Effects of Orientation and Dispersion on Electrical Conductivity and Mechanical Properties of Carbon Nanotube/Polypropylene Composite

The orientation and dispersion of nanoparticles can greatly influence the conductivity and mechanical properties of nanocomposites. In this study, the Polypropylene/ Carbon Nanotubes (PP/CNTs) nanocomposites were produced using three different molding methods, i.e., compression molding (CM), conventional injection molding (IM), and interval injection molding (IntM). Various CNTs content and shear conditions give CNTs different dispersion and orientation states. Then, three electrical percolation thresholds (4 wt.% CM, 6 wt.% IM, and 9 wt.% IntM) were obtained by various CNTs dispersion and orientations. Agglomerate dispersion (Adis), agglomerate orientation (Aori), and molecular orientation (Mori) are used to quantify the CNTs dispersion and orientation degree. IntM uses high shear to break the agglomerates and promote the Aori, Mori, and Adis. Large Aori and Mori can create a path along the flow direction, which lead to an electrical anisotropy of nearly six orders of magnitude in the flow and transverse direction. On the other hand, when CM and IM samples already build the conductive network, IntM can triple the Adis and destroy the network. Moreover, mechanical properties are also been discussed, such as the increase in tensile strength with Aori and Mori but showing independence with Adis. This paper proves that the high dispersion of CNTs agglomerate goes against forming a conductivity network. At the same time, the increased orientation of CNTs causes the electric current to flow only in the orientation direction. It helps to prepare PP/CNTs nanocomposites on demand by understanding the influence of CNTs dispersion and orientation on mechanical and electrical properties.


Introduction
Many theoretical and experimental studies have been done on the effects nanofillers on the mechanical and electrical properties of nanocomposites in the last decade [1][2][3]. Applications using carbon nanotubes (CNTs) as nanofillers have increased [4][5][6][7], such as burning anti-dripping performance, electromagnetic shielding, and sensing element. Polymer blend-based multicomponent nanocomposites with superior mechanical and thermal properties due to the modification of phase morphology have been reported [8]. Although CNTs have good mechanical properties, only a small fraction of their conductivity and strength can translate into the matrix in which CNTs are embedded and twisted [9]. CNTs dispersion and orientation can affect the final performance of nanocomposites, but many related theoretical and experimental results are still controversial.
For example, some researchers show that well-dispersed CNTs are efficiently interconnected and thus decrease the electrical percolation threshold [10][11][12]. Tanabi et al. [13] disperse the CNTs via magnetization and calculate the dispersion state using microscopy images. Results showed that the electric conductivity could be increased significantly with (CM), injection molding (IM), and interval injection molding (IntM). All samples were labeled according to CNTs content and molding method. For example, 2IntM means that the CNTs content was 2 wt.% and was molded using IntM. The central processing conditions were denoted as shown in Table 1. It is worth noting that melt viscosity will rise with increased CNTs content and even changes from a viscous fluid to an elastic solid with high CNTs content [16]. In this research, some samples were molded at a higher melt temperature to improve liquidity. However, if the CNTs content was 9 wt.%, even with higher temperatures, the melt viscosity was still too high to form a secondary flow, so we cannot get the IntM sample with 9 wt.% of CNTs.  CM: Provides a low shear condition (Figure 1a). Plates were compression molded with 1.2 mm thickness at 200 °C. Subsequently, the plate was cut into a dumbbell shape.
IM: Provides a moderate shear condition (Figure 1b). Melt filled the mold chamber under constant pressure. Dumbbell-type samples with 2 mm were prepared using a micro conventional injection molding (SJZS-10A, Wuhan Ruiming Co., Ltd., Wuhan, China) with a mold temperature of 50 °C. A barrel temperature of 200 °C was suitable for most samples, except the 9IM, which needed 210 °C for complete filling due to the high melt viscosity.
IntM: Provides a high shear condition (Figure 1c). The melt filled the mold in two flows. A gradient pressure setting achieved this: The initial injection pressure was too low to fill the cavity. After 1 s of this short shot, the filling was completed by a higher injection pressure. It is worth mentioning that most commercial injection equipment can implement this pressure setting to magnify the shear stress. In this manuscript, IntM samples were  CNTs content (wt.%) 1-6 1-5 6 1- 4 5 First Injection pressure (bar) * 5.5 5.5 2 2 Second Injection pressure (bar) * 5.5 5.5 * Note: Injection pressure is the set pressure of the equipment, not the melt pressure.
CM: Provides a low shear condition (Figure 1a). Plates were compression molded with 1.2 mm thickness at 200 • C. Subsequently, the plate was cut into a dumbbell shape.
IM: Provides a moderate shear condition (Figure 1b). Melt filled the mold chamber under constant pressure. Dumbbell-type samples with 2 mm were prepared using a micro conventional injection molding (SJZS-10A, Wuhan Ruiming Co., Ltd., Wuhan, China) with a mold temperature of 50 • C. A barrel temperature of 200 • C was suitable for most samples, except the 9IM, which needed 210 • C for complete filling due to the high melt viscosity.
IntM: Provides a high shear condition (Figure 1c). The melt filled the mold in two flows. A gradient pressure setting achieved this: The initial injection pressure was too low to fill the cavity. After 1 s of this short shot, the filling was completed by a higher injection pressure. It is worth mentioning that most commercial injection equipment can implement this pressure setting to magnify the shear stress. In this manuscript, IntM samples were also prepared using the micro conventional injection molding (similar to IM). Except for 6IntM, prepared under 210 • C barrel temperature, other samples were molded at 200 • C.

Measurement of Mechanical Properties
The tensile test was conducted at room temperature (26 • C) on an electro-universal testing machine (GOTECH-20KN, GOTECH Testing Machines Co., Ltd., Dongguan, China) with a 50 mm/min cross-head speed. All tests were conducted along the injection direction, and more than five sample properties were calculated.

Measurement of Electrical Conductivity
Electrical conductivity was performed using the Keithley 6487 source meter (Tektronix Inc., Shanghai, China). Both ends of the specimens were coated with conductive silver paint. The electrical conductivity (σ) was then calculated according to the following: L is the distance between the electrodes, R is the measured resistance, and A is the crosssectional area. For IM and IntM samples, the σ was measured along the flow and transverse directions. The values of σ were calculated as the average of four samples.

X-ray Measurements
The synchrotron 2D-WAXD experiment was carried out on a HomeLab (Rigaku, Japan) to calculate the molecular chain orientation (M ori ) of a sample. The dimension of the rectangle-shaped beam was 100 × 100 µm 2 , the light wavelength was 0.154 nm, and the X-rays were imaged after penetrating the sample.
The crystallinity (X c ) was calculated according to the following [22]: where A c and A a are the fitting intensity of the crystallization and amorphous peaks. The orientation of lamellar crystals in the injection-molded parts was calculated using the Hermans orientation function. In this method, the crystal orientation was characterized by the average orientation of the normal to the crystal plane concerning an external reference frame. Accordingly, the flow direction was taken as the reference direction. For a set of hkl planes, the average orientation, which can be expressed as cos 2 ϕ hkl , was calculated mathematically using the following equation [23]: with ϕ being the azimuthal angle and I(ϕ) being the scattered intensity along the angle ϕ.
Herman's orientation function, f, was defined as with f having a value of −0.5 with the normal of the reflection plane being perpendicular to the reference direction (ϕ = 90 • ), a value of 1 with the normal of the refection plane parallel being the reference direction (ϕ = 0 • ), and a value of 0 with the orientation being random. Thin slices cut using microtome were used for optical microscopy observations. The observation zones were along the flow direction (FD) or transverse direction (TD) as shown in Figure 2d. The slice thickness was fixed at 5 µm, and ImageJ was used to process the images after removing the non-clear parts from these images. More than nine microscopy photos for each sample were used to calculate the A dis (CNTs agglomerate dispersion) and A ori (CNTs agglomerate orientation). Moreover, using OM to count toosmall agglomerates can easily lead to errors, so only agglomerates with an area greater than 10 µm 2 were measured. Thin slices cut using microtome were used for optical microscopy observations. The observation zones were along the flow direction (FD) or transverse direction (TD) as shown in Figure 2d. The slice thickness was fixed at 5 µm, and ImageJ was used to process the images after removing the non-clear parts from these images. More than nine microscopy photos for each sample were used to calculate the Adis (CNTs agglomerate dispersion) and Aori (CNTs agglomerate orientation). Moreover, using OM to count too-small agglomerates can easily lead to errors, so only agglomerates with an area greater than 10 µm 2 were measured.

Scanning Electron Microscope (SEM)
A scanning electron microscope (ZEISS Gemini 300, ZEISS Microscopy LLC, Oberkochen, Germany) was used for fracture surface observations. The fracture surface was gold sputtered after being yield stretched.

CNTs Orientation
As shown in Figure 2d, IM and IntM samples were molded into dumbbell-type shapes, and the OM images of 2IM were obtained from both FD and TD. Oriented CNTs agglomerates can be observed in FD, as shown in Figure 2a, a typical three-layer structure is formed. As the name implies, the frozen layer is in contact with the cold mold wall, where polymer melts can be "frozen" instantly and unable to form oriented CNTs agglomerates. Shear layers, as shown in Figure 2a,b, are where a large number of CNTs agglomerates were oriented along the flow direction, while in the core layer, the CNTs agglomerates returned to a spherical form. In contrast, no oriented structure can be found in TD, as shown in Figure 2e,f. It means all CNT agglomerates in 2IM were oriented along FD and perpendicular to TD. So, this research used images captured from FD to calculate agglomerate orientation (Aori), while figures from TD were used to calculate agglomerate dispersion (Adis), in order to avoid the influence of orientation. The specific calculation method will be introduced later.

Scanning Electron Microscope (SEM)
A scanning electron microscope (ZEISS Gemini 300, ZEISS Microscopy LLC, Oberkochen, Germany) was used for fracture surface observations. The fracture surface was gold sputtered after being yield stretched.

CNTs Orientation
As shown in Figure 2d, IM and IntM samples were molded into dumbbell-type shapes, and the OM images of 2IM were obtained from both FD and TD. Oriented CNTs agglomerates can be observed in FD, as shown in Figure 2a, a typical three-layer structure is formed. As the name implies, the frozen layer is in contact with the cold mold wall, where polymer melts can be "frozen" instantly and unable to form oriented CNTs agglomerates. Shear layers, as shown in Figure 2a,b, are where a large number of CNTs agglomerates were oriented along the flow direction, while in the core layer, the CNTs agglomerates returned to a spherical form. In contrast, no oriented structure can be found in TD, as shown in Figure 2e,f. It means all CNT agglomerates in 2IM were oriented along FD and perpendicular to TD. So, this research used images captured from FD to calculate agglomerate orientation (A ori ), while figures from TD were used to calculate agglomerate dispersion (A dis ), in order to avoid the influence of orientation. The specific calculation method will be introduced later.  Figure 3. Shear can change the morphologies of CNTs agglomerates; for example, no oriented structure can be found in 2CM, while both IM and IntM can align CNTs agglomerates. The shear layer thickness of 2IntM was much greater than that of 2IM as shown in Figure 3b,c. As the enlarged images (Figure 3e,f) show some oriented CNTs agglomerates were longer than 100 µm along the flow direction. They were expected to form a conductive path in the flow direction with increased CNTs content, and their effects on mechanical properties will be discussed later. OM images of 2CM, 2IM, and 2IntM in FD are shown in Figure 3. Shear can change the morphologies of CNTs agglomerates; for example, no oriented structure can be found in 2CM, while both IM and IntM can align CNTs agglomerates. The shear layer thickness of 2IntM was much greater than that of 2IM as shown in Figure 3b,c. As the enlarged images (Figure 3e,f) show some oriented CNTs agglomerates were longer than 100 µm along the flow direction. They were expected to form a conductive path in the flow direction with increased CNTs content, and their effects on mechanical properties will be discussed later. The length-diameter ratio of CNTs agglomerate was calculated from OM images for different CNT content and processing methods. If CNTs agglomerate is abstracted into a cylinder, the greater its orientation, the larger the length-diameter ratio will be. So, as shown in Figure 4a, the length-diameter ratio of CNTs agglomerate was calculated and named as Aori. With the help of Image J, more than six OM pictures were used for each sample to calculate Aori. Aori = Llong/Lshort (5) where Llong is the length of the CNTs agglomerate in the longest direction, and Lshort is the length of the CNTs agglomerate in the shortest path. Larger Aori value suggests high agglomerate CNTs orientation.
Because both oriented and non-oriented CNT agglomerates existed in each sample, the Aori variance is significant. As displayed in Figure 4b, the Aori of IntM samples was always larger than that of IM and CM because the secondary flow formed a wider shear layer. In addition, CM-Aori did not equal 1 but remained about 2, because, before compression molding, the CNTs agglomerate had been stretched in the extrusion colling process. This stretched oriented structure can be retained at 200 °C. It is worth noticing that these oriented structures have been cut short and rearranged in CM, so they will not show anisotropy on the macro level. In general, although very low shear existed in the compression molding process, randomly orientated agglomerates remained. It is worth noting that when CNT content is higher than 6 wt.%, some CNTs agglomerates will connect and form a continuous phase (Figure 4d), which can hinder statistics on the shape of individual agglomerates, and Aori loses its value. In this way, if CNTs content was higher than 4 wt.%, Aori could not be used to describe the orientation. The length-diameter ratio of CNTs agglomerate was calculated from OM images for different CNT content and processing methods. If CNTs agglomerate is abstracted into a cylinder, the greater its orientation, the larger the length-diameter ratio will be. So, as shown in Figure 4a, the length-diameter ratio of CNTs agglomerate was calculated and named as A ori . With the help of Image J, more than six OM pictures were used for each sample to calculate A ori .
A ori = L long /L short (5) where L long is the length of the CNTs agglomerate in the longest direction, and L short is the length of the CNTs agglomerate in the shortest path. Larger A ori value suggests high agglomerate CNTs orientation. Because both oriented and non-oriented CNT agglomerates existed in each sample, the A ori variance is significant. As displayed in Figure 4b, the A ori of IntM samples was always larger than that of IM and CM because the secondary flow formed a wider shear layer. In addition, CM-A ori did not equal 1 but remained about 2, because, before compression molding, the CNTs agglomerate had been stretched in the extrusion colling process. This stretched oriented structure can be retained at 200 • C. It is worth noticing that these oriented structures have been cut short and rearranged in CM, so they will not show anisotropy on the macro level. In general, although very low shear existed in the compression molding process, randomly orientated agglomerates remained. It is worth noting that when CNT content is higher than 6 wt.%, some CNTs agglomerates will connect and form a continuous phase (Figure 4d), which can hinder statistics on the shape of individual agglomerates, and A ori loses its value. In this way, if CNTs content was higher than 4 wt.%, A ori could not be used to describe the orientation. Compared with Aori, every sample's molecular chain orientation (Mori) can be explored through the transmission mode of WAXD. Because CNTs flowed with PP during the molding process, Mori can reflect the CNTs orientation, especially for these dispersed CNTs. WAXD images are shown in Figure 5. For CM and IntM samples, such as 2CM, 6CM, 0IntM, 2IntM, and 6IntM, the orientation almost did not change with CNTs content, so only parts of them were selected for WAXD testing. The diffraction ring of CM always presented a complete circle, representing its random orientation structure. In contrast, the IntM sample presented a prominent arc bright spot inside the ring, indicating that it exists in both high orientation and random structure. Correspondingly, IM samples showed some IntM-like diffraction rings, but the orientation rises with increased CNTs content, which will be discussed later. The (040) α plane was calculated to estimate Mori. Figure 6a shows the azimuth angle of the CM, IM, and IntM samples with 2 or 6 wt.% CNTs. CM samples had a very gentle curve, while the peaks, denoted with arrows, indicated high orientation degrees formed using IM and IntM. In Figure 6b, the Mori can be separated into HIGH, MEDIUM, and Compared with A ori , every sample's molecular chain orientation (M ori ) can be explored through the transmission mode of WAXD. Because CNTs flowed with PP during the molding process, M ori can reflect the CNTs orientation, especially for these dispersed CNTs. WAXD images are shown in Figure 5. For CM and IntM samples, such as 2CM, 6CM, 0IntM, 2IntM, and 6IntM, the orientation almost did not change with CNTs content, so only parts of them were selected for WAXD testing. The diffraction ring of CM always presented a complete circle, representing its random orientation structure. In contrast, the IntM sample presented a prominent arc bright spot inside the ring, indicating that it exists in both high orientation and random structure. Correspondingly, IM samples showed some IntM-like diffraction rings, but the orientation rises with increased CNTs content, which will be discussed later.  Compared with Aori, every sample's molecular chain orientation (Mori) can be explored through the transmission mode of WAXD. Because CNTs flowed with PP during the molding process, Mori can reflect the CNTs orientation, especially for these dispersed CNTs. WAXD images are shown in Figure 5. For CM and IntM samples, such as 2CM, 6CM, 0IntM, 2IntM, and 6IntM, the orientation almost did not change with CNTs content, so only parts of them were selected for WAXD testing. The diffraction ring of CM always presented a complete circle, representing its random orientation structure. In contrast, the IntM sample presented a prominent arc bright spot inside the ring, indicating that it exists in both high orientation and random structure. Correspondingly, IM samples showed some IntM-like diffraction rings, but the orientation rises with increased CNTs content, which will be discussed later. The (040) α plane was calculated to estimate Mori. Figure 6a shows the azimuth angle of the CM, IM, and IntM samples with 2 or 6 wt.% CNTs. CM samples had a very gentle curve, while the peaks, denoted with arrows, indicated high orientation degrees formed using IM and IntM. In Figure 6b, the Mori can be separated into HIGH, MEDIUM, and  The (040) α plane was calculated to estimate M ori . Figure 6a shows the azimuth angle of the CM, IM, and IntM samples with 2 or 6 wt.% CNTs. CM samples had a very gentle curve, while the peaks, denoted with arrows, indicated high orientation degrees formed using IM and IntM. In Figure 6b, the M ori can be separated into HIGH, MEDIUM, and LOW areas. The dividing standards are shown in Table 2. When the CNTs content was lower than 6 wt.%, M ori showed a similar trend to A ori as shown in Figure 3: CM, IM and IntM increased in turn.  Table 2. When the CNTs content was lower than 6 wt.%, Mori showed a similar trend to Aori as shown in Figure 3: CM, IM and IntM increased in turn.   For CM samples, the Mori was lower than 0.5, and all were located in the LOW area. In comparison, all the IntM samples Mori were higher than 0.9 and located in the HIGH area. However, for IM samples, the orientation changed with CNTs content. When the CNT content was low, its Mori was located between CM and IntM, which was situated in the MEDIUM region. However, Mori jumped to the HIGH part after the CNT content reached 6 wt.%. Increased Mori attributes to added rigid particles such as CNTs, improve both the storage and the loss modulus, and can help increase the shear area [21,24]. In addition, CNTs not only improved the melt viscosity but also acted as a nucleation site to freeze the oriented molecular chains and form a hybrid shish-kebab structure, which can super improve the mechanical performance [25][26][27]. That is to say, with increased CNTs content, IM can obtain a high shear stress similar to IntM and make Mori greater than 0.91. It is worth mentioning that the 9IM-Mori p slightly because the molding temperature was 10℃ higher than others. The higher melt temperature made it easier for the oriented molecular chains to recover, and in higher CNTs content, the entangled CNTs network also hindered the orientation. Even though the 9IM-Mori was lower than 6IM-Mori, the 9IM-Mori was still located in the high area.

CNTs Dispersion
In order to quantity dispersion degree, we introduce the parameter of CNTs aggerate dispersion (Adis). The number of CNTs aggregates per unit area is used to represent the dispersion. OM Images obtained from TD were used to calculate Adis. Adis is equal to the number of agglomerates within 1 mm 2 , and the Adis can be obtained using Equation (6): where Anumber represents the number of agglomerates, Aarea is the OM images area in µm 2 .
When an aggregate has been completely aggregated into one mass, that is, the dispersion   For CM samples, the M ori was lower than 0.5, and all were located in the LOW area. In comparison, all the IntM samples M ori were higher than 0.9 and located in the HIGH area. However, for IM samples, the orientation changed with CNTs content. When the CNT content was low, its M ori was located between CM and IntM, which was situated in the MEDIUM region. However, M ori jumped to the HIGH part after the CNT content reached 6 wt.%. Increased M ori attributes to added rigid particles such as CNTs, improve both the storage and the loss modulus, and can help increase the shear area [21,24]. In addition, CNTs not only improved the melt viscosity but also acted as a nucleation site to freeze the oriented molecular chains and form a hybrid shish-kebab structure, which can super improve the mechanical performance [25][26][27]. That is to say, with increased CNTs content, IM can obtain a high shear stress similar to IntM and make M ori greater than 0.91. It is worth mentioning that the 9IM-M ori p slightly because the molding temperature was 10°C higher than others. The higher melt temperature made it easier for the oriented molecular chains to recover, and in higher CNTs content, the entangled CNTs network also hindered the orientation. Even though the 9IM-M ori was lower than 6IM-M ori , the 9IM-M ori was still located in the high area.

CNTs Dispersion
In order to quantity dispersion degree, we introduce the parameter of CNTs aggerate dispersion (A dis ). The number of CNTs aggregates per unit area is used to represent the dispersion. OM Images obtained from TD were used to calculate A dis . A dis is equal to the number of agglomerates within 1 mm 2 , and the A dis can be obtained using Equation (6): where A number represents the number of agglomerates, A area is the OM images area in µm 2 .
When an aggregate has been completely aggregated into one mass, that is, the dispersion is the worst, A dis is equal to 1. As the aggregate disperses into particles, A dis will gradually increase. The results of A dis are shown in Figure 7. When the CNTs content was 1 wt.%, the A dis of 1IntM was significantly higher than that of 1CM and 1IM, indicating that the shear formed by secondary flow can further promote the dispersion of CNTs. The large-size CNTs agglomerates can be ruptured by the high shear force, doubling the number of agglomerates per unit area. Other researchers have also reported that CNTs achieved a relatively better distribution when processed under high-shear conditions [16,28]. When CNTs content increased to 2 wt.%, such as 2IntM, about 6000 CNTs agglomerates existing in 1 mm 2 , while for CM samples, the number was relatively small, such as for 2CM which achieved 4000 CNTs agglomerates. It means that the diameter of the CNT agglomerates in CM was larger than IM and IntM, or some adjacent CNTs agglomerates have been interconnected and integrated. The A dis of each sample will reach the maximum value if the CNTs content increases to 4 wt.%.
Polymers 2023, 15, x FOR PEER REVIEW 9 of 15 is the worst, Adis is equal to 1. As the aggregate disperses into particles, Adis will gradually increase. The results of Adis are shown in Figure 7. When the CNTs content was 1 wt.%, the Adis of 1IntM was significantly higher than that of 1CM and 1IM, indicating that the shear formed by secondary flow can further promote the dispersion of CNTs. The largesize CNTs agglomerates can be ruptured by the high shear force, doubling the number of agglomerates per unit area. Other researchers have also reported that CNTs achieved a relatively better distribution when processed under high-shear conditions [16,28]. When CNTs content increased to 2 wt.%, such as 2IntM, about 6000 CNTs agglomerates existing in 1 mm 2 , while for CM samples, the number was relatively small, such as for 2CM which achieved 4000 CNTs agglomerates. It means that the diameter of the CNT agglomerates in CM was larger than IM and IntM, or some adjacent CNTs agglomerates have been interconnected and integrated. The Adis of each sample will reach the maximum value if the CNTs content increases to 4 wt.%. If the CNTs content is increased to 6 wt.%, the Adis of 6IM and 6CM drops to nearly 1200, indicating that the CNTs agglomerates cannot maintain a high dispersion at high CNTs content but combine to form larger agglomerates. Even if the secondary shearing of IntM can promote the distribution of CNTs, the Adis of 6IntM drops to around 3000. When the CNTs content reached 9 wt.%, the Adis of 9CM reduced to 20, and most CNTs were joined together. Meanwhile, although the Adis of 9IM was slightly higher by shearing, the number of agglomerates in 1mm 2 also decreased to 400. The decreased Adis and the formation of a continuous CNTs phase was expected to improve the conductivity, tensile strength, and modulus, which will be discussed in the next section. If the CNTs content is increased to 6 wt.%, the A dis of 6IM and 6CM drops to nearly 1200, indicating that the CNTs agglomerates cannot maintain a high dispersion at high CNTs content but combine to form larger agglomerates. Even if the secondary shearing of IntM can promote the distribution of CNTs, the A dis of 6IntM drops to around 3000. When the CNTs content reached 9 wt.%, the A dis of 9CM reduced to 20, and most CNTs were joined together. Meanwhile, although the A dis of 9IM was slightly higher by shearing, the number of agglomerates in 1mm 2 also decreased to 400. The decreased A dis and the formation of a continuous CNTs phase was expected to improve the conductivity, tensile strength, and modulus, which will be discussed in the next section. Figure 8 shows the relationship between tensile properties and the CNTs content of the samples obtained by different molding methods. These colors are used to divide the three M ori types, which are high, middle, and low. The dividing standards are already shown in Table 2, and the selectivity yield curves are given in support information in Figure S1. Regardless of the content of CNTs, CM, and IntM samples were located in the LOW and HIGH ranges, respectively. In contrast, IM-M ori can leap from Medium to High ranges when CNTs content reaches 6 wt.%. Due to the formation of oriented structures in PP/CNTs nanocomposites under high shear conditions, such as shish-kebab, hybrid shish-kebab, and oriented CNTs, the tensile strength and toughness of the material can be improved. Under the same CNT content, the tensile strength of the IntM sample was always higher than that of IM and CM due to the higher M ori (Figure 8a). The tensile strength of the IntM and CM samples did not change significantly, but the tensile strength of IM samples greatly increased when M ori jumped to HIGH ranges when the CNTs content reached 6 wt.%. This is also due to the massive formation of orientation structure at high M ori . As shown in Figure 8b, with the increased CNTs content, the tensile modulus of all samples showed an increasing trend. It has been proved that CNTs can improve the strength and stiffness of PP at the expense of toughness, because CNTs can induce α-nuclei in PP and increase the crystallinity leading to superior stiffness [29][30][31]. On the other hand, shear can promote the formation of oriented crystals, further improving the modulus. For example, the modulus of 6IntM was higher than that of 6IM and 6CM. In general, within the higher CNTs content, higher M ori always brought a higher strength and modulus [32]. As a result, the tensile strength of 4IntM was 13% higher than that of 0CM, while the tensile modulus of 5IntM was 35% higher than that of 0CM. and HIGH ranges, respectively. In contrast, IM-Mori can leap from Medium to High ranges when CNTs content reaches 6 wt.%. Due to the formation of oriented structures in PP/CNTs nanocomposites under high shear conditions, such as shish-kebab, hybrid shishkebab, and oriented CNTs, the tensile strength and toughness of the material can be improved. Under the same CNT content, the tensile strength of the IntM sample was always higher than that of IM and CM due to the higher Mori (Figure 8a). The tensile strength of the IntM and CM samples did not change significantly, but the tensile strength of IM samples greatly increased when Mori jumped to HIGH ranges when the CNTs content reached 6 wt.%. This is also due to the massive formation of orientation structure at high Mori. As shown in Figure 8b, with the increased CNTs content, the tensile modulus of all samples showed an increasing trend. It has been proved that CNTs can improve the strength and stiffness of PP at the expense of toughness, because CNTs can induce α-nuclei in PP and increase the crystallinity leading to superior stiffness [29][30][31]. On the other hand, shear can promote the formation of oriented crystals, further improving the modulus. For example, the modulus of 6IntM was higher than that of 6IM and 6CM. In general, within the higher CNTs content, higher Mori always brought a higher strength and modulus [32]. As a result, the tensile strength of 4IntM was 13% higher than that of 0CM, while the tensile modulus of 5IntM was 35% higher than that of 0CM.  Figure 9a shows the Low Mori-CNTs agglomerates in the tensile fraction surface, which is smooth and shows many CNTs agglomerates. In the fracture mode, as shown in Figure 9a, the CNTs agglomeration acts as stress concentration points, which is unfavorable for enhancing mechanical properties. Agglomeration can induce the generation of cracks, and the cracks are easy to spread along the interface of the un-oriented agglomerates without damaging CNTs. So, Low Mori-CNTs agglomerates are hard to exert a high mechanical strength [33]. However, cracks cannot bypass the CNTs agglomerates for high Mori products but destroy them. This is due to the CNTs bridge effect which has been highlighted for toughening mechanisms, since CNTs can induce crack propagation and crack deviation to increase fracture toughness [34]. In the destruction process, some CNTs were pulled out of the matrix, and good wettability allowed the PP matrix to be coated on CNTs, thus forming many fibers on the fracture surface, as shown in Figure 9b. This process can prevent the rapid propagation of cracks and improve the tensile strength of the parts.  Figure 9a shows the Low M ori -CNTs agglomerates in the tensile fraction surface, which is smooth and shows many CNTs agglomerates. In the fracture mode, as shown in Figure 9a, the CNTs agglomeration acts as stress concentration points, which is unfavorable for enhancing mechanical properties. Agglomeration can induce the generation of cracks, and the cracks are easy to spread along the interface of the un-oriented agglomerates without damaging CNTs. So, Low M ori -CNTs agglomerates are hard to exert a high mechanical strength [33]. However, cracks cannot bypass the CNTs agglomerates for high M ori products but destroy them. This is due to the CNTs bridge effect which has been highlighted for toughening mechanisms, since CNTs can induce crack propagation and crack deviation to increase fracture toughness [34]. In the destruction process, some CNTs were pulled out of the matrix, and good wettability allowed the PP matrix to be coated on CNTs, thus forming many fibers on the fracture surface, as shown in Figure 9b. This process can prevent the rapid propagation of cracks and improve the tensile strength of the parts.

Orientation Effect on Electrical Conductivity
The electrical conductivity (σ) of various samples were measured in FD and TD directions. As shown in Figure 10a, samples with different Mori values showed different percolation thresholds. That is, the sample conductivity underwent multiple orders of magnitude transitions at a certain CNTs content. For CM samples with low Mori, the percolation threshold was 4 wt.%, while for IM and IntM samples with high Mori, the percolation threshold was 6 wt.% in FD and 9 wt.% in TD, respectively. This phenomenon was also found by other researchers, such as Ameli et al. [35] who studied injection molded PP/CNTs nanocomposite foams, and their results showed low conductivity which was attributed to the one-dimensional oriented CNTs in the flow direction. This is consistent with our previous research conclusions on PP/PA/CNTs blends. When CNTs choose to disperse in the PA phase, although the elongated PA phase holds advantages in terms of its tensile properties, its conductivity network is defective [36]. In general, orientated conductive phases, such as elongated CNTs agglomerates or PA/CNTs phases, are relatively hard to form a conductive path. In addition, a higher orientation brings anisotropy while, at the same time, reducing conductivity. Figure 10b shows the samples anisotropy intensity derived using σFD/σTD. σFD and σTD are the conductivity in FD and TD directions, separately. For 6IM, 6IntM, and 9IM samples, the conductivity in FD was about four or five orders of magnitude higher than that in TD. These samples can be called anisotropic polymer composites, which have recently attracted much attention for their essential applications [37]. In general, a lower orientation helps to improve conductivity and reduce the percolation threshold, while a higher orientation leads to anisotropy.

Orientation Effect on Electrical Conductivity
The electrical conductivity (σ) of various samples were measured in FD and TD directions. As shown in Figure 10a, samples with different M ori values showed different percolation thresholds. That is, the sample conductivity underwent multiple orders of magnitude transitions at a certain CNTs content. For CM samples with low M ori , the percolation threshold was 4 wt.%, while for IM and IntM samples with high M ori , the percolation threshold was 6 wt.% in FD and 9 wt.% in TD, respectively. This phenomenon was also found by other researchers, such as Ameli et al. [35] who studied injection molded PP/CNTs nanocomposite foams, and their results showed low conductivity which was attributed to the one-dimensional oriented CNTs in the flow direction. This is consistent with our previous research conclusions on PP/PA/CNTs blends. When CNTs choose to disperse in the PA phase, although the elongated PA phase holds advantages in terms of its tensile properties, its conductivity network is defective [36]. In general, orientated conductive phases, such as elongated CNTs agglomerates or PA/CNTs phases, are relatively hard to form a conductive path.

Orientation Effect on Electrical Conductivity
The electrical conductivity (σ) of various samples were measured in FD and TD directions. As shown in Figure 10a, samples with different Mori values showed different percolation thresholds. That is, the sample conductivity underwent multiple orders of magnitude transitions at a certain CNTs content. For CM samples with low Mori, the percolation threshold was 4 wt.%, while for IM and IntM samples with high Mori, the percolation threshold was 6 wt.% in FD and 9 wt.% in TD, respectively. This phenomenon was also found by other researchers, such as Ameli et al. [35] who studied injection molded PP/CNTs nanocomposite foams, and their results showed low conductivity which was attributed to the one-dimensional oriented CNTs in the flow direction. This is consistent with our previous research conclusions on PP/PA/CNTs blends. When CNTs choose to disperse in the PA phase, although the elongated PA phase holds advantages in terms of its tensile properties, its conductivity network is defective [36]. In general, orientated conductive phases, such as elongated CNTs agglomerates or PA/CNTs phases, are relatively hard to form a conductive path. In addition, a higher orientation brings anisotropy while, at the same time, reducing conductivity. Figure 10b shows the samples anisotropy intensity derived using σFD/σTD. σFD and σTD are the conductivity in FD and TD directions, separately. For 6IM, 6IntM, and 9IM samples, the conductivity in FD was about four or five orders of magnitude higher than that in TD. These samples can be called anisotropic polymer composites, which have recently attracted much attention for their essential applications [37]. In general, a lower orientation helps to improve conductivity and reduce the percolation threshold, while a higher orientation leads to anisotropy. In addition, a higher orientation brings anisotropy while, at the same time, reducing conductivity. Figure 10b shows the samples anisotropy intensity derived using σ FD /σ TD . σ FD and σ TD are the conductivity in FD and TD directions, separately. For 6IM, 6IntM, and 9IM samples, the conductivity in FD was about four or five orders of magnitude higher than that in TD. These samples can be called anisotropic polymer composites, which have recently attracted much attention for their essential applications [37]. In general, a lower orientation helps to improve conductivity and reduce the percolation threshold, while a higher orientation leads to anisotropy.

Combined Influence by Orientation and Dispersion
To clarify the combined influence of orientation and dispersion, the area of circles has been used to express the electrical conductivity, as shown in Figure 11a. M ori is divided into three levels (LOW, MEDIUM, and HIGH), differentiated using color. When the M ori is LOW, higher conductivity can be obtained even if A dis is high; however, for other samples, the lower the A dis value is, the higher conductivity will be. The lower A dis helps oriented CNTs form a conductive network, while un-oriented CNTs can form a conductivity path regardless of A dis .

Combined Influence by Orientation and Dispersion
To clarify the combined influence of orientation and dispersion, the area of circles has been used to express the electrical conductivity, as shown in Figure 11a. Mori is divided into three levels (LOW, MEDIUM, and HIGH), differentiated using color. When the Mori is LOW, higher conductivity can be obtained even if Adis is high; however, for other samples, the lower the Adis value is, the higher conductivity will be. The lower Adis helps oriented CNTs form a conductive network, while un-oriented CNTs can form a conductivity path regardless of Adis. On the other hand, as shown in Figure 11b, the area of circles can be used to express the yield strength. The tensile strength is highly correlated with Mori and almost unaffected by Adis, meaning high tensile strength can only be obtained in the high Mori region. Meanwhile, the tensile strength shows no change with the increased dispersion degree.
The conductivity of the lower Mori sample is schematically shown in Figure 12a. The agglomerates and dispersive CNTs remained randomly arranged. The electronics can be transferred along the horizontal and vertical directions, which has a high probability of forming a conductive pathway in three-dimensions. Even if the agglomerates do not connect, they can still develop conductive pathways via a physical connection among individual fillers. So, the low-oriented CM sample obtained the lowest percolation threshold at 4 wt.%. However, when Mori was high, as shown in Figure 12b, with the orientated CNTs and CNTs agglomerates, electrons lost their ability to propagate in the vertical direction. The CNTs content must be increased to form a pathway in FD. Correspondingly, in FD, the percolation threshold of highly oriented IM and IntM samples rises to 6 wt.%. In high orientation, the conductive path in TD is the most difficult to form and has the lowest conductivity. In addition, shear provided by the injection molding can improve the CNTs interface and even generate a hybrid shish-kebab. Hence, a layer of PP matrix surrounding CNTs impairs the enhancement of σ [38,39]. Ultimately, the conductive path in TD is formed until Adis is less than 100, which corresponds to the highest percolation threshold of 9 wt.%. On the other hand, as shown in Figure 11b, the area of circles can be used to express the yield strength. The tensile strength is highly correlated with M ori and almost unaffected by A dis , meaning high tensile strength can only be obtained in the high M ori region. Meanwhile, the tensile strength shows no change with the increased dispersion degree.
The conductivity of the lower M ori sample is schematically shown in Figure 12a. The agglomerates and dispersive CNTs remained randomly arranged. The electronics can be transferred along the horizontal and vertical directions, which has a high probability of forming a conductive pathway in three-dimensions. Even if the agglomerates do not connect, they can still develop conductive pathways via a physical connection among individual fillers. So, the low-oriented CM sample obtained the lowest percolation threshold at 4 wt.%. However, when M ori was high, as shown in Figure 12b, with the orientated CNTs and CNTs agglomerates, electrons lost their ability to propagate in the vertical direction. The CNTs content must be increased to form a pathway in FD. Correspondingly, in FD, the percolation threshold of highly oriented IM and IntM samples rises to 6 wt.%. In high orientation, the conductive path in TD is the most difficult to form and has the lowest conductivity. In addition, shear provided by the injection molding can improve the CNTs interface and even generate a hybrid shish-kebab. Hence, a layer of PP matrix surrounding CNTs impairs the enhancement of σ [38,39]. Ultimately, the conductive path in TD is formed until A dis is less than 100, which corresponds to the highest percolation threshold of 9 wt.%. M ori can constrain the effect of A dis on conductivity. For low-oriented products (Figure 12c), the A dis does not affect the conductivity because even at high A dis , there is an opportunity to construct a three-dimensional conductive pathway for randomly distributed CNTs agglomerates. However, for oriented CNTs agglomerates (Figure 12d), high A dis is more likely to destroy their conductive pathways in the flow direction, thus increasing the percolation threshold. Mori can constrain the effect of Adis on conductivity. For low-oriented products ( Figure  12c), the Adis does not affect the conductivity because even at high Adis, there is an opportunity to construct a three-dimensional conductive pathway for randomly distributed CNTs agglomerates. However, for oriented CNTs agglomerates (Figure 12d), high Adis is more likely to destroy their conductive pathways in the flow direction, thus increasing the percolation threshold.

Conclusions
CM, IM, and IntM prepared PP/CNTs composites, which could provide different shear strengths. The dispersion and orientation of CNTs were quantified using Aori (Agglomerate orientation), Mori (Molecular orientation), and Adis (Agglomerate orientation) at both aggregate and molecular chain scales. The results showed that high shear can increase the Aori, Mori and Adis.
Increasing both orientation and CNTs content can increase the tensile strength and modulus by 13% and 35%, respectively, but dispersion degree at the micro level has little effect on the tensile strength. The oriented CNTs can form many fibers at the fracture interface and inhibit crack propagation. Thus, a high orientation results in a high tensile strength and modulus. Increasing CNTs content, the Mori of CM and IntM almost did not change, but Mori of the IM samples realized a transition from medium to high. Meanwhile, the tensile strength and modulus of IM also jumped with Mori. On the other hand, Adis almost does not affect the tensile properties.
Both high orientation and high dispersion are averse to the formation of conductive pathways. Three percolation thresholds of 4, 6, and 9 wt.% can be obtained under three special orientations and dispersion states of CNTs, respectively. The conductivity is affected by both CNTs orientation and dispersion. The conductivity percolation threshold of low Mori samples is 4 wt.%, the CNTs are more likely to form a three-dimensional conductive pathway, and Adis do not affect the conductivity. However, the percolation threshold of high Mori samples in FD is raised to 6 wt.%, and in TD is increased to 9 wt.%. High Mori samples get an anisotropy of nearly six orders of magnitude in FD and TD, which can already be used as anisotropically conductive polymer composites. High Mori samples cannot form a three-dimensional pathway but prioritize creating a pathway in the FD, then forming a pathway in TD with further increased CNTs content. Meanwhile, the value

Conclusions
CM, IM, and IntM prepared PP/CNTs composites, which could provide different shear strengths. The dispersion and orientation of CNTs were quantified using A ori (Agglomerate orientation), M ori (Molecular orientation), and A dis (Agglomerate orientation) at both aggregate and molecular chain scales. The results showed that high shear can increase the A ori , M ori and A dis .
Increasing both orientation and CNTs content can increase the tensile strength and modulus by 13% and 35%, respectively, but dispersion degree at the micro level has little effect on the tensile strength. The oriented CNTs can form many fibers at the fracture interface and inhibit crack propagation. Thus, a high orientation results in a high tensile strength and modulus. Increasing CNTs content, the M ori of CM and IntM almost did not change, but M ori of the IM samples realized a transition from medium to high. Meanwhile, the tensile strength and modulus of IM also jumped with M ori . On the other hand, A dis almost does not affect the tensile properties.
Both high orientation and high dispersion are averse to the formation of conductive pathways. Three percolation thresholds of 4, 6, and 9 wt.% can be obtained under three special orientations and dispersion states of CNTs, respectively. The conductivity is affected by both CNTs orientation and dispersion. The conductivity percolation threshold of low M ori samples is 4 wt.%, the CNTs are more likely to form a three-dimensional conductive pathway, and A dis do not affect the conductivity. However, the percolation threshold of high M ori samples in FD is raised to 6 wt.%, and in TD is increased to 9 wt.%. High M ori samples get an anisotropy of nearly six orders of magnitude in FD and TD, which can already be used as anisotropically conductive polymer composites. High M ori samples cannot form a three-dimensional pathway but prioritize creating a pathway in the FD, then forming a pathway in TD with further increased CNTs content. Meanwhile, the value of A dis is negatively correlated with the conductivity; that is, high conductivity can only be obtained under low CNTs aggregation dispersion.
In general, both high orientation and high dispersion of CNTs agglomerate against the formation of conductive network, while a high orientation can improve the mechanical properties. Data Availability Statement: Some or all data, models, or code generated or used during the study are available from the corresponding author by request.

Conflicts of Interest:
The authors declare no conflict of interest.