Glucose/Graphene-Based Aerogels for Gas Adsorption and Electric Double Layer Capacitors

In this study, three-dimensional glucose/graphene-based aerogels (G/GAs) were synthesized using the hydrothermal reduction and CO2 activation method. Graphene oxide (GO) was used as a matrix, and glucose was used as a binder for the orientation of the GO morphology in an aqueous media. We determined that G/GAs exhibited narrow mesopore size distribution, a high surface area (763 m2 g−1), and hierarchical macroporous and mesoporous structures. These features contributed to G/GAs being promising adsorbents for the removal of CO2 (76.5 mg g−1 at 298 K), CH4 (16.8 mg g−1 at 298 K), and H2 (12.1 mg g−1 at 77 K). G/GAs presented excellent electrochemical performance, featuring a high specific capacitance of 305.5 F g−1 at 1 A g−1, and good cyclic stability of 98.5% retention after 10,000 consecutive charge-discharge cycles at 10 A g−1. This study provided an efficient approach for preparing graphene aerogels exhibiting hierarchical porosity for gas adsorption and supercapacitors.


Introduction
Given the excessive consumption of fossil fuel, environmental pollution and the energy crisis have become increasingly prominent. Graphene presents a two-dimensional (2D) macrostructure featuring excellent interfacial properties. Because of its large specific surface area, low density, high electrical conductivity, and high mechanical strength, graphene has been widely used recently for energy and environmental studies. Macroscopic three-dimensional (3D) graphene structures have been obtained by interconnecting 2D graphene sheets that have been successfully synthesized via various methods. In addition to the inherent properties of 2D graphene, 3D graphene structures present large accessible surface areas, excellent mechanical strength and great flexibility because of their porous interconnected network structures [1][2][3][4]. Therefore, 3D graphene is widely studied in the gas adsorption and supercapacitor fields.
To address the environmental and energy issues caused by fossil fuel combustion, researchers have been focusing on developing renewable and clean energy sources. The utilization of H 2 , CH 4 , and other clean energy sources has become an urgent research topic [5]. Hydrogen, one of the most abundant elements in the universe, is an ideal green energy source. It emits no pollutants, and when combusted, it only produces water and heat. Moreover, the sources of hydrogen are very rich, and include solar, nuclear, and water energy. Hydrogen storage methods mainly include high-pressure hydrogen storage, low-temperature liquid hydrogen storage, and solid-state hydrogen storage. Compared with other polymers, such as propylene carbonate, p-phenylenediamine, and polyethyleneimine, were used as binders to crosslink GO when preparing GAs [22,23]. However, obtaining most of these synthetic polymers involved consuming fossil energy, which not only indirectly caused irreversible damage to the environment, but also contributed to the gradual depletion of the petrochemical resources, which led to increasing the scarcity of raw materials. Therefore, developing and utilizing biodegradable polymer materials instead of synthetic ones would be an effective solution. Glucose is the most widely distributed monosaccharide in nature, and it presents good biocompatibility, degradability, and crosslinkability. Therefore, in this study we prepared glucose/graphene-based aerogels (G/GAs) using the hydrothermal reduction method, employing GO and glucose as the framework and the binder, respectively. The effects of the glucose/GO mass ratio on the pore structure and adsorption performance of G/GAs were discussed, and the electrochemical properties of G/GAs were analyzed.

Materials
Nano-graphite powder and glucose were purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China). Potassium permanganate (KMnO 4 ), glacial acetic acid (HAc), sodium hydroxide (NaOH), sodium nitrate (NaNO 3 ), trimethylcarbinol, and ethanol were purchased from Tianjin Chemical Factory (Tianjin, China). All chemicals were of analytical grade (AR) and were used as received. Double-distilled water was used in all experiments.

Preparation of G/GAs
GO was synthesized from natural graphite using the modified Hummer's method [24]. For a typical reaction, 40 mL of 2 mg mL −1 GO suspension was prepared by sonication in water for 2 h. Then, 40 mL glucose solutions of different concentrations (2,4,6,8,10, and 15 mg mL −1 ) were added to the above dispersion under sonication. The obtained solution was then transferred to a 100 mL Teflon-lined stainless steel autoclave and was hydrothermally treated at 453 K for 18 h. Then, the autoclave was naturally cooled to 298 K, and flocculent graphene/glucose hydrogel materials were obtained. The resulting samples were blotted using filter paper to remove the surface-adsorbed water. Trimethylcarbinol was added to the samples, which were again blotted using filter paper to remove the excess solution. The thus-obtained hydrogels were then freeze-dried for 24 h to completely remove the trimethylcarbinol. Finally, the unactivated G/GAs were obtained, and were labeled as H-1, H-2, H-3, H-4, H-5, and H-6. High-temperature activation of G/GAs was performed at a heating rate of 5 K min −1 , flow rate of 166 cm 3 min −1 in N 2 , and by increasing the system temperature to 1073 K while maintaining a 200 cm 3 min −1 CO 2 flow 2 h. The obtained G/GAs were labeled as HA-1, HA-2, HA-3, HA-4, HA-5, and HA-6.

Characterization
The N 2 adsorption-desorption isotherms of the samples were obtained at 77 K using a specific surface porosity analyzer 3H-2000PS2 (BeiShiDe. Co., Beijing, China). The samples were degassed at 473 K for 12 h before measurements. The morphology of G/GAs was investigated using a scanning electron microscopy (SEM, S-4200/Hitachi, Tokyo, Japan) instrument. The XRD pattern and Raman spectra of the samples were obtained using an Aeris (PANalytical, Almelo, The Netherlands) instrument and a LabRAM HR800 (Horiba Jobin Yvon, Paris, France) apparatus, respectively.

CO 2 , CH 4 and H 2 adsorption measurements
Gas adsorption measurements were carried out using a 3H-2000PS2 specific surface porosity analyzer (BeiShiDe. Co., Beijing, China). The CO 2 adsorption isotherms of the samples were obtained using the volumetric method at 298 K in the 0-1 bar pressure range. The CH 4 and H 2 adsorption isotherms of the samples were also obtained using the volumetric method at 298 and 77 K, respectively, in the 0-1 bar pressure range.

Electrochemical measurements
Cyclic voltammetry (CV), galvanostatic charge-discharge (GCD), electro-chemical impedance spectroscopy (EIS) measurements and cyclic stability analysis of HA-2 were carried out on a CHI660E electrochemical station (Shanghai Chenhua, Shanghai, China). All electrochemical measurements were performed in a three-electrode electrochemical cell setup using a platinum electrode as a counter electrode, a saturated calomel electrode as a reference electrode, and a nickel foam electrode (1 mm × 10 mm × 40 mm) coated with 1 mg mixture of HA-2, acetylene black, and poly vinylidene-fluoride binder at an 8:1:1 mass ratio as a working electrode in a 6 M KOH electrolyte solution [19]. The specific capacitance (C s ), energy density (E), and power density (P) of the symmetric device were calculated using the following equations: where I is the current density (A g −1 ), ∆t is the discharge time (s), m is the mass of active material (g), and ∆V is the potential window (V).

Results and Discussion
The experimental procedure for the synthesis of G/GAs is illustrated in Figure 1. The prepared GO nanosheets were uniformly mixed with glucose particles under ultrasonic dispersion. After the hydrothermal reaction and freeze drying process, the lasagna-like unactivated G/GAs were synthesized using graphene nanosheets as matrix and glucose nanoparticles as binder between the layers. The G/GAs presented a spongy hierarchical pore size architecture after CO 2 activation. To observe the surface structure of the prepared samples, SEM images were obtained, and are presented in Figure 2. According to the various sizes of the GO nanosheets (Figure 2a), H-2 presented the relative size in Figure 2b,c. In particular, this layered structure of obtained using glucose as binder to facilitate the inter-connection of graphene sheets exhibited the fluffy formation and certain roughness on the surface of H-2 in Figure 2c. This indicated that the self-connecting cross-linked 3D structure between graphene and glucose ( Figure 2d) with the high mechanical strength could provide more active sites on surface. The framework, which consisted of the matrix and binder was very dense, featured a well-proportioned architecture, and maintained the anthill-like hierarchical pores perfectly.

Electrochemical measurements
Cyclic voltammetry (CV), galvanostatic charge-discharge (GCD), electro-chemical impedance spectroscopy (EIS) measurements and cyclic stability analysis of HA-2 were carried out on a CHI660E electrochemical station (Shanghai Chenhua, Shanghai, China). All electrochemical measurements were performed in a three-electrode electrochemical cell setup using a platinum electrode as a counter electrode, a saturated calomel electrode as a reference electrode, and a nickel foam electrode (1 mm × 10 mm × 40 mm) coated with 1 mg mixture of HA-2, acetylene black, and poly vinylidenefluoride binder at an 8:1:1 mass ratio as a working electrode in a 6 M KOH electrolyte solution [19]. The specific capacitance (Cs), energy density (E), and power density (P) of the symmetric device were calculated using the following equations: where I is the current density (A g −1 ), Δt is the discharge time (s), m is the mass of active material (g), and ΔV is the potential window (V). The experimental procedure for the synthesis of G/GAs is illustrated in Figure 1. The prepared GO nanosheets were uniformly mixed with glucose particles under ultrasonic dispersion. After the hydrothermal reaction and freeze drying process, the lasagna-like unactivated G/GAs were synthesized using graphene nanosheets as matrix and glucose nanoparticles as binder between the layers. The G/GAs presented a spongy hierarchical pore size architecture after CO2 activation. To observe the surface structure of the prepared samples, SEM images were obtained, and are presented in Figure 2. According to the various sizes of the GO nanosheets (Figure 2a), H-2 presented the relative size in Figures 2b, and c. In particular, this layered structure of obtained using glucose as binder to facilitate the inter-connection of graphene sheets exhibited the fluffy formation and certain The integration of the macroporous and mesoporous structures of G/GAs was confirmed using N2 adsorption-desorption measurements. The isotherms in Figure 3a are type II and type IV isotherms, and suggest the occurrence of a multilayer adsorption process on a macroporous solid at relatively high pressures (relative pressure (P/P0) = 0.85-0.95). The adsorption of N2 could not be observed at P/P0 < 0.4, which implied that no micropores were present in these samples. In addition, the relatively narrow hysteresis loop between the adsorption and desorption branches (at P/P0 = 0.4-0.8) suggested a highly uniform pore size and no pore-blocking effects during desorption because of the narrow pores [25]. The curves for all samples were compared and revealed that GO promoted the development of mesoporosity in the samples through glucose reduction at different concentrations. Figure 3b illustrates that the pore size distribution is narrow for all the samples. The Barrett-Joyner-Halenda (BJH) method revealed a narrow distribution of mesopores centered at 2-5 nm and a broad distribution of larger pores centered at 50-90 nm. The number of mesopores approximately 2-5 nm in size decreased gradually as the glucose concentration increased. The mean pore diameter of G/GAs could be finely controlled using the glucose reduction method for preparing mesoporous samples [16]. The integration of the macroporous and mesoporous structures of G/GAs was confirmed using N 2 adsorption-desorption measurements. The isotherms in Figure 3a are type II and type IV isotherms, and suggest the occurrence of a multilayer adsorption process on a macroporous solid at relatively high pressures (relative pressure (P/P 0 ) = 0.85-0.95). The adsorption of N 2 could not be observed at P/P 0 < 0.4, which implied that no micropores were present in these samples. In addition, the relatively narrow hysteresis loop between the adsorption and desorption branches (at P/P 0 = 0.4-0.8) suggested a highly uniform pore size and no pore-blocking effects during desorption because of the narrow pores [25]. The curves for all samples were compared and revealed that GO promoted the development of mesoporosity in the samples through glucose reduction at different concentrations. Figure 3b illustrates that the pore size distribution is narrow for all the samples. The Barrett-Joyner-Halenda (BJH) method revealed a narrow distribution of mesopores centered at 2-5 nm and a broad distribution of larger pores centered at 50-90 nm. The number of mesopores approximately 2-5 nm in size decreased gradually as the glucose concentration increased. The mean pore diameter of G/GAs could be finely controlled using the glucose reduction method for preparing mesoporous samples [16].

Results and Discussion
As illustrated in Table 1, the total pore volume of the samples increased as the mesopore volume increased, which confirmed the hierarchically meso-macroporous structures of the samples. The H-2 sample exhibited superior textural parameters including high specific surface area, large pore volume, and the largest mesopore volume formed by hydrothermal reduction compared to the other analyzed samples. The adsorption performance of the unactivated H-1 G/GAs was higher than that of the H-2 sample because H-1 presented a narrow size distribution of mesopores centered at 3 nm ( Figure 3b) and almost no macropores (Table 1). Therefore, the specific surface areas of all samples in this study mainly consisted of narrow mesopores. Table 2 illustrates that at the high activation temperature of 1073 K, the specific surface area, pore volume, and adsorption capacity increased for all the samples, compared to the unactivated samples, demonstrating that the CO 2 activation method was extremely efficient for improving the surface adsorption properties of G/GAs. We determined that G/GAs presented high specific surface areas of up to 763 m 2 g −1 , good adsorption capacity for CO 2 of 76.5 mg g −1 at 298 K, and the highest adsorption capacities of 16.8 mg g −1 for CH 4 at 298 K and 12.1 mg g −1 for H 2 at 77 K. As illustrated in Table 1, the total pore volume of the samples increased as the mesopore volume increased, which confirmed the hierarchically meso-macroporous structures of the samples. The H-2 sample exhibited superior textural parameters including high specific surface area, large pore volume, and the largest mesopore volume formed by hydrothermal reduction compared to the other analyzed samples. The adsorption performance of the unactivated H-1 G/GAs was higher than that of the H-2 sample because H-1 presented a narrow size distribution of mesopores centered at 3 nm ( Figure 3b) and almost no macropores (Table 1). Therefore, the specific surface areas of all samples in this study mainly consisted of narrow mesopores. Table 2 illustrates that at the high activation temperature of 1073 K, the specific surface area, pore volume, and adsorption capacity increased for all the samples, compared to the unactivated samples, demonstrating that the CO2 activation method was extremely efficient for improving the surface adsorption properties of G/GAs. We determined that G/GAs presented high specific surface areas of up to 763 m 2 g −1 , good adsorption capacity for CO2 of 76.5 mg g −1 at 298 K, and the highest adsorption capacities of 16.8 mg g −1 for CH4 at 298 K and 12.1 mg g −1 for H2 at 77 K. Mesopore volume calculated from N2 sorption isotherms by BJH method. d. Average of pore size distribution by BET method. e. CO2 uptake capacity at 298 K and 1 bar. f.CH4 uptake capacity at 298 K and 1 bar. g. H2 uptake capacity at 77 K and 1 bar.   Raman spectra (Figure 4) presented the typical D-band (1328 cm −1 ) and G-band (1599 cm −1 ), which were attributed to the vibrations of disordered carbon atoms presenting defects and sp 2 hybrid carbon atoms in the 2D hexagonal lattice, respectively. The I D /I G ratios assigned to GO (1.13), H-2 (1.17), and HA-2 (1.13) indicated the high degree of graphitization of GO and its fabricated materials, while demonstrating that G/GAs maintained the intrinsic properties of GO without severe fluctuation. The absence of the 2D-band from the spectra of H-2 and HA-2 indicated the amorphous nature of G/GAs, whereas the appearance of the 2D-band in the spectrum of GO indicated its intrinsic crystallinity [26]. The XRD patterns illustrating the crystalline structures and phases of H-2 and HA-2 are depicted in Figure 5. The prepared materials have been demonstrated to present identical crystalline structure, exhibiting peaks corresponding to the (002) and (422) planes which were attributed to the graphene of the graphite planes, at 2θ of 25.48 • and 44.15 • , respectively. The intensities of the G/GAs peaks in the Raman spectra and XRD patterns were higher after CO 2 activation, which indicated that the CO 2 activation method did not only enhance the specific surface and porosity, but also increased the degree of graphitization of G/GAs [27,28].
which were attributed to the vibrations of disordered carbon atoms presenting defects and sp 2 hybrid carbon atoms in the 2D hexagonal lattice, respectively. The ID/IG ratios assigned to GO (1.13), H-2 (1.17), and HA-2 (1.13) indicated the high degree of graphitization of GO and its fabricated materials, while demonstrating that G/GAs maintained the intrinsic properties of GO without severe fluctuation. The absence of the 2D-band from the spectra of H-2 and HA-2 indicated the amorphous nature of G/GAs, whereas the appearance of the 2D-band in the spectrum of GO indicated its intrinsic crystallinity [26]. The XRD patterns illustrating the crystalline structures and phases of H-2 and HA-2 are depicted in Figure 5. The prepared materials have been demonstrated to present identical crystalline structure, exhibiting peaks corresponding to the (002) and (422) planes which were attributed to the graphene of the graphite planes, at 2θ of 25.48° and 44.15°, respectively. The intensities of the G/GAs peaks in the Raman spectra and XRD patterns were higher after CO2 activation, which indicated that the CO2 activation method did not only enhance the specific surface and porosity, but also increased the degree of graphitization of G/GAs [27,28].   Based on the above results, we proposed a method for manufacturing G/GAs. First, the heat treatment in water constituted the origin of the formation of mesopores (2-5 nm) and macropores (>50 nm). The GO sheets were rich in oxygen-containing groups, such as hydroxyl groups. Upon heating, some of the oxygen-containing groups could be converted into G/GAs, which could escape from the GO sheets and create nanopores between the sheets. Second, glucose as the reducing agent underwent carbonization at high temperatures and reacted with GO to form mesoporous structures [29].
The adsorption capacities were reported as excess uptake in the CO2 and CH4 adsorption isotherms of all samples at two different temperatures (298 and 77 K) under the pressure of 1 bar pressure (Figures 6 and 7, respectively). Recent research has indicated that a large specific surface area and large total pore volume are not decisive factors for high CO2 adsorption capacity, and that the pore size distribution of samples, which was centered at 3 nm, was more effective than others for enhancing CO2 adsorption [22,30]. As can be seen from Figure 6 and Table 2, HA-4 exhibited the Based on the above results, we proposed a method for manufacturing G/GAs. First, the heat treatment in water constituted the origin of the formation of mesopores (2-5 nm) and macropores (>50 nm). The GO sheets were rich in oxygen-containing groups, such as hydroxyl groups. Upon heating, some of the oxygen-containing groups could be converted into G/GAs, which could escape from the GO sheets and create nanopores between the sheets. Second, glucose as the reducing agent underwent carbonization at high temperatures and reacted with GO to form mesoporous structures [29].
The adsorption capacities were reported as excess uptake in the CO 2 and CH 4 adsorption isotherms of all samples at two different temperatures (298 and 77 K) under the pressure of 1 bar pressure (Figures 6 and 7, respectively). Recent research has indicated that a large specific surface area and large total pore volume are not decisive factors for high CO 2 adsorption capacity, and that the pore size distribution of samples, which was centered at 3 nm, was more effective than others for enhancing CO 2 adsorption [22,30]. As can be seen from Figure 6 and Table 2, HA-4 exhibited the highest CO 2 adsorption capacity of 76.5 mg g −1 at 298 K and 1 bar. However, the CO 2 adsorption capacity of HA-2 was very close to it (73.0 mg g −1 ), thus indicating the superiority of the material obtained when 4 mg mL −1 glucose was used in the fabrication process. Masika et al. have synthesized carbon aerogels using resin and metal salt as matrix and template, respectively and obtained materials featuring for CO 2 adsorption capacities in the 44.0-96.8 mg g −1 range [22]. The adsorption capacity of G/GAs for CO 2 was within that range, therefore demonstrating that the adsorption properties of G/GAs were typical for carbon-based aerogels.  Sample HA-2 presented the highest CH4 adsorption capacity of 16.8 mg g −1 at 298 K and 1 bar ( Figure 6). Andrea et al. synthesized carbon aerogels featuring CH4 adsorption capacities in the 9.4-23.9 mg g −1 range, which indicated that G/GAs were good adsorbents for CH4 [31]. However, the adsorption capacity of HA-2 was lower than that of HA-4 at pressures smaller than 0.9 bar, mainly due to the narrow mesoporous structure of the HA-2 sample. Moreover, based on the CO2 and CH4  Sample HA-2 presented the highest CH4 adsorption capacity of 16.8 mg g −1 at 298 K and 1 bar ( Figure 6). Andrea et al. synthesized carbon aerogels featuring CH4 adsorption capacities in the 9.4-23.9 mg g −1 range, which indicated that G/GAs were good adsorbents for CH4 [31]. However, the adsorption capacity of HA-2 was lower than that of HA-4 at pressures smaller than 0.9 bar, mainly due to the narrow mesoporous structure of the HA-2 sample. Moreover, based on the CO2 and CH4 Sample HA-2 presented the highest CH 4 adsorption capacity of 16.8 mg g −1 at 298 K and 1 bar ( Figure 6). Andrea et al. synthesized carbon aerogels featuring CH 4 adsorption capacities in the 9.4-23.9 mg g −1 range, which indicated that G/GAs were good adsorbents for CH 4 [31]. However, the adsorption capacity of HA-2 was lower than that of HA-4 at pressures smaller than 0.9 bar, mainly due to the narrow mesoporous structure of the HA-2 sample. Moreover, based on the CO 2 and CH 4 adsorption isotherms, these adsorbents could also be practical for separating CO 2 /CH 4 gas mixtures. As can be seen from Figures 6 and 7, the adsorption capacity of G/GAs for CO 2 was significantly higher than that for CH 4 . This occurred because G/GAs contain more micropores, and feature a microporous linear structure. From a molecular polarity perspective, CO 2 is a type of non-polar molecule. However, its molecular structure is a quadrupole one featuring a certain degree of polarity, therefore CO 2 is sensitive to the presence of polar groups on solid surfaces. The CH 4 molecule is a type of non-polar molecule presenting spherical symmetry, and its molecular dynamic diameter is larger than that of CO 2 . According to the principle of preferential adsorption of small pore size molecules, the amount of adsorbed CO 2 would be larger than that of CH 4 [32,33].
The H 2 adsorption isotherms of all samples (Figure 8) indicated that the equilibrium amounts of adsorbed H 2 increased as the pressure of the system increased. As the adsorption sites approached saturation, the slopes of the isotherms decreased at higher pressures. The HA-2 sample also presented the highest H 2 uptake of all analyzed samples: 12.1 mg g −1 at 77 K and 1 bar ( Table 2). Although the H 2 uptake value of HA-2 was much lower than the U.S. Department of Energy (DOE) target of 65 mg g −1 (at present, no experimental H 2 storage materials meet the requirements for practical applications set by the U.S. DOE), HA-2 exhibited ultrahigh H 2 adsorption efficiency, as indicated by the uptake per unit specific surface area of 1.14 × 10 −3 wt % m 2 g −1 , which was close to the upper limit of H 2 adsorbed in a monolayer [34]. larger than that of CO2. According to the principle of preferential adsorption of small pore size molecules, the amount of adsorbed CO2 would be larger than that of CH4 [32,33]. The H2 adsorption isotherms of all samples ( Figure 8) indicated that the equilibrium amounts of adsorbed H2 increased as the pressure of the system increased. As the adsorption sites approached saturation, the slopes of the isotherms decreased at higher pressures. The HA-2 sample also presented the highest H2 uptake of all analyzed samples: 12.1 mg g −1 at 77 K and 1 bar ( Table 2). Although the H2 uptake value of HA-2 was much lower than the U.S. Department of Energy (DOE) target of 65 mg g −1 (at present, no experimental H2 storage materials meet the requirements for practical applications set by the U.S. DOE), HA-2 exhibited ultrahigh H2 adsorption efficiency, as indicated by the uptake per unit specific surface area of 1.14 × 10 −3 wt % m 2 g −1 , which was close to the upper limit of H2 adsorbed in a monolayer [34]. The electrochemical properties of HA-2 at different scanning rates were analyzed utilizing via a three-electrode test system using 6 M KOH as an electrolyte. We were able to demonstrate that the CV curves of HA-2 at different scanning rates (Figure 9) did not present any significant redox peaks, and presented the standard features of the typical graphene structure used as an electrode material. As the scan rate was lower than 200 mV s −1 , the rectangular characteristic of the electric double layer energy storage could be maintained, and was much higher than that of conventional graphene-based materials. This indicated that the 3D prepared materials featured good stability, and adding the binder was necessary [35]. The area of the CV curves increased as the scan rate increased, which suggested that G/GAs presented excellent rate capability. Typically, the nanoporous architecture of porous EDLCs electrodes presents short charge transportation distances, thus providing excellent charge transport paths during the charge-discharge process. The electrical double layer can form fast, and it can be quickly and effectively restructured at switching potentials. Moreover, the electrical double layer could subsequently reach a steady state which would result in rectangular-shaped CV curves. This indicated that the charge storage mechanisms of G/GAs resulted from the reversible The electrochemical properties of HA-2 at different scanning rates were analyzed utilizing via a three-electrode test system using 6 M KOH as an electrolyte. We were able to demonstrate that the CV curves of HA-2 at different scanning rates (Figure 9) did not present any significant redox peaks, and presented the standard features of the typical graphene structure used as an electrode material. As the scan rate was lower than 200 mV s −1 , the rectangular characteristic of the electric double layer energy storage could be maintained, and was much higher than that of conventional graphene-based materials. This indicated that the 3D prepared materials featured good stability, and adding the binder was necessary [35]. The area of the CV curves increased as the scan rate increased, which suggested that G/GAs presented excellent rate capability. Typically, the nanoporous architecture of porous EDLCs electrodes presents short charge transportation distances, thus providing excellent charge transport paths during the charge-discharge process. The electrical double layer can form fast, and it can be quickly and effectively restructured at switching potentials. Moreover, the electrical double layer could subsequently reach a steady state which would result in rectangular-shaped CV curves. This indicated that the charge storage mechanisms of G/GAs resulted from the reversible adsorption of the electrolyte ions onto the surface of carbon at the electrolyte/electrode interface. The rectangular like shapes of the present CV curves of G/GAs indicated fast ion transportation, and high ion diffusion rate within the electrode structure and at the electrode/electrolyte interface at various potentials [36,37]. In addition, the CV curves also maintained their rectangular shape at different scan rates, thus demonstrating the good stability of the charge storing process. The linear shape of the GCD curves at different scan rates ( Figure 10) also confirmed the properties of HA-2 as EDLCs. When the voltage was gradually reduced to −1.0 V, the shapes of the GCD curves became concave, indicating high graphitization, which was confirmed by both the XRD patterns and Raman spectra [38,39]. The maximum specific capacitance of 305.5 F g −1 was obtained at 1 A g −1 . In particular, it was observed that the discharging section of the curve was asymmetric compared to the charging one since the discharging time was longer than the charging one. This could be attributed to self-discharging, which usually occurs by redistributing the charges on a porous electrode material at low current densities since the charge storing process in porous carbon electrodes occurs more rapidly on the outer surface of the electrode than in the bulk of the electrode. The linear shape of the GCD curves at different scan rates ( Figure 10) also confirmed the properties of HA-2 as EDLCs. When the voltage was gradually reduced to −1.0 V, the shapes of the GCD curves became concave, indicating high graphitization, which was confirmed by both the XRD patterns and Raman spectra [38,39]. The maximum specific capacitance of 305.5 F g −1 was obtained at 1 A g −1 .
In particular, it was observed that the discharging section of the curve was asymmetric compared to the charging one since the discharging time was longer than the charging one. This could be attributed to self-discharging, which usually occurs by redistributing the charges on a porous electrode material at low current densities since the charge storing process in porous carbon electrodes occurs more rapidly on the outer surface of the electrode than in the bulk of the electrode.
Electrochemical impedance spectroscopy (EIS) is generally utilized for supercapacitor applications as an important electrochemical characterization, because it evaluates the impedance behavior including the resistive and capacitive behaviors, particularly at electrode/electrolyte interfaces [40]. The AC impedance spectrum in Figure 11 demonstrates the reasonably good impedance of HA-2 in the 0.01 Hz to 100 kHz frequency range. To identify the charge transfer behavior of materials using Nyquist plots, an equivalent-circuit diagram was generated for the EIS plot, which helped determine that the related resistance of HA-2 was 12.4 Ω. In the high frequency region, the Nyquist plot of HA-2 presented a well-fitted semicircle, while the low frequency region exhibited good linearity. The line is close to 45 • , which fits the standard of the mixed control between charge transfer and diffusion processes in electrochemical system. To sum up, G/GAs presents good electrochemical properties and stability and can be used as electrode materials for EDLCs [41,42].
The linear shape of the GCD curves at different scan rates ( Figure 10) also confirmed the properties of HA-2 as EDLCs. When the voltage was gradually reduced to −1.0 V, the shapes of the GCD curves became concave, indicating high graphitization, which was confirmed by both the XRD patterns and Raman spectra [38,39]. The maximum specific capacitance of 305.5 F g −1 was obtained at 1 A g −1 . In particular, it was observed that the discharging section of the curve was asymmetric compared to the charging one since the discharging time was longer than the charging one. This could be attributed to self-discharging, which usually occurs by redistributing the charges on a porous electrode material at low current densities since the charge storing process in porous carbon electrodes occurs more rapidly on the outer surface of the electrode than in the bulk of the electrode. To evaluate the stability of G/GAs electrodes, the specific capacitance retention (Figure 12) was repeatedly measured by GCD for 10,000 cycles at 10 A g −1 . It was observed that HA-2 exhibited a capacitance retention of 98.5%, Miao et al. synthesized a magnetic N-doped carbon aerogel featuring a capacity of 185.3 F g −1 and 90.2% capacitance retention after 5000 cycles at 10 A g −1 , which indicated that the prepared G/GAs presented very high cyclic stability, therefore demonstrating that the porous structure of G/GAs was an important factor for efficient ion diffusion [43]. The EDLCs device performances of G/GAs were examined using two HA-2 based electrode as positive and negative electrode for practical application, the results showed the specific capacitance of 135.2 F g −1 , good cycle stability, and increased wettability after 10,000 cycles at 10 A g −1 . In addition, the energy and power densities are also important properties of electrode materials. As displayed in the Ragone plots in Figure 13, the energy density of HA-2 linearly decreases from 42.43 to 2.11 Wh kg −1 for the HA-2 based supercapacitor as the power density increases from 634 to 6333 W kg −1 . These values were much higher than those of graphene-based hybrid electrodes [44], and were very close to those of two other hybrid electrodes reported in the literature [45,46]. However, these other electrodes did not contain added metal oxides, which illustrated that G/GAs could be used in a wider range of practical applications as an electrochemical material. To ensure the EDLCs device performances of the G/GAs based electrode, a symmetrical electrochemical capacitor device based on two G/GAs based electrode, as positive and negative electrodes, was measured in 6 M KOH. The results were showed in Figures S1-S4 (Supporting information).
two other hybrid electrodes reported in the literature [45,46]. However, these other electrodes did not contain added metal oxides, which illustrated that G/GAs could be used in a wider range of practical applications as an electrochemical material. To ensure the EDLCs device performances of the G/GAs based electrode, a symmetrical electrochemical capacitor device based on two G/GAs based electrode, as positive and negative electrodes, was measured in 6 M KOH. The results were showed in Figure  S1-S4 (Supporting information).

Conclusions
Herein, a facile synthesis of glucose/graphene-based G/GAs was obtained showing remarkable gas adsorption capacity and electrochemical performance of EDLCs with higher capacity and better high-rate performance. In this configuration, more micropores with polar groups on the G/GAs surface feature the relative sensitivity for the non-polar molecule CO2, and graphene layers connected by glucose-based spheres with nanopores centered at 3 and 50-90 nm work together to render remarkable absorbability and a high transport rate for electrons. This indicated the potential of G/GAs for applications in removal of CO2 from gas mixtures (such as natural gas, bio-gas, and landfill gas, etc.) by reason of the adsorption selectivity. Further studies toward the development of GAs featuring higher specific surface areas and more promising high electrochemical properties are worth conducting for active sites and high conductivity in the catalyst carrier field.

Conclusions
Herein, a facile synthesis of glucose/graphene-based G/GAs was obtained showing remarkable gas adsorption capacity and electrochemical performance of EDLCs with higher capacity and better high-rate performance. In this configuration, more micropores with polar groups on the G/GAs surface feature the relative sensitivity for the non-polar molecule CO 2 , and graphene layers connected by glucose-based spheres with nanopores centered at 3 and 50-90 nm work together to render remarkable absorbability and a high transport rate for electrons. This indicated the potential of G/GAs for applications in removal of CO 2 from gas mixtures (such as natural gas, bio-gas, and landfill gas, etc.) by reason of the adsorption selectivity. Further studies toward the development of GAs featuring higher specific surface areas and more promising high electrochemical properties are worth conducting for active sites and high conductivity in the catalyst carrier field.