SnO2 Nanoflower–Nanocrystalline Cellulose Composites as Anode Materials for Lithium-Ion Batteries

One of the biggest challenges in the commercialization of tin dioxide (SnO2)-based lithium-ion battery (LIB) electrodes is the volume expansion of SnO2 during the charge–discharge process. Additionally, the aggregation of SnO2 also deteriorates the performance of anode materials. In this study, we prepared SnO2 nanoflowers (NFs) using nanocrystalline cellulose (CNC) to improve the surface area, prevent the particle aggregation, and alleviate the change in volume of LIB anodes. Moreover, CNC served not only as the template for the synthesis of the SnO2 NFs but also as a conductive material, after annealing the SnO2 NFs at 800 °C to improve their electrochemical performance. The obtained CNC–SnO2NF composite was used as an active LIB electrode material and exhibited good cycling performance and a high initial reversible capacity of 891 mA h g−1, at a current density of 100 mA g−1. The composite anode could retain 30% of its initial capacity after 500 charge–discharge cycles.


Introduction
Over the past few years, metal oxides have attracted a great deal of attention as anode materials for rechargeable lithium-ion batteries (LIBs), owing to their high capacity, excellent rate capacity, and safety [1,2]. Among the various transition metal oxides used in LIBs, tin dioxide (SnO 2 ) has been extensively investigated owing to its high theoretical capacity and unique properties. Furthermore, the synthesis procedures for SnO 2 are cost-effective, facile, and achievable in environmentally benign conditions [3][4][5].

Preparation of CNC-SnO 2 NF Composites
First, certain amounts of SnCl 2 ·2H 2 O (0.1128 g) and C 6 H 5 Na 3 O 7 ·2H 2 O (0.2941 g) were dissolved in an 80 mL ethanol-deionized (DI) water solution. The resulting suspension was stirred continuously for 1 h. Then, 0.1 g CNC was added to the mixture, which was vigorously stirred for 0.5 h, and the resulting solution was then transferred to a 100 mL stainless steel autoclave. After heating at 180 • C for 8 h, the autoclave was naturally cooled to room temperature. The obtained sample was washed with DI water by centrifugation at 8000 rpm for 10 min. The powder samples were then annealed at 500 and 800 • C for 2 h under a nitrogen atmosphere. The final composite products obtained after annealing at 500 and 800 • C were labeled as CNC-SnO 2 NF500 and CNC-SnO 2 NF800, respectively.

Material Characterization
The structures and morphologies of the obtained composite materials were observed using scanning electron microscopy (SEM, S-4700, Hitachi Ltd., Tokyo, Japan). Transmission electron microscopy (TEM) analysis was carried out on a FEI Tecnai F30S-Twin transmission electron microscope, (Tecnai, F30S-Twin, Hillsboro, OR, USA). The X-ray diffraction (XRD) analysis of the obtained composite materials was carried out on a diffractometer (Rigaku/Smartlab, Tokyo, Japan) (40 kV, 30 mA X-Ray generator) at the Smart Materials Research Center for IoT, at Gachon University. The XRD patterns of the composites were recorded over the 2θ range of 10 • -80 • at a scanning rate of 1.0 • min −1 . The diffractometer was equipped with a Kβ filter for Cu. The Raman spectra of the composites were recorded on a micro-Raman instrument (Monora500i, ANDOR, Belfast, Northern Ireland) equipped with a 533 nm He-Ne laser (12 mW). Thermogravimetric analysis (TGA) was conducted in air at a heating rate of 10 • C min −1 .

Electrochemical Characterization
Electrochemical tests were carried out with CR2032-type coin cells. The working electrodes (mass load 0.088 mg/cm 2 ) were prepared by compressing slurries comprising 70 wt % active materials, 15 wt % Super P, 15 wt % polyvinylidene fluoride, and N-methyl pyrrolidone onto a copper foil (r = 0.6 cm). The electrodes were dried at 70 • C for 24 h in a vacuum oven and the cells were assembled in an argon-filled glove box. A polyethylene membrane and lithium foil were used as the separator and counter electrode, respectively. A solution of 1 M LiPF 6 in ethylene carbonate/diethylene carbonate (1:1 in volume) was used as the electrolyte. Charge and discharge experiments were carried out over the potential range of 0.01-2.0 V (vs Li/Li + ) at a constant current density of 100 mA g −1 with a battery cycler (WBCS3000, WonAtech, Seoul, Korea) system. Figure 1a shows the XRD patterns of CNC and the CNC-SnO 2 NF composites. The CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composites showed peaks characteristic of SnO 2 along with graphitic peaks. In the case of CNC, the peaks at 2θ = 19.8 • and 22.6 • could be indexed to ICSD data, PDF #03-0289 (native cellulose) and PDF #03-0228 (cellulose), respectively, and in agreement with the report from SK innovation. The presence of SnO 2 in the CNC-SnO 2 NF composites was confirmed by the peaks observed at around 2θ = 26.8 • , 34.1 • , 38.1 • , and 51.8 • corresponding to the (110), (101), (200), and (211) planes of SnO 2 , respectively (ICSD PDF 21-1250). Additionally, the peak corresponding to the (002) plane of CNC, which was observed in the XRD patterns of the CNC and CNC-SnO 2 NF500 samples, could not be observed in the XRD pattern of the CNC-SnO 2 NF800 composite. This indicates that CNC was successfully pyrolyzed [21,26,27], which is further confirmed by the Raman spectrum, as shown below. In the case of the composite materials, the graphitic carbon (002) peak overlapped the (110) peak of SnO 2 . Moreover, the (110), (101), (200), and (211) peaks shifted toward the right and became more intense and sharper in the case of CNC-SnO 2 NF800, indicating the high purity and crystallization of the composite.

Results and Discussion
To further examine the structure of the CNC-SnO 2 NF composites, their Raman spectrum was recorded over the wavenumber range of 500-2000 cm −1 (Figure 1b). CNC-SnO 2 NF800 composites showed the D-band peak at~1369 cm −1 and the G-band peak at~1594 cm −1 , while CNC-SnO 2 NF500 exhibited the D-band peak at~1361 cm −1 and the G-band peak at~1591 cm −1 , corresponding to the disordered and graphitic carbon atoms, respectively. These indicated the presence of the carbon formed by the pyrolysis of CNC in the CNC-SnO 2 NF composite and were consistent with previous reports [20,28,29]. The composite showed sharp D and G-band peaks because of the high carbonization temperature. Moreover, the sharpness of the D and G-band peaks and the I G /I D intensity ratio increased with an increase in the pyrolysis temperature. This was consistent with the results reported previously [30,31]. In addition, the peaks observed at around 600-750 cm −1 corresponded to the Sn-O bonds in the SnO 2 NFs [32]. This further confirmed the presence of SnO 2 NFs in the composites. In order to quantitatively determine the carbon content for CNC and CNC-SnO 2 NF800, thermogravimetric analysis (TGA) was implemented and Figure 1c shows the TGA profiles of the CNC and CNC-SnO 2 NF800 nanocomposites. The CNC exhibited weight loss mainly in the temperature range of 250-400 • C, and for CNC-SnO 2 NF800, the weight loss between 400 and 750 • C corresponded to pyrolysis of the CNC. The final residual weight of 38% was obtained for the final SnO 2 NFs and pyrolyzed CNC. Therefore, the mass percentage of the final pyrolyzed CNC can be calculated at 21% in the electrode. To further examine the structure of the CNC-SnO2NF composites, their Raman spectrum was recorded over the wavenumber range of 500-2000 cm −1 (Figure 1b). CNC-SnO2NF800 composites showed the D-band peak at ~1369 cm −1 and the G-band peak at ~1594 cm −1 , while CNC-SnO2NF500 exhibited the D-band peak at ~1361 cm −1 and the G-band peak at ~1591 cm −1 , corresponding to the disordered and graphitic carbon atoms, respectively. These indicated the presence of the carbon formed by the pyrolysis of CNC in the CNC-SnO2NF composite and were consistent with previous reports [20,28,29]. The composite showed sharp D and G-band peaks because of the high carbonization temperature. Moreover, the sharpness of the D and G-band peaks and the IG/ID intensity ratio increased with an increase in the pyrolysis temperature. This was consistent with the results reported previously [30,31]. In addition, the peaks observed at around 600-750 cm −1 corresponded to the Sn-O bonds in the SnO2 NFs [32]. This further confirmed the presence of SnO2 NFs in the composites. In order to quantitatively determine the carbon content for CNC and CNC-SnO2NF800, thermogravimetric analysis (TGA) was implemented and Figure 1c shows the TGA profiles of the CNC and CNC-SnO2NF800 nanocomposites. The CNC exhibited weight loss mainly in the temperature range of 250-400 °C, and for CNC-SnO2NF800, the weight loss between 400 and 750 °C corresponded to pyrolysis of the CNC. The final residual weight of 38% was obtained for the final SnO2 NFs and pyrolyzed CNC. Therefore, the mass percentage of the final pyrolyzed CNC can be calculated at 21% in the electrode.
The nanostructures and morphologies of the CNC-SnO2NF composites were examined using SEM and TEM. The SEM images of CNC-SnO2NF500, CNC-SnO2NF800, CNC, and CNC-SnO2NF are shown in Figure 2a-d, respectively. As can be observed from Figure 2a,b, both the CNC- The nanostructures and morphologies of the CNC-SnO 2 NF composites were examined using SEM and TEM. The SEM images of CNC-SnO 2 NF500, CNC-SnO 2 NF800, CNC, and CNC-SnO 2 NF are shown in Figure 2a-d, respectively. As can be observed from Figure 2a,b, both the CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composites showed a uniform flower-like structure consisting of SnO 2 nanosheets. However, the composite annealed at 800 • C showed more nanosheets and aggregation than that annealed at 500 • C. The magnified image shown in the inset of Figure 2b shows the highly porous surface and flower-like structure of the CNC-SnO 2 NF800 composite. Figure 2c shows a typical SEM image of the CNC film with a heterogeneous surface. In the case of CNC-SnO 2 NF, the SnO 2 NFs were uniformly distributed on the surface of CNC (Figure 2d). Compared with the CNC film, the CNC-SnO 2 NF film showed a porous surface, and hence showed improved electrode performance.
The structure of the CNC-SnO 2 NF was further examined using TEM and high-resolution TEM (HRTEM), as shown in Figure 3a-f. Both the CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composites showed uniformly distributed SnO 2 NFs, as can be observed from Figure 3a,d, respectively. The SnO 2 NFs were highly crystalline, with an average particle size of 8-10 nm. Moreover, the magnified HRTEM images in Figure 3b,e show the lattice fringes of the CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composites, respectively. As can be observed from Figure 3b, the lattice parameter of the CNC-SnO 2 NF500 composite was 0.293 nm, while that of the CNC-SnO 2 NF800 composite was 0.267 nm (Figure 3e), corresponding to the (110) and (101) lattice planes of SnO 2 nanoparticles. These results indicate that the CNC-SnO 2 NF800 nanocomposite showed better uniformity and crystallization and had a smaller nanosheet size than the CNC-SnO 2 NF500 composite. This is consistent with the XRD results. In addition, Figure 3c,f shows the low-magnification TEM images of the CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composites, respectively. Both of the images reveal that the SnO 2 NFs were uniformly distributed in the CNC layers, and the CNC-SnO 2 composites showed SnO 2 NF aggregation. These results are consistent with the SEM results. These results indicate that the SnO 2 NFs were successfully coated onto the CNC layer, and improved the electrochemical performance of the composite anodes.
Materials 2020, 13, x FOR PEER REVIEW 5 of 12 SnO2NF500 and CNC-SnO2NF800 composites showed a uniform flower-like structure consisting of SnO2 nanosheets. However, the composite annealed at 800 °C showed more nanosheets and aggregation than that annealed at 500 °C. The magnified image shown in the inset of Figure 2b shows the highly porous surface and flower-like structure of the CNC-SnO2NF800 composite. Figure 2c shows a typical SEM image of the CNC film with a heterogeneous surface. In the case of CNC-SnO2NF, the SnO2 NFs were uniformly distributed on the surface of CNC (Figure 2d). Compared with the CNC film, the CNC-SnO2NF film showed a porous surface, and hence showed improved electrode performance. The structure of the CNC-SnO2NF was further examined using TEM and high-resolution TEM (HRTEM), as shown in Figure 3a-f. Both the CNC-SnO2NF500 and CNC-SnO2NF800 composites showed uniformly distributed SnO2 NFs, as can be observed from Figure 3a,d, respectively. The SnO2 NFs were highly crystalline, with an average particle size of 8-10 nm. Moreover, the magnified HRTEM images in Figure 3b,e show the lattice fringes of the CNC-SnO2NF500 and CNC-SnO2NF800 composites, respectively. As can be observed from Figure 3b, the lattice parameter of the CNC-SnO2NF500 composite was 0.293 nm, while that of the CNC-SnO2NF800 composite was 0.267 nm (Figure 3e), corresponding to the (110) and (101) lattice planes of SnO2 nanoparticles. These results indicate that the CNC-SnO2NF800 nanocomposite showed better uniformity and crystallization and had a smaller nanosheet size than the CNC-SnO2NF500 composite. This is consistent with the XRD results. In addition, Figure 3c,f shows the low-magnification TEM images of the CNC-SnO2NF500 and CNC-SnO2NF800 composites, respectively. Both of the images reveal that the SnO2 NFs were uniformly distributed in the CNC layers, and the CNC-SnO2 composites showed SnO2 NF aggregation. These results are consistent with the SEM results. These results indicate that the SnO2 NFs were successfully coated onto the CNC layer, and improved the electrochemical performance of the composite anodes. The CNC-SnO2NF (CNC-SnO2NF500 and CNC-SnO2NF800) composites were used as LIB anodes. The charge-discharge capacity curves of the composite anodes, at a current density of 100 mA g −1 , are shown in Figure 4a,b. SnO2 and CNC exhibited theoretical capacities of 1490 mA h g −1 and 360 mA h g −1 , respectively. Therefore, the CNC-SnO2NF500 and CNC-SnO2NF800 composites showed different charge-discharge capacities because of the differences in their annealing temperatures and structures. Figure 4a shows the cycle performance properties of the CNC-SnO2NF500 composite electrode. The initial discharge capacity, charge capacity, and initial Coulomb The CNC-SnO 2 NF (CNC-SnO 2 NF500 and CNC-SnO 2 NF800) composites were used as LIB anodes. The charge-discharge capacity curves of the composite anodes, at a current density of 100 mA g −1 , are shown in Figure 4a,b. SnO 2 and CNC exhibited theoretical capacities of 1490 mA h g −1 and 360 mA h g −1 , respectively. Therefore, the CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composites showed different charge-discharge capacities because of the differences in their annealing temperatures and structures. Figure 4a shows the cycle performance properties of the CNC-SnO 2 NF500 composite electrode. The initial discharge capacity, charge capacity, and initial Coulomb efficiency (ICE) of the electrode were 1391 mA h g −1 , 726 mA h g −1 , and 52.21%, respectively. On the other hand, the initial discharge capacity, charge capacity, and ICE of the CNC-SnO 2 NF800 composite electrode were 1752 mA h g −1 , 891 mA h g −1 , and 50.84%, respectively (Figure 4b). The first discharge capacities of both of the electrodes were higher than the theoretical capacities of SnO 2 and CNC for the following reasons: (1) the formation of solid-electrolyte interface (SEI) layers on the surface and the decomposition of electrolyte during the first discharge process, leading to an increase in the irreversible capacity of the electrodes; (2) the carbon content of nanocellulose after pyrolysis in nanocomposites; (3) tiny vacancies existing between the SnO 2 and nanocellulose that can buffer the SnO 2 volume expansion, which could be seen in the SEM and HRTEM results; and (4) the constitution of a space charge layer comprised of lithium ions at the interface between the lithium salt and metal particles [7,28,33,34]. The initial Coulombic efficiencies of the nanocomposites were 52.21% and 50.84% for CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composites, respectively, which were very close to the theoretical values. The composite annealed at 800 • C exhibited a higher initial discharge capacity (1752/1391 mA h g −1 ) and charge capacity (891/726 mA h g −1 ) than that annealed at 500 • C. These results are consistent with the XRD and TEM results. Furthermore, the CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composites showed similar cycling performance and Coulombic efficiency after 500 cycles. The capacities of both of the electrodes decreased rapidly in the first 50 cycles, decreased slightly in the next 150 cycles, and remained constant after 200 cycles. The electrodes could retain 30% of their initial capacity after 500 cycles. This can be attributed to the collapse of the SnO 2 NF structure because of the volume change during the charge-discharge processes, which further decreased the reversible capacity of the electrode. Compared with the CNC-SnO 2 NF500 electrode, the CNC-SnO 2 NF800 electrode exhibited improved cyclic stability and electrochemical performance. After 500 cycles, the reversible capacity of the CNC-SnO 2 NF800 electrode was 267 mA h g −1 , which is higher than that of the CNC-SnO 2 NF500 composite (158 mA h g −1 ). This is consistent with previously reported results [21], according to which the performance of CNC-SnO 2 -based LIB anodes improves with an increase in the CNC pyrolysis temperature, and the conductivity of CNC can increase the capacity of CNC-SnO 2 composite materials.
Materials 2020, 13, x FOR PEER REVIEW 7 of 12 decreased the reversible capacity of the electrode. Compared with the CNC-SnO2NF500 electrode, the CNC-SnO2NF800 electrode exhibited improved cyclic stability and electrochemical performance. After 500 cycles, the reversible capacity of the CNC-SnO2NF800 electrode was 267 mA h g −1 , which is higher than that of the CNC-SnO2NF500 composite (158 mA h g −1 ). This is consistent with previously reported results [21], according to which the performance of CNC-SnO2-based LIB anodes improves with an increase in the CNC pyrolysis temperature, and the conductivity of CNC can increase the capacity of CNC-SnO2 composite materials. The rate capability and cyclability of the composite, with the discharge-charge capacity at different current densities from 300 to 1000 mA g −1 , was obtained for the CNC-SnO2NF800 sample, and the results are shown in Figure 5. The rate performance experiment was carried out by using the LIB cell after 500 cycles at a current density of 100 mA g −1 . The average reversible discharge capacities at 300, 500, and 1000 mA g −1 for the CNC-SnO2NF800 nanocomposites were 261.9, 197.2, and 187.3 mA h g −1 , respectively. When the specific current was retained at 300 mA g −1 , a capacity of 209.4 mA h g −1 was achieved, demonstrating good rate performance. Comparatively, with CNC-SnO2NF800 nanocomposites, at a discharge capacity of 267.1 mA h g −1 , a current density of 100 mA g −1 , and after The rate capability and cyclability of the composite, with the discharge-charge capacity at different current densities from 300 to 1000 mA g −1 , was obtained for the CNC-SnO 2 NF800 sample, and the results are shown in Figure 5. The rate performance experiment was carried out by using the LIB cell after 500 cycles at a current density of 100 mA g −1 . The average reversible discharge capacities at 300, 500, and 1000 mA g −1 for the CNC-SnO 2 NF800 nanocomposites were 261.9, 197.2, and 187.3 mA h g −1 , respectively. When the specific current was retained at 300 mA g −1 , a capacity of 209.4 mA h g −1 was achieved, demonstrating good rate performance. Comparatively, with CNC-SnO 2 NF800 nanocomposites, at a discharge capacity of 267.1 mA h g −1 , a current density of 100 mA g −1 , and after 500 cycles, the composite material showed stable cycling properties at different current densities. The rate capability and cyclability of the composite, with the discharge-charge capacity at different current densities from 300 to 1000 mA g −1 , was obtained for the CNC-SnO2NF800 sample, and the results are shown in Figure 5. The rate performance experiment was carried out by using the LIB cell after 500 cycles at a current density of 100 mA g −1 . The average reversible discharge capacities at 300, 500, and 1000 mA g −1 for the CNC-SnO2NF800 nanocomposites were 261.9, 197.2, and 187.3 mA h g −1 , respectively. When the specific current was retained at 300 mA g −1 , a capacity of 209.4 mA h g −1 was achieved, demonstrating good rate performance. Comparatively, with CNC-SnO2NF800 nanocomposites, at a discharge capacity of 267.1 mA h g −1 , a current density of 100 mA g −1 , and after 500 cycles, the composite material showed stable cycling properties at different current densities.  The rate performance at different current densities of CNC-SnO 2 NF800 composite electrodes between 0.01 and 2 V. The rate performance experiment was carried out by using the lithium-ion battery (LIB)'s cell after 500 cycles at a current density of 100 mA g −1 . Figure 6a,b show the typical charge and discharge capacities of the CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composite electrodes during the first, second, and third cycles over the potential range of 0.01-2.5 V (Li/Li + ), at a current density of 100 mA g −1 . The CNC-SnO 2 NF500 electrode showed a first discharge-charge capacity of 1391/726 mA h g −1 with a low ICE of 52% because of the decomposition of the electrolyte and the generation of the SEI layer. The CNC-SnO 2 NF800 composite showed a first discharge-charge capacity of 1752/891 mA h g −1 , corresponding to an initial ICE of 50%. The electrodes exhibited a large irreversible capacity loss during the first cycle owing to the material properties of SnO 2 . This is a common phenomenon in LIBs [1][2][3]35]. Furthermore, the discharge-charge curves changed slightly with an increase in the number of cycles. The curve shape remained the same during the second and third cycles, indicating that the composite electrodes exhibited stable cyclic performance from the second cycle onwards.
Materials 2020, 13, x FOR PEER REVIEW 8 of 12 Figure 6a,b show the typical charge and discharge capacities of the CNC-SnO2NF500 and CNC-SnO2NF800 composite electrodes during the first, second, and third cycles over the potential range of 0.01-2.5 V (Li/Li + ), at a current density of 100 mA g −1 . The CNC-SnO2NF500 electrode showed a first discharge-charge capacity of 1391/726 mA h g −1 with a low ICE of 52% because of the decomposition of the electrolyte and the generation of the SEI layer. The CNC-SnO2NF800 composite showed a first discharge-charge capacity of 1752/891 mA h g −1 , corresponding to an initial ICE of 50%. The electrodes exhibited a large irreversible capacity loss during the first cycle owing to the material properties of SnO2. This is a common phenomenon in LIBs [1][2][3]35]. Furthermore, the dischargecharge curves changed slightly with an increase in the number of cycles. The curve shape remained the same during the second and third cycles, indicating that the composite electrodes exhibited stable cyclic performance from the second cycle onwards.  Figure 7 shows the differential capacity plots of the CNC-SnO2NF500 and CNC-SnO2NF800 composite electrodes for the first three cycles over the potential range of 0.001-2.00 V. The differential capacities of the electrodes in the second and third cycles were significantly different from those in the first cycle. The curves indicated the occurrence of typical oxidation and reduction electrochemical  Figure 7 shows the differential capacity plots of the CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composite electrodes for the first three cycles over the potential range of 0.001-2.00 V. The differential capacities of the electrodes in the second and third cycles were significantly different from those in the first cycle. The curves indicated the occurrence of typical oxidation and reduction electrochemical processes. The first-cycle curve of CNC-SnO 2 NF500 (Figure 7a) showed two reduction peaks at 0.51 and 1.2 V, attributable to the Sn oxidation (SnO 2 + 4Li + + 4e − = Sn + 2Li 2 O) process. The reduction peaks at around 0.2, 0.3-0.4, and 0.7 V can be ascribed to the lithiation (Li x Sn) of Sn (Sn + xLi + xe − = Li x Sn (0 ≤ x ≤ 4.4)). Over the potential range of 0.001-2.0 V, the CNC-SnO 2 NF800 (Figure 7b) and CNC-SnO 2 NF500 electrodes showed similar differential capacity curves. The first-cycle differential capacity curves of the CNC-SnO 2 NF800 and CNC-SnO 2 NF500 electrodes showed clear redox peaks at (0.2 V, 0.5 V) and (0.75 V, 1.32 V). The first redox pair corresponds to the alloy-dealloy process (Li x Sn → Sn + xLi + + xe − ) and the formation of the SEI films. The other pair can be attributed to the formation of SnOx by the conversion reaction (Sn/SnO + Li 2 O → SnO/SnO 2 + 2Li + + 2e − ). Moreover, the differential capacity curves of the second and third cycles overlapped in the case of CNC-SnO 2 NF800 electrodes (Figure 7b), indicating the stability of its reversible capacities. However, a shift on the discharge peak is clearly observed in Figure 7a during the second and third cycles, which revealed unstable reversibility of the electrochemical reactions in the case of the CNC-SnO 2 NF500 electrode. These results are also consistent with the initial voltage profiles and cyclic performances. For comparison, the electrochemical properties of CNC film pyrolyzed at 800 °C were investigated. The cycling performance and initial voltage profiles of the pyrolyzed CNC are shown in Figure 8. Figure 8a shows the cycle performance of the pyrolyzed CNC electrode for 300 cycles. The CNC-SnO2NF800 composite (Figures 4b and 6b) showed significantly improved initial discharge (1752/237 mA h g −1 ) and charge capacities (891/234 mA h g −1 ) during 300 cycles, as compared with the pyrolyzed CNC film. After 200 cycles, the CNC-SnO2NF800 electrode showed a higher reversible capacity (339 mA h g −1 ) than the pyrolyzed CNC electrode (274 mA h g −1 ). However, the capacity of the pyrolyzed CNC electrode (Figure 8a) showed an increasing trend, and remained stable during 300 cycles, while that of the CNC-SnO2NF800 electrode decreased rapidly during the first 100 cycles and showed a capacity of 284 mA h g −1 , similar to that of the pyrolyzed CNC electrode after 300 cycles (276 mA h g −1 ). In addition, the pyrolyzed CNC electrode's capacity loss after the first cycle at 100 mA g −1 (Figure 8b) was lower than that of the CNC-SnO2NF800 composite electrode (Figure 6b). These results suggest that SnO2 cannot maintain the material structure of SnO2-based LIB electrodes because of its volume change during the charging-discharging processes. In addition, in the cycling process, the capacity of SnO2-based anode material starts to drop rapidly and has almost no capacity after 50 cycles, as shown in many previous reports [20,[35][36][37]. Thus, the excellent performance of the CNC-SnO2NF500 and CNC-SnO2NF800 composite electrodes can only be attributed to the presence of pyrolyzed CNC. For comparison, the electrochemical properties of CNC film pyrolyzed at 800 • C were investigated. The cycling performance and initial voltage profiles of the pyrolyzed CNC are shown in Figure 8. Figure 8a shows the cycle performance of the pyrolyzed CNC electrode for 300 cycles. The CNC-SnO 2 NF800 composite (Figures 4b and 6b) showed significantly improved initial discharge (1752/237 mA h g −1 ) and charge capacities (891/234 mA h g −1 ) during 300 cycles, as compared with the pyrolyzed CNC film. After 200 cycles, the CNC-SnO 2 NF800 electrode showed a higher reversible capacity (339 mA h g −1 ) than the pyrolyzed CNC electrode (274 mA h g −1 ). However, the capacity of the pyrolyzed CNC electrode (Figure 8a) showed an increasing trend, and remained stable during 300 cycles, while that of the CNC-SnO 2 NF800 electrode decreased rapidly during the first 100 cycles and showed a capacity of 284 mA h g −1 , similar to that of the pyrolyzed CNC electrode after 300 cycles (276 mA h g −1 ). In addition, the pyrolyzed CNC electrode's capacity loss after the first cycle at 100 mA g −1 (Figure 8b) was lower than that of the CNC-SnO 2 NF800 composite electrode (Figure 6b). These results suggest that SnO 2 cannot maintain the material structure of SnO 2 -based LIB electrodes because of its volume change during the charging-discharging processes. In addition, in the cycling process, the capacity of SnO 2 -based anode material starts to drop rapidly and has almost no capacity after 50 cycles, as shown in many previous reports [20,[35][36][37]. Thus, the excellent performance of the CNC-SnO 2 NF500 and CNC-SnO 2 NF800 composite electrodes can only be attributed to the presence of pyrolyzed CNC.
(276 mA h g −1 ). In addition, the pyrolyzed CNC electrode's capacity loss after the first cycle at 100 mA g −1 (Figure 8b) was lower than that of the CNC-SnO2NF800 composite electrode (Figure 6b). These results suggest that SnO2 cannot maintain the material structure of SnO2-based LIB electrodes because of its volume change during the charging-discharging processes. In addition, in the cycling process, the capacity of SnO2-based anode material starts to drop rapidly and has almost no capacity after 50 cycles, as shown in many previous reports [20,[35][36][37]. Thus, the excellent performance of the CNC-SnO2NF500 and CNC-SnO2NF800 composite electrodes can only be attributed to the presence of pyrolyzed CNC. To further confirm the structural stability of the CNC-SnO2NF800 composite, SEM images of it after 200 cycles were obtained ( Figure 9). The SEM images of the electrode before and after cycling (200 cycles) are shown in Figure 9a,b, respectively. It can be observed from the images that the To further confirm the structural stability of the CNC-SnO 2 NF800 composite, SEM images of it after 200 cycles were obtained ( Figure 9). The SEM images of the electrode before and after cycling (200 cycles) are shown in Figure 9a,b, respectively. It can be observed from the images that the electrode could not maintain the SnO 2 NF structure, and showed particle aggregation after 200 cycles. However, the SnO 2 NFs did not collapse completely, and the material network structure could be observed even after cycling. SnO 2 NFs often tended to be highly aggregated because of their high surface energy and magnetic dipole interaction. Thus, CNC can cover and separate SnO 2 NFs, in combination with the dispersion effect, to reduce the aggregation. The negatively charged surface of CNC can also improve the dispersion and colloidal stability of nanoparticles during cycling, which can be clearly observed from the SEM and TEM images. Therefore, the CNC-incorporated conductive network, which prevented the aggregation and transformation of the SnO 2 NFs during the charge-discharge processes, should be further optimized.
Materials 2020, 13, x FOR PEER REVIEW 10 of 12 electrode could not maintain the SnO2 NF structure, and showed particle aggregation after 200 cycles. However, the SnO2 NFs did not collapse completely, and the material network structure could be observed even after cycling. SnO2 NFs often tended to be highly aggregated because of their high surface energy and magnetic dipole interaction. Thus, CNC can cover and separate SnO2 NFs, in combination with the dispersion effect, to reduce the aggregation. The negatively charged surface of CNC can also improve the dispersion and colloidal stability of nanoparticles during cycling, which can be clearly observed from the SEM and TEM images. Therefore, the CNC-incorporated conductive network, which prevented the aggregation and transformation of the SnO2 NFs during the chargedischarge processes, should be further optimized.

Conclusions
In summary, we successfully prepared CNC-SnO2NF composites, which showed excellent electrochemical performance as LIB electrodes. CNC not only prevented the agglomeration and change in volume of the SnO2 NFs, but also served as a conducting base after high-temperature annealing of the SnO2 NFs. Moreover, the CNC structure enhanced the discharge-charge capacity and cycling performance of the SnO2 NFs during the cycling process. In addition, the CNC-SnO2NF800 composite showed an initial discharge capacity of 1752 mA h g −1 , and maintained a stable discharge capacity of 267 mA h g −1 after 500 cycles at 100 mA g −1 . The low-cost, lightweight, flexible, and environmentally favorable properties of CNC enable it to become an ideal green, non-toxic, and effective protectant, or dispersant matrix, in the development of metal oxide-nanocellulose composites, possibly applicable to advanced electrodes for LIBs. In particular, the properties of CNC may be utilized for a freestanding electrode in the future.

Conclusions
In summary, we successfully prepared CNC-SnO 2 NF composites, which showed excellent electrochemical performance as LIB electrodes. CNC not only prevented the agglomeration and change in volume of the SnO 2 NFs, but also served as a conducting base after high-temperature annealing of the SnO 2 NFs. Moreover, the CNC structure enhanced the discharge-charge capacity and cycling performance of the SnO 2 NFs during the cycling process. In addition, the CNC-SnO 2 NF800 composite showed an initial discharge capacity of 1752 mA h g −1 , and maintained a stable discharge capacity of 267 mA h g −1 after 500 cycles at 100 mA g −1 . The low-cost, lightweight, flexible, and environmentally favorable properties of CNC enable it to become an ideal green, non-toxic, and effective protectant, or dispersant matrix, in the development of metal oxide-nanocellulose composites, possibly applicable to advanced electrodes for LIBs. In particular, the properties of CNC may be utilized for a freestanding electrode in the future.