Formation of Polyaniline and Polypyrrole Nanocomposites with Embedded Glucose Oxidase and Gold Nanoparticles

Several types of polyaniline (PANI) and polypyrrole (Ppy) nanocomposites with embedded glucose oxidase (GOx) and gold nanoparticles (AuNPs) were formed by enzymatic polymerization of corresponding monomers (aniline and pyrrole) in the presence of 6 and 13 nm diameter colloidal gold nanoparticles (AuNPs(6nm) or AuNPs(13nm), respectively) or chloroaurate ions (AuCl4−). Glucose oxidase in the presence of glucose generated H2O2, which acted as initiator of polymerization reaction. The influence of polymerization bulk composition and pH on the formation of PANI- and Ppy-based nanocomposites was investigated spectrophotometrically. The highest formation rate of PANI- and Ppy-based nanocomposites with embedded glucose oxidase and gold nanoparticles (PANI/AuNPs-GOx and Ppy/AuNPs-GOx, respectively) was observed in the solution of sodium acetate buffer, pH 6.0. It was determined that the presence of AuNPs or AuCl4− ions facilitate enzymatic polymerization of aniline and pyrrole.

Hybrid materials based on CPs containing inorganic nanoparticles (e.g., gold or silver nanoparticles) have unique properties and, therefore, they are promising for the application in electronics, optoelectronics and in bio-devices [12,13,27,[32][33][34][35][36][37]. It was determined that the coordination of heteroatoms are responsible for the heterocycle linkage, because the presence of oxygen or nitrogen increases the adsorption-ability of polymers toward gold nanoparticles (AuNPs) [32]. First Au(III) is able to be reduced into Au(I) form, which can form a nuclei for nanoparticle and only then Au(I) is reduced to the state of zero-valent gold (Au(0)) [36] Au(I) is able to activate inert alkenes and 1,3-dienes and the formation of an Au(I)-diene complex is possible [32]. Similar interaction contributes to the formation of bonding between the gold nanoparticles and the conjugated diene-based moieties of CPs chains [32]. The second reduction step from Au(I) to Au(0) is responsible for the formation of clusters [36]. Therefore, both conducting polymer and AuNPs play a role in the formation of such nanocomposites [36,37]. Oxidized portions of polymer chain are related to an interaction with gold nanoparticles and its oxidative properties. AuNPs are able speed-up the polymerization of monomers [36,37]. Usually polymers/AuNPs-based nanocomposites are formed in the form of insoluble powder.
In this research enzymatic polymerization based formation of polyaniline and polypyrrole nanocomposites with embedded glucose oxidase and gold nanoparticles is described. Polyaniline and polypyrrole based composite formation rate in the presence of different AuNPs, at different pHs of solution was evaluated by UV/Vis spectroscopy.

Materials
Glucose oxidase (EC 1.1.3.4, type VII, from Aspergillus niger, 201 units mg −1 protein) and D-(+)-glucose were purchased from Fluka (Buchs, Switzerland) and Carl Roth GmbH+Co.KG (Karlsruhe, Germany), respectively. Before the investigations glucose solution was allowed to stay overnight for the formation of equilibrium between α and β optical isomers. Tetrachloroauric acid (HAuCl 4 ·3 H 2 O) was obtained from Alfa Aesar GmbH&Co KG (Karlsruhe, Germany), tannic acid -from Carl Roth GmbH + Co (Karlsruhe, Germany) and sodium citrate -from Penta (Praha, Czech Republic). All solutions were prepared using deionized water purified with water purification system Millipore S.A. (Molsheim, France). The solution of sodium acetate (SA) buffer (0.05 mol L −1 CH 3 COONa·3H 2 O) with 0.1 mol L −1 KCl was prepared by mixing of sodium acetate trihydrate and potassium chloride, which were obtained from Reanal (Budapest, Hungary) and Lachema (Neratovice, Czech Republic). Aniline and sodium hydroxide (NaOH) were purchased from Merck KGaA (Darmstadt, Germany), pyrrole -from Acros Organics (New Jersey, NJ, USA) and hydrochloric acid (HCl) -from Sigma-Aldrich (Saint Louis, MO, USA). All chemicals used in experiments were either analytically pure or of highest quality. Polymers were filtered before each measurement through 5 cm column filled by Al 2 O 3 powder to remove coloured components. All solutions were stored between measurements at +4 • C. The synthesis of AuNPs (6nm) and AuNPs (13nm) was performed according to methodology reported previously [38].

The Monitoring of PANI/AuNPs-GOx and Ppy/AuNPs-GOx Synthesis by UV/Vis Spectroscopy
The polymerization course was evaluated by UV/Vis spectroscopy. Optical absorbance of PANI/AuNPs-GOx and Ppy/AuNPs-GOx solutions was monitored by UV/Vis spectrometer Lambda 25 (Shelton, CT, USA) at the wave length range of 233-1000 nm. The investigations were performed at room temperature in plastic disposable cuvettes of 1 cm optical path length by the registration of UV/Vis spectra. After 5-10 minutes after the engagement of polymerization reaction at +20 ± 2 • C optical absorbance of PANI/AuNPs-GOx and Ppy/AuNPs-GOx solutions was registered. SigmaPlot software 12.5 was used to evaluate the data of UV/Vis measurements. The main steps of PANI/AuNPs-GOx and Ppy/AuNPs-GOx nanocomposite formation during enzymatic polymerization are presented in Figure 1.

136
After the mixing of all reagents used for PANI and Ppy formation in the presence of AuNPs(6nm)

138
in the presence of AuCl4 -instead of AuNPs the solution of pyrrole almost instantly becomes

139
intensively black, what is clear evidence of polymerization reaction. As it is seen from Figure 2 after

Results and Discussion
CPs such as polyaniline and polypyrrole are often used in catalysis [10,20] or in bio-electrocatalysis for the immobilization of various biological molecules [1]. There are some expectations that the incorporation of elementary gold into polymers can improve charge transfer from enzymes to the electrode. It is predicted that novel nanocomposites based on AuNPs and CPs could provide various interesting characteristics suitable for their application in biosensorics. Therefore, the main aim of present study was the formation of PANI/AuNPs-GOx and Ppy/AuNPs-GOx nanocomposites with incorporated enzyme-GOx. As it is seen from Figure 1 in the presence of glucose and dissolved oxygen enables GOx to generate lactone of gluconic acid and hydrogen peroxide, which is necessary to initiate pyrrole or aniline polymerization reaction [28].
After the mixing of all reagents used for PANI and Ppy formation in the presence of AuNPs (6nm) and AuNPs (13nm) in SA, pH 6.0, any optical absorbance peaks were registered in vis-spectra. Although, in the presence of AuCl 4 − instead of AuNPs the solution of pyrrole almost instantly becomes intensively black, what is clear evidence of polymerization reaction. As it is seen from Figure 2 after 3 days lasting formation of PANI/AuNPs-GOx and Ppy/AuNPs-GOx nanocomposites in the presence of AuNPs (6nm) , AuNPs (13nm) or HAuCl 4 become brown (in the presence of PANI) and black (in the presence of Ppy) sediments. Such colours are the most characteristic for the delocalised π-electron systems of CPs [28].  into polymerization bulk solution. If polymerization is performed in the presence of AuCl4 -the peak 156 maximum appears at = 450 nm. This fact is an agreement with other researches [13,24,37]. As it was 157 described by other researches the optical absorbance peak at =330 nm appears due to -* transition 158 of the benzenoid ring and another peak at = 440 nm -due to polaron  -transition [13,24]. Results

159
clearly demonstrate that the shift of optical absorption peak maximum depends on the composition 160 of polymerization bulk solution and the duration of polymerization. Optical absorbance at = 330 161 nm is indication of 5,10-dihydrophenazin formation, which is cyclic aniline dimer [21]. -* transition The intensity of colour of synthesized polymers also depends on the pH of initial polymerization bulk solution. The range of tested pHs was between 1.0 and 12. As it is seen from Figure 3A,B,C and 3D the UV/Vis spectra of PANI/AuNPs-GOx nanocomposites after 2-days lasting polymerization exhibit two basic wide peaks at λ = 285 nm and λ = 570 nm if AuNPs (6nm) are added into polymerization bulk solution and only one wide peak at λ = 550 nm appears if AuNPs (13nm) are added into polymerization bulk solution. If polymerization is performed in the presence of AuCl 4 − the peak maximum appears at λ = 450 nm. This fact is an agreement with other researches [13,24,37]. As it was described by other researches the optical absorbance peak at λ = 330 nm appears due to π-π* transition of the benzenoid ring and another peak at λ = 440 nm-due to polaron π-transition [13,24]. Results clearly demonstrate that the shift of optical absorption peak maximum depends on the composition of polymerization bulk solution and the duration of polymerization. Optical absorbance at λ = 330 nm is indication of 5,10-dihydrophenazin formation, which is cyclic aniline dimer [21]. π-π* transition is associated with the delocalization of electrons from benzene rings on nitrogen atoms of aniline [6,21,29]. The further oxidation of 5,10-dihydrophenazine is leading to the formation of phenazylium radical cation with the absorbance maximum at λ = 436 nm. It is due to electron's excitation of benzenoid highest occupied molecular orbital to quinoid lowest unoccupied molecular orbital and indicates the formation of emeraldine forms of PANI [6,13,21,24,29]. The absorbance at 570 nm is indicating the oxidation of E-PANI into P-PANI, according to other researches the optical absorbance peak of PANI-based sample, which consist of up to 50% of E-PANI and/or up to 100% of P-PANI, is in the range from 400 until 800 nm [39].

201
In research performed by another authors it was predicated that aniline in polymerization bulk 202 solution remain mobile and the synthesis of polymers could be proceeded without any enzyme [10]. The wavelength interval of spectra in B is in the range from 320 to 900 nm. Optical absorbance (E) was registered in 0.05 mol L −1 SA buffer, pH 6.0).
As it is seen from spectra presented in Figure 3A,B,C and D at pH values, which are lower than 6.0, PANI/AuNPs-GOx has a weak optical absorbance wave in the range from λ = 442 nm to λ = 570 nm. By the increase of pH value of polymerization solution, the polaron-related peak at λ = 420 nm gradually disappears and a strong absorbance due to excision transition of the quinoid rings at λ = 560-600 nm is emerging. At the same time in strong alkaline polymerization solution optical absorbance at λ = 257 nm and λ = 320 nm, which is observed due to ð-ð* transitions of the benzenoid rings, has increased [10]. The absorbance wave at λ = 442-570 nm and the peak at λ = 450 nm in the presence of AuNPs and AuCl 4 -, respectively, were evaluated to assess the formation of PANI/AuNPs-GOx nanocomposites during the polymerization. Synthesized PANI/AuNPs-GOx nanocomposites were formed in the E-PANI, which has been confirmed by the appearance of brown colour. The influence of pH value of polymerization solution on synthesized PANI/AuNPs-GOx nanocomposites is presented in Figure 3E. It was determined that very low pH value (pH < 1.0) is not suitable for the formation of E-PANI, because H + ions are produced during polymerization reaction. As seen from the presented curves ( Figure 3E), the increase in the pH of the polymerization solution was changed from 2.0 to 6.0 optical absorbance to 0.281 to 0.274 a.u., if AuNPs (6nm) were present in the polymerization solution; and from 0.256 to 0.223 a.u. in the case where AuNPs (13nm) were present in the polymerization solution and from 0.813 to 0.283 a.u. in the case where AuCl 4 − was present in the polymerization solution. Synthesis of some branched polyaniline chains is expected due to polaron transitions, which are reflected in spectra [10]. When the pH of polymerization solution has been increased until pH 12, then the decrease of optical absorbance until 0.096 and 0.605 a.u. was observed for polymerization solution containing AuNPs (6nm) or AuCl 4 − , respectively. When the pH of polymerization solution containing AuNPs (13nm) was equal to pH 10, then optical absorbance decreased until 0.217. In research performed by another authors it was predicated that aniline in polymerization bulk solution remain mobile and the synthesis of polymers could be proceeded without any enzyme [10]. Moreover, during recent our investigations it was observed that auto-polymerization is observed only for polyaniline in the presence of AuCl 4 − in pH range from 2.0 to 12. Meantime, the autopolymerization of PANI in the presence of AuNPs (6nm) and AuNPs (13nm) was observed only in pH ranges from 1.0 until 3.0. The auto-polymerization of aniline in polymerization solution of pH 2.0 with AuNPs (6nm) , AuNPs (13nm) or AuCl 4 − was 1.83, 1.79 and 2.78 times slower than that in polymerization solution with the same gold-based compounds and GOx. For enzymatic formation of PANI/AuNPs-GOx nanocomposites neutral polymerization solution is required due to best enzymatic activity and stability of GOx [9]. The influence of pH value of polymerization solution on optical absorbance during the formation of Ppy/AuNPs-GOx nanocomposites was investigated in the next stage of our investigations. During 2-days lasting enzymatic formation of Ppy/AuNPs-GOx nanocomposites at pH values ranging from 1.0 until 12 in the presence of AuNPs or AuCl 4 − ions were intensively black coloured and solutions above a sediment consisting of aggregated Ppy/AuNPs-GOx become dark green. Dark colour of formed Ppy-based nanocomposites is characterized for advanced π-conjugated system [28]. As it is seen from Figure 4A-C the absorbance was observed for spectra of formed Ppy/AuNPs-GOx nanocomposites at λ = 265 nm, λ = 312-361 nm, λ = 414 nm and λ = 560 nm, what is in an agreement with spectra of chemically synthesized polypyrrole [23,33,34]. The peak at λ = 265 nm is associated with the π-conjugated structure of pyrrole rings, at λ = 312-361 nm and at λ = 414 nm-with π-π* transition of the polypyrrole's chain [23,33,34]. The peak at λ = 560 nm is attributed to a transition from the valence bond to the antibonding polaron-or bipolaron-state and reveals that ultra-small clusters of AuNPs and Ppy are formed [23,33,34]. By the increase of pH value the optical absorbance at λ = 265 nm and λ = 312-361 nm was changed just slightly but at λ = 414 nm and λ = 560 nm changes of optical absorbance were very significant. The absorbance at λ = 414 nm is characteristic for the early stage of pyrrole oxidation.
As it is seen from Figure 4A-C the most rapid increase of optical absorbance was observed in strongly acidic solution at pH 1.0. Therefore this pH can be considered as the most optimal for the formation of Ppy/AuNPs-GOx. But like in the case of polyaniline formation the pH values over 1.0 are not suitable for enzymatic polymerization, because the activity and the stability of GOx at such extreme pHs are not sufficient enough. As it is seen from curves presented in Figure 4D  When polymerization compounds are mixed, then the polymerization of pyrrole and the reduction of AuCl 4 − into Au 0 occurs very quickly and simultaneously darkening of the solution is observed [33].
Similar effect was observed in the polymerization bulk solution containing AuNPs. It should be taken into account that the formation of Ppy is possible in the solution without any chemical oxidant or enzyme [11]. It was determined that auto-polymerization in the presence of AuNPs or AuCl 4 Changes of absorbance during the auto-polymerization were not observed in polymerization bulk solution at pH values in the interval of pH 5.5 and 6.0 and in alkaline medium at pH 8.0, 10 and 12. Hence, it was concluded that the auto-polymerization rate in the absence of GOx is not high when the pH of polymerization solution is higher than 3.0, what is an agreement with another investigations [8].
Enzymatic formation of PANI/AuNPs-GOx and Ppy/AuNPs-GOx depends on source of gold, which was AuNPs (6nm) , AuNPs (13nm) or AuCl 4 − ions. AuNPs are forming seeds for polymerization and AuCl 4 − ions are acting as oxidators, which initiates the polymerization of CPs [40] and forms Au 0 forms AuNPs, which act as seeds for polymerization. In the presence of HAuCl 4 the reduction of AuCl 4 − and the formation of oligoaniline is the dominant reaction in the polymerization bulk solution [13]. The reaction between AuCl 4 − ions and PANI is following by next steps. First of all, polyaniline coordinates Au(III) via an amine N, which is substituting Cl − in AuCl 4 − , because four Cl − anions are released into polymerization solution during PANI formation [13,24]. Then, Au(III) ions by two electrons are oxidizing PANI benzenoid group to quinoid group. Formed AuCl 2 − ion is able to coordinate with an imine N of the quinoid group through electron donation from N to Au and formation of N-H--Cl − type hydrogen bonds, therefore AuCl 4 − ion is taking active and important role in the formation of PANI/AuNPs based nanocomposites [24]. The influence of gold compounds and polymerization rate of polyaniline and polypyrrole nanocomposites formation was investigated in 0.05 mol L −1 sodium acetate buffer, pH 6.0, which was chosen as the most optimal for mentioned gold/polymers enzymatic polymerization. Higher value of optical absorbance of polyaniline was characterized for polymerization solution with AuCl 4 − and achieved 0.674 a.u. (Figure 5). However, in the presence of AuNPs (6nm) and AuNPs (13nm) the polymerization rate of polyaniline formation was very similar and optical absorbance of 0.274 and 0.256 a.u was registered, respectively. In the presence of AuCl 4 − the formation of PANI/AuNPs (AuCl4 − ) -GOx nanocomposites was 2.46 and 2.63 times faster than that in polymerization bulk solution containing AuNPs (6nm) and AuNPs (13nm) . The same influence of gold-based compounds was observed during the polymerization of pyrrole. As it is presented in Figure 5 optical absorbance of Ppy/AuNPs (AuCl4 During control experiments we tested: (i) the polymerization bulk solutions of PANI and Ppy, which did not contain AuNPs and (ii) the solution, which contained glucose, GOx, and AuNPs but did not contain any monomers (aniline or pyrrole), which are required for the formation of polymers. As it is presented in Figure 5 the optical absorbance of PANI/AuNPs (AuCl 4 − ) -GOx and Ppy/AuNPs (AuCl 4 − ) -GOx nanocomposites was 2.14 and 3.52 times higher if compared with that registered for PANI/GOx (0.315 a.u) [9] and Ppy/GOx (0.173 a.u.). The formation rate for PANI/AuNPs (6nm) -GOx and PANI/GOx was very similar; for Ppy/AuNPs (6nm) -GOx was 2.33 times higher than that obtained for Ppy/GOx nanocomposites. The formation rate of PANI/AuNPs-GOx and Ppy/AuNPs-GOx nanocomposites in comparison to that of PANI/GOx and Ppy/GOx is significantly higher, because AuNPs speed-up the agglomeration of formed oligomers and the most probably facilitate polymerization reaction [36,37]. As it was expected any observable composites were formed in the solution containing glucose, GOx and AuNPs in the absence of PANI and Ppy. It means that in enzymatic polymerization at least three compounds (glucose, GOx and aniline or pyrrole) are required for the formation of composite materials. Therefore, for further investigations of PANI/AuNPs-GOx and Ppy/AuNPs-GOx nanocomposites formation AuNPs (6nm) and AuCl 4 − were chosen, which were both considered to be the most suitable for the formation of these aniline-and pyrrole-based nanocomposites [30].
One of the most important parameters of polymerization process is the duration of the polymerization. Thus, the variation of duration of enzymatic polymerization enabled to achieve the optimal polymerization performance. The spectrometric investigation of enzymatic polymerization duration on formation of PANI/AuNPs-GOx and Ppy/AuNPs-GOx nanocomposites was performed in SA buffer, pH 6.0, in the presence of aniline or pyrrole and of AuNPs (6nm) or 0.6 mmol L −1 AuCl 4 − , correspondingly. Visible aggregation of polyaniline and polypyrrole in the presence of AuNPs and AuCl 4 − were observed after 2 and 4.5 days of enzymatic polymerization.
As it is presented in Figure 6A,B one well measurable peak at λ = 450 nm was achieved after 2 and 1 days for PANI/AuNPs (6nm) -GOx and PANI/AuNPs (AuCl 4 − ) -GOx nanocomposites formation. This optical absorbance band appears due to polaron transition from benzenoid group at highest occupied molecular orbital to quinoid group at lowest unoccupied molecular orbital, which indicates presence of emeraldine form of PANI/AuNPs-GOx nanocomposites and is in agreement with results by another authors [13,21,24,27,30].
As it is seen from Figure 6A,B the reduction of colloidal gold and polyaniline was observed until 10 th day of polymerization. It is indicated, that the highest value of optical absorbance for PANI/AuNPs (6nm) -GOx (1.05 a.u.) and PANI/AuNPs (AuCl 4 − ) -GOx (1.24 a.u.) was achieved after 10 days lasting enzymatic polymerization. The value of optical absorbance was 11.1 and 3.17 times higher than that after 5 hours lasing polymerization, respectively for PANI/AuNPs (6nm) -GOx and PANI/AuNPs (AuCl 4 − ) -GOx. Moreover, long polymerization's duration enables to synthesize larger PANI/AuNPs-GOx nanocomposites. Therefore, for the formation of smaller nanocomposites short duration of enzymatic polymerization is recommended. As it is seen from Figure 6C, by the increase of polymerization duration from 5 hours to 5 days in the presence of AuNPs (6nm) and 0.6 mmol L −1 AuCl 4 − optical absorbance at λ = 450 nm increased from 0.095 to 0.517 a.u. and from 0.391 to 1.11 a.u, respectively. The increase of optical absorbance by 5.44 and 2.84 times after 5 days for PANI/AuNPs (6nm) -GOx and PANI/AuNPs (AuCl 4 − ) -GOx formed nanocomposite colloidal solutions was observed. The appearance of this peak in the presence of small nanocomposites in polymerization solution could be explained by fast movement of free electrons to the surface of AuNPs-based nanocomposites, during which electrons are scattered and quickly lose the coherence. In other words, the surface plasmon resonance bandwidth increases by the decrease of AuNPs size [37]. were observed more clearly [11,28,33,34]. The absorbance at this wave length is related to electronic 360 transitions associated with polarons and/or bipolarons [11]. It was concluded that core/shell structure Enzymatic polymerization of pyrrole started very fast and after 5 hours of initiation of polymerization by addition of AuNPs (6nm) or 0.6 mmol L −1 AuCl 4 − to the reactants UV/Vis spectra ( Figure 6D,E) showed two wide waves of an absorbance between λ = 448 nm and λ = 550 nm and between λ = 460 nm and λ = 590 nm, respectively. It was investigated that firstly the absorbance maximum of Ppy/AuNPs (6nm) -GOx and Ppy/AuNPs (AuCl 4 − ) -GOx nanocomposites were achieved at λ = 550 nm and λ = 590 nm, respectively. After one day of enzymatic polymerization, these waves almost disappeared and new bands of π-π* transition of Ppy/AuNPs chain and a polaron transition similar to that of an ordinary Ppy/AuNPs (6nm) -GOx and Ppy/AuNPs (AuCl 4 − ) -GOx at λ = 448 nm and λ = 460 nm were observed more clearly [11,28,33,34]. The absorbance at this wave length is related to electronic transitions associated with polarons and/or bipolarons [11]. It was concluded that core/shell structure of Ppy/AuNPs-GOx nanocomposites was formed. The similar observation was reported by another authors during chemical and electrochemical polymerization of pyrrole [28,33,34]. Figure 6F illustrates that in the presence of AuNPs (6nm) or 0.6 mmol L −1 AuCl 4 − in polymerization bulk solution, a dark pyrrole was relatively rapidly synthesized and optical absorbance of formed nanocomposite colloidal solution, which was measured at two polymerization periods (after 5 h and 10 days) increased from 0.137 to 0.781 a.u. and from 0.159 to 1.05 a.u., respectively. It is seen that optical absorbance, which is characteristic for Ppy/AuNPs (6nm) -GOx and Ppy/AuNPs (AuCl 4 -) -GOx nanocomposites, after 10 days of polymerization was 5.70 and 6.60 times higher than that registered after 5 hours. This indicates the formation of polypyrrole oligomers [11]. From 5 hours until 4.5 days increased the duration of enzymatic formation of Ppy/AuNPs (6nm) -GOx and Ppy/AuNPs (AuCl 4 − ) -GOx nanocomposites has changed optical absorbance of polymerization bulk solution until 0.494 and 0.538 a.u, respectively. It was determined that after 4.5 days of enzymatic polymerization the value of optical absorbance for Ppy/AuNPs (6nm) -GOx and Ppy/AuNPs (AuCl 4 -) -GOx nanocomposites increased by 3.61 and 3.38 times, respectively. The decrease of absorbance value after 12 days of formation of nanocomposites is explained by aggregation of nanocomposites due their limited solubility.

Conclusions
Enzymatic polymerization of aniline and pyrrole monomers in the presence of AuNPs and AuCl 4 − was used to synthesize PANI/AuNPs-GOx and Ppy/AuNPs-GOx nanocomposites. The formation of emeraldine base's form of PANI and conducting Ppy nanocomposites with embedded glucose oxidase and AuNPs was determined by the evaluation of visible spectra, which showed characteristic waves of optical absorbance at λ = 450 nm and λ = 480 nm, respectively. It was determined that 26.0 nmol L −1 of AuNPs (6nm) and 0.6 mmol L −1 of AuCl 4 − are the most suitable for the enzymatic polymerization of PANI-and Ppy-based nanocomposites. The highest rate of PANI/AuNPs-GOx and Ppy/AuNPs-GOx formation was observed in the solution of SA buffer, pH 6.0. The most optimal duration of the enzymatic synthesis of nanocomposites was within 4.5 days. In present our research enzymatically formed nanocomposites are attractive, because any other chemical compounds except glucose, GOx, AuNPs or AuCl 4 − and corresponding monomer (aniline or pyrrole), which forms conducting polymer matrix, are used in the polymerization course.