Next Article in Journal
Analysis of Heat Transfer Characteristics of a GnP Aqueous Nanofluid through a Double-Tube Heat Exchanger
Next Article in Special Issue
Revealing the Exciton Fine Structure in Lead Halide Perovskite Nanocrystals
Previous Article in Journal
Layer-Scale and Chip-Scale Transfer Techniques for Functional Devices and Systems: A Review
Previous Article in Special Issue
Sulvanites: The Promise at the Nanoscale
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 11
Issue 4
10.3390/nano11040843
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Organic-to-Aqueous Phase Transfer of Alloyed AgInS2-ZnS Nanocrystals Using Simple Hydrophilic Ligands: Comparison of 11-Mercaptoundecanoic Acid, Dihydrolipoic Acid and Cysteine

by
Patrycja Kowalik
1,2,
Piotr Bujak
1,*,
Mateusz Penkala
3 and
Adam Pron
1
1
Faculty of Chemistry, Warsaw University of Technology, Noakowskiego 3, 00-664 Warsaw, Poland
2
Faculty of Chemistry, University of Warsaw, Pasteura 1 Str., PL-02-093 Warsaw, Poland
3
Institute of Chemistry, Faculty of Mathematics, Physics and Chemistry, University of Silesia, Szkolna 9, 40-007 Katowice, Poland
*
Author to whom correspondence should be addressed.
Nanomaterials 2021, 11(4), 843; https://doi.org/10.3390/nano11040843
Submission received: 28 February 2021 / Revised: 18 March 2021 / Accepted: 22 March 2021 / Published: 25 March 2021
(This article belongs to the Special Issue Nanocrystals: Synthesis, Properties and Applications)
Browse Figures
Review Reports Versions Notes

Abstract

:
The exchange of primary hydrophobic ligands for hydrophilic ones was studied for two types of alloyed AgInS2-ZnS nanocrystals differing in composition and by consequence exhibiting two different emission colors: red (R) and green (G). Three simple hydrophilic ligands were tested, namely, 11-mercaptoundecanoic acid, dihydrolipoic acid and cysteine. In all cases, stable aqueous colloidal dispersions were obtained. Detailed characterization of the nanocrystal surface before and after the ligand exchange by NMR spectroscopy unequivocally showed that the exchange process was the most efficient in the case of dihydrolipoic acid, leading to the complete removal of the primary ligands with a relatively small photoluminescence quantum yield drop from 68% to 40% for nanocrystals of the R type and from 48% to 28% for the G ones.

Graphical Abstract

1. Introduction

Colloidal nanocrystals of inorganic semiconductors attract the attention of materials science and materials chemistry communities mainly because of their tunable photo- and electroluminescence properties [1]. Among a plethora of binary, ternary and quaternary nanocrystals of different types, alloyed AgInS2-ZnS ones deserve special interest for two main reasons: (i) they do not contain toxic elements such as previously studied cadmium or lead chalcogenides, which makes them suitable for diversified biomedical applications; (ii) their photoluminescence spectrum can be precisely tuned by adjusting their composition. Moreover, in recent years, several efficient preparation procedures were elaborated by various research groups, leading to alloyed AgInS2-ZnS nanocrystals exhibiting high photoluminescence quantum yield (PLQY) values [2,3,4,5,6,7,8,9].
For many applications, including biomedical ones, nanocrystals of hydrophilic nature are needed, capable of forming stable aqueous colloidal solutions. Two strategies can be envisioned in the preparation of such nanocrystals [4,10]. In the first one, the nanocrystals are formed in aqueous solutions and their colloidal stability in this medium is assured by capping ligands of hydrophilic nature. The second one consists of preparing nanocrystals in non-aqueous media where they are stabilized with hydrophobic ligand. In the second step, the exchange of hydrophobic ligands for hydrophilic ones is performed, leading to the nanocrystals’ transfer to water, where they form stable dispersions. However, taking into account the possible versatility of the surface modification, the second method seems more appropriate. This especially applies to hybrid systems frequently containing complicated bio-active molecules. The use of hydrophilic primary ligands severely limits the number of possible surface modification pathways as well as ligand exchange procedures [4]. Moreover, it sometimes makes the introduction of biologically active molecules difficult.
As already mentioned, initial research on highly luminescent hydrophilic semiconductor nanocrystals was focused on binary cadmium or lead chalcogenides whose emission spectrum was tuned either by alloying with other binary semiconductors or by the quantum confinement effect [11]. However, in the majority of biomedical applications, the toxicity of cadmium constituted a real problem, especially for in vivo experiments. The leaching of cadmium cations to the environment could frequently be observed, despite depositions of protective layers of different types [12,13,14]. For these reasons, intensive research started, aimed at the preparation of free of toxic cadmium, ternary (AgInS2, AgInS2) and quaternary (AgInS2-ZnS and CuInS2-ZnS) nanocrystals either alloyed or core/shell type. Recent investigations demonstrated that their PLQY values could match those measured for cadmium chalcogenides [2,3,4,5,6,7,8,9]. Hydrophilic AgInS2-ZnS nanocrystals capped with bioactive ligands are especially interesting because in recent years they have been extensively tested in anti-cancer therapy [15,16,17,18,19,20,21].
We shared this interest working in the past decade on stoichiometric (AgInS2) and nonstoichiometric (Ag-In-S) ternary nanocrystals as well as alloyed quaternary ones (AgInS2-ZnS) [22,23,24,25]. We also tested them in anti-cancer therapies [17,18,20,21]. From this perspective, the elaboration of efficient ligand exchange procedures, facilitating the transfer of the modified nanocrystals to water, is of crucial importance. In this paper, we comparatively describe the ligand exchange-induced hydrophilization of two types of alloyed AgInS2-ZnS nanocrystals differing in composition and by consequence emitting light of different colors: red (R) and green (G). Three popular hydrophilic ligands were tested: 11-mercaptoundecanoic acid (MUA), dihydrolipoic acid (DHLA) and L-cysteine (Cys). Detailed characterization of nanocrystals and their surface was performed prior to the ligand exchange and after the exchange, which involved the determination of their size and shape, composition, crystal structure and luminescent properties. NMR was used for the identification of primary ligands and the ligands introduced upon the exchange.

2. Materials and Methods

2.1. Materials

Silver nitrate (99%), indium(III) chloride (98%), zinc stearate (technical grade), 1-dodecanethiol (DDT, 98%), sulfur (99%), 1-octadecene (ODE, 90%), oleylamine (OLA, 70%), 11-mercaptoundecanoic acid (MUA, 95%), lipoic acid (LA, 99%), NaBH4 (96%), L-cysteine (Cys, 96%), CDCl3 (100%, 99.96 atom% D), D2O (100%, 99.99 atom% D), and NaOD (40 wt. % in D2O, 99.5 atom% D) were supplied by Sigma-Aldrich (Merk KGaA, Darmstadt, Germany).

2.2. Preparation of AgInS2-ZnS Nanocrystals (R-“Red” and G-“Green” Types)

Initial hydrophobic AgInS2-ZnS nanocrystals (R and G) were synthesized by a modification of the method described in literature [22,23]. Detailed description of the applied procedure can be found in Supplementary Materials.

2.3. Primary Ligand Exchange for 11-Mercaptoundecanoic Acid (MUA)

All operations were carried out under a constant dry argon flow. A mixture of MUA (0.5 g, 2.3 mmol) and NaOH (0.1 g, 2.5 mmol) in water (10 mL) was heated with stirring at 50 °C until a homogenous solution was formed. Then, a toluene dispersion (10 mL) of nanocrystals (R or G) prepared as described in Supplementary Materials was injected into this solution. The as-obtained two-phase mixture was heated at 80 °C for 8 h under argon. After cooling, the reaction mixture was centrifuged to obtain a complete phase separation; the solid and the organic phase were discarded. The aqueous phase was then mixed with 20 mL of acetone which led to the precipitation of R-MUA (or G-MUA) nanocrystals. After centrifugation, the nanocrystals were redispersed in 10 mL of water.

2.4. Primary Ligand Exchange for Dihydrolipoic Acid (DHLA)

All operations were carried out under a constant dry argon flow. To a solution of lipoic acid (0.2 g, 0.97 mmol) and NaOH (0.05 g, 1.25 mmol) in water (10 mL), sodium borohydride (0.08 g, 2.11 mmol) was added and the resulting mixture was stirred at 40 °C under argon for 1 h. Then, a toluene dispersion (10 mL) of nanocrystals (R or G) prepared as described in Supplementary Materials was injected into this solution. The mixture was stirred at 40 °C for 4 h and additionally at room temperature for 8 h. Then, it was centrifuged to obtain a complete phase separation and the organic phase was discarded. The remaining aqueous phase was then mixed with 20 mL of acetone which led to the precipitation of R-DHLA (or G-DHLA) nanocrystals. After centrifugation, the nanocrystals were redispersed in 10 mL of water.

2.5. Primary Ligand Exchange for L-Cysteine (Cys)

All operations were carried out under a constant dry argon flow. A mixture of L-cysteine (3.0 g, 24.8 mmol), NaOH (0.05 g, 1.25 mmol) in water (10 mL) was heated with stirring at 40 °C until a homogenous solution was formed. Then, the toluene dispersion (10 mL) of nanocrystals (R-Cys or G) prepared as described in Supplementary Materials was injected into this solution. The as-obtained two-phase mixture was heated at 40 °C for an additional 4 h under argon. After cooling, the reaction mixture was centrifuged to obtain a complete phase separation, and the organic phase was discarded. The remaining aqueous phase was then mixed with 20 mL of acetone which led to the precipitation of R-Cys (or G-Cys) nanocrystals. After centrifugation, the nanocrystals were redispersed in 10 mL of water.

2.6. Characterization

Elemental analysis was performed with a multichannel Quantax 400 energy-dispersive X-ray spectroscopy (EDS) system with a 125 eV xFlash detector 5010 (Bruker, Billerica, MA, USA) using a 15 kV electron beam energy. Transmission electron microscopy (TEM) studies were carried out on a Zeiss Libra 120 electron microscope operating (Carl Zeiss, Oberkochen, Germany) at 120 kV. Emission spectra were recorded using a Hitachi F-7000 spectrophotometer (Hitachi, Tokyo, Japan) with a standard 10 mm cell. The quantum yields of luminescence were determined by the absolute method at room temperature, using an integrating sphere with solvent as a blank. 1H, and 1H-1H COSY NMR spectra were recorded on a Bruker Avance (400 MHz) spectrometer (Bruker, Billerica, MA, USA) and referenced with respect to tetramethylsilane (TMS) and solvents.

3. Results and Discussion

The ligand exchange described in this research was carried out for two types of alloyed AgInS2-ZnS nanocrystals, termed R (red) and G (green), respectively, differing in composition and by consequence emitting light of different wavelengths. These nanocrystals were prepared through the injection of sulfur dissolved in oleylamine (S/OLA) to a mixture of AgNO3, InCl3, zinc stearate, and 1-dodecanothiol (DDT) dissolved in 1-octadecene (ODE). This procedure allows for obtaining alloyed nanocrystals of orthorhombic AgInS2—hexagonal ZnS smoothly varying in composition via strict control of the precursor molar ratios [23,24]. As a result, their luminescence can be precisely tuned over essentially the entire range of the visible spectrum, still retaining high photoluminescence quantum yield (PLQY) values.
R and G nanocrystals were spherical in shape. Their diameters, as determined from TEM images, were 6.2 ± 0.9 nm and 4.2 ± 0.6 nm, respectively (Figure 1). The results of EDS analysis led to the following empirical formulae: Ag1.00In2.80Zn1.30S4.00(S6.00) (R) and Ag1.00In1.50Zn7.80S17.0(S10.50) (G) (see Figure S1 in Supplementary Materials). The emission spectra of both types of nanocrystals showed a rather broad peak at 720 nm (R) and 543 nm (G) (see Figure 2). High values of their PLQYs should be noted (67% (R) and 58% (G)) and for this reason they were selected for the ligand exchange investigations. All microscopic and spectroscopic data of the studied nanoparticles are collected in Table 1.
For the identification of primary ligands, we used a procedure previously elaborated in our group and applied with success to nanocrystals of various types [26]. It consists of dissolving the inorganic core followed by extraction of the organic residue which is then investigated by 1H NMR. Application of this procedure to R and G nanocrystals allowed for unequivocal identification of two types of ligands: stearic acid anions bound to zinc cations and 1-aminooctadecane co-ordinated to indium cations. The latter is a product of the hydrogenation of OLA occurring in the course of the nanocrystals’ synthesis [24].
Three simple and popular hydrophilic ligands were selected for the investigation of the ligand exchange process, namely, 11-mercaptoundecanoic acid (MUA), dihydrolipoic acid (DHLA) and L-cysteine (Cys) (Scheme 1).
Ligands were exchanged in one step. In a typical procedure, dispersions of R or G nanocrystals in toluene were added to a saturated alkaline solution of either MUA or DHLA or Cys. The resulting mixtures were vigorously stirred for 4 to 8 h. Then, the nanocrystals were precipitated with acetone and separated by centrifugation. Finally, they were redispersed in water. The chemical compositions of the resulting nanocrystals (R-MUA, R-DHLA, R-Cys, G-MUA, G-DHLA, G-Cys) were determined by EDS (for the corresponding spectra see Figures S2 and S3). Their extended characterization data are collected in Table 1.
11-Mercaptoundecanoic acid (MUA) seems to be the most popular ligand used for rendering binary and ternary nanocrystals hydrophilic via the exchange of hydrophobic primary ligands [27,28]. At room temperature, it is practically insoluble in water. Thus, the exchange of ligands had to be carried out at 50 °C in a saturated solution of MUA formed by mixing 500 mg of MUA and 100 mg of NaOH in 10 mL of water.
In Figure 3, the 1H NMR spectrum of MUA dissolved in NaOD/D2O (pH ~10) is compared with the spectra of aqueous dispersions of R-MUA and G-MUA. Careful analysis of the spectra registered for nanocrystal dispersions in the spectral range of signals originating from the methylene groups of long aliphatic chains (1.2–1.5 ppm) seems to indicate incomplete exchange of primary ligands for MUA. This effect is more pronounced in the spectrum of R-MUA.
Before discussing in detail the spectra of R-MUA and G-MUA dispersions, it is instructive to describe specific features of the spectrum of “free” MUA. Two distinctive triplets can be distinguished in it: at 2.13 and 2.49 ppm. They correspond to methylene protons in α position with respect to -COOH and -SH terminal groups. In the range of 1.47–1.59 ppm, overlapping multiplets originating from β-methylene protons are observed. In the spectrum of the dispersion of R-MUA, a slight shift of the triplet corresponding to -CH2COOH is observed from 2.13 to ~2.16 ppm. Significantly more pronounced changes are observed in the case of the signals originating from to -CH2SH. The presence of three poorly resolved co-existing triplets can be distinguished at 2.49, 2.68 and 2.77 ppm which can be interpreted in terms of three non-equivalent co-ordination sites imposing different conformations of the bound ligands. Large shifts of the signal corresponding to -CH2CH2SH additionally corroborate the binding of MUA to the nanocrystal surface. The same effect was previously observed in the case of primary ligands binding to the surface of growing Ag2S and AgInS2 nanocrystals [25]. The presence of only one triplet attributable to -CH2SH in the spectrum of the dispersion of G-MUA indicates that all MUA are in this case spectroscopically equivalent. All these attributions were verified through the analysis of 1H-1H COSY spectra presented in Supplementary Materials (Figures S4 and S5).
Chemical composition of nanocrystals before and after the exchange of ligands can be determined from the EDS data. First, it provides information on the molar ratio of elements constituting the inorganic core. Second, it allows for the estimation of the organic part contribution to the total mass of ligand-capped nanocrystals. Carbon is the diagnostic element here because it is present only in the organic part. A small drop in the content of carbon is observed after the ligand exchange, i.e., the transformation of R into R-MUA and G into G-MUA (see Table 1). This decrease in the content of carbon is caused by replacing longer aliphatic chains (C18) of primary ligands in R and G by shorter ones (C11) in R-MUA and G-MUA. This drop is lower than expected, indicating incomplete ligand exchange, consistent with the obtained NMR data (vide supra).
As judged from elemental analysis, ligand exchange induces a decrease in the content of indium. For G-MUA, a drop in the content of zinc is additionally observed. The case of sulfur is more complex. In R and G, all sulfur originates from the inorganic core since the primary ligands do not contain this element. Upon ligand exchange, organic sulfur is introduced, and in R-MUA and G-MUA organic and inorganic forms of this element are present. Irrespective of this, after the exchange of ligands, the content of sulfur significantly exceeds the value expected from the molar ratio of metals in the inorganic core. This excess could in principle be assigned to the ligand-originating sulfur.
Although ligand exchange induces significant changes even in the inorganic core composition, they have a rather small effect on the nanocrystal size, which is diminished by less than 10% for R-MUA and nearly 11% in the case of G-MUA. The exchange procedure has the most pronounced effect of PLQY values, which drop from 67% in R to 30% in R-MUA and from 48% in G to 25% in G-MUA, still remaining among the highest reported for aqueous dispersions of semiconductor nanocrystals.
Dihydrolipoic acid (DHLA) is a popular bidentate hydrophilic ligand used for the stabilization of colloidal nanocrystals of inorganic semiconductors [29,30]. More frequently, it constitutes a binding segment of more complex ligands, frequently of macromolecular nature [31,32,33,34,35,36,37]. DHLA and its derivatives can be relatively easily obtained from commercially available lipoic acid (LA) through its reduction with NaBH4 [38,39]. Alternatively, it can be obtained photochemically through UV irradiation (300 nm < λ < 400 nm) [36].
The procedure of primary ligand exchange in alloyed AgInS2-ZnS nanocrystals for DHLA, elaborated for this research, consists of two steps. In the first step, DHLA is generated in situ in a mixture of LA (200 mg) and NaOH (50 mg) in water to which NaBH4 (80 mg) is added. The reduction is carried out at 40 °C for 1 h. LA is sparingly soluble in water but the solubility of its reduction product (DHLA) is much better. In the second step, R (or G) nanocrystal dispersions are added and the ligand exchange is carried out in the same manner as in the case of MUA ligands. For NMR studies, all these reactions were carried out in D2O.
In Figure 4, the 1H NMR spectrum of LA in CDCl3 is compared with the spectrum of a sample taken from the reaction medium saturated with DHLA prior to the addition of R (or G) nanocrystals. The remaining two spectra were registered for R-DHLA and G-DHLA, i.e., nanocrystals dispersed in D2O after ligand exchange. The analysis of the 1H-1H COSY spectrum (Figure S6 in Supplementary Materials) facilitates unequivocal attribution of signals originating from LA. In particular, multiplets in the spectral ranges 3.53–3.60 ppm and 3.08–3.21 ppm should be attributed to protons of -CHS- and -CH2S groups, respectively, whereas a triplet at 2.37 ppm originates from protons of the methylene group adjacent to the carboxylic one. Increased solubility in D2O of DHLA formed in situ in the mixture of LA and NaBH4 made the registration of its spectrum possible. The signals observed in the spectra ranges of 3.56–3.70 ppm and 3.07–3.24 ppm are broadened. They can be ascribed to protons of the following groups -CHSH and -CH2SH. A clear triplet at 2.11 pm originates from protons of the methyl group adjacent to the carboxylic one, (-CH2COOH), whereas a multiplet at 1.33–1.38 ppm is attributed to thiol groups -SH [31], which is corroborated by couplings in this spectral range of the 1H-1H COSY spectrum (Figure S7, Supplementary Materials). The presence of the reducing agent (NaBH4) is spectroscopically manifested by two multiplets at ca. −0.2 ppm, namely, a quartet (1:1:1:1; J = 80.6 Hz) at ca. −0.2 ppm and a septet (1:1:1:1:1:1:1; J = 27 Hz) originating from 1H and 11B (I = 3/2) and 10B (I = 1). The clear difference in their intensities has its origin in the different abundance of 11B and 10B isotopes (80.22% and 19.78%, respectively).
Aqueous dispersions of R-DHLA are stable. Moreover, contrary to the case of R-MUA, in their 1H NMR, no signals in the spectral range of 1.0–1.3 ppm, attributable to the presence of primary ligands, can be observed. Thus, in this case, the ligand exchange process is efficient and complete. The broadening of spectral lines of free DHLA generated in situ (Figure 4b) is caused by its limited solubility in the reaction medium. To the contrary, spectral lines originating from R-DHLA nanocrystals are narrow and well resolved, indicating very good dispersibility of this system in water, indicating that aggregation of nanoparticles does not take place. A similar effect was previously observed for nanocrystals of the same core composition to which electroactive ligands were attached which improved their dispersibility [40].
All signals expected for the DHLA ligand are present in the 1H NMR spectrum of R-DHLA. Binding of DHLA ligands to the nanocrystal surface is manifested by small shifts of selected signals as compared to their position in the spectrum of “free” DLHA. In the spectral ranges 3.74–3.81 ppm and 3.21–3.33 ppm, multiplets are observed originating from protons attached to carbons directly linked to the thiol groups, i.e., -CHSH and -CH2SH. The signal at 2.21 ppm corresponds to the methylene group adjacent to the carboxylic one, as revealed by the 1H-1H COSY spectrum (see Figures S8 and S9, Supplementary Materials). It strongly overlaps with the line ascribed to acetone, which was used for the precipitation of R-DHLA nanocrystals in the process of the ligand exchange. Lines clearly visible in the spectral range 1.44–1.51 ppm originate from protons of the thiol groups. The corresponding spectrum of G-DHLA is very similar; however, in the spectral ranges of 1.0–1.1 ppm and 3.5–3.6 ppm, i.e., diagnostic of protons of SH and -CHSH groups, additional multiplets are present, suggesting different conformations of ligands bound to the nanocrystal surface.
The exchange of primary ligands for DHLA results in significant changes in the elemental analysis (see Table 1). The content of carbon drops from 57.6% in R to 8.7% in R-DHLA and from 55.3% in G to 20.9% G-DHLA. This finding clearly indicates that in this case the ligand exchange process is very efficient and no initial ligands are present in the sample, consistent with the results of NMR spectroscopy. The exchange process also leads to a modification of the inorganic core composition manifested in R-DHLA as well as in G-DHLA by a distinct decrease in indium content and less pronounced changes in zinc content. As in the case of nanocrystals capped with MUA, the new ligands in R-DHLA and G-DHLA introduce organic sulfur in addition to the inorganic one already present in R and G; as a result, the content of sulfur significantly increases after the ligand exchange.
Changes in the chemical composition of R-DHLA nanocrystals, as compared to R, are accompanied by distinct diminution of their size. This is spectroscopically reflected by a hypsochromic shift of their emission band from 720 to 672 nm originating from the quantum confinement effect (see Figure 2). Size reduction is much less pronounced in the case of the transformation of G into G-DHLA. As a result, no quantum confinement effect can be observed in this case and the emission bands of G and G-DHLA nanocrystals are located at essentially the same positions (~540 nm) (Figure 2).
Finally, it should be stated that transforming hydrophobic R into hydrophilic R-DHLA allows for retaining the PLQY value at the relatively high level of 40%. In the case of G-DHLA, this value is 28%.
L-Cysteine (in the subsequent text abbreviated as Cys) is a hydrophilic molecule frequently used as a primary ligand in the syntheses of colloidal semiconductor nanocrystals carried out in aqueous media. It is less frequently used in processes of nanocrystal hydrophilization through ligand exchange [4]. Cysteine is more soluble in water than MUA and DHLA. Apart from obvious advantages, this good solubility brings some difficulties in the preparation of solutions used for the ligand exchange. The efficiency of this process requires the application of the highest possible gradient of the ligands to be introduced, which can be assured by the use of saturated solutions. In the case of Cys, this solution is very concentrated. The same solutions were used in the ligand exchange process. Dispersions of R (or G) in toluene were mixed with 3.0 g of L-cysteine and 50 mg NaOH dissolved in 10 mL of water and then vigorously stirred at 40 °C for 4 h. After precipitation in acetone, the resulting R-Cys and G-Cys could be readily redispersed in water.
In Figure 5, the 1H NMR spectra of the free ligand, i.e., L-cysteine in D2O (or NaOD/D2O), registered at three different pH (~7.0, ~11.0 and >13.0) (a–c), are compared with the spectrum of R-Cys (pH ~11.0) (d). At pH ~7.0, Cys is of zwitterionic nature; thus, its NMR spectra should be pH dependent. Indeed, with increasing pH, an increasing shift of all NMR signals is observed as a result of the deprotonation of the cationic part (-NH3+) of the zwitterion. This shift is caused by an increase in the electron density at the nitrogen atom, leading to more efficient shielding of all protons and their resonance at a higher field. Moreover, with increasing pH, the differentiation between diastereotopic protons of the methylene group in -CH2SH becomes more pronounced.
In the spectrum of R-Cys, no signals are observed in the spectral range 1.0–1.5 ppm, which implies absence of the initial ligands and confirms the efficacity of the ligand exchange process. However, if the spectrum of R-Cys is compared with the corresponding spectrum of free Cys registered and the same pH ~11, some differences in the chemical shifts of all protons can be noticed (compare Figure 5b,d). Moreover, the observed shifts are opposite to those induced by increasing pH. Thus, the binding of Cys to the nanocrystal surface results in electron density lowering in this molecule, decreasing shielding and resonance at the lower field.
As expected, the replacement of primary ligands in R (or G) by Cys to yield R-Cys (or G-Cys) resulted in a significant decrease in the content of carbon from 57.6% in R to 26.7% in R-Cys and from 55.3% in G to 24.6% in G-Cys. Ligand exchange also induced changes in the composition of the inorganic core, leading to a lowering of indium and zinc contents in R-Cys as compared to R. As in the case of R-DHLA, composition changes in the core of R-Cys were accompanied by a lowering of the nanocrystal size but had a rather limited effect on the emission band position. It was shifted from 720 nm for R to 707 nm for R-Cys (see Table 1 and Figure 2). This unexpected bathochromic shift accompanying decreasing nanocrystal size probably has its origin in two effects of opposite nature. Lowering the nanocrystal size induces a hypsochromic shift of the emission band due to the quantum confinement effect. To the contrary, diminution of the content of zinc results in a bathochromic shift of this band. The resultant weak bathochromic shift measured in R-Cys as compared to R must be considered as the product of these two opposite effects. The PLQY value drops from 67% in R to 28% in R-Cys.
G-Cys is characterized by the most pronounced change in the chemical composition of the inorganic core as compared to G which involves diminution in the content of silver and zinc. Since N is present only in Cys in the atomic ratio N/S = 1, the content of the “organic” sulfur can be estimated on the basis of nitrogen determination. This makes possible the estimation of the content of “inorganic”, core-originating sulfur by subtracting the content of “organic” sulfur from the total content of sulfur. The calculated molar ratio of silver to core-originating sulfur is 6.8 (R-Cys) and 38.7 (G-Cys). In both cases, these ratios are higher than those calculated assuming stoichiometric ratios of cations and anions. This means that the nanocrystals surface is enriched in anions in these cases. The discussed profound changes in the core composition of G-Cys as compared to G had only a weak effect on the position of its emission band which was slightly hypsochromically shifted from 543 nm in G to 524 nm in G-Cys. However, its PLQY value was significantly reduced from 48% to 16%.

4. Conclusions

To summarize, we have demonstrated that the exchange of hydrophobic primary ligands for hydrophilic ones in quaternary alloyed AgInS2-ZnS nanocrystals of varying composition can be relatively easily performed in a one-step procedure. This facile and efficient procedure cannot be applied to nanocrystals which contain strongly bound hydrophobic thiols as primary capping ligands such as DDT, for example. We have demonstrated that labile primary ligands, e.g., stearate anions co-ordinated by zinc cations and 1-aminooctadecane molecules co-ordinated by In(III) cations, are being readily exchanged for hydrophilic ligands containing thiol co-ordinating groups. Detailed characterization of nanocrystals in pre- and post-ligand exchange states has revealed that the exchange has a significant effect on the composition of nanocrystals, including the composition of their cores, and a much weaker effect on the nanocrystal size. These ligand exchange-induced composition and size changes have not affected the nanocrystals’ photoluminescence color to a large extent but have led to a significant diminution of the PLQY values. Among the three hydrophilic ligands tested—11-mercaptoundecanoic acid (MUA), L-cysteine (Cys) and dihydrolipoic acid (DHLA)—DHLA turned out to be the most promising since it assured the complete removal of the primary ligand and relatively high PLQY values after the ligand exchange: 40% for nanocrystals emitting red light and 28% for those emitting green light.

Supplementary Materials

The following are available online at https://www.mdpi.com/article/10.3390/nano11040843/s1. Preparation of alloyed AgInS2-ZnS (R and G) nanocrystals, Figures S1–S3: EDS spectra of alloyed AgInS2-ZnS capped with initial ligands (R and S) and hydrophilic ligands: MUA, DHLA and Cys, Figures S4–S9: 1H-1H COSY NMR spectra of R-MUA, G-MUA, lipoic acid, dihydrolipoic acid, R-DHLA and G-DHLA.

Author Contributions

P.K. designed the concepts, P.K. prepared the samples of nanocrystals, M.P. made the NMR measurements, P.K., P.B. and M.P. discussed the results, P.K., P.B., M.P. and A.P. supervised the manuscript. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the National Science Centre of Poland, Grant No. 2019/33/B/ST5/00582. P.K. additionally acknowledges financial support from the Operational Program Knowledge Education Development 2014–2020 co-financed by the European Social Fund, Project No POWR.03.02.00-00-I007/16-00 (POWER 2014-2020).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Talapin, D.V.; Lee, J.-S.; Kovalenko, M.V.; Shevchenko, E.V. Prospects of Colloidal Nanocrystals for Electronic and Optoelectronic Applications. Chem. Rev. 2010, 110, 389–458. [Google Scholar] [CrossRef]
  2. Aldakov, D.; Lefrançois, A.; Reiss, P. Ternary and Quaternary Metal Chalcogenide Nanocrystals: Synthesis, Properties and Applications. J. Mater. Chem. C 2013, 1, 3756–3776. [Google Scholar] [CrossRef]
  3. Reiss, P.; Carrière, M.; Lincheneau, C.; Vaure, L.; Tamang, S. Synthesis of Semiconductor Nanocrystals, Focusing on Nontoxic and Earth-Abundant Materials. Chem. Rev. 2016, 18, 10731–10819. [Google Scholar] [CrossRef]
  4. Jing, L.; Kershaw, S.V.; Li, Y.; Huang, X.; Li, Y.; Rogach, A.L.; Gao, M. Aqueous Based Semiconductor Nanocrystals. Chem. Rev. 2016, 116, 10623–10730. [Google Scholar] [CrossRef] [PubMed]
  5. Bujak, P. Core and Surface Engineering in Binary, Ternary and Quaternary Semiconductor Nanocrystals – A Critical Review. Synth. Met. 2016, 222, 93–114. [Google Scholar] [CrossRef]
  6. Coughlan, C.; Ibáñez, M.; Dobrozhan, O.; Singh, A.; Cabot, A.; Ryan, K.M. Compound Copper Chalcogenide Nanocrystals. Chem. Rev. 2017, 117, 5865–6109. [Google Scholar] [CrossRef]
  7. Girma, W.M.; Fahmi, M.Z.; Permadi, A.; Abate, M.A.; Chang, J.-Y. Synthetic Strategies and Biomedical Applications of I-III-VI Ternary Quantum Dots. J. Mater. Chem. B 2017, 5, 6193–6216. [Google Scholar] [CrossRef]
  8. Sobiech, M.; Bujak, P.; Luliński, P.; Pron, A. Semiconductor Nanocrystal-Polymer Hybrid Nanomaterials and their Application in Molecular Imprinting. Nanoscale 2019, 11, 12030–12074. [Google Scholar] [CrossRef] [PubMed]
  9. Moodelly, D.; Kowalik, P.; Bujak, P.; Pron, A.; Reiss, P. Synthesis, Photophysical Properties and Surface Chemistry of Chalcopyrite-Type Semiconductor Nanocrystals. J. Mater. Chem. C 2019, 7, 11665–11709. [Google Scholar] [CrossRef]
  10. Palui, G.; Aldeek, F.; Wang, W.; Mattoussi, H. Strategies for Interfacing Inorganic Nanocrystals with Biological Systems Based on Polymer-Coating. Chem. Soc. Rev. 2015, 44, 193–227. [Google Scholar] [CrossRef] [PubMed]
  11. Reiss, P.; Protière, M.; Li, L. Core/Shell Semiconductor Nanocrystals. Small 2009, 5, 154–168. [Google Scholar] [CrossRef]
  12. Derfus, A.M.; Chan, W.C.W.; Bhatia, S.N. Probing the Cytotoxicity of Semiconductor Quantum Dots. Nano Lett. 2004, 4, 11–18. [Google Scholar] [CrossRef]
  13. Kirchner, C.; Liedl, T.; Kudera, S.; Pellegrino, T.; Javier, A.M.; Gaub, H.E.; Stölzle, S.; Fertig, N.; Parak, W.J. Cytotoxicity of Colloidal CdSe and CdSe/ZnS Nanoparticles. Nano Lett. 2005, 5, 331–338. [Google Scholar] [CrossRef]
  14. Ye, L.; Yong, K.-T.; Liu, L.; Roy, I.; Hu, R.; Zhu, J.; Cai, H.; Law, W.-C.; Liu, J.; Wang, K.; et al. A Pilot Study in Non-Human Primates Shows No Adverse Response to Intravenous Injection of Quantum Dots. Nat. Nanotechnol. 2012, 7, 453–458. [Google Scholar] [CrossRef] [PubMed]
  15. Song, J.; Ma, C.; Zhang, W.; Yang, S.; Wang, S.; Lv, L.; Zhu, L.; Xia, R.; Xu, X. Tumor Cell-Targeted Zn3In2S6 and Ag-In-Zn-S Quantum Dots for Color Adjustable Luminophores. J. Mater. Chem. B 2016, 4, 7909–7918. [Google Scholar] [CrossRef]
  16. Song, J.; Ma, C.; Zhang, W.; Li, X.; Zhang, W.; Wu, R.; Cheng, X.; Ali, A.; Yang, M.; Zhu, L.; et al. Bandgap and Structure Engineering via Cation Exchange: From Binary Ag2S to Ternary AgInS2, Quaternary AgZnInS alloy and AgZnInS/ZnS Core/Shell Fluorescent Nanocrystals for Bioimaging. ACS Appl. Mater. Interfaces 2016, 8, 24826–24836. [Google Scholar] [CrossRef] [PubMed]
  17. Matysiak-Brynda, E.; Bujak, P.; Augustin, E.; Kowalczyk, A.; Mazerska, Z.; Pron, A.; Nowicka, A.M. Stable Nanoconjugates of Transferrin with Alloyed Quaternary Nanocrystals Ag-In-Zn-S as a Biological Entity for Tumor Recognition. Nanoscale 2018, 10, 1286–1296. [Google Scholar] [CrossRef]
  18. Pilch, J.; Matysiak-Brynda, E.; Kowalczyk, A.; Bujak, P.; Mazerska, Z.; Nowicka, A.M.; Augustin, E. New Unsymmetrical Bisacridine Derivatives Noncovalently Attached to Quaternary Quantum Dots Improve Cancer Therapy by Enhancing Cytotoxicity toward Cancer Cells and Protecting Normal Cells. ACS Appl. Mater. Interfaces 2020, 12, 17276–17289. [Google Scholar] [CrossRef]
  19. Delices, A.; Moodelly, D.; Hurot, C.; Hou, Y.; Ling, W.L.; Saint-Pierre, C.; Gasparutto, D.; Nogues, G.; Reiss, P.; Kheng, K. Aqueous Synthesis of DNA-Functionalized Near-Infrared AgInS2/ZnS Core/Shell Quantum Dots. ACS Appl. Mater. Interfaces 2020, 12, 44026–44038. [Google Scholar] [CrossRef]
  20. Pilch, J.; Kowalik, P.; Bujak, P.; Nowicka, A.M.; Augustin, E. Quantum Dots as a Good Carriers of Unsymmetrical Bisacridines for Modulating Cellular Uptake and the Biological Response in Lung and Colon Cancer Cells. Nanomaterials 2021, 11, 462. [Google Scholar] [CrossRef] [PubMed]
  21. Ruzycka-Ayoush, M.; Kowalik, P.; Kowalczyk, A.; Bujak, P.; Nowicka, A.M.; Wojewodzka, M.; Kruszewski, M.; Grudzinski, I.P. Quantum Dots as Targeted Doxorubicin Drug Delivery Nanosystems. Cancer Nanotechnol. 2021, 12, 8. [Google Scholar] [CrossRef]
  22. Gabka, G.; Bujak, P.; Giedyk, K.; Ostrowski, A.; Malinowska, K.; Herbich, J.; Golec, B.; Wielgus, I.; Pron, A. A Simple Route to Alloyed Quaternary Nanocrystals Ag-In-Zn-S with Shape and Size Control. Inorg. Chem. 2014, 53, 5002–5012. [Google Scholar] [CrossRef] [PubMed]
  23. Gabka, G.; Bujak, P.; Kotwica, K.; Ostrowski, A.; Lisowski, W.; Sobczak, J.W.; Pron, A. Luminophores of Tunable Colors from Ternary Ag-In-S and Quaternary Ag-In-Zn-S Nanocrystals Covering the Visible to Near-Infrared Spectral Range. Phys. Chem. Chem. Phys. 2017, 19, 1217–1228. [Google Scholar] [CrossRef]
  24. Bujak, P.; Wróbel, Z.; Penkala, M.; Kotwica, K.; Kmita, A.; Gajewska, M.; Ostrowski, A.; Kowalik, P.; Pron, A. Highly Luminescent Ag-In-Zn-S Quaternary Nanocrystals: Growth Mechanism and Surface Chemistry Elucidation. Inorg. Chem. 2019, 58, 1358–1370. [Google Scholar] [CrossRef] [PubMed]
  25. Kowalik, P.; Penkala, M.; Bujak, P.; Kmita, A.; Gajewska, M.; Ostrowski, A.; Slodek, A.; Pron, A. From Ag2S to Luminescent Ag-In-S Nanocrystals via an Ultrasonic Method—An in situ Synthesis Study in an NMR Tube. J. Mater. Chem. C 2020, 8, 8942–8952. [Google Scholar] [CrossRef]
  26. Gabka, G.; Bujak, P.; Gryszel, M.; Kotwica, K.; Pron, A. Anchor Groups Effect on Spectroscopic and Electrochemical Properties of Quaternary Nanocrystals Cu-In-Zn-S Capped with Arylamine Derivatives. J. Phys. Chem. C 2015, 119, 9656–9664. [Google Scholar] [CrossRef]
  27. Tamang, S.; Beaune, G.; Texier, I.; Reiss, P. Aqueous Phase Transfer of InP/ZnS Nanocrystals Conserving Fluorescence and High Colloidal Stability. ACS Nano 2011, 9392–9402. [Google Scholar] [CrossRef]
  28. Zhang, W.; Zhong, X. Facile Synthesis of ZnS-CuInS2-Alloyed Nanocrystals for a Color-Tunable Fluorchrome and Photocatalyst. Inorg. Chem. 2011, 50, 4065–4072. [Google Scholar] [CrossRef] [PubMed]
  29. Mattoussi, H.; Mauro, J.M.; Goldman, E.R.; Anderson, G.P.; Sundar, V.C.; Mikulec, F.V.; Bawendi, M.G. Self-Assembly of CdSe-ZnS Quantum Dot Bioconjugates Using an Engineered Recombinant Protein. J. Am. Chem. Soc. 2000, 122, 12142–12150. [Google Scholar] [CrossRef]
  30. Fang, Z.; Liu, L.; Xu, L.L.; Yin, X.G.; Zhong, X.H. Synthesis of Highly Stable Dihydrolipoic Acid Capped Water-Soluble CdTe Nanocrystals. Nanotechnology 2008, 19, 235603. [Google Scholar] [CrossRef]
  31. Uyeda, H.T.; Medintz, I.L.; Jaiswal, J.K.; Simon, S.M.; Mattoussi, H. Synthesis of Compact Multidentate Ligands to Prepare Stable Hydrophilic Quantum Dot Fluorophores. J. Am. Chem. Soc. 2005, 127, 3870–3878. [Google Scholar] [CrossRef]
  32. Susumu, K.; Uyeda, H.T.; Medintz, I.L.; Pons, T.; Delehanty, J.B.; Mattoussi, H. Enhancing the Stability and Biological Functionalities of Quantum Dots via Compact Multifunctional Ligands. J. Am. Chem. Soc. 2007, 129, 13987–13996. [Google Scholar] [CrossRef]
  33. Liu, W.; Howarth, M.; Greytak, A.B.; Zheng, Y.; Nocera, D.G.; Ting, A.Y.; Bawendi, M.G. Compact Biocompatible Quantum Dots Functionalized for Cellular Imaging. J. Am. Chem. Soc. 2008, 130, 1274–1284. [Google Scholar] [CrossRef]
  34. Mei, B.C.; Susumu, K.; Medintz, I.L.; Delehanty, J.B.; Mountziaris, T.J.; Mattoussi, H. Modular Poly(ethylene glycol) Ligands for Biocompatible Semiconductor and Gold Nanocrystals with Extended pH and Ionic Stability. J. Mater. Chem. 2008, 18, 4949–4958. [Google Scholar] [CrossRef]
  35. Stewart, M.H.; Susumu, K.; Mei, B.C.; Medintz, I.L.; Delehanty, J.B.; Blanco-Canosa, J.B.; Dawson, P.E.; Mattoussi, H. Multidentate Poly(ethylene glycol) Ligands Provide Colloidal Stability to Semiconductor and Metallic Nanocrystals in Extreme Conditions. J. Am. Chem. Soc. 2010, 132, 9804–9813. [Google Scholar] [CrossRef] [PubMed]
  36. Palui, G.; Avellini, T.; Zhan, N.; Pan, F.; Gray, D.; Alabugin, I.; Mattoussi, H. Photoinduced Phase Transfer of Luminescent Quantum Dots to Polar and Aqueous Media. J. Am. Chem. Soc. 2012, 134, 16370–16378. [Google Scholar] [CrossRef] [PubMed]
  37. Zhan, N.; Palui, G.; Mattoussi, H. Preparation of Compact Biocompatible Quantum Dots Using Multicoordinating Molecular-Scale Ligands Based on a Zwitterionic Hydrophilic Motif and Lipoic Acid Anchors. Nat. Protoc. 2015, 10, 859–874. [Google Scholar] [CrossRef]
  38. Gunsalus, I.C.; Barton, L.S.; Gruber, W. Biosynthesis and Structure of Lipoic Acid Derivatives. J. Am. Chem. Soc. 1956, 78, 1763–1766. [Google Scholar] [CrossRef]
  39. Roux, S.; Garcia, B.; Bridot, J.-L.; Salomé, M.; Marquette, C.; Lemelle, L.; Gillet, P.; Blum, L.; Perriat, P.; Tillement, O. Synthesis, Characterization of Dihydrolipoic Acid Capped Gold Nanoparticles, and Functionalization by the Electroluminescent Luminol. Langmuir 2005, 21, 2526–2536. [Google Scholar] [CrossRef]
  40. Kowalik, P.; Bujak, P.; Wróbel, Z.; Penkala, M.; Kotwica, K.; Maroń, A.; Pron, A. From Red to Green Luminescence via Surface Functionalization. Effect of 2-(5-Mercaptothien-2-yl)-8(thien-2-yl)-5-hexylthieno[3,4-c]pyrrole-4,6-dione Ligands on the Photoluminescence of Alloyed Ag-In-Zn-S Nanocrystals. Inorg. Chem. 2020, 59, 14594–14604. [Google Scholar] [CrossRef] [PubMed]
Nanomaterials 11 00843 g001 550
Figure 1. TEM images of alloyed AgInS2-ZnS nanocrystals (R-“Red” and G-“Green”) before and after the exchange of initial capping ligands for 11-mercaptoundecanoic acid (MUA), dihydrolipoic acid (DHLA), L-cysteine (Cys), and their histograms.
Figure 1. TEM images of alloyed AgInS2-ZnS nanocrystals (R-“Red” and G-“Green”) before and after the exchange of initial capping ligands for 11-mercaptoundecanoic acid (MUA), dihydrolipoic acid (DHLA), L-cysteine (Cys), and their histograms.
Nanomaterials 11 00843 g001
Nanomaterials 11 00843 g002 550
Figure 2. Photoluminescence spectra of alloyed AgInS2-ZnS nanocrystals (R-“Red” and G-“Green”) before (dispersion in toluene, dashed lines) and after the exchange of initial capping ligands for MUA, DHLA, Cys, (dispersion in water, solid lines).
Figure 2. Photoluminescence spectra of alloyed AgInS2-ZnS nanocrystals (R-“Red” and G-“Green”) before (dispersion in toluene, dashed lines) and after the exchange of initial capping ligands for MUA, DHLA, Cys, (dispersion in water, solid lines).
Nanomaterials 11 00843 g002
Nanomaterials 11 00843 sch001 550
Scheme 1. Structures of the hydrophilic organic ligands used for the transfer of nanocrystals to aqueous phase.
Scheme 1. Structures of the hydrophilic organic ligands used for the transfer of nanocrystals to aqueous phase.
Nanomaterials 11 00843 sch001
Nanomaterials 11 00843 g003 550
Figure 3. 1H NMR spectra of MUA (in NaOD/D2O) (a) and D2O dispersion of AgInS2-ZnS nanocrystals capped with MUA: R-MUA (b) and G-MUA (c).
Figure 3. 1H NMR spectra of MUA (in NaOD/D2O) (a) and D2O dispersion of AgInS2-ZnS nanocrystals capped with MUA: R-MUA (b) and G-MUA (c).
Nanomaterials 11 00843 g003
Nanomaterials 11 00843 g004 550
Figure 4. 1H NMR spectra of lipoic acid (LA) (in CDCl3) (a) and DHLA (in D2O) (b) and D2O dispersion of AgInS2-ZnS nanocrystals capped with DHLA: R-DHLA (c) and G-DHLA (d).
Figure 4. 1H NMR spectra of lipoic acid (LA) (in CDCl3) (a) and DHLA (in D2O) (b) and D2O dispersion of AgInS2-ZnS nanocrystals capped with DHLA: R-DHLA (c) and G-DHLA (d).
Nanomaterials 11 00843 g004
Nanomaterials 11 00843 g005 550
Figure 5. 1H NMR spectra of L-cysteine (Cys) in D2O, in pH ~7.0 (a), in NaOD/D2O, in pH ~11.0 (b), >13.0 (c) and D2O dispersion of AgInS2-ZnS nanocrystals capped with L-cysteine: R-Cys in pH ~11.0 (d).
Figure 5. 1H NMR spectra of L-cysteine (Cys) in D2O, in pH ~7.0 (a), in NaOD/D2O, in pH ~11.0 (b), >13.0 (c) and D2O dispersion of AgInS2-ZnS nanocrystals capped with L-cysteine: R-Cys in pH ~11.0 (d).
Nanomaterials 11 00843 g005
Table
Table 1. Characteristics (composition, size, maximum of the photoluminescence band, and photoluminescence quantum yield (PLQY)) of alloyed AgInS2-ZnS nanocrystals before (R and G) and after the exchange of initial capping ligands for MUA, DHLA, Cys.
Table 1. Characteristics (composition, size, maximum of the photoluminescence band, and photoluminescence quantum yield (PLQY)) of alloyed AgInS2-ZnS nanocrystals before (R and G) and after the exchange of initial capping ligands for MUA, DHLA, Cys.
LigandAg/In/Zn/S(S)%wt. C%wt. S%wt. NSize
(nm)		PL
(nm)		Q.Y.(%)
Red (R)Initial1.00/2.80/1.30/4.00(6.00)57.65.1-6.2 ± 0.972067.0
MUA1.00/1.00/1.10/3.50(3.10)42.914.0-5.6 ± 0.873030.0
DHLA1.00/1.00/1.00/3.30(3.00)8.723.0-4.6 ± 0.667240.0
Cys1.00/1.00/0.80/19.40(2.80)26.722.56.44.3 ± 0.770728.0
Green (G)Initial1.00/1.50/7.80/17.0(10.50)55.311.5-4.2 ± 0.654348.0
MUA1.00/1.20/5.60/9.40(7.90)50.213.2-3.7 ± 0.657625.0
DHLA1.00/1.00/8.80/25.10(10.80)20.920.7-3.6 ± 0.754028.0
Cys1.00/5.80/12.10/126.2(21.3)24.620.96.33.7 ± 1.052416.0
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Kowalik, P.; Bujak, P.; Penkala, M.; Pron, A. Organic-to-Aqueous Phase Transfer of Alloyed AgInS2-ZnS Nanocrystals Using Simple Hydrophilic Ligands: Comparison of 11-Mercaptoundecanoic Acid, Dihydrolipoic Acid and Cysteine. Nanomaterials 2021, 11, 843. https://doi.org/10.3390/nano11040843

AMA Style

Kowalik P, Bujak P, Penkala M, Pron A. Organic-to-Aqueous Phase Transfer of Alloyed AgInS2-ZnS Nanocrystals Using Simple Hydrophilic Ligands: Comparison of 11-Mercaptoundecanoic Acid, Dihydrolipoic Acid and Cysteine. Nanomaterials. 2021; 11(4):843. https://doi.org/10.3390/nano11040843

Chicago/Turabian Style

Kowalik, Patrycja, Piotr Bujak, Mateusz Penkala, and Adam Pron. 2021. "Organic-to-Aqueous Phase Transfer of Alloyed AgInS2-ZnS Nanocrystals Using Simple Hydrophilic Ligands: Comparison of 11-Mercaptoundecanoic Acid, Dihydrolipoic Acid and Cysteine" Nanomaterials 11, no. 4: 843. https://doi.org/10.3390/nano11040843

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.