Enhancing Emission and Stability in Na-Doped Cs3Cu2I5 Nanocrystals

Lead-free Cs3Cu2I5 metal halides have garnered significant attention recently due to their non-toxic properties and deep-blue emission. However, their relatively low photoluminescence quantum efficiency and poor stability have limited their applications. In this work, sodium iodide (NaI) is used to facilitate the synthesis of Cs3Cu2I5 nanocrystals (NCs), demonstrating improved photoluminescence intensity, photoluminescence quantum yield, and stability. Systematic optoelectronic characterizations confirm that Na+ is successfully incorporated into the Cs3Cu2I5 lattice without altering its crystal structure. The improved Photoluminescence Quantum Yield (PLQY) and stability are attributed to the strengthened chemical bonding, which effectively suppresses vacancy defects in the lattice. Additionally, light-emitting diodes (LEDs) based on 10% NaI-doped Cs3Cu2I5 NCs were assembled, emitting vibrant blue light with a maximum radiant intensity of 82 lux and Commission Internationale de l’Eclairage (CIE) chromaticity coordinates of (0.15, 0.1). This work opens new possibilities for commercial lighting display applications.

Among various lead-free perovskites, copper halide perovskites like Cs 3 Cu 2 I 5 have shown promise with robust self-trapped exciton (STE) emissions [12][13][14].Since 2019, further insights into the STE mechanisms of Cs 3 Cu 2 I 5 have been revealed by Cheng and colleagues, attracting significant attention for its pure-blue emissions [15].Investigations by Wang et al. [16] and Zhao et al. [17] demonstrated high-efficiency deep-blue and cold-white UV-pumped LEDs using Cs 3 Cu 2 I 5 , achieving high color rendering indices (CRI) up to 90.However, Cs 3 Cu 2 I 5 is susceptible to phase transitions under high radiation and in polar solvents, which impairs its emission performance [13,18,19].Moreover, its photoluminescence quantum yield (PLQY) lags that of lead-based materials, making enhancements in PLQY and stability vital for its application [20][21][22][23].
In this study, we employ a Na-doping strategy in Cs 3 Cu 2 I 5 nanocrystals to enhance both PLQY and stability.Our systematic characterizations show successful interstitial doping of Na + , which notably improves the PL intensity (100% enhancement), the PLQY (10% enhancement), and the stability (30% enhancement) by minimizing defects and inhibiting ion migration.Moreover, stable light-emitting diodes (LEDs) have been fabricated, and blue light which is close to the standard blue spectrum has been achieved.

Structural and Morphological Characteristics
A series of xNaI-Cs 3 Cu 2 I 5 (x = 0, 5%, 10%, 15%) nanocrystals (NCs) were synthesized using an anti-solvent method, as illustrated in Figure 1a.Note that the ratio of CsI and CuI in the precursor is optimized at 2:1 to ensure pure phase and high PL intensity, as shown and explained in the supporting information (Figure S1).In addition, for a better clarity, the content of Na in the final product is calculated by the quantitative X-ray photoelectron spectroscopy (XPS) analysis as 6.32% for the 10% NaI-doped precursor.The phase and structure of the samples were characterized by X-ray diffraction (XRD).As depicted in Figure 1b, the XRD patterns confirm that all NCs crystallize in the orthorhombic system with a Pnma space group.The diffraction peaks closely match the standard PDF#450077 (JCPDS) [31,32], confirming the crystallinity of the samples and indicating that Na + doping does not alter the Cs 3 Cu 2 I 5 crystal lattice structure.The primary peaks at 13.1   , and 30.6 • correspond to the (111), ( 002), ( 122), (312), ( 222), ( 131) and (313) planes of Cs 3 Cu 2 I 5 , respectively.The Rietveld refinement of the XRD pattern is shown in Figure S2, reconfirming the space group and revealing the lattice parameters of the Na-dope Cs 3 Cu 2 I 5 .As shown in Figure 1c, the peak at 25.6 • remains unchanged with increasing Na + concentration, indicating stable lattice integration.Additionally, there are no NaI-related diffraction peaks observed at different doping concentrations, further confirming the successful incorporation of Na + into the Cs 3 Cu 2 I 5 lattice.A detailed analysis of the XRD patterns also reveals additional peaks at 27.6 • and 39.  alkali metal cations [24][25][26][27][28][29].For instance, Na + -doping in CsPbBr3 and Cs2AgInCl6 significantly improved PLQY, reducing nonradiative recombination and effectively controlling self-trapped excitons (STEs) [6,30].These advancements underscore the potential of a tailored doping strategy for Cs3Cu2I5 to boost its emission performance and stability.
In this study, we employ a Na-doping strategy in Cs3Cu2I5 nanocrystals to enhance both PLQY and stability.Our systematic characterizations show successful interstitial doping of Na + , which notably improves the PL intensity (100% enhancement), the PLQY (10% enhancement), and the stability (30% enhancement) by minimizing defects and inhibiting ion migration.Moreover, stable light-emitting diodes (LEDs) have been fabricated, and blue light which is close to the standard blue spectrum has been achieved.

Structural and Morphological Characteristics
A series of xNaI-Cs3Cu2I5 (x = 0, 5%, 10%, 15%) nanocrystals (NCs) were synthesized using an anti-solvent method, as illustrated in Figure 1a.Note that the ratio of CsI and CuI in the precursor is optimized at 2:1 to ensure pure phase and high PL intensity, as shown and explained in the supporting information (Figure S1).In addition, for a better clarity, the content of Na in the final product is calculated by the quantitative X-ray photoelectron spectroscopy (XPS) analysis as 6.32% for the 10% NaI-doped precursor.The phase and structure of the samples were characterized by X-ray diffraction (XRD).As depicted in Figure 1b, the XRD patterns confirm that all NCs crystallize in the orthorhombic system with a Pnma space group.The diffraction peaks closely match the standard PDF#450077 (JCPDS) [31,32], confirming the crystallinity of the samples and indicating that Na + doping does not alter the Cs3Cu2I5 crystal lattice structure.The primary peaks at 13.1°, 15.1°, 23.9°, 25.6°, 26.3°, 28.2°, and 30.6° correspond to the (111), (002), ( 122), (312), ( 222), ( 131) and (313) planes of Cs3Cu2I5, respectively.The Rietveld refinement of the XRD pattern is shown in Figure S2, reconfirming the space group and revealing the lattice parameters of the Na-dope Cs3Cu2I5.As shown in Figure 1c, the peak at 25.6° remains unchanged with increasing Na + concentration, indicating stable lattice integration.Additionally, there are no NaI-related diffraction peaks observed at different doping concentrations, further confirming the successful incorporation of Na + into the Cs3Cu2I5 lattice.A detailed analysis of the XRD patterns also reveals additional peaks at 27.6° and 39.5°, which are attributable to the (110) and (200) planes of the excess CsI.The morphology and fine structure of the obtained nanocrystals were further analyzed using high-resolution transmission electron microscopy (HRTEM).Compared to the control sample, Na + doping can significantly improve the crystallinity of the nanocrystals, resulting in larger crystal sizes (Figure 2a,b).This result is in consistent with the analysis of the XRD pattern, as shown in Table S1.The inserted HRTEM images of Cs 3 Cu 2 I 5 and 10%NaI-Cs 3 Cu 2 I 5 NCs were analyzed to characterize the fine lattice structure.For Cs 3 Cu 2 I 5 NCs, the lattice spacing is 3.37 Å, consistent with the lattice plane of (222).10%NaI-Cs 3 Cu 2 I 5 shows a lattice spacing of 3.29 Å, aligning with the lattice plane of (130), reaffirming that Na + doping does not alter the crystal structure, corroborating the XRD pattern.Both samples display distinct and regular lattice fingers, indicating high crystallinity (Figure S3).In addition, as shown in Figure 2c,d, the average diameter of Cs 3 Cu 2 I 5 is 1.76 nm with a size deviation of ±0.576 nm, while the average diameter of 10%NaI-Cs 3 Cu 2 I 5 is 2.88 nm with a size deviation of ±0.811 nm, increased by 63.6%, which also confirms the formation of higher quality Cs 3 Cu 2 I 5 NCs.Moreover, Figure 2e,f showcase the high-resolution elemental mapping images of Cs 3 Cu 2 I 5 and 10%NaI-Cs 3 Cu 2 I 5 NCs, further confirming the uniform doping and distribution of Na + and the formation of high-quality nanocrystals.
Nanomaterials 2024, 14, 1118 3 of 10 The morphology and fine structure of the obtained nanocrystals were further analyzed using high-resolution transmission electron microscopy (HRTEM).Compared to the control sample, Na + doping can significantly improve the crystallinity of the nanocrystals, resulting in larger crystal sizes (Figure 2a,b).This result is in consistent with the analysis of the XRD pattern, as shown in Table S1.The inserted HRTEM images of Cs3Cu2I5 and 10%NaI-Cs3Cu2I5 NCs were analyzed to characterize the fine lattice structure.For Cs3Cu2I5 NCs, the lattice spacing is 3.37 Å, consistent with the lattice plane of (222).10%NaI-Cs3Cu2I5 shows a lattice spacing of 3.29 Å, aligning with the lattice plane of (130), reaffirming that Na + doping does not alter the crystal structure, corroborating the XRD pattern.Both samples display distinct and regular lattice fingers, indicating high crystallinity (Figure S3).In addition, as shown in Figure 2c,d, the average diameter of Cs3Cu2I5 is 1.76 nm with a size deviation of ±0.576 nm, while the average diameter of 10%NaI-Cs3Cu2I5 is 2.88 nm with a size deviation of ±0.811 nm, increased by 63.6%, which also confirms the formation of higher quality Cs3Cu2I5 NCs.Moreover, Figure 2e,f showcase the high-resolution elemental mapping images of Cs3Cu2I5 and 10%NaI-Cs3Cu2I5 NCs, further confirming the uniform doping and distribution of Na + and the formation of highquality nanocrystals.

Optical Properties
Figure 3a shows the PL intensity of Cs3Cu2I5 nanocrystals doped with different concentrations of NaI.Notably, as the doping concentration increases, the PL intensity first increases and then decreases.The maximum PL intensity is achieved when the NaI doping concentration reaches 10%, which shows a 100% improvement compared with the control samples.Figure 3b displays the excitation-wavelength-dependent PL characteristics of the 10%NaI-Cs3Cu2I5 NCs.It is evident that the PL spectra at different excitation wavelengths maintain the same features, showing the same peak positions for the undoped sample.This consistency indicates that NaI doping does not alter the emission mechanism.

Optical Properties
where IS represents the integrated area of the PL spectrum, and ER and ES correspond to the integrated areas of the excitation spectrum without and with the sample, respectively.Figure 3c,d show the PLQY of Cs3Cu2I5 NCs without and with NaI doping.The results prove that NaI doping can enhance the emission performance, yielding a PLQY value of over 90% which is among the high-level PLQY values in the literature reports (Table S2).To further understand the impact of NaI doping on the excited state dynamics, timeresolved photoluminescence spectra were obtained of Cs3Cu2I5 NCs and 10% NaI-Cs3Cu2I5 NCs under 290 nm pulsed laser excitation, as shown in Figure 3e,f.The obtained data were fitted by bi-exponential mode (Equation ( 2)), with the two components attributed to radiative recombination (longer lifetime τ2) and trap-mediated recombination (shorter lifetime τ1).Here, A(t) signifies the PL intensity at time t.The parameters A1 and A2 are utilized in the fitting process to represent the amplitudes of two exponential decay components.Meanwhile, τ1 and τ2 are employed to denote the lifetimes associated with these two exponential decay terms.

𝐴 𝑡 = A exp − 𝑡 τ + A exp − 𝑡 τ
(2) For the Cs3Cu2I5 and 10%NaI-Cs3Cu2I5 samples, their average lifetimes have been determined to be 1267 ns and 1480 ns, and the corresponding results are shown in Table S3.The calculated τ1 is improved to 1466 ns for the doped sample, implying that the trap or defect concentration is reduced by the Na + dopant.The fitted value of calculated τ2 is also increased, demonstrating that NaI effectively decreases the potential non-radiative recombination.Therefore, Na + doping shows enhanced photoluminescence performance.This can be partly attributed to the enhanced crystallinity of Na-doped samples, and more underlying mechanisms will be discussed in the following text.Photoluminescence quantum yield (PLQY) is an important parameter describing emission performance, defined as the ratio of the number of emitted photons to the number of absorbed photons.The specific formula for calculating is as follows: where I S represents the integrated area of the PL spectrum, and E R and E S correspond to the integrated areas of the excitation spectrum without and with the sample, respectively.Figure 3c,d show the PLQY of Cs 3 Cu 2 I 5 NCs without and with NaI doping.The results prove that NaI doping can enhance the emission performance, yielding a PLQY value of over 90% which is among the high-level PLQY values in the literature reports (Table S2).
To further understand the impact of NaI doping on the excited state dynamics, timeresolved photoluminescence spectra were obtained of Cs 3 Cu 2 I 5 NCs and 10% NaI-Cs 3 Cu 2 I 5 NCs under 290 nm pulsed laser excitation, as shown in Figure 3e,f.The obtained data were fitted by bi-exponential mode (Equation ( 2)), with the two components attributed to radiative recombination (longer lifetime τ 2 ) and trap-mediated recombination (shorter lifetime τ 1 ).Here, A(t) signifies the PL intensity at time t.The parameters A 1 and A 2 are utilized in the fitting process to represent the amplitudes of two exponential decay components.Meanwhile, τ 1 and τ 2 are employed to denote the lifetimes associated with these two exponential decay terms.
For the Cs 3 Cu 2 I 5 and 10%NaI-Cs 3 Cu 2 I 5 samples, their average lifetimes have been determined to be 1267 ns and 1480 ns, and the corresponding results are shown in Table S3.The calculated τ 1 is improved to 1466 ns for the doped sample, implying that the trap or defect concentration is reduced by the Na + dopant.The fitted value of calculated τ 2 is also increased, demonstrating that NaI effectively decreases the potential non-radiative recombination.Therefore, Na + doping shows enhanced photoluminescence performance.This can be partly attributed to the enhanced crystallinity of Na-doped samples, and more underlying mechanisms will be discussed in the following text.

Stability
We conducted comprehensive environmental stability studies to evaluate the suitability of 10%NaI-Cs 3 Cu 2 I 5 NCs for LED applications, including air exposure, temperature, moisture, and UV irradiation.In the initial experiment, the nanocrystals were exposed to ambient air for six months, and their X-ray diffraction (XRD) patterns demonstrate exceptional phase stability, as shown in Figure 4a, indicating that even after prolonged exposure to external conditions, their crystal structure does not show significant changes.Meanwhile, tracking the photoluminescence performance further proves the significant role of NaI doping in enhancing air stability, as shown in Figure 4b.Compared to the undoped samples which maintain 81.1% of their PL intensity after three months of aging in air, the 10%NaI-Cs 3 Cu 2 I 5 NCs did not show significant PL intensity attenuation.

Stability
We conducted comprehensive environmental stability studies to evaluate the suitability of 10%NaI-Cs3Cu2I5 NCs for LED applications, including air exposure, temperature, moisture, and UV irradiation.In the initial experiment, the nanocrystals were exposed to ambient air for six months, and their X-ray diffraction (XRD) patterns demonstrate exceptional phase stability, as shown in Figure 4a, indicating that even after prolonged exposure to external conditions, their crystal structure does not show significant changes.Meanwhile, tracking the photoluminescence performance further proves the significant role of NaI doping in enhancing air stability, as shown in Figure 4b.Compared to the undoped samples which maintain 81.1% of their PL intensity after three months of aging in air, the 10%NaI-Cs3Cu2I5 NCs did not show significant PL intensity attenuation.We used thermogravimetric analysis to assess the thermal stability of Cs3Cu2I5 and 10%NaI-Cs3Cu2I5 NCs, with the results shown in Figure 4c.It was found that the decomposition temperature of 10%NaI-Cs3Cu2I5 NCs is higher than undoped samples, which may be related to the formation of high-quality crystals induced by doping.Furthermore, we investigated photoluminescence changes under prolonged 254 nm UV lamp irradiation to study the stability of these nanocrystals in more detail.The results, shown in Figure 4d, demonstrate that the 10% doped nanocrystals exhibit better stability than the undoped nanocrystals (88.2%), with photoluminescence intensity retaining 93.7% of the initial value after 60 min of UV irradiation.The accelerated humidity stability tests by dispersing We used thermogravimetric analysis to assess the thermal stability of Cs 3 Cu 2 I 5 and 10%NaI-Cs 3 Cu 2 I 5 NCs, with the results shown in Figure 4c.It was found that the decomposition temperature of 10%NaI-Cs 3 Cu 2 I 5 NCs is higher than undoped samples, which may be related to the formation of high-quality crystals induced by doping.Furthermore, we investigated photoluminescence changes under prolonged 254 nm UV lamp irradiation to study the stability of these nanocrystals in more detail.The results, shown in Figure 4d, demonstrate that the 10% doped nanocrystals exhibit better stability than the undoped nanocrystals (88.2%), with photoluminescence intensity retaining 93.7% of the initial value after 60 min of UV irradiation.The accelerated humidity stability tests by dispersing the NCs into a mixture of isopropanol and water were also conducted, revealing that 10%NaI-Cs 3 Cu 2 I 5 NCs have better humidity stability, as shown in Figure S4.

Mechanisms of the Enhanced Photoluminescence Performance and Stability
To understand the mechanisms underlying the improved PL, PLQY and stability in NaI-doped Cs 3 Cu 2 I 5 NCs, X-ray Photoelectron Spectroscopy (XPS) measurements were performed to examine the chemical state and chemical bonds after NaI doping.In Figure 5a, the survey spectra of the 10% NaI-doped and undoped samples are presented.Through semi-quantitative analysis of different elements, we can observe a significant change in the Cu-I ratio in the NCs before and after doping, shifting from 2:2.8 in the undoped samples to 2:3.04.This intuitively indicates that NaI doping has significantly altered the potential path of crystal growth, effectively suppressing the formation of I vacancies.Additionally, a notable Na 1s signal appears at 1071 eV (Figure 5b), indicating that Na + has been successfully integrated into the NCs.Furthermore, the fine spectra of I 3d and Cu 2p are shown in Figure 5c,d, respectively.After Na + doping, the peak positions of I 3d and Cu 2p have shifted towards higher binding energy by 0.43 eV and 0.61 eV, respectively.This change suggests that the chemical bonding between Cu + and I − in Cs 3 Cu 2 I 5 NC has strengthened, which helps suppress I vacancy defects and enhances the PL, PLQY, and stability.
the NCs into a mixture of isopropanol and water were also conducted, revealing that 10%NaI-Cs3Cu2I5 NCs have better humidity stability, as shown in Figure S4.

Mechanisms of the Enhanced Photoluminescence Performance and Stability
To understand the mechanisms underlying the improved PL, PLQY and stability in NaI-doped Cs3Cu2I5 NCs, X-ray Photoelectron Spectroscopy (XPS) measurements were performed to examine the chemical state and chemical bonds after NaI doping.In Figure 5a, the survey spectra of the 10% NaI-doped and undoped samples are presented.Through semi-quantitative analysis of different elements, we can observe a significant change in the Cu-I ratio in the NCs before and after doping, shifting from 2:2.8 in the undoped samples to 2:3.04.This intuitively indicates that NaI doping has significantly altered the potential path of crystal growth, effectively suppressing the formation of I vacancies.Additionally, a notable Na 1s signal appears at 1071 eV (Figure 5b), indicating that Na + has been successfully integrated into the NCs.Furthermore, the fine spectra of I 3d and Cu 2p are shown in Figure 5c,d, respectively.After Na + doping, the peak positions of I 3d and Cu 2p have shifted towards higher binding energy by 0.43 eV and 0.61 eV, respectively.This change suggests that the chemical bonding between Cu + and I -in Cs3Cu2I5 NC has strengthened, which helps suppress I vacancy defects and enhances the PL, PLQY, and stability.

Demonstration of LEDs
The high-quality Cs3Cu2I5 nanocrystals synthesized via Na + doping, with their exceptional environmental stability, significantly improved PL, PLQY, and standard blue

Demonstration of LEDs
The high-quality Cs 3 Cu 2 I 5 nanocrystals synthesized via Na + doping, with their exceptional environmental stability, significantly improved PL, PLQY, and standard blue emission capability, are promising candidates for optoelectronic display applications.Here, we preliminarily demonstrate their application in down-conversion lighting.As shown in Figure 6a, down-conversion LED devices were fabricated by combining UV LED chips with our nanocrystal powders.Under a forward bias current of 15 mA, the LED emits vibrant blue light with a maximum achievable radiant intensity of 82 lux and exhibits CIE chromaticity coordinates of (0.15, 0.1), as shown in Figure 6b, meeting the requirements of standard blue display specified by National Television Standards Committee (NTSC) [33,34].To further improve the optical and photoluminescent properties of Cs 3 Cu 2 I 5 for practical applications, we should focus on fabricating high-quality films or crystals with stable local structures, reducing the recombination centers in the materials, introducing additional light-emitting centers such as rare-earth elements, and modifying the compositions such as manipulating the ratio of CsCu 2 I 3 and Cs 3 Cu 2 I 5 to obtain white-emitting LEDs.
emission capability, are promising candidates for optoelectronic display applications.Here, we preliminarily demonstrate their application in down-conversion lighting.As shown in Figure 6a, down-conversion LED devices were fabricated by combining UV LED chips with our nanocrystal powders.Under a forward bias current of 15 mA, the LED emits vibrant blue light with a maximum achievable radiant intensity of 82 lux and exhibits CIE chromaticity coordinates of (0.15, 0.1), as shown in Figure 6b, meeting the requirements of standard blue display specified by National Television Standards Committee (NTSC) [33,34].To further improve the optical and photoluminescent properties of Cs3Cu2I5 for practical applications, we should focus on fabricating high-quality films or crystals with stable local structures, reducing the recombination centers in the materials, introducing additional light-emitting centers such as rare-earth elements, and modifying the compositions such as manipulating the ratio of CsCu2I3 and Cs3Cu2I5 to obtain whiteemitting LEDs.

Conclusions
This study delves into the impact of alkali metal Na + doping on the PL intensity, PLQY and stability of Cs3Cu2I5 nanocrystals.Detailed structural characterization fully proved that Na + was successfully incorporated into the Cs3Cu2I5 crystals and significantly improved the crystallinity.Further photoluminescence performance characterization showed that as the Na + doping concentration increased, the PL intensity exhibited a trend of first rising and then falling, reaching the maximum PL at 10% Na + doping concentration with a high PLQY of over 90%.Moreover, the average PL lifetime was increased by 16.8% with 10% Na + doping.Various environmental stability tests showed that the doped Cs3Cu2I5 nanocrystals had lower sensitivity to air exposure, temperature changes, and UV light, processing excellent stability.The XPS results explained in depth the reasons for the improved PL intensity, PLQY, and stability of doped Cs3Cu2I5 nanocrystals, highlighting the stronger chemical bonding between Cu + and I -in the Cs3Cu2I5 nanocrystals, significantly suppressing the formation of I vacancy defects.Finally, we demonstrated the utilization of doped Cs3Cu2I5 nanocrystals in down-conversion LEDs, showing high-performance blue emission that meets NTSC standard displays, which opens more possibilities for potential commercial lighting display applications.

Conclusions
This study delves into the impact of alkali metal Na + doping on the PL intensity, PLQY and stability of Cs 3 Cu 2 I 5 nanocrystals.Detailed structural characterization fully proved that Na + was successfully incorporated into the Cs 3 Cu 2 I 5 crystals and significantly improved the crystallinity.Further photoluminescence performance characterization showed that as the Na + doping concentration increased, the PL intensity exhibited a trend of first rising and then falling, reaching the maximum PL at 10% Na + doping concentration with a high PLQY of over 90%.Moreover, the average PL lifetime was increased by 16.8% with 10% Na + doping.Various environmental stability tests showed that the doped Cs 3 Cu 2 I 5 nanocrystals had lower sensitivity to air exposure, temperature changes, and UV light, processing excellent stability.The XPS results explained in depth the reasons for the improved PL intensity, PLQY, and stability of doped Cs 3 Cu 2 I 5 nanocrystals, highlighting the stronger chemical bonding between Cu + and I -in the Cs 3 Cu 2 I 5 nanocrystals, significantly suppressing the formation of I vacancy defects.Finally, we demonstrated the utilization of doped Cs 3 Cu 2 I 5 nanocrystals in down-conversion LEDs, showing high-performance blue emission that meets NTSC standard displays, which opens more possibilities for potential commercial lighting display applications.

Synthesis of Na-Doped Cs 3 Cu 2 I 5 Nanocrystals
The synthesis of Cs 3 Cu 2 I 5 nanocrystals follows the widely used anti-solvent method at room temperature.In brief, 0.6 mmol of CsI and 0.3 mmol of CuI were dissolved in 7.5 mL of DMSO as the precursor in the glove box.Regarding the Na + -doped Cs 3 Cu 2 I 5 nanocrystals synthesis, a series of precursor solutions for xNaI-Cs 3 Cu 2 I 5 (x = 0, 5%, 10%, 15%) nanocrystals were prepared by co-solving NaI with molar ratios of 0, 5%, 10%, and 15% in the above precursor.As an example, 10% NaI-Cs 3 Cu 2 I 5 , 0.6 mmol of CsI, 0.3 mmol of CuI, and 0.015 mmol of NaI were diluted in 7.5 mL of DMSO, and sonicated until completely dissolved to form precursor solutions.Subsequently, 200 µL of the precursor solution was injected into 5 mL toluene under vigorous stirring in the air.Then, the solution was centrifuged for 5 min at 8000 rpm.After centrifugation, the supernatant was discarded, and the precipitate was redispersed in isopropanol to form a long-term stable colloidal solution for subsequent characterization.

Fabrication of LEDs
The centrifuged precipitate is dried in a vacuum drying oven at 60 °C and ground with an agate mortar to obtain a fine powder.Na-doped Cs 3 Cu 2 I 5 NCs powder, as blue light emitters, was mixed with PMMA in 1 mL of toluene at a weight ratio of 1:20 and stirred well.Finally, the paste-like mixture was dropped on a 290 nm UV LED chip and dried under vacuum at 60 • C for 1 h to prepare NCs-PMMA composite LEDs.

Characterizations
XRD was performed using a Bruker D8 X-ray diffractometer with a radiation source from the Cu target (KA = 1.5406Å).An FEI Tecnai G2 F20 transmission electron microscope (TEM) was used to assess the fine morphology and lattice structure; energy dispersive X-ray spectroscopy (EDXS) surface scan was used to obtain the elemental distribution (mapping) and EDX semi-quantitative data.XPS was conducted on a Thermo Scientific ESCALAB Xi+ instrument.Thermogravimetric analysis (TGA) was measured using a Discovery TGA 550 with a heating rate of 5 • C/min under a nitrogen atmosphere.The PL excitation (PLE) and PL spectra were measured using a Shimadzu RF-6000 fluorescence spectrophotometer.The measurement of photoluminescence quantum yield was performed using an Edinburgh FLS1000 with an integrating sphere, and the photoluminescence lifetime was obtained using an Edinburgh FLS1000 at the specified wavelengths with a microsecond pulsed laser, the measurement of absorption spectra was performed on a UV-Vis 1800 UV-Vis absorption spectrometer.

Figure
Figure 3a shows the PL intensity of Cs 3 Cu 2 I 5 nanocrystals doped with different concentrations of NaI.Notably, as the doping concentration increases, the PL intensity first increases and then decreases.The maximum PL intensity is achieved when the NaI doping concentration reaches 10%, which shows a 100% improvement compared with the control samples.Figure 3b displays the excitation-wavelength-dependent PL characteristics of the 10%NaI-Cs 3 Cu 2 I 5 NCs.It is evident that the PL spectra at different excitation wavelengths maintain the same features, showing the same peak positions for the undoped sample.This consistency indicates that NaI doping does not alter the emission mechanism.

Figure 4 .
Figure 4. (a) XRD patterns of the NCs before and after 6 months of aging.(b) Comparison of the stability in nitrogen and air for three months.(c) Thermogravimetric of doped and undoped NCs; (d) The PL spectra of xNaI-Cs3Cu2I5 (x = 0, 5%, 10%, 15%) under 60 min of UV irradiation.

Figure 4 .
Figure 4. (a) XRD patterns of the NCs before and after 6 months of aging.(b) Comparison of the stability in nitrogen and air for three months.(c) Thermogravimetric of doped and undoped NCs; (d) The PL spectra of xNaI-Cs 3 Cu 2 I 5 (x = 0, 5%, 10%, 15%) under 60 min of UV irradiation.

Figure 6 .
Figure 6.(a) Systematic illumination of the down-conversion LED.(b) CIE coordinate diagram of Na + doped Cs3Cu2I5 NCs-based LEDs.The inset is a photograph of a prepared blue-emitting LED based on Na + -doped Cs3Cu2I5 NCs.

Figure 6 .
Figure 6.(a) Systematic illumination of the down-conversion LED.(b) CIE coordinate diagram of Na + doped Cs 3 Cu 2 I 5 NCs-based LEDs.The inset is a photograph of a prepared blue-emitting LED based on Na + -doped Cs 3 Cu 2 I 5 NCs.