Naturally Drug-Loaded Chitin: Isolation and Applications

Naturally occurring three-dimensional (3D) biopolymer-based matrices that can be used in different biomedical applications are sustainable alternatives to various artificial 3D materials. For this purpose, chitin-based structures from marine sponges are very promising substitutes. Marine sponges from the order Verongiida (class Demospongiae) are typical examples of demosponges with well-developed chitinous skeletons. In particular, species belonging to the family Ianthellidae possess chitinous, flat, fan-like fibrous skeletons with a unique, microporous 3D architecture that makes them particularly interesting for applications. In this work, we focus our attention on the demosponge Ianthella flabelliformis (Linnaeus, 1759) for simultaneous extraction of both naturally occurring (“ready-to-use”) chitin scaffolds, and biologically active bromotyrosines which are recognized as potential antibiotic, antitumor, and marine antifouling substances. We show that selected bromotyrosines are located within pigmental cells which, however, are localized within chitinous skeletal fibers of I. flabelliformis. A two-step reaction provides two products: treatment with methanol extracts the bromotyrosine compounds bastadin 25 and araplysillin-I N20 sulfamate, and a subsequent treatment with acetic acid and sodium hydroxide exposes the 3D chitinous scaffold. This scaffold is a mesh-like structure, which retains its capillary network, and its use as a potential drug delivery biomaterial was examined for the first time. The results demonstrate that sponge-derived chitin scaffolds, impregnated with decamethoxine, effectively inhibit growth of the human pathogen Staphylococcus aureus in an agar diffusion assay.


Introduction
Development of three-dimensional (3D) scaffolds based on natural biopolymers is a recent trend in materials and biomaterials science. The scientific community now focuses on development of fabrication methods which will allow for precise control of the architecture and pore structures in such scaffolds. Evolutionary optimized 3D constructs of natural origin can be found in marine demosponges (phylum Porifera, class Demospongiae), which are recognized among the first multicellular organisms on our planet. These organisms evolved and survived for more than 600 million years due to their ability to excellently combine the mechanical stability of their voluminous, fiber-based, water-filtering skeletons [1] and their diverse chemical defense strategies [2,3] due to biosynthesis of secondary metabolites with anti-predatory and antibiotic properties [4]. The demosponges can produce both proteinaceous (spongin)-or polysaccharide (chitin)-based and up to 2-m-high skeletons (for an overview, see References [5][6][7][8][9][10]). Representatives of the family Ianthellidae (Hyatt, 1875) possess chitinous, flat, fan-like skeletons with unique 3D architecture [11,12] (Figures 1 and 2A), some of which can reach up to 2 m in diameter [12]. One main advantage of skeletons of the ianthellid sponges with respect to their practical application is that chitinous scaffolds can be easily isolated from them (for details, see Reference [11]). These scaffolds exhibit the characteristic shape, size, and meshwork-like structural motif of demosponges, throughout which mesophyll cells are perfectly distributed ( Figures 1B,C). Recently, 3D chitin scaffolds isolated from the demosponge Ianthella basta (Pallas, 1766) were successfully used in tissue engineering of human mesenchymal stromal cells (hMSC), as well as human dermal MSCs [13]. Additional advantages of these sponges for use in technological [14,15] and biomedical applications [16] is their exceptional ability to regenerate their skeletons in situ, with a growth rate of up to 12 cm/year [12]. Consequently, marine farming of these sponges in coastal areas in Australia and Guam (United States of America) [17] is planned to be developed in the near future.
In this work, we focus our attention on Ianthella flabelliformis (Linnaeus, 1759) (Demospongiae, Verongiida, Ianthellidae) [28], originally designated by Linneaus as Spongia flabelliformis [29] and later transferred to the genus Ianthella (Gray, 1869), for simultaneous extraction of both naturally occurring chitin scaffolds, and biologically active bromotyrosines which are recognized as potential antibiotic, antitumor, and marine antifouling substances. In this species, bromotyrosines are located within specialized, pigmental cells that are tightly associated with skeletal chitin. Special attention was paid to investigations on the applicability of 3D chitinous spacer fabric-like scaffolds as potential drug delivery biomaterials, filled with a quaternary ammonium compound, decamethoxine [30], which is a well-recognized antiseptic against diverse human diseases [31]. We used a clinical strain of the human pathogen Staphylococcus aureus as the test microorganism in this study. One main advantage of skeletons of the ianthellid sponges with respect to their practical application is that chitinous scaffolds can be easily isolated from them (for details, see Reference [11]). These scaffolds exhibit the characteristic shape, size, and meshwork-like structural motif of demosponges, throughout which mesophyll cells are perfectly distributed ( Figure 1B,C). Recently, 3D chitin scaffolds isolated from the demosponge Ianthella basta (Pallas, 1766) were successfully used in tissue engineering of human mesenchymal stromal cells (hMSC), as well as human dermal MSCs [13]. Additional advantages of these sponges for use in technological [14,15] and biomedical applications [16] is their exceptional ability to regenerate their skeletons in situ, with a growth rate of up to 12 cm/year [12]. Consequently, marine farming of these sponges in coastal areas in Australia and Guam (United States of America) [17] is planned to be developed in the near future.
In this work, we focus our attention on Ianthella flabelliformis (Linnaeus, 1759) (Demospongiae, Verongiida, Ianthellidae) [28], originally designated by Linneaus as Spongia flabelliformis [29] and later transferred to the genus Ianthella (Gray, 1869), for simultaneous extraction of both naturally occurring chitin scaffolds, and biologically active bromotyrosines which are recognized as potential antibiotic, antitumor, and marine antifouling substances. In this species, bromotyrosines are located within specialized, pigmental cells that are tightly associated with skeletal chitin. Special attention was paid to investigations on the applicability of 3D chitinous spacer fabric-like scaffolds as potential drug delivery biomaterials, filled with a quaternary ammonium compound, decamethoxine [30], which is a well-recognized antiseptic against diverse human diseases [31]. We used a clinical strain of the human pathogen Staphylococcus aureus as the test microorganism in this study.

Results
The methodology of how to obtain chitin in the size, shape, and unique architecture of the I. flabelliformis fan-like skeleton is described in Section 4.2. However, one of the most important steps is obtaining a pigmented skeletal structure that is tissue-free (Figure 2A,B). Additional treatment with 5% NaOH at 37 • C over 4 h exposes chitinous fibers with visible inner channels which are typically located within skeletal fibers of verongiid demosponges (see also References [9,11]). These channels permit verongiid chitin to be saturated with diverse liquids due to the capillary effect (for details, see Reference [32]), and the presence of similar channels in our samples suggests that a similar mechanism of capillary uptake might be possible in the skeleton of I. flabelliformis ( Figure 2C).

Results
The methodology of how to obtain chitin in the size, shape, and unique architecture of the I. flabelliformis fan-like skeleton is described in Section 4.2. However, one of the most important steps is obtaining a pigmented skeletal structure that is tissue-free (Figures 2 A,B). Additional treatment with 5% NaOH at 37 °C over 4 h exposes chitinous fibers with visible inner channels which are typically located within skeletal fibers of verongiid demosponges (see also References [9,11]). These channels permit verongiid chitin to be saturated with diverse liquids due to the capillary effect (for details, see Reference [32]), and the presence of similar channels in our samples suggests that a similar mechanism of capillary uptake might be possible in the skeleton of I. flabelliformis ( Figure 2C). Importantly, using this method, isolation of pigmented chitinous fibers ( Figure 3) is possible, in which the presence of reddish-violet cells was visualized using light microscopy ( Figure 3C). These so-called "fiber cells" [33], "pigmental cells" [34][35][36][37], or "spherulous cells" [38,39] are presumable characteristic features for representatives of the Ianthellidae family [37,40]. The size of these cells in I. flabelliformis is 11.8 µm ± 1.15 µm. Importantly, using this method, isolation of pigmented chitinous fibers ( Figure 3) is possible, in which the presence of reddish-violet cells was visualized using light microscopy ( Figure 3C). These so-called "fiber cells" [33], "pigmental cells" [34][35][36][37], or "spherulous cells" [38,39] are presumable characteristic features for representatives of the Ianthellidae family [37,40]. The size of these cells in I. flabelliformis is 11.8 µm ± 1.15 µm.
Single-spot energy-dispersive X-ray spectroscopy (EDX) analysis using SEM strongly confirmed the presence of bromine within individual pigmental cells ( Figure 4). These results correlate well with those reported previously for similar cells observed in the verongiid demosponge Aplysina aerophoba (Nardo, 1833) [39]. Single-spot energy-dispersive X-ray spectroscopy (EDX) analysis using SEM strongly confirmed the presence of bromine within individual pigmental cells ( Figure 4). These results correlate well with those reported previously for similar cells observed in the verongiid demosponge Aplysina aerophoba (Nardo, 1833) [39].    showing the interlayer location of the pigmental cell that lost its oval morphology due to the drying procedure. This cell is definitively of eukaryotic and not bacterial origin.
Due to the evident presence of bromine within pigmented cells of I. flabelliformis, we suggest that bromotyrosines are responsible for this naturally occurring event. Thus, the corresponding methanol extract obtained after treatment of the pigmented skeletal fibers ( Figure 3) was subjected to HPLC for isolation, analysis, and identification of possible bromotyrosine derivatives. Compounds were identified by analyzing the mass spectra and comparing with the data obtained for the same compounds previously isolated from I. flabelliformis sponge [41,42] [42,43].
Further treatment of pigmented chitinous fibers using acetic acid and alkali (see Section 4.2) ( Figure 6) led to the isolation of ready-to-use 3D chitinous scaffolds which visually resemble the wellknown architecture of fabric-based bandage materials ( Figure 7). Due to the evident presence of bromine within pigmented cells of I. flabelliformis, we suggest that bromotyrosines are responsible for this naturally occurring event. Thus, the corresponding methanol extract obtained after treatment of the pigmented skeletal fibers ( Figure 3) was subjected to HPLC for isolation, analysis, and identification of possible bromotyrosine derivatives. Compounds were identified by analyzing the mass spectra and comparing with the data obtained for the same compounds previously isolated from I. flabelliformis sponge [41,42] [42,43].
Further treatment of pigmented chitinous fibers using acetic acid and alkali (see Section 4.2) ( Figure 6) led to the isolation of ready-to-use 3D chitinous scaffolds which visually resemble the well-known architecture of fabric-based bandage materials (Figure 7).  As reported by us previously [13], similar tubular, flat, 3D scaffolds isolated from the marine demosponge Ianthella basta closely related to I. flabelliformis [11] were applied in the tissue engineering of hMSCs. However, in this study, we decided to examine the possibility of such constructs as drug delivery matrices for the future development of alternatives to well-recognized antimicrobial textiles (for an overview, see References [44][45][46][47]).  As reported by us previously [13], similar tubular, flat, 3D scaffolds isolated from the marine demosponge Ianthella basta closely related to I. flabelliformis [11] were applied in the tissue engineering of hMSCs. However, in this study, we decided to examine the possibility of such constructs as drug delivery matrices for the future development of alternatives to well-recognized antimicrobial textiles (for an overview, see References [44][45][46][47]). As reported by us previously [13], similar tubular, flat, 3D scaffolds isolated from the marine demosponge Ianthella basta closely related to I. flabelliformis [11] were applied in the tissue engineering of hMSCs. However, in this study, we decided to examine the possibility of such constructs as drug delivery matrices for the future development of alternatives to well-recognized antimicrobial textiles (for an overview, see References [44][45][46][47]).
We used here the chemical compound 10- Figure 8A), known also as decamethoxine (molecular formula C 38 H 74 Cl 2 N 2 O 4 ; molecular weight 693.9 g/mol). It is highly soluble both in water and ethanol. Due to the characteristic nanoporous structure of tubular chitin in verongiid sponges [9,11] (Figure 8B), we suggest that this reagent can easily move through membrane-like walls of chitin fiber both via absorption from the solution and via diffusion (after drying and fixation) on and within the chitinous matrix ( Figure 8C). The principal scheme is shown in Figure 8.  Figure 8A), known also as decamethoxine (molecular formula C38H74Cl2N2O4; molecular weight 693.9 g/mol). It is highly soluble both in water and ethanol. Due to the characteristic nanoporous structure of tubular chitin in verongiid sponges [9,11] (Figure 8B), we suggest that this reagent can easily move through membrane-like walls of chitin fiber both via absorption from the solution and via diffusion (after drying and fixation) on and within the chitinous matrix ( Figure 8C). The principal scheme is shown in Figure 8. The 3D chitin scaffold of I. flabelliformis impregnated with a 0.1% water solution of decamethoxine and dried with sterile filter paper inhibited the growth of S. aureus in an agar diffusion assay (6 mm from the edge of the matrix) (Figure 9(3)). The chitin scaffold impregnated with 0.1% ethanol solution of decamethoxine and then dried for ethanol evaporation showed less activity (4mm growth inhibition from the edge of the matrix) (Figure 9(4)). This phenomenon is based, probably, on the difference between water and ethanol with respect to their hydrophilicity. Both samples retained properties to release antiseptic on their second and third use, after moving to a fresh The 3D chitin scaffold of I. flabelliformis impregnated with a 0.1% water solution of decamethoxine and dried with sterile filter paper inhibited the growth of S. aureus in an agar diffusion assay (6 mm from the edge of the matrix) (Figure 9(3)). The chitin scaffold impregnated with 0.1% ethanol solution of decamethoxine and then dried for ethanol evaporation showed less activity (4-mm growth inhibition from the edge of the matrix) (Figure 9(4)). This phenomenon is based, probably, on the difference between water and ethanol with respect to their hydrophilicity. Both samples retained properties to release antiseptic on their second and third use, after moving to a fresh microbe culture. Control samples of chitinous scaffolds used without any treatment, with the exception of sterilization at 121 • C (Figure 9(1),(2)), did not show any antibacterial activity under the same experimental conditions.

Discussion
After the discovery of pigmental cells in the fibrous skeletons of Ianthellids by Flemming in 1872, there were numerous reports discussed by de Laubenfels in 1948 where the possible origin, location, and function of these cells was proposed. Carter, for example, described Ianthella sponge in 1881 as follows: "Sarcode charged with dark purple pigmental cells, especially numerous on the surface and in the horny laminae of the fiber, which appear to be secreted by them." [34]. At the same time, Lendenfeld (1882) [33] stated the following" "The most characteristic whereby Ianthella is set off is its unique content of fiber cells. These are not scattered through the pith, but are either actually embedded in the fiber walls, or adherent to the inner surface of the hollow cylinder of the fiber which surrounds the pith. These cells must have reached their buried location alive, but how they obtained food and oxygen seems mysterious. Perhaps the pith is quite permeable and acts as supply tube. Another hypothesis is that cells get caught in the forming fiber and die, but leave a pattern of their shape behind, like footprints, or their original substance replaced by bacteria-resistant chemicals." [33]. Indeed, until the discovery of chitin in fibrous skeletons of verongiid demosponges by our group in 2007 [8], as well as in the verongiid species of the genus Ianthella [11], the most accepted opinion was that skeletal fibers are made of a "horny", proteinaceous, biomaterial called spongin [6]. It is also well known that pigment oxidation is responsible for the rapid Ianthella sponge tissue changes in color (mostly from yellow to purple, or even blackish purple) [33,35,48]. Preserved specimens usually remain in the dark violet condition (Figures 1, 3, and 4A).

Discussion
After the discovery of pigmental cells in the fibrous skeletons of Ianthellids by Flemming in 1872, there were numerous reports discussed by de Laubenfels in 1948 where the possible origin, location, and function of these cells was proposed. Carter, for example, described Ianthella sponge in 1881 as follows: "Sarcode charged with dark purple pigmental cells, especially numerous on the surface and in the horny laminae of the fiber, which appear to be secreted by them." [34]. At the same time, Lendenfeld (1882) [33] stated the following" "The most characteristic whereby Ianthella is set off is its unique content of fiber cells. These are not scattered through the pith, but are either actually embedded in the fiber walls, or adherent to the inner surface of the hollow cylinder of the fiber which surrounds the pith. These cells must have reached their buried location alive, but how they obtained food and oxygen seems mysterious. Perhaps the pith is quite permeable and acts as supply tube. Another hypothesis is that cells get caught in the forming fiber and die, but leave a pattern of their shape behind, like footprints, or their original substance replaced by bacteria-resistant chemicals." [33]. Indeed, until the discovery of chitin in fibrous skeletons of verongiid demosponges by our group in 2007 [8], as well as in the verongiid species of the genus Ianthella [11], the most accepted opinion was that skeletal fibers are made of a "horny", proteinaceous, biomaterial called spongin [6]. It is also well known that pigment oxidation is responsible for the rapid Ianthella sponge tissue changes in color (mostly from yellow to purple, or even blackish purple) [33,35,48]. Preserved specimens usually remain in the dark violet condition (Figures 1, 3 and 4A).
In this study, we showed that the pigmental cells of I. flabelliformis are located within skeletal fibers between microlayers of chitin ( Figure 5) and contain bromotyrosines. Previously, the biosynthesis of several bromotyrosine-related compounds, i.e., bastadins, by I. flabelliformis demosponge was reported [41]. Compounds such as bastadin 25, 15-O-sulfonatobastadin 11, and bastadin 26 were identified in I. flabelliformis; however, their origin was heretofore elusive, with their production in special cells discovered here. Interestingly, there are still no reports of bastadin or araplysillin as typical bromotyrosines of Ianthella species being microbially derived [48]. The intriguing question about the possible ancient microbial origin of the pigmental cells remains open.
The biological function of bromotyrosine-producing cells could be based on previously reported results [49] concerning the inhibition of microbial chitinases using bromotyrosines. In this case, verongiids developed a unique chemical defense strategy to protect their skeletal fibrous chitin from bacterial and fungal invasion. Taking into account our discovery of exceptionally preserved chitin in 505-million-years-old fossil remains of the vernogiid sponge Vauxia gracilenta [1], we believe that the appearance of this strategy was crucial in the evolution of the sponges belonging to the order Verongiida. Previously, we also showed that partially depigmented chitinous skeletons of selected verongiids are still resistant to diverse bacterial chitinases under experimental conditions in vitro [11]. Only completely purified sponge chitin becomes soluble in chitinase-containing solutions [50,51].
In the near future, we plan to use such a "naturally loaded" bromotyrosine chitin ( Figure 3C) to study the possible diffusion of corresponding bromotyrosines using model systems with sea water, physiological solutions, and artificial body fluid.
To our best knowledge, there are no reports on the application of pure chitinous scaffolds for drug delivery. Most papers are dedicated to chitosan or ionically cross-linked chitin microspheres [52]. In one case, a chitin-amphipathic anion/quaternary ammonium salt dressing was prepared [53]. In our study, however, we utilized a recognized antibacterial compound-decamethoxine.
Decamethoxine (its structural formula is shown in Figure 8A) is a cationic gemini surfactant [54], which exhibits strong bactericidal and fungicidal effects. It modifies the permeability of the microbial cell membrane, resulting in the destruction and death of diverse microorganisms [55]. For example, it has a wide spectrum of antimicrobial action on Gram-positive bacteria (Staphylococcus, Streptococcus, Pneumococcus), Gram-negative bacteria (Pseudomonoas, Neisseria gonorrhoeae, Chlamydia trachomatis) [56], protozoa, dermatophyte, yeast-like fungi of Candida genus, and viruses [57]. It was also proven that decamethoxine at a concentration of 10 µg/ml drastically reduces the adhesion of coryneform bacteria, Salmonella, Staphylococcus, and Escherichia [56]. Its method of action may be achieved via adhesion or competitive binding to bacterial adhesins, or to the surface receptors of host cells. Due to its high bacteriostatic effect, decamethoxine is used for the disinfection of surfaces of diverse surgical tools [58], as well as of contact lenses [59].
Our first results (Figure 9) confirmed that decamethoxine can be successfully absorbed from corresponding water and ethanol-containing solutions by chitinous scaffolds isolated from I. flabelliformis. Furthermore, this compound can subsequently diffuse from the chitinous matrix surface, as well as, probably, from the inner space of microtubular and nanoporous structures. The appearance of death zones around colonies of S. aureus during 24 h of incubation confirms the antibiotic activity of decamethoxine through diffusion from the chitinous scaffold. Now, we need a longer assay including studies on a Fickian diffusion, as well as on possible non-Fickian behavior [60,61], of this previously non-investigated microtubular chitin matrix. On this first stage, we did not differentiate between the release of substance adsorbed to the outside of the matrix, substance absorbed via nanopores, substance sucked up and released via capillary action, etc. Consequently, it is also not clear with what kind of diffusion-controlled system (matrix-type system or reservoir-type system) [62] is used here. Understanding the structure-function relationship of the sponge biomaterial system represented in this study as a new antimicrobial drug release scaffold [63] could be the key to the successful application of this special delivery system. The drug release kinetics [64] with respect to decamethoxine and other antimicrobial compounds which can be used in naturally pre-structured sponge chitin will be studied in detail in the near future.

Location and Collection
The sponge Ianthella flabelliformis (WAM Z87073) was collected by J. Fromont

Isolation of Chitinous Skeleton from the Sponge and Identification of Selected Bromotyrosines
The isolation of chitinous scaffolds from the ianthellid sponges was conducted as described by us previously [11]. In brief, it was performed in three main steps: (i) sponge skeletons were washed three times with distilled water for the removal of water-soluble compounds, and then bromotyrosines were extracted with methanol; (ii) residual fragments were treated with NaOH (2.5 M, Merck) at 37 • C for 72 h for deproteinization; (iii) lastly, the isolated scaffolds were treated with acetic acid (20%, Roth) at 37 • C for a period of 6 h to remove residual calcium and magnesium carbonates, and then washed in distilled water up to pH 6.8. This isolation procedure was repeated three times to obtain colorless tubular scaffolds. The purity of isolated chitinous scaffolds was proven using standard analytical procedures as described previously [11].
The methanolic extracts of sponge fragments shown in Figure 3C were analyzed using a Shimadzu HPLC system, coupled to an ultraviolet-visible light (UV-Vis) detector (Shimadzu, Kyoto, Japan; Waters SunFire Prep OBD C18 column (30 × 75 mm)). Routine detection was at 215 and 241 nm. A solvent system consisting of MeCN (A) and H 2 O (B) at a gradient increasing linearly from 0% to 100% was used for compound separation. LCMS analyses were carried out on an Agilent 1100 (Agilent, Santa Clara, California, USA) LC system equipped with a G1956 MSD detector. A Zorbax C18 RR column was used, and gradient elution with 0.1% HCOOH in H 2 O-MeCN was applied.

Antimicrobial Activity of Chitin Matrix
The prepared chitin scaffold of I. flabelliformis was cut into 1-cm 2 squares, washed twice for 15 min in sterile distilled water, and put into 0.1% (w/v) water or ethanol solution of decamethoxine (Yuria-pharm, Kyiv, Ukraine). Samples used for control were put into sterile distilled water or 70% ethanol. After 2 h of incubation, the samples were dried with sterile filter paper (for the water solution) or in a thermostat (for ethanol-based solutions). Dry samples were placed on a Petri dish with fresh culture of a clinical strain of Staphylococcus aureus ATCC 6538P (FDA 209P) on meat-peptone agar (MPA) and cultivated for 24 h at 37 • C. In 24 h, the zones of growth inhibition for first use were measured, and samples were moved with sterile forceps to a Petri dish with a fresh daily culture of S. aureus. Cultivation and measuring were repeated three times with the same samples of chitin scaffold and fresh cultures (first use, second use, and third use). All tests were provided with proper control (sterility control of nutritive environment (MPA), and control of microorganism growth without compound).

Stereomicroscopy and Light Microscopy Imaging
I. flabelliformis sponge samples in different stages of chemical treatment and isolated chitinous scaffolds were observed with a Keyence VHX-6000 (Keyence, Osaka, Japan) digital optical stereomicroscope, and using a BZ-9000 microscope (Keyence, Osaka, Japan) in the light microscopy mode (Machalowski et al., 2019).

Transmission Electron Microscopy (TEM), Scanning Electron Microscopy (SEM), and EDX
For TEM investigations, samples of I. flabelliformis chitin as represented in Figure 3C were fixed with 2.5% glutaraldehyde in phosphate-buffered saline (PBS) at room temperature, post-fixed with 1.5% osmium tetroxide, dehydrated in a graduated series of acetone (including a staining step with 1% uranylacetate), and embedded in Epoxy resin according to Spurr (1969) [66]. Ultra-thin sections (about 70 nm) of samples were prepared on a Leica EM UC6 ultramicrotome (Leica, Wetzlar, Germany) equipped with a Diatome diamond knife, mounted on Pioloform-coated copper grids, post-stained with uranylacetate and lead citrate (according to Reynolds, 1963 [67]), and analyzed using a Zeiss CTEM 902 (Carl Zeiss, Wetzlar, Germany) at 80 kV (University of Bayreuth).
For SEM analysis, samples were prepared as described for TEM analyses without osmium tetroxide and uranylacetate. For elemental analyses (EDX), the block faces of samples were cut on a Leica EM UC6 ultramicrotome equipped with a Diatome diamond knife, carbon-coated, mounted on an SEM sample holder, and analyzed on a Philips ESEM XL 30 (FEI Company, Peabody, MA, USA) at suitable accelerating voltages. For EDX spectra, accelerating voltages between 15 kV and 30 kV were used.

Conclusions
The demand of biomaterials of natural origin is increasing for different reasons, including the major sustainability in their production pipeline leading to the reduction of environmental impact of microplastics and of CO 2 emissions. In this context, the chitin-based materials of marine origin are considered of recent interest, and the results of this work clearly underline that sponges of the order Verongiida can now be considered as a relevant resource in this perspective. The methodology here developed for the first time on I. flabelliformis allows a double exploitation of this sponge species: (i) as a source of bromotyrosines of well-known pharmaceutical properties, and (ii) as a source of unique biomaterial that could potentially substitute artificial fabric-based bandages, for its peculiar structural organization and for its capacity to be filled with anti-bacterial compounds. The purified 3D chitin matrix isolated from I. flabelliformis does not have innate antibacterial activity, but is prospective as a naturally prefabricated dressing material due to its ability for incorporation of antiseptic solutions using the capillary effect or the fixing of dry antiseptic on the surface of its nanoporous, membrane-like chitin microtubes. Consequently, the very promising results here shown are prodromal for further development both in the field of mariculture and of sponge cell biology. The production of chitin-based scaffolds will be in fact realistically sustainable only after a careful analysis of the farming potentialities of this sponge species. Its widespread presence in the Indo-Pacific does not exclude "a priori" the possibility to develop sponge farming facilities in many geographical areas, and the concrete feasibility of this approach is the consequential evolution of this study. The bromotyrosines produced by I. flabelliformis are also well-known interesting compounds. On this specific topic, the interest will be to improve their production not only via simple extraction from farmed sponges but also by developing specific bioreactors for culturing the bromotyrosine-producing cells isolated from the sponge chitinous structures (Figure 10).  Figure 3C were fixed with 2.5% glutaraldehyde in phosphate-buffered saline (PBS) at room temperature, post-fixed with 1.5% osmium tetroxide, dehydrated in a graduated series of acetone (including a staining step with 1% uranylacetate), and embedded in Epoxy resin according to Spurr (1969) [66]. Ultra-thin sections (about 70 nm) of samples were prepared on a Leica EM UC6 ultramicrotome (Leica, Wetzlar, Germany) equipped with a Diatome diamond knife, mounted on Pioloform-coated copper grids, post-stained with uranylacetate and lead citrate (according to Reynolds, 1963 [67]), and analyzed using a Zeiss CTEM 902 (Carl Zeiss, Wetzlar, Germany) at 80 kV (University of Bayreuth).
For SEM analysis, samples were prepared as described for TEM analyses without osmium tetroxide and uranylacetate. For elemental analyses (EDX), the block faces of samples were cut on a Leica EM UC6 ultramicrotome equipped with a Diatome diamond knife, carbon-coated, mounted on an SEM sample holder, and analyzed on a Philips ESEM XL 30 (FEI Company, Peabody, MA, USA ) at suitable accelerating voltages. For EDX spectra, accelerating voltages between 15 kV and 30 kV were used.

Conclusions
The demand of biomaterials of natural origin is increasing for different reasons, including the major sustainability in their production pipeline leading to the reduction of environmental impact of microplastics and of CO2 emissions. In this context, the chitin-based materials of marine origin are considered of recent interest, and the results of this work clearly underline that sponges of the order Verongiida can now be considered as a relevant resource in this perspective. The methodology here developed for the first time on I. flabelliformis allows a double exploitation of this sponge species: (i) as a source of bromotyrosines of well-known pharmaceutical properties, and (ii) as a source of unique biomaterial that could potentially substitute artificial fabric-based bandages, for its peculiar structural organization and for its capacity to be filled with anti-bacterial compounds. The purified 3D chitin matrix isolated from I. flabelliformis does not have innate antibacterial activity, but is prospective as a naturally prefabricated dressing material due to its ability for incorporation of antiseptic solutions using the capillary effect or the fixing of dry antiseptic on the surface of its nanoporous, membrane-like chitin microtubes. Consequently, the very promising results here shown are prodromal for further development both in the field of mariculture and of sponge cell biology. The production of chitin-based scaffolds will be in fact realistically sustainable only after a careful analysis of the farming potentialities of this sponge species. Its widespread presence in the Indo-Pacific does not exclude "a priori" the possibility to develop sponge farming facilities in many geographical areas, and the concrete feasibility of this approach is the consequential evolution of this study. The bromotyrosines produced by I. flabelliformis are also well-known interesting compounds. On this specific topic, the interest will be to improve their production not only via simple extraction from farmed sponges but also by developing specific bioreactors for culturing the bromotyrosineproducing cells isolated from the sponge chitinous structures ( Figure 10). Figure 10. Schematic overview of the challenging tasks: in the near future, we must elaborate an effective method for the isolation of pigmental, bromotyrosine-producing cells from chitinous skeletal Figure 10. Schematic overview of the challenging tasks: in the near future, we must elaborate an effective method for the isolation of pigmental, bromotyrosine-producing cells from chitinous skeletal fibers of ianthellids with the aim of obtaining cell cultures which should be able to synthetize corresponding bromotyrosines using bioreactors.