Next Article in Journal
Optimization of Single α-Phase for Promoting Ferromagnetic Properties of 44Fe–28Cr–22Co–3Mo–1Ti–2V Permanent Magnet with Varying Co Concentration for Energy Storage
Next Article in Special Issue
Experimental and Simulation Investigation of Nd Additions on As-Cast Microstructure and Precipitate Development in Mg–Nd System Alloys
Previous Article in Journal
Leaching of Copper Contained in Waste Printed Circuit Boards, Using the Thiosulfate—Oxygen System: A Kinetic Approach
Previous Article in Special Issue
Metallization on Sapphire and Low-Temperature Joining with Metal Substrates
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Improved Anti-Vulcanization and Bonding Performance of a Silver Alloy Bonding Wire by a Cathodic Passivation Treatment with Palladium

1
State Key Laboratory of Precision Electronic Manufacturing Technology and Equipment, Guangdong University of Technology, Guangzhou 510006, China
2
Jihua Laboratory, Foshan 528225, China
3
School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, China
4
State Key Laboratory of Materials Processing and Die & Mould Technology, School of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China
5
Key Laboratory for New Type of Functional Materials in Hebei Province, School of Materials Science, Hebei University of Technology, Tianjin 300401, China
*
Authors to whom correspondence should be addressed.
Materials 2022, 15(7), 2355; https://doi.org/10.3390/ma15072355
Submission received: 3 March 2022 / Revised: 19 March 2022 / Accepted: 20 March 2022 / Published: 22 March 2022
(This article belongs to the Special Issue Physical Metallurgy of Metals and Alloys)

Abstract

:
As a traditional interconnect material, silver alloy bonding wires are widely used in electronic packaging, but their propensity to vulcanize quickly has not been sufficiently addressed. The current surface anti-oxidation and anti-sulfidation treatments are often accompanied by a decline in bonding performance, which hinders the use of silver alloy bonding wires in new applications. In the present paper, we develop a new cathodic passivation treatment in a Pd-containing solution for silver bonding wires, which not only significantly improves their vulcanization resistance, but also maintains their bonding performance. The surface of the treated wires remains unaffected after vulcanization in 0.3 μg/m3 of ammonium sulfide for 60 min. Compared to a Pd-free passivation treatment, the bonding strength of the wire passivated with the Pd-containing solution improves from 0.20 to 0.27 N. XPS analysis confirms the existence of Pd on the surface of the wire. The solder ball formed an obtuse angle instead of a sharp angle on the pad, which is beneficial for bonding strength.

1. Introduction

As a traditional packaging interconnect technology, wire bonding still occupies an important place in electronic packaging, due to its simple process and low cost [1]. The materials for bonding wires have developed from pure metals to a variety of alloys based on, for example, gold, silver, copper, and aluminum [2,3,4,5]. Among these metals, silver has the best electrical and thermal conductivity, and its price is relatively moderate. Therefore, silver bonding wires have been considered as a potential alternative to gold bonding wires. However, silver alloy bonding wires can be easily contaminated when used in an environment without a protective gas [6,7], which becomes an obstacle for extending their use to new applications.
Bonding reliability is another important property of bonding wires. The device will fail, as long as one of the bonding points is damaged. Generally, the failure modes of the solder ball of wire bonding can be divided into intra-ball failure and interfacial failure, which usually start from the intermetallic compounds, interfacial voids and interfacial corrosion points [8,9]. Zhang et al. [10] studied the failure of LED packages and pointed out that the stress concentration generated in the thermal shock test can lead to the neck fracture of the solder balls. On the other hand, interfacial failures are also widely observed. Wu et al. [11] conducted power cycle life tests on different types of insulated gate bipolar translator (IGBT) modules, and found that the recrystallization and electrothermal migration could lead to the fracture of the bonding interface. Zheng et al. [12] found that the separation of the bonding wire and the pad is the main failure mode of IGBT modules. The mismatch of thermal expansion coefficients between the bonding wire and the chip causes stress concentration and leads to cracks at the bonding interface to form an open circuit.
To address these problems, various technologies, such as alloying and surface treatments, were developed. For instance, Cheng and Hsiao [13] tried to improve the oxidation and interfacial corrosion resistance of Ag wires through the addition of Au and Pd. Guo and Jong-Soo [14] revealed that doping with Pd can improve the bonding force of the wire by increasing the interconnect reliability between the solder ball and the pad interface. Tseng et al. [15] plated silver wires with gold to improve its oxidation resistance and mechanical properties. Fei-Yi et al. [16] galvanized aluminum bonding wires to control the shape of the solder ball. However, new problems appeared with these treatments. After the bonding wire was alloyed, its electrical and thermal conductivity decreased, which would lead to an increase in manufacturing costs [17]. The thickness of the noble metal element electroplated on the bonding wires was relatively large (~100 nm) and also expensive [18]. The application of a surface treatment affected the mechanical performance of the bonding wires, thereby reducing the life of the package structure [16,19]. As a result, finding a new anti-vulcanization processing method that combines low cost, facile operation, and minimal influence on the bonding performance remains a challenge for the use of silver bonding wires.
In this study, we develop a new cathodic passivation solution for the anti-vulcanization treatment of silver bonding wires. Through the addition of palladium nitrate in solution, the vulcanization resistance of the passivated wires is significantly improved. On the other hand, the treatment also improved the surface wettability of the bonding wires on Au pads. Therefore, the solder ball tends to form an obtuse angle instead of a sharp angle on the pad, which is beneficial to reducing the interface stress concentration and improving the bonding strength. This study could provide a way to improve the sulfidation resistance of bonding wires with less impact on the bonding performance, and shows that wettability modulation may be an effective way to improve the reliability of bonding interfaces.

2. Experiments

2.1. Preparation of the Materials

Silver alloy bonding wires with a diameter of 20 μm were purchased from Xinqipai Electronic Technology Co., Ltd., Chongqing, China. The compositions of the silver alloy bonding wires are shown in Table 1. A hydrotropic solution with 0.010 mol/L of chromium acetate, 0.008 mol/L of trisodium citrate, 0.010 mol/L of sodium tartrate, 0.015 mol/L of crystalline sodium acetate, and 0.140 mol/L of sodium hydroxide was used as the Pd-free passivation solution. Another Pd-containing passivation solution was prepared by adding 0.001 mol/L of palladium nitrate to the Pd-free passivation solution.

2.2. Experimental Methods

Figure 1a provides an illustration of the cathodic passivation device. The silver alloy bonding wire was sequentially immersed into the passivation solution and deionized water. A current of 500 A/m2 was applied to the wires and the passivation solution. The wire is the cathode. The wire was processed in the passivation solution for 5 s at 25 °C.
Figure 1b shows a flow chart of the experimental procedures after the passivation treatment. The original silver wires and the passivated wires in the Pd-free and Pd-containing solutions were bonded onto Au pads (diameter = 50 μm) using an automatic bonding tool (AW386, Ada Intelligent Equipment Co., Ltd., Foshan, China) for the ball shear force test. The wires formed two bond points, the first being the ball bond and the second being the wedge bond. The detailed bonding parameters are shown in Table 2. After the bonding wires were attached on the Au pads, the cross-sections of the ball bonds on the Au pads were observed by a scanning electron microscope (SEM, HITACHI SU8220, Tokyo, Japan). Using a thrust tester (Condor Sigma, XYZTEC), the ball bonds were pushed away from the Au pads, and the bonding strength was recorded. The fracture morphologies of the Au pads after the shear tests were observed by the SEM.
The original silver wires and the passivated wires in the Pd-free and Pd-containing solutions were placed in a sealed 3 × 3 × 3 cm3 box filled with ammonium sulfide gas with a concentration of 0.3 μg/m3. The surface condition of the wires was recorded by an optical microscope. Due to the small size of the silver alloy bonding wires, silver plates with a thickness of 10 μm were passivated in the solutions using the same parameters. The surfaces of the passivated silver plates were analyzed by X-ray photoelectron spectroscopy (XPS, Escalab 250Xi).

3. Results and Discussions

3.1. Vulcanization Resistance of the Passivated Silver Alloy Bonding Wires in Different Solutions

Figure 2 shows the surface of the passivated silver alloy bonding wires in different solutions, before and after vulcanization in ammonium sulfide for 20 and 60 min. The surface of the untreated silver alloy bonding wire turned yellow after 20 min of vulcanization, and the surface was further vulcanized to dark red after 60 min. The surface of the silver alloy bonding wire treated with the standard, Pd-free passivation solution turned pale yellow after vulcanization for 20 min. After 60 min of vulcanization, the surface of the bonding wire darkened further. The surface of the silver alloy bonding wire treated with the new Pd-containing passivation solution after vulcanization for 60 min had the same appearance and silver-white color as the surface of the wire before vulcanization. This result indicate that the Pd-containing passivation solution provides better vulcanization resistance than the Pd-free passivation solution.

3.2. Surface Analysis

Figure 3 shows the XPS spectra of the passivated silver plates in the Pd-free solution after storage for 5 days. Peaks of Ag3d, O1s, Cr2p, and C1s electrons are apparent. The Ag3d fine spectrum (Figure 3b) shows 2 characteristic peaks at binding energies of 368.40 and 374.40 eV, corresponding to the Ag3d5/2 and Ag3d3/2 electrons, respectively. It has been reported that the peaks of Ag are at 368.2 eV [20] and 374.27 eV [21], and the peaks of Ag2O are at 367.4 eV [22] and 373.90 eV [23], respectively. As the peaks of the Ag3d fine spectrum in Figure 3b show highly symmetrical shapes, it can be concluded that most of the Ag element is in the form of Ag, but not AgO. The Cr2p3/2 fine spectrum (Figure 3c) shows 2 characteristic peaks at binding energies of 577.28 and 576.30 eV, corresponding to Cr(OH)3 and Cr2O3, respectively [24,25,26], The peak of Cr is at 574.13 eV [27], which is not observed in the spectrum in Figure 3. The Cr ions are present because they are in the passivation solution. The O1s fine spectrum (Figure 4d) shows 3 characteristic peaks after peak fitting, with binding energies of 532.00, 531.28 and 529.44 eV, respectively. The peak at 529.44 eV corresponds to O2− [28], which indicates that the surface contains metallic oxides. The peak at 531.28 eV corresponds to organic C–O and OH [29,30], and the peak at 532.00 eV corresponds to organic C=O and OH [29,31]. These two peaks and the existence of the C1s peak indicate that the surface of the passivated silver plate contains some residual organics, which are difficult to avoid in XPS measurements [32]. Based on the XPS spectra, it can be concluded the metallic species on the surface of the passivated silver plates in the Pd-free solution are Ag, Cr(OH)3 and Cr2O3.
Figure 4 shows the XPS spectra of the passivated silver plates in the Pd-containing solution after storage for 5 days. Peaks of Ag3d, O1s, Pd3d, Cr2p, and C1s electrons can be observed. The spectra of Ag3d (Figure 4b) and Cr2p (Figure 4c) are similar to that of the passivated silver plates in the Pd-free solution. In the O1s fine spectrum (Figure 4d), the O2- peak at 529.44 eV is relatively smaller than that in Figure 3d, as marked by the red arrow. In Figure 4e, the Pd3d3/2 fine spectrum shows 2 characteristic peaks at 340.18 and 339.68 eV, and the Pd3d5/2 fine spectrum shows 2 characteristic peaks at 334.85 and 334.41 eV. These peaks correspond to Pd [33]. The peaks of PdO, PdO2 and PdO3 are at 336.90, 337.50 and 337.7 eV, respectively [34,35], which are not observed in the spectrum in Figure 4. Their absence indicates that the Pd on the surface of the passivated silver plate is in the form of Pd. Based on the XPS spectra, it can be concluded the metallic species on the surface of the passivated silver plates in the Pd-containing solution mainly contains Ag, Cr(OH)3, Cr2O3 and Pd. Based on the XPS spectra, the relative atomic concentrations of different metallic species on the surfaces of the passivated Ag plates are calculated and shown in Table 3. In comparison, the surface of the silver plates in the Pd-containing solution contains a small amount of Pd, and the concentrations of Ag and Cr2O3 have slightly decreased.

3.3. Shear Tests of the Passivated Silver Alloy Bonding Wires in Different Solutions

Figure 5 shows the cross-section images of the bonded wires on the pads before the shear force tests. As the wires are melted during the wire bonding process, the solder ball and the pad form a contact angle, which are summarized in Table 4. For the untreated wire (Figure 5a), the average contact angle is 104°, whereas for the wires passivated in the Pd-free solution (Figure 5b), the average contact angle is 136°, corresponding to a lower wettability. As a result, the contact interface between the solder ball and the pad tends to shrink, and eventually forms a sharp angle on the edge. Due to the stress concentration caused by the sharp angle and the relatively low contact area, a low bonding strength can be expected. For the wire passivated in the Pd-containing solution (Figure 5c), the average contact angle decreased to 108°, which is close to the contact angle of the untreated wires.
One possible reason for the different contact angles of the wires relates to the content of elements on the surface of the wires. For the wires passivated in the Pd-containing solution, there is a small amount of Pd on the surface. As revealed in previous studies [36,37,38,39,40], the existence of noble metal elements, such as Pd, is beneficial for the oxidation and vulcanization resistance of the Cu and Ag bonding wires. The presence of Pd in the passivated layer might hinder the oxidation of the wires during the bonding process, which decreases the surface energy and increases the wettability of the solder ball. Therefore, smaller contact angles are formed.
Figure 6 shows the measured bonding strength of the wires. The untreated wires, the wires passivated in the Pd-free solution, and the wires passivated in the Pd-containing solution. fractured at mean shear forces of 0.30, 0.20, and 0.27 N, respectively. Through the use of the Pd-containing solution for passivation, the strength of the treated bonding wire increased by 35%, compared to the wire treated in the standard Pd-free solution.
Figure 7 shows the fracture surface of the untreated silver alloy bonding wires and silver alloy bonding wires passivated in different solutions. For the untreated wires, the whole fracture surface is covered by striped fracture patterns, indicating a good interconnection between the bonding wire and the pad. The average bond force is relatively high (0.30 N). For the passivated wire in the Pd-free solution, only half of the fracture surface is covered with the fracture pattern, and the other half of the surface retains the original flat morphology. The presence of some of the original morphology indicates that the bonding wire has not made sufficient contact with the pad. The average bond force is relatively low (0.20 N). For the wire passivated in the Pd-containing solution, the fracture surface is almost completely covered with the fracture pattern, indicating a good interconnection between the bonding wire and the pad. The average bond force is close to that of the untreated wires (0.27 N).
Based on the measured contact angles and bonding strength, it can be found that a smaller contact angle corresponds to a higher strength. This is because the obtuse angle between the solder ball and the pad is beneficial to reducing the stress concentration on the interface. These results indicate that wettability modulation may be an effective way to improve the interface reliability of wire bonding.
Based on the above results and discussion, the improved vulcanization resistance and bonding performance of the silver alloy bonding wires passivated in the Pd-containing solution can be reasonably understood. The results show that Pd plays a key role in improving the performance of the bonding wire. If Pd is added to the bonding wire by alloying, the required amount of Pd is relatively high, which adds to product cost and may lead to problematic inhomogeneous compositions. In comparison, the cathodic passivation method has the advantages of simple processing, fast reaction times, reduced material consumption, and applicability for different material components.

4. Conclusions

A cathodic passivation solution with palladium nitrate has been developed to improve the resistance to vulcanization while retaining the bonding performance of silver alloy bonding wires. For the passivated wires treated with a Pd-free solution, the vulcanization resistance is improved, but the bonding strength of the wire significantly decreases from 0.30 to 0.20 N. With the addition of palladium nitrate to the passivation solution, the surface of the wire can maintain its original silver-white color after vulcanization in 0.3 μg/m3 of ammonium sulfide for 60 min. The wettability of the wires is improved, as the contact angle between the solder balls and the Au pad decreases from 136° to 108°. The bonding strength of the wire is 0.27 N, 35% stronger than the wire treated with the Pd-free solution. The cathodic passivation treatment in the Pd-containing solution in this study provides an effective and facile method for the improvement of the properties of silver alloy bonding wires.

Author Contributions

G.Y.: Conceptualization, Data curation, Formal analysis, Investigation, Methodology, Software, Visualization, Writing—original draft. Z.Z.: Investigation, Visualization. H.Z.: Visualization. Y.Z.: Funding acquisition. Z.P.: Conceptualization, Supervision. P.G.: Methodology, Visualization. X.W.: Methodology, Visualization. C.C.: Supervision, Funding acquisition. All authors have read and agreed to the published version of the manuscript.

Funding

We acknowledge the support of the National Natural Science Foundation of China (Grant Nos. 62174039, 61874155), Guangdong Basic and Applied Basic Research (Grant Nos. 2021A1515110656, 2022A1515010141, 2021A1515011642), National Key R&D Program of China (Grant No. 2018YFE0204601), and the Key Research and Development Program of Guangdong Province (Grant Nos. 2021B0101290001, 2020B0101290001).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The datasets generated during and/or analyzed during the current study are available from the corresponding author on reasonable request.

Conflicts of Interest

The authors declare no conflict of interest. The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

References

  1. Yang, J. Wire Bonding in Microelectronics. Assem. Autom. 2011, 31, 395. [Google Scholar] [CrossRef]
  2. Liu, H.; Chen, Q.; Zhao, Z.; Wang, Q.; Zeng, J.; Chae, J.; Lee, J. Reliability of Au-Ag Alloy Wire Bonding. In Proceedings of the 2010 Proceedings 60th Electronic Components and Technology Conference, Las Vegas, NV, USA, 1–4 June 2010; pp. 234–239. [Google Scholar]
  3. Tseng, Y.-W.; Hung, F.-Y.; Lui, T.-S.; Chen, M.-Y.; Hsueh, H.-W. Effect of annealing on the microstructure and bonding interface properties of Ag–2Pd alloy wire. Microelectron. Reliab. 2015, 55, 1256–1261. [Google Scholar] [CrossRef]
  4. Chuang, T.-H.; Tsai, C.-H.; Wang, H.-C.; Chang, C.-C.; Chuang, C.-H.; Lee, J.-D.; Tsai, H.-H. Effects of Annealing Twins on the Grain Growth and Mechanical Properties of Ag-8Au-3Pd Bonding Wires. J. Electron. Mater. 2012, 41, 3215–3222. [Google Scholar] [CrossRef]
  5. Yurechko, M.; Grushko, B.; Velikanova, T.; Urban, K. Isothermal sections of the Al–Pd–Co alloy system for 50–100 at.% Al. J. Alloys Compd. 2002, 337, 172–181. [Google Scholar] [CrossRef]
  6. Wu, J.; Rockey, T.; Yauw, O.; Shen, L.; Chylak, B. Bonding of Ag-alloy wire in LED packages. In Proceedings of the 2012 35th IEEE/CPMT International Electronics Manufacturing Technology Conference (IEMT), Ipoh, Malaysia, 6–8 November 2012; pp. 1–4. [Google Scholar]
  7. Guo, R.; Gao, L.; Mao, D.; Li, M.; Wang, X.; Lv, Z.; Chiu, H. Study of free air ball formation in Ag–8Au–3Pd alloy wire bonding. Microelectron. Reliab. 2014, 54, 2550–2554. [Google Scholar] [CrossRef]
  8. Fan, S.H.; Amp, A.S. Failure Mode and Failure Mechanism Analysis of Semiconductor Device Wire Bonding. Environ. Technol. 2018, 36, 54–61. [Google Scholar]
  9. Ma, Z.-Q.; Hu, H.-N.; Wang, Q. Failure Analysis of a Model Audion Inner Lead Bonding. Fail. Anal. Prev. 2007, 4, 50–54. [Google Scholar]
  10. Zhang, S.-U.; Lee, B.W. Fatigue life evaluation of wire bonds in LED packages using numerical analysis. Microelectron. Reliab. 2014, 54, 2853–2859. [Google Scholar] [CrossRef]
  11. Wu, W.; Held, M.; Jacob, P.; Scacco, P.; Birolini, A. Investigation on the long term reliability of power IGBT modules. In Proceedings of the International Symposium on Power Semiconductor Devices and IC’s: ISPSD’95, Yokohama, Japan, 23–25 May 1995; pp. 443–448. [Google Scholar]
  12. Zheng, L.B.; Li, H.; Jin, P.Y.; Fang, H.C.; Wang, C.L.; Wang, Z.P. Investigation of the Temperature Character of IGBT Wire Bonding Lift-Off Based the 3-D Thermal-Electro Coupling FEM. Adv. Mater. Res. 2013, 616–618, 1689–1692. [Google Scholar] [CrossRef]
  13. Cheng, C.H.; Hsiao, H.L.; Chu, S.I.; Shieh, Y.Y.; Sun, C.Y.; Peng, C. Low cost silver alloy wire bonding with excellent reliability performance. In Proceedings of the 2013 IEEE 63rd Electronic Components and Technology Conference (ECTC), Las Vegas, NV, USA, 28–31 May 2013; pp. 1569–1573. [Google Scholar]
  14. Cho, J.-S.; Yoo, K.-A.; Moon, J.-T.; Son, S.-B.; Lee, S.-H.; Oh, K.H. Pd effect on reliability of Ag bonding wires in microelectronic devices in high-humidity environments. Met. Mater. Int. 2012, 18, 881–885. [Google Scholar] [CrossRef]
  15. Tseng, Y.; Hung, F.; Lui, T. Microstructure, tensile and electrical properties of gold-coated silver bonding wire. Microelectron. Reliab. 2015, 55, 608–612. [Google Scholar] [CrossRef]
  16. Hung, F.-Y.; Lui, T.-S.; Chu, K.-M.; Tseng, Y.-W. Aluminium wires have the free air balls (FABs): Electronic flame-off, fracture strength, electrical properties, and bonding characteristics of nano Zn Film Al–Si bonding wires. Metals 2017, 7, 152. [Google Scholar] [CrossRef] [Green Version]
  17. Cho, J.-S.; Jeong, H.-S.; Moon, J.-T.; Yoo, S.-J.; Seo, J.-S.; Lee, S.-M.; Ha, S.-W.; Her, E.-K.; Kang, S.-H.; Oh, K.-H. Thermal reliability & IMC behavior of low cost alternative Au-Ag-Pd wire bonds to Al metallization. In Proceedings of the 2009 59th Electronic Components & Technology Conference, San Diego, CA, USA, 26–29 May 2009; pp. 1569–1573. [Google Scholar]
  18. Xu, H.; Qin, I.; Clauberg, H.; Chylak, B.; L.Acoff, V. Behavior of palladium and its impact on intermetallic growth in palladium-coated Cu wire bonding. Acta Mater. 2013, 61, 79–88. [Google Scholar] [CrossRef]
  19. Chuang, T.-H.; Lin, H.-J.; Chuang, C.-H.; Shiue, Y.-Y.; Shieu, F.-S.; Huang, Y.-L.; Hsu, P.-C.; Lee, J.-D.; Tsai, H.-H. Thermal stability of grain structure and material properties in an annealing twinned Ag–4Pd alloy wire. J. Alloys Compd. 2014, 615, 891–898. [Google Scholar] [CrossRef]
  20. Johansson, G.; Hedman, J.; Berndtsson, A.; Klasson, M.; Nilsson, R. Calibration of electron spectra. J. Electron Spectrosc. Relat. Phenom. 1973, 2, 295–317. [Google Scholar] [CrossRef]
  21. Yan, L.; Jordan, R.G.; Qiu, S.L. Electronic structures of ordered Ag-Mg alloys. Phys. Rev. B Condens. Matter 1994, 49, 4478. [Google Scholar]
  22. Hammond, J.S.; Gaarenstroom, S.W.; Winograd, N. X-ray photoelectron spectroscopic studies of cadmium- and silver-oxygen surfaces. Anal. Chem. 2002, 47, 2193–2199. [Google Scholar] [CrossRef]
  23. Tjeng, L.H.; Meinders, M.B.J.; Vanelp, J.; Ghijsen, J.; Sawatzky, G.A.; Johnson, R.L. Electronic structure of Ag2O. Phys. Rev. B Condens. Matter 1990, 41, 3190. [Google Scholar] [CrossRef] [PubMed]
  24. Shuttleworth, D. Preparation of metal-polymer dispersions by plasma techniques. An ESCA investigation. J. Phys. Chem. 1980, 84, 1629–1634. [Google Scholar] [CrossRef]
  25. Capece, F.M.; Castro, V.D.; Furlani, C.; Mattogno, G.; Fragale, C.; Gargano, M.; Rossi, M. “Copper chromite” catalysts: XPS structure elucidation and correlation with catalytic activity. J. Electron. Spectrosc. Relat. Phenom. 1982, 27, 119–128. [Google Scholar] [CrossRef]
  26. Howng, W.-Y.; Thorn, R.J. Investigation of the electronic structure of La1−x(M2+)xCrO3, Cr2O3 and La2O3 by X-ray photoelectron spectroscopy. J. Phys. Chem. Solids 1980, 41, 75–81. [Google Scholar] [CrossRef]
  27. Moffat, T.P.; Latanision, R.M.; Ruf, R.R. An X-ray photoelectron spectroscopy study of chromium-metalloid alloys—III. Electrochim. Acta 1995, 40, 1723–1734. [Google Scholar] [CrossRef]
  28. Sugimoto, K.; Sawada, Y. The role of molybdenum additions to austenitic stainless steels in the inhibition of pitting in acid chloride solutions. Corros. Sci. 1977, 17, 425–445. [Google Scholar] [CrossRef]
  29. Asami, K.; Hashimoto, K. The X-ray photo-electron spectra of several oxides of iron and chromium. Corros. Sci. 1977, 17, 559–570. [Google Scholar] [CrossRef]
  30. López, G.; Castner, D.G.; Ratner, B.D. XPS O 1s binding energies for polymers containing hydroxyl, ether, ketone and ester groups. Surf. Interface Anal. 1991, 17, 267–272. [Google Scholar] [CrossRef]
  31. Khan, M.T.; Srivastava, S. Some new ruthenium (III) schiff base complexes: A photoelectron spectroscopic study. Polyhedron 1988, 7, 1063–1065. [Google Scholar] [CrossRef]
  32. Yang, G.; Zou, Q.; Wang, P.; Lai, H.; Lai, T.; Zeng, X.; Li, Z.; Luo, J.; Zhang, Y.; Cui, C. Towards understanding the facile synthesis of well-covered Cu-Ag core-shell nanoparticles from a complexing model. J. Alloys Compd. 2021, 874, 159900. [Google Scholar] [CrossRef]
  33. Schleich, B.; Schmeisser, D.; Göpel, W. Structure and reactivity of the system Si/SiO2/Pd: A combined XPS, UPS and HREELS study. Surf. Sci. 1987, 191, 367–384. [Google Scholar] [CrossRef]
  34. Tressaud, A.; Khairoun, S.; Touhara, H.; Watanabe, N. X-ray Photoelectron Spectroscopy of Palladium Fluorides. Z. Anorg. Allg. Chem. 2010, 540, 291–299. [Google Scholar] [CrossRef]
  35. Shafeev, G.A.; Themlin, J.M.; Bellard, L.; Marine, W.; Cros, A. enhanced adherence of areaselective electroless metal plating on insulators. J. Vac. Sci. Technol. A 1996, 14, 319–326. [Google Scholar] [CrossRef]
  36. Uno, T. Enhancing bondability with coated copper bonding wire. Microelectron. Reliab. 2011, 51, 88–96. [Google Scholar] [CrossRef]
  37. Zhang, B.; Qian, K.; Wang, T.; Cong, Y.; Wang, J. Behaviors of Palladium in Palladium coated copper wire bonding process. In Proceedings of the 2009 International Conference on Electronic Packaging Technology & High Density Packaging (ICEPT-HDP’09), Beijing, China, 10–13 August 2009. [Google Scholar]
  38. Koh, W.; Lee, T.-K.; Ng, H.-S.; Goh, K.-S.; Ho, H.-M. Investigation of palladium coverage on bonded balls of palladium-coated copper wires. In Proceedings of the 2011 12th International Conference on Electronic Packaging Technology and High Density Packaging, Shanghai, China, 8–11 August 2011; pp. 1–7. [Google Scholar]
  39. Rui, G.; Cheng, Y.; Mao, D.; Ming, L.; Chiu, H. Thermal reliability of Ag-8Au-3Pd alloy wire bonds. In Proceedings of the 2013 3rd IEEE CPMT Symposium Japan, Kyoto, Japan, 11–13 November 2013. [Google Scholar]
  40. Tura, J.M.; Regull, P.; Victori, L.; Castellar, M. XPS and IR (ATR) analysis of Pd oxide films obtained by electrochemical methods. Surf. Interface Anal. 1988, 11, 447–449. [Google Scholar] [CrossRef]
Figure 1. (a) Illustration of the cathodic passivation device. (b) Illustrations of the wire bond and the shear force test.
Figure 1. (a) Illustration of the cathodic passivation device. (b) Illustrations of the wire bond and the shear force test.
Materials 15 02355 g001
Figure 2. Comparison of the surface of the passivated silver alloy bonding wires in different solutions, before and after vulcanization for 20 and 60 min.
Figure 2. Comparison of the surface of the passivated silver alloy bonding wires in different solutions, before and after vulcanization for 20 and 60 min.
Materials 15 02355 g002
Figure 3. XPS spectra of the passivated silver plates in the Pd-free solution after storage for 5 days. (a) Survey spectra; (b) Ag3d spectra; (c) Cr2p spectra; (d) O1s spectra.
Figure 3. XPS spectra of the passivated silver plates in the Pd-free solution after storage for 5 days. (a) Survey spectra; (b) Ag3d spectra; (c) Cr2p spectra; (d) O1s spectra.
Materials 15 02355 g003
Figure 4. XPS spectra of the passivated silver plates in the Pd-containing solution after storage for 5 days. (a) Survey spectra; (b) Ag3d spectra; (c) Cr2p spectra; (d) O1s spectra; (e) Pd3d spectra.
Figure 4. XPS spectra of the passivated silver plates in the Pd-containing solution after storage for 5 days. (a) Survey spectra; (b) Ag3d spectra; (c) Cr2p spectra; (d) O1s spectra; (e) Pd3d spectra.
Materials 15 02355 g004
Figure 5. Cross-section images of the bonded wires on the pads before the shear force tests. (a) Untreated wire. (b) Wire passivated in the Pd-free solution. (c) Wire passivated in the Pd-containing solution.
Figure 5. Cross-section images of the bonded wires on the pads before the shear force tests. (a) Untreated wire. (b) Wire passivated in the Pd-free solution. (c) Wire passivated in the Pd-containing solution.
Materials 15 02355 g005
Figure 6. Bonding strength of the untreated silver alloy bonding wires and the silver alloy bonding wires passivated in different solutions.
Figure 6. Bonding strength of the untreated silver alloy bonding wires and the silver alloy bonding wires passivated in different solutions.
Materials 15 02355 g006
Figure 7. Fracture surface of the untreated and passivated silver alloy bonding wires in different solutions. (a) Untreated wire. (b) Wire passivated in the Pd-free solution. (c) Wire passivated in the Pd-containing solution.
Figure 7. Fracture surface of the untreated and passivated silver alloy bonding wires in different solutions. (a) Untreated wire. (b) Wire passivated in the Pd-free solution. (c) Wire passivated in the Pd-containing solution.
Materials 15 02355 g007
Table 1. Compositions of the silver alloy bonding wires.
Table 1. Compositions of the silver alloy bonding wires.
ElementAg (%)Fe (ppm)Pd (ppm)Mg (ppm)Si (ppm)
Content≥99≤5≤1≤2≤1
Table 2. Bonding parameters for the silver bonding wires.
Table 2. Bonding parameters for the silver bonding wires.
Parameters1st Bond2nd Bond
Bonding time (ms)1414
Power (mW)5580
Pressure (gf)2440
Bonding temperature (°C)150150
Electronic flame-off current (mA)280
Electronic flame-off time (μs)5300
Table 3. Relative atomic concentrations of different metallic species on the surfaces of the passivated Ag plates.
Table 3. Relative atomic concentrations of different metallic species on the surfaces of the passivated Ag plates.
TreatmentConcentrations (in at. %)
AgCr(OH)3Cr2O3Pd
Passivated in Pd-free solution68.8%16.4%9.2%-
Passivated in Pd-containing solution62.3%13.5%8.4%15.8%
Table 4. Measured contact angles of the bonded wires on the pads.
Table 4. Measured contact angles of the bonded wires on the pads.
Wire Treatment TypeContact Angle (°)
MaximumMinimumMeanStandard Error
Untreated113931048
Passivated in Pd-free solution 15710413616
Passivated in Pd-containing solution120941088
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Yang, G.; Zhou, Z.; Zhang, H.; Zhang, Y.; Peng, Z.; Gong, P.; Wang, X.; Cui, C. Improved Anti-Vulcanization and Bonding Performance of a Silver Alloy Bonding Wire by a Cathodic Passivation Treatment with Palladium. Materials 2022, 15, 2355. https://doi.org/10.3390/ma15072355

AMA Style

Yang G, Zhou Z, Zhang H, Zhang Y, Peng Z, Gong P, Wang X, Cui C. Improved Anti-Vulcanization and Bonding Performance of a Silver Alloy Bonding Wire by a Cathodic Passivation Treatment with Palladium. Materials. 2022; 15(7):2355. https://doi.org/10.3390/ma15072355

Chicago/Turabian Style

Yang, Guannan, Zhiqiang Zhou, Haide Zhang, Yu Zhang, Zhen Peng, Pan Gong, Xin Wang, and Chengqiang Cui. 2022. "Improved Anti-Vulcanization and Bonding Performance of a Silver Alloy Bonding Wire by a Cathodic Passivation Treatment with Palladium" Materials 15, no. 7: 2355. https://doi.org/10.3390/ma15072355

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop