Metal Organic Frameworks Based Materials for Heterogeneous Photocatalysis

The increase in environmental pollution due to the excessive use of fossil fuels has prompted the development of alternative and sustainable energy sources. As an abundant and sustainable energy, solar energy represents the most attractive and promising clean energy source for replacing fossil fuels. Metal organic frameworks (MOFs) are easily constructed and can be tailored towards favorable photocatalytic properties in pollution degradation, organic transformations, CO2 reduction and water splitting. In this review, we first summarize the different roles of MOF materials in the photoredox chemical systems. Then, the typical applications of MOF materials in heterogeneous photocatalysis are discussed in detail. Finally, the challenges and opportunities in this promising field are evaluated.


Introduction
A significant and ongoing challenge is the increasing pollution associated with the highly increased global energy consumption [1,2]. The exploration of more sustainable and clean energy sources has become an extremely important and challenging task that humanity needs to address urgently, as CO 2 and other pollutants have a detrimental effect on our climate and health. As an abundant and sustainable energy source, solar energy represents the most attractive clean energy source to replace fossil fuels. Photosynthesis is a transformation process where a plant can harvest solar radiation and convert carbon dioxide (CO 2 ) and water (H 2 O) into carbohydrates. Great efforts have been devoted to developing artificial photosynthetic systems (or simply photocatalytic systems) for chemical transformations by using inorganic or/and organic materials. The first photocatalytic system was achieved by Fujishima and Honda in their pioneering work on water splitting with TiO 2 under UV light irradiation [3]. Since then, various types of materials have been studied and employed for the application of photocatalysis [4]. However, the nanostructures and functionalization of these materials need to be optimized to maximize utilization of sunlight as well as increase their photocatalytic performance.
The classical photocatalytic process consists of the following three fundamental steps: (1) photosensitizers absorb solar irradiation to create charge-separated excited states; (2) redox equivalents (mobile electrons and holes) are produced and migrate to catalytic centers; (3) redox equivalents react with substrates at the reactive centers. Therefore, an excellent photocatalyst ought to possess the following features: (1) strong absorption of sunlight; (2) a long lifetime of excited state; (3) high yield of charge-separated states; and (4) good charge mobility.
Porphyrins are known to be light harvesting compounds and have been used as building blocks to synthesize MOFs with an excellent photocatalytic performance [37]. Rosseinsky and coworkers reported a red porphyrin-based MOF H2TCPP[AlOH]2(DMF3-(H2O)2) by using the free-base mesotetra(4-carboxyl-phenyl) porphyrin (H2TCPP) as the organic linker [36]. Due to the zero occupancy of the Al atom at the center of porphyrin ligand, H2TCPP[AlOH]2 reacted with anhydrous Zn(AC)2 through porphyrin metalation, generating a purple material Zn0.986(12)H2TCPP[AlOH]2. H2TCPP[AlOH]2 exhibits a strong absorption band at 415 nm, belonging to the S0→S2 absorption process. Another four Q bands at lower energies were originated from the π-π* transitions in the freebase porphyrin ligand (Figure 1c). After porphyrin metalation, Zn0.986(12)H2TCPP[AlOH]2 exhibits a slight red shift in the absorption edge at 425 nm. Due to the higher symmetry of the now metalated material, there are only two Q bands left. As the porphyrin-based MOFs are photocatalytically active (b) Proposed mechanism for the photocatalytic CO 2 reduction over NH2-MIL-125(Ti) under visible light irradiation. Reproduced with permission from Reference [33]. Porphyrins are known to be light harvesting compounds and have been used as building blocks to synthesize MOFs with an excellent photocatalytic performance [37]. Rosseinsky and coworkers reported a red porphyrin-based MOF H 2 TCPP[AlOH] 2 (DMF 3 -(H 2 O) 2 ) by using the free-base meso-tetra(4-carboxyl-phenyl) porphyrin (H 2 TCPP) as the organic linker [36]. Due to the zero occupancy of the Al atom at the center of porphyrin ligand, H 2 TCPP[AlOH] 2 reacted with anhydrous Zn(AC) 2 through porphyrin metalation, generating a purple material Zn 0.986 (12) 2 exhibits a strong absorption band at 415 nm, belonging to the S 0 →S 2 absorption process. Another four Q bands at lower energies were originated from the π-π* transitions in the free-base porphyrin ligand (Figure 1c). After porphyrin metalation, Zn 0.986 (12) H 2 TCPP[AlOH] 2 exhibits a slight red shift in the absorption edge at 425 nm. Due to the higher symmetry of the now metalated material, there are only two Q bands left. As the porphyrin-based MOFs are photocatalytically active in the visible light region, the authors evaluated the photocatalytic performance of the two MOFs for hydrogen evolution from water ( Figure 1d).
Due to their strong visible light absorption and long-lived excited states, they have been used as homogeneous photocatalysts. The incorporation of the photoredox-capable dyes into MOF frameworks could broaden and deepen the photocatalytic applications of MOFs. Meanwhile, the self-quenching induced by aggregation of dye-photocatalysts in homogeneous systems can be avoided thanks to the highly ordered distribution of dye-photocatalysts in MOF structures.

MOFs as Co-Catalysts and/or Hosts
MOFs can act as hosts for photoredox species. They benefit from their high porosity, which provides additional possibilities for photocatalytic applications. Photocatalytically active species can be encapsulated into the pores of MOFs as guest molecules, provided that they obtain the right properties. These host MOFs display enhanced photocatalytic performance compared to homogeneous photocatalysts. This effect is due to the isolation of guest molecules and the mutual effect on the framework of MOFs. MOFs can act either as mere hosts or participate in photocatalytic processes. The high porosity of MOFs provides the necessary space for the interaction between the embedded catalytically active species and the substrates. Moreover, the very uniform pore size can result in reactant or product shape selectivity. Among the species that can be encapsulated are precious metals, semiconductor nanoparticles (NPs), as well as molecule catalysts which obtain the appropriate size [40,41].
The encapsulation of precious metals (Such as Pt, Pd and Au) into MOFs can inhibit the recombination between the photogenerated electrons and holes [42,43]. Due to the formation of a Schottky barrier at the junction between MOFs and precious metals, the photogenerated electrons in the conduction band (CB) of MOFs can transfer to the precious metals. This results in the efficient separation of the photogenerated charge carriers [44]. This way, the photocatalytic performance of MOF-based materials can be significantly enhanced. In 2014, Li and coworkers reported a series of M/NH 2 -MIL-125(Ti) materials (M = Pt and Au), which were used for CO 2 reduction under visible light irradiation [45]. The Pt/NH 2 -MIL-125(Ti) exhibits an improved photocatalytic performance compared to NH 2 -MIL-125(Ti), while Au exhibits a detrimental effect on this reaction. The hydrogen-assisted formed Ti 3+ plays a positive role in photocatalytic formate production. However, the ESR signal of Ti 3+ was only observed in Pt/NH 2 -MIL-125(Ti). Neither in Au/NH 2 -MIL-125(Ti) nor in pure NH 2 -MIL-125(Ti) was the ESR signal observed, resulting in different effects on CO 2 reduction. Interestingly, Jiang and coworkers incorporated uniform Pt NPs into MIL-125(Ti), followed by coating with Au nanorods (NRs) on the MIL-125(Ti) surface to form Pt@MIL-125(Ti)/Au ( Figure 2) [46]. This integrated both the plasmonic effect of Au nanorods and a Schottky junction in a single MOF for the first time. The spatial separation of Au NRs and Pt NPs by MIL-125(Ti) steers the charge flow and greatly accelerates the charge migration, resulting in an exceptionally high photocatalytic performance of H 2 evolution under visible light irradiation. These results show that with the appropriate use and distribution of precious metals in MOF materials, this is a very promising approach to improve the photocatalytic performance of MOFs. Semiconductor NPs such as TiO2, CdS and ZnO, have a strong quantum-size effect and exhibit high photocatalytic activity [47]. Semiconductor NPs also have several disadvantages, including the aggregation in reactions, high recombination rate of photogenerated electron-hole pairs, and difficult separation from reaction systems. These are limiting their possible photocatalytic applications when used individually [48]. Hybrid materials between semiconductor NPs and MOFs do not only possess advantages from both two components, but also can overcome their individual limitations. The pioneering research on semiconductor NPs-MOF hybrid materials including CdSe/ZnS-MOF [49] and GdN/ZIF-8 [50], has mainly focused on enhancing light harvesting. Recently, Zhu and coworkers solvothermally synthesized a novel CdS NPs attached MOF material by using cadmium acetate as the CdS precursor and MIL-100(Fe) as the support [51]. The resulting CdS-MIL-100(Fe) nanocomposites showed remarkable photocatalytic efficiency in the selective oxidation of benzyl alcohol to benzaldehyde under visible light irradiation. The improved photocatalytic performance can be ascribed to the combined effect of enhanced light harvesting, high separation efficiency of photogenerated electron-hole pairs, as well as high dispersion of CdS NPs in MIL-100(Fe). The results indicate that the combination of semiconductors and MOF materials shows to be a promising approach for converting solar-energy into chemical energy.
Polyoxometalates (POMs), a subclass of metal oxides, have attracted extensive attention in various fields because of their highly negative charges, various structural characteristics, and excellent redox ability [52]. Recently, POMs were encapsulated into MOFs. The specific interaction between the two led to reversible multiple electron transfer reactions without structural degradation of the framework. A porphyrinic MOF-545 containing the sandwich-type POM [(PW9O34)2Co4(H2O)2] 10− was recently used for visible-light-driven water oxidation [53]. The high photocatalytic activity of this hybrid material was speculatively ascribed to the synergistic effect of the photoactive porphyrin ligands and the cobalt POM's catalytic sites that immobilized in the pore of MOF-545. Another example of POM-based MOF-101 hybrid material contains P2W15V3, P2W17Ni, or P2W17Co polyoxianions [54] which behaves as a photocatalyst in hydrogen production.
In some cases, MOF-based heterogeneous catalysts showed a reduced catalytic performance compared to homogeneous catalysts because the framework of MOFs can block the access of reactants to the catalytic sites. The reuse of MOF-based heterogeneous catalysts can extend the lifetime of the photocatalysts and reduce waste and contamination. The long term stability of MOFs as catalyst hosts under photocatalytic conditions is of great importance, and remains an issue. More efforts should be devoted to synthesizing robust MOFs that are stable in water or even acidic and basic solutions. Semiconductor NPs such as TiO 2 , CdS and ZnO, have a strong quantum-size effect and exhibit high photocatalytic activity [47]. Semiconductor NPs also have several disadvantages, including the aggregation in reactions, high recombination rate of photogenerated electron-hole pairs, and difficult separation from reaction systems. These are limiting their possible photocatalytic applications when used individually [48]. Hybrid materials between semiconductor NPs and MOFs do not only possess advantages from both two components, but also can overcome their individual limitations. The pioneering research on semiconductor NPs-MOF hybrid materials including CdSe/ZnS-MOF [49] and GdN/ZIF-8 [50], has mainly focused on enhancing light harvesting. Recently, Zhu and coworkers solvothermally synthesized a novel CdS NPs attached MOF material by using cadmium acetate as the CdS precursor and MIL-100(Fe) as the support [51]. The resulting CdS-MIL-100(Fe) nanocomposites showed remarkable photocatalytic efficiency in the selective oxidation of benzyl alcohol to benzaldehyde under visible light irradiation. The improved photocatalytic performance can be ascribed to the combined effect of enhanced light harvesting, high separation efficiency of photogenerated electron-hole pairs, as well as high dispersion of CdS NPs in MIL-100(Fe). The results indicate that the combination of semiconductors and MOF materials shows to be a promising approach for converting solar-energy into chemical energy.

MOFs as Precursors
Polyoxometalates (POMs), a subclass of metal oxides, have attracted extensive attention in various fields because of their highly negative charges, various structural characteristics, and excellent redox ability [52]. Recently, POMs were encapsulated into MOFs. The specific interaction between the two led to reversible multiple electron transfer reactions without structural degradation of the framework. A porphyrinic MOF-545 containing the sandwich-type POM [(PW 9 O 34 ) 2 Co 4 (H 2 O) 2 ] 10− was recently used for visible-light-driven water oxidation [53]. The high photocatalytic activity of this hybrid material was speculatively ascribed to the synergistic effect of the photoactive porphyrin ligands and the cobalt POM's catalytic sites that immobilized in the pore of MOF-545. Another example of POM-based MOF-101 hybrid material contains P 2 W 15 V 3 , P 2 W 17 Ni, or P 2 W 17 Co polyoxianions [54] which behaves as a photocatalyst in hydrogen production.
In some cases, MOF-based heterogeneous catalysts showed a reduced catalytic performance compared to homogeneous catalysts because the framework of MOFs can block the access of reactants to the catalytic sites. The reuse of MOF-based heterogeneous catalysts can extend the lifetime of the photocatalysts and reduce waste and contamination. The long term stability of MOFs as catalyst hosts under photocatalytic conditions is of great importance, and remains an issue. More efforts should be devoted to synthesizing robust MOFs that are stable in water or even acidic and basic solutions.

MOFs as Precursors
In recent years, MOFs have served as sacrificial templates or precursors in preparing more stable and conductive porous carbon, metal oxides, or porous carbon/metal oxides composite nanomaterials via a simple pyrolysis process [19]. MOFs have an inherent high porosity and a uniform dispersion of metal nodes in their network. Because of this, the MOF-derived nanomaterials keep the high porosity and the high surface area, and also show uniform heteroatom doping and adjustable morphology [55]. Therefore, the MOF-derived nanomaterials are promising candidates for catalytic applications. Zhao and coworkers successfully prepared TiO x /C composites by direct pyrolysis of MIL-125(Ti) under Ar atmosphere at different temperatures [56]. Among all the TiO x /C samples, T10, which was pyrolyzed at 1000 • C, possessed the highest photocatalytic activity for the photodegradation of methylene blue (MB). This was due to the reduced Ti 3 O 5 composition, the conductive carbon support, as well as the high surface area. The incorporation of cocatalysts into TiO 2 semiconductor photocatalysts has been applied for promoting charge separation and enhancing the photocatalytic performance. Xiong and coworkers synthesized a Cu/TiO 2 octahedral-shell photocatalyst derived from Cu 3 (BTC) 2 /TiO 2 core-shell structures (BTC = benzene-1,3,5-tricarboxylate) [57]. The Cu 3 (BTC) 2 MOF not only serves as the sacrificial precursor to form the hollow structure but is also used as a Cu source to prepare the Cu/TiO 2 composite. Because Cu can function as a cocatalyst, the Cu/TiO 2 composites show improved electron-hole separation and can be used as a photocatalyst for hydrogen production

MOFs for Photocatalytic Degradation of Organic Pollutants
There are various approaches to remove organic pollutants from industrial wastewater: electrochemical oxidation, photocatalysis, adsorption, and biodegradation [58][59][60][61][62][63]. Photocatalytic degradation is considered as one of the most competitive methods for organic pollutants removal, due to its high efficiency, utilization of renewable solar energy, and environmental-friendliness [64]. In 2007, Garcia and coworkers demonstrated that MOF-5 exhibited photocatalytic activity for phenol degradation under UV light irradiation [65]. Since then, many MOF-based materials have been studied as photocatalysts for organic pollutants degradation (Table 1). For instance, MIL-53(M) (M = Fe, Al, Cr) was used to decolorize MB following first-order kinetics [66]. Recently, Wang and coworkers reported a pillared-layer MOF NNU-36 with broad-range visible light absorption and good chemical stability, which exhibits an efficient photocatalytic performance for aqueous Cr(VI) reduction and Rhodamine B (RhB) degradation [67]. Zhang et al. constructed two 3D MOFs [Cu(4,4'-bipy)Cl] n and [Co(4,4'-bipy)·(HCOO) 2 ] n with photocatalytic activity for MB degradation under visible light irradiation [68]. Upon adding H 2 O 2 electron acceptors, the photocatalytic performance of MB degradation was remarkably enhanced, following the LMCT mechanism. These results show that MOFs exhibit potential in photocatalytic organic pollutants degradation. However, it is still a great challenge to develop highly efficient MOF-based photocatalysts for organic pollutants degradation.
Several methods have been explored to improve the photocatalytic activity of MOF-based materials for organic pollutants degradation. For example, metal NPs loading and photocatalytically active composites modification. Karmaoui and coworkers modified the band gap of NH 2 -MIL-125(Ti) with Ag 3 PO 4 NPs because of its narrow band gap [69]. The hybrid material NH 2 -MIL-125(Ti)@Ag 3 PO 4 was synthesized by coating Ag 3 PO 4 NPs on the edge of NH 2 -MIL-125(Ti) to form a core-shell structure, which was confirmed by the results of transmission electron microscopy (TEM) (Figure 3a). The band gap of NH 2 -MIL-125(Ti) in the hybrid material was decreased to 2.39 eV, indicating their potential for photocatalytic applications. The photocatalytic MB and RhB degradation under visible light irradiation were used to evaluate the photocatalytic activity of NH 2 -MIL-125(Ti)@Ag 3 PO 4 . As expected, NH 2 -MIL-125(Ti)@Ag 3 PO 4 exhibits remarkably enhanced photocatalytic performance compared to P25 (P25 = Evonik commercial mixed anatase-rutile phase TiO2 nanophosphor), Ag 3 PO 4 andNH 2 -MIL-125(Ti). This can be ascribed to the formation of an heterojunction between NH 2 -MIL-125(Ti) and Ag 3 PO 4 (Figure 3b,c). Considering the surface plasmon resonance (SPR) of Ag NPs, Mehraj and coworkers developed a novel three-component photocatalyst Ag/Ag 3 PO 4 /HKUST-1 [70]. The deposition of Ag 3 PO 4 NPs in this heterostructured system extends the light absorption to the visible region. Furthermore, the strong SPR effect of Ag NPs helps to boost the electron-hole separation at the interface of this composite, resulting in the drastically enhanced photocatalytic performance of HKUST-1. Photocatalytic degradation of Ponceau BS (PBS) was used to investigate the photocatalytic activity of the Ag/Ag 3 PO 4 /HKUST-1 system. It exhibited 87% degradation as compared to 60% by Ag 3 PO 4 /HKUST-1 and 40% by HKUST-1 (Figure 3d). The enhanced photocatalytic performance of the prepared system was attributed to the synergistic effects of the sequential energy transfer through the Z-scheme mechanism and the SPR effect of Ag NPs ( Figure 3e). Additionally, the Ag/Ag 3 PO 4 /HKUST-1 system is highly stable and reusable ( Figure 3f). These results indicate that the application of metal NPs on MOF-based materials is a potential approach to enhance the photocatalytic activity of MOFs. The deposition of Ag3PO4 NPs in this heterostructured system extends the light absorption to the visible region. Furthermore, the strong SPR effect of Ag NPs helps to boost the electron-hole separation at the interface of this composite, resulting in the drastically enhanced photocatalytic performance of HKUST-1. Photocatalytic degradation of Ponceau BS (PBS) was used to investigate the photocatalytic activity of the Ag/Ag3PO4/HKUST-1 system. It exhibited 87% degradation as compared to 60% by Ag3PO4/HKUST-1 and 40% by HKUST-1 ( Figure 3d). The enhanced photocatalytic performance of the prepared system was attributed to the synergistic effects of the sequential energy transfer through the Z-scheme mechanism and the SPR effect of Ag NPs ( Figure  3e). Additionally, the Ag/Ag3PO4/HKUST-1 system is highly stable and reusable ( Figure 3f). These results indicate that the application of metal NPs on MOF-based materials is a potential approach to enhance the photocatalytic activity of MOFs. Graphitic carbon nitride (g-C3N4) has been studied intensively because of its appealing electronic structure and high chemical stability [71]. More importantly, g-C3N4 possesses appropriate band positions and gap (2.7 eV) for light absorption up to 450 nm. Therefore, g-C3N4 can be used as a photocatalyst for organic pollutants degradation and many other reactions. Wen and coworkers designed a novel hybrid photocatalyst of protonated g-C3N4 coated MIL-100(Fe) frameworks through an in-situ protonation followed by a dip-coating procedure [72]. As compared with the parent materials, the protonated g-C3N4 coated MIL-100(Fe) material showed improved photocatalytic performance in MB and RhB degradation, as well as in oxidative denitrogenation for pyridine by molecular oxygen under visible light irradiation. The excellent photocatalytic activity of this hybrid material can be attributed to the enhanced absorption ability by introducing protonated g-C3N4 on Graphitic carbon nitride (g-C 3 N 4 ) has been studied intensively because of its appealing electronic structure and high chemical stability [71]. More importantly, g-C 3 N 4 possesses appropriate band positions and gap (2.7 eV) for light absorption up to 450 nm. Therefore, g-C 3 N 4 can be used as a photocatalyst for organic pollutants degradation and many other reactions. Wen and coworkers designed a novel hybrid photocatalyst of protonated g-C 3 N 4 coated MIL-100(Fe) frameworks through an in-situ protonation followed by a dip-coating procedure [72]. As compared with the parent materials, the protonated g-C 3 N 4 coated MIL-100(Fe) material showed improved photocatalytic performance in MB and RhB degradation, as well as in oxidative denitrogenation for pyridine by molecular oxygen under visible light irradiation. The excellent photocatalytic activity of this hybrid material can be attributed to the enhanced absorption ability by introducing protonated g-C 3 N 4 on MIL-100(Fe) frameworks and the enhanced photogenerated electron-hole separation through the coating effect. Another study on carbon nitrides and MOFs hybrid materials for photocatalysis was reported by Dontsva and coworkers [73]. In this study, the potassium poly(heptazine imide)/MIL-125-NH 2 (PHIK/MIL-125-NH 2 ) composites were prepared through the dispersion of both materials in water. The results of the surface ζ-potentials of the parent solids suggested that the driving forces of composite formation are the K + ions diffusion from PHIK to MIL-125-NH 2 and the electrostatic interactions between the solids. The formation of this composite was further confirmed by the analysis of FTIR, photoluminescence spectra, as well as SEM. The composites exhibited a remarkable enhanced photocatalytic performance in RhB degradation under blue light irradiation. The reaction rate of this composite was twofold higher than the reaction rate of the parent MOF compound and it displayed a sevenfold enhancement in comparison to the pristine PHIK. Based on the results of EPR studies and Mott-Schottky analysis, the excellent photocatalytic activity of the composite was due to the charge transfer from MIL-125-NH 2 to PHIK. Except for carbon nitrides, many other kinds of photocatalytically active composites are being extensively explored to improve the photocatalytic activity of MOFs in recent years [74][75][76].
By calcination of MOFs, various carbons, metal or metal oxides, and nanomaterials with different properties can be easily fabricated. Chen and coworkers synthesized ZnO NPs with N-doped nanoporous carbon (N-NpC) via a simple approach of encapsulation and carbonization using ZIF-8 as the carbon source [77]. In the fabrication of ZnO@ZIF-8, ZnO NPs not only acts as the support, but also serves as the Zn source for synthesizing ZIF-8 ( Figure 4a). The ZnO@N-NpC core-shell heterostructures were obtained after calcination under N 2 atmosphere at 700 • C. As expected, the prepared ZnO@N-NpC core-shell composites exhibited excellent absorption and photocatalytic MB degradation over the pure ZnO. MB dyes were almost completely degraded in the presence of ZnO@N-NpC core-shell composites under UV light irradiation after 20 min (Figure 4b). Furthermore, this hybrid composite could be reused for five cycles (Figure 4c) and stored for 2 months, indicating its potential in practical photocatalytic applications. Xiao and coworkers successfully synthesized core-shell-structured Fe 3 O 4 @C/Cu and Fe 3 O 4 @CuO composites through direct calcinations of magnetic Fe 3 O 4 @HKUST-1 under N 2 or air ( Figure 4d) [78]. The analysis of UV-vis diffuse reflectance spectroscopy (UV-vis DRS) showed the calcined composites could absorb visible light up to 700 nm. The calculated band gap energy (E g ) value of Fe 3 O 4 @C/Cu was around 1.75 eV, lower than that of Fe 3 O 4 @CuO (1.82 eV), g-C 3 N 4 (2.7 eV) [79], and TiO 2 (3.2 eV) [80]. This can be ascribed to the SPR effect of Cu NPs. Cu NPs can accept the photoinduced electrons from Fe 3 O 4 microsphere, while the photoinduced holes remain on Fe 3 O 4 microspheres, therefore promoting the effective charge separation and decreasing electron-hole recombination. As a result, the Fe 3 O 4 @C/Cu composites exhibited excellent photocatalytic activity for MB degradation in comparison with Fe 3 O 4 @CuO, g-C 3 N 4 , and TiO 2 under visible light irradiation in the presence of H 2 O 2 ( Figure 4e). Furthermore, the magnetic Fe 3 O 4 @C/Cu composites could be easily separated from the reaction media with the help of an external magnetic field (Figure 4f) and be reused five times while preserving the reactivity under photocatalytic conditions. These results show that novel nanocomposites derived from MOF-based materials through a simple calcination procedure, show high stability and superior photocatalytic activity for organic pollutants degradation. This can be used for degrading organic pollutants from industrial waste water.

MOFs for Organic Photocatalysis
The use of MOF-based materials for light-induced organic transformations has attracted extensive interest due to the solar-energy based "green" organic synthesis condition. In comparison to other photocatalytic applications, photocatalytic transformations always need precise control of the adequate reaction rates and selectivity. Therefore, it is a great challenge to fabricate a MOF-based photocatalytic system with high selectivity. Due to the remarkable activity of TiO2 in photocatalysis [81], Ti-containing MOFs have been investigated for photocatalytic oxidation of amines, hydrazine, alkylphenols, alcohols and so on [82,83]. Mechanistic studies suggest that Ti 3+ centers are generated upon UV-vis excitation, accompanying the oxidation of alcohols. When the highly active Ti 3+ centers

MOFs for Organic Photocatalysis
The use of MOF-based materials for light-induced organic transformations has attracted extensive interest due to the solar-energy based "green" organic synthesis condition. In comparison to other photocatalytic applications, photocatalytic transformations always need precise control of the adequate reaction rates and selectivity. Therefore, it is a great challenge to fabricate a MOF-based photocatalytic system with high selectivity. Due to the remarkable activity of TiO 2 in photocatalysis [81], Ti-containing MOFs have been investigated for photocatalytic oxidation of amines, hydrazine, alkylphenols, alcohols and so on [82,83]. Mechanistic studies suggest that Ti 3+ centers are generated upon UV-vis excitation, accompanying the oxidation of alcohols. When the highly active Ti 3+ centers are oxidized into Ti 4+ , the O 2 are reduced into superoxide diatomic · O 2 − , which then reacts with the carbon-centered radicals to form aldehydes or imines. Zr-containing MOFs, particularly the UiO-type MOFs, are extensively explored in photocatalysis because of their ultra-high stability in water. In 2012, Wang and coworkers used NH 2 -UiO-66(Zr) as photocatalysts for aerobic oxygenation of various organic compounds, such as cyclic alkanes, olefins, and alcohols with high efficiency and selectivity [84].  [88] showing excellent photocatalytic activity for the oxygenation of sulfides and phenols with higher selectivity than that of the homogeneous catalyst Sn IV (OH) 2 TPyP. Zhou and coworkers designed a porph-MOF (SO-PCN) with 1,2-bis(2-methyl-5-(pyridin-4-yl)thiophen-3-yl)cyclopent-1-ene (BPDTE) as a photochromic switch and TCPP as a photosensitizer [89]. This exhibits reversible control of 1 O 2 generation and can be applied in 1,5-dihydroxynaphthalene (DHN) photo-oxidation ( Figure 5). In 2014, Zhang and coworkers prepared an anionic porph-MOF UNLPF-10 with in-situ metalation in porphyrin using tetrakis 3,5-bis[(4-carboxy)-phenyl]phenylporphine (H 10 tbcppp) as organic linkers [90]. UNLPF-10 can be used as a photocatalyst for the selective oxygenation of sulfides with excellent yields (Figure 6). It also showed high stability and preserved its crystalline nature after reactions. These studies show that the immobilization of photoactive sites on/in MOFs can result in a remarkable photocatalytic performance for organic transformations. are oxidized into Ti 4+ , the O2 are reduced into superoxide diatomic · O2 − , which then reacts with the carbon-centered radicals to form aldehydes or imines. Zr-containing MOFs, particularly the UiO-type MOFs, are extensively explored in photocatalysis because of their ultra-high stability in water. In 2012, Wang and coworkers used NH2-UiO-66(Zr) as photocatalysts for aerobic oxygenation of various organic compounds, such as cyclic alkanes, olefins, and alcohols with high efficiency and selectivity [84]. The Fe-containing MOFs have received increasing attention in photocatalytic applications because the extensive Fe-O clusters in Fe-containing MOFs can be directly excited by visible light. Two Fe-containing MOFs, MIL-100(Fe) and MIL-68(Fe), were reported for photocatalytic hydroxylation of benzene to phenol with high selectivity under visible light irradiation [85]. A maximal benzene conversion of 30.6% was achieved under optimal conditions (H2O2:Benzene = 3:4, CH3CN:H2O = 1:1 (v/v)) over MIL-100(Fe) after 24 h irradiation. This work shows the potential of Fecontaining MOFs as photocatalysts for benzene hydroxylation with H2O2 as an oxidant, leading to a green and economical process for phenol production. Incorporation of metalloligand complexes like Ru(bpy)3 2+ and Ir(ppy)2(bpy) + into MOFs can extend the MOF-based photocatalytic transformations to Aza-Henry reactions, oxidation of sulfides and arylboronic acids, as well as oxidative coupling of amines [86,87]. The resulting MOFs have exhibited slightly lower photocatalytic activity in comparison to the homogeneous catalysts, while excellent yields and reusability were achieved for these MOF materials.
Porph-MOFs show great potential in photocatalysis. For instance, Wu and coworkers synthesized a tin-porphyin MOF [Zn2(H2O)4Sn IV (TPyP)(HCOO)2]·4NO3·DMF·4H2O (Sn IV TPyP = 5,10,15,20-tetra(4-pyridyl)-tin(IV)-porphyrin) [88] showing excellent photocatalytic activity for the oxygenation of sulfides and phenols with higher selectivity than that of the homogeneous catalyst Sn IV (OH)2TPyP. Zhou and coworkers designed a porph-MOF (SO-PCN) with 1,2-bis(2-methyl-5-(pyridin-4-yl)thiophen-3-yl)cyclopent-1-ene (BPDTE) as a photochromic switch and TCPP as a photosensitizer [89]. This exhibits reversible control of 1 O2 generation and can be applied in 1,5dihydroxynaphthalene (DHN) photo-oxidation ( Figure 5). In 2014, Zhang and coworkers prepared an anionic porph-MOF UNLPF-10 with in-situ metalation in porphyrin using tetrakis 3,5-bis[(4carboxy)-phenyl]phenylporphine (H10tbcppp) as organic linkers [90]. UNLPF-10 can be used as a photocatalyst for the selective oxygenation of sulfides with excellent yields (Figure 6). It also showed high stability and preserved its crystalline nature after reactions. These studies show that the immobilization of photoactive sites on/in MOFs can result in a remarkable photocatalytic performance for organic transformations.   In 2016, Li and coworkers prepared a Pd@MIL-100(Fe) catalytic system by a double-solvent impregnation, followed by a photo-reduction process [91]. TEM images revealed that Pd NPs are dispersed inside the MIL-100(Fe) cavity with an average size of 1.7 nm. After encapsulation of Pd NPs, the UV-vis DRS spectrum of Pd@MIL-100(Fe) exhibited an enhanced absorption in the range of 200-550 nm. This can be compared to the pure MIL-100(Fe), with the absorption edge extending to around 650 nm. Therefore, the Pd@MIL-100(Fe) composites show significant superior photocatalytic activity for N-alkyation of amines with alcohols under visible light irradiation. The Pd@MIL-100(Fe) catalytic system exhibited the highest conversion of aniline of 88%, and a selectivity to Nbenzylaniline of 76% with the aniline/benzyl alcohol ratio of 1:30 after 24 h irradiation. Recently, the same group prepared a bimetallic PdAu@MIL-100(Fe) catalytic system for the light-induced tandem reaction between amines and alcohols to produce N-alkyl amines (Figure 7) [92]. This can be ascribed to the promoting effect in the photocatalytic alcohol-to-aldehyde dehydrogenation of metallic Au. Non-noble metal NPs incorporated MOF composites were also applied for photocatalytic transformations. Wu and coworkers reported that CdS-NH2-UiO-66 composites decorated CdS NRs on the surface of NH2-UiO-66 via a facile photo deposition approach [93]. This work showed that the CdS-NH2-UiO-66 composites can be used as a potential photocatalyst for the selective oxidation of alcohols to their corresponding aldehydes with O2 as the oxidant under visible light irradiation. The large specific surface area of NH2-UiO-66 and the effective charge separation could be responsible for the improved photocatalytic performance. In 2016, Li and coworkers prepared a Pd@MIL-100(Fe) catalytic system by a double-solvent impregnation, followed by a photo-reduction process [91]. TEM images revealed that Pd NPs are dispersed inside the MIL-100(Fe) cavity with an average size of 1.7 nm. After encapsulation of Pd NPs, the UV-vis DRS spectrum of Pd@MIL-100(Fe) exhibited an enhanced absorption in the range of 200-550 nm. This can be compared to the pure MIL-100(Fe), with the absorption edge extending to around 650 nm. Therefore, the Pd@MIL-100(Fe) composites show significant superior photocatalytic activity for N-alkyation of amines with alcohols under visible light irradiation. The Pd@MIL-100(Fe) catalytic system exhibited the highest conversion of aniline of 88%, and a selectivity to N-benzylaniline of 76% with the aniline/benzyl alcohol ratio of 1:30 after 24 h irradiation. Recently, the same group prepared a bimetallic PdAu@MIL-100(Fe) catalytic system for the light-induced tandem reaction between amines and alcohols to produce N-alkyl amines (Figure 7) [92]. This can be ascribed to the promoting effect in the photocatalytic alcohol-to-aldehyde dehydrogenation of metallic Au. Non-noble metal NPs incorporated MOF composites were also applied for photocatalytic transformations. Wu and coworkers reported that CdS-NH 2 -UiO-66 composites decorated CdS NRs on the surface of NH 2 -UiO-66 via a facile photo deposition approach [93]. This work showed that the CdS-NH 2 -UiO-66 composites can be used as a potential photocatalyst for the selective oxidation of alcohols to their corresponding aldehydes with O 2 as the oxidant under visible light irradiation. The large specific surface area of NH 2 -UiO-66 and the effective charge separation could be responsible for the improved photocatalytic performance.

MOFs for Photocatalytic CO2 Reduction
The solar transformation of CO2 into desirable organic products such as CO, methane (CH4), methanol (CH3OH), and HCOOH is a promising approach to reduce the green-house effect and produce renewable energy. Therefore, MOFs are very promising in the field of CCU (Carbon Capture and Utilization). Considerable research has been done in recent years (Table 2) [94].
Recently, Wang and coworkers reported a visible light-driven catalytic system using a cobaltcontaining zeolitic imidazolate framework (Co-ZIF-9) as a robust MOF co-catalyst and [Ru(bpy)3]Cl2·6H2O as a photosensitizer [95]. This photocatalytic system could reduce CO2 to CO with triethanolamine (TEOA) as a sacrificial electron donor at 20 °C and 1 atm CO2. Upon visible-light irradiation, the CO and H2 production rates were 1.4 and 1.0 μmolmin −1 , respectively. However, the CO2 reduction could not occur in the dark or without the ruthenium-based photosensitizer. Moreover, it was hindered drastically when the photocatalytic system was operated without Co-ZIF-9. Furthermore, the CO and H2 evolution decreased sharply when the residues of ZIF-9 after calcination at 1200 °C in helium gas were applied in this system. The results show that the framework of ZIF-9 plays a vital role in CO2 reduction through the promotion of the substrate concentration and carrier transfer. Later, the same group used nanoscale ZIF-67 instead of Co-ZIF-90 as the cocatalyst for CO2 splitting [96]. The new hybrid CO2 reduction system achieved an enhanced photocatalytic performance with a CO and H2 evolution rate of 37.4 and 13 μmol/30 min, respectively, which indicated that ZIF-67 was a novel and efficient cocatalyst for photocatalytic CO2 reduction.
Atomically dispersed photocatalysts, including mononuclear metal compounds or single metal atoms anchored on supports, exhibit the maximum efficiency of metal atoms and allow to investigate the photocatalytic process at the molecular level [97]. Yaghi and coworkers fabricated in 2017 a Recontaining UiO-67 (Ren-MOF) by covalently attaching Re I (CO)3(BPYDC)(Cl) (ReTC, BPYDC = 2,2′bipyridine-5,5′-dicarboxylate) to a zirconium MOF for CO2-to-CO conversion (Figure 8a) [98]. The precise and quantitative control of the density of photoactive Re centers in the MOF unit could change the photocatalytic activity. Re3-MOF, in which each MOF cell unit contains three ReTCs, was found to exhibit the highest photocatalytic activity. Additionally, coating plasmonic Ag NPs on Re3-MOFs enhanced CO conversion by seven times under visible light irradiation with long-term stability up to

MOFs for Photocatalytic CO 2 Reduction
The solar transformation of CO 2 into desirable organic products such as CO, methane (CH 4 ), methanol (CH 3 OH), and HCOOH is a promising approach to reduce the green-house effect and produce renewable energy. Therefore, MOFs are very promising in the field of CCU (Carbon Capture and Utilization). Considerable research has been done in recent years (Table 2) [94].
Recently, Wang and coworkers reported a visible light-driven catalytic system using a cobalt-containing zeolitic imidazolate framework (Co-ZIF-9) as a robust MOF co-catalyst and [Ru(bpy) 3 ]Cl 2 ·6H 2 O as a photosensitizer [95]. This photocatalytic system could reduce CO 2 to CO with triethanolamine (TEOA) as a sacrificial electron donor at 20 • C and 1 atm CO 2 . Upon visible-light irradiation, the CO and H 2 production rates were 1.4 and 1.0 µmolmin −1 , respectively. However, the CO 2 reduction could not occur in the dark or without the ruthenium-based photosensitizer. Moreover, it was hindered drastically when the photocatalytic system was operated without Co-ZIF-9. Furthermore, the CO and H 2 evolution decreased sharply when the residues of ZIF-9 after calcination at 1200 • C in helium gas were applied in this system. The results show that the framework of ZIF-9 plays a vital role in CO 2 reduction through the promotion of the substrate concentration and carrier transfer. Later, the same group used nanoscale ZIF-67 instead of Co-ZIF-90 as the cocatalyst for CO 2 splitting [96]. The new hybrid CO 2 reduction system achieved an enhanced photocatalytic performance with a CO and H 2 evolution rate of 37.4 and 13 µmol/30 min, respectively, which indicated that ZIF-67 was a novel and efficient cocatalyst for photocatalytic CO 2 reduction.
Atomically dispersed photocatalysts, including mononuclear metal compounds or single metal atoms anchored on supports, exhibit the maximum efficiency of metal atoms and allow to investigate the photocatalytic process at the molecular level [97]. Yaghi and coworkers fabricated in 2017 a Re-containing UiO-67 (Re n -MOF) by covalently attaching Re I (CO) 3 (BPYDC)(Cl) (ReTC, BPYDC = 2,2 -bipyridine-5,5 -dicarboxylate) to a zirconium MOF for CO 2 -to-CO conversion (Figure 8a) [98]. The precise and quantitative control of the density of photoactive Re centers in the MOF unit could change the photocatalytic activity. Re 3 -MOF, in which each MOF cell unit contains three ReTCs, was found to exhibit the highest photocatalytic activity. Additionally, coating plasmonic Ag NPs on Re 3 -MOFs enhanced CO conversion by seven times under visible light irradiation with long-term stability up to 48 h (Figure 8b). This exceptional photocatalytic performance of CO 2 -to-CO conversion was ascribed to the synergistic effect of the spatially confined photoactive Re sites and the plasmonic Ag NPs. A Zr-MOF Zr 6 O 4 (OH) 4 (TCPP-H 2 ) 3 (MOF-525, TCPP = 4,4 ,4 ,4 -(porphyrin-5,10,15,20-tetrayl) tetrabenzoate) constructed by Zr 6 clusters and light-harvesting porphyrin linkers, was selected by Ye and coworkers as MOF support, because of its high CO 2 capture capacity and visible-light utilization [99]. A new composite (MOF-525-Co) with single Co sites was generated by incorporating unsaturated Co centers into the porphyrin units. The active Co sites in MOF-525-Co were isolated by the porphyrin linkers and exposed to molecular CO 2 simultaneously. As a result, MOF-525-Co showed significantly enhanced photocatalytic CO 2 conversion. The CO and CH 4 evolution rate of 200.6 and 36.76 mmolg −1 h −1 respectively, were 3.13 times higher than those of the parent MOF-525 (CO: 64.02 mmolg −1 h −1 ; CH 4 : 6.2 mmolg −1 h −1 ). The incorporated single Co sites in MOF-525 enhanced the CO 2 capture capacity and increased the charge separation efficiency in porphyrin linkers. This results in a significantly enhanced photocatalytic performance of CO 2 conversion. These results indicate that the rational introduction of atomically dispersed photocatalysts into MOF frameworks is a promising approach for CO 2 conversion. 48 h (Figure 8(b)). This exceptional photocatalytic performance of CO2-to-CO conversion was ascribed to the synergistic effect of the spatially confined photoactive Re sites and the plasmonic Ag NPs. A Zr-MOF Zr6O4(OH)4(TCPP-H2)3 (MOF-525, TCPP = 4,4′,4′′,4′′′-(porphyrin-5,10,15,20-tetrayl) tetrabenzoate) constructed by Zr6 clusters and light-harvesting porphyrin linkers, was selected by Ye and coworkers as MOF support, because of its high CO2 capture capacity and visible-light utilization [99]. A new composite (MOF-525-Co) with single Co sites was generated by incorporating unsaturated Co centers into the porphyrin units. The active Co sites in MOF-525-Co were isolated by the porphyrin linkers and exposed to molecular CO2 simultaneously. As a result, MOF-525-Co showed significantly enhanced photocatalytic CO2 conversion. The CO and CH4 evolution rate of 200.6 and 36.76 mmolg −1 h −1 respectively, were 3.13 times higher than those of the parent MOF-525 (CO: 64.02 mmolg −1 h −1 ; CH4: 6.2 mmolg −1 h −1 ). The incorporated single Co sites in MOF-525 enhanced the CO2 capture capacity and increased the charge separation efficiency in porphyrin linkers. This results in a significantly enhanced photocatalytic performance of CO2 conversion. These results indicate that the rational introduction of atomically dispersed photocatalysts into MOF frameworks is a promising approach for CO2 conversion. Besides their use as cocatalysts or supports, MOF-derived nanomaterials are also very promising for photocatalytic CO2 conversion. Wang et al. converted the core-shell ZIF-8@ZIF-67 crystals into a novel porous ZnO@Co3O4 composite through a seed-mediated growth process followed by a twostep calcination process (Figure 9a-c) [100]. The resultant porous ZnO@Co3O4 composite exhibited a much higher photocatalytic performance of CO2 conversion with a CH4 evolution rate of 0.99 μmolg −1 h −1 . This was a 66fold enhancement compared to the commercial ZnO (0.015 μmolg −1 h −1 ) and 367fold enhancement compared to commercial TiO2 (P25) (0.0027 μmolg −1 h −1 ) (Figure 9d). The exceptional photocatalytic activity of ZnO@Co3O4 composite was ascribed to its advantageous porous Besides their use as cocatalysts or supports, MOF-derived nanomaterials are also very promising for photocatalytic CO 2 conversion. Wang et al. converted the core-shell ZIF-8@ZIF-67 crystals into a novel porous ZnO@Co 3 O 4 composite through a seed-mediated growth process followed by a two-step calcination process (Figure 9a-c) [100]. The resultant porous ZnO@Co 3 O 4 composite exhibited a much higher photocatalytic performance of CO 2 conversion with a CH 4 evolution rate of 0.99 µmolg −1 h −1 . This was a 66fold enhancement compared to the commercial ZnO (0.015 µmolg −1 h −1 ) and 367fold enhancement compared to commercial TiO 2 (P25) (0.0027 µmolg −1 h −1 ) (Figure 9d). The exceptional photocatalytic activity of ZnO@Co 3 O 4 composite was ascribed to its advantageous porous structure and the cocatalytic function of Co 3 O 4 NPs. Additionally, Co 3 O 4 NPs can significantly decrease the ZnO photocorrosion and thus, improve its photocatalytic stability. Zhang and coworkers prepared a ZnO/NiO porous hollow sphere with sheet-like subunits through thermal treatment of Ni-Zn MOFs for CO 2 conversion [101]. The NiO content in the ZnO/NiO porous hollow spheres was optimized to improve the special surface, CO 2 uptake, and the electron-charge separation of the composites. The excess NiO decreased the incident light absorption and accelerated charge recombination, therefore decreasing the photocatalytic activity. As a result, ZnO/NiO composites with 30% Ni 2+ , denoted as ZN-30, exhibited excellent photocatalytic CO 2 conversion with the CH 3 OH evolution of 1.57 µmolg −1 h −1 . This was due to the highly specific surface area, CO 2 capture capacity, and increased light absorption of the porous hollow structure. Additionally, the authors believed that the n-type ZnO and n-type NiO were derived from Zn-Ni MOFs mixed together homogeneously, leading to the formation of various p-n heterojunctions which could boost the electron-hole separation. These results demonstrate the design of a novel heterogeneous composite with a special structure, by using MOFs as templates, providing new insights to fabricate new photocatalysts with high CO 2 reduction performance. structure and the cocatalytic function of Co3O4 NPs. Additionally, Co3O4 NPs can significantly decrease the ZnO photocorrosion and thus, improve its photocatalytic stability. Zhang and coworkers prepared a ZnO/NiO porous hollow sphere with sheet-like subunits through thermal treatment of Ni-Zn MOFs for CO2 conversion [101]. The NiO content in the ZnO/NiO porous hollow spheres was optimized to improve the special surface, CO2 uptake, and the electron-charge separation of the composites. The excess NiO decreased the incident light absorption and accelerated charge recombination, therefore decreasing the photocatalytic activity. As a result, ZnO/NiO composites with 30% Ni 2+ , denoted as ZN-30, exhibited excellent photocatalytic CO2 conversion with the CH3OH evolution of 1.57 μmolg −1 h −1 . This was due to the highly specific surface area, CO2 capture capacity, and increased light absorption of the porous hollow structure. Additionally, the authors believed that the n-type ZnO and n-type NiO were derived from Zn-Ni MOFs mixed together homogeneously, leading to the formation of various p-n heterojunctions which could boost the electron-hole separation. These results demonstrate the design of a novel heterogeneous composite with a special structure, by using MOFs as templates, providing new insights to fabricate new photocatalysts with high CO2 reduction performance.

MOFs for Water Oxidation
Photocatalytic water splitting into hydrogen and oxygen is a promising and effective strategy to transfer solar energy into chemical energy. To date, many MOF-based materials have been employed as photocatalysts for hydrogen production (Table 3). Du and coworkers reported a Cu2I2-based MOF, Cu-I-bipy, for hydrogen production by UV light with TEOA as a sacrificial agent [102]. It exhibited highly efficient photocatalytic hydrogen evolution with an average rate of 7.09 mmolg −1 h −1 . This exceeds most of the reported MOF-based materials [103]. The Cu2I2 clusters of Cu-I-bipy, serving as the photoelectron generators, can accelerate the Cu(I) hydride interaction, thus providing redox

MOFs for Water Oxidation
Photocatalytic water splitting into hydrogen and oxygen is a promising and effective strategy to transfer solar energy into chemical energy. To date, many MOF-based materials have been employed as photocatalysts for hydrogen production (Table 3). Du and coworkers reported a Cu 2 I 2 -based MOF, Cu-I-bipy, for hydrogen production by UV light with TEOA as a sacrificial agent [102]. It exhibited highly efficient photocatalytic hydrogen evolution with an average rate of 7.09 mmolg −1 h −1 . This exceeds most of the reported MOF-based materials [103]. The Cu 2 I 2 clusters of Cu-I-bipy, serving as the photoelectron generators, can accelerate the Cu(I) hydride interaction, thus providing redox reaction sites for hydrogen production, which is responsible for the excellent photocatalytic activity for hydrogen generation. Furthermore, Cu-I-bipy can be reused at least five times with negligible loss of catalytic activity, indicating it could be a practical application in water splitting. Integration of appropriate co-catalysts like metal NPs, POMs, metal oxides and carbon nitrides has proved to be a potential approach to improve the photocatalytic performance for water splitting. Wang and coworkers reported a NH 2 -MIL-125(Ti)/0.75CN/Ni 15.8 Pd 2.1 photocatalytic system, exhibiting enhanced photocatalytic activity for hydrogen production under visible light irradiation [104]. It exhibited a high hydrogen evolution rate of 8.7 mmolg −1 h −1 , 332 and 1.3 times higher than those of NH 2 -MIL-125(Ti)/0.75CN and NH 2 -MIL-125(Ti)/Ni 15.8 Pd 4.1 , respectively. The improved photocatalytic activity of hydrogen production was ascribed not only to the strong light-absorbing capacity and increased charge transfer of loaded NiPd NPs, but also to the enhanced electron holes separation of heterostructure between NH 2 -MIL-125(Ti) and CN.
Due to the maximized atomic efficiency, single-atom catalysts have exhibited excellent catalytic activity for various reactions, such as electrocatalysis, oxidation, water-gas shift, and hydrogenation. A highly stable porph-MOF Al-TCPP, formulated as (AlOH) 2 H 2 TPCC, was used as the support to anchor Pt(II) into the porphyrin centers (Figure 10a) [105]. Thus, a single Pt atom catalyst (Al-TCPP-Pt) was easily synthesized through a simple reduction process of Al-TCPP-Pt(II). As expected, Al-TCPP-0.1Pt exhibited an excellent photocatalytic performance for hydrogen evolution under visible irradiation, using TEOA as the sacrificial agent. The hydrogen evolution rate of Al-TCPP-0.1Pt was 129 µmolg −1 h −1 and the calculated turnover frequency (TOF) of Al-TCPP-0.1Pt reached 35 h −1 , 30 times higher than that of Al-TCPP-PtNPs (Figure 10b). The results of spectroscopic characterizations and DFT calculations confirmed that the single Pt atoms anchored into porphyrin centers of Al-TCPP open a channel for highly efficient electron transfer, and enhance the hydrogen binding energy, thus resulting in the enhanced photocatalytic performance of hydrogen evolution. reaction sites for hydrogen production, which is responsible for the excellent photocatalytic activity for hydrogen generation. Furthermore, Cu-I-bipy can be reused at least five times with negligible loss of catalytic activity, indicating it could be a practical application in water splitting.
Integration of appropriate co-catalysts like metal NPs, POMs, metal oxides and carbon nitrides has proved to be a potential approach to improve the photocatalytic performance for water splitting. Wang and coworkers reported a NH2-MIL-125(Ti)/0.75CN/Ni15.8Pd2.1 photocatalytic system, exhibiting enhanced photocatalytic activity for hydrogen production under visible light irradiation [104]. It exhibited a high hydrogen evolution rate of 8.7 mmolg −1 h −1 , 332 and 1.3 times higher than those of NH2-MIL-125(Ti)/0.75CN and NH2-MIL-125(Ti)/Ni15.8Pd4.1, respectively. The improved photocatalytic activity of hydrogen production was ascribed not only to the strong light-absorbing capacity and increased charge transfer of loaded NiPd NPs, but also to the enhanced electron holes separation of heterostructure between NH2-MIL-125(Ti) and CN.
Due to the maximized atomic efficiency, single-atom catalysts have exhibited excellent catalytic activity for various reactions, such as electrocatalysis, oxidation, water-gas shift, and hydrogenation. A highly stable porph-MOF Al-TCPP, formulated as (AlOH)2H2TPCC, was used as the support to anchor Pt(II) into the porphyrin centers (Figure 10a) [105]. Thus, a single Pt atom catalyst (Al-TCPP-Pt) was easily synthesized through a simple reduction process of Al-TCPP-Pt(II). As expected, Al-TCPP-0.1Pt exhibited an excellent photocatalytic performance for hydrogen evolution under visible irradiation, using TEOA as the sacrificial agent. The hydrogen evolution rate of Al-TCPP-0.1Pt was 129 μmolg −1 h −1 and the calculated turnover frequency (TOF) of Al-TCPP-0.1Pt reached 35 h −1 , 30 times higher than that of Al-TCPP-PtNPs (Figure 10b). The results of spectroscopic characterizations and DFT calculations confirmed that the single Pt atoms anchored into porphyrin centers of Al-TCPP open a channel for highly efficient electron transfer, and enhance the hydrogen binding energy, thus resulting in the enhanced photocatalytic performance of hydrogen evolution.   [106]. Ni 4 P 2 -MOF-1 exhibited excellent catalytic activity of hydrogen evolution in an acidic aqueous solution (pH = 1.2) with MeOH as the sacrificial electron donor under visible light irradiation. The hydrogen evolution rate of Ni 4 P 2 -MOF-1 was 4.4 mmolg −1 h −1 , and the turnover number (TON) of Ni 4 P 2 -MOF-1 reached 1476 in 72 h irradiation. However, Ni 4 P 2 -MOF-2 only produced trace amounts of hydrogen after 20 h irradiation under identical conditions. They believed that the proximity of Ni 4 P 2 to multiple photosensitizers in Ni 4 P 2 -MOF realizes the multi-electron transfer and enhances the photocatalytic hydrogen evolution performance. Electrochemical and photophysical studies revealed that Ni 4 P 2 can only oxidatively quench the excited state of [Ir(ppy) 2 (bpy)] + as the initiating step of hydrogen evolution, resulting in the drastic differences of photocatalytic performance between the two Ni 4 P 2 -MOF systems.
To use semiconductor NPs as cocatalysts for photocatalytic hydrogen evolution, Ao and coworkers reported a series of heterostructured ZnIn 2 S 4 @NH 2 -MIL-125(Ti) composites with ZnIn 2 S 4 nanosheets highly dispersed on the surface of NH 2 -MIL-125(Ti) [107]. The heterostructure between ZnIn 2 S 4 nanosheets and NH 2 -MIL-125(Ti) could have increased the capacity of electron transfer and promoted the photogenerated charge separation, resulting in the enhanced photocatalytic performance of hydrogen evolution. Tang and coworkers encapsulated the Cu-BTC MOF into a ZnO/graphene oxide (GO) photocatalytic system through electrostatic interaction to form the electrostatic interaction assembly of ZnO/GO and Cu-BTC, which exhibited enhanced photocatalytic activity of hydrogen evolution [74]. In this prepared heterostructure, ZnO acted as the photoelectron generator, and GO served as the channel of photoelectron transfer from ZnO to Cu-BTC as well as the supporting matrix for ZnO and Cu-BTC ( Figure 11). The electron spin resonance (ESR) results have revealed that the Cu-BTC could extend the lifetime of free radicals and boost the H recombination to form H 2 , enhancing the photocatalytic performance of hydrogen evolution. As a result, the electrostatic interaction assembly of ZnO/GO and Cu-BTC showed the highest hydrogen evolution rate of 129 µmolg −1 h −1 , which is ninefold and threefold higher than that of ZnO/GO and ZnO/(Cu-BTC)/GO complex, respectively. hydrogen evolution, resulting in the drastic differences of photocatalytic performance between the two Ni4P2-MOF systems.
To use semiconductor NPs as cocatalysts for photocatalytic hydrogen evolution, Ao and coworkers reported a series of heterostructured ZnIn2S4@NH2-MIL-125(Ti) composites with ZnIn2S4 nanosheets highly dispersed on the surface of NH2-MIL-125(Ti) [107]. The heterostructure between ZnIn2S4 nanosheets and NH2-MIL-125(Ti) could have increased the capacity of electron transfer and promoted the photogenerated charge separation, resulting in the enhanced photocatalytic performance of hydrogen evolution. Tang and coworkers encapsulated the Cu-BTC MOF into a ZnO/graphene oxide (GO) photocatalytic system through electrostatic interaction to form the electrostatic interaction assembly of ZnO/GO and Cu-BTC, which exhibited enhanced photocatalytic activity of hydrogen evolution [74]. In this prepared heterostructure, ZnO acted as the photoelectron generator, and GO served as the channel of photoelectron transfer from ZnO to Cu-BTC as well as the supporting matrix for ZnO and Cu-BTC ( Figure 11). The electron spin resonance (ESR) results have revealed that the Cu-BTC could extend the lifetime of free radicals and boost the H recombination to form H2, enhancing the photocatalytic performance of hydrogen evolution. As a result, the electrostatic interaction assembly of ZnO/GO and Cu-BTC showed the highest hydrogen evolution rate of 129 μmolg −1 h −1 , which is ninefold and threefold higher than that of ZnO/GO and ZnO/(Cu-BTC)/GO complex, respectively. Figure 11. Schematic illustration of the electrostatic interaction assembly of ZnO/GO and Cu-BTC and its photocatalytic H2 evolution mechanism. Reproduced with permission from Reference [74]. Copyright Tsinghua University Press and Springer-Verlag GmbH Germany 2017.

Conclusions
In this review, we have discussed the functions of MOF materials in the photoredox chemical systems. MOFs can be used as photocatalysts due to the facile modification of organic linkers with photocatalytic active groups such as amine and porphyrin. In addition, the high porosity of MOFs makes them capable to act as hosts for photoredox species, like precious metals, semiconductor NPs, Figure 11. Schematic illustration of the electrostatic interaction assembly of ZnO/GO and Cu-BTC and its photocatalytic H 2 evolution mechanism. Reproduced with permission from Reference [74]. Copyright Tsinghua University Press and Springer-Verlag GmbH Germany 2017.

Conclusions
In this review, we have discussed the functions of MOF materials in the photoredox chemical systems. MOFs can be used as photocatalysts due to the facile modification of organic linkers with photocatalytic active groups such as amine and porphyrin. In addition, the high porosity of MOFs makes them capable to act as hosts for photoredox species, like precious metals, semiconductor NPs, and POMs, providing additional possibilities for photocatalytic applications. In recent years, MOFs have served as sacrificial templates or precursors in preparing more stable and conductive porous carbon, metal oxides, or porous carbon/metal oxides composite nanomaterials via simple pyrolysis processes. MOFs have an inherent high porosity and a uniform dispersion of metal nodes in their network. Because of this, the MOF-derived nanomaterials keep their high porosity and the high surface area, and show uniform heteroatom doping and adjustable morphology. Therefore, the MOF-derived nanomaterials are promising candidates for photocatalytic applications. The typical applications of MOFs in heterogeneous photocatalysis were summarized in detail, indicating that MOFs are promising candidates for heterogeneous photocatalysis. These applications were including pollutants degradation, organic transformations, CO 2 reduction, and water splitting. There are still some problems that need to be solved. Only a tiny fraction of the many MOFs that have been reported are suitable for photocatalysis. Therefore, new MOFs with redox active metals and/or functional organic ligands should be designed and fabricated for heterogeneous photocatalysis. The photocatalytic efficiencies of MOFs do not yet meet the requirements for practical applications. It is of great importance to improve the photocatalytic efficiencies of MOFs. Finally, cost-effective photocatalytic systems should avoid the use of expensive precious metals, and replace them by abundant transition metals or by metal-free variants. Council and UGENT-BOF grant for financial support. We also thank Heleen de Froe for polishing the English of this review.