Flower-like Thiourea–Formaldehyde Resin Microspheres for the Adsorption of Silver Ions

Around a quarter of annual worldwide silver consumption comes from recycling. It remains a primary target for researchers to increase the silver ion adsorption capacity of the chelate resin. Herein, a series of flower-like thiourea–formaldehyde microspheres (FTFM) possessing diameters of 15–20 μm were prepared via a one-step reaction under acidic conditions, and the effects of the monomer molar ratio and reaction time on the micro-flower morphology, specific surface area, and silver ion adsorption performance were explored. The nanoflower-like microstructure showed the maximum specific surface area 18.98 ± 0.949 m2/g, which was 55.8 times higher than that of the solid microsphere control. As a result, the maximum silver ion adsorption capacity was 7.95 ± 0.396 mmol/g, which was 10.9 times higher than that of the control. Kinetic studies showed that the equilibrium adsorption amount of FT1F4M was 12.61 ± 0.016 mmol/g, which was 11.6 times higher than that of the control. Additionally, the isotherm study of the adsorption process was performed, and the maximum adsorption capacity of FT1F4M was 18.17 ± 1.28 mmol/g, which was 13.8 times that of the control according to the Langmuir adsorption model. Its high absorption efficiency, convenient preparation strategy, and low cost recommend FTFM bright for further use in industrial applications.


Introduction
Growing industrialization and urbanization resulted in severe pollution, particularly that of the aquatic environment [1]. The wastewater produced by the industrial society contains abundant toxic heavy metals such as gold, silver, and cadmium [2,3]. Silver is a noble metal that is widely used in the photography, electronics, chemical, and jewelry industries [1,4,5]. Studies showed that around a quarter of the silver produced from the industry was from wastewater recycling [2,6]. In recent decades, various silver ion recycling strategies have been proposed and evaluated, such as adsorption [1], sedimentation [7], precipitation [8], ion exchange [9], nano-filtration [10], and electrolysis [11]. Among these methods, the adsorbents used for silver recycling have received increasing attention due to their low cost [5]. Common adsorbents include chelating resins [12], activated carbon [5,13], and other biomimetic materials [14].
Polymeric materials containing sulfinyl groups can be used as silver adsorbents due to the high binding affinity between the carbon-sulfur double bond (-C=S-) and silver ion according to hard-soft-acid-base theory [15,16]. Thiourea-formaldehyde resin is a The FTFM was synthesized, characterized, and used as a silver ion adsorbent for the first time. Variety types of thiourea-formaldehyde resins were synthesized with different reaction conditions to verify the raised hypothesis (Scheme 1). The chemical structures of the formulations were characterized by Fourier transform infrared (FTIR) spectroscopy measurements. Additionally, the morphology of the resin microspheres was examined by scanning electron microscopy (SEM), and the specific surface area of each formulation was tested according to BET test. The silver ion adsorbent efficiency was calculated based on ultraviolet (UV)-visible (vis) spectra of the adsorbent suspension after adsorption; also the corresponding adsorption kinetic was studied. Furthermore, the relationship between the synthesis conditions and micromorphology was constructed, and the corresponding affection towards the silver ion adsorbent efficiency was evaluated and discussed. The microflower was synthesized via a one-step reaction in aqueous environment, followed by simple rinsing and filtration after precipitation. The microflowers showed a high specific surface area, which significantly enhanced the silver ion adsorption efficiency. Its simple preparation, low cost, and high efficiency give FTFM a bright future in industrial applications. The FTFM was synthesized, characterized, and used as a silver ion adsorbent for the first time. Variety types of thiourea-formaldehyde resins were synthesized with different reaction conditions to verify the raised hypothesis (Scheme 1). The chemical structures of the formulations were characterized by Fourier transform infrared (FTIR) spectroscopy measurements. Additionally, the morphology of the resin microspheres was examined by scanning electron microscopy (SEM), and the specific surface area of each formulation was tested according to BET test. The silver ion adsorbent efficiency was calculated based on ultraviolet (UV)-visible (vis) spectra of the adsorbent suspension after adsorption; also the corresponding adsorption kinetic was studied. Furthermore, the relationship between the synthesis conditions and micromorphology was constructed, and the corresponding affection towards the silver ion adsorbent efficiency was evaluated and discussed. The microflower was synthesized via a one-step reaction in aqueous environment, followed by simple rinsing and filtration after precipitation. The microflowers showed a high specific surface area, which significantly enhanced the silver ion adsorption efficiency. Its simple preparation, low cost, and high efficiency give FTFM a bright future in industrial applications. Scheme 1. The structure and silver ion adsorption process of FTFM.

Preparation of FTFM
Thiourea (T) (Tianjin Damao Chemical Reagent Factory, Tianjin, China) and formaldehyde (F) (37~40%, Beijing Innochem Technology Co., Ltd., Beijing, China) were reacted together to form a thiourea-formaldehyde resin via the Mannich reaction. Deionized (DI) water (100 mL) was charged into a 150 mL beaker, and thiourea and formaldehyde were added. The molar ratio of thiourea to formaldehyde was listed in Table 1 along with the corresponding sample abbreviations. The pH value of the mixture was adjusted to 2.0 by formic acid (≥98%) and ammonia (28~30%) (Beijing Bailingwei Technology Co., Ltd., Beijing, China) at 25 ℃. The solution was then stirred in a water bath at 50 °C for 4 h, and a white precipitate appeared at the bottom of the beaker, which was FTFM. FTFM was then collected by filtration and washed with DI water 3 times to remove the unreacted reagents.
Solid thiourea-formaldehyde microspheres (STFM) were fabricated by adding NH4Cl (Shanghai Macklin Biochemical Co., Ltd., Shanghai, China) to the mixture after adjusting the pH to 2. The white precipitation was generated after stirring for 4 h. The molar amount of the NH4Cl and the corresponding abbreviations are listed in Table 1. STFM was collected by filtration(filter paper specification: nylon-66, 0.45 µm) and then washed 3 times with DI water (100 mL). Scheme 1. The structure and silver ion adsorption process of FTFM.

Preparation of FTFM
Thiourea (T) (Tianjin Damao Chemical Reagent Factory, Tianjin, China) and formaldehyde (F) (37~40%, Beijing Innochem Technology Co., Ltd., Beijing, China) were reacted together to form a thiourea-formaldehyde resin via the Mannich reaction. Deionized (DI) water (100 mL) was charged into a 150 mL beaker, and thiourea and formaldehyde were added. The molar ratio of thiourea to formaldehyde was listed in Table 1 along with the corresponding sample abbreviations. The pH value of the mixture was adjusted to 2.0 by formic acid (≥98%) and ammonia (28~30%) (Beijing Bailingwei Technology Co., Ltd., Beijing, China) at 25°C. The solution was then stirred in a water bath at 50 • C for 4 h, and a white precipitate appeared at the bottom of the beaker, which was FTFM. FTFM was then collected by filtration and washed with DI water 3 times to remove the unreacted reagents.
Solid thiourea-formaldehyde microspheres (STFM) were fabricated by adding NH 4 Cl (Shanghai Macklin Biochemical Co., Ltd., Shanghai, China) to the mixture after adjusting the pH to 2. The white precipitation was generated after stirring for 4 h. The molar amount of the NH 4 Cl and the corresponding abbreviations are listed in Table 1. STFM was collected by filtration (filter paper specification: nylon-66, 0.45 µm) and then washed 3 times with DI water (100 mL).

Characterization of the FTFM
The morphology of FTFM was characterized by SEM. A small amount of the sample was dispersed in aqueous solution, a few drops were placed onto the silicon wafer, and the sample was dried with infrared light. The surface was sprayed with gold (10 mA) by an Oxford Quorum SC7620 sputter coater for 45 s under vacuum. The surface morphologies of the samples were obtained using SEM (TESCAN MIRA LMS, Beijing Yake Chenxu Technology Co., Ltd., Beijing, China) operated at an accelerating voltage of 3 kV. The surface element distribution of the samples was tested by energy dispersive X-ray spectroscopy (EDS), and the accelerating voltage was set to 15 kV. The structure of FTFM was characterized by FTIR measurements. Dry FTFM powder (approximately 1 mg) and dry KBr (approximately 200 mg) were mixed and grinded for 1 min. The mixture was then placed on the tablet press with a pressure of 15 MPa for 30-60 s to obtain a transparent tablet. The FTIR spectra of the samples were recorded using a Fourier transform interferometer (ALPHA-T, Bruker, Germany) in the range 400-4000 cm -1 . The special surface area was observed by BET analysis. The samples were pretreated under vacuum at 120 • C for 7 h in the standard degassing station. Testing was performed by a fully automated specific surface area analyzer (APSP 2460, Micromeritics, Norcross, GA, USA). The porosity of the sample surface was characterized through nitrogen adsorption-desorption isotherm analysis at 77 K, and the surface areas were calculated by the BET equation. The silver ion adsorption capacity was obtained by UV absorption test. After reaching the specified adsorption time, the microspheres in the solution were removed with a disposable needle filter (pore size 0.45 µm, MCF film). Additionally, the UV absorption maximum corresponding to silver ions was determined by measuring the absorbance of the supernatant at 400 nm using a UV−vis spectrophotometer (Lambda 35, PerkinElmer).

Calculation of Adsorption Capacity
The FTFM (0.1g) with a different monomer ratio was placed with 25 mL 0.1mol/L AgNO 3 solution for 20 min. After adsorption for 20 min, 1 mL of the suspension was subjected to UV absorption measurements (Hitachi U4150, Beijing, China). The concentration of remaining silver ions in the solution was measured, and the monomer ratio with the maximum adsorption capacity was obtained. Furthermore, the optimal monomer ratio that yielded the maximum adsorption capacity was obtained. These data are presented in the supporting information [29].

Adsorption Kinetics
The FTFM adsorbent (0.1 g) was added to 25 mL of 0.1 mol/L AgNO3 solution (pH = 6.0) in a centrifuge tube, and adsorption was allowed to occur for 10-480 min. Samples of 5 mL solution were withdrawn at scheduled time intervals and analyzed for silver ion concentration. Based on Brandani's research on adsorption kinetics [30], the obtained data were fitted to pseudo-first-order (PFO) [31] and pseudo-second-order (PSO) [32] models.

Adsorption Isotherms
At the optimal pH of 6.0, a solution of silver ion (25 mL, 20-100 mmol/L) and FTFM (0.1 g) were placed in a centrifuge tube. The obtained data were fitted to the Langmuir model. The Langmuir model assumes that the adsorption process occurs in a single layer on a homogeneous medium [33].

Results and Discussions
The molar ratio between thiourea and formaldehyde varied in order to optimize the morphology by controlling the self-assembly process. The formulation details and abbreviations for each sample set were illustrated in Table 1. Figure 1 shows SEM images of the particles obtained at different reaction times. For FT 1 F 1 M, flower-like microspheres with a diameter of 10 µm were obtained after 1 h (Figure 1b). However, fractures were presented in the sample, indicating the incompletion of the self-assembly process (Figure 1a). The amount of fractures reduced significantly when the reaction time reached 2 h, as presented in Figure 1c, and the diameter of the FTFM was around 15 µm (Figure 1d), which was significantly higher than that of the sample of 1 h reaction. The fractures of the thioureaformaldehyde resin were hardly observed when the reaction time increased to 4 h, as shown in Figure 1e. Additionally, the corresponding diameter of FTFM remains approximately 15 µm, showing no significant difference compared with that of the sample after 2 h reaction. The amount and distribution of the resin fractures showed no significant change when the reaction time increased to 8 h (Figure 1g), and the diameter of FTFM kept almost unchanged, which was around 15 µm, as presented by Figure 1h. The results indicated that the reaction between formaldehyde and thiourea and the corresponding self-assembly process was completed when the reaction time exceeded 4 h, and the extent of the reaction time showed no significant influence on the diameter of the FTFM.
The effect of the thiourea-to-formaldehyde ratio on the particle morphology was explored, which was presented in Figure 2. As mentioned previously, the reaction time was set to 4 h. The diameter of FT 1 F 0.5 M was around 15 µm, as demonstrated in Figure 2a. The petal size decreased significantly when the formulations came to FT 1 F 1 M, as presented in Figure 1b, and the diameter of the micro-flower showed no significant change. The diameter of the FTFM kept around 15 µm in FT 1 F 2 M, as shown in Figure 2c. The petal size decreased and the petal density increased significantly, compared with that of FT 1 F 1 M. Up to increasing the molar ratio further (FT 1 F 4 M; see Figure 2d), the petal size continues to decrease, and the petal density increases. At the same time, the diameter showed no significant change. The petals on the FTFM became smaller and were distributed more compactly when the molar ration between thiourea and formaldehyde increased from 1:0.5 to 1:4. The self-assembly mechanism of the FTFM was not totally clear. The proposed reason was that the self-assembly was accelerated when the proportion of the formaldehyde increased due to the increasing number of hydrogen bonds. In addition to the formation of the microflowers, solid microspheres were formed by the addition of ammonia chloride; the probable reason for this was that the Mannich reaction between thiourea and formaldehyde was suppressed, further reducing the size or even preventing the formation of petals. Figure 2c demonstrated the morphology of S 1 T 1 F 4 M, in which the molar ratio between ammonia chloride and thiourea was 0.0187:1. The petal size of S 1 T 1 F 4 M significantly reduced and the petal density increased compared with that of FT 1 F 4 M. At the same time, the solid microspheres appeared. When the ratio between ammonia chloride and thiourea increased to 0.0374:1 (S 2 T 1 F 4 M), no microflowers were observed (Figure 2f). The results indicated that the variation of the monomer ratio may dominate the petal size and density for FTFM. However, the corresponding influence of times towards the FTFM dimension was not significant. The introduction of ammonia chloride led to the formation of thiourea-formaldehyde microspheres with a diameter ranging from 8-10 µm, which could be used as the control to investigate the importance of the microflower morphology for silver ion adsorption. The effect of the thiourea-to-formaldehyde ratio on the particle morphology was explored, which was presented in Figure 2. As mentioned previously, the reaction time was set to 4 h. The diameter of FT1F0.5M was around 15 µm, as demonstrated in Figure 2a. The petal size decreased significantly when the formulations came to FT1F1M, as presented in Figure 1b, and the diameter of the micro-flower showed no significant change. The diameter of the FTFM kept around 15 µm in FT1F2M, as shown in Figure 2c. The petal size decreased and the petal density increased significantly, compared with that of FT1F1M. Up to increasing the molar ratio further (FT1F4M; see Figure 2d), the petal size continues to decrease, and the petal density increases. At the same time, the diameter showed no significant change. The petals on the FTFM became smaller and were distributed more compactly when the molar ration between thiourea and formaldehyde increased from 1:0.5 to 1:4. The self-assembly mechanism of the FTFM was not totally clear. The proposed reason was that the self-assembly was accelerated when the proportion of the formaldehyde increased due to the increasing number of hydrogen bonds. In addition to the formation of the microflowers, solid microspheres were formed by the addition of ammonia chloride; the probable reason for this was that the Mannich reaction between thiourea and formaldehyde was suppressed, further reducing the size or even preventing the formation of petals. Figure 2c demonstrated the morphology of S1T1F4M, in which the molar ratio The specific surface area of the FTFM with different formulations was evaluated in order to verify the proposed hypothesis. Figure 3 demonstrated that the BET specific area of the solid thiourea-formaldehyde microsphere (S 2 T 1 F 4 M) was 0.34 ± 0.017 m 2 /g. This value was increased more than 20 times to 7.46 ± 0.373 m 2 /g when the formulation changed to FT 1 F 0.5 M where the flower-like morphology was formed, which indicated that the self-assembly of the thiourea-formaldehyde petals was able to dramatically increase the specific surface area compared with that of the solid spheres. The specific surface area increased to 14.18 ± 0.709, 16.15 ± 0.808, and 18.98 ± 0.949 m 2 /g for FT 1 F 1 M, FT 1 F 2 M, and FT 1 F 4 M, respectively. The results were consistent with the morphology evaluation, i.e., with an increase in the thiourea-to-formaldehyde molar ratio, the petal size decreased and the petal density increased. thiourea increased to 0.0374:1 (S2T1F4M), no microflowers were observed (Figure 2f). The results indicated that the variation of the monomer ratio may dominate the petal size and density for FTFM. However, the corresponding influence of times towards the FTFM dimension was not significant. The introduction of ammonia chloride led to the formation of thioureaformaldehyde microspheres with a diameter ranging from 8-10 µm, which could be used as the control to investigate the importance of the microflower morphology for silver ion adsorption. The specific surface area of the FTFM with different formulations was evaluated in order to verify the proposed hypothesis. Figure 3 demonstrated that the BET specific area of the solid thiourea-formaldehyde microsphere (S2T1F4M) was 0.34 ± 0.017 m 2 /g. This value was increased more than 20 times to 7.46 ± 0.373 m 2 /g when the formulation changed to FT1F0.5M where the flower-like morphology was formed, which indicated that the self-assembly of the thiourea-formaldehyde petals was able to dramatically increase the specific surface area compared with that of the solid spheres. The specific surface area increased to 14.18 ± 0.709, 16.15 ± 0.808, and 18.98 ± 0.949 m 2 /g for FT1F1M, FT1F2M, and FT1F4M, respectively. The results were consistent with the morphology evaluation, i.e., with an increase in the thiourea-to-formaldehyde molar ratio, the petal size decreased and the petal density increased.  The silver ion adsorption capacity was evaluated via the suspension UV-vis spectrum after adsorption. Silver ion has the maximum UV absorption at 303 nm as presented in Figure 4a, and the UV extinction coefficient of silver ion at 303 nm was 6.9 × 10 3 cm 2 /mol. The corresponding calculation and fitting information were presented in the supplementary Information. For the adsorption experiments, 0.15 g of FT1F4M was added to 25 mL 0.1 mol/L AgNO3 solution. As shown in Figure 4a, the UV absorption peak at 303 nm reduced significantly after 10 min of adsorption, indicating that FTFM was able to reduce the concentration of silver ions in the solution. The amount of residual silver ion kept decreasing with the adsorption time, and the corresponding adsorption capacity was calculated and presented in the supplementary section. Figure 4b concludes the silver ion adsorption capacity of FTFM with different formulations after 20 min incubation in the AgNO3 solution. The maximum adsorption capacity of the solid spheres was 0.73 ± 0.037 mmol/g, which increased significantly to 4.02 ± 0.201 mmol/g for FT1F0.5M and increased further to 5.52 ± 0.276, 6.96 ± 0.348, and 7.95 ± 0.398 mmol/g for FT1F1M, FT1F2M, and FT1F4M, respectively. The adsorption capacity result was consistent with the morphology and BET specific area that the close-packed microflower endowed the microspheres with a larger specific surface area, increasing the interaction between the silver ions and the The silver ion adsorption capacity was evaluated via the suspension UV-vis spectrum after adsorption. Silver ion has the maximum UV absorption at 303 nm as presented in Figure 4a, and the UV extinction coefficient of silver ion at 303 nm was 6.9 × 10 3 cm 2 /mol. The corresponding calculation and fitting information were presented in the Supplementary Information. For the adsorption experiments, 0.15 g of FT 1 F 4 M was added to 25 mL 0.1 mol/L AgNO 3 solution. As shown in Figure 4a, the UV absorption peak at 303 nm reduced significantly after 10 min of adsorption, indicating that FTFM was able to reduce the concentration of silver ions in the solution. The amount of residual silver ion kept decreasing with the adsorption time, and the corresponding adsorption capacity was calculated and presented in the supplementary section. Figure 4b concludes the silver ion adsorption capacity of FTFM with different formulations after 20 min incubation in the AgNO 3 solution. The maximum adsorption capacity of the solid spheres was 0.73 ± 0.037 mmol/g, which increased significantly to 4.02 ± 0.201 mmol/g for FT 1 F 0.5 M and increased further to 5.52 ± 0.276, 6.96 ± 0.348, and 7.95 ± 0.398 mmol/g for FT 1 F 1 M, FT 1 F 2 M, and FT 1 F 4 M, respectively. The adsorption capacity result was consistent with the morphology and BET specific area that the close-packed microflower endowed the microspheres with a larger specific surface area, increasing the interaction between the silver ions and the thiourea-formaldehyde resin. Subsequently, the morphology and element composition of FT 1 F 4 M after 20 min adsorption were examined via SEM-EDS. The microsphere kept its flower-like shape after the adsorption, and the diameter showed no significant change, i.e., it remained at approximately 15 µm. However, the petals became significant thicker due to the stacking of silver on the surface. Figure 4d-g shows the element distribution on the surface of the FTFM microsphere after 20 min adsorption, and the silver atoms were uniformly distributed on the surface of the microflower. The homogeneous distribution of the N and S atoms indicated that the thiourea-formaldehyde structure was not disturbed by the adsorption. Among them, silver atoms account for 68.68 wt% of the surface elements ( Figure S1).  The chemical structure of the FTFM before and after the adsorption was further verified by the FTIR, and the corresponding spectrum was plotted in Figure 5. The peaks located at 3311 and 1541 cm −1 were assigned to the N-H stretching and bending vibrations, respectively, which were greatly weakened after the thiourea-formaldehyde resin was formed. Additionally, this trend became more prominent when the molar ratio between thiourea and formaldehyde increased from 1:0.5 to 1:4 as more N-H was replaced by N-C. Correspondingly, the peaks located at 1327 cm −1 representing the N-C connection kept increasing during this process. The peaks caused by the vibration of N-H became wide and unsignificant for the solid microspheres (S2T1F4M) quenched by ammonia chloride. Figure 5b demonstrates the FTIR spectrum of the FTFM samples after 20 min adsorption at 0.1 mol/L AgNO3 solution under room temperature. The peaks located around 1403 cm −1 were assigned to C=S from the thiourea and were greatly reduced after the absorption in the AgNO3 solution, which was supposed to be caused by the chelation between C=S and silver ions. The peaks located around 3311 and 1541 cm −1 were broadened and weakened after adsorption, indicating the chelation between silver ions and N-H during the adsorption. The change of C=S structure of the solid microspheres (S2T1F4M) was hardly observed from the FTIR spectrum; however, the reduction in the peak around 1541 cm −1 The chemical structure of the FTFM before and after the adsorption was further verified by the FTIR, and the corresponding spectrum was plotted in Figure 5. The peaks located at 3311 and 1541 cm −1 were assigned to the N-H stretching and bending vibrations, respectively, which were greatly weakened after the thiourea-formaldehyde resin was formed. Additionally, this trend became more prominent when the molar ratio between thiourea and formaldehyde increased from 1:0.5 to 1:4 as more N-H was replaced by N-C. Correspondingly, the peaks located at 1327 cm −1 representing the N-C connection kept increasing during this process. The peaks caused by the vibration of N-H became wide and unsignificant for the solid microspheres (S 2 T 1 F 4 M) quenched by ammonia chloride. Figure 5b demonstrates the FTIR spectrum of the FTFM samples after 20 min adsorption at 0.1 mol/L AgNO 3 solution under room temperature. The peaks located around 1403 cm −1 were assigned to C=S from the thiourea and were greatly reduced after the absorption in the AgNO 3 solution, which was supposed to be caused by the chelation between C=S and silver ions. The peaks located around 3311 and 1541 cm −1 were broadened and weakened after adsorption, indicating the chelation between silver ions and N-H during the adsorption. The change of C=S structure of the solid microspheres (S 2 T 1 F 4 M) was hardly observed from the FTIR spectrum; however, the reduction in the peak around 1541 cm −1 indicated the chelation between silver ions and N-H on the surface of the solid microspheres. The FTIR spectrum confirmed the Mannich reaction between formaldehyde and thiourea and the chemical structure evolution of different formulations. Additionally, the chelation of NH-Ag + and C=S-Ag + was confirmed for all flower-like microspheres. The adsorption kinetics of FTFM to silver ions were studied. Figure 6 illustrates the relationship between the silver ion adsorption capacity of the thiourea-formaldehyde microspheres and time. The solid thiourea-formaldehyde spheres were able to adsorb silver in aqueous environment, and the capacity increased with the incubation time, which was much lower than that of the flower-like microspheres due to the low specific surface area. The silver ion adsorption capacity of FTFM increased with the raise of the molar ratio between the formaldehyde and the thiourea. The results of the kinetic study were consistent with those of the specific surface area. It was clearly reflected by Figure 6a that the increasing speed of the adsorption capacity slowed down when the adsorption time exceeded 120 min and showed no significant change after 240 min. This indicated that the adsorption and de-adsorption process on the petal surfaces reached equilibrium when the incubation time exceeded 240 min. The pseudo-first order fitting was applied to the adsorption process of FTFM according to Equation (1) presented in Table 2. The values of ln(Qe-Qt) and time are linear fitted and plotted in Figure 6b, where Qe is the experimental equilibrium adsorption capacity whose value is 240 min, and Qt refers to the adsorption capacity when time is t. The coefficient of determination (R 2 ) of the pseudo-first-order fitting is presented in Table 2, ranging from 0.845 to 0.949. The calculated equilibrium adsorption capacity of the pseudo-first-order fitting (Qe1) from the intercept of the linear fitting is illustrated in Table 2, ranging from 0.53 ± 1.223 to 3.55 ± 2.061 mmol/g, significantly lower than the experimental values.
Moreover, the pseudo-second-order fitting of the adsorption process is plotted in Figure 6c according to Equation (2). The value of t/Qt and the adsorption time was linear fitted. The R 2 of the pseudo-second-order fittings for FTFM ranged from 0.991 to 0.998, as presented in Table 2, which was significantly higher than that of the pseudo-first-order fitting. Moreover, the equilibrium adsorption capacity calculated from the slopes by the The adsorption kinetics of FTFM to silver ions were studied. Figure 6 illustrates the relationship between the silver ion adsorption capacity of the thiourea-formaldehyde microspheres and time. The solid thiourea-formaldehyde spheres were able to adsorb silver in aqueous environment, and the capacity increased with the incubation time, which was much lower than that of the flower-like microspheres due to the low specific surface area. The silver ion adsorption capacity of FTFM increased with the raise of the molar ratio between the formaldehyde and the thiourea. The results of the kinetic study were consistent with those of the specific surface area. It was clearly reflected by Figure 6a that the increasing speed of the adsorption capacity slowed down when the adsorption time exceeded 120 min and showed no significant change after 240 min. This indicated that the adsorption and de-adsorption process on the petal surfaces reached equilibrium when the incubation time exceeded 240 min. The pseudo-first order fitting was applied to the adsorption process of FTFM according to Equation (1) presented in Table 2. The values of ln(Q e -Q t ) and time are linear fitted and plotted in Figure 6b, where Q e is the experimental equilibrium adsorption capacity whose value is 240 min, and Q t refers to the adsorption capacity when time is t. The coefficient of determination (R 2 ) of the pseudofirst-order fitting is presented in Table 2, ranging from 0.845 to 0.949. The calculated equilibrium adsorption capacity of the pseudo-first-order fitting (Q e1 ) from the intercept of the linear fitting is illustrated in Table 2, ranging from 0.53 ± 1.223 to 3.55 ± 2.061 mmol/g, significantly lower than the experimental values. i = t/Qt and yi = t/Qe + 1/k2Qe 2 for the pseudo-second-order fitting. The AARD1 and AARD2 were compared by calculating the R(1-2) value according to Equation (4), which is presented in Table 2. The AARD1 ranged from 118.86% to 421.76%, two orders higher than AARD2, which ranged from 1.15% to 3.91%. The R(1-2) values were equal to or greater than 0.99, indicating that the silver ion adsorption of FTFM followed the pseudo-second-order model. Thus, the adsorption process on the FTFM surface was dominated by the chemical chelation, and a single layer of silver was supposed to be generated on the petals after the adsorption.   Moreover, the pseudo-second-order fitting of the adsorption process is plotted in Figure 6c according to Equation (2). The value of t/Q t and the adsorption time was linear fitted. The R 2 of the pseudo-second-order fittings for FTFM ranged from 0.991 to 0.998, as presented in Table 2, which was significantly higher than that of the pseudo-first-order fitting. Moreover, the equilibrium adsorption capacity calculated from the slopes by the pseudo-second-order fitting (Q e2 ) ranged from 1.09 ± 0.012 to 12.61 ± 0.016 mmol/g, which was consistent with the experimental values. However, it was not scientific when only the coefficient of determination and the calculated adsorption capacity were considered in the metal ion adsorption model. In addition, the assessment of data correlation quality (AARD) should be calculated and compared (reference). The AARD was calculated according to Equation (3), whereŷ i = ln(Q e -Q t ) and y i = lnQ e -k 1 t for the pseudo-first-order fitting, and y i = t/Q t and y i = t/Q e + 1/k 2 Q e 2 for the pseudo-second-order fitting. The AARD 1 and AARD 2 were compared by calculating the R (1-2) value according to Equation (4), which is presented in Table 2. The AARD 1 ranged from 118.86% to 421.76%, two orders higher than AARD 2 , which ranged from 1.15% to 3.91%. The R (1)(2) values were equal to or greater than 0.99, indicating that the silver ion adsorption of FTFM followed the pseudo-secondorder model. Thus, the adsorption process on the FTFM surface was dominated by the chemical chelation, and a single layer of silver was supposed to be generated on the petals after the adsorption.
** R (1-2) 2 was calculated to compare the correlation quality between pseudo-first order and pseudo-second-order fitting according to the following equation: The isothermal study of the silver ion adsorption was applied to the FTFM calculating the maximum adsorption capacity (Q max ) for the parallel comparison. As presented by the kinetic study, the adsorption reached equilibrium when the time exceeded 240 min. However, the adsorption capacity at the equilibrium was affected by the initial concentration of AgNO 3 (C 0 ), and the relationship between Q e and C 0 was demonstrated by Figure 7a. The Q e kept increasing with the initial concentration, and the corresponding value for the solid microsphere was significantly lower than that of the flower-like microspheres due to the huge difference in the specific surface area. The Q e of the FTFM samples with different thiourea/formaldehyde molar ratios kept at the same level when the C 0 was 20 and 40 mmol/L, however, changed significantly when C 0 exceeded 60 mmol/L. When the C 0 was 100 mmol/L, the Q e increased significantly with the molar ratio between formaldehyde and thiourea, which was consistent with the structure characterization results. The residual silver ion concentration at the adsorption equilibrium (C e ) was calculated according to the UV vis spectrum. All of the adsorption processes were fitted by the Langmuir adsorption model (Equation (5)). The C e and C e /Q e were linear fitted and presented by Figure 7b. The R 2 of all the FTFM samples was larger than 0.99, and the value for the solid microspheres was 0.959. The fitting results indicated that the silver ion adsorption process presented in this work followed the Langmuir model. The Q max for all of the samples was calculated by the reciprocal of the linear fitting slops demonstrated in Table 3. The Q max of S 2 T 1 F 4 M was only 1.32 ± 0.16 mmol/g, and the corresponding value for FT 1 F 0.5 M was 10.92 ± 0.46 mmol/g, which was around an order higher than that of the solid microspheres. Q max kept increasing with the molar ratio between formaldehyde and thiourea, which was consistent with the BET specific area results. The maximum Q max in this work reached 18.17 ± 1.28 mmol/g for FT 1 F 4 M, which was 13.8 times that of the thiourea-formaldehyde solid microspheres. c e Q e = c e Q max + 1 bQ max (5)    = Q + 1 bQ As shown in Table S1, the Ag + adsorption capacity of FT1F4M prepared in this work was significantly higher than the published works about thiourea-aldehyde Ag + adsorption resin, which are presented in the supplementary section.

Conclusions
Thiourea-formaldehyde resin silver adsorbent with flower-like microspheres micromorphology was prepared and characterized. The silver adsorption capacity was greatly enhanced by the flower-like microsphere structure by increasing the specific areas rather than the chemical formulation optimization. The flower-like microsphere structure was controllable by turning the reaction conditions, and the relationship between the morphology and the adsorption ability was researched. The adsorption kinetic was explored,  As shown in Table S1, the Ag + adsorption capacity of FT 1 F 4 M prepared in this work was significantly higher than the published works about thiourea-aldehyde Ag + adsorption resin, which are presented in the supplementary section.

Conclusions
Thiourea-formaldehyde resin silver adsorbent with flower-like microspheres micromorphology was prepared and characterized. The silver adsorption capacity was greatly enhanced by the flower-like microsphere structure by increasing the specific areas rather than the chemical formulation optimization. The flower-like microsphere structure was controllable by turning the reaction conditions, and the relationship between the morphology and the adsorption ability was researched. The adsorption kinetic was explored, indicating that the adsorption process on the FTFM surface was dominated by the chemical chelation, and a single layer of silver was supposed to be generated on the petals after the adsorption. The results indicated that the specific surface area of FTFM was up to 18.97 m 2 /g, which was 55.8 times than that of the solid microspheres control. The silver ion adsorption ability was greatly enhanced, reaching 7.95 ± 0.396 mmol/g in AgNO 3