High Performance Soluble Polyimides from Ladder-Type Fluorinated Dianhydride with Polymorphism

A novel rigid semi-alicyclic dianhydride 9,10-difluoro-9,10-bis(trifluoromethyl)-9,10-dihydroanthracene-2,3,6,7-tetracarboxylic acid dianhydride (8FDA) was reported, and its single crystal X-ray diffraction result revealed the existence of the polymorphic structure in this compound. The detail geometric configuration transition during the synthesized process was investigated, exhibiting a transition of from trans- to cis- when the hydroxyl groups were substituted by fluoride with diethylaminosulfur trifluoride (DAST). Compared with the dianhydride 4,4′-(Hexaflouroisopropylidene) diphthalic anhydride (6FDA) and 1S,2R,4S,5R-cyclohexanetetracarboxylic dianhydride (HPMDA), the resulting polyimide (PI) films based on 8FDA exhibited an obviously higher glass transition temperature (Tg, 401 °C) and a much lower coefficient of thermal expansion (CTE, 14 ppm K−1). This indicates that 8FDA is an ideal building block in high-performance soluble PIs with low CTE.


Introduction
Recently, the demand of high-performance transparent polymer substrates increases dramatically with the rapid development of flexible electronics, especially for the flexible OLED displays [1][2][3]. Because of the severe conditions during the TFT fabrication for OLED displays, the ideal flexible transparent substrates require a high T g over 370 • C, a small CTE value lower than 20 ppm K −1 , high transparency, and so on [4]. Due to their outstanding chemical and irradiation resistance, high thermal stability, and excellent optical and mechanical properties, transparent PI films became the best choice for transparent substrates in flexible OLED displays [5][6][7][8][9].
6FDA is a well-known building block for transparent PIs. The sp 3 hybrid quaternary carbon in 6FDA increases the degree of molecular distortions and reduces the conjugation length in the backbone. The steric congestion caused by the CF 3 group disrupts the chain packing and decreases the intermolecular interaction [11,19,26]. Then, the formation of charge-transfer complex (CTC), which will result in a deep yellow color in the PI films, is suppressed, and then the transparency of the PI films is improved [13]. However, the flexibility of 6FDA will lead to a large linear thermal expansion coefficient (CTE) value of about 50 ppm K −1 and a lower T g of less than 350 • C [27]. The introduction of alicyclic segments in the backbone of PIs was another effective method of the synthesis transparent PIs. The 1,2,4,5-cyclohexanetetracarboxylic dianhydride (HPMDA) is widely used to prepare transparent PIs [28,29]. However, the HPMDA-based PI films suffer from high CTE over 50 ppm K −1 and weak antioxidant capacity, and are prone to yellow stain under high temperatures [28,30,31]. So, it is necessary to develop new dianhydride monomers to satisfy the urgent need of flexible OLED displays.
Considering the integrated advantages of 6FDA, and HPMDA that are mentioned above, the low dimension stabilities of PI are derived from alicyclic structure-modified dianhydrides and diamines [28][29][30][32][33][34]. Herein, a rigid semi-alicyclic dianhydride 8FDA was developed to prepare high-performance, transparent PIs. The rigid structure of 8FDA was expected to increase the T g and decrease the CTE at the same time. Additionally, the 1,4-cyclohexadiene segments in 8FDA can break the conjugation of the polymer chain and increase the free volume, which will decrease the charge transfer absorptions and improve the optical properties. The ladder structure of 8FDA will improve the solubility of 8FDA-based PIs. The possible reaction mechanism of 8FDA and the geometric configuration transition processes during the synthesis was investigated in detail. Additionally, the single crystal X-ray diffraction test proved that 8FDA is a novel polymorphic crystal [35].

Instrumentation
IR spectra were recorded on a Perkin Elmer Fourier Transform Infrared spectrometer Perkin Elmer SP one FT-IR (PerkinElmer, Waltham, MA, USA). 1 H NMR, 13 C NMR, and 19 F NMR spectra were measured on a Bruker DRX 600 spectrometer with CDCl 3 and DMSO-d 6 as the solvent and tetramethylsilane as the internal reference. Single crystal diffraction was measured on BRUKER, SMART APEX CCD. The melting points were measured with a microscopic melting point meter SGW-X4. Elemental analyses were carried out on a Perkin-Elmer-240 (11) C, H, N analyzer. Wide-angle X-ray diffraction (WAXD) measurement were performed at 25 • C on a Bede XRD Di system, using graphite-monochromatized Cu-Kα radiation (λ = 0.15405 nm). Ultraviolet visible (UV-vis) spectra of the polymer films were recorded on a Shimadzu UV-visible spectrophotometer UV-2450 (Shimadzu, Kyoto, Japan). Thermogravimetric analysis (TGA) was conducted with Perkin-Elmer TGA-2 in flowing nitrogen at a heating rate of 10 • C min −1 . Dynamic mechanical analysis was conducted with DMA Q800 V20.22 Build 41 using tensile mode at the frequency of 1 Hz. Thermal mechanical analysis (TMA) was characterized through TMA Q400. An Instron universal tester model 1122 (GB/T1040.  was used to study the stress-strain behavior of the PIs film samples at room temperature with a stretching rate of 2.5 mm min −1 , and the data was the average value of five experiments excluding the maximum and the minimum values. Contact angle measurements were carried out using Drop Master 300 Contact AM system (Kyowa Interface Science Co., Saitama, Japan). Atomic force microscope (AFM) images were measured by Veeco Dimension 3100 NanoScope in a tapping mode with Bruker RTESPA-300 probes (Bruker Nano Inc., Karlsruhe, Germany). The refractive indices of the pure polyimide films were measured with a dual rotating-compensator Mueller matrix ellipsometer 38-40 (ME-Lellipsometer, Wuhan Eoptics Technology Co., Ltd., Wuhan, China), and the Cauchy model was used in the tests.

Polymer Preparation
A series of polyimide films was prepared by conventional thermal imidization of 8FDA, 6FDA, and HPMDA with TFDB and TFODA, respectively. For convenience, the PI films derived from 8FDA, 6FDA, and HPMDA are coded as PI-x. The synthesis of the polyimides based on 8FDA, 6FDA, and HPMDA were shown in Scheme 2. The synthesis of PI-4 (6FDA/TFODA) was used as an example to illustrate the general thermal imidized synthetic procedure to prepare the polyimide films. TFODA (1.010 g, 3.004 mmol) was dissolved in 13.11 g dried DMAC in a 50.00 mL flask, and then 6FDA (1.321 g, 2.974 mmol) was added to the solution in one portion. The mixture was stirred at room temperature for 24 h to obtain a viscous poly(amic acid) (PAA) solution. Then, the PAA solution was poured onto a clean glass plate, followed by heating at 80 • C for 1 h for the slow release of the solvent, and sequential heating at 100 • C for 1 h, 150 • C for 1 h, 200 • C for 1 h, 250 • C for 1 h, and 280 • C for 1 h. The PAA was subsequently converted into PI-4 film by thermal imidization process. Then, it was peeled from the glass surface after being soaked in deionized water. IR (cm −1 , film): 1781, 1728 (imide carbonyl asym. and sym. stretching), 1385 (C-N stretching), 1121, and 727 (imide ring deformation). The processing procedure is shown in Figure 1a; FT-IR spectra and photos of PI films are shown in Figure S17.

Monomer Synthesis
8FDA was prepared by a five-step synthesis, as shown in Scheme 1. The isolated yield for the first step reaction was about 30%, which needs to be further improved. For the other steps 2-5, all the isolated yields were higher than 80%. The structure of 8FDA was confirmed via FT-IR; elemental analysis; single-crystal X-ray diffraction; and 1 H, 13 C, and 19 F NMR, as shown in Figures S1-S16. The crystal data was summarized in Table S1. The possible mechanism is depicted in the supporting information and shown in Scheme S1. and 8FDA (6a, 6b, and 6c) The crystal data of all the six compounds are summarized in Table S1. They were crystallized in the triclinic (2), monoclinic (4, 6a, 6b, and 6c) and tetragonal space groups, respectively. In Compounds 2 and 3, their asymmetric units both consisted of one half of their molecules ( Figure S18a,b). Additionally, each complete molecule exists in the asymmetric units of compounds 4, 6b, and 6c ( Figure S18c,e,f). For 6a, there are two independent 8FDA molecules in its asymmetric unit ( Figure S18d). For 6c, two toluene molecules were incorporated into the crystal lattice (Figure S18f)). As the three polymorphs of 8FDA, the dihedral angles between two lateral benzene rings in one molecule (21.1(1)o/24.0(1)o) in 6a are apparently smaller than those in 6b (27.9(1)o) and 6c (26.8(1)o). Thus, the reactivity of 8FDA may be mediated by its various morphologies in the synthesis of PI-1 and PI-2. Except for this, the bond and angle parameters in the parent structures of these six crystals are common to some analogs [35].

Description of Crystal Structure of Compounds 2-4,
As for their crystal packing in compounds 2-4, some weak molecular interactions such as O-H . . . O, C-H . . . π, C-H . . . F, and F . . . F have been observed ( Figures S19-S21). According to the raw materials, the two trifluoromethyl groups in compounds 2-3 are both expectedly residing at the trans conformations. However, in the subsequent compounds 4 and 8FDA (6a-c), they are all surprisingly re-constructed into a cis arrangement via a proposed mechanism (Scheme S1 and vide infra). What is more, the intra-molecular conformation flexibility and inter-molecular interaction characteristics of 8FDA may also illustrate the reaction mechanism to a certain extent.
For compounds 6a and 6b, they are non-solvated, in which the molecules are linked by intermolecular C-H . . . O interactions into one-dimensional structure along the [0 1 0] axis. In 6a it appears as wavy-like shape, and in 6b it looks like more linear (Figure 2a,b). There also exists extensive F . . . F and C-F . . . π interactions. The molecules in 6c are assembled into a two-dimensional layer structure ( Figure S22). Because of the incorporation of toluene, no F . . . F and C-F . . . π interactions were observed. This indicates that 8FDA with different morphologies may react with the specific di-amine to form PI-1 and PI-2 via the assistance of different intermolecular interactions. Further research of the effect of the crystallization process such as temperature and solvent on the morphologies of 8FDA and its reactivity will be carried out by us in the near future.

The Solubility and WAXD of the Polyimide Films
The solubility of the PI films was tested in various solvents, and the results are summarized in Table 1. Most of the PI films were soluble in typical polar solvents such as N,N-dimethylacetamide (DMAC) and N-methyl-2-pyrrodidon (NMP) at room temperature. The data listed in Table 1 demonstrates that the solubility of films derived from 8FDA is as good as 6FDA and HPMDA for given diamines. It can be explained that the rigid 8FDA monomer owned more linear, semi-alicyclic structures and CF3 groups, which disrupted the chain packing and reduced the interchain interaction. It also reduced the crystallinity and endowed good solubility. It is reported that [27,36] highly organo-soluble PI films include some solubility promoting groups (e.g., CF3, -O-, and flexible groups) [37,38]. These segments would hinder polymer-polymer interaction, and thus disrupt the chain packing, prevent crystallization, and improve solubility.
Further evidence could be obtained from the wide angle X-ray diffraction (WAXD) measurement. The average inter-chain spacing distance (d-spacing) was calculated from the most prominent WAXD peak in the glassy amorphous polymer spectra based on Bragg's equation: 2dsinθ = nλ (n = 1, λ = 1.54 Å ) [15]. From Figure 2b, it was observed that all of the films presented amorphous states. Generally, the polyimide films exhibited d-spacing value in the range of 5.79-6.39 Å . Additionally, the solvent resistance of PIs with the same dianhydride was shown in the decreasing order of TFODA > TFDB, which agreed with the reduced nonplanar steric degree and improved rigidity of mentioned diamines.

The Solubility and WAXD of the Polyimide Films
The solubility of the PI films was tested in various solvents, and the results are summarized in Table 1. Most of the PI films were soluble in typical polar solvents such as N,N-dimethylacetamide (DMAC) and N-methyl-2-pyrrodidon (NMP) at room temperature. The data listed in Table 1 demonstrates that the solubility of films derived from 8FDA is as good as 6FDA and HPMDA for given diamines. It can be explained that the rigid 8FDA monomer owned more linear, semi-alicyclic structures and CF 3 groups, which disrupted the chain packing and reduced the interchain interaction. It also reduced the crystallinity and endowed good solubility. It is reported that [27,36] highly organo-soluble PI films include some solubility promoting groups (e.g., CF 3 , -O-, and flexible groups) [37,38]. These segments would hinder polymer-polymer interaction, and thus disrupt the chain packing, prevent crystallization, and improve solubility.
Further evidence could be obtained from the wide angle X-ray diffraction (WAXD) measurement. The average inter-chain spacing distance (d-spacing) was calculated from the most prominent WAXD peak in the glassy amorphous polymer spectra based on Bragg's equation: 2dsinθ = nλ (n = 1, λ = 1.54 Å) [15]. From Figure 2b, it was observed that all of the films presented amorphous states. Generally, the polyimide films exhibited d-spacing value in the range of 5.79-6.39 Å. Additionally, the solvent resistance of PIs with the same dianhydride was shown in the decreasing order of TFODA > TFDB, which agreed with the reduced nonplanar steric degree and improved rigidity of mentioned diamines. measured with 100 mg of the polymer in 2 mL of solvent. +, soluble at room temperature; +s, soluble after heating; +-, slightly soluble after heating; -, insoluble; b The most prominent WAXD peak in the amorpous glassy polymer spectra was adopted to calculate the d-spacing value according to Bragg's equation: 2dsinθ = nλ (n = 1, λ = 1.54 Å); c Water absorption (%) = ((W − W 0 )/W 0 ) × 100%, in which W is the weight of polymer sample after being immersed in water for 96 h at room temperature and W 0 the weight of polymer sample after being dried in vacuum at 100 • C for 8 h. d Equilibrium contact angle was measured at ambient temperature using double distilled water as solvent for a time period of 120 s depending on the stability of the drop, and the data were the average value of 10 experiments.

Optical Properties of PIs
Pictures of PI films are shown in Figure 3. The UV-Visible spectra of all films were shown in Figure 4a, and the transmittance at 400 nm (T 400 ) and cutoff wavelength (λ 0 ) were summarized in Table 1, and, according to Figure 4a, 8FDA-based films exhibited T 400 from 46% to 64% and λ 0 below 345 nm. Additionally, 6FDA series films showed T 400 from 38% to 74% and λ 0 below 360 nm. Meanwhile, PIs that originated from HPMDA exhibited T 400 from 79% to 83% and λ 0 below 295 nm. The T 400 of PIs with the same diamines decreased in the order of HPMDA > 6FDA > 8FDA. Although the T 400 of 8FDA-based PIs was slightly lower than the contrast dianhydrides, it was still better than other reported rigid alicyclic, (Ref. [15] T 400 lower than 10%, Ref. [39] T 400 lower than 20%, Ref. [40] T 400 lower than 15%, and so on) and much better than the traditional ArPIs with the color of deep yellow or brown. Additionally, it can be explained that the existence of 1,4-cyclohexadiene segments can break the conjugation of the polymer chain, which can decrease the charge transfer [29]. In addition, the electron-withdrawing, steric hindrance of pendent CF 3 groups and fluorine atoms enlarged the average distance of the backbone and induced the separation of the chain backbones, and reduced the inter-and intra-molecular CTC formation that imparted brown color to the polymer as well, which was largely hindered, and optical properties improved [27]. These factors helped 8FDA-based polyimides (PI-1 and PI-2) possess good optical properties.

Optical Properties of PIs
Pictures of PI films are shown in Figure 3. The UV-Visible spectra of all films were shown in Figure 4a, and the transmittance at 400 nm (T400) and cutoff wavelength (λ0) were summarized in Table 1, and, according to Figure 4a, 8FDA-based films exhibited T400 from 46% to 64% and λ0 below 345 nm. Additionally, 6FDA series films showed T400 from 38% to 74% and λ0 below 360 nm. Meanwhile, PIs that originated from HPMDA exhibited T400 from 79% to 83% and λ0 below 295 nm. The T400 of PIs with the same diamines decreased in the order of HPMDA > 6FDA > 8FDA. Although the T400 of 8FDA-based PIs was slightly lower than the contrast dianhydrides, it was still better than other reported rigid alicyclic, (Ref. [15] T400 lower than 10%, Ref. [39] T400 lower than 20%, Ref. [40] T400 lower than 15%, and so on) and much better than the traditional ArPIs with the color of deep yellow or brown. Additionally, it can be explained that the existence of 1,4-cyclohexadiene segments can break the conjugation of the polymer chain, which can decrease the charge transfer [29]. In addition, the electron-withdrawing, steric hindrance of pendent CF3 groups and fluorine atoms enlarged the average distance of the backbone and induced the separation of the chain backbones, and reduced the inter-and intra-molecular CTC formation that imparted brown color to the polymer as well, which was largely hindered, and optical properties improved [27]. These factors helped 8FDA-based polyimides (PI-1 and PI-2) possess good optical properties. The transmittance of polyimides derived from the same dianhydride with different diamines showed the tendency of TFODA > TFDB. For instance, PI-3 (8FDA/TFDB) showed T400 of 43% and λ0 of 370 nm, whereas T400 and λ0 values of the PI-2 (8FDA/TFODA) were 71% and 353 nm, respectively. It can be explained that TFODA monomer consists of flexible ether bond, and -CF3 groups caused bigger steric hindrance, smaller interchain interaction, and weakened CTC than TFDB [41].
The cutoff wavelength (λ0) of a polyimide film was another parameter of the optical transparency; herein, the cutoff was considered to be the wavelength at which the transmittance became less than 1% [29], and the dada is summarized in Table 2. As the transmittance of PI-x improved, the cutoff wavelength shortened [33]. For example, PI-2 with T400 of 64% and λ0 of 344 nm exhibited a shorter cutoff wavelength than PI-1with T400 of 46% and λ0 of 358 nm. Therefore, the optical properties of 8FDA-based PIs met the applicable criterion for some advanced optoelectronics. The transmittance of polyimides derived from the same dianhydride with different diamines showed the tendency of TFODA > TFDB. For instance, PI-3 (8FDA/TFDB) showed T 400 of 43% and λ 0 of 370 nm, whereas T 400 and λ 0 values of the PI-2 (8FDA/TFODA) were 71% and 353 nm, respectively. It can be explained that TFODA monomer consists of flexible ether bond, and -CF 3 groups caused bigger steric hindrance, smaller interchain interaction, and weakened CTC than TFDB [41].
The cutoff wavelength (λ 0 ) of a polyimide film was another parameter of the optical transparency; herein, the cutoff was considered to be the wavelength at which the transmittance became less than 1% [29], and the dada is summarized in Table 2. As the transmittance of PI-x improved, the cutoff wavelength shortened [33]. For example, PI-2 with T 400 of 64% and λ 0 of 344 nm exhibited a shorter cutoff wavelength than PI-1with T 400 of 46% and λ 0 of 358 nm. Therefore, the optical properties of 8FDA-based PIs met the applicable criterion for some advanced optoelectronics.

Thermal Properties of PIs
The thermal decomposition and stability properties of the films of PIs were evaluated by thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA), and thermal mechanical analysis (TMA). All data were obtained from the PIs films, and are shown in Table 2. According to the DMA curve in Figure 4b, it was found that 8FDA-based PIs exhibited higher Tg values than the corresponding 6FDA-based and HPMDA-based PIs films. The Tg values of PI-1 and PI-2 were in the range of 369-401 °C, while the Tg of the contrast PIs (PI-3 to PI-6) were in the range of 292-348 °C. The Tg of PI-1 is 401 °C, which is 86 °C higher than that of PI-3. This can be attributed to the rigid structure of 8FDA monomer. According to the single crystal structure, 8FDA has 1,4-cyclohexadiene as the bridge between two phenyl anhydrides. The planarity of 8FDA is much better than that of 6FDA and HPMDA, with a bridge of quaternary carbon between two phenyl anhydrides and alicyclic structure. The linear structure, rigidity, and inter-chain interaction of 8FDA-based PIs were stronger than the PIs based on 6FDA and HPMDA [42]. According to the literature, the Tg of polyimides were dictated by the chain rigidity, as well as the inter-and intra-molecular interactions that originated from the CTC between the electron-withdrawing dianhydride residue and the electron-donating diamine residue [28]. For a given dianhydride, the Tg value of PIs were in the order of TFDB > TFODA. Because the rigidity of TFODA, which consisted of flexible ether, the bond was lower than TFDB.
As shown in Table 2 and Figure 4c, no significant weight loss was detected until the temperature was as high as 460 °C. The 1% weight loss temperature (Td1) and the char yield of these polyimides ranged from 462 to 518 °C and 50%-64%, respectively. 8FDA-based PIs exhibited higher Td1 more values than the corresponding 6FDA and HPMDA films. As mentioned above, multi-substituted and rigid semi-alicyclic 1,4-cyclohexadiene in 8FDA featured more rigid structure, which enhanced the inter-chain interaction and accumulation degree [43], as well as increased their thermal resistance.

Thermal Properties of PIs
The thermal decomposition and stability properties of the films of PIs were evaluated by thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA), and thermal mechanical analysis (TMA). All data were obtained from the PIs films, and are shown in Table 2. According to the DMA curve in Figure 4b, it was found that 8FDA-based PIs exhibited higher T g values than the corresponding 6FDA-based and HPMDA-based PIs films. The T g values of PI-1 and PI-2 were in the range of 369-401 • C, while the T g of the contrast PIs (PI-3 to PI-6) were in the range of 292-348 • C. The T g of PI-1 is 401 • C, which is 86 • C higher than that of PI-3. This can be attributed to the rigid structure of 8FDA monomer. According to the single crystal structure, 8FDA has 1,4-cyclohexadiene as the bridge between two phenyl anhydrides. The planarity of 8FDA is much better than that of 6FDA and HPMDA, with a bridge of quaternary carbon between two phenyl anhydrides and alicyclic structure. The linear structure, rigidity, and inter-chain interaction of 8FDA-based PIs were stronger than the PIs based on 6FDA and HPMDA [42]. According to the literature, the T g of polyimides were dictated by the chain rigidity, as well as the inter-and intra-molecular interactions that originated from the CTC between the electron-withdrawing dianhydride residue and the electron-donating diamine residue [28]. For a given dianhydride, the T g value of PIs were in the order of TFDB > TFODA. Because the rigidity of TFODA, which consisted of flexible ether, the bond was lower than TFDB.
As shown in Table 2 and Figure 4c, no significant weight loss was detected until the temperature was as high as 460 • C. The 1% weight loss temperature (T d1 ) and the char yield of these polyimides ranged from 462 to 518 • C and 50%-64%, respectively. 8FDA-based PIs exhibited higher T d1 more values than the corresponding 6FDA and HPMDA films. As mentioned above, multi-substituted and rigid semi-alicyclic 1,4-cyclohexadiene in 8FDA featured more rigid structure, which enhanced the inter-chain interaction and accumulation degree [43], as well as increased their thermal resistance.
The 5% weight loss temperature (T d5 ) of PI-x in N 2 stayed in the range of 497-557 • C. The curves in Figure 4c indicated that the thermal stability of PI-x originated from the same dianhydride decreased in the order of TFDB and TFODA. It can be accounted for that TFDB-based PIs possessed higher rigidity and showed good thermal stability. The TFODA monomer was bridged by ether bond, and the bond energy of C-O is 326 KJ mol −1 , which is the lowest one among all the bonds in the backbone. When it was heated, the PIs based on TFODA were more prone to fracture; they thus decreased the thermal resistance of TFODA-based PIs.
The TMA results are shown in Table 2 and Figure 4d. The CTE values of PI-1 and PI-2 derived from 8FDA were 14 to 18 ppm K −1 , respectively, while the contrast PIs based on 6FDA and HPMDA ranged from 44 to 63 ppm K −1 . Compared with 6FDA and HPMDA, it is the bent-shaped rigid dianhydride moiety containing cis-type 1,4-cyclohexadiene skeleton that suppress CTE. As described in the literature [44], coefficient of thermal expansion (CTE) is divided into the lateral (in-plane) CTE of polyimide films and the vertical (out-of-plane) CTE. Additionally, the vertical CTE values were different from lateral CTE. In this work, the CTE data were the lateral CTE data and were measured using a thermal mechanical analyzer (TA Instruments, New Castle, PA, USA) in expansion mode. Ando's [45] group reported the relationship between the molecular orientation and CTEs parallel and perpendicular to the film plane. They evaluated these CTE values separately and also exact CVE value by means of not only conventional TMA measurement but also an optical interferometric method in near-IR region, respectively. They found a good linear relationship between anisotropy in CTE and molecular orientation. If the intrinsic birefringence values, ∆n 0 , are same among the target samples, one can directly compare the birefringence, although ∆n 0 value depends on the density and also optical polarizability tensor components. As shown in Figure S23, 8FDA-based PI-1 and PI-2 possessed biggest birefringence (0.129 for PI-1, 0.123 for PI-2); it was reported [46] that birefringence data ≥0.1 represents a criterion in which aromatic PI chains are highly aligned parallel to the film plane, so that lateral CTE values of 8FDA-based PIs were lower than the contrast PI-3-PI-6 (from 0.016 to 0.066), which originated from 6FDA and HPMDA. Additionally, in the OLED display area, dimensional stability is more concerned about lateral CTE. As depicted in the reference, the CVE of aromatic PIs decreased with increasing the density. WAXD data revealed longer intermolecular distance of PI-1 and PI-2, that is, lower density, so that the CVE of PI-1 and PI-2 was bigger than contrast PIs. It can be explained that according to the single crystal diffraction test, 8FDA has more linear and semi-alicyclic modified structure, which enlarged the average distance of 8FDA-based polyimides and led to lower density and increased the CVE.
Compared with the CTE value of polyimide films derived from the more rigid dianhydride (PMDA and NTDA) with rigid diamines and summarized in Table S2, it was found that, for a given dianhydride, with increasing the rigidity of diamine, the CTE value decreased [47]. It can be explained that the PMDA [46,48] and the NTDA [49,50] monomer had more rigid and linear structure, while endowed rigid dianhydride-based polyimides have better in-plane orientation in CTE than 8FDA-based polyimide. For instance, CTE of PI-1 (8FDA/TFDB) was 14 ppm K −1 , while the CTE of CPI-1(NTDA/APAB) and CPI-3 (PMDA/APAB) was 3.0 and 2.0 ppm K −1 , respectively, so that the orientation, density, and the structure of PIs affected the CTE value together. The results revealed that 8FDA is a useful dianhydride monomer that provides unique PIs possessing lower CTE [15,28].

Mechanical Properties
Mechanical properties of the PIs are summarized in Table 2. The stress-strain curves are shown in Figure 5a. PI-1 and PI-2 showed the tensile strengths at break of 96.0-113.0 MPa, the elongation at break of 2.1-7.0%, and the tensile modulus of 1.2-4.5 GPa. As a comparison, PI-3 to PI-6 showed lower tensile strengths at break of 39.0-84.0 MPa, comparable elongation at break of 2.7-5.8%, and lower tensile modulus of 1.1-1.8 GPa. Figure 5a depicts that PI-1 and PI-2 exhibited better mechanical properties than contrast PI-x (6FDA and HPMDA series). It can be explained that molecular structure of 8FDA, which was bridged by multi-substitute 1,4-cyclohexadiene segment, was more planar and regular than 6FDA and HPMDA. These characters made 8FDA-based PIs exhibit stronger rigidity and closer accumulation. The structure characters of 8FDA enhanced its mechanical properties. Both series followed the tendency based on the same dianhydride in the decreasing order of TFDB and TFODA in terms of tensile strengths and tensile modulus. It should be noted that the tensile stress and tensile module enhanced as the rigidity of the PI's main chain increased [51]. Thus, the results of tensile curves demonstrated that by incorporating the rigid semi-alicyclic segment in the backbone of the polyimide, the tensile strengths, the tensile modulus, and the elongation at break were significantly enhanced. exhibit stronger rigidity and closer accumulation. The structure characters of 8FDA enhanced its mechanical properties. Both series followed the tendency based on the same dianhydride in the decreasing order of TFDB and TFODA in terms of tensile strengths and tensile modulus. It should be noted that the tensile stress and tensile module enhanced as the rigidity of the PI's main chain increased [51]. Thus, the results of tensile curves demonstrated that by incorporating the rigid semi-alicyclic segment in the backbone of the polyimide, the tensile strengths, the tensile modulus, and the elongation at break were significantly enhanced.  Figure 5b described the contours of the droplet on the PI-x surface. Additionally, the contact angle was summarized in Table 1. As shown in Table 1 and Figure 5b, all of the contact angles against water of the PIs were above 70° [38], in the range of 82.0°-95.0°, which demonstrated that all the surfaces of PI-x were hydrophobic. The increased hydrophobicity of 8FDA-based PIs (θ values range from 92°-95.0°) can be attributed to its steric effects, semi-alicyclic segments, and higher content of fluorine atoms. Compared with 6FDA-and HPMDA-derived PI-x, 8FDA-based PI-x, being more rigid and planar, had higher regularity and packing degree, which increased their hydrophobicity. It has been reported that alicyclic segments in the backbone can improve the hydrophobicity of the PIs [33]. Meanwhile, the trifluoromethyl groups and fluorine atoms made the migration of the fluorocarbon chain to the film surface and fluorine enrichment at the surface [52], which reduced the surface tension and made the surface become more hydrophobic.

Surface Properties of the PIs
PIs usually showed higher moisture uptakes than the hydrocarbon polymers because of the hydrophilic imide groups [53]. It should be noted that structures of the PIs played an important role in the moisture absorption. It can be seen in Table 1 that all the PIs exhibited low water uptakes. The better hydrophobicity of 8FDA-based PIs led to the low affinity for water. Additionally, the  Figure 5b described the contours of the droplet on the PI-x surface. Additionally, the contact angle was summarized in Table 1. As shown in Table 1 and Figure 5b, all of the contact angles against water of the PIs were above 70 • [38], in the range of 82.0 • -95.0 • , which demonstrated that all the surfaces of PI-x were hydrophobic. The increased hydrophobicity of 8FDA-based PIs (θ values range from 92 • -95.0 • ) can be attributed to its steric effects, semi-alicyclic segments, and higher content of fluorine atoms. Compared with 6FDA-and HPMDA-derived PI-x, 8FDA-based PI-x, being more rigid and planar, had higher regularity and packing degree, which increased their hydrophobicity. It has been reported that alicyclic segments in the backbone can improve the hydrophobicity of the PIs [33]. Meanwhile, the trifluoromethyl groups and fluorine atoms made the migration of the fluorocarbon chain to the film surface and fluorine enrichment at the surface [52], which reduced the surface tension and made the surface become more hydrophobic.

Surface Properties of the PIs
PIs usually showed higher moisture uptakes than the hydrocarbon polymers because of the hydrophilic imide groups [53]. It should be noted that structures of the PIs played an important role in the moisture absorption. It can be seen in Table 1 that all the PIs exhibited low water uptakes. The better hydrophobicity of 8FDA-based PIs led to the low affinity for water. Additionally, the trifluoromethyl groups and fluorine atoms possessed water repelling features, which inhibited the absorption of moisture molecules on the surface of the fluorinated polymer films [54].
It is reported that alicyclic segments of the main chain can decrease the moisture uptakes of PIs. Therefore, it was found that PIs based on 8FDA possessed the lowest water barrier properties. Besides, PI-x exhibited lower water uptake than traditional aromatic polyimide. These results demonstrated that polyimides containing rigid, semi-alicyclic segments and fluorine-contained groups showed greater practical reliability with regard to withstanding long-term humid working environment for optoelectronics and microelectronics application.
Atomic Force Microscope (AFM) was used to characterize the surface morphologies and roughness of polymer films. AFM images are shown in Figure 6. Additionally, the root mean square (RMS) roughness is listed in Table 1. Normally, RMS strongly interrelated with the degrees of order or disorder in the grain structure distribution and associated with the shape-size complexity [55]. Therefore, PI-x originated from 8FDA, which possessed more neat main chains and exhibited lower RMS. For instance, RMS value of PI-1 (8FDA/TFDB) is 1.16 nm, and PI-2 (8FDA/TFODA) is 1.79 nm. Additionally, all the PIs owned low RMS, which indicated that PIs can be used as flexible substrate.
Polymers 2018, 10, x FOR PEER REVIEW 14 of 17 trifluoromethyl groups and fluorine atoms possessed water repelling features, which inhibited the absorption of moisture molecules on the surface of the fluorinated polymer films [54]. It is reported that alicyclic segments of the main chain can decrease the moisture uptakes of PIs. Therefore, it was found that PIs based on 8FDA possessed the lowest water barrier properties. Besides, PI-x exhibited lower water uptake than traditional aromatic polyimide. These results demonstrated that polyimides containing rigid, semi-alicyclic segments and fluorine-contained groups showed greater practical reliability with regard to withstanding long-term humid working environment for optoelectronics and microelectronics application.
Atomic Force Microscope (AFM) was used to characterize the surface morphologies and roughness of polymer films. AFM images are shown in Figure 6. Additionally, the root mean square (RMS) roughness is listed in Table 1. Normally, RMS strongly interrelated with the degrees of order or disorder in the grain structure distribution and associated with the shape-size complexity [55]. Therefore, PI-x originated from 8FDA, which possessed more neat main chains and exhibited lower RMS. For instance, RMS value of PI-1 (8FDA/TFDB) is 1.16 nm, and PI-2 (8FDA/TFODA) is 1.79 nm. Additionally, all the PIs owned low RMS, which indicated that PIs can be used as flexible substrate.

Conclusions
In conclusion, a polymorphic dianhydride 8FDA and a transparent polyimide based on 8FDA were reported. The geometric configuration transition during the synthesis of 8FDA was traced using single crystal X-ray diffraction of the intermediate compounds. Compared with the widely used dianhydride 6FDA and HPMDA, 8FDA-based transparent PI films showed much better thermal and dimensional stabilities. The new building block for transparent PIs is a promising key monomer toward the substrate for flexible OLEDs display.

Conclusions
In conclusion, a polymorphic dianhydride 8FDA and a transparent polyimide based on 8FDA were reported. The geometric configuration transition during the synthesis of 8FDA was traced using single crystal X-ray diffraction of the intermediate compounds. Compared with the widely used dianhydride 6FDA and HPMDA, 8FDA-based transparent PI films showed much better thermal and dimensional stabilities. The new building block for transparent PIs is a promising key monomer toward the substrate for flexible OLEDs display.