Effect of Various Surface Treatments on the Performance of Jute Fibers Filled Natural Rubber (NR) Composites
Previous Article in Journal
PDMS Based Hybrid Sol-Gel Materials for Sensing Applications in Alkaline Environments: Synthesis and Characterization
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 12
Issue 2
10.3390/polym12020370
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Poly(ionic liquid)-Modified Metal Organic Framework for Carbon Dioxide Adsorption

by
Guangyuan Yang
1,2,
Jialin Yu
2,
Sanwen Peng
1,*,
Kuang Sheng
1 and
Haining Zhang
2,*
1
China Tobacco Hubei Industrial Cigarette Materials, LLC, Wuhan 430051, China
2
State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, China
*
Authors to whom correspondence should be addressed.
Polymers 2020, 12(2), 370; https://doi.org/10.3390/polym12020370
Submission received: 22 December 2019 / Revised: 17 January 2020 / Accepted: 1 February 2020 / Published: 7 February 2020
Browse Figures
Versions Notes

Abstract

:
The design and synthesis of solid sorbents for effective carbon dioxide adsorption are essential for practical applications regarding carbon emissions. Herein, we report the synthesis of composite materials consisting of amine-functionalized imidazolium-type poly(ionic liquid) (PIL) and metal organic frameworks (MOFs) through complexation of amino groups and metal ions. The carbon dioxide adsorption behavior of the synthesized composite materials was evaluated using the temperature-programmed desorption (TPD) technique. Benefiting from the large surface area of metal organic frameworks and high carbon dioxide diffusivity in ionic liquid moieties, the carbon dioxide adsorption capacity of the synthesized composite material reached 19.5 cm3·g−1, which is much higher than that of pristine metal organic frameworks (3.1 cm3·g−1) under carbon dioxide partial pressure of 0.2 bar at 25 °C. The results demonstrate that the combination of functionalized poly(ionic liquid) with metal organic frameworks can be a promising solid sorbent for carbon dioxide adsorption.

1. Introduction

The unavoidable emission of CO2 generated by anthropogenic activities is one of the major contributors to the greenhouse effect and the accordingly induced environmental problems, particularly climate change and global warming [1,2,3]. Development of effective CO2 cleansing technologies is thus of great importance. Moreover, CO2 is also an important C1-chemical feedstock in different industrial fields, including chemical engineering, agriculture, and biosystems [4,5]. Capture through adsorption and further conversion of CO2 have become an important direction adopted in both academic and industrial areas.
Adsorption of CO2 by alkaline amine-based solutions is a commercially available technique that is often applied due to its excellent adsorption capacity [6,7]. However, the high volatility and decomposition of the applied alkaline amine and the serious corrosion to scrubbers have limited the practical applications [8,9,10]. Thus, the development of solid sorbents with a reasonable adsorption capacity and stability has become a widely investigated research area [11]. Particularly, amine-functionalized porous materials with a large surface area have been extensively investigated, and literature results have revealed that these materials are promising solid sorbents for CO2 adsorption [12,13,14,15,16,17,18,19,20]. Of the solid porous materials applied for CO2 adsorption, metal organic frameworks (MOFs) have attracted great attention due to their large surface area and the easy process for surface modification as pioneered by Yaghi [21,22,23,24,25,26,27,28] and well described in recently published topic reviews [29,30]. Among the developed MOF materials, Cu3(BTC)2 synthesized from Cu2+ and 1,3,5-benzenetricarboxylic acid (BTC) displays a promising ability for CO2 adsorption due to the large number of unsaturated active sites generated during thermal treatment for interaction with CO2 molecules [31]. The resulting CO2 storage capacity reached about 207 cm3·g−1 at 25.7 bar [31]. In addition, the exposed copper sites make the modification of the formed MOF possible through complexation with electron-rich atoms [32].
It has been reported that imidazolium-type ionic liquids exhibit high efficiency for CO2 capture due to the high solubility of CO2 caused by the formation of imidazolium-carbonate salts [33,34,35,36,37]. However, the dramatically increased viscosity of the reaction system after CO2 adsorption leads to the difficulty of mass transport of CO2 and the subsequent treatment for recycling [38]. This has led researchers’ interests to poly(ionic liquid) (PIL), which exhibits both the unique characteristics of ionic liquids and the physicochemical properties of polymers [39,40,41]. For example, Tang et al. reported that synthesized PIL showed an enhanced CO2 absorption capacity and fast adsorption/desorption rates compared to room-temperature ionic liquids [39].
Inspired by the advantages of MOFs and PIL on CO2 capture, amine-functionalized imidazolium-type PIL-modified Cu3(BTC)2 materials were designed and synthesized through complexation of amino groups on PIL with the exposed active sites of copper ions after thermal treatment. The idea behind this conceptual design was to improve the CO2 adsorption through the interaction of CO2 molecules with copper ions and ionic liquid moieties in addition to the physisorption in micropores of MOFs, and the application of the temperature-programmed desorption (TPD) technique was to differentiate the physisorption and chemisorption of CO2 molecules. The CO2 adsorption behavior of the thus synthesized composite material was evaluated under relatively mild conditions with the CO2 partial pressure of 0.2 bar at 25 °C by using the TPD technique. It is expected that the PIL-modified Cu3(BTC)2 can exhibit an improved CO2 adsorption capacity compared with Cu3(BTC)2 and pure PILs.

2. Materials and Methods

2.1. Materials

1-Vinylimidazole (1-VIm, purity of 99%), 2-bromoethanamine hydrobromide (98%), and 2,2-azobisisobutyronitrile (AIBN) were purchased from Alfa Aesar (MA, US). Prior to use, AIBN was recrystallized from methanol. Triethylamine (>99.5%), copper (II) nitrate hydrate (99%), and 1,3,5-benzenetricarboxylic acid (98%) were received from Aladdin (Shanghai, China). Deionized water with resistivity of 18.2 MΩ·cm−1 was generated from an Ulupure-H ultrapure water generator (Ulup, China). Unless otherwise specified, all the other solvents and reagents were used as received. The Cu3(BTC)2 was synthesized by following the literature [31].

2.2. Synthesis of Monomeric Ionic Liquid (VIm-NH2·HBr)

The monomeric ionic liquid was synthesized according to the literature with slight modification [42]. Briefly, in a two-neck flask, 1-VIm (9.41 g) was dissolved in absolute ethanol (50 mL). After refluxing under protection of argon atmosphere, 2-bromoethanamine hydrobromide (20.50 g) was added to the above solution. The mixture was continuously refluxed for 24 h and the resulting white precipitation was separated by centrifugation, followed by extensive washing with ethanol. The product (26.50 g) was obtained after drying under vacuum at 120 °C for 12 h. 1H NMR (D2O, 298 K, 300 MHz, ppm) δ: 7.92 (s, 1H, N=CH–N), 7.65 (s, 1H, N–CH=C), 7.13 (s, 1H, N–CH=C), 5.84 (dd, 2H, =CH2), 5.46 (dd, 1H, =CH), 4.77 (s, residue water in D2O), 4.58 (d, 1H, =N–CH–), 3.53 (t, 2H, C–CH2–N). FTIR (KBr pallet, cm−1): 3320, 3240, 3095, 3067, 2912, 1628, 1564, 1517, 1488, 1381, 1255, 1210, 1123.

2.3. Synthesis of Poly(ionic liquid) (PIL-NH2)

To a mixed solvent of N,N′-dimethylformamide (25 mL) and deionized water (10 mL), the synthesized VIm-NH2·HBr (3.98 g) and AIBN (4.0 mg) were added to form a homogenous solution. After removal of the dissolved oxygen in the solution by three freeze-thaw cycles, the solution was placed in a thermostat at 80 °C for polymerization and the polymerization time was set to 2 h. After polymerization, the resulting white precipitate was separated by centrifugation and was then dispersed in methanol (10 mL). Excessive triethylamine was added to the above dispersion to remove hydrobromide and the white solid was dissolved rapidly. The products were finally collected by precipitation after addition of ethyl acetate, followed by drying using a lyophilizer.

2.4. Synthesis of PIL-NH2-Modified Cu3(BTC)2 (Denoted as Cu3(BTC)2-PIL-NH2)

A 0.80 g amount of Cu3(BTC)2 was placed in a tube furnace and activated at 250 °C for 2.5 h, during which time the sample’s color turned from blue to purple. The activated sample of Cu3(BTC)2 was subsequently added to a solution of PIL-NHs (2.0 g) in methanol (5.0 mL) under protection of argon and the mixture was continuously stirred at room temperature for 24 h until the color of Cu3(BTC)2 became blue. The final composite product (0.91 g) was obtained after centrifugation and extensive washing with methanol, followed by drying at 70 °C under vacuum for 12 h.

2.5. Characterization

1H nuclear magnetic resonance (1H NMR, Mercury VX-300 spectrometer) was applied to determine the chemical structure of the synthesized monomer using tetramethylsilane as internal standard. Fourier-transform infrared (FTIR) spectra were recorded on a 60SXB spectrometer (Nicolet) in the range of 400–4000 cm−1 with a resolution of 4 cm−1 to qualitatively determine the synthesis of the corresponding products. Thermal stability of the samples was investigated by thermogravimetric analysis (TGA) and differential scan calorimetry (DSC) using an STA449F3 thermal analyzer (Netzsch) under a dynamic heating mode with ramp rate of 10 °C per minute in air over the temperature range of 30–1000 °C. X-ray diffraction (XRD) patterns were recorded from 5° to 70° to determine the crystal structure of Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2 using Cu Kα irradiation sources with wavelength of 1.54 Å. The surface area and the porous structure of the samples were determined by nitrogen adsorption–desorption isotherms on a Micromeritics ASAP 2020 instrument at 77 K in the relative pressure range of 10−8 to 0.998. Prior to the measurements, samples were degassed at 120 °C for 6 h. The Brunauer–Emmett–Teller (BET) model was applied to calculate specific surface area and the Barrett–Joyner–Halenda (BJH) approach was taken to obtain the pore size distribution. X-ray photoelectron spectroscopy (XPS, VG Multilab2000X, Al Kα irradiation source) was applied to determine the elemental composition near the surface of samples.

2.6. CO2 Adsorption

The CO2 adsorption behavior was performed on a TPD apparatus TP-5080 (Tianjin Xianquan, China) using helium as carrier gas. The typical procedure includes pre-adsorption of CO2 at desired temperature under CO2 partial pressure of 0.2 bar, followed by temperature-dependent desorption and finally complete desorption of the adsorbed CO2 molecules at 200 °C. The detailed procedure was described elsewhere [43]. The adsorbed amount of CO2 was calculated from the detected TPD signals of thermal conductivity detector using the software from the supplier.

3. Results

The idea behind the design of the composite materials for CO2 adsorption was to take the advantages of the large surface area of MOF materials and the great CO2 adsorption capacity of amine-functionalized imidazolium-type poly(ionic liquid)s. Thus, the designed amine-functionalized poly(ionic liquid) (PIL-NH2) was first synthesized through simple free-radical polymerization, as illustrated in Figure 1a. The amino groups on the synthesized PIL-NH2 can therefore interact with the exposed copper ions on the preformed metal organic framework through complexation, leading to the modification of Cu3(BTC)2 by poly(ionic liquid), as shown in Figure 1b.
The FTIR spectrum was first recorded to monitor the interaction of Cu3(BTC)2 and poly(ionic liquid), as shown in Figure 2a. For better comparison, the FTIR spectrum of Cu3(BTC)2 was plotted in the same figure. In both FTIR spectra, the characteristic absorption bands for benzene rings from Cu3(BTC)2 can be clearly observed at 1625 and 1571 cm−1 [31]. The absorption bands at 1375 and 1280 cm−1 are assigned to the bending vibration of hydroxy groups of COOH and the stretching vibration of C–O, respectively. Compared to the spectrum of Cu3(BTC)2, two new absorption bands appeared at 3126 and 1163 cm−1 in the FTIR spectrum of Cu3(BTC)2-PIL-NH2 assigned to the stretching vibration of =C–H and the stretching vibration of C–N of the imidazole rings, indicating the successful complex formation [41]. Figure 2b displays the XRD patterns of Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2. It can be seen that the diffraction peaks are very sharp for Cu3(BTC)2, suggesting the great crystallinity. In addition, the position of diffraction peaks agrees well with those reported in the literature [31], indicating that crystallized Cu3(BTC)2 was successfully synthesized. For Cu3(BTC)2-PIL-NH2, diffraction peaks were observed at the same angles of Cu3(BTC)2 with decreased intensity and a new broad diffraction peak appeared at 2θ of 15–30°, revealing the existence of amorphous poly(ionic liquid)s and the partially destroyed crystalline structure of Cu3(BTC)2.
Figure 3 shows XPS results of the synthesized Cu3(BTC)2-PIL-NH2 composite material. The full XPS survey (Figure 3a) clearly suggests the existence of atoms including Cu (781.2 eV for Cu 2p), N (400.8 eV for N 1s), O (531.3 eV for O 1s), C (285.6 eV for C 1s), and Br (67.7 eV for Br 3d), further confirming the formation of composite materials. To evaluate the bonding formation between Cu3(BTC)2 and PIL-NH2, the high-resolution N 1s peak was deconvoluted, as shown in Figure 3b. It can be seen that N atoms in the composite material have four different bonding states with the binding energy centered at 398.28, 398.99, 400.09, and 401.03 eV. It has been reported that the peaks centered at 400.09 and 401.03 eV corresponded to the C–N and C=N bonding on the imidazole rings of ionic liquid moieties [28]. The peaks at 398.28 and 398.99 eV can be therefore assigned to amino groups. It is expected that two types of amino groups exist in the designed composite materials as free amino groups and the bonded amino groups with copper ions. Since the complexation of amino groups with transition metal ions can lead to reduced binding energy, the peak centered at 398.28 should correspond to amino groups interacted with copper ions and the peak centered at 398.99 is related to free amino groups in the composite material.
The porous structure of sorbents has significant influence on their adsorption behavior of gaseous species. Nitrogen adsorption/desorption isotherms were therefore recorded to determine the porous structure of Cu3(BTC)2-PIL-NH2 and Cu3(BTC)2, as shown in Figure 4. It is apparent that Cu3(BTC)2 exhibited the typical Type I isotherms, suggesting the existence of micropores. With the grafting of PILs onto the sample’s surface, the shape of the isotherm changed significantly, particularly under the low relative pressure, suggesting the significant decrease in numbers of micropores due to the blockage of surface-attached polymer chains. The derived porous parameters including surface area, pore volume, and average pore size are listed in Table 1. It can be seen that Cu3(BTC)2 has a surface area of 1352 cm2·g−1 with average pore size of 1.8 nm and pore volume of 0.61 cm3·g−1. However, both surface area and pore volume dramatically decreased to 107 m2·g−1 and 0.12 cm3·g−1, respectively. This could be attributed to the tensive coverage of micropores on Cu3(BTC)2 by the introduced polymer chains. The increased average pore diameter of the sample after complexation with PIL-NH2 is possibly related to slit pores or the formed pores due to accumulation of the PIL-NH2-modified particles.
Since CO2 adsorption was investigated using the temperature-programmed desorption (TPD) technique, the thermal stability of sorbents is one essential parameter to be achieved. Figure 5 shows the TG and DTG curves of Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2. It can be seen that both samples have apparent weight losses under temperatures below 120 °C and under temperatures above 275 °C, corresponding to the release of the physically adsorbed water molecules and the decomposition of organic parts (BTC and PIL), respectively. Compared with Cu3(BTC)2, Cu3(BTC)2-PIL-NH2 exhibits one additional weight loss region between 210 and 275 °C, possibly attributed to the release of structured water molecules that are interacted with N atoms in PIL through hydrogen bonding. It can be thus concluded that the synthesized Cu3(BTC)2-PIL-NH2 is thermally stable at temperatures below 200 °C and the operational temperature for TPD measurements can be set to 200 °C.
The CO2 adsorption behavior was determined by desorption (TPD technique) under the temperature range of 25 to 200 °C of pre-adsorbed CO2 molecules in the samples at 25 °C under CO2 pressure of 0.2 bar for 2 h. The TPD response curves for Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2 are plotted in Figure 6. It is evident that only one desorption peak at about 95 °C was observed for Cu3(BTC)2. The corresponding calculated CO2 adsorption capacity is about 3.09 cm3·g−1. The observed desorption peak can be therefore assigned to the desorption of physically adsorbed CO2 molecules and the adsorbed CO2 molecules through weak interaction with copper ions in Cu3(BTC)2 [31]. For Cu3(BTC)2-PIL-NH2, there are two desorption peaks at about 96 and 200 °C, respectively. Similar to that for Cu3(BTC)2, the desorption peak at 96 °C can be attributed to the release of physically adsorbed CO2 molecules. The physically adsorbed amount is about 2.24 cm3·g−1, smaller than that of Cu3(BTC)2 due to the decreased surface area. It is thus hypothesized that the desorption at temperatures above 100 °C could be attributed to the chemical adsorption of CO2 molecules induced by the presence of PIL-NH2 chains as the release of chemically adsorbed CO2 molecules requires more energy. Since both amino groups and 2-position carbon atoms in the imidazole ring can be chemically interacted with CO2 molecules [36,37,41], the Cu3(BTC)2-PIL-NH2 exhibited a considerably large chemical adsorption capacity of about 17.3 cm3·g−1.

4. Discussion

To validate the hypothesis on the physisorption and chemisorption of CO2 using Cu3(BTC)2-PIL-NH2 as sorbent, the adsorption of CO2 at different temperatures was performed and the same TPD process was applied. The CO2 TPD response curves are displayed in Figure 7. In general, the physisorption capacity of gaseous species decreased with the increase in temperature due to the existing equilibrium of adsorption and desorption, whereas the chemisorption capacity increased with the increase in temperature because of the enhanced reaction kinetics [11,13,21]. It is evident that the peak intensity at temperature of about 95 °C decreased and the peak intensity at about 200 °C increased while the adsorption temperature increased from 10 to 40 °C. The corresponding desorbed amount at 95 °C calculated from TPD curves decreased from 3.4 to 1.4 cm3·g−1 with the increase in adsorption temperature from 10 to 40 °C, suggesting that the desorption at 95 °C resulted from the physically adsorbed CO2. In contrast, the desorbed amount at 200 °C increased from 14.6 to 17.6 cm3·g−1 with the increase in adsorption temperature from 10 to 40 °C, indicating that the desorption at 200 °C resulted from the chemisorption of CO2 molecules through the interaction between CO2 molecules with amino groups and 2-position carbon atoms of imidazolium-type poly(ionic liquid)s. It should be mentioned that the chemically adsorbed amount at 40 °C is only slightly higher than that at 25 °C. The total CO2 adsorption capacity at 25 °C (19.5 cm3·g−1) is higher than that at 40 °C (19.0 cm3·g−1) due to the good physical adsorption. It should also be mentioned that the total CO2 adsorption capacity of Cu3(BTC)2-PIL-NH2 derived from the TPD technique is still quite low for practical applications due to the possibly slow adsorption kinetics and the limitation of the apparatus which cannot be applied at high pressure. It is expected that the CO2 adsorption capacity can be greatly improved with the increase in operational pressures with which physical adsorption of CO2 on porous materials can be significantly enhanced.

5. Conclusions

In summary, anamine-functionalized imidazolium-type poly(ionic liquid)-modified metal organic framework was synthesized as sorbent for carbon dioxide adsorption via complexation of amino groups on polymer chains and metal ions. After modification with functionalized poly(ionic liquid) chains, the surface area of the metal organic framework reduced significantly, leading to a decreased physical adsorption capacity of carbon dioxide molecules. However, the chemical adsorption through interaction of amino groups and 2-position carbon atoms on the imidazolium rings with carbon dioxide dominates the total adsorption capacity under the relatively low carbon dioxide pressure. Moreover, the physisorption and chemisorption of carbon dioxide on the synthesized composite sorbents can be easily identified using the temperature-programmed desorption technique. The results in this work demonstrate that the modification of porous materials with amine-functionalized imidazolium-type poly(ionic liquid)s can be a promising approach in the design and synthesis of model sorbents for efficient carbon dioxide adsorption by improving the physical adsorption kinetics under high pressure.

Author Contributions

Conceptualization, S.P. and H.Z.; methodology, G.Y., J.Y., and K.S.; data curation, K.S.; writing—original draft preparation, G.Y. and J.Y.; writing—review and editing, H.Z.; supervision, S.P. and H.Z. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the Natural Science Foundation of China, grant number 21878239.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Stocker, T.F.; Qin, D.; Plattner, G.K.; Tignor, M.; Allen, S.K.; Boschung, J.; Nauels, A.; Xia, Y.; Bex, V.; Midgley, P.M. Climate change 2013: The physical science basis. In Intergovernmental Panel on Climate Change, Working Group I Contribution to the IPCC Fifth Assessment Report (AR5); Cambridge University Press: New York, NY, USA, 2013. [Google Scholar]
  2. Knudsen, J.N.; Jensen, J.N.; Vilhelmsen, P.J.; Biede, O. Experience with CO2 capture from coal flue gas in pilot-scale: Testing of different amine solvents. Energy Procedia 2009, 1, 783–790. [Google Scholar] [CrossRef] [Green Version]
  3. White, C.M.; Strazisar, B.R.; Granite, E.J.; Hoffmann, J.S.; Pennline, H.W. Separation and capture of CO2 from large stationary sources and sequestration in geological formations—Coalbeds and deep saline aquifers. J. Air Waste Manag. Assoc. 2003, 53, 645–715. [Google Scholar] [CrossRef]
  4. Li, L.; Zhao, N.; Wei, W.; Sun, Y.H. A review of research progress on CO2 capture, storage, and utilization in Chinese Academy of Sciences. Fuel 2013, 108, 112–130. [Google Scholar] [CrossRef]
  5. MacDowell, N.; Florin, N.; Buchard, A.; Hallett, J.; Galindo, A.; Jackson, G.; Adjiman, C.S.; Williams, C.K.; Shah, N.; Fennell, P. An overview of CO2 capture technologies. Energy Environ. Sci. 2010, 3, 1645–1669. [Google Scholar] [CrossRef] [Green Version]
  6. Dutcher, B.; Fan, M.; Russell, A.G. Amine-based CO2 capture technology development from the beginning of 2013-a review. ACS Appl. Mater. Interfaces 2015, 7, 2137–2148. [Google Scholar] [CrossRef]
  7. Sharma, S.D.; Azzi, M. A critical review of existing strategies for emission control in the monoethanolamine-based carbon capture process and some recommendations for improved strategies. Fuel 2014, 212, 178–188. [Google Scholar] [CrossRef]
  8. Rochelle, G.T. Amine scrubbing for CO2 capture. Science 2009, 325, 1652–1654. [Google Scholar] [CrossRef]
  9. Abdelhamid, A.; Heydari-Gorji, A.; Yang, Y. CO2-induced degradation of amine-containing adsorbents: Reaction products and pathways. J. Am. Chem. Soc. 2012, 134, 13834–13842. [Google Scholar]
  10. Dahl, K.H.; Helgesen, L. Safety assessment of emissions from amine-based post combustion CO2-capture. Toxicol. Lett. 2012, 211, S122–S123. [Google Scholar] [CrossRef]
  11. Pera-Titus, M. Porous inorganic membranes for CO2 capture: Present and prospects. Chem. Rev. 2014, 114, 1413–1492. [Google Scholar] [CrossRef]
  12. Knoefel, C.; Martin, C.; Hornebecq, V.; Llewellyn, P.L. Study of carbon dioxide adsorption on mesoporous aminopropylsilane-functionalized silica and titania combining microcalorimetry and in situ infrared spectroscopy. J. Phys. Chem. C 2009, 113, 12726–12734. [Google Scholar] [CrossRef]
  13. Vaidhyanathan, R.; Iremonger, S.S.; Shimizu, G.K.H.; Boyd, P.G.; Alavi, S.; Woo, T.K. Direct observation and quantification of CO2 binding within an amine-functionalized nanoporous solid. Science 2010, 330, 650–653. [Google Scholar] [CrossRef]
  14. Qi, G.; Wang, Y.; Estevez, L.; Duan, X.; Anako, N.; Park, A.H.A.; Li, W.; Jones, C.W.; Giannelis, E.P. High efficiency nanocomposite sorbents for CO2 capture based on amine-functionalized mesoporous capsules. Energy Environ. Sci. 2011, 4, 444–452. [Google Scholar] [CrossRef] [Green Version]
  15. Sculley, J.P.; Zhou, H.C. Enhancing amine-supported materials for ambient air capture. Angew. Chem. Int. Ed. 2012, 51, 12660–12661. [Google Scholar] [CrossRef]
  16. Aquino, C.C.; Richner, G.; Kimling, M.C.; Chen, D.; Puxty, G.; Feron, P.H.M.; Caruso, R.A. Amine-functionalized titania-based porous structures for carbon dioxide postcombustion capture. J. Phys. Chem. C 2013, 117, 9747–9757. [Google Scholar] [CrossRef]
  17. Bali, S.; Leisen, J.; Foo, G.S.; Sievers, C.; Jones, C.W. Aminosilanes grafted to basic alumina as CO2 adsorbents-role of grafting conditions on CO2 adsorption properties. ChemSusChem 2014, 7, 3145–3156. [Google Scholar] [CrossRef]
  18. Linneen, A.N.; Pfeffer, R.; Lin, Y.S. CO2 adsorption performance for amine grafted particulate silica aerogels. Chem. Eng. J. 2014, 254, 190–197. [Google Scholar] [CrossRef]
  19. Liu, Q.; Shi, J.; Wang, Q.; Tao, M.; He, Y.; Shi, Y. Carbon dioxide capture with polyethylenimine-functionalized industrial-grade multiwalled carbon nanotubes. Ind. Eng. Chem. Res. 2014, 53, 17468–17475. [Google Scholar] [CrossRef]
  20. Prenzel, T.; Wilhelm, M.; Rezwan, K. Tailoring amine functionalized hybrid ceramics to control CO2 adsorption. Chem. Eng. J. 2014, 235, 198–206. [Google Scholar] [CrossRef]
  21. Millward, A.R.; Yaghi, O.M. Metal-organic-framework with exceptionally high capacity for storage of carbon dioxide at room temperature. J. Am. Chem. Soc. 2005, 127, 17998–17999. [Google Scholar] [CrossRef]
  22. Furukawa, H.; Ko, N.; Go, Y.N.; Aratani, N.; Choi, S.B.; Choi, E.; Yazaydin, O.; Snurr, O.Q.; O’Keeffe, M.; Kim, J.; et al. Ultrahigh porosity in metal-organic- frameworks. Science 2010, 329, 424–428. [Google Scholar] [CrossRef] [Green Version]
  23. Wang, S.; Yao, W.; Lin, J.; Ding, Z.; Wang, X. Cobalt imidazolate metal-organic frameworks photosplit CO2 under mild reaction conditions. Angew. Chem. Int. Ed. 2014, 53, 1034–1038. [Google Scholar] [CrossRef]
  24. Fracaroli, A.M.; Furukawa, H.; Suzuki, M.; Dodd, M.; Okajima, S.; Gandara, F.; Reimer, J.A.; Yaghi, O.M. Metal-organic frameworks with precisely designed interior for carbon dioxide capture in the presence of water. J. Am. Chem. Soc. 2014, 136, 8863–8866. [Google Scholar] [CrossRef] [Green Version]
  25. Lai, L.S.; Yeong, Y.F.; Ani, A.C.; Lau, K.K.; Shariff, A.M. Effect of synthesis parameters on the formation of zeolitic imidazolate framework 8 (ZIF-8) nanoparticles for CO2 adsorption. Part. Sci. Technol. 2014, 32, 520–528. [Google Scholar] [CrossRef]
  26. Martinez, F.; Sanz, R.; Orcajo, G.; Briones, D.; Yanguez, V. Amino-impregnated MOF materials for CO2 capture at post-combustion conditions. Chem. Eng. Sci. 2016, 142, 55–61. [Google Scholar] [CrossRef]
  27. Qian, X.; Ren, Q.; Wu, X.; Sun, J.; Wu, H.; Lei, J. Enhanced water stability in Zn-doped zeolitic imidazolate framework (ZIF) for CO2 capture applications. ChemsitrySelect 2018, 3, 657–661. [Google Scholar] [CrossRef]
  28. Song, X.; Yu, J.; Wei, M.; Li, R.; Pan, X.; Yang, G.; Tang, H. Ionic liquids-functionalized zeolitic imidazolate framework for carbon dioxide adsorption. Materials 2019, 12, 2361. [Google Scholar] [CrossRef] [Green Version]
  29. Dhakshinamoorthy, I.; Li, Z.; Garcia, H. Catalysis and photocatalysis by metal organic frameworks. Chem. Soc. Rev. 2018, 47, 8134–8172. [Google Scholar] [CrossRef]
  30. Dhakshinamoorthy, I.; Asiri, A.M.; Garcia, H. 2D Metal–Organic Frameworks as Multifunctional Materials in Heterogeneous Catalysis and Electro/Photocatalysis. Adv. Mater. 2019, 31, 201900617. [Google Scholar] [CrossRef]
  31. Thi, T.V.N.; Luu, C.L.; Hoang, T.C.; Nguyen, T.; Bui, T.H.; Nguyen, P.H.D.; Thi, T.P.P. Synthesis of MOF-199 and application to CO2 adsorption. Adv. Nat. Sci. Nanosci. Nanotechnol. 2013, 4, 035016. [Google Scholar]
  32. Demessence, A.; D’Alessandro, D.M.; Foo, M.L.; Long, J.R. Strong CO2 binding in a water-stable, triazolate-bridged metal−organic framework functionalized with ethylenediamine. J. Am. Chem. Soc. 2009, 131, 8784–8786. [Google Scholar] [CrossRef]
  33. Finotello, A.; Bara, J.E.; Camper, D.; Boble, R.D. Room-temperature ionic liquids: Temperature dependence of gas solubility. Ind. Eng. Chem. Res. 2008, 47, 3453–3459. [Google Scholar] [CrossRef]
  34. Condemarin, R.; Scovazzo, P. Gas permeabilities, solubilities, diffusivities, and diffusivity correlations for ammonium-based room temperature ionic liquids with comparison to imidazolium and phosphonium RTIL data. Chem. Eng. J. 2009, 147, 51–57. [Google Scholar] [CrossRef]
  35. Shannon, M.S.; Tedstone, J.M.; Danielsen, S.P.O.; Hindman, M.S.; Irvin, A.C.; Bara, J.E. Free volume as the basis of gas solubility and selectivity in imidazolium-based ionic liquids. Ind. Eng. Chem. Res. 2012, 51, 5565–5576. [Google Scholar] [CrossRef]
  36. Gurau, G.; Rodriguez, H.; Kelley, S.P.; Janiczek, P.; Kalb, R.S.; Rogers, R.D. Demonstration of chemisorption of carbon dioxide in 1,3-dialkylimidazolium acetate ionic liquids. Angew. Chem. Int. Ed. 2011, 50, 12024–12026. [Google Scholar] [CrossRef]
  37. Seo, S.; DeSilva, M.A.; Brennecke, J.F. Physical properties and CO2 reaction pathway of 1-ethyl-3-methylimidazolium ionic liquids with aprotic heterocyclic anions. J. Phys. Chem. B 2014, 118, 14870–14879. [Google Scholar] [CrossRef]
  38. Gutowski, K.E.; Maginn, E.J. Amine-functionalized task-specific ionic liquids: A mechanistic explanation for the dramatic increase in viscosity upon complexation with CO2 from molecular simulation. J. Am. Chem. Soc. 2008, 130, 14690–14704. [Google Scholar] [CrossRef]
  39. Tang, J.; Tang, H.; Sun, W.; Radosz, M.; Shen, Y. Poly(ionic liquid)s as new materials for CO2 absorption. J. Polym. Sci. A Polym. Chem. 2005, 43, 5477–5489. [Google Scholar] [CrossRef]
  40. Magalhaes, T.O.; Aquino, A.S.; Dalla Vecchia, F.; Bernard, F.L.; Seferin, M.; Menezes, S.C.; Ligabue, R.; Einloft, S. Syntheses and characterization of new poly(ionic liquid)s designed for CO2 capture. RSC Adv. 2014, 4, 18164–18170. [Google Scholar] [CrossRef]
  41. Yuan, J.; Fan, M.; Zhang, F.; Xu, Y.; Tang, H.; Huang, C.; Zhang, H. Amine-functionalized poly(ionic liquid) brushes for carbon dioxide adsorption. Chem. Eng. J. 2017, 316, 903–910. [Google Scholar] [CrossRef]
  42. Fang, W.; Luo, Z.; Jiang, J. CO2 capture in poly(ionic liquid) membranes: Atomistic insight into the role of anions. Phys. Chem. Chem. Phys. 2013, 15, 651–658. [Google Scholar] [CrossRef]
  43. Li, N.; Qu, R.; Han, X.; Lin, W.; Zhang, H.; Zhang, Z.J. The counterion effect of imidazolium-type poly(ionic liquid) brushes on carbon dioxide adsorption. ChemPlusChem 2019, 84, 281–288. [Google Scholar] [CrossRef]
Polymers 12 00370 g001 550
Figure 1. (a) Synthesis of amine-functionalized imidazolium-type poly(ionic liquid). (b) Schematic illustration of the synthetic process of composite sorbent of Cu3(BTC)2 and poly(ionic liquid).
Figure 1. (a) Synthesis of amine-functionalized imidazolium-type poly(ionic liquid). (b) Schematic illustration of the synthetic process of composite sorbent of Cu3(BTC)2 and poly(ionic liquid).
Polymers 12 00370 g001
Polymers 12 00370 g002 550
Figure 2. (a) FTIR spectra and (b) XRD patterns of Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2 as indicated in the figure. Dashed lines in the FTIR spectrum are a visual guide.
Figure 2. (a) FTIR spectra and (b) XRD patterns of Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2 as indicated in the figure. Dashed lines in the FTIR spectrum are a visual guide.
Polymers 12 00370 g002
Polymers 12 00370 g003 550
Figure 3. (a) Full XPS survey and (b) high-resolution N 1s XPS spectrum of Cu3(BTC)2-PIL-NH2. The deconvolution results of N 1s peak are also displayed in (b).
Figure 3. (a) Full XPS survey and (b) high-resolution N 1s XPS spectrum of Cu3(BTC)2-PIL-NH2. The deconvolution results of N 1s peak are also displayed in (b).
Polymers 12 00370 g003
Polymers 12 00370 g004 550
Figure 4. Nitrogen adsorption–desorption isotherms for Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2.
Figure 4. Nitrogen adsorption–desorption isotherms for Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2.
Polymers 12 00370 g004
Polymers 12 00370 g005 550
Figure 5. (a) TG (black) and DTG (blue) curves of Cu3(BTC)2. (b) TG (black) and DTG (blue) curves of Cu3(BTC)2-PIL-NH2. The corresponding weight loss values are listed in the figure.
Figure 5. (a) TG (black) and DTG (blue) curves of Cu3(BTC)2. (b) TG (black) and DTG (blue) curves of Cu3(BTC)2-PIL-NH2. The corresponding weight loss values are listed in the figure.
Polymers 12 00370 g005
Polymers 12 00370 g006 550
Figure 6. CO2 TPD response curves for Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2. Red line in the figure refers to the temperature profile for desorption.
Figure 6. CO2 TPD response curves for Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2. Red line in the figure refers to the temperature profile for desorption.
Polymers 12 00370 g006
Polymers 12 00370 g007 550
Figure 7. CO2 TPD response curves of Cu3(BTC)2-PIL-NH2 for pre-adsorption of CO2 at different temperatures. Red line in the figure refers to the temperature profile for desorption.
Figure 7. CO2 TPD response curves of Cu3(BTC)2-PIL-NH2 for pre-adsorption of CO2 at different temperatures. Red line in the figure refers to the temperature profile for desorption.
Polymers 12 00370 g007
Table
Table 1. The derived porous parameters of Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2.
Table 1. The derived porous parameters of Cu3(BTC)2 and Cu3(BTC)2-PIL-NH2.
SamplesSurface Area (m2·g−1)Pore Volume (cm3·g−1)Pore Size (nm)
Cu3(BTC)213520.601.8
Cu3(BTC)2-PIL-NH21070.124.5

Share and Cite

MDPI and ACS Style

Yang, G.; Yu, J.; Peng, S.; Sheng, K.; Zhang, H. Poly(ionic liquid)-Modified Metal Organic Framework for Carbon Dioxide Adsorption. Polymers 2020, 12, 370. https://doi.org/10.3390/polym12020370

AMA Style

Yang G, Yu J, Peng S, Sheng K, Zhang H. Poly(ionic liquid)-Modified Metal Organic Framework for Carbon Dioxide Adsorption. Polymers. 2020; 12(2):370. https://doi.org/10.3390/polym12020370

Chicago/Turabian Style

Yang, Guangyuan, Jialin Yu, Sanwen Peng, Kuang Sheng, and Haining Zhang. 2020. "Poly(ionic liquid)-Modified Metal Organic Framework for Carbon Dioxide Adsorption" Polymers 12, no. 2: 370. https://doi.org/10.3390/polym12020370

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop