Study on the Performance and Mechanism of Cement Solidified Desulfurization Manganese Residue

Desulfurized manganese residue (DMR) is an industrial solid residue produced by high-temperature and high-pressure desulfurization calcination of electrolytic manganese residue (EMR). DMR not only occupies land resources but also easily causes heavy metal pollution in soil, surface water, and groundwater. Therefore, it is necessary to treat the DMR safely and effectively so that it can be used as a resource. In this paper, Ordinary Portland cement (P.O 42.5) was used as a curing agent to treat DMR harmlessly. The effects of cement content and DMR particle size on flexural strength, compressive strength, and leaching toxicity of a cement-DMR solidified body were studied. The phase composition and microscopic morphology of the solidified body were analyzed by XRD, SEM, and EDS, and the mechanism of cement-DMR solidification was discussed. The results show that the flexural strength and compressive strength of a cement-DMR solidified body can be significantly improved by increasing the cement content to 80 mesh particle size. When the cement content is 30%, the DMR particle size has a great influence on the strength of the solidified body. When the DMR particle size is 4 mesh, the DMR particles will form stress concentration points in the solidified body and reduce its strength. In the DMR leaching solution, the leaching concentration of Mn is 2.8 mg/L, and the solidification rate of Mn in the cement-DMR solidified body with 10% cement content can reach 99.8%. The results of XRD, SEM, and EDS showed that quartz (SiO2) and gypsum dihydrate (CaSO4·2H2O) were the main phases in the raw slag. Quartz and gypsum dihydrate could form ettringite (AFt) in the alkaline environment provided by cement. Mn was finally solidified by MnO2, and Mn could be solidified in C-S-H gel by isomorphic replacement.


Introduction
Manganese is an important industrial metal used as an additive in the production of various steels, alloys, electronic components, and special chemicals [1]. More than 98% of the world's electrolytic manganese metal is produced in China [2]. According to statistics, 8~12 tons of EMR will be produced for every ton of manganese metal produced [3][4][5][6][7][8][9], and the accumulated stock of EMR in China has reached hundreds of millions of tons. At present, most electrolytic manganese enterprises transport EMR to the storage yard for wet storage, which occupies a lot of land resources, and at the same time, there are serious environmental pollution and safety risks [10]. Under the action of leaching and rainwater leaching, manganese and ammonia nitrogen in surface water will exceed the standard, which will cause great harm to the environment. Besides, EMR also contains a small amount of Cr, Cu, Ni, Pb, and As. The research shows that the leaching concentrations of manganese and ammonia nitrogen reach 912.34 mg/L and 1030 mg/L, respectively, far exceeding the values specified in the reference standard [11][12][13]. Moreover, heavy metals in EMR will migrate to rivers, lakes, and groundwater during stacking, which will cause research in this paper can provide a reference for the harmless treatment and resource utilization of DMR.

Materials and Instruments
Desulfurized manganese residue (DMR) is taken from a stockyard of Ningxia Tianyuan Manganese Industry Group Co., Ltd., Ningxia, China; cement is taken from Horse Racing Cement Plant (P. O 42.5); sulfuric acid (H2SO4) and nitric acid (HNO3) were purchased from Ningxia Dazheng Chemical Co., Ltd. (Ningxia, China), both of which were analytically pure. The water is distilled water.
An X-ray fluorescence spectrometer (XRF) (Netherlands PANalytical Axios Co., Ltd., Almolo, The Netherlands) was used to analyze the main chemical components of DMR and cement, and the results are shown in Table 1. An X-ray diffractometer (XRD) was used to analyze DMR and the main minerals of cement. The results are shown in Figures 1 and 2.     research in this paper can provide a reference for the harmless treatment and resource utilization of DMR.

Materials and Instruments
Desulfurized manganese residue (DMR) is taken from a stockyard of Ningxia Tianyuan Manganese Industry Group Co., Ltd., Ningxia, China; cement is taken from Horse Racing Cement Plant (P.O 42.5); sulfuric acid (H2SO4) and nitric acid (HNO3) were purchased from Ningxia Dazheng Chemical Co., Ltd. (Ningxia, China), both of which were analytically pure. The water is distilled water.
An X-ray fluorescence spectrometer (XRF) (Netherlands PANalytical Axios Co., Ltd., Almolo, The Netherlands) was used to analyze the main chemical components of DMR and cement, and the results are shown in Table 1. An X-ray diffractometer (XRD) was used to analyze DMR and the main minerals of cement. The results are shown in Figures 1 and 2.    As can be seen from Table 1 and Figure 1, DMR is not a simple mineral but consists of quartz, gypsum, orthorhombic wollastonite, and other minerals. The content of gypsum  4 2− ) is high, and ettringite (Aft) can be formed in an alkaline environment [30]. The hydration reaction of tricalcium silicate and dicalcium silicate in cement components is as shown in Formulas (1) and (2), which can produce xCaO·SiO 2 ·yH 2 O(C-S-H), and the Ca(OH) 2 can provide a good alkaline environment for cement-DMR solidified bodies. In addition, the diffraction peaks of SiO 2 , Ca 6 (SiO 4 )(Si 3 O 10 ), and CaSO 4 ·2H 2 O are sharp, which indicates that they have high crystallinity and large crystalline grains, and the content of silicate compounds in DMR is high, so they belong to industrial waste residues with high silicate content.
As can be seen from Figure 2, the hydration products of cement for 28d are mainly ettringite, calcium hydroxide, hydrated calcium silicate, and a small amount of calcium carbonate. At 39.37 • , the diffraction peak of calcium carbonate is sharp, and then the intensity gradually decreases, which is due to the absorption of carbon dioxide in the air by calcium hydroxide to generate calcium carbonate. With the reaction, the amount of calcium hydroxide gradually decreases, and the amount of calcium carbonate also decreases gradually.

Pretreatment of DMR
The bulk DMR (Figure 3a) was dried at 105 • C for 48 h. After cooling, crushing, grinding, and sieving, five DMR with different particle sizes-80 mesh, 28 mesh, 14 mesh, 8 mesh, and 4 mesh-were obtained, respectively. The treatment effect is shown in Figure 3b-f. As can be seen from Table 1 and Figure 1, DMR is not a simple mineral but consists of quartz, gypsum, orthorhombic wollastonite, and other minerals. The content of gypsum (SO4 2− ) is high, and ettringite (Aft) can be formed in an alkaline environment [30]. The hydration reaction of tricalcium silicate and dicalcium silicate in cement components is as shown in Formulas (1) and (2), which can produce xCaO·SiO2·yH2O(C-S-H), and the Ca(OH)2 can provide a good alkaline environment for cement-DMR solidified bodies. In addition, the diffraction peaks of SiO2, Ca6(SiO4)(Si3O10), and CaSO4·2H2O are sharp, which indicates that they have high crystallinity and large crystalline grains, and the content of silicate compounds in DMR is high, so they belong to industrial waste residues with high silicate content.
As can be seen from Figure 2, the hydration products of cement for 28d are mainly ettringite, calcium hydroxide, hydrated calcium silicate, and a small amount of calcium carbonate. At 39.37°, the diffraction peak of calcium carbonate is sharp, and then the intensity gradually decreases, which is due to the absorption of carbon dioxide in the air by calcium hydroxide to generate calcium carbonate. With the reaction, the amount of calcium hydroxide gradually decreases, and the amount of calcium carbonate also decreases gradually.

Pretreatment of DMR
The bulk DMR (Figure 3a) was dried at 105 °C for 48 h. After cooling, crushing, grinding, and sieving, five DMR with different particle sizes-80 mesh, 28 mesh, 14 mesh, 8 mesh, and 4 mesh-were obtained, respectively. The treatment effect is shown in Figure  3b-f.

Preparation of Cement Solidified DMR Solidified Body
The larger the specific surface area is, the more active sites can be provided for the hydration reaction, and the reaction is more sufficient. Therefore, 80 mesh DMR with a larger specific surface area is selected to study the influence of different cement content

Preparation of Cement Solidified DMR Solidified Body
The larger the specific surface area is, the more active sites can be provided for the hydration reaction, and the reaction is more sufficient. Therefore, 80 mesh DMR with a larger specific surface area is selected to study the influence of different cement content on the cement-DMR solidified body; Fang et al. [31] obtained 80 mesh EMR under 30% cement content, and the strength of the solidified body exceeded 10 MPa to meet the requirements of comprehensive utilization. Therefore, the influence of DMR with different particle sizes on the cement-DMR solidified body was studied under 30% cement content. The specific test scheme is as follows: (1) The influence of different cement content: the ratio of cement to 80 mesh DMR is 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, and the water cement ratio is 0.44; (2) Put the cement and DMR into a mixer and mix them at low speed for 1 min, then add water to the mixture slowly and stir for 3 min, and then inject them into a test mold of 40 mm × 40 mm × 160 mm after mixing evenly. Vibrate the cement mortar on the shaking table for 120 times until it is compact, and smooth it with a scraper after vibrating. After curing at 22 • C and 96% humidity for 24 h, demoulding was carried out, and curing was continued to the specified curing ages of 3d, 7d, 14d, and 28d under the above conditions, and the cement-DMR solidified specimens to be tested were obtained.

Flexural Strength and Compressive Strength
According to GB/T 17671-2021 [32], the flexural strength and compressive strength of cement-DMR solidified body specimens for 3d, 7d, 14d and 28d were tested by an electronic pressure testing machine controlled by a microcomputer (Hangzhou Xin Hi-Tech Co., Ltd., Hangzhou, China). The loading rate of flexural strength is 50 N/s, the loading rate of compressive strength is 2400 N/s, and the average value is taken for each group of three samples.

Characterization of Solidified Body
The main components of the cured body after the hydration reaction were analyzed by an X-ray diffractometer (Germany BRUKER AXS Co., Ltd., Karlsruhe, Germany), and the cured body was milled through a 200 mesh sieve hole for scanning, the scanning range was 5~70 • , and the scanning rate was 2 ( • )/min; Scanning electron microscope-energy dispersive spectroscopy (SEM-EDS, Germany Carl Zeiss Co., Ltd., Oberkochen, Germany) was used to analyze the microscopic morphology and main elements of the cured body.

Leaching Toxicity Test
Leaching toxicity test according to HJ 557-2010 [33]. The leached toxic specimens were cured to the specified age, and after being crushed, they were sampled and dried at 105 • C and passed through a 3 mm sieve. A total of 10 g of sample was weighed and placed in a 250 mL flask, and 100 g of extractant (mixed sulfuric acid and nitric acid) was added. The cap of the flask was tightly sealed and placed in a speed-regulating, multi-purpose oscillator. The flask was shaken at (25 ± 2) • C at a frequency of (110 ± 10 oscillations/min) for 8 h, and then the flask was removed. After standing for 16 h, the concentration of heavy metal elements was measured by triple quadrupole ICP-MS (Japan Agilent Technologies Co., Ltd., Tokyo, Japan), and the ammonia nitrogen content was measured by a UV-VIS spectrophotometer (Shanghai Aoyi Instrument Co., Ltd., Shanghai, China). Figure 4 shows the test results for flexural strength and compressive strength of a cement-DMR solidified body under different cement content and different age conditions with an 80 mesh DMR ratio.

Flexural Strength and Compressive Strength
As can be seen from Figure 4, with the increase in cement content and curing time, the flexural and compressive strengths of the solidified body increase. When the cement content is 10~15%, the flexural strength and compressive strength increase slowly, but when the cement content reaches 15%, the compressive strength increases rapidly. The flexural strength and compressive strength are the highest at each age when the cement content is 50%. The flexural strengths of 3d, 7d, 14d, and 28d are 10.5 MPa, 12.9 MPa, 14.3 MPa, and 15.6 MPa, respectively. which is 17.5, 12.9, 11.9, and 10.4 times that of 3d, 7d, 14d, and 28d, respectively, when the cement content is 10%. The compressive strength is 23.2 MPa, 32.1 MPa, 41.6 MPa, and 49.6 MPa, respectively, which is 12.2, 14.6, 13.4, and 11.8 times of the 3d, 7d, 14d, and 28d strengths when the cement content is 10%. The results show that more hydrated calcium silicate gel (C-S-H) can be formed in the cement-DMR solidified body with higher cement content [34], and more ettringite (AFt) can be formed in the alkaline environment of cement hydration due to a large amount of gypsum dihydrate (CaSO 4 ·2H 2 O) in the DMR solidified body. In addition, DMR is obtained by desulfurization and deamination calcination of EMR at high temperature and pressure. It is mainly a solid calcined slag with low-temperature inert phases such as cristobalite, calcium sulfate, and silicates such as calcium and aluminum as main phases and has high activity [35]. In addition, DMR itself has weak volcanism and promotes the hydration reaction of cement [36]. To sum up, it is precisely because of the enhancement of the hydration reaction, the increase of hydration products, and the formation of more C-S-H and AFt that the flexural strength and compressive strength of the solidified body at each age are significantly improved under 50% cement content.  As can be seen from Figure 4, with the increase in cement content and curing time, the flexural and compressive strengths of the solidified body increase. When the cement content is 10~15%, the flexural strength and compressive strength increase slowly, but when the cement content reaches 15%, the compressive strength increases rapidly. The flexural strength and compressive strength are the highest at each age when the cement content is 50% The flexural strengths of 3d, 7d, 14d, and 28d are 10.5 MPa, 12.9 MPa, 14.3 MPa, and 15.6 MPa, respectively. which is 17.5, 12.9, 11.9, and 10.4 times that of 3d, 7d, 14d, and 28d, respectively, when the cement content is 10%. The compressive strength is 23.2 MPa, 32.1 MPa, 41.6 MPa, and 49.6 MPa, respectively, which is 12.2, 14.6, 13.4, and 11.8 times of the 3d, 7d, 14d, and 28d strengths when the cement content is 10%. The results show that more hydrated calcium silicate gel (C-S-H) can be formed in the cement-DMR solidified body with higher cement content [34], and more ettringite (AFt) can be formed in the alkaline environment of cement hydration due to a large amount of gypsum dihydrate (CaSO4·2H2O) in the DMR solidified body. In addition, DMR is obtained by desulfurization and deamination calcination of EMR at high temperature and pressure. It is mainly a solid calcined slag with low-temperature inert phases such as cristobalite, calcium sulfate, and silicates such as calcium and aluminum as main phases and has high activity [35]. In addition, DMR itself has weak volcanism and promotes the hydration reaction of cement [36]. To sum up, it is precisely because of the enhancement of the hydration reaction, the increase of hydration products, and the formation of more C-S-H and AFt that the flexural strength and compressive strength of the solidified body at each age are significantly improved under 50% cement content. Figure 5 shows the test results for flexural strength and compressive strength of a cement-DMR solidified body with different particle sizes at 30% cement content.  As can be seen from Figure 5, the particle size of DMR has a great influence on the strength of the cured body. The flexural strength and compressive strength of the cured body with DMR particle size of 28 mesh are the highest, and the flexural strength of the cured body with DMR particle size of 80 mesh is increased by 10.9%, 13.6%, 7.5%, and 7.1% for 3d, 7d, 14d, and 28d, respectively. The compressive strength increased by 3.6%, 8.7%, 4.0%, and 6.8%, respectively. The flexural strength and compressive strength of the 80 As can be seen from Figure 5, the particle size of DMR has a great influence on the strength of the cured body. The flexural strength and compressive strength of the cured body with DMR particle size of 28 mesh are the highest, and the flexural strength of the cured body with DMR particle size of 80 mesh is increased by 10.9%, 13.6%, 7.5%, and 7.1% for 3d, 7d, 14d, and 28d, respectively. The compressive strength increased by 3.6%, 8.7%, 4.0%, and 6.8%, respectively. The flexural strength and compressive strength of the 80 mesh DMR solidified body at 28d were 9.8 MPa and 32.2 MPa, respectively, and the flexural strength and compressive strength of the 28 mesh DMR solidified body at 28 mesh size were 10.5 MPa and 34.4 MPa, respectively. It can be seen that with the slight increase of particle size, DMR with slightly larger particles acted as a part of the aggregate in the hardened body, so the strength increased slightly. However, with the increase in particle size, the flexural strength and compressive strength of the DMR solidified body decreased. The flexural strength and compressive strength of the DMR solidified body at 28d with 30% cement content and 4 mesh particle size were 6.3 MPa and 20.1 MPa, respectively, which decreased by 40.0% and 41.6%, respectively, compared with 28 mesh. The analysis shows that when the particle size is large, the DMR in the middle of the agglomerated particles cannot be fully mixed with cement uniformly, forming a failure stress concentration point similar to honeycomb, and the uneven stress distribution during flexural and compressive resistance leads to stress concentration, which reduces the strength of the solidified body. In addition, DMR has certain pozzolanic properties, and the finer the particle size, the more obvious the effect, which can promote the strength of a cement-DMR-solidified body. At the same time, when DMR is ground to a certain extent, its surface area is larger. When the fine DMR powder acts as a physical filling, it can be more effectively dispersed into the pores of the cured body, which improves the pore structure of the cured body, makes its structure denser, and shows greater macroscopic strength.

Toxicity Leaching Test of Cement Solidified Desulfurization Manganese Residue
The content of heavy metals in DMR was determined by triple quadrupole ICP-MS, and the content of ammonia nitrogen was measured by a UV-VIS spectrophotometer. The test results are shown in Table 2. The concentrations of Mn and NH 4 -N in the leaching solution of DMR are 2.8 mg/L and 0 mg/L, respectively, which are 1.4 times and 0 times the Class I emission standard in GB8978-1996 [37]. Only the leaching concentration of Mn slightly exceeds the standard, and other heavy metals such as Pb, Ni, Cu, and Zn are far lower than the requirements of GB8978-1996. Therefore, Mn is the pollutant that needs attention in DMR, and the concentration of Mn in the solidified body is mainly determined. The reason why ammonia nitrogen is not detected is that ammonia nitrogen is decomposed into ammonia and nitrogen at high temperatures and pressures. Ammonia is collected for manufacturing ammonia water, while nitrogen is discharged into the air. It can be seen that ammonia nitrogen in EMR can be effectively removed by high-temperature and high-pressure calcination.          As can be seen from Figures 6 and 7, the content of leaching toxicity decreases with the increase in cement content and increases with the increase in particle size. The concentration of Mn is 5.43 × 10 −3 mg/L and 0.01 × 10 −3 mg/L when the cement content is 10% and 50%, and the solidification rate of Mn by cement is over 99.8%. The concentrations of Mn in 80 mesh and 4 mesh solidified bodies for 28d were 1.32 × 10 −3 mg/L and 4.59 × 10 −3 mg/L, respectively. With the increase in DMR particle size, the curing effect of Mn decreases slightly, but all of them can meet the Class I emission standard in GB8978-1996. There are three main reasons for the low leaching concentration of Mn in cement-DMRsolidified bodies. One is the high alkalinity and strong acid retarding ability of DMR itself; second, the cement hydration reaction provides a better alkaline environment and physical encapsulation; third, the hydration products produced by cement solidification of DMR have a strong acid retarding ability, and a large amount of acid is needed to leach Mn from DMR [36].
To sum up, cement can effectively solidify soluble Mn in DMR, and increasing the content of cement can further remove Mn; DMR particles with larger particle sizes are not as good as DMR particles with smaller particle sizes. The reason for the analysis is that the specific surface area of DMR particles with a larger particle size is smaller. In contrast, DMR particles with a smaller particle size and larger specific surface area can participate in hydration reaction more fully, have a better curing effect, and lower leaching toxicity.
Combined with XRD spectrum analysis of DMR, it can be seen (Figure 1) that the main components of DMR are low temperature cristobalite and gypsum, and the heavy metal Mn may have been wrapped by the combined crystals of quartz, calcium sulfate and other minerals melted at high temperature, and melted with other metal elements to transform into silicate crystals, finally forming stable silicate compounds. The leaching toxicity of DMR obtained by high temperature and high-pressure desulfurization calcination treatment has been significantly reduced, and the Mn in DMR can be further stabilized by cement solidification.

Study on Hydration Products and Micro-Morphology Analysis of Cement Solidified
Desulfurization Manganese Residue Solidified Body 3.3.1. XRD Analysis Figure 8 is the XRD pattern of DMR with 80 mesh particle size solidified body at 28d under different cement content. [36].
To sum up, cement can effectively solidify soluble Mn in DMR, and increasing the content of cement can further remove Mn; DMR particles with larger particle sizes are not as good as DMR particles with smaller particle sizes. The reason for the analysis is that the specific surface area of DMR particles with a larger particle size is smaller. In contrast, DMR particles with a smaller particle size and larger specific surface area can participate in hydration reaction more fully, have a better curing effect, and lower leaching toxicity. Combined with XRD spectrum analysis of DMR, it can be seen (Figure 1) that the main components of DMR are low temperature cristobalite and gypsum, and the heavy metal Mn may have been wrapped by the combined crystals of quartz, calcium sulfate and other minerals melted at high temperature, and melted with other metal elements to transform into silicate crystals, finally forming stable silicate compounds. The leaching toxicity of DMR obtained by high temperature and high-pressure desulfurization calcination treatment has been significantly reduced, and the Mn in DMR can be further stabilized by cement solidification. Figure 8 is the XRD pattern of DMR with 80 mesh particle size solidified body at 28d under different cement content. As can be seen from Figure 8, with the increase in cement content, the intensity of the diffraction peaks of the gypsum dihydrate phase (CaSO4·2H2O) and quartz phase (SiO2) As can be seen from Figure 8, with the increase in cement content, the intensity of the diffraction peaks of the gypsum dihydrate phase (CaSO 4 ·2H 2 O) and quartz phase (SiO 2 ) decreases obviously. Analysis shows that in an alkaline environment, quartz and gypsum dihydrate can be activated to promote the formation of hydration products, and OHleads to the fracture of chemical bonds between Al-O and Si-O. At the same time, DMR provides a high sulfate environment, combining Ca 2+ and SO 4 2− to form Aft [38]. The main reactions are shown in Formulas (3)- (6), and the reactions shown in Formulas (3)-(6) consume OH − , which promotes the forward hydration reaction of Portland cement as shown in Formulas (1) and (2). With the increase in cement content, the alkaline environment of the whole system is stronger, and the content of hydration products C-S-H and Aft increases, which has a positive effect on strength formation.

XRD Analysis
It can be seen from Figure 8 that the diffraction peaks of AFt and C-S-H are at 9.1 • . with the increase of cement content, and the peak is constantly sharp, which explains that it has higher early strength under high cement content. A small amount of soluble Mn in DMR combined with the OH − ion in an alkaline environment, and soluble Mn finally formed stable and insoluble MnO 2 [19].
3.3.2. SEM-EDS Analysis Figure 9 shows the SEM micrographs of the 28d solidified body with an 80 mesh particle size DMR ratio of 10% and 50% cement content.
it has higher early strength under high cement content. A small amount of soluble Mn in DMR combined with the OH − ion in an alkaline environment, and soluble Mn finally formed stable and insoluble MnO2 [19].  Figure 9 shows the SEM micrographs of the 28d solidified body with an 80 mesh particle size DMR ratio of 10% and 50% cement content.  As can be seen from Figure 9, ettringite (Aft) crystal is needle-rod shape, C-S-H gel is fibrous shape [39,40], silicon dioxide crystal (SiO 2 ) is a spherical particle, and gypsum crystal (CaSO 4 ·2H 2 O) is rod shape in the cured body, among which AFt crystal is the main source of strength in the cured body. On the other hand, from Figure 9a,b, it can be seen that under low cement content, the solidified body is mainly rod-like gypsum crystal and spherical silica crystal, with less C-S-H gel, and the solidified body has obvious pores, which explains why the compressive strength of the solidified body at 10% cement content for 28d is low. With the increase in cement content, the C-S-H gel and Ca(OH) 2 content of the hydration reaction increased, which promoted the formation of AFt. As can be seen from Figure 9c,d, the flocculent C-S-H gels are closely aggregated and connected to each other [41], showing needle-bar ettringite crystals, which are closely overlapped to form a dense network structure and jointly improve the mechanical strength [18], which is consistent with the results of flexural strength and compressive strength shown in Section 2.1. Figure 10 is the element analysis of the SEM-EDS spectrum of 28d solidified body under raw slag, 80 mesh particle size DMR mixed with 10% and 50% cement. the hydration reaction increased, which promoted the formation of AFt. As can be seen from Figure 9c,d, the flocculent C-S-H gels are closely aggregated and connected to each other [41], showing needle-bar ettringite crystals, which are closely overlapped to form a dense network structure and jointly improve the mechanical strength [18], which is consistent with the results of flexural strength and compressive strength shown in Section 2.1. Figure 10 is the element analysis of the SEM-EDS spectrum of 28d solidified body under raw slag, 80 mesh particle size DMR mixed with 10% and 50% cement. It can be seen from Figure 10 that the main elements in DMR raw slag are Ca, Si, Fe, Al, K, Mg, and Mn. Combined with SEM, it can be seen that the crystal phase in the raw slag is distinct, and it shows that the main phases at the sample point are SiO2 and CaSO4·2H2O. At the same time, the distribution of Ca and S proves the existence of CaSO4·2H2O. Combined with the SEM images of Figure 10b,c and the distribution of elements, C-S-H gel is formed with Ca, Si, and O as the main elements, and there is metal Mn in the cured C-S-H gel, which is due to the isomorphic transformation during the formation of layered C-S-H gel, and Mn can undergo displacement reactions with Ca, Al, Si, and Fe plasma in its lattice [42], thus immobilizing the lattice into the crystal structure and existing in a more stable form. This also explains that the leaching toxicity of Mn is significantly reduced after DMR is cured by cement. It can be seen from Figure 10 that the main elements in DMR raw slag are Ca, Si, Fe, Al, K, Mg, and Mn. Combined with SEM, it can be seen that the crystal phase in the raw slag is distinct, and it shows that the main phases at the sample point are SiO 2 and CaSO 4 ·2H 2 O. At the same time, the distribution of Ca and S proves the existence of CaSO 4 ·2H 2 O. Combined with the SEM images of Figure 10b,c and the distribution of elements, C-S-H gel is formed with Ca, Si, and O as the main elements, and there is metal Mn in the cured C-S-H gel, which is due to the isomorphic transformation during the formation of layered C-S-H gel, and Mn can undergo displacement reactions with Ca, Al, Si, and Fe plasma in its lattice [42], thus immobilizing the lattice into the crystal structure and existing in a more stable form. This also explains that the leaching toxicity of Mn is significantly reduced after DMR is cured by cement.

Conclusions
In this paper, P.O 42.5 cement was used to solidify DMR. Through the tests of flexural strength, compressive strength, and leaching toxicity, the effects of cement content and DMR particle size on the mechanical strength and leaching toxicity of the cement-DMR-solidified body were analyzed. At the same time, the DMR mechanism of cement solidification was analyzed by means of XRD, SEM, and EDS. The following conclusions are drawn: (1) DMR, prepared by high-temperature and high-pressure desulfurization and deamination calcination, has a solidified body mixed with cement that has good flexural and compressive strength. Under 80 mesh particle size, the increase in cement content can significantly improve the flexural strength and compressive strength of the solidified body at different ages. Under the condition of 30% cement content, DMR with different particle sizes has a great influence on the strength of the solidified body, and the solidified body formed by 30% cement with four mesh particle sizes will form stress concentration points, thus reducing the strength of the solidified body. Institutional Review Board Statement: Not applicable.
Informed Consent Statement: Not applicable.

Data Availability Statement:
The data presented in this study are available on request from the corresponding author.

Conflicts of Interest:
The authors declare no conflict of interest.