Investigation on Physico Chemical and X-ray Shielding Performance of Zinc Doped Nano-WO3 Epoxy Composite for Light Weight Lead Free Aprons

This report addresses a way to reduce the usage of highly toxic lead in diagnostic X-ray shielding by developing a cost-effective, eco-friendly nano-tungsten trioxide (WO3) epoxy composite for low-weight aprons. Zinc (Zn)-doped WO3 nanoparticles of 20 to 400 nm were synthesized by an inexpensive and scalable chemical acid–precipitation method. The prepared nanoparticles were subjected to X-ray diffraction, Raman spectroscopy, UV-visible spectroscopy, photoluminescence, high-resolution–transmission electron microscope, scanning electron microscope, and the results showed that doping plays a critical role in influencing the physico-chemical properties. The prepared nanoparticles were used as shielding material in this study, which were dispersed in a non-water soluble durable epoxy resin polymer matrix and the dispersed materials were coated over a rexine cloth using the drop-casting method. The X-ray shielding performance was evaluated by estimating the linear attenuation coefficient (μ), mass attenuation coefficient (μm), half value layer (HVL), and X-ray percentage of attenuation. Overall, an improvement in X-ray attenuation in the range of 40–100 kVp was observed for the undoped WO3 nanoparticles and Zn-doped WO3 nanoparticles, which was nearly equal to lead oxide-based aprons (reference material). At 40 kVp, the percentage of attenuation of 2% Zn doped WO3 was 97% which was better than that of other prepared aprons. This study proves that 2% Zn doped WO3 epoxy composite yields a better particle size distribution, μm, and lower HVL value and hence it can be a convenient lead free X-ray shielding apron.


Introduction
It is known that numerous clinical personnel are exposed to diagnostic radiation every day [1]. Exposure to radiation at a certain level causes serious issues for human beings. Long-term exposure to radiation above the safety level or without appropriate productive gear may cause serious and fatal effects such as cancer, cell damage, and other undesirable health issues [2]. Lead (Pb) is the traditional material used in aprons which acts as radiation shielding material for clinical operators due to its high atomic density and high X-ray attenuation co-efficient [3]. However, Pb poses a serious threat to human health, especially infants and it is very difficult to recycle and store. The incorporation of lead oxide nanoparticles onto a polymer matrix creates a nanocomposite material that is more robust and requires less maintenance. Consequently, the content of lead used in shielding material would lessen. The polymer matrix acts as a protective layer around

Synthesis of Zn-WO 3 Nanoparticles
WO 3 nanoparticles were prepared through the acid-precipitation method [28]. First, sodium tungstate dihydrate (Na 2 WO 4 ·2H 2 O) was dissolved in 600 mL of double distilled water. In this solution, 0.0, 1.0, 2.0, and 3.0 mol% of zinc chloride (ZnCl 2 ) was added, and hydrochloric acid (HCl) was added dropwise until the pH of the medium turns 1. After adding HCl, the solution was turned yellow in color which indicated the formation of tungstic acid (H 2 WO 4 ). Then it was allowed to age for 24 h at room temperature under normal stirring and subjected to sonication. The precipitate was collected by centrifugation and washed with the help of distilled water to remove sodium chloride (NaCl), which was shown in the chemical reaction (R2). The precipitate was calcinated at 500 • C and H 2 O got evaporated, which was given by the chemical reaction (R2) [29].

Fabrication of Zn-WO 3 Nanocomposite Apron and Measurement Set-Up
The filler (prepared nanoparticles) and epoxy polymers were mixed in a 1:1 ratio weight percentage using a magnetic stirrer and uniformly dispersed. A glass cuboid template with a dimension of 4 cm × 4 cm was placed over a rexine cloth. The nanocomposite was spread using the drop-casting method over the rexine cloth to mimic the fabric of the apron. It was allowed to rest for 12 h at room temperature and the desired study material was acquired. This preparation process for the apron is shown in Figure 1a,b, respectively. sodium tungstate dihydrate (Na2WO4·2H2O) was dissolved in 600 mL of double distilled water. In this solution, 0.0, 1.0, 2.0, and 3.0 mol% of zinc chloride (ZnCl2) was added, and hydrochloric acid (HCl) was added dropwise until the pH of the medium turns 1. After adding HCl, the solution was turned yellow in color which indicated the formation of tungstic acid (H2WO4). Then it was allowed to age for 24 h at room temperature under normal stirring and subjected to sonication. The precipitate was collected by centrifugation and washed with the help of distilled water to remove sodium chloride (NaCl), which was shown in the chemical reaction (R2). The precipitate was calcinated at 500 °C and H2O got evaporated, which was given by the chemical reaction (R2) [29]. Finally, the calcinated product was ground for further characterization and apron fabrication. The 0.0, 1.0, 2.0, and 3.0% Zn doped samples were labeled as WZ0, WZ1, WZ2, and WZ3 respectively hereafter.

Fabrication of Zn-WO3 Nanocomposite Apron and Measurement Set-Up
The filler (prepared nanoparticles) and epoxy polymers were mixed in a 1:1 ratio weight percentage using a magnetic stirrer and uniformly dispersed. A glass cuboid template with a dimension of 4 cm × 4 cm was placed over a rexine cloth. The nanocomposite was spread using the drop-casting method over the rexine cloth to mimic the fabric of the apron. It was allowed to rest for 12 h at room temperature and the desired study material was acquired. This preparation process for the apron is shown in Figure 1a,b, respectively.
A sample size of 4 cm × 4 cm was kept over a sample holder made up of lead with an opening of 3 cm × 3 cm at the center. The sample and detector were located at 50 cm and 100 cm respectively from the X-ray source [30]. A lead box was placed behind the sample enclosing the detector to prevent the scattering of X-rays. The exposure was set at 10 mAs, time was set at 2 s and the X-ray tube voltage was between 40 and 100 kVp. An X-ray beam of 1 cm × 1 cm width from the X-ray source was allowed to pass through the sample. The penetrated radiation was received by the detector and read from the display.  A sample size of 4 cm × 4 cm was kept over a sample holder made up of lead with an opening of 3 cm × 3 cm at the center. The sample and detector were located at 50 cm and 100 cm respectively from the X-ray source [30]. A lead box was placed behind the sample enclosing the detector to prevent the scattering of X-rays. The exposure was set at 10 mAs, time was set at 2 s and the X-ray tube voltage was between 40 and 100 kVp. An X-ray beam of 1 cm × 1 cm width from the X-ray source was allowed to pass through the sample. The penetrated radiation was received by the detector and read from the display.

Characterization
The structural properties were identified using the model Empyrean, Malvern Panalytical Powder X-ray Diffraction (XRD) instrument (Malvern, UK) using the Cu K α source (λ = 0.154 nm). The optical properties of prepared samples were analyzed through UVvisible (UV-Vis) optical spectrometer using the model Jasco V770, 28600 mary's court Easton, MD, USA 21601. The defect and local structural properties were confirmed and analyzed through photoluminescence (PL) and Raman scattering studies using the perkins Elmer LS45 (Ulm, Germany), and WiTec alpha 300 (355 and 532 nm laser) (Ulm, Germany) respectively. The surface morphology, elemental analysis, and elemental mapping were carried out by EVO 18 model's scanning electron microscope (SEM) (Jena, Germany) and energy dispersive X-ray spectroscopy (EDX) (Jena, Germany) studies respectively. The fine structure such as lattice planes, grain size, and selected area diffraction (SAED) was carried out by high-resolution transmission electron microscope (HR-TEM) model JEOL JEM 2100 (Peabody, MA, USA). For X-ray attenuation studies, M/S Wipro Ge Healthcare's fixed radiography model HF (Banglore, India)advantage was used for producing a 40-100 kV X-ray source with an average exposure time of 2 s and the source to image distance (SID) of 100 cm [30,31] detected using the RTI Piranha 557 electrometer (Molndal, Swedan).

XRD Analysis
XRD analysis was performed to investigate the crystalline size, crystal structure and lattice characteristics of Zn-doped WO 3 nanopowders. Table 1 shows the crystalline structure of prepared nanoparticles. Figure 2a shows the X-ray diffraction patterns of pure WO 3 and Zn-doped WO 3 nanopowders annealed at 500 • C. The XRD result shows major intense peaks at 23.  [32]. The prominent peak of WZ0 is located at (200) direction. The direction of the prominent peak changed when the dopant is introduced. Zn prefers to locate in the (120) direction for the samples WZ1 and WZ2. WZ3 peak is located at the (002) direction. For pure WO 3 particles, the lattice parameters have been calculated as a = 0.732 nm, b = 0.750 nm, and c = 0.768 nm from Equation (1) [33], which was also in good agreement with the standard data. Upon doping, the peak positions remain the same with negligible shift but the intensity changes with respect to the dopant concentration since the zero presence of additional peaks belong to elemental or compound impurities, which shows that there is no secondary phase formation or elemental impurity presence in the prepared samples. The crystallite size (D), cell volume (v), dislocation density (δ) and the micro strain (E) are calculated using Equations (1)-(5) [33,34].
where, θ-peak position and λ-X-ray wavelength (Cu kα = 0.1514 nm). The changes in lattice parameters are due to different concentrations of doping and are given in Table 1. This is due to the incorporation of Zn ions into the WO3 lattice matrix where it alters the crystalline properties of the WO3 nanoparticles [35]. From the XRD result, it is evident that doping causes the structural parameters to change. Especially the sharp increase in intensity of the peak (120) shows less crystallite size for 2% doping, owing to the smaller ionic radii of Zn 2+ (0.074 nm) ions compared to W 6+ ions (0.078 nm) [27]. Causes the charge imbalance in lattice planes and alters the interplanar distance. This change in interplanar distance causes other parameters to deviate, resulting in an improved crystallite size. For increased Zn concentrations, crystallite size is found to be slightly greater than 2% but smaller when compared to a pure sample. Among all the samples, WZ2 exhibits better crystalline quality than other prepared materials. Figure 2b shows the crystallite size vs dislocation density trend for various Zn dopant concentrations in the WO3 matrix. Using the formula below, we are able to determine the stacking fault (SF) and texture coefficient (TC) [36,37]. The changes in lattice parameters are due to different concentrations of doping and are given in Table 1. This is due to the incorporation of Zn ions into the WO 3 lattice matrix where it alters the crystalline properties of the WO 3 nanoparticles [35]. From the XRD result, it is evident that doping causes the structural parameters to change. Especially the sharp increase in intensity of the peak (120) shows less crystallite size for 2% doping, owing to the smaller ionic radii of Zn 2+ (0.074 nm) ions compared to W 6+ ions (0.078 nm) [27]. Causes the charge imbalance in lattice planes and alters the interplanar distance. This change in interplanar distance causes other parameters to deviate, resulting in an improved crystallite size. For increased Zn concentrations, crystallite size is found to be slightly greater than 2% but smaller when compared to a pure sample. Among all the samples, WZ2 exhibits better crystalline quality than other prepared materials. Figure 2b shows the crystallite size vs dislocation density trend for various Zn dopant concentrations in the WO 3 matrix. Using the formula below, we are able to determine the stacking fault (SF) and texture coefficient (TC) [36,37].
where, N is the number of diffraction peaks, I (hkl) and I 0(hkl) are the measured relative intensity of a plane and the standard intensity of the plane, taken from JCPDS data. The TC value is varied for different doping concentrations. The sample WZ2 has the highest TC value which indicates that it has plenty of closely oriented crystallites and the lowest TC value of the sample WZ3 represents that it possesses randomly oriented crystallites. The fluctuation of SF is caused by the formation of crystal defects. The presence of SF in a crystal produces a shift in the phase of incident and scattered X-rays with regard to the lattice, altering the consequent peak location. As WZ0 has the highest crystalline size, SF is low. When dopant is introduced, the crystalline size is reduced resulting in an increase in SF. Among the samples, WZ2 is associated with the highest SF value (Table 1). These properties of WZ2 make it a better X-ray attenuation material. Figure 2c shows the Raman spectra of prepared pure WO 3 and Zn-doped WO 3 (WZ0, WZ1, WZ2, WZ3) nanoparticles. Table 2 shows the Raman spectra peak position of prepared nanoparticles. The pure WO 3 particles exhibit intense peaks at 81, 131, 188, 272, 326, 713, and 807 cm −1 . In general, the observed peaks from 200 to 500 cm −1 and from 600 to 1000 cm −1 represent the O-W-O bending modes and W-O stretching modes of the WO 3 system respectively. Peaks below 200 cm −1 are attributed to the translational or rotational lattice modes in WO 6 octahedron [32,38]. Among these, the peaks at 81 and 131 cm −1 correspond to the vibration of W 2 O 2 chains which is a unique mode of the monoclinic phase of WO 3 nanoparticles [32]. The peaks at 713 and 808 cm −1 represent the stretching vibration of O-W-O ions [39]. This is in good agreement with the XRD results and confirms the formation of monoclinic WO 3 particles. The peaks at 272 and 326 cm −1 reveal the plane bending vibration of the O-W-O ions [39]. Upon doping of Zn ions into a lattice, the peak positions show negligible shifts and a sharp change in intensity. The negligible peak position shift may originate from several factors such as a laser-induced heating effect or morphological changes in the focusing point [34]. The observed results reveal the complete dissolution of Zn ions into the WO 3 lattices. The change in the Raman peak intensity is ascertained by Zn doping effect.

Optical Properties
The optical properties of pure WO 3 and Zn-doped WO 3 nanoparticles were explored using UV-Vis-DRS spectra. The DRS spectra of the prepared nanoparticles manifest strong band edge absorption in the UV-Vis region. All the samples exhibit their band edge absorption between 320 to 345 nm (shown in Figure 3a), which might be due to the intermolecular charge transfer or to the conjugation system [40]. The sharp absorption peak between 320 to 345 nm shows the well crystalline quality of all the samples [41,42]. All the Zn-doped WO 3 nanoparticles are blue-shifted when compared to the WZ0 sample, which confirms that the optical properties of WO 3 nanoparticles are highly influenced by Zn doping [43]. Using the Kubelka-Munk plot (Figure 3b), the optical bandgap is estimated to be 2.88 eV at room temperature for WZ0. The optical bandgap energy of doped samples namely WZ1, WZ2, and WZ3 is higher than that of the pure WZ0 nanosystem, the energy gap values of the samples are calculated as 3.01 eV, 3.09 eV, and 2.97 eV respectively. This result reveals that the Burstein-Moss effect plays a major role [44]. The doping of semiconductor materials moves the fermi level beyond the conduction band due to the formation of a larger number of donor levels [45]. Hence the bandgap obtained from such doped material is found to be enlarged. For the doped oxide nanoparticles, the optical bandgap energy variation is owing to the synergetic effect betwixt Zn and WO 3 [33,43]. The values are consistent with the reported value [46]. Urbach energy (E u ) is known as the width of the defect bands, which are produced by the charge disproportionation, and creates an impact on the optical transitions betwixt the valance and conduction bands as well. These defect bands introduced the Urbach tail or localised states in band tails. E u is the term for the energy connected to this defect tail. These defects may also have developed throughout the development process, leading to lattice abnormalities and stress in the sample. The E u has been calculated by taking the inverse of the slope of the equation [47]. bond formation between epoxy and WO3 nanoparticles. This will give rise to strong structural integrity.  Figure 4a shows the TEM image of WZ0nanoparticles with agglomerated pseudocuboid morphology which may become clustered together during the growth and annealing process. The larger particles are anchored by the smaller particles on the surface, such agglomeration and clustering are common limitations in the solution-grown nanoparti- The creation of defect levels in betwixt the band gaps obviously enhances the E u with Zn dopant. A higher E u shows that the sample WZ2 is more prone to transform weak bonds into defects [48]. This is also consistent with the strain behaviour reported in XRD studies (Figure 3c).

HR-TEM and SAED Analysis
The defect properties of prepared nanoparticles were investigated using photoluminescence (PL) spectra at room temperature. The excitation wavelength of the PL spectrum is 355 nm. The WO 3 nanoparticles at various dopant concentration levels exhibit three emission bands as shown in Figure 3c. The PL spectra for both WO 3 and Zn-doped WO 3 nanoparticles showcase similar emission bands and dopants do give or raise any new peaks from PL phenomena. However, the intensity of dopant materials (WZ1, WZ2, WZ3) is found to be reduced compared to WZ0. The sharp and high-intensity peak centred at 365 nm (3.39 eV) corresponds to the ultraviolet (UV) band. It is due to the recombination of electrons from the internal states of the charged oxygen vacancies in the conduction band to the valence band [49,50]. WZ3 material has a strong emission band at the wavelength of 365 nm (3.39 eV) originating from higher content of surface oxygen vacancy. Due to this vacancy, the WZ3 material has less crystallinity compared with WZ0 [33,51]. The second emission band was observed as blue emission of 449 nm (2.76 eV) which may be attributed to the presence of radiative recombination betwixt the bandgap energy of 2.76 eV or oxygen vacancy defect in WO 3 [52,53]. The third emission band for the samples WZ0, WZ1, WZ2, and WZ3 are located at 522, 517, 513, and 521 nm respectively. The low intense and broad peak is related to green band emission caused by the presence of interstitial oxygen vacancy. The oxygen defects or vacancy gives rise to the green colour for WO 3 nanoparticles rather than its native yellow colour [54]. While increasing the Zn dopant concentration from WZ1 to WZ2 the intensity of the green emission peak decreases and shifts to a lower wavelength. Further increasing the Zn concentration, the intensity of the green emission becomes raised, and position of the peak is shifted to a higher wavelength region. This phenomenon is ascertained by the deep defect level present in the material WZ3 [33,55]. It is noteworthy that, after dispersing the WO 3 nanoparticles in the epoxy resin, the colour of the WO 3 changes much dark and turns bluish-grey in colour. The change in colour is assumed as epoxy reacts with WO 3 nanoparticles and there may be a bond formation between epoxy and WO 3 nanoparticles. This will give rise to strong structural integrity. Figure 4a shows the TEM image of WZ0nanoparticles with agglomerated pseudocuboid morphology which may become clustered together during the growth and annealing process. The larger particles are anchored by the smaller particles on the surface, such agglomeration and clustering are common limitations in the solution-grown nanoparticles [28]. The particle size distribution plot for Figure 4a shown in Figure 4c conveys the poly-dispersed state of the nanoparticles. i.e., the size of the larger particles was in the range of 300-700 nm and the size of smaller particles adhered on the surface of the larger particle was in the range of 20-100 nm. This smaller particle anchoring on the larger particle can be seen clearly in Figure 4a. The TEM micrograph of WZ2 nanoparticles showcased the distinct and agglomeration-free state. The doping of Zn into WO 3 reduces the overall size of the nanoparticles (Figure 4d) compared to WZ0. The average size distribution of the particles in the WZ2 sample is found to be 10-50 nm. It is also witnessed that medium-size particles are in the range from 60-250 nm and with aggregated particles are in the range of 300-400 nm (Figure 4f). Also, upon doping, the morphology of the particles transformed from cuboid shape to cube and rods with uneven edges. The WZ2 shows well-defined lattice fringes in Figure 4e. The incorporation of Zn into the WO 3 monoclinic system orients the crystallites into a single direction and limits the poly crystallization of WO 3 . Also, the 2% Zn doping improves the crystalline quality of the particle which is in good agreement with the XRD analysis findings.

HR-TEM and SAED Analysis
Figure 5a-f shows the SAED pattern images of undoped WO3 and 2% Zn doped WO3 nanoparticles obtained from HR-TEM. The inverse contrast image of the SAED pattern clearly distinguishes the pure and doped WO3. In the pure WO3, the dot patterns are arranged precisely with high periodicity, on the other hand, the doped one exhibits less distorted spots. The observation clearly demonstrates the differences in the lattice property of the Zn-doped lattice from the pure WO3. Overall, the result proves the formation of monoclinic WO3 and the incorporation of Zn ions into the WO3 lattice does not alter the monoclinic structure of WO3.

SEM-EDAX Analysis
The cross-sectional view of WZ0 and WZ2 impregnated epoxy-resin aprons was subjected to SEM and elemental mapping analysis and the results are shown in Figure 6a-j. The presence of carbon in the elemental mapping is reasoned for the rexine cloth. Zn, W,

SEM-EDAX Analysis
The cross-sectional view of WZ0 and WZ2 impregnated epoxy-resin aprons was subjected to SEM and elemental mapping analysis and the results are shown in Figure 6a-j. The presence of carbon in the elemental mapping is reasoned for the rexine cloth. Zn, W, O are also witnessed in the study which confirms the formation of compound Zn doped WO 3 . Figure 6h-

X-ray Shielding Analysis
Much experimental evidence for the interaction of X-ray photons with matter are available in literature starting from Thomson scattering to Compton scattering. Many researchers have realised that their works reveal either absorbed (or) scattered (or) attenuated matter. In the energy range, below 200 kVp, the photoelectric effect (PEE) is the predominant phenomenon of X-rays that is accompanied by characteristic radiation, photoelectrons, and positive ions. Above 200 kVp, Compton scattering comes into existence with X-ray photons [56]. In the present study, employed diagnostic X-rays are in the energy range of 20-140 kVp which is primarily used in the angiographic, orthopaedic and dental X-ray imaging processes [33]. To estimate the innate attenuation of X-rays by the rexine and epoxy resin, X-ray attenuation studies were performed on the pure epoxy coated over a rexine cloth. The results show that (Figure 7a,b), the epoxy rexine layers have linear attenuation throughout the 40-100 kVp range. The epoxy shows higher X-ray attenuation than the bare rexine cloth. The prepared WZ0, WZ1, WZ2, and WZ3 nanoparticles are separately dispersed uniformly in the epoxy resin under vigorous stirring and coated over the rexine cloth via the drop-casting method. Though a wide variety of aprons are commercially available in market, by following the same experimental protocol we prepare a PbO impregnated epoxy resin-rexine cloth apron as a reference material. The X-ray attenuation percentage is evaluated from the relation below [31] %Attenuation = Electrometer reading without sample − Electrometer reading with sample Electrometer reading without sample 100% (9)  Figure 6k,l shows the EDS spectra of WZ0 distributed apron and WZ2 impregnated epoxy-rexine apron. The spectra show the presence of carbon, tungsten, and oxygen. The peak of carbon is originated from the rexine and epoxy. Zn, W and O peaks in the spectra confirmed that Zn is doped in the WO 3 lattice. The apron with a low concentration of Zn exhibits a less intense peak. The other small peaks presented in EDS are attributed due to the rexine and epoxy compound materials.

X-ray Shielding Analysis
Much experimental evidence for the interaction of X-ray photons with matter are available in literature starting from Thomson scattering to Compton scattering. Many researchers have realised that their works reveal either absorbed (or) scattered (or) attenuated matter. In the energy range, below 200 kVp, the photoelectric effect (PEE) is the predominant phenomenon of X-rays that is accompanied by characteristic radiation, photoelectrons, and positive ions. Above 200 kVp, Compton scattering comes into existence with X-ray photons [56]. In the present study, employed diagnostic X-rays are in the energy range of 20-140 kVp which is primarily used in the angiographic, orthopaedic and dental X-ray imaging processes [33]. To estimate the innate attenuation of X-rays by the rexine and epoxy resin, X-ray attenuation studies were performed on the pure epoxy coated over a rexine cloth. The results show that (Figure 7a,b), the epoxy rexine layers have linear attenuation throughout the 40-100 kVp range. The epoxy shows higher X-ray attenuation than the bare rexine cloth. The prepared WZ0, WZ1, WZ2, and WZ3 nanoparticles are separately dispersed uniformly in the epoxy resin under vigorous stirring and coated over the rexine cloth via the drop-casting method. Though a wide variety of aprons are commercially available in market, by following the same experimental protocol we prepare a PbO impregnated epoxy resin-rexine cloth apron as a reference material. The X-ray attenuation percentage is evaluated from the relation below [31] %Attenuation = Electrometer reading without sample − Electrometer reading with sample Electrometer reading without sample × 100% The WZ0, WZ1, WZ2, and WZ3 nanoparticles-based apron and the PbO-based apron show similar trends in X-ray attenuation performance over the entire test range. This trend is maintained in the X-ray attenuation at higher tube voltages, especially between 70 and 100 kVp. A slight increase in the attenuation value of a Pb-based apron is attributed to its high atomic number (Pb = 82) compared to tungsten (W = 74), but the difference in X-ray attenuation between the prepared aprons is less significant in real-world operation [8]. Also, contrary to expectation, among the Zn-doped WO3 system-based apron, WZ2 performed well in the X-ray attenuation compared to pure and other dopant concentrations (WZ0, WZ1 and WZ3). The X-ray attenuation of WZ2 is better than that of PbO for lower tube voltage (40)(41)(42)(43)(44)(45)(46)(47)(48)(49)(50). Besides, Half-Value-Layer measurements are also made for the prepared aprons, the numerical value of the HVL is found using the relation (10) and (11), which is also an important parameter to estimate the X-ray attenuating apron [8]. It is also interesting to notice that HVL is the thickness of the sample adequate enough to reduce the initial intensity of the X-rays into half [57,58].
where, µ-Liner attenuation coefficient, t-thickness of the sample, I-intensity of attenu- The WZ0, WZ1, WZ2, and WZ3 nanoparticles-based apron and the PbO-based apron show similar trends in X-ray attenuation performance over the entire test range. This trend is maintained in the X-ray attenuation at higher tube voltages, especially between 70 and 100 kVp. A slight increase in the attenuation value of a Pb-based apron is attributed to its high atomic number (Pb = 82) compared to tungsten (W = 74), but the difference in X-ray attenuation between the prepared aprons is less significant in real-world operation [8]. Also, contrary to expectation, among the Zn-doped WO 3 system-based apron, WZ2 performed well in the X-ray attenuation compared to pure and other dopant concentrations (WZ0, WZ1 and WZ3). The X-ray attenuation of WZ2 is better than that of PbO for lower tube voltage (40)(41)(42)(43)(44)(45)(46)(47)(48)(49)(50). Besides, Half-Value-Layer measurements are also made for the prepared aprons, the numerical value of the HVL is found using the relation (10) and (11), which is also an important parameter to estimate the X-ray attenuating apron [8]. It is also interesting to notice that HVL is the thickness of the sample adequate enough to reduce the initial intensity of the X-rays into half [57,58].
where, µ-Liner attenuation coefficient, t-thickness of the sample, I-intensity of attenuated beam and I o -initial intensity, µ m -mass attenuation coefficient, ρ-density of the material (density of unknown materials was calculated by the Archimedes method), m1-mass in air, m2-mass in immersion liquid and ρ l is the density of the immersion liquid (here, ethanol is immersion liquid ρ l = 0.789 g/cm −1 ). From the results (Figure 7c), WZ2 showed a low HVL value for a low energy range of 40-50 kVp of tube voltage. Beyond which, it is found that the value of HVL increases linearly throughout the voltage range. The prepared aprons WZ0, WZ1 and WZ3 also showed a similar trend of increasing HVL values. All the samples exhibit a higher value than the Pb based apron. The sample WZ2 shows low HVL for the energy range 40-50 kVp and starts to increase exponentially for the energy range 50-100 kVp. It is noteworthy that, the value of the HVL of WZ2 based apron is higher for than the HVL value of PbO based apron in the higher energy range (80-100 kVp). Figure 7d represents the tube voltage vs exposure, which provides the information about quality of radiation reaching the detector after passing through the apron. It is understood that PbO and WZ2 have identical and lowest exposure among all the samples. After which the second lowest exposure is exhibited by WZ0 followed by WZ1-and WZ3-based aprons. The important reason behind the similar exposure of WZ2 and PbO in X-ray shielding is that the size effect of Zn-doped WO 3 nanoparticles compared to the micro-sized PbO particles in an apron. The uniform distribution of nanoparticles in the epoxy matrix is also attributed to similar exposure behaviour of PbO-based apron and WZ2-based apron [26]. Linear attenuation coefficient (µ) is calculated by Equation (11). If the thickness (t) of the material varies, µ might vary in the same material. It means, µ depends on the t of the given material. In the present study t of samples was not changed and Figure 7e shows the µ value for prepared WZ0, WZ1, WZ2, and WZ3 based aprons and PbO-based apron. At low tube voltage (40-50 kVp) WZ2 has a high µ value. As tube voltage increases further (50-100 kVp), µ of PbO was slightly more than that of WZ2 since in this energy region, photoelectric effect absorption is high for higher atomic number (Pb = 82) [59]. Also, µ of WZ2 is better than WZ0, WZ1, and WZ3. By dividing the µ by density (ρ), the resultant coefficient is ρ independent and is known as the mass attenuation coefficient (µ m ). The µ m and ρ of the aprons are calculated by Equations (12) and (13), the ρ tabulated in Table 3. Figure 7f shows that WZ2 based apron had the highest µ m value in lower tube voltage (40)(41)(42)(43)(44)(45)(46)(47)(48)(49)(50) and PbO marginally high in the higher tube voltage (50 kV-100 kVp). µ m values of WZ0, WZ1 and WZ3 based aprons are lower than WZ2 based apron. Due to the photoelectric effect, the attenuation value dropped as photon energy increased in the low energy range (40-100 kVp) [60]. The comparison of µ m between the prepared sample and other polymer metal oxide composites and alloy materials is tabulated in Table 4. Figure 8 shows the reason for the better X-ray shielding property of WZ2 based apron than other aprons. Since there were no materials to block the X-ray, there was only 25% of the incident X-rays are attenuated (Figure 8a). The presence of pure WO 3 in the apron (Figure 8b) increases the attenuation up to 92%. There were no sufficient smaller-size particles in the pure WO 3 to block the X-rays. However, 2% Zn-doped WO 3 (Figure 8c) shows increased attenuation of 97% which is reasoned as a high amount of smaller-sized particles (10-50 nm) of WZ2 in WZ2 based aprons which seal the space between the largesized nanoparticles and epoxy resin fibers. Our report proves that doping Zn in a WO 3 matrix can alter the X-ray attenuation property of a material. The reduced particle size with improved crystallinity (obtained from TEM and XRD) of WZ2 also supports the above argument. The smaller the particle, the higher the grain boundary scattering probability coupled with the secondary scattering events, since, the number of particles per gram is greater compared to the lead particles [61][62][63].  Further, we presumed that the high surface to volume ratio of the nanosystem shows enhanced X-ray attenuation properties, since a greater number of WO3 (or) Zn-doped WO3 system are exposed themselves to incoming X-ray radiation. This phenomenon also greatly increases the chance of absorbing the X-ray photon which ends up with the blocking of X-rays. Thus, nanoparticle impregnation, in an either undoped (or) doped form improves the X-ray attenuation coefficient than (or) equal to PbO-based apron. There are several types of tungsten-based polymer composites that can be used for X-ray shielding; Table 4 compares their X-ray attenuation performance. Only minimal studies have been conducted on tungsten-based epoxy nanocomposite. In this study, Zn-doped WO3-based epoxy nanocomposite material is used for the first time to the best of my knowledge in an x-ray shielding application and the results are compared to other materials. Results show that the addition of a dopant enhanced the X-ray attenuation performance.  Further, we presumed that the high surface to volume ratio of the nanosystem shows enhanced X-ray attenuation properties, since a greater number of WO 3 (or) Zn-doped WO 3 system are exposed themselves to incoming X-ray radiation. This phenomenon also greatly increases the chance of absorbing the X-ray photon which ends up with the blocking of X-rays. Thus, nanoparticle impregnation, in an either undoped (or) doped form improves the X-ray attenuation coefficient than (or) equal to PbO-based apron. There are several types of tungsten-based polymer composites that can be used for X-ray shielding; Table 4 compares their X-ray attenuation performance. Only minimal studies have been conducted on tungsten-based epoxy nanocomposite. In this study, Zn-doped WO3-based epoxy nanocomposite material is used for the first time to the best of my knowledge in an X-ray shielding application and the results are compared to other materials. Results show that the addition of a dopant enhanced the X-ray attenuation performance.

Conclusions
The X-ray shielding properties of Zn-doped WO 3 composite aprons were studied and discussed in detail. The pure and Zn-doped WO 3 nanoparticles were prepared using the acid preparation method. The XRD results show the crystalline nature with a monoclinic structure and reduction in crystalline size on the addition of Zn dopant, Raman vibration modes also confirmed the monoclinic structure. The optical study of UV-visble spectroscopy showed bandgap changes due to Zn doping. The addition of a dopant creates a defect in the parent material, which is shown by the photoluminescence study. TEM image revealed that the particle size of 2% Zn-doped WO 3 was smaller than undoped WO 3 and smaller particles in the 2% Zn-doped WO 3 were anchored to the larger particles, creating a better X-ray attenuation property by sealing the space between the large particles. The HVL of the 2% Zn-doped WO 3 system revealed less value and hence, it exhibited better attenuation in low-energy region. The study revealed that the WZ2-based apron had good mass attenuation coefficient (µ m ), which made it as an efficient material in X-ray shielding process. The results of the study demonstrate that doping can affect the X-ray attenuation efficiency of a material and that Zn doped WO 3 can be used as an alternative to lead for environmentally friendly and durable X-ray shielding applications.