Nyrdvomenshor Nephrite Deposit, Polar Urals, Russia

: We studied the quality characteristics, chemical, mineral and isotope composition of nephrite, diopsidite and rodingite of the Nyrdvomenshor nephrite deposit in the Polar Urals. We applied visual petrographic and mineralogical studies, X-ray spectral ﬂuorescence, ICP-MS analysis, and a scanning electron microscope with a dispersive microanalysis system, to measure the oxygen isotope composition. According to its quality characteristics, the nephrite was substandard. Here, uvarovite, which forms idiomorphic grains, sometimes sheath-like and less often xenomorphic elongated, and substituting the chromite, was commonly encountered. The nephrite was formed due to both metamorphic and metasomatic processes. The serpentinite was replaced by diopsidite, which was then replaced by nephrite. The metamorphism intensiﬁed the metasomatism of the serpentinite melange and provided the cryptocrystalline tangled-ﬁbrous structure of the nephrite. Then, metamorphism and metasomatism led to the formation of omphacite and the cracking of the nephrite, which reduced its quality. As these processes progressed, the contribution of the crustal ﬂuid increased.


Introduction
Nephrite consist of fibrous tremolite or actinolite. The general formula for the tremoliteactinolite-ferroactinolite isomorphic series is Ca 2 (Mg,Fe) 5 Si 8 O 22 (OH) 2 . It is a highly valuable jewelry and ornamental stone, long used by humankind, and especially popular in China and New Zealand. The most expensive samples are white translucent, black and bright green with a minimum amount of ore minerals, or with the "cat's eye" effect nephrites, as well as alluvial pebbles with edges of coloring.
Nephrite deposits belong to two endogenous geological industrial types: those formed at the ultramafic metasomatites of ophiolites (serpentinite type, S-type) and those formed at the carbonate tremolite-calcite magnesian skarns (dolomite type, D-type) [1,2]. Deposits of the S-type are a source of predominantly green, brown and black nephrite, while deposits of the D-type produce mainly light-colored nephrite, in colors from white through to light green and brown (honey), due to the fact that the oxidation of divalent iron to trivalent, black nephrite, is less common [3,4]. The Dahua deposit in the Guangxi Zhuang Autonomous Region [3] and the Luodian deposit in Guizhou Province [5] in southern China, formed on the contact of diabases and limestones, are close to the D-type. The exogenous geological industrial type is represented by placers, of which the alluvial ones are the most productive.
In China, D-type nephrite deposits are the most common, so they are the best studied. There are few deposits of S-type nephrite outside of Russia. In China, the Manas deposit

Materials and Methods
In order to assess the quality and composition of the nephrite from the Nyrdvomenshor deposit, which includes the Nyrdvomenshor and Ray-Iz sites, we studied 8 polished plates of alluvial material. An angular rodingite sample and a polished jadeite plate were examined as additional material.
Visual petrographic and mineralogical studies were performed in natural light, using photofixation. Decorative properties (color, shade, pattern, presence of edges, degree of roughness) were determined using an MBS-10 binocular microscope and a special CYZ-B05 flashlight.
The chemical composition of the rocks was determined using the X-ray spectral fluorescence method on an XRF-1800 wave X-ray fluorescence spectrometer (Shimadzu, Kyoto, Japan) at the "Geoanalitic" Research Center at IGG UrB RAS, Ekaterinburg, according to the method in [42], and the analysts N.P. Gorbunova, L.A. Tatarinova, I.A. Zhelunitsyn and A.A. Nekrasova.
The samples were decomposed and the impurity element content was analyzed using ICP-MS analysis at the "Geoanalitic" Research Center at IGG UrB RAS, by analyst D.V. Kiseleva, on a NexION300S quadrupole ICP mass spectrometer, Perkin Elmer, USA. The microwave decomposition of the samples was carried out using a mixture of HCl + HNO 3 + HF acids, using the Berghof Speedwave MWS 3+ system. Typical operating conditions of the mass spectrometer are as follows: the power of the radio frequency generator is 1300 W and the material of the interface cones is platinum. All measurements were carried out in the mode of quantitative analysis, with the construction of calibration curves. Multi-element standard solutions certified in accordance with ISO 9001 Perkin Elmer Instruments were used to construct the calibration dependencies. Certified samples of BCR-2 basalt and AGV-2 andesite USGS were used to control the correctness and accuracy while determining the trace element composition. The obtained concentrations of scattered, rare-earth and trace elements correspond to the certified values, with an acceptable deviation of within 15%. The errors in element identification are (rel. %): 24 (Cr, Ni, Co, Cu, V, Ba, Sr), 30 (Rb), 41 (REE), 50 (Zr), and 60 (Y, Hf, Ta, Nb, Th, U).
The mineral composition was studied using a LEO-1430VP scanning electron microscope, Carl Zeiss, Germany, with the INCA Energy 350 energy dispersive microanalysis system, Oxford Instruments, UK, at the "Geospectr" Research Center at GIN SB RAS, Ulan-Ude, by the analyst E.A. Khromova. The research conditions are as follows: accelerating voltage-20 kV, probe current-0.3-0.4 nA, probe size-<0.1 microns, and measurement time-50 s (live time),with the analysis error in the amount reaching 2-4 wt. %, depending on the quality of the sample surface and the characteristics of its composition. The content of trivalent iron was calculated using stoichiometry.
The oxygen isotope composition was measured on a FINNIGAN MAT 253 gas mass spectrometer at the "Geospectr" Research Center at GIN SB RAS, Ulan-Ude, by the analyst V.F. Posokhov, using the double intake system in the classical version, with a standard sample. To determine δ 18 O values, the samples were prepared using the laser fluorination (LF) method in the mode "laser ablation with oxygen extraction from silicates" in the presence of a BrF 5 reagent, according to the method in [43]. The calculations were carried out with respect to the O 2 working standard, and calibrated using the V-SMOW scale by regular oxygen measurements for the international standards for NBS-28 quartz and NBS-30 biotite. The correctness of the values obtained was controlled by regular measurements of the center's own internal standard for GI-1 quartz and laboratory IGEM RAS Polaris quartz. The measurement error of the obtained δ 18 O values was at the level of (1 s) ± 0.2%.

Geology of Nyrdvomenshor Deposit
The Nyrdvomenshor deposit is located on the contact of the Rai-Iz ultramafite massif in the Polar Urals with metamorphic and intrusive rocks at the basin of the upper and middle reaches of the Nyrdvomenshor stream, 56 km northwest of Labytnangi town in the Priuralsky district of the Yamalo-Nenets Autonomous Okrug.
Nephrite was found here in 1974 by the "Sevkvartssamotsvety" enterprise. In 1975-1980, 250 nephrite and 60 jadeite locations were found in the bedrock and boulder placers. Some of them were industrially assessed and underwent pilot testing with inventory calculation. In 1980-1981, 21.8 tons of ornamental nephrite (1st grade) were mined from alluvial placers. Protocol No. 20\7 of 26 February 1982 from the Ministry of Geology of the USSR approved the nephrite reserves of 21.8 tons. In 1985-1990, the Polar-Ural Geological Exploration Expedition performed a 1:50,000 survey of this area. In 1991, the "Nord Rifei" enterprise reassessed the nephrite and jadeite sites. Protocol No. 46\91 of 28 December 1991 from the "Zapsibkomgeologiya" geological section tested the forecast resources: nephrite-1000 tons; jadeite-5000 tons, jasper-10,000 tons.
On the 14 October 2013, the Department for Subsoil Use in the Yamalo-Nenets Autonomous Okrug put up the Nyrdvomenshor site (nephrite, jadeite, jasper) for auction. Four companies submitted an application, but were not admitted to the auction, and the auction did not happen. On the 31 July 2014, the authorities of the Yamalo-Nenets Autonomous Okrug established the Polar-Urals Nature Park, which included the territory of the licensed area. According to protocols No. 24-TV of 25 December 2019 and No. 12-TV of 6 October 2020, "NTS-Uralnedra" tested the forecasted resources of nephrite, jadeite and jasper of the Rai-Iz site, which was not included in the natural park, and found the following: nephrite (raw)-3000 tons; jadeite (raw)-15,000 tons; jasper (raw)-11,000 tons. On the 9 November 2020, the Department for Mineral Resources in the Ural Federal District announced an auction for the right to use the subsoil for the purpose of the geological study, exploration and extraction of nephrite, jadeite and jasper at the Rai-Iz site. According to the results of the auction, the license was issued to the "Salekhard Mining Enterprise".
The deposit is confined to the zone of northern tectonic contact along the Main Ural fault of the Ray-Iz ultramafic massif with metamorphic and intrusive rocks of the Harbey block of the Middle-Late Proterozoic and metamorphosed sedimentary-volcanogenic rocks of the Lemvin structural-facies zone of the Paleozoic age ( Figure 1). The Rai-Iz massif is composed mainly of harzburgites, dunites and serpentinites, formed after these [20,44]. Paleozoic sedimentary-volcanogenic formations are represented by clay-siliceous and carbonaceous-siliceous shales with interlayers of metaeffusives of ultramafic composition. The contact of the Rai-Iz massif along the Main Ural fault is a zone of polymictic melange with formations of diopsidites, rodingites, plagioclasites, albite-jadeitites, and nephrites. Eluvial-deluvial, fluvioglacial and alluvial deposits are common.
Nephrite sites are known to be in bedrocks, piles and placers, mostly in the area of the Nyrdvomenshor and Kharamatalaus faults ( Figure 2) within serpentine melange (Figure 3), in the contact zones of after-gabbro bodies. In the bedrock, nephrite forms with more than 300 lenticular veins, with a length of 1-60 m and a thickness of several centimeters to 3 m. There are five main types of nephrite localization: the veins in serpentinites; in the contact zone of serpentinites and metaeffusives; metaeffusives; in the contact zone of after-gabbroid rodingites and serpentinites; and in rodingites [20].
The erosion of most nephrite veins provided the bulk of block-boulder material that makes up the industrial glacial-alluvial placer deposit-the main object of nephrite extraction ( Figure 4). During the boulder transportation, there was a natural improvement in the quality of nephrite, due to abrasion of the talc-tremolite sheath [20]. The alluvial placer of nephrite is confined to the channel and floodplain parts of the Nyrdvomenshor Creek and its tributaries-the Nephritovyi and Obraztsovyi streams. The width of the placer ranges from 20 to 60 m, and the length is up to 4.5 km. The size of the nephrite boulders is 0.1-2.9 m. The average frequency of occurrence is 1 boulder per 680-700 m 2 .      The erosion of most nephrite veins provided the bulk of block-boulder material that makes up the industrial glacial-alluvial placer deposit-the main object of nephrite extraction ( Figure 4). During the boulder transportation, there was a natural improvement in the quality of nephrite, due to abrasion of the talc-tremolite sheath [20]. The alluvial placer of nephrite is confined to the channel and floodplain parts of the Nyrdvomenshor Creek and its tributaries-the Nephritovyi and Obraztsovyi streams. The width of the placer ranges from 20 to 60 m, and the length is up to 4.5 km. The size of the nephrite boulders is 0.1-2.9 m. The average frequency of occurrence is 1 boulder per 680-700 m 2 .  The erosion of most nephrite veins provided the bulk of block-boulder material that makes up the industrial glacial-alluvial placer deposit-the main object of nephrite extraction ( Figure 4). During the boulder transportation, there was a natural improvement in the quality of nephrite, due to abrasion of the talc-tremolite sheath [20]. The alluvial placer of nephrite is confined to the channel and floodplain parts of the Nyrdvomenshor Creek and its tributaries-the Nephritovyi and Obraztsovyi streams. The width of the placer ranges from 20 to 60 m, and the length is up to 4.5 km. The size of the nephrite boulders is 0.1-2.9 m. The average frequency of occurrence is 1 boulder per 680-700 m 2 .

Diopside and Rodingite
The two samples, 162 and 3/12 ( Figure 5), are represented by diopsidites, "karkaro" [1]. No. 162 is grayish-white with greenish streaks of uvarovite and black grains of chromite, while no. 3/21 is of a heterogeneous light-green color, due to the uneven distribution of tremolite and chlorite.

Diopside and Rodingite
The two samples, 162 and 3/12 ( Figure 5), are represented by diopsidites, "kark [1]. No. 162 is grayish-white with greenish streaks of uvarovite and black grains of mite, while no. 3/21 is of a heterogeneous light-green color, due to the uneven distrib of tremolite and chlorite.  The chemical analysis of another sample (Table 3) indicates that Californian jade is, vesuvianite, is also present at the deposit.   Local light-green rodingite with a yellowish shade is traditionally called "californite", that is, Californian jade. However, as a result of the sample analysis, it turned out that it consists of hydrogrossular Ca 2.89 Al 2.00 Si 2.89 O 12 (OH) 0.11 (  8 , forming veinlets and cloud-like aggregates. The chemical analysis of another sample (Table 3) indicates that Californian jade, that is, vesuvianite, is also present at the deposit.  Notes: n-the number of analyzes.

Characteristics of Nephrite
Nephrite is mostly heterogeneously colored; a homogeneous color is less common ( Figure 6). It is a trickle-like grayish-green to olive-green; dark grayish-green, often with spots, with flakes of a lighter grayish-green color up to 3 mm across. Thin, rare grains of ore minerals are characteristic. Ore mineral grains of up to 2 mm in size, making up to 3% of the sample area, are evenly distributed. In sample 2/21, there are numerous visually distinguishable needle-like tremolite crystals all over the surface. One can see matte weathering crusts of a lighter grayish-green color up to 0.5 cm thick. The translucency is up to 0.2 cm.

Mineral Composition of Nephrite
We studied the mineral composition of the nephrite. It is dominated by cryptocrystalline tremolite (Ca1.90Na0.04K0.02Al0.02)∑1.98(Mg4.53Fe0.45Mn0.01)∑4.99Si8.02O22(OH)2 (Table 4) diverse in morphology from fine-fibrous (Figure 7a,b) to rare radiaxial (Figure 7c). There are also larger, individual needle-like crystals (Figure 7g,h) (Table 4). Intense fracturing is observed, and in sample 2/21 it reaches foliation. Nephrite reacts badly to polishing, with intense shagreen and notches. Mirror polishing occurs less often, but with cracks, or shagreen, there is an undulated pattern and cracks. Polishing is often heterogeneous: areas of extraneous mineral formation in practice do not respond to a polish, and they remain matte.
Chromite grains (Table 4) are rarely idiomorphic and homogeneous; they are more often fragmented, with an increased chromium and iron content (Figure 7b (Table 4) composes separate cloud-shaped isometric-to-elongated sections, cuts and overgrows chromite (Figure 7b,c), and, less often, forms veinlets with grains of chromite and pentlandite. Chlorite, cutting or overgrowing chromite, contains more chromium and magnesium.
Chromite grains (Table 4) are rarely idiomorphic and homogeneous; they are more often fragmented, with an increased chromium and iron content (Figure 7b

Isotope Composition of the Rocks
We studied the oxygen isotope composition of the rocks of the Nyrvomenshor deposit ( Table 5). The isotope composition of diopsidites is -6.8 and 7.8‰ δ 18 O. The hydrogarnet rodingite values were even lower-6.6‰ δ 18 O. The nephrites had a heavier isotope composition: 8.2-9.7‰ δ 18 O (based on six analyses). The isotope composition of the jadeite was close to nephrite-8.8% δ 18 O.

Discussion
The nephrite of the Nyrdvomenshor deposit is characterized by heterogeneous, unattractive coloration, jointing from foliation, and low translucency. Therefore, in terms of its quality characteristics, it does not correspond to standard jewelry or ornamental nephrite.
In Russia, the S-type nephrite is mainly mined in the Eastern Sayans, in the Oka district of the Republic of Buryatia. The nephrite of the Ospa deposit is of the best quality. The color is different shades of green, mostly bright bluish-green, brownish in some places, or with white veins and spots. The nephrite is massive, and less often is indistinctly striped cryptocrystalline. The structure is tangled and fibrous. Tremolite makes up 95%-100%, and there is a fine uniform inclusion of chrome spinel, replaced by magnetite (1%), up to 2 mm in size [20,47]. There is a "cat's eye" effect [48].
The color of the nephrite of the Gorlykgol deposit is heterogeneous, spotted, and mostly green of different tones, although a black color also occurs. The nephrite is cryptocrystalline and massive, less often being shale. The structure is tangled and fibrous, and fibroblastic. It is transparent to a depth of 4-10 mm [47].
The color of the nephrite of the Bortogol deposit is green, of various tones. The contact areas have a shale texture, and prismatic tremolite and chlorite are present there [20]. There is a "cat's eye" effect.
The nephrite of the Sagan-Sair deposit has a non-uniform color, from gray-green to dark green, with bluish-green spots and greenish veins. The texture ranges from massive to shale, and the structure is cryptocrystalline. The inclusions of ore minerals account for up to 2%, and it is transparent to a depth of 2-3 mm. The nephrite is of low quality, due to fracturing, and shows a presence of large-crystalline lamellar tremolite, chlorite, talc, and serpentine. However, at the same time there are signs of the "cat's eye" effect.
The nephrite of the Ulan-Khoda deposit is different. In the central part, it is massive, light green like a green apple, and with the marginal parts composed of shale nephrite of a brownish-green color. The structure is tangled and fibrous, i.e., nemato-fibroblastic. There are uniformly scattered rounded grains of chrome spinel, up to 1 mm in size. Light-green nephrite is transparent in plates with a thickness of more than 2 cm, and brown-green-to a depth of 1 cm. Light-green nephrite is replaced by a brownish-green nephrite also near the cracks and in the areas of catalase. The nephrite recrystallizes in the areas of maximum cataclysm, and becomes grayish without ore inclusions [20,49].
Nephrite is mined in the western Hamar-Daban, Zakamensky district of the Republic of Buryatia. The color of the nephrite of the Khamarkhuda deposit ranges from green to brownish-grayish with yellowish, greenish shades, as well as black. Bluish-green nephrite is characteristic and massive, with rare fine-ore mineral inclusions. The structure is tangled and fibrous, i.e., fibroblastic, and the texture is massive. In an amount of up to 1%, there is chlorite, chrome spinel, magnetite, clinocoisite, and sulfides. The marginal parts of the veins are composed of dark-green spotted nephrite with clinocoisite and magnetite. The black color is caused by the intensive development of fine graphite. The graphite is evenly distributed in the rock, often forming flakes, clusters at the grain boundary, and cracks. There is a "cat's eye" effect [20].
The color of the nephrite of the Khargantinskoye deposit is uneven-trickled, spotted, and zonal; the core is blue-green, the 15-20 cm wide border is brownish-green and, grayishgreen. The texture is massive and the structure is cryptocrystalline. It is transparent to a depth of 1-8 mm. There are inclusions of calcite, chlorite, ore minerals, and asbestos streaks [47].
Nephrite is occasionally mined in the Western Sayan, in the Krasnoyarsk region and Tuva. The color of the nephrite of the Kurtushiba deposit is bluish-green, grayish-green, and gray, with varying degrees of tone density. The nephrite is dense, massive cryptocrystalline. The structure is tangled and fibrous. Chlorite, magnetite and chrome spinel are observed there [20].
Previously, the Akademia deposit was developed in the Southern Urals, in the Chelyabinsk Oblast. The nephrite color is uniform, a mottled bluish-green, green, light green, rarely almost white, brownish-yellow and brownish-gray. There are veins of white, gray-hite, bluish-white to brownish-yellow and brown colors. The structure of the nephrite involves tangled fibrous, radially radiant leafy aggregates and larger felt-like clusters of the finest tremolite crystals. The nephrite is transparent up to 2 cm deep. Inclusions of ore minerals are characteristic: chromite, magnetite, nickeline, cobaltite, maucherite, pyrite and chalcopyrite. Sometimes there is up to 5% of actinolite and relics of antigorite in amounts up to 35%. Chromite is replaced by garnet of the uvarovite-grossular series. Vesuvianus is found in association with the garnet. Secondary minerals are scaly, flake-like tremolite, and zoisite [20,39].
Nephrite is extracted at the Bazhenovskoye deposit of chrysotile asbestos in the Middle Urals in the Sverdlovsk Oblast. The nephrite color is homogeneous-to-heterogeneous green, light green, bluish-green, grayish-green, ans greenish. There are spots, veins, and lenses of a bright bluish-green or light-green color. The texture is massive, spotted and striped. The bulk (65%-75%, and less often more than 80%) of the nephrite is represented by tremolite. The mineral forms a fibroblastic tangled fibrous, sometimes porphyroblastic, sheaf-like structure. In the bulk, there is antigorite, sometimes forming finely scaled aggregates; in this case, its content can reach 25%-35%. There are diopside and talc. There is a rare, homogeneously distributed inclusion of black chromite, from 3 to 5%, with a grain size of up to 2 mm, replaced by chromic grossular. Inclusions of thin, less than 1 mm, grains of nickeline and maucherite are evenly spaced. The nephrite is transparent to a depth of 0.5 to 2 cm [35].
The mineral composition of the Nyrdvomenshor nephrite is peculiar. Minerals such as omphacite, barite, and millerite have not been previously observed in S-type nephrite. Fe-dominant mineral from the shuiskite group has not been described at all before.
Uvarovite is of even greater interest. It forms visually distinguishable secretions, and is present in all samples in large quantities, forming independent grains and replacing the chromite. Uvarovite was previously described in the nephrite of the Fentien deposit, Taiwan [12]. However, the published garnet analysis results correspond to chromium grossular (11.6 wt. % Cr 2 O 3 on average; the maximum content is 12.86 wt. %, and the higher crystal core analysis results correspond to a mixture of chromium grossular and chromite). Uvarovite was mentioned as a mineral of the nephrite of the Nyrdvomenshor and the deposits of British Columbia, Canada [20] and Ya'an, Sichuang Province, China [50] without any analysis data attached.
Garnet of a grossular-uvarovite composition was found in the nephrite of the Nasławice deposit in Poland [28], the Bazhenov chrysotile-asbestos deposit [35] and the Pounamu Ultramafics, Westland, New Zealand [30]. So far, the only reliable finding of abundant low-alumina uvarovite in S-type nephrite has been recorded at the Manas deposit in the Northern Tien Shan in the north of the Xinjiang Uygur Autonomous Region of China [7]. A single uvarovite analysis is also reported from the nearby Puserka jadeite deposit, related to the Syum-Key ultramafic massif [51].
The S-type of nephrite was specified according to its chemical composition. It is believed that S-type nephrite has usual values of Fe 2+ /(Mg + Fe 2+ ) > 0.06, whereas for the D-type nephrite it is <0.06 [52]. The Nyrdvomenshor nephrite value of Fe 2 O 3∑ /(MgO + Fe 2 O 3∑ ) varies within the range of 0.19-0.21 (Table 3).
The content range is wider for the Russian deposits.  [20].
The content of these elements in the Nyrdvomenshor nephrite (based on our data) is reduced (Cr 400-700 ppm, Ni 400 ppm, Co 21-24 ppm, Table 3), due to the interaction of the serpentinite melange with terrigenous and intrusive rocks, but it still corresponds to the S-type nephrite. Previously, higher values were shown: 1110, 570, and 68, based on 7 analyses [20]. Thus, the Nyrdvomenshor nephritie is typically the S-type.
The content of rare earth elements (REE) ranges from 0.460 to 0.948 ppm (Table 3), and the distribution pattern is flat with a weak right slope-this is from the enrichment with light REE, a positive Eu anomaly (Figure 8).
A positive Eu anomaly is observed at the Manas deposit, and a negative one at the Eastern Sayan deposits, with a right slope [7]. A positive Eu anomaly indicates a complex source of ore-forming fluid [7]. The Kutcho deposit has a left slope-this indicated enrichment with heavy REE, which is explained by the acidic environment of nephrite formation; the weakly negative Eu anomaly is attributed to the reducing metallogenic environment [24]. The REE profiles of the Kutcho and Polar (Canada), Rim and South Westland (New Zealand), Golmud (Qinghai, China), Manas (Xinjiang, China) and Ulankhoda (Eastern Sayan, Russia) deposits were compared [24]. The ΣREE contents ranged from 0.250 to 7.660 ppm-the Kutcho nephrite had a higher ΣREE value (2.141-2.920 ppm), while the ΣREE value of New Zealand nephrite was the lowest (0.378-0.671 ppm). Since the value of ΣREE increases with decreasing pH, it is assumed that the metallogenic environment of the Kutcho nephrite was very acidic. In relatively restorative conditions, δEu shows a negative anomaly, which is shown for all five deposits. Golmud, Manas and Ulankhoda show a right slope [24]. Based on the peculiarities of the distribution of REE in the Nyrdvomenshor nephrite, it can be assumed that it was formed under the influence of a complex, non-acidic solution in an oxidizing environment. A positive Eu anomaly is observed at the Manas deposit, and a negative one at the Eastern Sayan deposits, with a right slope [7]. A positive Eu anomaly indicates a complex source of ore-forming fluid [7]. The Kutcho deposit has a left slope-this indicated enrichment with heavy REE, which is explained by the acidic environment of nephrite formation; the weakly negative Eu anomaly is attributed to the reducing metallogenic environment [24]. The REE profiles of the Kutcho and Polar (Canada), Rim and South Westland (New Zealand), Golmud (Qinghai, China), Manas (Xinjiang, China) and Ulankhoda (Eastern Sayan, Russia) deposits were compared [24]. The ΣREE contents ranged from 0.250 to 7.660 ppm-the Kutcho nephrite had a higher ΣREE value (2.141-2.920 ppm), while the ΣREE value of New Zealand nephrite was the lowest (0.378-0.671 ppm). Since the value of ΣREE increases with decreasing pH, it is assumed that the metallogenic environment of the Kutcho nephrite was very acidic. In relatively restorative conditions, δEu shows a negative anomaly, which is shown for all five deposits. Golmud, Manas and Ulankhoda show a right slope [24]. Based on the peculiarities of the distribution of REE in the Nyrdvomenshor nephrite, it can be assumed that it was formed under the influence of a complex, non-acidic solution in an oxidizing environment.
Fluids containing calcium and silica come either from late intrusive bodies or as a result of long-range transport along tectonic ruptures.
At the regressive or metamorphic stage, the diopside is replaced by a tremolite aggregate-nephrite: 2CaMgSi2O6 + Mg 2+ + 4Si 4+ + H2O + 5.5O2 → Ca2Mg5[Si4O11]2(OH)2. The mineral composition reveals a complicated formation history of the nephrite involving the combination of tectonic and metasomatic processes. At the progressive stage, serpentine is replaced by diopside:  2 , but in the equation we use the formula of the tremolite with no end-member, so as not to introduce the Fe.
The relic chromite is crushed with an increase in the content of the manganese and zinc, and replaced by uvarovite and an unnamed mineral from the shuiskite group. Heazlewudite is replaced by pentladite-tremolite and pentlandite appear in a small amount in one sample of diopsidite. Chlorite and part of the uvarovite of the nephrite are inherited from the diopsidite.
The third progressive stage led to the replacement of the tremolite with omphacite (the reaction is not balanced, due to the variable composition of the omphacite) and to the crushing of the nephrite, which worsened its quality as an ornamental stone.
A further process in the development, with an increase in the sodium and aluminum content, should lead to the formation of jadeite NaAlSi 2 O 3. Previously, the Nyrdvomenshor jadeite was believed [36] to have been formed before the nephrite.
The joint occurrence of jadeitite and nephrite boulders in the region, noted in the Nyrdvomenshor deposit, has long been known [56]. But even at the Nyrvomenshor deposit, their bedrock outcrops are separated spatially: nephrite outcrops are located to the east, and jadeitite outcrops to the west, where the pressure was higher. Syum-Keu jadeitites were previously studied: their origin under the influence of subduction fluids was shown either in association with omphacite from subduction peridotites [57], or after trondhjemite, with omphacite as an intermediate phase [58].
At the Nyrdvomenshor deposit, the isotope composition of the diopsodites-6.8 and 7.3‰ δ 18 O, and of the hydrogarnet rodingite-6.6‰ δ 18 O indicates the deep origin of the oxygen inherited from the ultramafites that underwent serpentinization and metasomatosis-diopsidization with a small addition of the crustal component. The nephrites, apparently formed as a result of the further metasomatism of the diopsidites, have a heavier isotope composition-8.2-9.7 δ 18 O. This indicates that the crustal fluid contribution to the metasomatism is increasing. The isotope composition of the jadeite is close to that of the nephrite-8.8% δ 18 O, since when nephrite is replaced with jadeite, it does not indicate absorption, but disposal of the fluid.
An important indicator of the nephrite formation processes is the isotopic composition of oxygen. At the Fengtien deposit in Taiwan, for the ordinary nephrite the δ 18 O is 4.5%-5.3%, for the wax-like nephrite it is 4.7%-5.0%, and for the nephrite with the "cat's eye" effect it is 5.1%-5.3%. For the diopside from diopsidite it is 3.7%-4.5%. It is concluded that nephrite inherits its composition from serpentinites and diopsidites [13]. The oxygen isotopic composition has been identified for a number of deposits of S-type nephrite in Russia: Param in Northern Transbaikalia, δ 18 O-6.13%-9.54‰; Ospa in the Eastern Sayans-8.43; and Khamarkhudia in the Khamar-Daban-6.72-7.87. It is believed that the fluid phase of the nephrites indicates their transformation from serpentinites during metamorphism [59]. At the Jordanov deposit in Poland the δ 18 O is 6.1%, and for the shale nephrite it is 6.7 [26]. The isotopic composition of oxygen for the S-type nephrite in the Chinese province of Qinghai is (δ 18  It is shown that ore-forming fluids are formed as a result of metamorphism [60]. Single analyses were performed for the S-type nephrite from the Chara Dzhelgra River (false name?) in Siberia (δ 18 O-6.9), Red Mountain in New Zealand (7.5), Mount Ogden, Canada (9.6), and the Shulaps Range, Canada (8.4). These values are explained by the inheritance of the isotopic composition of the initial serpentinite with the possible influence of the contact with the metagabbro or crystalline shales [61].
Metamorphism reinforced the metasomatic processes in the serpentinite melange, with the formation of a cryptocrystalline tangled-fibrous structure of the nephrite, but then led to its fragmentation and replacement with omphacite. There are eight stages of the deformation process for the region [62], during which the regressive and progressive regimes were able to replace each other.
The results obtained allow the subsurface user to refuse the license or adjust the territory of the subsurface site, and allow the authorities of the Yamal-Nenets Autonomous Okrug to expand the natural park and make it more attractive, due to additional knowledge.

Conclusions
The green nephrite of the Nyrdvomenshor deposit is tremolite in composition. The accessory minerals are diopside, chromite, uvarovite, omphacite, pentlandite, barite, millerite, the unnamed Fe-dominant mineral of the shuiskite group, chlorite. The nephrite isotope composition is 8.2-9.7‰ δ 18 O. It is linked to the serpentinite type. The Nyrdvomenshor nephrite value Fe 2 O 3∑ /(MgO + Fe 2 O 3∑ ) varies within the range of 0.19-0.21, and the content of Cr is 400-700 ppm, Ni is 400 ppm, and Co is 21-24 ppm. The content of rare earth elements ranges from 0.460 to 0.948 ppm, and the distribution pattern is flat, with a weak right slope-due to enrichment with light REE, a positive Eu anomaly. The green nephrite of the Nyrdvomenshor deposit was formed by both multistage metasomatic and superimposed metamorphic processes. Initially, diopsidite formed after serpentinite, and then it was replaced by the nephrite. Metamorphism reinforced the metasomatism in the serpentinite melange and provided the cryptocrystalline tangled-fibrous structure of the nephrite. Then, metamorphism and metasomatism resulted in omphacite formation and nephrite cracking, which reduced its quality. As these processes progressed, the contribution of the crustal fluid increased.