High-Temperature Compressive Properties of TiB-Reinforced Ti Alloy via In Situ Synthesis

In this investigation, in situ synthesis of TiB-reinforced Ti-based alloy was carried out by powder metallurgy. The Ti (TiH2)—Al and B powders were ball milled for 40 h to obtain a mixed powder with a nominal composition of Ti-7Al-0.2B (wt. %) and TiH2-7Al-0.2B (wt. %). After milling the mixed powder by using a vacuum hot pressing sintering furnace (1200 ◦C sintering temperature, 30 MPa pressure, 1 h holding pressure), TiB-reinforced Ti-based alloy was prepared in situ. The compression tests were carried out on a WDW-200 universal testing machine at 550 ◦C, 600 ◦C, and 650 ◦C, and at the strain rates of 1 × 10−4 s−1, 3 × 10−4 s−1, and 5 × 10−4 s−1 to investigate the alloy compression and rheological behavior of the prepared alloy. It was observed that Ti-7Al-0.2B and TiH2-7Al-0.2B alloy formed a TiB phase and α-Ti duplex structure after low-energy ball milling and hot pressed sintering. This is because the in situ synthesis of TiB fiber reinforced phase hinders grain boundary migration and grain growth. Therefore, the TiB phase in Ti-7Al-0.2B alloy is fine, evenly distributed and effective in suppressing grain growth. Alloy materials are heat sensitive and strain-rate sensitive alloys, and the peaks of high-temperature compressive stress decrease with the decrease of the strain rate and the increase of the temperature. At the same temperature and rate conditions, the highest peak flow stress of TiH2-7Al-0.2B is slightly higher than that of Ti-7Al-0.2B. In the ball milling and sintering process of TiH2-7Al-0.2B alloy, the decomposition of H from TiH2 cleanses the surface of Ti particles. This leads to the reduction of the possibility of contamination, and also has a good effect in improving the compression performance.


Introduction
Ti-based composites have a range of excellent properties such as high temperature resistance, corrosion resistance, high specific strength, high specific modulus and excellent high temperature creep resistance, oxidation resistance, high thermal stability, and thermal fatigue strength [1], while the common Ti alloys do not possess these unique properties.Owing to these, the Ti-based composite materials have become unique in the field of aerospace and show potential in the development of structural materials [2].
The hot workability of Ti-based composites was determined by the microstructure of Ti matrices and distribution of reinforcements [3].Gorsse et al. [4] found out TiB has better chemical stability, less residual stresses, and higher stiffness, as compared with other reinforcing phases such as Ti 5 Si 3 , CrB, B 4 C, and SiC.Therefore, TiB can be considered as the best reinforcement for Ti matrices.In situ synthesis of Ti-based composites could be carried out by powder metallurgy, where the resulting TiB reinforcements do not have any interfacial reaction with the Ti matrix, and the interface is clean and has a strong binding force [5][6][7][8].This synthesis method has become the trend of research in recent years.The size and morphology of the reinforcing phase in the composites and its distribution in the matrix have a great influence on the properties of the generated composites.Therefore, studies on the formation mechanism of reinforcements and its influence on the properties of composite materials are of great significance for the development of high performance Ti-based composites.
The particle-reinforcing phase in the in situ synthesis of Ti-based composite materials have high strength, high hardness, and other improved characteristics.Compared to the Ti alloy matrix, the strength and elastic modulus of Ti-based composites are significantly improved.However, the existence of the particle-reinforcing phase enhances the Ti-based composites, while also lacerating the continuity of Ti alloy substrate, making it in the process of plastic deformation and showing inhomogeneity.Different from the non-reinforced Ti alloy substrate, the plastic deformation of reinforced Ti alloy substrate is a gradual process from the local to the whole.The result is that the plasticity of Ti-based composites is not only related to the plasticity of the matrix but also related to the plastic deformation of the matrix and reinforcing phases.Therefore, the strength of Ti-based composites is significantly improved while the elongation declines.In this case, the mechanical properties of Ti-based composite materials, with the same volume content as the reinforcing phase but using different processing method, could be very different [9].
Powder metallurgy is the ideal process for preparing low-cost Ti alloys [10,11].In the preparation of Ti alloy, TiH 2 powder is commonly used instead of Ti powder.This is because the price of TiH 2 powder is lower than that of Ti powder, and TiH 2 powder can generate reversible alloying of H [12].In the sintering process, the decomposition of TiH 2 releases H which cleans the surface of Ti powder particles.So, the possibility of Ti alloy being polluted in the production process is also reduced.In this manner, the performance of the material had been improved [13][14][15][16].
In this study, Ti-7Al alloy (α-Ti alloy) was used as the matrix of the composite material, and an in situ synthesis of TiB-reinforced Ti alloy was carried out using powder metallurgy.The major focus of this study is the preparation of TiB by using TiH 2 powder instead of Ti powder, and comparing the differences between them, as well as studying their high-temperature compression properties.The compressive deformation of the composite material could well characterize the plastic deformation behavior of the material, hence providing valuable and practical insights to the deformation and strengthening mechanisms of the composite.

Materials and Methods
Ti (TiH 2 ) powder, B powder, and Al powder were mixed and formulated into the nominal composition of the alloy with Ti-7Al-0.2B(wt.%) and TiH 2 -7Al-0.2B(wt.%).The supplier of Ti, Al, B, and TiH 2 powders is the General Research Institute for Nonferrous Metals (Beijing, China).The purity of Ti, TiH 2 , and B powders are greater than 99.5%, and the purity of Al powder is 99.9%.The size of Ti powder, B powder, Al powder, and TiH 2 powder are 25 µm, 5 µm, 75 µm, and 75 µm, respectively.
Horizontal planetary ball mill (NJ1-QM-ISP04, Beijing and KTGY Yuanda science and Technology Ltd., Beijing, China) was used for low energy ball milling with a 10:1 ball-to-powder mass ratio and speed of 160 r/min for 40 h.The mixed powder was vacuum hot-pressed sintered by vacuum hot pressing sintering furnace (ZT-40-20-type, Shanghai Chenhua Electric Furnace Limited Company, Shanghai, China)with 1200 • C of sintering temperature, and 30 MPa pressure.Heat preservation and keep pressure were 1 h.After the furnace cooling, the sintered structure is the organization of α-Ti with less than 500 nm and fine TiB phase.The sintered alloy rod was cut into a compressed sample of Φ 6 mm × 9 mm (Chinese Standard GB/T 7314).
Compression tests were performed on a universal testing machine (DDL50, CIMACH, Changchun, China).The deformation temperature was 550 • C, 600 • C, and 650 • C, the strain rate was 1 × 10 −4 s −1 , 3 × 10 −4 s −1 , and 5 × 10 −4 s −1 , and compression deformation was 40%.Because the sample was prone to cracking at 550 • C, the amount of compressive deformation was set to 30% at 550 • C. In order to obtain the organization of high-temperature compression, the sample was cooled by quench after the compression was completed.

Status of the Ball Milling Powders
Figure 1 shows the SEM images of milled powders.Specifically, Figure 1a,c are images of the low energy ball milling of Ti-7Al-0.2Bfor 5 h and 40 h, respectively, whereas Figure 1b,d are the images of low energy ball milling of TiH 2 -7Al-0.2Bfor 5 h and 40 h, respectively.Compared with ball milling for 5 h, Ti-7Al-0.2B,and TiH 2 -7Al-0.2Bpowder obtained after ball milling for 40 h shows a certain degree of refinement, where the size of most of the particles is reduced to 10 µm and 5 µm, respectively.It can be observed that the shape of large particles in Ti-7Al-0.2B is equiaxed, and the corners of powder particles become dull.As the impact of the low energy ball mill is small, the larger powder particles cannot be broken.In contrast, the large powder particles can be broken in the thin and regular edges.This is due to the action of centrifugal force, and the continuous extrusion of the grinding ball and its impact on the powder particles.Hence, the edge of the powder particles is blunted.After milling for 40 h, the particle breakage of the TiH 2 -7Al-0.2Bcomposite powder is more obvious than that of Ti-7Al-0.2B,and the effect of powder refining is better.This is mainly due to the higher brittleness of TiH 2 powder [17], so the refinement effect of TiH 2 -7Al-0.2B is more obvious in the ball milling process.

Status of the Ball Milling Powders
Figure 1 shows the SEM images of milled powders.Specifically, Figure 1a,c are images of the low energy ball milling of Ti-7Al-0.2Bfor 5 h and 40 h, respectively, whereas Figure 1b,d are the images of low energy ball milling of TiH2-7Al-0.2B for 5 h and 40 h, respectively.Compared with ball milling for 5 h, Ti-7Al-0.2B,and TiH2-7Al-0.2Bpowder obtained after ball milling for 40 h shows a certain degree of refinement, where the size of most of the particles is reduced to 10 μm and 5 μm, respectively.It can be observed that the shape of large particles in Ti-7Al-0.2B is equiaxed, and the corners of powder particles become dull.As the impact of the low energy ball mill is small, the larger powder particles cannot be broken.In contrast, the large powder particles can be broken in the thin and regular edges.This is due to the action of centrifugal force, and the continuous extrusion of the grinding ball and its impact on the powder particles.Hence, the edge of the powder particles is blunted.After milling for 40 h, the particle breakage of the TiH2-7Al-0.2Bcomposite powder is more obvious than that of Ti-7Al-0.2B,and the effect of powder refining is better.This is mainly due to the higher brittleness of TiH2 powder [17], so the refinement effect of TiH2-7Al-0.2B is more obvious in the ball milling process.In order to investigate the phase change of the powder after ball milling for 40 h, the powder was analyzed by XRD and the obtained results are shown in Figure 2. In TiH2-7Al-0.2B powder, after low energy ball milling, TiH2 takes a small amount of H to form TiH1.971, and the XRD patterns of TiH2-7Al-0.2B show the diffraction peaks of TiH1.971 and elemental Al.The diffraction peak of B is not observed, because the amount of added B is small and the atomic weight is low.The diffraction peak of elemental Al still exists in the low-energy ball milling process.Al does not form a significant solid In order to investigate the phase change of the powder after ball milling for 40 h, the powder was analyzed by XRD and the obtained results are shown in Figure 2. In TiH 2 -7Al-0.2Bpowder, after low energy ball milling, TiH 2 takes a small amount of H to form TiH 1.971 , and the XRD patterns of TiH 2 -7Al-0.2Bshow the diffraction peaks of TiH 1.971 and elemental Al.The diffraction peak of B is not observed, because the amount of added B is small and the atomic weight is low.The diffraction peak of elemental Al still exists in the low-energy ball milling process.Al does not form a significant solid solution into the Ti lattice, and also does not react with Ti to form any intermetallic such as TiAl or Ti 3 Al.B probably reacts with Ti to form borides during ball milling, but the amount of boride is small, so the XRD is not detected.Similarly, in the case of Ti-7Al-0.2B,only the diffraction peaks of Ti and Al can be detected and no solid solution phenomenon or phase change is observed.solution into the Ti lattice, and also does not react with Ti to form any intermetallic such as TiAl or Ti3Al.B probably reacts with Ti to form borides during ball milling, but the amount of boride is small, so the XRD is not detected.Similarly, in the case of Ti-7Al-0.2B,only the diffraction peaks of Ti and Al can be detected and no solid solution phenomenon or phase change is observed.

Differential Thermal Analysis
In order to analyze the phase characteristics of the milled powder, two milled powders were subjected to differential scanning calorimetry (DSC, STA 409 PC/PG, NETZSCH, Bavaria, Germany).Figure 3 shows the obtained DSC curves for Ti-7Al-0.2B.An obvious exothermic peak appears at around 660 °C for the ball milling and non-ball milling, which may be due to the phase transition that occurred between Ti and B powders to generate the TiB phase.It can be observed that no endothermic peak appears on the curve.In other words, there is no endothermic phenomenon of Al melting.As the melting point of Al is about 660 °C, it implies that there is no Al existing after the phase change occurred between Ti and B. The phase change temperature of the ball milling powder is slightly lower than that of the non-ball milling powder, and it shows that the reaction between Ti and B more easily occurred after ball milling.The TiH2-7Al-0.2B test curve is shown in Figure 4.In the temperature range of 450~550 °C, the endothermic peak appears, and TiH2 is completely decomposed into Ti and H, while a part of the Ti and B phase transformation reaction occurs at about 660 °C to form TiB. According to the DSC analysis, the TiH2-7Al-0.2Balloy powder dehydrogenation, after ball milling and hot press sintering, caused the reaction to occur between Ti and B to generate TiB phase.The phase composition in the final sintered organization is the same as that of the Ti-7Al-0.2Balloy.

Differential Thermal Analysis
In order to analyze the phase characteristics of the milled powder, two milled powders were subjected to differential scanning calorimetry (DSC, STA 409 PC/PG, NETZSCH, Bavaria, Germany).Figure 3 shows the obtained DSC curves for Ti-7Al-0.2B.An obvious exothermic peak appears at around 660 • C for the ball milling and non-ball milling, which may be due to the phase transition that occurred between Ti and B powders to generate the TiB phase.It can be observed that no endothermic peak appears on the curve.In other words, there is no endothermic phenomenon of Al melting.As the melting point of Al is about 660 • C, it implies that there is no Al existing after the phase change occurred between Ti and B. The phase change temperature of the ball milling powder is slightly lower than that of the non-ball milling powder, and it shows that the reaction between Ti and B more easily occurred after ball milling.The TiH 2 -7Al-0.2Btest curve is shown in Figure 4.In the temperature range of 450~550 • C, the endothermic peak appears, and TiH 2 is completely decomposed into Ti and H, while a part of the Ti and B phase transformation reaction occurs at about 660 • C to form TiB. According to the DSC analysis, the TiH 2 -7Al-0.2Balloy powder dehydrogenation, after ball milling and hot press sintering, caused the reaction to occur between Ti and B to generate TiB phase.The phase composition in the final sintered organization is the same as that of the Ti-7Al-0.2Balloy.

Differential Thermal Analysis
In order to analyze the phase characteristics of the milled powder, two milled powders were subjected to differential scanning calorimetry (DSC, STA 409 PC/PG, NETZSCH, Bavaria, Germany).Figure 3 shows the obtained DSC curves for Ti-7Al-0.2B.An obvious exothermic peak appears at around 660 °C for the ball milling and non-ball milling, which may be due to the phase transition that occurred between Ti and B powders to generate the TiB phase.It can be observed that no endothermic peak appears on the curve.In other words, there is no endothermic phenomenon of Al melting.As the melting point of Al is about 660 °C, it implies that there is no Al existing after the phase change occurred between Ti and B. The phase change temperature of the ball milling powder is slightly lower than that of the non-ball milling powder, and it shows that the reaction between Ti and B more easily occurred after ball milling.The TiH2-7Al-0.2B test curve is shown in Figure 4.In the temperature range of 450~550 °C, the endothermic peak appears, and TiH2 is completely decomposed into Ti and H, while a part of the Ti and B phase transformation reaction occurs at about 660 °C to form TiB. According to the DSC analysis, the TiH2-7Al-0.2Balloy powder dehydrogenation, after ball milling and hot press sintering, caused the reaction to occur between Ti and B to generate TiB phase.The phase composition in the final sintered organization is the same as that of the Ti-7Al-0.2Balloy.

Microstructure Analysis
Figure 5 shows the XRD pattern of ball milling powders after sintering.As shown in the picture, both Ti-7Al-0.2Band TiH2-7Al-0.2Bform α-Ti and TiB phase after vacuum hot-pressing sintering.It can be verified that the H in TiH2-7Al-0.2B powder has no effect on the final sintering microstructure composition due to the dehydrogenation of the power after sintering.This is in conformity with the phenomena found in the study by Bhosle et al. [16] that the phase transformation of TiH2 powder in a vacuum environment can be divided into two steps TiH2 → TiHX(0.7 < X < 1.1) and TiHX → Ti.   6a, it can be seen that the microstructure of sintered Ti-7Al-0.2Balloy is dense, and the TiB reinforcing phase, composed of fine fibers, are uniformly distributed on the α-Ti matrix.In contrast, in Figure 6b there are many residual pores in the microstructure of TiH2-7Al-0.2B after TiH2 dehydrogenation [18], and the TiB phase of TiH2-7Al-0.2B alloy is wilder and shorter than that of the Ti-7Al-0.2Balloy.The grain size of TiH2-7Al-0.2B alloy is slightly larger than that of Ti-7Al-0.2Balloy, and TiH2-7Al-0.2Balloy has a grain size between 9 and 44 μm, and Ti-7Al-0.2Balloy has a grain size between 6 and 25 μm.This is because the TiB reinforcing phase hinders grain boundary migration and grain growth [19], which makes the TiB phase in Ti-7Al-0.2Balloy finer and more evenly distributed.Figure 6c,d show the energy dispersive spectrometer (EDS) results of Ti-7Al-0.2Band TiH2-7Al-0.2Balloys after sintering.The chemical compositions of Ti-7Al-0.2Band TiH2-7Al-0.2Balloys are Ti, Al, and B, which verify that their chemical compositions are the same.
Figure 7 shows the TEM image of the sintered microstructure of Ti-7Al-0.2Balloy.Because the sintered microstructure of TiH2-7Al-0.2B has some pores, the transmissive samples are easily broken in the process of preparation.TiH2-7Al-0.2B and Ti-7Al-0.2Balloys have the same components and the same microstructure after the hot-press sintering as discussed earlier, so the morphology shown

Microstructure Analysis
Figure 5 shows the XRD pattern of ball milling powders after sintering.As shown in the picture, both Ti-7Al-0.2Band TiH 2 -7Al-0.2Bform α-Ti and TiB phase after vacuum hot-pressing sintering.It can be verified that the H in TiH 2 -7Al-0.2Bpowder has no effect on the final sintering microstructure composition due to the dehydrogenation of the power after sintering.This is in conformity with the phenomena found in the study by Bhosle et al. [16] that the phase transformation of TiH 2 powder in a vacuum environment can be divided into two steps TiH 2 → TiH X (0.7 < X < 1.1) and TiH X → Ti.

Microstructure Analysis
Figure 5 shows the XRD pattern of ball milling powders after sintering.As shown in the picture, both Ti-7Al-0.2Band TiH2-7Al-0.2Bform α-Ti and TiB phase after vacuum hot-pressing sintering.It can be verified that the H in TiH2-7Al-0.2B powder has no effect on the final sintering microstructure composition due to the dehydrogenation of the power after sintering.This is in conformity with the phenomena found in the study by Bhosle et al. [16] that the phase transformation of TiH2 powder in a vacuum environment can be divided into two steps TiH2 → TiHX(0.7 < X < 1.1) and TiHX → Ti. Figure 6a,b show the SEM images of Ti-7Al-0.2Band TiH2-7Al-0.2Balloys after sintering.From Figure 6a, it can be seen that the microstructure of sintered Ti-7Al-0.2Balloy is dense, and the TiB reinforcing phase, composed of fine fibers, are uniformly distributed on the α-Ti matrix.In contrast, in Figure 6b there are many residual pores in the microstructure of TiH2-7Al-0.2B after TiH2 dehydrogenation [18], and the TiB phase of TiH2-7Al-0.2B alloy is wilder and shorter than that of the Ti-7Al-0.2Balloy.The grain size of TiH2-7Al-0.2B alloy is slightly larger than that of Ti-7Al-0.2Balloy, and TiH2-7Al-0.2Balloy has a grain size between 9 and 44 μm, and Ti-7Al-0.2Balloy has a grain size between 6 and 25 μm.This is because the TiB reinforcing phase hinders grain boundary migration and grain growth [19], which makes the TiB phase in Ti-7Al-0.2Balloy finer and more evenly distributed.Figure 6c,d show the energy dispersive spectrometer (EDS) results of Ti-7Al-0.2Band TiH2-7Al-0.2Balloys after sintering.The chemical compositions of Ti-7Al-0.2Band TiH2-7Al-0.2Balloys are Ti, Al, and B, which verify that their chemical compositions are the same.
Figure 7 shows the TEM image of the sintered microstructure of Ti-7Al-0.2Balloy.Because the sintered microstructure of TiH2-7Al-0.2B has some pores, the transmissive samples are easily broken  From Figure 6a, it can be seen that the microstructure of sintered Ti-7Al-0.2Balloy is dense, and the TiB reinforcing phase, composed of fine fibers, are uniformly distributed on the α-Ti matrix.In contrast, in Figure 6b there are many residual pores in the microstructure of TiH 2 -7Al-0.2Bafter TiH 2 dehydrogenation [18], and the TiB phase of TiH 2 -7Al-0.2Balloy is wilder and shorter than that of the Ti-7Al-0.2Balloy.The grain size of TiH 2 -7Al-0.2Balloy is slightly larger than that of Ti-7Al-0.2Balloy, and TiH 2 -7Al-0.2Balloy has a grain size between 9 and 44 µm, and Ti-7Al-0.2Balloy has a grain size between 6 and 25 µm.This is because the TiB reinforcing phase hinders grain boundary migration and grain growth [19], which makes the TiB phase in Ti-7Al-0.2Balloy finer and more evenly distributed.Figure 6c,d show the energy dispersive spectrometer (EDS) results of Ti-7Al-0.2Band TiH 2 -7Al-0.2Balloys after sintering.The chemical compositions of Ti-7Al-0.2Band TiH 2 -7Al-0.2Balloys are Ti, Al, and B, which verify that their chemical compositions are the same.
Figure 7 shows the TEM image of the sintered microstructure of Ti-7Al-0.2Balloy.Because the sintered microstructure of TiH 2 -7Al-0.2Bhas some pores, the transmissive samples are easily broken in the process of preparation.TiH 2 -7Al-0.2Band Ti-7Al-0.2Balloys have the same components and the same microstructure after the hot-press sintering as discussed earlier, so the morphology shown in Figure 7 can reflect the morphology of these two types of ingredients.From Figure 7a,b, it can be observed that the dislocations are gathered around TiB, and the dislocation density is highest at the boundary.This indicates the reinforcing phase of TiB strongly hinders the dislocation movement in the matrix.The hindering effect of the reinforcing phase on the dislocation is reflected on the improvement of the flow stress of the alloy.A large number of dislocations accumulate at the boundary of the reinforcing phase.When the dislocation density increases to a certain extent, dislocation subgrains are formed.These dislocation subgrains can be used as the core of dynamic recrystallization.In addition, in the deformation process, when the TiB particles rotate in the matrix under the compressive stress, the lattice on both sides of the particle produces a certain phase difference under certain conditions, which can also form subgrains.This subcrystal is also a favorable position for the dynamic recrystallization nucleation.Therefore, in the composite alloys, the hindering effect of the reinforcing phase on dislocation, not only improves the flow stress but also provides favorable conditions for the nucleation and development of dynamic recrystallization.Figure 7c shows the TEM of the net structure.An internal stress is introduced between the powder particles in the process of ball milling, and the internal stress is partially released during the vacuum hot press sintering.The remaining parts form the dislocation structures at grain or grain boundaries.Finally, the dislocation net is formed by dislocation climbing and entanglement.
in Figure 7 can reflect the morphology of these two types of ingredients.From Figure 7a,b, it can be observed that the dislocations are gathered around TiB, and the dislocation density is highest at the boundary.This indicates the reinforcing phase of TiB strongly hinders the dislocation movement in the matrix.The hindering effect of the reinforcing phase on the dislocation is reflected on the improvement of the flow stress of the alloy.A large number of dislocations accumulate at the boundary of the reinforcing phase.When the dislocation density increases to a certain extent, dislocation subgrains are formed.These dislocation subgrains can be used as the core of dynamic recrystallization.In addition, in the deformation process, when the TiB particles rotate in the matrix under the compressive stress, the lattice on both sides of the particle produces a certain phase difference under certain conditions, which can also form subgrains.This subcrystal is also a favorable position for the dynamic recrystallization nucleation.Therefore, in the composite alloys, the hindering effect of the reinforcing phase on dislocation, not only improves the flow stress but also provides favorable conditions for the nucleation and development of dynamic recrystallization.Figure 7c shows the TEM of the net structure.An internal stress is introduced between the powder particles in the process of ball milling, and the internal stress is partially released during the vacuum hot press sintering.The remaining parts form the dislocation structures at grain or grain boundaries.Finally, the dislocation net is formed by dislocation climbing and entanglement.HRTEM analysis of the sample is shown in Figure 8.In Figure 8a, the area of the electron diffraction pattern containing TiB is selected.In Figure 8b, the HRTEM morphology analysis of the selected TiB grain boundaries is shown.The width of the grain boundary between Ti and TiB is 3.84 nm, the interplanar distance of TiB is 0.405 nm, and the angle between the two adjacent interfaces is 57°.The bottom left box area in Figure 8b is the stress field caused by the uniform stress concentration.

True Stress-True Strain Curve Analysis
Ti-7Al-0.2B and TiH2-7Al-0.2B were compressed into Φ 6 mm × 9 mm samples at the deformation temperatures of 550 °C, 600 °C, and 650 °C.The strain rates are 1 × 10 −4 s −1 , 3 × 10 −4 s −1 , and 5 × 10 −4 s −1 .The deformability of the composite depends on the temperatures of sintering and deformation [20].An increase in the temperature shows the softening phenomenon of the matrix.In this case, the bearing capacity of the reinforcing phase for load is weakened, and enhancement is also reduced.This can be observed from the compressive yield strength curve, where the slope of the yield strength curve is reduced with the increase in the temperature.
As shown in Figures 9 and 10, the true stress-strain curves of Ti-7Al-0.2Band TiH2-7Al-0.2Bshow a similar trend under the same compression conditions.The true stress of the first phase of the experiment begins to increase slowly with an increase in true strain, indicating that there is a dense compressing process of the sample at the beginning of the experiment.The experimental alloys show sensitivity to deformation temperature and strain rate during high-temperature compression.
When the strain rate is constant, the peak of compressive flow stress decreases with an increase in the deformation temperature.Compressing Ti-7Al-0.2Bat a rate of 1 × 10 −4 s −1 , a maximum stress of 464 MPa is obtained at 550 °C, and a minimum stress of 201 MPa at 650 °C.From compressing TiH2-7Al-0.2B at a rate of 1 × 10 −4 s −1 , a maximum stress of 512 MPa is obtained at 550 °C, and a minimum stress rate of 230 MPa at 650 °C.HRTEM analysis of the sample is shown in Figure 8.In Figure 8a, the area of the electron diffraction pattern containing TiB is selected.In Figure 8b, the HRTEM morphology analysis of the selected TiB grain boundaries is shown.The width of the grain boundary between Ti and TiB is 3.84 nm, the interplanar distance of TiB is 0.405 nm, and the angle between the two adjacent interfaces is 57 • .The bottom left box area in Figure 8b is the stress field caused by the uniform stress concentration.

True Stress-True Strain Curve Analysis
Ti-7Al-0.2B and TiH2-7Al-0.2B were compressed into Φ 6 mm × 9 mm samples at the deformation temperatures of 550 °C, 600 °C, and 650 °C.The strain rates are 1 × 10 −4 s −1 , 3 × 10 −4 s −1 , and 5 × 10 −4 s −1 .The deformability of the composite depends on the temperatures of sintering and deformation [20].An increase in the temperature shows the softening phenomenon of the matrix.In this case, the bearing capacity of the reinforcing phase for load is weakened, and enhancement is also reduced.This can be observed from the compressive yield strength curve, where the slope of the yield strength curve is reduced with the increase in the temperature.
As shown in Figures 9 and 10, the true stress-strain curves of Ti-7Al-0.2Band TiH2-7Al-0.2Bshow a similar trend under the same compression conditions.The true stress of the first phase of the experiment begins to increase slowly with an increase in true strain, indicating that there is a dense compressing process of the sample at the beginning of the experiment.The experimental alloys show sensitivity to deformation temperature and strain rate during high-temperature compression.
When the strain rate is constant, the peak of compressive flow stress decreases with an increase in the deformation temperature.Compressing Ti-7Al-0.2Bat a rate of 1 × 10 −4 s −1 , a maximum stress of 464 MPa is obtained at 550 °C, and a minimum stress of 201 MPa at 650 °C.From compressing TiH2-7Al-0.2B at a rate of 1 × 10 −4 s −1 , a maximum stress of 512 MPa is obtained at 550 °C, and a minimum stress rate of 230 MPa at 650 °C.[20].An increase in the temperature shows the softening phenomenon of the matrix.In this case, the bearing capacity of the reinforcing phase for load is weakened, and enhancement is also reduced.This can be observed from the compressive yield strength curve, where the slope of the yield strength curve is reduced with the increase in the temperature.
As shown in Figures 9 and 10, the true stress-strain curves of Ti-7Al-0.2Band TiH 2 -7Al-0.2Bshow a similar trend under the same compression conditions.The true stress of the first phase of the experiment begins to increase slowly with an increase in true strain, indicating that there is a dense compressing process of the sample at the beginning of the experiment.The experimental alloys show sensitivity to deformation temperature and strain rate during high-temperature compression.When the strain rate is constant, the peak of compressive flow stress decreases with an increase in the deformation temperature.Compressing Ti-7Al-0.2Bat a rate of 1 × 10 −4 s −1 , a maximum stress

Metals 2018, 8 ,
x FOR PEER REVIEW 4 of 10 solution into the Ti lattice, and also does not react with Ti to form any intermetallic such as TiAl or Ti3Al.B probably reacts with Ti to form borides during ball milling, but the amount of boride is small, so the XRD is not detected.Similarly, in the case of Ti-7Al-0.2B,only the diffraction peaks of Ti and Al can be detected and no solid solution phenomenon or phase change is observed.

Figure 5 .
Figure 5. XRD pattern of the sintered alloy.

Figure
Figure6a,b show the SEM images of Ti-7Al-0.2Band TiH2-7Al-0.2Balloys after sintering.From Figure6a, it can be seen that the microstructure of sintered Ti-7Al-0.2Balloy is dense, and the TiB reinforcing phase, composed of fine fibers, are uniformly distributed on the α-Ti matrix.In contrast, in Figure6bthere are many residual pores in the microstructure of TiH2-7Al-0.2B after TiH2 dehydrogenation[18], and the TiB phase of TiH2-7Al-0.2B alloy is wilder and shorter than that of the Ti-7Al-0.2Balloy.The grain size of TiH2-7Al-0.2B alloy is slightly larger than that of Ti-7Al-0.2Balloy, and TiH2-7Al-0.2Balloy has a grain size between 9 and 44 μm, and Ti-7Al-0.2Balloy has a grain size between 6 and 25 μm.This is because the TiB reinforcing phase hinders grain boundary migration and grain growth[19], which makes the TiB phase in Ti-7Al-0.2Balloy finer and more evenly distributed.Figure6c,dshow the energy dispersive spectrometer (EDS) results of Ti-7Al-0.2Band TiH2-7Al-0.2Balloys after sintering.The chemical compositions of Ti-7Al-0.2Band TiH2-7Al-0.2Balloys are Ti, Al, and B, which verify that their chemical compositions are the same.Figure7shows the TEM image of the sintered microstructure of Ti-7Al-0.2Balloy.Because the sintered microstructure of TiH2-7Al-0.2B has some pores, the transmissive samples are easily broken in the process of preparation.TiH2-7Al-0.2B and Ti-7Al-0.2Balloys have the same components and the same microstructure after the hot-press sintering as discussed earlier, so the morphology shown

Figure 5 .
Figure 5. XRD pattern of the sintered alloy.

Figure 5 .
Figure 5. XRD pattern of the sintered alloy.

Figure
Figure 6a,b show the SEM images of Ti-7Al-0.2Band TiH 2 -7Al-0.2Balloys after sintering.From Figure6a, it can be seen that the microstructure of sintered Ti-7Al-0.2Balloy is dense, and the TiB reinforcing phase, composed of fine fibers, are uniformly distributed on the α-Ti matrix.In contrast, in Figure6bthere are many residual pores in the microstructure of TiH 2 -7Al-0.2Bafter TiH 2 dehydrogenation[18], and the TiB phase of TiH 2 -7Al-0.2Balloy is wilder and shorter than that of the Ti-7Al-0.2Balloy.The grain size of TiH 2 -7Al-0.2Balloy is slightly larger than that of Ti-7Al-0.2Balloy, and TiH 2 -7Al-0.2Balloy has a grain size between 9 and 44 µm, and Ti-7Al-0.2Balloy has a grain size between 6 and 25 µm.This is because the TiB reinforcing phase hinders grain boundary migration and grain growth[19], which makes the TiB phase in Ti-7Al-0.2Balloy finer and more evenly distributed.Figure6c,dshow the energy dispersive spectrometer (EDS) results of Ti-7Al-0.2Band TiH 2 -7Al-0.2Balloys after sintering.The chemical compositions of Ti-7Al-0.2Band TiH 2 -7Al-0.2Balloys are Ti, Al, and B, which verify that their chemical compositions are the same.