Fabrication of TiB2–Al1050 Composites with Improved Microstructural and Mechanical Properties by a Liquid Pressing Infiltration Process

This study was conducted on titanium diboride (TiB2) reinforced Al metal matrix composites (MMCs) with improved properties using a TiB2 and aluminum (Al) 1050 alloy. Al composites reinforced with fine TiB2 at volume ratios of more than 60% were successfully fabricated via the liquid pressing infiltration (LPI) process, which can be used to apply gas pressure at a high temperature. The microstructure of the TiB2–Al composite fabricated at 1000 °C with pressurization of 10 bar for 1 h showed that molten Al effectively infiltrated into the high volume-fraction TiB2 preform due to the improved wettability and external gas pressurization. In addition, the interface of TiB2 and Al not only had no cracks or pores but also had no brittle intermetallic compounds. In conclusion, TiB2–Al composite, which has a sound microstructure without defects, has improved mechanical properties, such as hardness and strength, due to effective load transfer from the Al matrix to the fine TiB2 reinforcement.


Introduction
The demand for lightweight materials with specific performances for such applications as automobiles, aerospace technology, and armor, has gradually increased. Many studies on aluminum matrix composites (AMCs) have been conducted, because AMCs fabricated by adding ceramic reinforcements, such as silicon carbide (SiC) [1], alumina (Al 2 O 3 ) [2], boron carbide (B 4 C) [3], titanium carbide (TiC) [4], titanium diboride (TiB 2 ) [5], and hybrid [6] to an aluminum (Al) matrix, have excellent mechanical properties while maintaining low densities. Among the many ceramic reinforcements used in the fabrication of AMCs, TiB 2 is a very attractive reinforcement due to its superior Young's modulus [7], excellent hardness [8], and chemical stability with Al [9].
Most of the processes used in recent decades in the manufacturing of metal matrix composites (MMCs) are ex-situ methods in which reinforcement materials are added from the outside to the base material. Compared to in-situ methods, ex-situ processes make it easier to control the volume ratio of reinforcements and are advantageous in terms of cost and productivity. However, ex-situ methods have a limitation in that, because the reinforcement is physically bonded to the base, the interface between the reinforcement and the base is unstable [7,10,11]. Therefore, many researchers have implemented additional processes to compensate for interface defects, the main disadvantage

Materials and Methods
To optimize the experimental conditions before fabricating the TiB 2 -Al composites, the sessile drop method was used to measure the contact angle between Al and TiB 2 by dropping molten Al on a TiB 2 plate (20 × 20 × 2 mm 3 ) at 700-1000 • C under vacuum. Al1050 alloy (Portland Aluminum, Portland, Australia) was selected as the matrix material to minimize the effects of additive elements. The chemical composition of Al1050 is expressed in Table 1. Composition 99.8% ≥ 0.1% ≤ 0.001% ≤ 0.001% ≤ 0.02% ≤ 0.05% ≤ 0.04% ≤ 0.02% ≤ 0.002% ≤ TiB 2 powders (Kojundo Chemical Laboratory Co., Ltd., Saitama, Japan) with an average particle size of 2-3 µm were used as the reinforcement. TiB 2 powders were compressed under a uniaxial pressure of 80 MPa, and were sintered at 1000 • C for 60 min under argon atmosphere to fabricate a porous TiB 2 preform with a diameter of 50 mm and a height of 20 mm. The porosity of the fabricated TiB 2 preform was calculated by measuring the volume and weight of the preform. TiB 2 -Al composites were fabricated by the LPI process, which was developed to infiltrate molten metal into a ceramic preform via hydrostatic pressure, which leads to a uniform dispersion of reinforcement inside the metal matrix [20]. The TiB 2 preform and Al1050 were inserted into a magnesium oxide (MgO) crucible and heated to 1000 • C at a heating rate of 10 • C/min in a vacuum atmosphere (2.8 × 10 −1 torr). After holding for 1 h at the target temperature, 10 bar of argon gas was injected to assist infiltration of the molten Al alloy into the porous TiB 2 preform to fabricate the TiB 2 -Al composites.

Characterization
Microstructures of the TiB 2 -Al composites fabricated by LPI process ere analyzed by scanning electron microscope (SEM, JSM-6610LV, JEOL, Tokyo, Japan), transmission election microscope (TEM, Materials 2020, 13, 1588 3 of 11 JEM-ARM200F, JEOL, Tokyo, Japan), and electron probe micro analyzer (EPMA, JXA-8530F, JEOL, Tokyo, Japan). X-ray diffraction (XRD, D/Max-2500, Rigaku, Tokyo, Japan) using Cu Kα radiation at 30 kV and 250 mA was used to analyze the phase of the TiB 2 -Al composite. In addition, to calculate the relative density, the density of the composite was measured using the Archimedes method and compared with the theoretical density of the composite. Coefficient of thermal expansion (CTE) was measured from room temperature to 400 • C using a dilatometer (DIL 402C, NETZSCH, Selb, Germany). Room temperature tensile and compressive tests of TiB 2 -Al composites were carried out using a universal testing machine (5882 model, INSTRON, Norwood, MA, USA) at a strain rate of 5 × 10 −4 . In addition, a Vickers hardness tester (FM-700, Future-tech, Kanagawa, Japan) was employed to measure the hardness of the TiB 2 -Al1050 composites and Al1050 alloy at 300 KgF for 10 s. To confirm the reliability of the experiment, five tension samples, five compression samples, and three Vickers hardness samples were tested.

Contact Angle Between TiB 2 and Al
To fabricate sound MMCs, it is very important to control the processing conditions-temperature, environment, etc. This experiment focused on the temperature, which increases the wettability between TiB 2 and Al matrix in a vacuum. Contact angle measurement of TiB 2 and Al was conducted up to 1000 • C in a vacuum to find the optimum processing conditions. Figure 1 shows the measured contact angles and provides images of the TiB 2 plate and pure Al at 700, 800, 900, and 1000 • C.
Materials 2020, 13, x FOR PEER REVIEW 3 of 11 JEOL, Tokyo, Japan). X-ray diffraction (XRD, D/Max-2500, Rigaku, Tokyo, Japan) using Cu Kα radiation at 30 kV and 250 mA was used to analyze the phase of the TiB2-Al composite. In addition, to calculate the relative density, the density of the composite was measured using the Archimedes method and compared with the theoretical density of the composite. Coefficient of thermal expansion (CTE) was measured from room temperature to 400 °C using a dilatometer (DIL 402C, NETZSCH, Selb, Germany). Room temperature tensile and compressive tests of TiB2-Al composites were carried out using a universal testing machine (5882 model, INSTRON, Norwood, MA, USA) at a strain rate of 5 × 10 −4 . In addition, a Vickers hardness tester (FM-700, Future-tech, Kanagawa, Japan) was employed to measure the hardness of the TiB2-Al1050 composites and Al1050 alloy at 300 KgF for 10 s. To confirm the reliability of the experiment, five tension samples, five compression samples, and three Vickers hardness samples were tested.

Contact Angle Between TiB2 and Al
To fabricate sound MMCs, it is very important to control the processing conditionstemperature, environment, etc. This experiment focused on the temperature, which increases the wettability between TiB2 and Al matrix in a vacuum. Contact angle measurement of TiB2 and Al was conducted up to 1000 °C in a vacuum to find the optimum processing conditions. Figure 1 shows the measured contact angles and provides images of the TiB2 plate and pure Al at 700, 800, 900, and 1000 °C. The time is defined as the moment at which a droplet completely melts into a sphere; the spreading time is calculated from this point onward. The contact angles of Al and TiB2 at 700 and 800 °C were over 100°, even 6000 s after molten Al fell onto the TiB2 substrate, indicating the difficulty of spontaneous infiltration of molten Al into the TiB2 preform. On the other hand, the contact angles at 900 and 1000 °C dropped below 40°. In particular, the contact angle fell to 90° after 94 s of holding of the droplet on the TiB2 substrate at 1000 °C, indicating greatly increased wettability between TiB2 and Al. These results reveal that, at 1000 °C, molten Al can easily infiltrate into a porous TiB2 preform in a relatively short time. In this research, therefore, TiB2-Al1050 composites were fabricated at 1000 °C using the LPI process. The time is defined as the moment at which a droplet completely melts into a sphere; the spreading time is calculated from this point onward. The contact angles of Al and TiB 2 at 700 and 800 • C were over 100 • , even 6000 s after molten Al fell onto the TiB 2 substrate, indicating the difficulty of spontaneous infiltration of molten Al into the TiB 2 preform. On the other hand, the contact angles at 900 and 1000 • C dropped below 40 • . In particular, the contact angle fell to 90 • after 94 s of holding of the droplet on the TiB 2 substrate at 1000 • C, indicating greatly increased wettability between TiB 2 and Al. These results reveal that, at 1000 • C, molten Al can easily infiltrate into a porous TiB 2 preform in a relatively short time. In this research, therefore, TiB 2 -Al1050 composites were fabricated at 1000 • C using the LPI process.

Morphology of TiB 2 Preform
The uniform dispersion of reinforcement in the composite is considered to help effective infiltration of the molten metal alloy and improve the mechanical properties of MMCs. In this experiment, to fabricate uniformly dispersed homogeneous TiB 2 -Al composites, a TiB 2 reinforcement was prepared in the form of a porous structure. As-received TiB 2 powder has irregular shapes, as shown in Figure 2a. The uniform dispersion of reinforcement in the composite is considered to help effective infiltration of the molten metal alloy and improve the mechanical properties of MMCs. In this experiment, to fabricate uniformly dispersed homogeneous TiB2-Al composites, a TiB2 reinforcement was prepared in the form of a porous structure. As-received TiB2 powder has irregular shapes, as shown in Figure 2a. In addition, it was confirmed that the observed TiB2 particle size was in the range of 2-3 μm, although relatively large particles of about 5 μm and small debris particles several nm in size also existed. In this experiment, TiB2 powders were sintered at 1000 °C, which is much lower than the sintering temperature of TiB2 ceramic [21], to form weakly bonded TiB2 preforms. The inset of Figure  2b shows the pre-sintered TiB2 preform at 1000 °C; it has a diameter of 50 mm and a height of 20 mm. It is important for successful infiltration of molten Al during the LPI process that the ceramic preform maintains the shape of the porous body by slight bonding between ceramic particles, without grain growth. An SEM image of the sintered TiB2 preform shows a porous microstructure with 2-3 μm sized TiB2 particles, indicating no grain growth after sintering at 1000 °C ( Figure 2b). TiB2 particles were weakly bonded to each other while maintaining their origin shapes, resulting in the generation of about 35 vol.% porosity. Consequently, at elevated temperature, molten Al is effectively infiltrated into the uniformly generated open pores in the TiB2 preform. Figure 3 provides SEM and OM images of the TiB2-Al composite fabricated by LPI process. After the infiltration of molten Al into the TiB2 preform, the color changed from gray to silver (inset of Figure 3). In addition, it was confirmed that the observed TiB 2 particle size was in the range of 2-3 µm, although relatively large particles of about 5 µm and small debris particles several nm in size also existed. In this experiment, TiB 2 powders were sintered at 1000 • C, which is much lower than the sintering temperature of TiB 2 ceramic [21], to form weakly bonded TiB 2 preforms. The inset of Figure 2b shows the pre-sintered TiB 2 preform at 1000 • C; it has a diameter of 50 mm and a height of 20 mm. It is important for successful infiltration of molten Al during the LPI process that the ceramic preform maintains the shape of the porous body by slight bonding between ceramic particles, without grain growth. An SEM image of the sintered TiB 2 preform shows a porous microstructure with 2-3 µm sized TiB 2 particles, indicating no grain growth after sintering at 1000 • C ( Figure 2b). TiB 2 particles were weakly bonded to each other while maintaining their origin shapes, resulting in the generation of about 35 vol.% porosity. Consequently, at elevated temperature, molten Al is effectively infiltrated into the uniformly generated open pores in the TiB 2 preform. After the infiltration of molten Al into the TiB 2 preform, the color changed from gray to silver (inset of Figure 3).

Microstructure of TiB 2 -Al1050 Composites
Due to the effective infiltration of molten Al into the porous TiB 2 preform during the LPI process with the aid of applied gas pressure, TiB 2 reinforcements did not aggregate; rather, they individually dispersed in the Al1050 matrix. The volume fraction of the TiB 2 reinforcement, analyzed using the Image J program on several SEM images taken from the center and side area of the sample, was about 65%, which proves that the Al substrate was ideally infiltrated into the porous TiB 2 preform, which had a porosity of about 35%. In addition, the particle size of the TiB 2 reinforcement in the TiB 2 -Al composite fabricated by LPI process is similar to the particle size of raw TiB 2 . Therefore, it was confirmed that no grain growth of the TiB 2 reinforcement occurred at 1000 • C during the LPI process.  Due to the effective infiltration of molten Al into the porous TiB2 preform during the LPI process with the aid of applied gas pressure, TiB2 reinforcements did not aggregate; rather, they individually dispersed in the Al1050 matrix. The volume fraction of the TiB2 reinforcement, analyzed using the Image J program on several SEM images taken from the center and side area of the sample, was about 65%, which proves that the Al substrate was ideally infiltrated into the porous TiB2 preform, which had a porosity of about 35%. In addition, the particle size of the TiB2 reinforcement in the TiB2-Al composite fabricated by LPI process is similar to the particle size of raw TiB2. Therefore, it was confirmed that no grain growth of the TiB2 reinforcement occurred at 1000 °C during the LPI process. Figure 4 shows experimental results of EPMA for composition analysis of TiB2-Al composites fabricated by LPI process. The element mapping image indicates that Ti and B atoms were detected only at the TiB2 particle sites. The Al and TiB2 regions can be clearly distinguished. TiB2 reinforcements in the composites were observed to be homogeneously dispersed, without aggregation, despite the high volume ratio. From the Al mapping image, it was confirmed that molten Al infiltrated not only the micro-sized places between TiB2 reinforcements having average particle sizes of 2-3 μm, but also the narrow places between TiB2 reinforcements of sub-micron size. If wettability between the ceramic   Due to the effective infiltration of molten Al into the porous TiB2 preform during the LPI process with the aid of applied gas pressure, TiB2 reinforcements did not aggregate; rather, they individually dispersed in the Al1050 matrix. The volume fraction of the TiB2 reinforcement, analyzed using the Image J program on several SEM images taken from the center and side area of the sample, was about 65%, which proves that the Al substrate was ideally infiltrated into the porous TiB2 preform, which had a porosity of about 35%. In addition, the particle size of the TiB2 reinforcement in the TiB2-Al composite fabricated by LPI process is similar to the particle size of raw TiB2. Therefore, it was confirmed that no grain growth of the TiB2 reinforcement occurred at 1000 °C during the LPI process. Figure 4 shows experimental results of EPMA for composition analysis of TiB2-Al composites fabricated by LPI process. The element mapping image indicates that Ti and B atoms were detected only at the TiB2 particle sites. The Al and TiB2 regions can be clearly distinguished. TiB2 reinforcements in the composites were observed to be homogeneously dispersed, without aggregation, despite the high volume ratio. From the Al mapping image, it was confirmed that molten Al infiltrated not only the micro-sized places between TiB2 reinforcements having average particle sizes of 2-3 μm, but also the narrow places between TiB2 reinforcements of sub-micron size. If wettability between the ceramic The element mapping image indicates that Ti and B atoms were detected only at the TiB 2 particle sites. The Al and TiB 2 regions can be clearly distinguished. TiB 2 reinforcements in the composites were observed to be homogeneously dispersed, without aggregation, despite the high volume ratio. From the Al mapping image, it was confirmed that molten Al infiltrated not only the micro-sized places between TiB 2 reinforcements having average particle sizes of 2-3 µm, but also the narrow places between TiB 2 reinforcements of sub-micron size. If wettability between the ceramic reinforcement and metal matrix is poor, infiltration of molten metal will be more difficult in high volume fraction MMCs than in low volume fraction MMCs because of the increase of interfacial area and the high surface energy. This result proves that the superior wettability between TiB 2 and Al was actually obtained by fabrication of high volume fraction composite at the process temperature of 1000 • C. On the other hand, a few Mg-related oxides were observed in the microstructure of the TiB 2 -Al composites. This was probably generated by the reactions of minor elements in Al1050 with additional Mg and O from the MgO crucible. However, the number of phases was extremely low, such that the effect of these phases on the mechanical properties of TiB 2 -Al composites was negligible. Figure 5 shows the results of XRD analysis of TiB 2 -Al composites, allowing identification of the reaction phase formed during the fabrication process. reinforcement and metal matrix is poor, infiltration of molten metal will be more difficult in high volume fraction MMCs than in low volume fraction MMCs because of the increase of interfacial area and the high surface energy. This result proves that the superior wettability between TiB2 and Al was actually obtained by fabrication of high volume fraction composite at the process temperature of 1000 °C. On the other hand, a few Mg-related oxides were observed in the microstructure of the TiB2-Al composites. This was probably generated by the reactions of minor elements in Al1050 with additional Mg and O from the MgO crucible. However, the number of phases was extremely low, such that the effect of these phases on the mechanical properties of TiB2-Al composites was negligible. Figure 5 shows the results of XRD analysis of TiB2-Al composites, allowing identification of the reaction phase formed during the fabrication process. Generally, TiB2 is more thermodynamically stable than intermetallic compounds such as AlB2 and Al3Ti, as well as other ceramics such as B4C and TiC with Al [22,23]. Therefore, no interfacial reaction between TiB2 and the Al matrix occurred during the LPI process. XRD results for TiB2-Al composites fabricated by LPI process at 1000 °C showed only Al and TiB2 peaks. Although some Mg oxide was found in the EPMA mapping images, the XRD results do not indicate any Mg oxide peaks, indicating the generation of an extremely small amount of Mg oxide in the Al matrix.
The microstructures of the TiB2-Al composites fabricated by LPI process were analyzed using TEM, as indicated in Figure 6. Generally, TiB 2 is more thermodynamically stable than intermetallic compounds such as AlB 2 and Al 3 Ti, as well as other ceramics such as B 4 C and TiC with Al [22,23]. Therefore, no interfacial reaction between TiB 2 and the Al matrix occurred during the LPI process. XRD results for TiB 2 -Al composites fabricated by LPI process at 1000 • C showed only Al and TiB 2 peaks. Although some Mg oxide was found in the EPMA mapping images, the XRD results do not indicate any Mg oxide peaks, indicating the generation of an extremely small amount of Mg oxide in the Al matrix.
The microstructures of the TiB 2 -Al composites fabricated by LPI process were analyzed using TEM, as indicated in Figure 6.
The microstructure of the TiB 2 -Al composite was found to be an extremely clean TiB 2 /Al1050 interface without any vacancies or defects. It can be assumed that the TiB 2 /Al interface is likely to have a semi-coherent nature. These results reveal that, due to the improved wettability between TiB 2 and Al at a high processing temperature and the Ar gas pressurization applied, molten Al effectively infiltrated the TiB 2 preform. In addition, the clean TiB 2 particles show that they formed a sound interface without damaging the reinforcement during the fabrication process, despite the difference in CTE between TiB 2 (6-8 ppmK −1 ) and the Al matrix (26.28 ppmK −1 ). Figure 6 also provides energy-dispersive X-ray spectroscopy (EDS) element mapping images of the TiB 2 /Al1050 interface, allowing an analysis of the formation of chemical compounds at the interface between TiB 2 and Al. As mentioned earlier, because it is chemically very stable, TiB 2 is expected not to form chemical compounds during the composite fabrication process [22,23]. Actually, the results of EDS analysis of the TiB 2 /Al1050 interface indicate no chemical reaction between TiB 2 and the Al1050 matrix at 1000 • C, implying that the TiB 2 -Al composites fabricated in this experiment do not have extremely brittle compounds such as Al 3 Ti or AlB 2 , which are formed through chemical reactions [24][25][26]. Consequently, the TiB 2 -Al composites fabricated by LPI process, having sound microstructures without brittle compounds, indicate the possibility of achieving mechanical properties better than those of other composites fabricated by other ex-situ processes. The microstructure of the TiB2-Al composite was found to be an extremely clean TiB2/Al1050 interface without any vacancies or defects. It can be assumed that the TiB2/Al interface is likely to have a semi-coherent nature. These results reveal that, due to the improved wettability between TiB2 and Al at a high processing temperature and the Ar gas pressurization applied, molten Al effectively infiltrated the TiB2 preform. In addition, the clean TiB2 particles show that they formed a sound interface without damaging the reinforcement during the fabrication process, despite the difference in CTE between TiB2 (6-8 ppmK −1 ) and the Al matrix (26.28 ppmK −1 ). Figure 6 also provides energydispersive X-ray spectroscopy (EDS) element mapping images of the TiB2/Al1050 interface, allowing an analysis of the formation of chemical compounds at the interface between TiB2 and Al. As mentioned earlier, because it is chemically very stable, TiB2 is expected not to form chemical compounds during the composite fabrication process [22,23]. Actually, the results of EDS analysis of the TiB2/Al1050 interface indicate no chemical reaction between TiB2 and the Al1050 matrix at 1000 °C, implying that the TiB2-Al composites fabricated in this experiment do not have extremely brittle compounds such as Al3Ti or AlB2, which are formed through chemical reactions [24][25][26]. Consequently, the TiB2-Al composites fabricated by LPI process, having sound microstructures without brittle compounds, indicate the possibility of achieving mechanical properties better than those of other composites fabricated by other ex-situ processes. Figure 7 shows the tensile and compressive stress-strain curves of TiB2-Al composites tested at room temperature.  The insets of the figure are images of TiB2-Al composite specimens taken before and after the test. In the graph, the black line indicates the TiB2-Al1050 composite and the red line indicates the Al1050 alloy. Due to the influence of the strong and brittle TiB2 reinforcement, the strength of the TiB2-Al composite was significantly improved, while elongation decreased compared with that of the Al1050 alloy. As can be seen from the slope of the tensile stress-strain curve, the elastic modulus of the composite seems to be significantly improved compared to Al1050 due to the high elastic modulus (530 GPa) of TiB2 [7]. In general, it is difficult to measure the tensile strengths of ceramics due to their brittle nature, which was confirmed by fracturing in the elastic deformation region during the tensile test at room temperature. High volume fraction ceramic reinforced MMCs also exhibit the same fracture behavior as normal ceramics. Therefore, stress-strain curves of MMCs usually show fractures in the elastic deformation region [27][28][29]. However, TiB2-Al1050 composites The insets of the figure are images of TiB 2 -Al composite specimens taken before and after the test. In the graph, the black line indicates the TiB 2 -Al1050 composite and the red line indicates the Al1050 alloy. Due to the influence of the strong and brittle TiB 2 reinforcement, the strength of the TiB 2 -Al composite was significantly improved, while elongation decreased compared with that of the Al1050 alloy. As can be seen from the slope of the tensile stress-strain curve, the elastic modulus of the composite seems to be significantly improved compared to Al1050 due to the high elastic modulus (530 GPa) of TiB 2 [7]. In general, it is difficult to measure the tensile strengths of ceramics due to their brittle nature, which was confirmed by fracturing in the elastic deformation region during the tensile test at room temperature. High volume fraction ceramic reinforced MMCs also exhibit the same fracture behavior as normal ceramics. Therefore, stress-strain curves of MMCs usually show fractures in the elastic deformation region [27][28][29]. However, TiB 2 -Al1050 composites fabricated by the LPI process showed not only slight plastic deformation in the tensile test but also obvious plastic deformation behavior in the compression test. This phenomenon is very interesting and requires precise analysis. If the fine reinforcement is uniformly dispersed in the metal matrix while maintaining a good interface with the matrix, the tensile strength of the composite will increase without severe elongation deterioration. The results reveal that fine TiB 2 dispersed Al MMCs having sound interface were successfully fabricated by LPI process by increasing infiltration temperature and with the aid of applied pressure. Table 2 summarizes mechanical and physical properties, such as density, hardness, strength, and CTE values of the TiB 2 -Al1050 composites and the Al1050 alloy, respectively. Due to the relatively high density of TiB 2 (4.52 g/cm 3 ), the density of the TiB 2 -Al1050 composite increased 1.4 times compared to that of the Al1050 alloy. However, the ultimate tensile strength (UTS) of the TiB 2 -Al1050 composite dramatically increased to 7.0 times compared with Al1050. The tensile strength of Al1050 at room temperature was 67.1 MPa, as shown in Table 2. However, the average tensile strength of the TiB 2 -Al composites was 471.5 MPa, which was significantly high.

Mechanical Properties of TiB 2 -Al1050 Composites
The compressive yield strength (CYS) of the TiB 2 -Al1050 composite also increased about 8.4 times compared with that of the Al1050 matrix. In addition, Vickers hardness showed an 8.4-times increase compared with that of the Al1050 matrix. The CTE value of the TiB 2 -Al1050 composite, measured from room temperature to 100 • C, was 12.97 ppmK −1 , which is about 49% lower than that of Al1050. The characteristics of the composites might be anticipated by considering approximate values obtained using the rule of mixtures (ROM), which can be used to determine the characteristics and compositions of mixed materials [30]. The rule of mixtures follows this formula: Most of the measured properties of the TiB 2 -Al1050 composites fabricated by LPI process were within the ranges of properties calculated based on ROM. However, the tensile strength of the TiB 2 -Al1050 composite is extraordinarily higher than those of monolithic bulk TiB 2 and Al. This phenomenon is very interesting, as mentioned in the results of the stress-strain curve showing the plastic deformation behavior of the composites. The tensile strength of bulk ceramics is usually low due to premature failure; there are no standard values because the strength of a bulk ceramic depends on the grain size and distribution of defects. This result is believed to be due to the synergistic effect of the fine microstructure and the sound interface between TiB 2 and the Al1050 matrix.
Fracturing through tensile load commonly starts at defects such as voids. In the case of ceramic-reinforced metal matrix composites, when tension is applied in the vertical direction to composites in which soft Al, having low strength, is present, the material stretches, and fractures proceed as defects are formed at interface between reinforcements and the matrix. If this interface is not sound, the reinforcements-matrix interface plays a major role in the formation of defects such as voids [31]. Therefore, composites having poor interfaces may exhibit poor mechanical properties due to interfacial delamination. Figure 8a,b shows the fracture surfaces after tensile testing of Al10150 and TiB 2 -Al1050 composites, respectively, under the same magnification.
of the fine microstructure and the sound interface between TiB2 and the Al1050 matrix.
Fracturing through tensile load commonly starts at defects such as voids. In the case of ceramicreinforced metal matrix composites, when tension is applied in the vertical direction to composites in which soft Al, having low strength, is present, the material stretches, and fractures proceed as defects are formed at interface between reinforcements and the matrix. If this interface is not sound, the reinforcements-matrix interface plays a major role in the formation of defects such as voids [31]. Therefore, composites having poor interfaces may exhibit poor mechanical properties due to interfacial delamination. Figure 8a,b shows the fracture surfaces after tensile testing of Al10150 and TiB2-Al1050 composites, respectively, under the same magnification. The fractography of Al10150 shows that, when load was applied to the specimen in the vertical direction, the specimen broke while forming coarse dimples of several tens of micrometers. In the case of the TiB2-Al1050 composite, the microstructure became very fine compared with that of the Al matrix; this was due to the presence of fine TiB2 reinforcement and the grain refined Al matrix. Figure  8c shows the microstructure observed at high magnification to allow for the analysis of the fracture surface of the TiB2-Al1050 composite; significantly fine dimples and lots of broken TiB2 particles can be seen. This fracture behavior appeared when cracks formed at the soft matrix were effectively transferred to the reinforcements. Through this phenomenon, the TiB2-Al1050 composite fabricated by LPI process is considered to exhibit fracture behavior in which brittle fracturing of TiB2 and ductile fracturing of Al are mixed by effective load transfer, without interfacial delamination between TiB2 and Al [28]. Consequently, highly improved tensile strength and moderate ductility of TiB2-Al1050 composites were achieved by using the LPI process at 1000 °C and the aid of applied gas pressure to reinforce a high-volume fraction of fine TiB2 in the Al matrix. The fractography of Al10150 shows that, when load was applied to the specimen in the vertical direction, the specimen broke while forming coarse dimples of several tens of micrometers. In the case of the TiB 2 -Al1050 composite, the microstructure became very fine compared with that of the Al matrix; this was due to the presence of fine TiB 2 reinforcement and the grain refined Al matrix. Figure 8c shows the microstructure observed at high magnification to allow for the analysis of the fracture surface of the TiB 2 -Al1050 composite; significantly fine dimples and lots of broken TiB 2 particles can be seen. This fracture behavior appeared when cracks formed at the soft matrix were effectively transferred to the reinforcements. Through this phenomenon, the TiB 2 -Al1050 composite fabricated by LPI process is considered to exhibit fracture behavior in which brittle fracturing of TiB 2 and ductile fracturing of Al are mixed by effective load transfer, without interfacial delamination between TiB 2 and Al [28]. Consequently, highly improved tensile strength and moderate ductility of TiB 2 -Al1050 composites were achieved by using the LPI process at 1000 • C and the aid of applied gas pressure to reinforce a high-volume fraction of fine TiB 2 in the Al matrix.

Conclusions
In this study, fabrication of TiB 2 -Al composites with improved mechanical properties and microstructures was attempted to compensate for the unstable interfaces of composites fabricated by ex-situ methods. Using the advantage of improved wettability between TiB 2 and Al with increasing temperature, TiB 2 -Al composites having uniformly dispersed fine TiB 2 reinforcements at about 65% volume ratios were successfully fabricated using the LPI process, which applies gas pressure at a high temperature. At the high temperature of 1000 • C, molten Al1050 alloy was well infiltrated into the very narrow sub-micron regions between TiB 2 particles; no interfacial defects were produced due to the good wettability between TiB 2 and the Al matrix and the aid of the applied gas pressure. The density of the composite was 3.84 g/cm 3 , which is 1.4 times higher than that of the matrix. The tensile strength, CYS, and Vickers hardness of the TiB 2 -Al composite were 471.5 MPa, 500.4 MPa, and 194.4 Hv, respectively, which are 7.0, 8.4, and 8.4 times higher than those values of Al1050. In addition, CTE of the composite is about 49% lower than that of Al1050 in the range of room temperature to 100 • C. Because of the absence of brittle intermetallic compounds and interfacial defects in the TiB 2 -Al composite, the load applied to the composite was effectively transferred from the soft Al matrix to the high strength TiB 2 reinforcement, resulting in mixed fracture behavior, including ductile and brittle fracturing. For this reason, tensile and compressive tests show that the strength and elongation of TiB 2 -Al composites are significantly improved compared to those values of conventional high-volume fraction MMCs fabricated by ex-situ methods. Therefore, with their excellent mechanical and physical properties, TiB 2 -Al composites fabricated by LPI process are considered applicable in various fields, such as those pertaining to automobiles, aerospace, and armor.