) metals [17].K. Tahmasbi et al. created fatigue specimens using rotary friction welding (RFW) at various rotational speeds.The temperature dynamics were investigated using RFW experiments on dissimilar polymer rods, and the outcomes were compared to simulations conducted using ANSYS Workbench 2023 software.The experimental setup for fatigue testing is depicted in Figure 6, where a rotating-beam fatigue test was employed to conduct numerous tests on welded components.The results revealed three key phenomena: (a) The simulation results closely mirrored the experimental outcomes of rotary friction welding across six different rotational speeds.(b)Discrepancies between the software-predicted weld interface heating rates and experimental results ranged from approximately 3.7% to 9.3%, averaging around 4.48%.(c)Similarly, discrepancies in the simulation results for the highest temperature at the weld interface compared to experimental data ranged from roughly 0.77% to 6.5%, averaging approximately 3.16%.The fatigue life exhibited an improvement of nearly 1.4 times.In conclusion, it is suggested that domain knowledge is utilized for dissimilar polymer rods fused using a computer numerical control turning machine with variable speed rotation [18].K. Tahmasbi et al. created fatigue specimens using rotary friction welding (RFW) at various rotational speeds.The temperature dynamics were investigated using RFW experiments on dissimilar polymer rods, and the outcomes were compared to simulations conducted using ANSYS Workbench 2023 software.The experimental setup for fatigue testing is depicted in Figure 6, where a rotating-beam fatigue test was employed to conduct numerous tests on welded components.The results revealed three key phenomena: (a) The simulation results closely mirrored the experimental outcomes of rotary friction welding across six different rotational speeds.(b) Discrepancies between the software-predicted weld interface heating rates and experimental results ranged from approximately 3.7% to 9.3%, averaging around 4.48%.(c) Similarly, discrepancies in the simulation results for the highest temperature at the weld interface compared to experimental data ranged from roughly 0.77% to 6.5%, averaging approximately 3.16%.The fatigue life exhibited an improvement of nearly 1.4 times.In conclusion, it is suggested that domain knowledge is utilized for dissimilar polymer rods fused using a computer numerical control turning machine with variable speed rotation [18].The present work may be limited to a specific temperature range, and extrapolating the findings to other temperatures could be challenging.Table 1 shows the limitations of the present work and recommendations for future work.Al alloy should not be used for high-temperature applications. 3 The Ni-Cr-Mo-V alloy bolt's fatigue life is reduced at the constant rise in temperature.
Ni-Cr alloy bolts and components are not able to resist elevated temperatures.
This type of alloy can be useful for uniform-temperature or low-temperature ranges.

4
Only marginal decrement in fatigue life and stress of Ni-Cr alloy, between 200-360 °C The small size of the sample tested for a short duration, which does not represent real-world applications.
Ni-Cr alloy can be used for soft components in a lower temperature range.

Lack of long-term exposure and simplified loading conditions
Studies are typically conducted for a short duration, but in real life, materials can go through repeated stress for a long time, and this study is not accurate for long durations.
High-strength alloys should be used and tested under real-world conditions in experiments.

Effect of Residual Stresses
Residual stresses are internal stresses that remain in a material even after the external loads are removed.These stresses can arise from a variety of sources, such as manufacturing processes, welding, or thermal treatment.Residual stresses can have a significant effect on the fatigue life of components, as they can either increase or decrease the component's resistance to cyclic loading [19].
Residual stresses are present in nearly all mechanical parts.Several aspects that lead to fatigue failure should be included in an effective fatigue forecast.One of the elements that should be taken into account in the forecasting of fatigue is residual stress.However, one of the main factors contributing to residual stresses being introduced into the structural componentsis the manufacturing process [20].Investigations have been performed The present work may be limited to a specific temperature range, and extrapolating the findings to other temperatures could be challenging.Table 1 shows the limitations of the present work and recommendations for future work.Mechanical properties deteriorate at elevated temperatures.
Al alloy should not be used for high-temperature applications. 3 The Ni-Cr-Mo-V alloy bolt's fatigue life is reduced at the constant rise in temperature.
Ni-Cr alloy bolts and components are not able to resist elevated temperatures.
This type of alloy can be useful for uniform-temperature or low-temperature ranges.

4
Only marginal decrement in fatigue life and stress of Ni-Cr alloy, between 200-360 • C The small size of the sample tested for a short duration, which does not represent real-world applications.
Ni-Cr alloy can be used for soft components in a lower temperature range.

5
Lack of long-term exposure and simplified loading conditions Studies are typically conducted for a short duration, but in real life, materials can go through repeated stress for a long time, and this study is not accurate for long durations.
High-strength alloys should be used and tested under real-world conditions in experiments.

Effect of Residual Stresses
Residual stresses are internal stresses that remain in a material even after the external loads are removed.These stresses can arise from a variety of sources, such as manufacturing processes, welding, or thermal treatment.Residual stresses can have a significant effect on the fatigue life of components, as they can either increase or decrease the component's resistance to cyclic loading [19].
Residual stresses are present in nearly all mechanical parts.Several aspects that lead to fatigue failure should be included in an effective fatigue forecast.One of the elements that should be taken into account in the forecasting of fatigue is residual stress.However, one of the main factors contributing to residual stresses being introduced into the structural componentsis the manufacturing process [20].Investigations have been performed regarding the effects of the manufacturing process on Al 7075.An analysis of the induced residual stress from three different machining cases and one un-machined case has been performed using the layer-removal milling method.Residual stresses were affected by the different parameters of machining such as the feed rate and cutting speed.In all three cases, there was a significant surface compressive stress that occurred within 0.05 mm of the surface.Case 1 had the largest residual stress, whereas the unmachined case had the lowest.A reduction in the compressive residual surface stress was found in cases 1 to 3. The residual stress for cases 1, 2, and 3 were 46 MPa, 16 MPa, and 8 MPa, respectively.The reason for this is that while the cutting speed increases from 251 to 375 to 500 m/min, the feed rate is reduced from 0.3 to 0.25 to 0.2 mm/rev.A material's surface residual stress is reduced by increasing the cutting speed, while it is enhanced by increasing the feed per tooth.The low-cycle-regime fatigue life is improved by machining-induced residual stresses [15].
The impact of residual stress on the fatigue life of AISI 52100 (60-62 HRC) hard-turned steel has been investigated.There were five distinct types of fatigue specimens developed, including ground surfaces with and without super finishes, hard-turned surfaces with and without white layers, and hard-turned surfaces with super finishes.The compressive residual stress of ground specimens has its maximum at the surface and then slopes sharply downwards as it becomes less compressive.Conversely, it was observed that all surfaces that underwent hard turning showed peak compressive residual stresses at a depth of 10 to 20 µm from the surface, which was subsequently followed by a gradual decrease in the magnitude of the compressive stresses.In both cases, super finishing serves to maintain the original profile beyond a depth of 20 µm, while also improving the compressive nature of the residual stress within the top 10-20 µm of the surface.The researcher asserted that the hard-turned specimen had a fatigue life of more than 56,000 cycles, compared to 27,360 cycles for the ground surface.The distribution of individual stress had the biggest impact on fatigue life.It was found that the maximum compressive residual stress and the surface compressive residual stress had a direct correlation with the specimen's fatigue life.The hard-turned specimens' fatigue life was consistently at least as good as that of the baseline ground specimens [21].
To gain a better understanding of how laser shock peening (LSP) impacts the distribution of residual stress and variations in surface roughness, researchers examined the high-cycle fatigue properties of a nickel aluminum bronze (NAB) alloy.Upon application of the laser shock wave, the residual stress on the NAB surface changed from tensile to compressive.Moreover, with an increase in laser pulse energy, both the depth of the residual compressive stress and its dispersion increased, which could be attributed to the work hardening of the material.The LSP process resulted in surface hardening of the material and reduced the attenuation rate of subsequent pressure pulses.
Optimizing the laser pulse energy parameters can enhance the distribution of residual compressive stress on the surface of marine equipment components, thereby lowering the potential for stress concentration failure and increasing fatigue life [35].
The progression of residual stress under fatigue loading at room temperature was investigated.The beneficial effects of compressive residual stress diminished due to the relaxation of these stresses during fatigue loading [36].The extent of cyclic residual stress relaxation mainly depended on the number of cycles and the stress levels [37,38].In the investigation of the LSP ATI 718Plus alloy, the author identified three distinct levels of relaxation in compressive residual stress [39].It is worth noting that the initial compressive residual stresses experienced significant relaxation during the initial cycles [38,40], as observed at various points in the study.Figure 7 demonstrates a slight decrease in residual stress after 10 to 10,000 cycles, primarily attributed to microplastic deformation.Interestingly, when the number of cycles nears the material's failure point, more substantial stress relaxation occurs [41].Luan s. et al. measured residual stress (RS) along with fatigue crack growth (FCG) on heat-treated and welded specimens.Two types of specimens were selected for RS distribution with FCG, with gradually decreasing distances between the notch tip and the weld centerline.The parent material was 10 mm thick Q345B steel with ER50-G as the weld material.Welding was performed using a tungsten inert gas process on two plates.To eliminate RS from the weld joint, a box-type resistance furnace (SX-4-10) was used for heat treatment, ranging from room temperature to 600 °C.The distribution of RS primarily depends on geometric constraints during FCG, with the RS distribution calculated based on the distance of the weld from the centerline.During fatigue, compressive strain remains consistent away from the weld material as long as the tensile RS is constant.Fatigue-induced redistribution of RS leads to an increase in compressive RS near the fracture tip.At the onset of FCG, there is no fatigue retardation or crack closure when the crack length is zero.As FCG progresses, the length of the contacted crack wake length (Wp) increases, leading to a reduction in the FCG rate due to the presence of compressive RS.For a long crack, this implies that as the crack enlarges due to rising RS, crack wake length increases while the rate of FCG decreases accordingly, and conversely [42].This study investigated how different laser shock peening (LSP) patterns affect the fatigue life of TC4 specimens containing notches.The research demonstrated that LSP induces a compressive residual stress field in components, effectively halting the initiation and propagation of fatigue cracks.The effectiveness of LSP in enhancing fatigue properties depends on factors such as laser impact properties and treatment patterns [43].
The research explored how laser peening-induced compressive residual stress affects the fatigue strength of AA7075 specimens.The study employed rotary bending fatigue tests and sequential polishing to analyze residual stress in shot-peened (SP), laser-peened (LP), and untreated samples.Notched fatigue specimens, as shown in Figure 2, were used for testing.At a stress level of 204 MPa, untreated specimens failed after 2.3 × 10 4 cycles, whereas SP and LP specimens endured for 9.9 × 10 4 and 4.4 × 10 5 cycles, respectively.LP-treated specimens showed a fatigue life 19 times longer than untreated ones, while SP-treated specimens demonstrated a 4.3-fold improvement.LP consistently surpassed SP in enhancing fatigue life, attributed to its ability to induce compressive residual stress in deeper regions.Particularly, specimens with low-stress concentrations (~1.4) and deep high-load stress areas benefited more from LP treatment due to its effectiveness in penetrating deeper layers.This suggests LP treatment's potential to enhance fatigue strength, particularly in thicker materials, by establishing compressive residual stress in deeper regions compared to SP treatment [44].Luan s. et al. measured residual stress (RS) along with fatigue crack growth (FCG) on heat-treated and welded specimens.Two types of specimens were selected for RS distribution with FCG, with gradually decreasing distances between the notch tip and the weld centerline.The parent material was 10 mm thick Q345B steel with ER50-G as the weld material.Welding was performed using a tungsten inert gas process on two plates.To eliminate RS from the weld joint, a box-type resistance furnace (SX-4-10) was used for heat treatment, ranging from room temperature to 600 • C. The distribution of RS primarily depends on geometric constraints during FCG, with the RS distribution calculated based on the distance of the weld from the centerline.During fatigue, compressive strain remains consistent away from the weld material as long as the tensile RS is constant.Fatigueinduced redistribution of RS leads to an increase in compressive RS near the fracture tip.At the onset of FCG, there is no fatigue retardation or crack closure when the crack length is zero.As FCG progresses, the length of the contacted crack wake length (Wp) increases, leading to a reduction in the FCG rate due to the presence of compressive RS.For a long crack, this implies that as the crack enlarges due to rising RS, crack wake length increases while the rate of FCG decreases accordingly, and conversely [42].This study investigated how different laser shock peening (LSP) patterns affect the fatigue life of TC4 specimens containing notches.The research demonstrated that LSP induces a compressive residual stress field in components, effectively halting the initiation and propagation of fatigue cracks.The effectiveness of LSP in enhancing fatigue properties depends on factors such as laser impact properties and treatment patterns [43].
The research explored how laser peening-induced compressive residual stress affects the fatigue strength of AA7075 specimens.The study employed rotary bending fatigue tests and sequential polishing to analyze residual stress in shot-peened (SP), laser-peened (LP), and untreated samples.Notched fatigue specimens, as shown in Figure 2, were used for testing.At a stress level of 204 MPa, untreated specimens failed after 2.3 × 10 4 cycles, whereas SP and LP specimens endured for 9.9 × 10 4 and 4.4 × 10 5 cycles, respectively.LP-treated specimens showed a fatigue life 19 times longer than untreated ones, while SP-treated specimens demonstrated a 4.3-fold improvement.LP consistently surpassed SP in enhancing fatigue life, attributed to its ability to induce compressive residual stress in deeper regions.Particularly, specimens with low-stress concentrations (~1.4) and deep high-load stress areas benefited more from LP treatment due to its effectiveness in penetrating deeper layers.This suggests LP treatment's potential to enhance fatigue strength, particularly in thicker materials, by establishing compressive residual stress in deeper regions compared to SP treatment [44].
The stress concentration in corroded fillet and butt-welded specimens was analyzed numerically using real 3D solid models.Corrosion in steel constructions diminishes the fatigue strength in affected areas, exacerbating the stress concentration and inducing material embrittlement.The presence of residual stresses in the fatigue region of welded connections could be mitigated to some extent by employing surface preparation techniques such as clean blasting, as addressed in this study.For both butt and fillet welds, the real geometry was accurately represented through reverse engineering of 3D solid models.During fatigue testing, digital measurements were used to identify crack initiation locations, which closely corresponded to those predicted numerically in most cases.Furthermore, the study demonstrates that employing local approaches can significantly reduce scatter in SN curves by accounting for real geometry and residual stresses, highlighting the method's high reliability [45].
Mikihito H et al. mitigated the residual stresses and improved the fatigue life of steel structure elements.A series of experiments utilized local induction heating to achieve these objectives.Induction heating was applied to improve the fatigue life and mitigate tensile residual stresses around box-welded joints.The efficacy of stress reduction through local heating was verified via residual stress measurements, supported by numerical simulations elucidating the stress mitigation mechanism.Base plates were fabricated using SM400A material, while gusset plates employed G3106 material.Three heating sequences were utilized, targeting a maximum heating temperature of 350 • C for 40 s.Experiments were conducted with and without local heating specimens to evaluate its impact on residual stress.The results demonstrated that local heating substantially reduced residual stresses under both tensile and compressive loading conditions at the weld toe.This stress reduction contributed to the enhanced fatigue performance of the welded joints, primarily influenced by the loading conditions [46].
Table 2 shows the quantitative analysis of the fatigue life cycle at different stress amplitudes.High values of residual stress decreased the fatigue life compared to lower stress values.Residual stresses can have both beneficial and detrimental effects on fatigue life, depending on their magnitude, distribution, and orientation relative to the applied cyclic loading.Some key points regarding the effect of residual stresses on fatigue life, along with the limitations of the present work, are shown in Table 3.

S.No. Present Work Limitations Recommendations
1.
Al 7075 unmachined surfaces have significant compressive stress at lower cutting speeds.Machined surfaces have a higher fatigue life as compared to un-machined surfaces.
Un-machined samples may not be useful for real-world applications.It is typical to maintain a high cutting speed to lower the residual stresses.
High cutting speeds and a lower feed rate are required to overcome the negative effects of residual stresses.

2.
In low-cycle fatigue and high-cycle fatigue, shot peening has different impacts.Critical residual stress is the dominating variable in high-cycle fatigue, whereas roughness is the dominant variable in low-cycle fatigue.
Due to tensile residual stresses, fracture initiation occurs after shot peening.
Nickel-aluminium-bronze alloy can be used for laser shock peening applications because the tensile stresses are converted into compressive stresses after laser shock peening treatment.

3.
Hard-turned steel has a longer fatigue life as compared to ground surface or non-hard-turned surface steel.
A heat treatment process is required for hard-turned surfaces.
Instead of AlSI alloy, SS alloy can be used without heat treatment.

4.
Residual stresses can undergo redistribution during cyclic loading, particularly in the presence of plastic deformation.
Redistribution can influence crack growth behavior and alter fatigue life predictions.
Proper heat treatment and cooling processes can overcome the tensile residual stresses in the manufacturing process.

5.
The present work is only for specific materials and simplified loading conditions.
Simplified and constant loading conditions may not be useful for real-world applications.
It would be valuable to investigate the effect of residual stresses under more realistic loading conditions with material diversity.

Effect of Hardness
Hardness, the capacity of a substance to resist deformation, is measured using a common test that measures the surface resistance to indentation.The most popular hardness tests can be categorized based on the size, shape, and force required to generate the indent.The hardness of the material and resistance to plastic deformation are the two elements that influence fatigue life.Due to a natural drop in material strength, as material hardness declines, fatigue life is also reduced.However, contact stress and resistance to plastic deformation also decrease at the same time [47].
Axles for trains have frequently been made using EA4T steel [48].In addition to other methods of problem-solving, the author took into account the failure behavior of railway axles.In order to repair train wheels, laser cladding remanufacturing was employed.The micro-hardness of EA4T steel subsequent to laser cladding was assessed using an HVS-1000 Vickers Hardness Tester, which applied a force of 1.96 N for a duration of 20 s.The microhardness test was performed in three locations: the cladding layer, the transition zone, and the substrate.Cladding layers have higher microhardness than the substrate and the heat-affected zone [49].Elastic tension emerges in the cladding layers as a result of the short-range internal stress caused by the disparity in the elastic moduli of the solute atoms and the unequal distribution of solute atoms caused by non-equilibrium solidification during the laser cladding process.Atoms in solvents slow down boundary and dislocation motion.The cladding layers have microhardness values ranging from 360 to 380 HV, whereas the substrate has an average microhardness of 260 HV.The process of laser cladding causes thermal cycling between the bone zone and the heat-affected zone, which results in a microstructure that is super-heated and produces a microhardness value between 275 HV and 360 HV [47,50].
The microhardness of API 5L X65 was measured using Berkovich indentation for both annealed and as-received specimens, and it was found to change during the duration of fatigue life.The findings demonstrated that although specimens in their as-received state would first soften and then harden, annealed specimens would do the opposite.The importance of the initial material state, as in the dislocation structure, was brought to light by this.The results also show that the change is undeniably more noticeable on the surface.Indentation depths of 2, 4, and 6 µm were evaluated, and the data from the 2 µm test revealed the most significant decrease in hardness [51].
Other authors also investigated the impact of adding different alloy elements on the hardness of a nickel-based hardfacing alloy [52] and their effect on the deposited layer's wear resistance.The five varieties of nickel hardfacing alloys include carbide, boron, silicide, intermetallic, and solid solution, with silicide and boron being the most commonly utilized types.The addition of niobium, chromium, and molybdenum to the flux can increase both the microstructure and hardness of the deposited layer.Initially, the deposited layer's hardness shows an increase, but it subsequently decreases upon the addition of alloying elements and carbon content [53].Although there are other factors that affect a material's ability to withstand wear, hardness unquestionably has an impact.Carbon can be added to materials to increase hardness, which is greatly desired.Although carbon increases brittleness, it can also be combined with another alloy to generate a high-hardness carbide that protects against abrasive wear.Yet, it can also produce strong solution strength.The addition of carbon is, therefore, a very effective strategy in conditions of consistent wear with little influence.The carbon, silicon, and boron levels will decrease as the niobium percentage rises, lowering the hardness of the deposited layers in the process.When the aforementioned alloy elements are simultaneously added to carbon, the hardness of the deposited layer has a tendency to first rise and then fall as the alloy element is increased.Higher hardness will reduce wear loss and increase the fatigue life of the hardfacing alloy [54].
In order to examine the microhardness of AISI 4340 steel, a micro-hardness tester (LECOLM700AT) was used, and AerMet 100 steel powder was clad onto a grind-out portion with a 2.5 kW ND:YAG laser.Hardness was tested in various zones, including the laser-clad zone, heat-added zone (HAZ), and substrate zone.The clad zone exhibited a hardness of approximately 650 Hv (Vickers hardness), which is 30-40% greater than the substrate material (580 Hv), owing to the formation of hard and brittle martensite during rapid cooling [55][56][57].Similarly, the hardness of the heat-affected zone (HAZ) increased from 600 Hv to 720 Hv due to rapid self-quenching.The substrate zone was found to have a lower hardness than the clad and HAZ zones, and the over-tempered zone, the region around the substrate in welding operations, had a lower hardness due to softening caused by carbon atom diffusion from martensite in the substrate [58].The hardness of the over-tempered zone was slightly lower than that of the substrate zone due to overheating.The as-clad hardness of AerMet 100 (560-580 Hv) was softer than the as-clad hardness of AISI 4340 (20% difference) due to compositional differences, particularly the decreased carbon content.When compared to AISI 4340, AerMet 100 exhibited a substantial increase in fatigue life.However, the overly hard and brittle nature of the clad and HAZ sections decreased the fatigue life of AISI 4340.To avoid overheating, it is recommended to reduce the heat input and increase substrate thickness [59].
Ye et al. conducted research on hardness that evolves in response to fatigue damage [60,61].They employed Vickers indentation to assess microhardness levels and noted that the average microhardness values for both ferrite and pearlite exhibited variations throughout the fatigue life.Specifically, both phases displayed an initial increase in hardness, followed by a period of stabilization, and ultimately a decrease leading to failure, as illustrated in Figure 8 [54], which encompasses the entire range of data points.Furthermore, in their research, Ye and Wang [62] asserted that hardness measurements inherently possess stochastic characteristics, implying that the damage variable should be regarded as a probabilistic function.Consequently, they put forth the idea of representing the damage variable as a probabilistic function and modified the normal distribution function to depict the probabilistic accumulation of damage over the course of fatigue life.Berkovich indentation was employed to investigate the microhardness evolution in API 5L X65 specimens, both in their as-received and annealed states, throughout the fatigue life [63,64].The findings revealed that the annealed specimens initially experienced a hardening effect followed by subsequent softening in the early stages of the fatigue life, whereas the as-received specimens exhibited an initial softening before transitioning to hardening [65].These results underscore the importance of the initial material condition, particularly in terms of the dislocation structure.Furthermore, the tests were conducted at indentation depths of 2, 4, and 6 µm, with the results indicating that the observed changes in hardness were most pronounced at the surface, with the 2 µm measurements displaying the most significant variations [23].
Furthermore, in their research, Ye and Wang [62] asserted that hardness measurements inherently possess stochastic characteristics, implying that the damage variable should be regarded as a probabilistic function.Consequently, they put forth the idea of representing the damage variable as a probabilistic function and modified the normal distribution function to depict the probabilistic accumulation of damage over the course of fatigue life.Berkovich indentation was employed to investigate the microhardness evolution in API 5L X65 specimens, both in their as-received and annealed states, throughout the fatigue life [63,64].The findings revealed that the annealed specimens initially experienced a hardening effect followed by subsequent softening in the early stages of the fatigue life, whereas the as-received specimens exhibited an initial softening before transitioning to hardening [65].These results underscore the importance of the initial material condition, particularly in terms of the dislocation structure.Furthermore, the tests were conducted at indentation depths of 2, 4, and 6 μm, with the results indicating that the observed changes in hardness were most pronounced at the surface, with the 2 μm measurements displaying the most significant variations [23].High-strength steel S690 was utilized to test the hardness of two distinct types of butt-welded connection.These connections consist of CR690 joints, which are formed by joining rolled steel S690 with cast steel G10MnMoV6-3, and VR690 junctions, which were created by connecting rolled steel S690 [28].The material properties for S690 include uniform elongation of 15%, yield strength of 790 MPa, and ultimate strength of 847 MPa.In contrast, G10MnMoV6-3 exhibits consistent elongation of 18.6% and possesses yield and maximum strengths of 743 MPa and 799 MPa, respectively.Hardness measurements were carried out on the cross-section of the weld at three specific locations: the root of the weld (RW), the middle of the weld, and the weld cap, with an applied stress of 9.807 N, following ISO-6507 standards [66].Figure 9 illustrates the positions where hardness measurements were taken, while Figures 10 and 11 show the VR690 and CR690 joints, respectively.Notably, in the case of the weld cap and the middle of the weld, the hardness is highest at the heat-affected zone and lowest at the base materials, although this trend is not observed at the weld root.These findings reveal that, typically, the hardness at the weld root tends to be lower compared to that at the top and center of the weld [67,68].High-strength steel S690 was utilized to test the hardness of two distinct types of buttwelded connection.These connections consist of CR690 joints, which are formed by joining rolled steel S690 with cast steel G10MnMoV6-3, and VR690 junctions, which were created by connecting rolled steel S690 [28].The material properties for S690 include uniform elongation of 15%, yield strength of 790 MPa, and ultimate strength of 847 MPa.In contrast, G10MnMoV6-3 exhibits consistent elongation of 18.6% and possesses yield and maximum strengths of 743 MPa and 799 MPa, respectively.Hardness measurements were carried out on the cross-section of the weld at three specific locations: the root of the weld (RW), the middle of the weld, and the weld cap, with an applied stress of 9.807 N, following ISO-6507 standards [66].Figure 9 illustrates the positions where hardness measurements were taken, while Figures 10 and 11 show the VR690 and CR690 joints, respectively.Notably, in the case of the weld cap and the middle of the weld, the hardness is highest at the heat-affected zone and lowest at the base materials, although this trend is not observed at the weld root.These findings reveal that, typically, the hardness at the weld root tends to be lower compared to that at the top and center of the weld [67,68].
P. Mendes et al. analyzed hardness properties using Vickers hardness testing.The primary objective of their work was to examine the impact of heat input during the final stages on the preceding steps in the tempering heat treatment process.Temper treatment typically induces a reduction in hardness values, underscoring the necessity of microhardness tests in comprehending the evolution of this mechanical property.This phase plays a crucial role in ensuring stringent process quality control, as variations in heat input can significantly influence both microstructural and mechanical properties, potentially rendering the weld unsuitable for industrial applications.To evaluate the microhardness of the welded joint, two distinct stages of the welding process were employed: focusing solely on the root steps and encompassing all welding steps.This methodology facilitated the identification of the point at which the mechanical properties of the heat-affected zone (HAZ) are significantly altered by the heat treatment from tempering.For this study, the EMCO M4U hardness tester was utilized, employing the HV10 Vickers test with a 15 s pressing period and an applied force of 10 kgf (98.07 N).The findings revealed that the HAZ displayed the largest data disparity and the most notable fluctuations in hardness levels, indicative of an inconsistent cooling rate within this region.The slower cooling rate inherent in thicker materials contributed to lower HAZ hardness ratings in thicker joints.Thick materials, owing to their superior heat dissipation capabilities, tend to cool more slowly than their thinner counterparts, potentially resulting in larger grain sizes and lower hardness ratings.Conversely, thinner materials cool more rapidly, yielding higher hardness values and finer grain structures.Consistently, hardness data demonstrated that the weld material zone exhibited higher hardness values than the base material, underscoring the weld's superior quality and reliability [69].ratings in thicker joints.Thick materials, owing to their superior heat dissipation capabilities, tend to cool more slowly than their thinner counterparts, potentially resulting in larger grain sizes and lower hardness ratings.Conversely, thinner materials cool more rapidly, yielding higher hardness values and finer grain structures.Consistently, hardness data demonstrated that the weld material zone exhibited higher hardness values than the base material, underscoring the weld's superior quality and reliability [69].The relationship between hardness and fatigue is complex and depends on various factors.In Table 4, an overview of the effect of hardness on fatigue life is presented, along with limitations and future recommendations for the present work.

1.
EA4T steel has a high hardness with a laser cladding process.
Laser cladding is a typical and costly process in manufacturing.
Instead of the laser cladding process other coating processes like PTAW and GTAW can be utilized.

2.
The use of Niobium, Chromium, Nickel's carbon content decreases the The high amount of carbon The relationship between hardness and fatigue is complex and depends on various factors.In Table 4, an overview of the effect of hardness on fatigue life is presented, along with limitations and future recommendations for the present work.

1.
EA4T steel has a high hardness with a laser cladding process.
Laser cladding is a typical and costly process in manufacturing.
Instead of the laser cladding process other coating processes like PTAW and GTAW can be utilized.

2.
The use of Niobium, Chromium, and Molybdenum with Nickel has a high hardness for electrical applications.
Nickel's carbon content decreases the hardness of the components.
The high amount of carbon content is not recommended with Nickel as it reduces the hardness.

3.
AerMet 100 steel powder was used to clad over the AlSI 4340 steel.AerMet 100 has more hardness than the AlSI 4340 substrate.
The hardness of the AlSI is reduced due to the hard and brittle nature of AlSI in heat added zone It is recommended to reduce heat input and increase substrate thickness.

4.
Load is applied for a short duration for specific materials and idealized geometries Not fully represent real-world applications.Real-world factors such as stress concentrations, surface roughness, and environmental effects can influence the relationship between hardness and fatigue.
Hardness can be increased by applying different coating methods under variable loading conditions.

Effect of Hardfacing
In the metalworking process of hardfacing, a base metal is coated with a tougher or harder substance.In order to reduce wear, a component's surface may be hardfaced via welding [70], thermal spraying [71], or a similar procedure.In order to restore damaged components as well as the original equipment, hardfacing is used.
The production of structures on an AISI 4130 steel substrate using laser cladding involved the use of two different hardfacing alloys: Stellite 6 (Co-based) and Deloro 40G (Ni-based).These structures underwent rotating bending fatigue tests, which revealed that the fatigue life of specimens coated with Stellite 6 and Deloro 40G was negatively correlated with the coating thickness, as tensile residual stress was present in the coating area of the laser-coated specimen.This means that an increase in coating thickness would lead to a decrease in fatigue life.Moreover, the fatigue life of laser-clad AISI 4130 steel specimens of Stellite 6 and Deloro 40G with the same size was lower than that of unclad specimens [72,73].The thermal fatigue behavior of coatings made from Stellite-6 powder and WC particles, produced by laser cladding Co-coated WC (WC-12Co) particles and Stellite-6 powder on AISI H13 hot work tool steel, was studied and compared.Surface cracks were observed in these coatings before the thermal fatigue test [73].This is mostly related to the residual stress imposed by the thermal expansion coefficient mismatch between the Stellite matrix and the WC, as well as the coating cooling quickly during laser cladding.After thermal fatigue tests, the coating's surface showed significantly more cracks as the WC concentration increased.In contrast, less surface cracking was visible with the coatings of WC-12Co particles than with WC.This behavior was particularly found when the WC level was greater than 20 weight percent.The uses of WC-12Co particles increase the lifespan of Stellite-6/WC coatings [74].
Under cyclic 4-point bending loads, the fatigue life of clad Stellite 21 alloy powder [] on X5CrNi18-10 and 42CrMo4 cylindrical substrates was investigated.After grinding, the cladding, which was performed in the center parallel section, still has a thickness of around 1.28 mm.The fatigue strength of both types of clad specimens was found to have decreased, but the 42CrMo4 clad specimens exhibited a more significant reduction in fatigue performance due to the presence of hardness and tensile residual stresses [16].In contrast to steel 42CrMo4, the hardness of the clad X5CrNi18-10 steel decreased in the HAZ.The crack initiation locations of the 42CrMo4 specimens were below the surface, whereas the steel X5CrNi18-10 specimens cracked above the surface, which is also a region of lowerfatigue life [75].
To enhance wear resistance and prevent self-welding in sodium-cooled fast reactors, a Ni-Cr-B-Si alloy (SFRs) was applied as a hardfacing material onto 316LN stainless-steel components [29,76].Three hardfacing techniques were used in this investigation: laser cladding, PTA, and GTA, for high-temperature applications.The shear strengths offered by the laser hardfacing process were 62% and 24.3% higher than that of the GTA and PTA hardfacing methods, respectively.The laser hardfacing technique prevents deposit debonding by combining strong microhardness, little dilution, and high bonding shear strength.The laser hardfacing method is recommended for 316LN SS nuclear components to ensure their function as intended throughout a long 20-year lifespan [77,78].
S. Kanga et al. investigated the application of ultrasonic fatigue testing as an innovative, efficient, and reproducible method for understanding and predicting the behavior of welded surface coatings [79].The study compared two flux-cored wires with identical nominal chemical compositions from different manufacturing sources under identical welding conditions [80].The base material was a steel bar of AISI 4145H Mod.42CrMo4 type and exhibited a hardness of 32-34 HRC.Flux-cored wires known as TeroMatec OA 4923 were used for welding.The process of preparing the samples is depicted in Figure 10.As shown schematically in Figure 12c, the authors extracted two sets of fatigue samples, named the C-series and the E-series, from the welded steel plates [81].An ultrasonic resonance testing system with a power supply was used to conduct the fatigue tests.The stress amplitude versus loading cycles until failure, as displayed in Figure 13a, revealed the results of the ultrasonic fatigue tests conducted on these two sample series.Each sample series underwent high-cycle fatigue tests, encompassing up to 1 × 10 8 loading cycles under continuous tension.Using the step test technique, the author determined that the selected stress amplitudes for the E-series and C-series samples were 460 MPa and 600 MPa, respectively.It is evident that weld overlays produced with C-wires exhibited significantly greater resistance to high-cycle fatigue compared to those made with E-type materials.Figure 13b-e illustrates the typical fracture surfaces of the failed samples, highlighting the final overload area, the crack propagation zone, and the sites where cracks initiated near or at the surface.It was identified that the presence of larger carbide particles near or at the surface was responsible for reduced cycles until failure at the given stress amplitude.As expected, fatigue cracks consistently originated in the areas of stress concentration at the root of the notch.The final rupture areas in both cases exhibited the morphology and characteristics of ductile-type fractures, featuring dimples.The improved fatigue properties of the C-series samples were likely attributed to their microstructure [82], which contained a higher proportion of austenite.Interestingly, the hardness and wear characteristics of the two weld overlays did not show significant differences.Conversely, the E-series material demonstrated reduced resistance to fatigue crack propagation due to the presence of larger carbide particles and a higher proportion of hard and brittle martensitic phases [83].The presence of retained austenite was known to have a positive impact on the fatigue resistance of high-strength steel weldments near the fatigue threshold [84].Previous studies have highlighted the importance of residual stress within the substrate beneath contact on the substrate's fatigue life.One author observed a significant influence of metal subsurface layers on fatigue failure.They found that residual stress in the metal subsurface layers notably affected the fatigue life of samples coated with MAO (Microarc Oxidation).Fatigue fracture initiation occurred within the substrate beneath the interface, as shown in Figure 14, They observed that as the thickness of coatings increased from 14 to 65 mm, the fatigue strength of the aluminum alloy substrate decreased by 30 to 58%.These results suggest that the residual compressive stress (RCS) present in MAO coatings hampers the initiation and propagation phases of the fatigue process [85].The effect of hardfacing on fatigue life can be influenced by various factors and limitations in the present work.Table 5 shows an overview of the topic, along with limitations and recommendations.The effect of hardfacing on fatigue life can be influenced by various factors and limitations in the present work.Table 5 shows an overview of the topic, along with limitations and recommendations.The fatigue life of the unclad specimen is longer than that of the cladded specimen due to the coating thickness.
Reduce the coating thickness to increase the fatigue life of cladded alloy.WC-12Co particles can be used for cladding.

2.
Ni-Cr-B-Si alloy coating is used on 316LN SS material in sodium-cooled fast reactor applications.
Laser cladding had high shear strength and microhardness as compared to PTA and GTA hardfacing processes.
Ni and Cr alloy coatings can be used to strengthen the product.Laser cladding is recommended for the hardfacing of sodium-cooled reactors and nuclear applications.

3.
The screws and barrels of plastic and rubber injection machines have been treated with lasers.In the same conditions, the lifespan of laser-treated screws is 50-60% longer compared to high alloy screws treated with nitriding.
The treatment depth and coverage may be limited, and the underlying bulk material properties may remain unchanged.
This method can be extended to other parts in various industries that are susceptible to corrosion and erosion.
Rapid cooling and heating developed a heat-added zone, which altered the residual stress and also reduced mechanical properties.
Laser cladding is typically limited to materials that can be processed in powdered form.Not all materials are suitable for laser cladding.

Effect of Mechanical Properties on Fatigue Life of the Structural Components
Nguyen et al. [86] investigated the impact of tensile and bending loads on the fatigue life of welded structures.An arithmetic model was employed to investigate several weld geometry characteristics, such as the flank angle, weld toe undercut, weld toe radius, plate thickness, and misalignment.The linear elastic fracture approach was used to forecast the fatigue crack growth rates of the weld shapes.The study focused on ASTM A36 structural steel due to its numerous applications in welded structures.Static and fatigue tests were conducted to examine various parameters such as load, displacement, strain, frequency, and number of cycles.The fatigue life of butt-welded joints can be significantly improved by minimizing or eliminating the undercut tip radius at the weld toes [87].Although welding results in tensile residual stresses that can decrease fatigue life and weaken structures, the fatigue life and strength of welded joints can be increased by surface treatment processes such as surface peening or tensile pre-loading.The mathematical model used in this research can accurately calculate the combined effects of the butt weld geometry parameters and residual stresses [88].The study concluded that reducing the tip radius from 0.35 to 0.05 increased the fatigue life by 12%.The fatigue life of the welded joint was reduced by 58.3% and 75%, respectively, when compared to an undercut-free union and a flush ground-welded plate.Butt joint fatigue occurred regardless of the degree of misalignment, and strength was reduced from 10% to 60% when subjected to mixed loading.
Knez et al. [89] performed the rotary bending test for the prediction of the low fatigue life cycle of S1100Q steel.The rotary bending test was performed on a new machine, as shown in Figure 15, which consisted of three main parts, namely the driving unit, loading, unit, and driving unit, which enables it to set the rotation frequency in the range of 0.3 to 60 Hz.A low-cycle fatigue test was conducted on twelve samples with different strain rates.The Coffin-Manson method was employed to determine the fatigue life periods, and the Ramberg-Osgood law was utilized to calculate the stress distribution.Based on the experiment [90], it was observed that the stress generated on rotating bending was 18.18% lower than that of axial tension and 30.76% lower than that of static tension.The fatigue life cycle observed with the rotating bending test was 20,000 at 0.004ε a .The estimated rotating bending fatigue life cycle was 20,000 at 0.002ε a , which is equal to the estimated axial tension fatigue life.The axial fatigue life of S1100Q was approximately 4000 at 0.004ε a , which was 80% less than that of the estimated axial fatigue life and rotating bending fatigue life; due to specimen buckling, overall strain is usually restricted to 1%.
Technologies 2024, 12, x FOR PEER REVIEW 22 of 33 strain rates.The Coffin-Manson method was employed to determine the fatigue life periods, and the Ramberg-Osgood law was utilized to calculate the stress distribution.
Based on the experiment [90], it was observed that the stress generated on rotating bending was 18.18% lower than that of axial tension and 30.76% lower than that of static tension.The fatigue life cycle observed with the rotating bending test was 20,000 at 0.004εa.The estimated rotating bending fatigue life cycle was 20,000 at 0.002εa, which is equal to the estimated axial tension fatigue life.The axial fatigue life of S1100Q was approximately 4000 at 0.004εa, which was 80% less than that of the estimated axial fatigue life and rotating bending fatigue life; due to specimen buckling, overall strain is usually restricted to 1%. Lee et al. [91] calculated the low cycle fatigue and thermo mechanical fatigue life of Ni-base super alloy for high-speed rotating parts in aerospace and automobile applications [92].Cylindrical types of specimens were made up of Ni-based super alloy GTD-111 for testing.A tensile test for LCF was performed at room temperature and 850 °C on hydraulic machines.IP-TMF (in-phase thermo mechanical testing) and OP-TMF (out-phase thermo mechanical testing) tensile tests were performed using a furnace, cooling, and control system.
The TMF test was conducted over a temperature range of 400 °C to 800 °C, with a 20 min break between cycles.The IP-TMF test showed temperature-dependent strain, while Lee et al. [91] calculated the low cycle fatigue and thermo mechanical fatigue life of Ni-base super alloy for high-speed rotating parts in aerospace and automobile applications [92].Cylindrical types of specimens were made up of Ni-based super alloy GTD-111 for testing.A tensile test for LCF was performed at room temperature and 850 • C on hydraulic machines.IP-TMF (in-phase thermo mechanical testing) and OP-TMF (out-phase thermo mechanical testing) tensile tests were performed using a furnace, cooling, and control system.
The TMF test was conducted over a temperature range of 400 • C to 800 • C, with a 20 min break between cycles.The IP-TMF test showed temperature-dependent strain, while the OP-TMF test exhibited a decrease in strain as temperature increased.During the tensile experiment, the specimen exhibited a tensile strength of 1140 MPa at ambient temperatures and 1120 MPa at 850 • C. The yield strength at room temperature was 1020 MPa, whereas at 850 • C, it was reduced to 830 MPa.At higher temperatures, the yield strength of GTD-111 decreased by 20% while the strain increased by 33%, leading to the material's ductility.Figure 16 shows that at high temperatures, the IP and OP-TMF tests had shorter fatigue lives than the LCF test.Because of the high temperature in the tensile zone, the IP-TMF test had a shorter life cycle than the OP-TMF test.Li et al. [93] developed a cladding alloy to repair the deep pits in nodular cast iron.Previously, nodular cast iron had a low tensile strength in the interface region and shrunk at a lower temperature.The higher residual stress values were also a big problem, which was a cause of the initiation of cracks.Fe-36Ni alloy and NiCu alloy were used as cladding powder in this experiment because of their low expansion coefficient.A scanning electron microscope and optical microscope were used to characterize the microstructure.It predicted that there is no crack visible in the interface region of the cladded alloy.The value of thermal expansion of the substrate region was 17.40% less than that of the cladding region at low temperatures (100-200 °C) and high temperatures (1000 °C).The average microhardness was 30.43% lower than that of the Ni-Cu layer of the substrate material and the same as the Fe-36Ni layer.Minimizing the thermal expansion coefficient effectively reduced the occurrence of cracks during the repair of deep pits in nodular cast iron.
Masaki et al. [94] conducted a fatigue test to determine thefatigue crack point and static strength of extruded Mg-Al-Z composites.The fatigue tests were performed on three different Mg-Al-Zn alloys.Commercially, three different types of extruded magnesium alloys, namely AZ31, AZ61, and AZ80, were utilized.The 6 mm-width specimen was used to test fatigue strength, while the 5 mm-width specimen was used to study the fatigue life.The fatigue strength of AZ31 was 90 MPa at 10 8 cycles, which was the same as the 0.2% compressive proof stress of the material.AZ61 had a fatigue strength of 150 MPa at 10 8 cycles.The fatigue crack occurred after 8×10 8 cycles with a stress amplitude of 130 MPa, equivalent to the material's compressive stress.AZ80 had a fatigue strength of 140 MPa at 10 8 cycles.It was also observed that the tensile and compressive properties of AZ80 were higher than those of AZ61.Based on the stress amplitude, the maximum fatigue life cycles of AZ31, AZ61, and AZ80 were 1.18 × 10 8 , 0.89×10 8 , and 1.04×10 8 at 90 MPa, 150 MPa, and 140 MPa, respectively.
Zhang et al. [95] performed a fatigue test on Cr-coated SS316 and investigated the failure mechanism.The mechanism of fatigue crack initiation consisted of surface extrusion and intrusion.A flat dogbone-shape specimen was prepared using an SS316 sheet Li et al. [93] developed a cladding alloy to repair the deep pits in nodular cast iron.Previously, nodular cast iron had a low tensile strength in the interface region and shrunk at a lower temperature.The higher residual stress values were also a big problem, which was a cause of the initiation of cracks.Fe-36Ni alloy and NiCu alloy were used as cladding powder in this experiment because of their low expansion coefficient.A scanning electron microscope and optical microscope were used to characterize the microstructure.It predicted that there is no crack visible in the interface region of the cladded alloy.The value of thermal expansion of the substrate region was 17.40% less than that of the cladding region at low temperatures (100-200 • C) and high temperatures (1000 • C).The average microhardness was 30.43% lower than that of the Ni-Cu layer of the substrate material and the same as the Fe-36Ni layer.Minimizing the thermal expansion coefficient effectively reduced the occurrence of cracks during the repair of deep pits in nodular cast iron.
Masaki et al. [94] conducted a fatigue test to determine thefatigue crack point and static strength of extruded Mg-Al-Z composites.The fatigue tests were performed on three different Mg-Al-Zn alloys.Commercially, three different types of extruded magnesium alloys, namely AZ31, AZ61, and AZ80, were utilized.The 6 mm-width specimen was used to test fatigue strength, while the 5 mm-width specimen was used to study the fatigue life.The fatigue strength of AZ31 was 90 MPa at 10 8 cycles, which was the same as the 0.2% compressive proof stress of the material.AZ61 had a fatigue strength of 150 MPa at 10 8 cycles.The fatigue crack occurred after 8 × 10 8 cycles with a stress amplitude of 130 MPa, equivalent to the material's compressive stress.AZ80 had a fatigue strength of 140 MPa at 10 8 cycles.It was also observed that the tensile and compressive properties of AZ80 were higher than those of AZ61.Based on the stress amplitude, the maximum fatigue life cycles of AZ31, AZ61, and AZ80 were 1.18 × 10 8 , 0.89 × 10 8 , and 1.04 × 10 8 at 90 MPa, 150 MPa, and 140 MPa, respectively.
Zhang et al. [95] performed a fatigue test on Cr-coated SS316 and investigated the failure mechanism.The mechanism of fatigue crack initiation consisted of surface extrusion and intrusion.A flat dogbone-shape specimen was prepared using an SS316 sheet [96].The fatigue test was conducted on two groups of stainless steel; the uncoated specimen was considered in the first group, while a thin layer of polycrystalline Chromium coating specimen was considered inthe second group.The bending rotating test was performed on an LFE-150 fatigue testing machine [97] with a variable motor speed at a 20 Hz frequency.The fatigue life cycle of the chromium-coated specimen at a lower stress amplitude (260 MPa) was 2 × 10 6 cycles more than the uncoated specimen.However, at a high-stress amplitude (460 MPa), the fatigue life of the uncoated specimen was longer than that of the Cr-coated specimen.The density of the polycrystalline chromium coating and the height of the surface extrusion increased as the stress amplitude increased.It was reported that the fatigue life initially improved due to the coating.
Ding et al. [98] conducted a fatigue test on TC17 specimens, both with and without scratches, and also analyzed the wear and tear damage parameters using Murakami's hypothesis.They found that the presence of micromechanical scratches reduced the fatigue life of TC17 in the high-cyclefatigue zone.A new approach was proposed by the study, which defines fatigue damage from microscopic scratches as the square root of the triangle area of the scratch section.The proposed model demonstrated a good correlation between experimental and predicted data.
Hu et al. [99] evaluated the effect of selective laser melting technology on Ti-6Al-4V.The selective laser melting technology leads to lower fatigue life.The lower fatigue life is mainly due to manufacturing defects and the lack of fusion defects.It was also found that the low porosity, random distribution of defect size, and position also lead to lower fatigue life.The resistance to fatigue life was found using numerical modeling, in which the stress intensity factor was considered.The account of stress intensity factor also considered defect size and location, which were responsible for the lower fatigue life.In contrast, the nominal stress amplitude could not show resistance to fatigue life.
Kim et al. [100] provided recommendations on the design of a 78 kW agricultural tractor gearbox and calculated the fatigue life of the spiral bevel gear.The fatigue life was estimated for the three bevel gear specimens at five different sites, and an accelerated life test was conducted under static load conditions for sites 1 and 2. Ploughing and rotary tilling were performed at site 3 with an area of 4000 m 2 , while ballet work was completed atsite 4 with an area of 14,400 m 2 , and loader work was completed at site 5 with an area of 4000 m 2 .The outcomes demonstrated that the fatigue life of the spiral bevel gear was 214 times longer under integrated equivalent loads and 9400 times longer under plough-equivalent loads when compared to the rated load.These findings may be useful in optimizing the design of tractor gearbox spiral bevel gears, taking into account the field-equivalent load.
Abdullah et al. [101] compared the fatigue life of leaf springs for various road load strain conditions (highway, campus, and rural) using reliability and hazard assessment parameters.The leaf springs were broken due to the high speed of the speed breakers.The failure mode of leaf springs was calculated using the Coffin-Manson, Morrow, and Smith-Watson-Topper (SWT) methods.The Coffin-Manson model's fatigue life was longer than the other two models.According to the SWT approach, the fatigue life of a highway road is 99.70% and 99.62% higher than that of a campus road and rural road, respectively.The reliability cycle-until-failure danger rate's 3D distribution contour was found to increase the leaf spring's durability.
Berry et al. [15] investigated the effect of residual stresses on the fatigue life of aluminum alloys.A specimen of an aluminum 7075 bar was made for the testing of the fatigue life cycle using a three-point bending test, as shown in Figure 17.The three-point bending test was carried out three times on machined and un-machined surfaces.After the experiment, it was noted that the fatigue life had increased due to an increase in residual surface stresses.The fatigue life of the specimen depends on the crack initiation.The machined surface depicted the crack initiation at the corner of the surface, whereas the unmachined surface showed it at the center.As shown in Figure 18, an increase in the residual stress surface led to a longer fatigue life in the machined surface specimen than in the unmachined surfaces.Simunek et al. [6] conducted a fatigue test on flat mild steel S355 specimens with V-shaped and semi-elliptical notches subjected to continuous and varying amplitude loading.The study shows that the presence of beach markings inside the fractured area can speed up, slow down, or even stop crack propagation depending on the load sequence.Single-edge notch tension (SENT) specimens were used, with the V-notch wire eroded into one of the specimen's edges, as shown in Figure 19.Two crack gauges were installed on either side of the specimen's surface, and the crack length offset was assumed to represent the observed value after pre-cutting for the numerical and analytical investigation [98,99].The study performed two tests under constant-amplitude loading (CAL) at stress levels of 150 MPa and 100 MPa, respectively.Additionally, a synthetic test with variable-amplitude loading (VAL) was designed for both stress amplitudes, using block lengths of 20,000 load cycles for each alternating stress level, starting with the highest stress level.The residual service life obtained from the CAL test at 100 MPa was almost four times longer than that obtained from the test at 150 MPa.The VAL specimen had a higher start crack propagation rate than the equivalent CAL specimen at 150 MPa, which can be attributed to the slightly longer crack initiation in the CAL test specimen.Simunek et al. [6] conducted a fatigue test on flat mild steel S355 specimens with V-shaped and semi-elliptical notches subjected to continuous and varying amplitude loading.The study shows that the presence of beach markings inside the fractured area can speed up, slow down, or even stop crack propagation depending on the load sequence.Single-edge notch tension (SENT) specimens were used, with the V-notch wire eroded into one of the specimen's edges, as shown in Figure 19.Two crack gauges were installed on either side of the specimen's surface, and the crack length offset was assumed to represent the observed value after pre-cutting for the numerical and analytical investigation [98,99].The study performed two tests under constant-amplitude loading (CAL) at stress levels of 150 MPa and 100 MPa, respectively.Additionally, a synthetic test with variable-amplitude loading (VAL) was designed for both stress amplitudes, using block lengths of 20,000 load cycles for each alternating stress level, starting with the highest stress level.The residual service life obtained from the CAL test at 100 MPa was almost four times longer than that obtained from the test at 150 MPa.The VAL specimen had a higher start crack propagation rate than the equivalent CAL specimen at 150 MPa, which can be attributed to the slightly longer crack initiation in the CAL test specimen.Simunek et al. [6] conducted a fatigue test on flat mild steel S355 specimens with V-shaped and semi-elliptical notches subjected to continuous and varying amplitude loading.The study shows that the presence of beach markings inside the fractured area can speed up, slow down, or even stop crack propagation depending on the load sequence.Single-edge notch tension (SENT) specimens were used, with the V-notch wire eroded into one of the specimen's edges, as shown in Figure 19.Two crack gauges were installed on either side of the specimen's surface, and the crack length offset was assumed to represent the observed value after pre-cutting for the numerical and analytical investigation [98,99].The study performed two tests under constant-amplitude loading (CAL) at stress levels of 150 MPa and 100 MPa, respectively.Additionally, a synthetic test with variable-amplitude loading (VAL) was designed for both stress amplitudes, using block lengths of 20,000 load cycles for each alternating stress level, starting with the highest stress level.The residual service life obtained from the CAL test at 100 MPa was almost four times longer than that obtained from the test at 150 MPa.The VAL specimen had a higher start crack propagation rate than the equivalent CAL specimen at 150 MPa, which can be attributed to the slightly longer crack initiation in the CAL test specimen.Wang et al. [102] investigated the effect of lanthanum oxide on contact fatigue damage to ferrous alloy-coated wheel and rail specimens under oil lubrication conditions.Laser cladding was used to cover the Fe-based alloy,which makes the rails more resistant to wear.The utilization of lanthanum oxide offers ease of application and the ability to enhance the microstructure and grain boundary of cladding materials, making it advantageous.Untreated specimens of wheels and rails have numerous visible fatigue cracks, whereas specimens with no lanthanum oxide coating are identified by their fatigue cracks.On the other hand, specimens coated with lanthanum oxide do not have any visible fatigue cracks.When lubricated with oil, the addition of 1.2% lanthanum oxide in Fe-based alloys results in the wheel and rail samples having the most favorable fatigue resistance properties.
Tanaka and Mura [103] investigated fatigue fracture initiation in ductile materials using slip plastic flow concepts.The dislocation dipole layers become free surfaces when the surface energy and the stored energy equalize, which happens when the fracture begins to form [104,105].
Yao et al. [106] examined how damage caused by heat affected the dynamic fracture toughness.The experiment was conducted in a split Hopkinson pressure bar using mortar from notch specimens that had undergone heat treatment.X-ray computer tomography was used to assess chemically and thermally induced microcracks.The fracture hardness appeared to decline.This is because of the heat treatment and fracture damage, which together had the effects of microcracking, chemical alterations, and a decline in the binding property.
A. Zanichelli et al.'s [107] research work involved the production and endurance testing of four types of specimens: plain specimens, sharp-notch specimens (with a root radius of 0.07 mm), circular-notch specimens (with a root radius of 2 mm), and blunt-notch specimens (with a root radius of 5 mm).The root mean square error method (TRMS) was utilized for accurate assessment.Overall TRMS values for plain and blunt-notched specimens were less than 2, while circular-notched specimens showed slightly higher values, and specimens with a sharp notch had values lower than 3, indicating satisfactory outcomes.Furthermore, it appears that the accuracy level remained largely unaffected by the load design.This observation underscores the robustness of the methodology, as it consistently delivered satisfactory results irrespective of specimen type, loading conditions, degree of multiaxiality, or non-proportionality.
S. Abazari et al. [108] investigated the impact of the short-fiber concentration of Al2O3 on the high-cycle fatigue properties of AZ91D alloy.Their findings indicated that adding reinforcement improved the matrix's fatigue strength.Moreover, they observed that composite crack initiation typically occurred at the sites of agglomerated reinforcing fibers.The fatigue crack was predominantly initiated along the highest shear stress and then propagated outward from the original cracked grain.It was noted that grain Wang et al. [102] investigated the effect of lanthanum oxide on contact fatigue damage to ferrous alloy-coated wheel and rail specimens under oil lubrication conditions.Laser cladding was used to cover the Fe-based alloy, which makes the rails more resistant to wear.The utilization of lanthanum oxide offers ease of application and the ability to enhance the microstructure and grain boundary of cladding materials, making it advantageous.Untreated specimens of wheels and rails have numerous visible fatigue cracks, whereas specimens with no lanthanum oxide coating are identified by their fatigue cracks.On the other hand, specimens coated with lanthanum oxide do not have any visible fatigue cracks.When lubricated with oil, the addition of 1.2% lanthanum oxide in Fe-based alloys results in the wheel and rail samples having the most favorable fatigue resistance properties.
Tanaka and Mura [103] investigated fatigue fracture initiation in ductile materials using slip plastic flow concepts.The dislocation dipole layers become free surfaces when the surface energy and the stored energy equalize, which happens when the fracture begins to form [104,105].
Yao et al. [106] examined how damage caused by heat affected the dynamic fracture toughness.The experiment was conducted in a split Hopkinson pressure bar using mortar from notch specimens that had undergone heat treatment.X-ray computer tomography was used to assess chemically and thermally induced microcracks.The fracture hardness appeared to decline.This is because of the heat treatment and fracture damage, which together had the effects of microcracking, chemical alterations, and a decline in the binding property.
A. Zanichelli et al.'s [107] research work involved the production and endurance testing of four types of specimens: plain specimens, sharp-notch specimens (with a root radius of 0.07 mm), circular-notch specimens (with a root radius of 2 mm), and blunt-notch specimens (with a root radius of 5 mm).The root mean square error method (TRMS) was utilized for accurate assessment.Overall TRMS values for plain and blunt-notched specimens were less than 2, while circular-notched specimens showed slightly higher values, and specimens with a sharp notch had values lower than 3, indicating satisfactory outcomes.Furthermore, it appears that the accuracy level remained largely unaffected by the load design.This observation underscores the robustness of the methodology, as it consistently delivered satisfactory results irrespective of specimen type, loading conditions, degree of multiaxiality, or non-proportionality.
S. Abazari et al. [108] investigated the impact of the short-fiber concentration of Al 2 O 3 on the high-cycle fatigue properties of AZ91D alloy.Their findings indicated that adding reinforcement improved the matrix's fatigue strength.Moreover, they observed that composite crack initiation typically occurred at the sites of agglomerated reinforcing fibers.The fatigue crack was predominantly initiated along the highest shear stress and then propagated outward from the original cracked grain.It was noted that grain boundaries played a crucial role in impeding the spread of these microcracks.Furthermore, the particle size was found to influence microstructural fatigue parameters, and grain refinement was identified as a potential method to enhance fatigue performance.
Different methods can have varying effects on the fatigue life of components.Table 6 shows some common methods and their advantages and disadvantages.

Constant loading
Reduce the chance of crack initiation and provide longer fatigue life for SS alloy material [96,109].
Required specialized and costly equipment.

2.
Variable loading [110] Needed specialized equipment, and highly skilled labor.Appropriate for small areas.

Heat treatment or tempering
Proper heat treatment can enhance a component's fatigue life by optimizing its microstructure and mechanical properties.
Following the heat treatment process, a subsequent cooling stage is necessary, thereby rendering it an expensive and time-intensive procedure [111].

Spot heating
Quality method for repairing the components.Equipment is easily available.
Applicable for local and small areas only.

5.
Shot peening, Needle peening [112] Improves fatigue life and reduces the risk of corrosion and cracking.
It is necessary to have specialized equipment.It is also noisy and tedious.

6.
Hardness method and multilayer method [113,114] Specimens with lower carburizing depth have a shorter fatigue lifespan, while specimens with higher carburizing depth have a longer fatigue lifespan.
Hardness itself and a lower carbon percentage are the regionsof a low fatigue cycle.

Environmental Factors
Environmental conditions, such as temperature, humidity, corrosive agents, and vibration, can influence fatigue life.
Elevated temperatures, aggressive chemicals, or corrosive atmospheres can reduce fatigue life.

Chronological Evaluation and Development
The chronological evaluation and development of fatigue analysis based on fatigue problems and the adoption of new technology are shown in Table 7.
Table 7. Chronological evaluation and development.

S.No. Time Period
Key Developments 1 Before 1990 In the 1960s, P.C.Paris pioneered methodologies for predicting the progression rate of individual fatigue cracks, thereby enabling the estimation of fatigue life.He illustrated the relationship between the rate of fracture length alteration and the number of cycles through practical demonstrations.In the early 1990s, only destructive testing was utilized for fatigue analysis.A number of researchers focused on fatigue damage analysis and fatigue life predictions through SHM and field measurements.The adoption of multistage modeling techniques is on the rise, facilitating the analysis of fatigue and bridging the divide between component-level behavior and microstructural features.Machine learning methods are being employed to forecast fatigue damage and predict fatigue life more accurately.The emphasis on sustainable design has spurred research into fatigue analysis for renewable energy structures and lightweight materials.Continued enhancements are being made to fatigue analysis models to address the complex loading conditions prevalent in the marine, automotive, and aerospace sectors.Automation and digitalization have revolutionized fatigue testing and analysis techniques, streamlining processes.Research endeavors are exploring the fatigue behavior of materials in challenging environments, such as high temperatures and corrosive settings.Additionally, investigations into biologically inspired methods aim to enhance the fatigue resistance of engineered structures.

Future Trends and Development
Across diverse industries such as aerospace, automotive, and infrastructure, where sustainability and durability are increasingly prioritized, researchers and engineers are proactively investigating innovative strategies to prolong the fatigue life of structural components and systems.Several researchers have examined the fatigue characteristics of advanced high-strength steels, aluminum alloys, titanium alloys, and many more each with tailored microstructures and mechanical properties.However, enhancing fatigue life may involve exploring the fatigue resistance of composite materials reinforced with nanoparticles or carbon fibers to achieve superior strength and durability.Si-based alloys can also be used instead of Al alloys.The hardfacing of Ni and Co base alloys can reduce crack growth and strengthen the components.If future researchers do not want to perform heat treatment, they can work on SS alloys for higher fatigue life, but for other alloys like Ni, Cr, and Al, heat treatment reduces the effect of residual stresses.Advanced non-destructive evaluation techniques, including neutron diffraction and digital image correlation, offer the precise quantification of residual stresses in manufactured components.Applications such as shot peening and laser peening can be used to create advantageous compressive stresses and enhance fatigue resistance.Nickel-aluminum-bronze alloys can be used for laser shock peening applications.Currently, the additive manufacturing process is widely used in the production area.To mitigate the defects and improve the fatigue life, in situ monitoring methods should be used.Non-destructive testing can be used for accurate fatigue assessment and cost-effective evaluations.The composition of corrosive mediums in natural environments is intricate, with numerous elements impacting corrosion processes.The locations and forms of corrosion remain highly uncertain.Future research demands a probabilistic prediction model that incorporates spatial variability.Nevertheless, more complex fatigue models that make use of probabilistic techniques are necessary to provide accurate estimates of usable lifespans.

Conclusions
The fatigue life of components is affected by several factors, including residual stresses, hardness, temperature, and hardfacing.Designers and engineers must take these factors into account when designing components for high-cycle fatigue applications.Residual stresses can occur during the manufacturing process.During manufacturing, these internal stresses may result in a combination of both compressive and tensile stresses.Residual stresses have both positive and negative effects on the fatigue life of components.The presence of compressive residual stresses increases the fatigue life of components via the retardation of the formation of microcracks.
High temperatures significantly reduce the fatigue life of components, particularly in materials with low thermal conductivity.This is because elevated temperatures increase the rate of crack growth and lead to premature failure.In addition, thermal expansion and contraction generate residual stresses, which further reduce the fatigue life of components.
The hardness of materials has a significant effect on the fatigue life of structural components.Hard materials are more susceptible to fatigue failure because they have less ductility and are less able to absorb energy when they undergo cyclic loading.This is the cause of more rapid crack initiation and propagation, leading to a shorter fatigue life.On the other hand, materials that are too soft also have a shorter fatigue life because they are more prone to plastic deformation and experience more rapid crack growth.
The application of hardfacing generates residual stresses, which reduces the fatigue life of the component.The effectiveness of hardfacing depends on the specific application and loading conditions, particularly in high-stress applications.The type of hardfacing material also affects fatigue life.Some hardfacing materials such as chromium carbide provide excellent wear resistance but are prone to cracks under high-stress conditions, which reduce the fatigue life.Other materials such as nickel-based alloys have a better fatigue resistance but are more expensive to apply.
Future work should concentrate on developing new models and new technologies to predict the fatigue life and strength of various materials.This will be beneficial to broadening the fields of failure mode and fatigue analysis to further encompass different materials.

Figure 2 .
Figure 2. Stages of failure in terms of crack length versus time/cycles of service [11].

Figure 4 .
Figure 4. (a) Comparison of the number of cycles until failure under the different loading sequences for AA6061, (b) Comparison of the number of cycles until failure under the different loading sequences for AA7075 [30].

Figure 4 .
Figure 4. (a) Comparison of the number of cycles until failure under the different loading sequences for AA6061, (b) Comparison of the number of cycles until failure under the different loading sequences for AA7075 [30].

Figure 7 .
Figure 7. Residual stress relaxation with number of cycles for LSP ATI 718Plus alloy samples tested [41].

Figure 7 .
Figure 7. Residual stress relaxation with number of cycles for LSP ATI 718Plus alloy samples tested [41].

Figure 8 .
Figure 8. Change and error bars with the total range of microhardness in ferrite and pearlite during fatigue loading [54].

Figure 8 .
Figure 8. Change and error bars with the total range of microhardness in ferrite and pearlite during fatigue loading [54].

Figure 10 .
Figure 10.Hardness distribution of VR690 joints [68].P. Mendes et al. analyzed hardness properties using Vickers hardness testing.The primary objective of their work was to examine the impact of heat input during the final stages on the preceding steps in the tempering heat treatment process.Temper treatment typically induces a reduction in hardness values, underscoring the necessity of micro-

Figure 10 .
Figure 10.Hardness distribution of VR690 joints [68].P. Mendes et al. analyzed hardness properties using Vickers hardness testing.The primary objective of their work was to examine the impact of heat input during the final stages on the preceding steps in the tempering heat treatment process.Temper treatment typically induces a reduction in hardness values, underscoring the necessity of microhardness tests in comprehending the evolution of this mechanical property.This phase

33 Figure 12 .
Figure 12.Sample preparation technique for welded joints: (a) steel base material with a U-groove, (b) steel disc, (c) schematic drawing showing the sample preparation concept [81].

Figure 13 .
Figure 13.Comparison of the fatigue data (stress amplitude against loading cycles until failure for E and C welded samples series (a).Typical overview images and details of the fatigue fracture surfaces of (b,d) E-and (c,e) C-weld samples series [82].

Figure 12 . 33 Figure 12 .
Figure 12.Sample preparation technique for welded joints: (a) steel base material with a U-groove, (b) steel disc, (c) schematic drawing showing the sample preparation concept [81].

Figure 13 .
Figure 13.Comparison of the fatigue data (stress amplitude against loading cycles until failure for E and C welded samples series (a).Typical overview images and details of the fatigue fracture surfaces of (b,d) E-and (c,e) C-weld samples series [82].

Figure 13 .
Figure 13.Comparison of the fatigue data (stress amplitude against loading cycles until failure for E and C welded samples series (a).Typical overview images and details of the fatigue fracture surfaces of (b,d) E-and (c,e) C-weld samples series [82].

Figure 13 .
Figure 13.Comparison of the fatigue data (stress amplitude against loading cycles until failure for E and C welded samples series (a).Typical overview images and details of the fatigue fracture surfaces of (b,d) E-and (c,e) C-weld samples series [82].
predicting fatigue life.Advancements in understanding the mechanics governing the initiation and propagation of fatigue cracks.Introduction of probabilistic approaches to fatigue analysis, incorporating uncertainties in loads and material properties.
of industrial applications are embracing studies on both low-cycle fatigue (LCF) and high-cycle fatigue (HCF).The development of fatigue analysis software capable of tackling intricate loading scenarios and modeling material behaviors is underway.Research efforts are focusing on the fatigue characteristics of advanced materials such as shape memory alloys and composites.42005-2010Fatigue analysis now incorporates computational materials science methodologies, allowing for microstructure-sensitive assessments.Fatigue studies are expanding into novel domains including nanomaterial and additive manufacturing.The adoption of innovative experimental techniques such as digital image correlation (DIC) is enhancing the characterization of fatigue damage.Applied field strain measurement upon linear fatigue damage law and performed fatigue analysis according to Continuous Damage Mechanics (CDM) on a bridge in Hong Kong.
testing methodologies include the implementation of high-throughput testing approaches, expediting fatigue evaluation processes.Integration of digital twins allows for the real-time monitoring and prediction of fatigue damage in structural components.Research efforts are underway to understand the influence of environmental factors on fatigue behavior, particularly focusing on corrosion fatigue and environmental cracking.

Table 1 .
Influence of temperature on fatigue life and limitations and recommendations of present work.

Table 1 .
Influence of temperature on fatigue life and limitations and recommendations of present work.
The fatigue life of AA 6061 decreases above 300 • C and increases below 300 • C. Consequently, AA 6061 is not suitable for high-temperature applications.AA6061 can be replaced by Si-based Al alloy. 2 Material fatigue life increased at elevated temperatures.

Table 2 .
Influence of residual stress on fatigue life.

Table 3 .
Influence of residual stresses on fatigue life and limitations and recommendations of present work.

Table 4 .
Influence of hardness on fatigue life and limitations and recommendations of present work.

Table 4 .
Influence of hardness on fatigue life and limitations and recommendations of present work.

Table 5 .
Influence of hardfacing on fatigue life and limitations and recommendations of present work.

Table 6 .
Advantages and disadvantages of different methods in present work.