Synthesis and Characterization of Chemically and Green-Synthesized Silver Oxide Particles for Evaluation of Antiviral and Anticancer Activity

Silver oxide (Ag2O) particles are wonderful candidates due to their unique properties, and their use in a wide range of research, industrial and biomedical applications is rapidly increasing. This makes it fundamental to develop simple, environmentally friendly methods with possible scaling. Herein, sodium borohydride and Datura innoxia leaf extract were applied as chemical and biological stabilizing and reducing agents to develop Ag2O particles. The primary aim was to evaluate the anticancer and antiviral activity of Ag2O particles prepared via two methods. XRD, UV-visible and SEM analyses were used to examine the crystallite structure, optical properties and morphology, respectively. The resulting green-synthesized Ag2O particles exhibited small size, spherically agglomerated shape, and high anticancer and antiviral activities compared to chemically synthesized Ag2O particles. The MTT (3-(4,5-dimethylthiazol-2-yl)-2,5 diphenyltetrazolium-bromide) assay of green-synthesized Ag2O particles showed high anticancer activity against MCF-7 cells with IC50 = 17.908 µg/mL compared to chemically synthesized Ag2O particles with IC50 = 23.856 µg/mL. The antiviral activity of green-synthesized Ag2O particles and chemically synthesized Ag2O particles was also evaluated by a plaque-forming assay, and green-synthesized Ag2O particles showed higher antiviral ability with IC50 = 0.618 µg/mL as compared to chemically synthesized Ag2O particles with IC50 = 6.129 µg/mL. We propose the use of green-synthesized Ag2O particles in cancer treatment and drug delivery.


Introduction
The global cancer problem is progressively increasing every year [1].According to the World Health Organization (WHO) 2020 reports, there were 9.9 million deaths globally, with breast cancer mortality (2.26 million) being particularly high in developing countries, especially in Pakistan [2][3][4].
Metal oxide particles have been leading the way in materials research for industrial, energy, and biomedical applications over the last few decades.
A number of benefits, including ease of use, environmental friendliness, and ease of scaling, have generated considerable interest in green nanotechnology.Herbals are ingredients (extracts) that are derived from plants, either in combination or alone, and are used to treat and prevent many diseases.Many plant extracts have shown anticancer activity against several cancer cells without harming the growth of healthy cells.Plants are widely considered the optimal choice of material due to their stabilizing capabilities and bio-reducing properties [5,6].
In the current study, Ag 2 O particles were prepared via a green synthesis process by using Datura innoxia leaf extract.The extract effectively decreased and stabilized the ions present in the silver nitrate solution, resulting in Ag 2 O particle synthesis without requiring any chemical reducing or stabilizing agent.However, in the chemical synthesis process, sodium borohydride was used to prepare the Ag 2 O particles, which is a very strong stabilizing/reducing agent.The green and chemically prepared Ag 2 O particles were characterized.Finally, the anticancer and antiviral efficacy of green and chemically prepared Ag 2 O particles were explored.We suggest that further in vivo anticancer and antiviral studies of Datura innoxia Ag 2 O particles should be performed.

X-ray Diffraction Analysis
An X-ray diffraction (XRD) study was used to determine the crystal structure and calculate the crystallite size of Ag 2 O particles prepared using chemical and green synthesis processes.Figure 1a,b present the crystal structure patterns of the chemical and green synthesis of Ag 2 O particles prepared by coprecipitation processes and annealed at 400 • C for 12 h for refinement.The crystal structure of chemically and green-prepared Ag 2 O particles was investigated and calculated as cubic crystal structure and justified while comparing JCPDS No. 01-087-0719.The miller indices of maximum intensity peak are labeled with the (111) reflection/lattice plane at a diffraction angle of 38.4 • , while the remaining lattice planes appeared in the following order: peaks at two thetas (2θ) = 44.5 • , 64.6 • , 77.6 • and 82.3 • labeled, and with respective indices of (200), (220), (311) and (222) in both chemical and green processes, respectively.The XRD pattern was similar in both conditions.In addition, it was observed that the maximum intensity peak had a broad size, which confirmed the growth of the particles.The average crystallite sizes of chemically and green-synthesized Ag 2 O particles were ~63 and ~54 nm, respectively, as shown in Table 1.Moreover, the crystallite size was calculated from X-ray diffraction (XRD) data using the given formulas [26][27][28][29].

FTIR Analysis
The chemical bond and functional groups of both chemically and green-synthesized Ag2O particles were investigated using Fourier transform infrared spectroscopy (FTIR) in the wavelength range of 500-4000 cm −1 .In Figure 2a,b, it can be observed that the FTIR spectra of chemically synthesized Ag2O particles exhibited a shift in the bands compared to those synthesized using Datura innoxia plant extract.The addition of Datura innoxia plant extract to silver nitrate resulted in a change in the functional groups of Ag2O particles.The green-synthesized Ag2O particles showed several peaks corresponding to major functional groups at 3357, 2347, and 1631 cm −1 , while the chemically synthesized Ag2O particles showed a shift in the bands at 3390, 2364, and 1620 cm −1 .These peaks are associated with the stretching vibration of the hydroxyl group (H-bonded O-H stretch) [30][31][32].Additionally, the O-H bending vibration of water molecules absorbed on the surface of Ag2O particles, which may be crucial for biomedical assays such as anticancer and antimicrobial activities [30,31], and a weak stretching vibration of C=C [17], were observed.The weak peaks at 1395 and 1387 cm −1 of Ag2O correspond to NO 3− ions (nitrates).

FTIR Analysis
The chemical bond and functional groups of both chemically and green-synthesized Ag 2 O particles were investigated using Fourier transform infrared spectroscopy (FTIR) in the wavelength range of 500-4000 cm −1 .In Figure 2a,b, it can be observed that the FTIR spectra of chemically synthesized Ag 2 O particles exhibited a shift in the bands compared to those synthesized using Datura innoxia plant extract.The addition of Datura innoxia plant extract to silver nitrate resulted in a change in the functional groups of Ag 2 O particles.The greensynthesized Ag 2 O particles showed several peaks corresponding to major functional groups at 3357, 2347, and 1631 cm −1 , while the chemically synthesized Ag 2 O particles showed a shift in the bands at 3390, 2364, and 1620 cm −1 .These peaks are associated with the stretching vibration of the hydroxyl group (H-bonded O-H stretch) [30][31][32].Additionally, the O-H bending vibration of water molecules absorbed on the surface of Ag 2 O particles, which may be crucial for biomedical assays such as anticancer and antimicrobial activities [30,31], and a weak stretching vibration of C=C [17], were observed.The weak peaks at 1395 and 1387 cm −1 of Ag 2 O correspond to NO 3− ions (nitrates).Furthermore, the presence of an O-Ag-O bending mode of vibration at 611 cm −1 confirmed the formation of metal-oxygen bonding [9,30,31].Moreover, the FTIR spectra of Datura innoxia leaf extract are shown in Figure 2c, which are quite similar to those in the previously published article [17].
Furthermore, the presence of an O-Ag-O bending mode of vibration at 611 cm −1 confirmed the formation of metal-oxygen bonding [9,30,31].Moreover, the FTIR spectra of Datura innoxia leaf extract are shown in Figure 2c, which are quite similar to those in the previously published article [17].

UV-Visible Analysis
UV-visible spectroscopy was employed to analyze the optical density or absorption spectra of both chemically and green-synthesized particles.In the current experimental strategy, chemically and green-synthesized Ag2O particles were carefully examined.When chemically and green-synthesized Ag2O particle samples were dispersed in deionized water to find the absorption spectra in the range of 350 nm to 850 nm, we revealed a sharp absorption band at 410 nm in the absorption spectra of chemically synthesized Ag2O particles, as depicted in Figure 3a.This might indicate the presence of chemically synthesized Ag2O particles such as in [17].The absorption spectra of green-synthesized Ag2O particles are depicted in Figure 3b, where the presence of Ag2O particles is confirmed from the green-synthesized Ag2O sample using these spectra.Generally, green-synthesized Ag2O particles in deionized water absorbed radiation near the wavelength of 414.7 nm.It was observed from the UV-visible graph that the confirmation of the surface plasmon resonance peak near 425 nm indicates the presence of green-synthesized Ag2O particles, as shown in Figure 3b.On the metallic surface of green-synthesized Ag2O particles, there

UV-Visible Analysis
UV-visible spectroscopy was employed to analyze the optical density or absorption spectra of both chemically and green-synthesized particles.In the current experimental strategy, chemically and green-synthesized Ag 2 O particles were carefully examined.When chemically and green-synthesized Ag 2 O particle samples were dispersed in deionized water to find the absorption spectra in the range of 350 nm to 850 nm, we revealed a sharp absorption band at 410 nm in the absorption spectra of chemically synthesized Ag 2 O particles, as depicted in Figure 3a.This might indicate the presence of chemically synthesized Ag 2 O particles such as in [17].The absorption spectra of green-synthesized Ag 2 O particles are depicted in Figure 3b, where the presence of Ag 2 O particles is confirmed from the green-synthesized Ag 2 O sample using these spectra.Generally, green-synthesized Ag 2 O particles in deionized water absorbed radiation near the wavelength of 414.7 nm.It was observed from the UV-visible graph that the confirmation of the surface plasmon resonance peak near 425 nm indicates the presence of green-synthesized Ag 2 O particles, as shown in Figure 3b.On the metallic surface of green-synthesized Ag 2 O particles, there are resonant oscillations of free electrons through interbond transitions and surface plasmon resonance (SPR) bands [33].In the graph, the surface plasmon peak indicates the presence of Ag 2 O particles with different sizes, and the spherical shape is confirmed in SEM.The absorption spectra of Datura innoxia leaf extract is depicted in Figure 3c, which shows a peak at ~220 nm.For more details about the absorbance of the Datura innoxia leaf extract, see the previously published paper [34].
Pharmaceuticals 2024, 17, x FOR PEER REVIEW 5 of 14 are resonant oscillations of free electrons through interbond transitions and surface plasmon resonance (SPR) bands [33].In the graph, the surface plasmon peak indicates the presence of Ag2O particles with different sizes, and the spherical shape is confirmed in SEM.The absorption spectra of Datura innoxia leaf extract is depicted in Figure 3c, which shows a peak at ~220 nm.For more details about the absorbance of the Datura innoxia leaf extract, see the previously published paper [34].

SEM and EDX Analysis
The surface morphology of both chemically and green-synthesized Ag2O particles was analyzed using scanning electron microscopy (SEM).The SEM images of chemically and green-synthesized Ag2O particles are shown in Figure 4a,b at a scale of 3 µm scale, respectively.Spherical grains of the chemically and green-synthesized Ag2O particles can be seen in Figure 4, with some non-uniformly distributed aggregates present.The SEM micrographs confirmed that the chemically and green-synthesized Ag2O particles mostly have spherical shapes of various sizes.In Figure 4b, the bioagents of Datura innoxia leaf extract strongly interact with Ag ions to produce uniform spherical shapes with small sizes.The green-synthesized Ag2O particles had spherical shapes of dissimilar sizes but were smaller than the chemically synthesized Ag2O particles.The spherical grains were circulated with red circles.Hence, the SEM results of green-synthesized Ag2O particles

SEM and EDX Analysis
The surface morphology of both chemically and green-synthesized Ag 2 O particles was analyzed using scanning electron microscopy (SEM).The SEM images of chemically and green-synthesized Ag 2 O particles are shown in Figure 4a,b at a scale of 3 µm scale, respectively.Spherical grains of the chemically and green-synthesized Ag 2 O particles can be seen in Figure 4, with some non-uniformly distributed aggregates present.The SEM micrographs confirmed that the chemically and green-synthesized Ag 2 O particles mostly have spherical shapes of various sizes.In Figure 4b, the bioagents of Datura innoxia leaf extract strongly interact with Ag ions to produce uniform spherical shapes with small sizes.The green-synthesized Ag 2 O particles had spherical shapes of dissimilar sizes but were smaller than the chemically synthesized Ag 2 O particles.The spherical grains were circulated with red circles.Hence, the SEM results of green-synthesized Ag 2 O particles were much better than those of the chemical Ag 2 O particles.The energy-dispersive X-spectroscopy (EDX) technique was employed to conduct an elemental compositional analysis of both chemically and green-synthesized Ag 2 O particles.The results from the EDX analysis verified the existence of Ag as a main element and O and C as the primary elements in the samples, as depicted in Figure 4c,d.The negligible percentage of carbon is due to lab environment or lab equipment.Kasthuri et al. [17] and Gajendaran et al. [35] also reported similar results, where elemental silver was detected in the graph obtained by EDX analysis, confirming the reduction of silver ions to elemental silver.
Pharmaceuticals 2024, 17, x FOR PEER REVIEW 6 of 14 were much better than those of the chemical Ag2O particles.The energy-dispersive X-ray spectroscopy (EDX) technique was employed to conduct an elemental compositional analysis of both chemically and green-synthesized Ag2O particles.The results from the EDX analysis verified the existence of Ag as a main element and O and C as the primary elements in the samples, as depicted in Figure 4c,d.The negligible percentage of carbon is due to lab environment or lab equipment.Kasthuri et al. [17] and Gajendaran et al. [35] also reported similar results, where elemental silver was detected in the graph obtained by EDX analysis, confirming the reduction of silver ions to elemental silver.

Anticancer Activity against MCF-7 Cells
The results of the cytotoxicity investigation of both types of Ag2O particles on the breast cancer (MCF-7) cell line revealed that both particles were cytotoxic against the cancer cell line and were less toxic towards the Vero cell line.Maximum cell death was detected for the green-synthesized Ag2O particles with an IC50 of 17.908 µg/mL, compared to chemically synthesized Ag2O particles with an IC50 of 23.856 µg/mL against MCF-7 cells after 48 h of exposure.As can be seen in Figure 5, the cytotoxicity of both Ag2O particles is concentration-dependent [36].

Anticancer Activity against MCF-7 Cells
The results of the cytotoxicity investigation of both types of Ag 2 O particles on the breast cancer (MCF-7) cell line revealed that both particles were cytotoxic against the cancer cell line and were less toxic towards the Vero cell line.Maximum cell death was detected for the green-synthesized Ag 2 O particles with an IC 50 of 17.908 µg/mL, compared to chemically synthesized Ag 2 O particles with an IC 50 of 23.856 µg/mL against MCF-7 cells after 48 h of exposure.As can be seen in Figure 5, the cytotoxicity of both Ag 2 O particles is concentration-dependent [36].

Cytotoxicity Activity against Vero Cells
To rule out the possibility that cellular toxicity may be the cause of the decline in infectivity, a range of concentrations (1, 5, 10, 50, and 100 µg/mL) were incubated with Vero cell monolayers, as shown in Figure 6.Each concentration of Ag2O particles was incubated for various time periods (48 h), and cell viability was measured using the 3-(4,5dimethyllthiazol-2-yl)-2,5 diphenyl-tetrazolium-bromide (MTT) assay.Chemically prepared Ag2O particles had toxic effects in the concentration range of 10-50 µg/mL.However, green-synthesized Ag2O particles within the range were shown/found to have low cytotoxicity in Vero cells.These statistics were valuable for determining concentrations for testing in antiviral assays.We used concentrations that were significantly below the cytotoxic threshold, ranging from 0.5 to 10 µg/mL.

Cytotoxicity Activity against Vero Cells
To rule out the possibility that cellular toxicity may be the cause of the decline in infectivity, a range of concentrations (1, 5, 10, 50, and 100 µg/mL) were incubated with Vero cell monolayers, as shown in Figure 6.Each concentration of Ag 2 O particles was incubated for various time periods (48 h), and cell viability was measured using the 3-(4,5-dimethyllthiazol-2-yl)-2,5 diphenyl-tetrazolium-bromide (MTT) assay.Chemically prepared Ag 2 O particles had toxic effects in the concentration range of 10-50 µg/mL.However, green-synthesized Ag 2 O particles within the range were shown/found to have low cytotoxicity in Vero cells.These statistics were valuable for determining concentrations for testing in antiviral assays.We used concentrations that were significantly below the cytotoxic threshold, ranging from 0.5 to 10 µg/mL.

Cytotoxicity Activity against Vero Cells
To rule out the possibility that cellular toxicity may be the cause of the decline in infectivity, a range of concentrations (1, 5, 10, 50, and 100 µg/mL) were incubated with Vero cell monolayers, as shown in Figure 6.Each concentration of Ag2O particles was incubated for various time periods (48 h), and cell viability was measured using the 3-(4,5dimethyllthiazol-2-yl)-2,5 diphenyl-tetrazolium-bromide (MTT) assay.Chemically prepared Ag2O particles had toxic effects in the concentration range of 10-50 µg/mL.However, green-synthesized Ag2O particles within the range were shown/found to have low cytotoxicity in Vero cells.These statistics were valuable for determining concentrations for testing in antiviral assays.We used concentrations that were significantly below the cytotoxic threshold, ranging from 0.5 to 10 µg/mL.

Antiviral
A stock solution of silver oxide particles was prepared via a chemical-synthesis process as well as a green-synthesis process with a concentration solution of 10 mg/L by dispersing the working solution of silver oxide particles (0.1, 0.5, 1, 2, 4, 8 and 10 µg/mL) into Newcastle disease virus (NDV)-incorporated Vero cells.The solution was then removed, washed and inoculated with 0.5% methyl cellulose for 72 h.The medium was aspirated, and the cells were fixed with 10% formaldehyde and stained with 1% crystal violet; then, the plaques were counted.The plaque analysis formation was calculated.Green-synthesized Ag 2 O particles showed significant toxicity against NDV virus compared to chemically synthesized Ag 2 O particles (Figure 7).

Antiviral Activity
A stock solution of silver oxide particles was prepared via a chemical-synthesis process as well as a green-synthesis process with a concentration solution of 10 mg/L by dispersing the working solution of silver oxide particles (0.1, 0.5, 1, 2, 4, 8 and 10 µg/mL) into Newcastle disease virus (NDV)-incorporated Vero cells.The solution was then removed, washed and inoculated with 0.5% methyl cellulose for 72 h.The medium was aspirated, and the cells were fixed with 10% formaldehyde and stained with 1% crystal violet; then, the plaques were counted.The plaque analysis formation was calculated.Green-synthesized Ag2O particles showed significant toxicity against NDV virus compared to chemically synthesized Ag2O particles (Figure 7).

Properties of Green-Synthesized Ag2O Particles
The Ag2O particles prepared using the green-synthesis process, which utilizes plant extracts, showed distinct properties compared to those prepared through traditional chemical methods.Some of the new properties of green-synthesized Ag2O particles are mentioned, such as smaller crystallite size, higher surface area, improved stability, increased antimicrobial and antioxidant potential, anticancer and antiviral properties, reduced toxicity and environmental impact, unique crystal structures and morphologies, potential for large-scale production, and cost-effectiveness.The green-synthesis method offers a sustainable and eco-friendly approach to producing Ag2O particles with advanced properties for various applications [6,12,13,16,17].For more information on the properties of green-synthesized particles, see Table 2.

Preparation of Extract
Fresh leaves of Datura innoxia were cut into small pieces, washed twice with distilled water and dried [17].In the next step, 200 g of powdered Datura innoxia was mixed with 750 mL of distilled water and heated at 80 • C for 3 h.Then, the obtained solution was filtered and scraped to obtain a dark yellow colored extract.Next, 0.407 g of extract was dissolved in 50 mL of deionized water and stirred continuously for 10 min for homogeneity.

Green Synthesis Method
An amount of 3.5 g of AgNO 3 was dissolved in 200 mL of distilled water.The prepared extract was added dropwise into the AgNO 3 solution until the color of the solution turned dark brown and maintained its pH (9)(10)(11), and finally, we obtained the precipitates.The solution was centrifuged at 7000 rpm for 10 min and dried.Then, it was annealed at 400 • C for 12 h.Finally, the prepared precipitate was ground to obtain a fine powder [17,18,45].A schematic flow chart is depicted in Figure 8. 3. Materials and Methods

Preparation of Extract
Fresh leaves of Datura innoxia were cut into small pieces, washed twice with distilled water and dried [17].In the next step, 200 g of powdered Datura innoxia was mixed with 750 mL of distilled water and heated at 80 °C for 3 h.Then, the obtained solution was filtered and scraped to obtain a dark yellow colored extract.Next, 0.407 g of extract was dissolved in 50 mL of deionized water and stirred continuously for 10 min for homogeneity.

Green Synthesis Method
An amount of 3.5 g of AgNO3 was dissolved in 200 mL of distilled water.The prepared extract was added dropwise into the AgNO3 solution until the color of the solution turned dark brown and maintained its pH (9)(10)(11), and finally, we obtained the precipitates.The solution was centrifuged at 7000 rpm for 10 min and dried.Then, it was annealed at 400 °C for 12 h.Finally, the prepared precipitate was ground to obtain a fine powder [17,18,45].A schematic flow chart is depicted in Figure 8.

Chemical Method
An amount of 0.407 g of NaBH 4 was dissolved in 50 mL of deionized water and kept in an ice bath for 3 h.In the next step, 3.5 g of AgNO 3 was taken and dissolved in 200 mL of distilled water and kept under continuous stirring on a magnetic stirrer for 40 min to obtain a homogeneous solution [46].Next, the NaBH 4 solution was removed from the ice bath and placed in a magnetic stirrer, and then the AgNO 3 solution was added dropwise.The solution was constantly stirred for 3 h to obtain dark-colored precipitates; then, 0.3 g Polyvinylpyrrolidone was mixed in 10 mL of water, and precipitates were prepared.The solution was centrifuged at 7000 rpm for 10 min and dried.Then, it was annealed at 400 • C for 12 h, and finally, the dark precipitate was ground to obtain a fine powder [27,47].A schematic flow chart is depicted in Figure 8.

Characterization of the Synthesized Nanomaterial
X-ray diffraction (D8 advance Bruker, Karlsruhe, Germany) was used to confirm the crystal structure of the prepared particles.UV-visible spectroscopy (BK-UV1800PC DB, Bio-base, Jinan, China) was employed to compute the optical density, and FTIR (Spectrum 2, Perkin Elmer, Waltham, MA, USA) was used to study the functional groups (stretching and vibrational).The surface morphology of both chemically and green-synthesized Ag 2 O particles was analyzed using scanning electron microscopy (Cube 10 Emcraft, Hanam, Republic of Korea) analysis.An energy-dispersive X-ray (EDX) spectrometer was used to confirm the elemental composition of the synthesized materials.
3.6.Bioassay 3.6.1.Cell Lines and Viruses MCF-7 and green African monkey kidney (Vero) cell lines were gifted from the National Institute of Biotechnology and Genetic Engineering (NIBGE) in Faisalabad, Pakistan.MCF-7 and Vero cells were cultivated in DMEM/F-12 medium containing 1% (v/v) antibiotics and 10% (v/v) FBS.The flasks were kept at 37 • C in a humidified atmosphere with 5% CO 2 .NDV was grown in 9-day-old chicken embryo eggs.Before use, stock viruses were collected, titrated, and stored [46].

Cytotoxicity Assay
MTT assays were used to measure the cytotoxicity of the chemically and greensynthesized Ag 2 O particles.MCF-7 cells were seeded in 96-well plates.Cells were incubated with increasing concentrations of particles at 37 • C and 5% CO 2 for 48 h.The cells were treated with a 5 mg/mL MTT solution and then incubated for 4 h.After removing the MTT, 150 µL of DMSO was added and left for 5 min.The optical density was calculated using a microplate reader.Each experiment was performed in triplicate.The cytotoxicity level was quantified by determining the IC 50 value, representing the concentration of particles that suppressed the growth of MCF-7 cells by half (50%) in comparison to untreated cells.Due to chemically synthesized Ag 2 O particles, the basicity of the solution may increase and hence become toxic towards the cell line.On the other hand, green-synthesized Ag 2 O particles were synthesized in a water-based extract, so they exhibited low toxicity.The percentage viability of Ag 2 O particles was calculated using the following formula [48,49].

Antiviral Activity
Chemically and green-synthesized Ag 2 O particles were dissolved in DMEM without serum and used at concentrations of 0.5, 1, 2, 4, 8 and 10 µg/mL.The percentage (%) inhibition was calculated by dividing the number of plaques acquired in the positive control, which had 0% inhibition (no antiviral compounds added to the cell monolayers).A plaque-forming assay was performed to check the antiviral activity of both chemically and green-synthesized Ag 2 O particles.For confluent Vero cell monolayers (12-well plates) were cleaned with phosphate-buffered saline and infected with NDV for 1 h at 37 • C, with an infection diversity of 0.02 plaque-forming units per cell.The virus inoculum was mixed with Ag 2 O particles to perform the test.Unencapsulated virus was inactivated using citrate buffer at pH 3.After being washed in PBS, the samples were incubated for 48 h in fresh growing medium with carboxymethylcellulose.Monolayers infected with NDV were fixed and stained with 10% formaldehyde.The plates were then stained with crystal violet after fixation.Microscopically, the plaques were counted.The mean plaque count for each drug concentration was expressed as a percentage of the mean plaque count of the control virus, using the formula shown below.The plaques were quantified under a microscope.The mean plaque count for every drug concentration was calculated as a ratio to the mean plaque count of the control virus, using the formula below.A graph was plotted to show the relationship between the number of plaques and the drug concentration [29,49].Statistical analysis (S.A) was performed using Student's t-test.All cytotoxic results on MCF-7 and Vero cell line experiments were reported as mean ± SD (standard deviation).A value of p ≤ 0.05 was statistically significant (indicated by *), and a value of p ≤ 0.01 was considered highly significant (indicated by **).

Conclusions
Silver oxide (Ag 2 O) particles were synthesized via a chemical-and green-synthesis approach.The XRD results revealed a cubic crystal structure.UV-visible spectroscopy results gave maximum absorption spectra at 410 nm and 414.7 nm, respectively, confirming the growth of chemically and green-synthesized Ag 2 O particles.An in vitro MTT assay of the green and chemically Ag 2 O particles revealed that both possess significant anticancer activity against MCF-7 cells with IC 50 17.908µg/mL and IC 50 23.856µg/mL, respectively.The antiviral activity of both particles was also evaluated by plaque-forming assay, and the green-synthesized Ag 2 O particles exhibited a higher antiviral ability with IC 50 0.618 µg/mL compared to chemically synthesized Ag 2 O particles with IC 50 6.129µg/mL.These results revealed that green-synthesized Ag 2 O particles proved to be better than chemically synthesized Ag 2 O particles against cancer and viral infections.In the case of chemically synthesized Ag 2 O particles, toxicity (toxic behavior) was observed against normal (Vero) cells, unlike green-synthesized Ag 2 O particles.This observation further supports the idea that green-synthesized Ag 2 O particles are safer than chemically synthesized Ag 2 O particles.This research could potentially play a role in biomedical applications, particularly in the field of nanomedicine in the near future.We also suggest that in vivo anticancer and antiviral studies of green-synthesized Ag 2 O particles should be performed.

Figure 1 .Table 1 .
Figure 1.XRD graph of (a) chemically synthesized Ag2O particles and (b) green-synthesized Ag2O particles.Table 1.(a) shows the parameters, miller indices, diffraction angle, and crystallite size of chemically synthesized Ag2O particles.(b) shows the parameters, miller indices, diffraction angle, and crystallite size of the green-synthesized Ag2O particles.

Figure 5 .
Figure 5. Cytotoxicity evaluation of both green-and chemically synthesized Ag2O particles against MCF-7 cell lines.

Figure 5 .
Figure 5. Cytotoxicity evaluation of both green-and chemically synthesized Ag 2 O particles against MCF-7 cell lines.

Figure 8 .
Figure 8. Schematic flow chart of chemically and green-synthesized Ag2O particles.

Figure 8 .
Figure 8. Schematic flow chart of chemically and green-synthesized Ag 2 O particles.

Table 1 .
(a) shows the parameters, miller indices, diffraction angle, and crystallite size of chemically synthesized Ag 2 O particles.(b) shows the parameters, miller indices, diffraction angle, and crystallite size of the green-synthesized Ag 2 O particles.