A Study on Modified Bitumen with Metal Doped Nano-TiO2 Pillared Montmorillonite

TiO2 pillared montmorillonite (T/M) modifiers have been studied to alleviate the aging of asphalt pavement and degrade automobile exhaust, but the photocatalytic activity of ordinary TiO2 is not good enough. In this study, in order to improve the photocatalytic performance of T/M, different metal (Ce, Cu, Fe) doped modifiers were prepared based on T/M. Metal doped TiO2 pillared montmorillonite was prepared by the sol-gel method. The modifier was characterized by X-ray diffraction (XRD) and an Ultraviolet visible (UV-Vis) spectrophotometer. The results show that TiO2 with different metal ions successfully entered into the layer of organic montmorillonite (OMMT) to form a pillared structure. Compared with the undoped TiO2 pillared montmorillonite (T/M), the optical absorption edge of the metal doped TiO2 pillared montmorillonite has an obvious red shift. In addition, the influences of the different content of modifiers on the properties of the original bitumen and catalytic capacities for automobile exhaust were also investigated. The results show that Ce doped TiO2 (Ce-T/M) pillared montmorillonite has the best improvement in high temperature performance and ultraviolet (UV) resistance of bitumen. In the experiment of automobile exhaust degradation, the degradation law of NO and HC showed Cu-T/M > Ce-T/M > Fe-T/M > T/M. These three kinds of metal ions can effectively improve the photocatalytic degradation efficiency of T/M.


Introduction
With the increasing number of cars, the impact of automobile exhaust on the environment is becoming more and more serious. In practical road applications, heavy traffic also creates higher requirements for asphalt pavement. Common bitumen easily causes various road diseases because of its poor rheological performance, high temperature sensitivity, inadequate aging resistance, and other problems [1][2][3][4]. Therefore, it is of great significance for modern road construction to develop a kind of bitumen modifier that can not only improve the performance of asphalt pavement but also protect the environment and reduce automobile exhaust pollution [5,6].
Montmorillonite (MMT) is one of the most extensively studied mineral modifiers, which can enhance the high-temperature properties and aging resistance of bitumen. However, there are many inorganic ions in the montmorillonite layers, which show hydrophilic properties and poor dispersion in organic polymer materials. Incorporation of organic component in montmorillonite can solve this problem [7,8]. Organic montmorillonite (OMMT) has larger lamellar spacing, which makes it easier for organics and metal ions to enter the interlayer. Through organic modification, the montmorillonite can also change from hydrophilic to lipophilic and has good organic compatibility and dispersion [9][10][11]. Moreover, its unique lamellar structure can more easily be propped up by pillared compounds. It can be used to modify the structure of bitumen by using its interlayer characteristics, and the pavement performance of bitumen can be further enhanced after mixing with bitumen.
A series of nano-photocatalytic materials, for example TiO 2 , Fe 3 O 4 and ZnO, have been widely used to adsorb and catalyze the degradation of pollutants [12][13][14]. However, the direct addition of nano-materials to bitumen is often ineffective, which is related to the compatibility and dispersion of materials and whether if it will form agglomeration. Therefore, the montmorillonite can be combined with the nano-materials to allow the nanoparticles to enter into the montmorillonite layer to form a pillared modified montmorillonite. This method is conducive to enlarging the interlayer spacing of montmorillonite, forming an exfoliated structure in the organic polymer materials, increasing the surface area of the materials and improving the catalytic performance and interlayer cation exchangeability of the materials [15,16].
TiO 2 is one of the most common photocatalytic materials, but the catalytic activity of TiO 2 is not good enough in the visible light range. Therefore, researchers use ion-doping method to improve catalytic performance, such as TiO 2 /montmorillonite composites [17,18]. In this paper, TiO 2 pillared montmorillonite (T/M) was doped with Ce, Fe, and Cu ions to improve the performance of T/M. Different metal doped TiO 2 pillared montmorillonite has a wider ultraviolet absorption wavelength range than T/M, and the optical absorption ranges are extended from ultraviolet to visible light. The metal doped TiO 2 pillared montmorillonite has a better photocatalytic ability. The addition of metal doped TiO 2 pillared montmorillonite could also effectively increase the resistance to rutting and permanent deformation under high temperature conditions. In this study, metal doped modifiers were evaluated at the microscopic level by X-ray diffraction (XRD) and an Ultraviolet visible (UV-Vis) spectrophotometer [19]. The high temperature performance, UV aging resistance, and degradation of the automobile exhaust performance of metal doped modified bitumen were also studied. Metal doped modified asphalt has the potential to catalyze automobile exhaust and improve the aging resistance of asphalt. Metal doped, modified bitumen offers a certain contribution to the development of environmental protection and the long-life of asphalt pavement.

Materials
Sodium hydroxide (NaOH), nitric acid (HNO 3 ), ethyl alcohol absolute (C 2 H 5 OH), tetra-n-butyl titanate (C 16 H 36 O 4 Ti), cupric nitrate (Cu(NO 3 ) 2 ), ferrous nitrate (Fe(NO 3 ) 3 ), cerium (III) nitrate hexahydrate (Ce(NO 3 ) 3 ), acetic acid (CH 3 COOH), and hexadecyl trimethyl ammonium bromide (CATB) were analytical grade and used without further purification. Na-montmorillonite clay (MMT, 90 meq/100 g) was collected from Xinyang, China. Original bitumen with a penetration grade of 70# (TZ70) was supplied by the China National Offshore Oil Corporation Taizhou Petroleum Asphalt Factory (Taizhou, China). The performance of the original bitumen is shown in Table 1. 10 mL tetra-n-butyl titanate, 10 mL ethyl alcohol absolute, and 2 mL acetic acid were mixed for 20 min to form the transparent, yellowish Solution A. Preparation of Solution B begun with 24 mL HNO 3 (1 mol/L) and 5 mL ethyl alcohol absolute. The light-yellow transparent sol of Ti was obtained by adding liquid A into liquid B with the aid of a separating funnel with intense magnetic stirring. The TiO 2 pillared agent can be obtained by adjusting pH = 2 with a NaOH solution (1 mol/L) and continuous stirring.
2 g of MMT, which went through a 200 mesh sieve, was slowly added into 200 mL of deionized water under continuous stirring. The solution was subjected to ultrasonic vibration for 5 mins and then stirred continuously for 2 h with an electric agitator to form a suspension with a mass concentration of 1 wt %.
The prepared TiO 2 pillared agent was continuously dripped into the suspension of MMT and stirred for 6 h at 65 • C. After being stirred completely, the solution was centrifuged to remove the separated upper liquid until the supernatant was near neutral, and the excess sol and other impurity ions were washed away. The precipitate was taken out and placed in a drying oven at 80 • C. The precursor of the TiO 2 pillared montmorillonite (P-T/M) was obtained by being grinded through a 200 mesh sieve after the water was completely removed.
The pillared precursor was calcinated at 500 • C for 3 h with a heating rate of 2 • C/min. The TiO 2 pillared montmorillonite (T/M) was obtained by grinding and passing the material through a 200 mesh sieve after being naturally cooled down to room temperature.
Metal doped TiO 2 pillared montmorillonite was also prepared by the sol-gel method. The metals were doped to TiO 2 with a molar mass ratio of [Ti 4+ /Metal ion] = 3/1. Corresponding Fe, Cu, and Ce metal salts were added to the above Solution A with the same procedure as the TiO 2 pillared montmorillonite. The precursor of the metal doped TiO 2 pillared montmorillonite was recorded as P-Cu-T/M, P-Fe-T/M, P-Ce-T/M, and the metal doped TiO 2 pillared montmorillonite was recorded as Cu-T/M, Fe-T/M, Ce-T/M.

Preparation of Modified Bitumen
Different amounts (4 wt %, 5 wt %, and 6 wt %) of Cu-T/M, Fe-T/M, Ce-T/M, and T/M as bitumen modifiers were added into the 70# bitumen (TZ70) after being heated at 120 • C. Then, the bitumen was dispersed for 40 min under 140-155 • C with a rotation speed of 5000 rpm. Finally, the modified bitumen of the T/M, Cu-T/M, Fe-T/M, and Ce-T/M with different contents were prepared (named TZ70 + X% Y-T/M, X = 4, 5, 6, and Y for Cu, Fe, Ce). And 5 wt % of the T/M modified bitumen (TZ70 + 5% T/M) was selected for comparison.

Microscopic Tests of Samples
The phase identification of the MMT, T/M, and metal doped TiO 2 pillared montmorillonite was investigated by X-ray diffraction (XRD) (Rigaku D/max 2550, Tokyo, Japan, Cu Kα radiation, 2θ = 0.5-80 • . The UV-Vis spectra were determined by Shimadzu UV-2600 UV-Vis spectrophotometer (Kyoto, Japan) with a wavelength range of 300-1000 nm. The transmission electron microscopy (TEM) image of Ce-T/M was recorded by a JEOL JEM-2100 F electron microscope (Tokyo, Japan). The DM3000 fluorescence microscope (FM) was produced by Leica (Wetzlar, Germany), the excitation light was blue light, the eyepiece magnification was 10 times, the objective lens was adjustable in multiple gears, and the modified bitumen with 5 wt % Ce-T/M sample was tested.

High Temperature Rheological Tests
The high temperature rheological properties of the modified bitumen were tested with an MCR 301 intelligent dynamic shear rheometer (DSR) produced by Anton Paar (Graz, Austria). The test method is referred to AASHTO T 315-2012 [20,21]. Two parallel circular plates with a diameter of 25 mm and a spacing of 1 mm were used. The temperature ranged from 40 • C to 90 • C, with an increment of 2 • C/min. The oscillation frequency was 10 rad/s, and the strain values of the original sample and the ultraviolet aged sample were fixed at 12% and 10%, respectively. Three parallel samples were prepared, and the results were averaged. The complex shear modulus (G*) phase angle (δ) obtained from DSR can be used to calculate the resistance of the modified bitumen to rutting and permanent deformation under high temperature conditions. G*/sinδ is used as an indicator to reflect the permanent deformation of bitumen materials. From the perspective of anti-rutting, higher G* values and lower δ values are ideal.

Ultraviolet (UV) Aging Test
Prolonged UV radiation will cause the aging of bitumen, which will shorten the service life of the bitumen. The UV aging test aims to reveal the effects of Cu-T/M, Fe-T/M, Ce-T/M, and T/M on bitumen resistance to UV aging. 3.5 g of the modified bitumen or original bitumen was poured into a span with a diameter of 95 mm, resulting in a film thickness of about 1 mm. Then, the bitumen films were placed under a UV intensity of 3.18 W/m 2 for 336 h to simulate three years of UV aging under an atmosphere. Finally, the residual bitumen sample after aging was analyzed by DSR. The aging index (AI) value is calculated according to the following formula: where G * aged is the complex shear modulus of bitumen after aging, and G * f resh is the complex shear modulus of the fresh bitumen. The lower AI value reflects the better UV aging resistance of the bitumen.

Degradation Test of Automobile Exhaust
In the previous experiments, degradation tests of the automobile exhaust of modified bitumen were investigated by a self-designed UV environment simulation cabinet [5]. The environmental cabinet can effectively simulate the actual road environment and is equipped with an exhaust detection system (Gasboard-5030, Foshan Analyzer Co. Ltd., Foshan, China) to test the photocatalytic degradation of automobile exhaust. The instrument light source system adopts ultraviolet light emitting diode (UV-LED).
The average intensity of ultraviolet light in the experimental area was 0.52 W/m 2 . In order to speed up the experimental process, the UV intensity of this experiment was 10.4 W/m 2 , which was 20 times that of natural light. In this experiment, the dosage of the metal doped modifier was selected as 6 wt % and compared with the modified bitumen with 6 wt % T/M to determine the difference and promotion of the three metal doped modifiers. In this test, the irradiation time of all four samples was 90 min, the ambient temperature of the experimental cabinet was kept constant at 25 • C, and NO, HC was introduced to simulate the automobile exhaust environment. The composition and concentration of the automobile exhaust was the same as those of the previous experiments, according to the actual automobile exhaust [5]. A 60 g amount of modified bitumen was paved on a flat plate with dimensions of 20 mm × 30 mm, and the resultant thickness of the films was about 1 mm. Then, the plate of bitumen was put into the environmental cabinet, and the test was carried out at 25 • C for 90 min. The changes in concentration of NO, HC over this period were collected every 5 min [22,23].
In this paper, η is used as the degradation rate of gas, and the equation is: where C 0 is the initial concentration of gas and C 1 is the concentration of gas reaching the specified time.
The summary of samples and experiments are show in Table 2.

Automobile Exhaust Degradation (Bitumen)
Original bitumen Ce-T/M has broad diffraction peaks with a higher peak height, which may be due to lattice distortion and a decrease in grain size of the TiO 2 influenced by the doping of Ce. The unsaturated bonds and dangling bonds on the surface increase after the doping procedure; the surface effect is remarkable, and the photocatalyst surface has a strong chemical reactivity [25]. The UV-vis spectrum of the metal doped TiO2 pillared montmorillonite are shown in Figure 2. All the absorbance curves of Cu-T/M, Fe-T/M and Ce-T/M move to the right with a noticeable red shift in the absorption edge after the TiO2 was doped with Cu, Fe, and Ce metals. Ion doping introduces specific metal ions into the lattice of the TiO2, which has a good effect on the formation and recombination of electron holes in the lattice. Some metal ions can replace Ti 4+ in the lattice and promote the red shift of absorption wavelength. The specific surface area, adsorption performance and degradation ability of the lattice are enhanced [26][27][28]. Compared with the absorbance curve of T/M, the absorption range of ultraviolet light by Fe-T/M and Ce-T/M is extended to 300-500 nm, indicating the enhanced absorption capacity of UV light. The absorption wavelength range of ultraviolet light was clearly enlarged after being doped by Cu. Ce-T/M has a good absorption effect on ultraviolet light in a wavelength range of 300-600 nm and can still maintain better absorption capacity in the wavelength range of 600-1000 nm. Different metal doped TiO2 pillared montmorillonite has a wider ultraviolet absorption wavelength range than T/M, and the optical absorption ranges are extended from ultraviolet to visible light. The metal doped TiO2 pillared montmorillonite has a better photocatalytic ability, especially for Cu-T/M [29,30]. The UV-vis spectrum of the metal doped TiO 2 pillared montmorillonite are shown in Figure 2. All the absorbance curves of Cu-T/M, Fe-T/M and Ce-T/M move to the right with a noticeable red shift in the absorption edge after the TiO 2 was doped with Cu, Fe, and Ce metals. Ion doping introduces specific metal ions into the lattice of the TiO 2 , which has a good effect on the formation and recombination of electron holes in the lattice. Some metal ions can replace Ti 4+ in the lattice and promote the red shift of absorption wavelength. The specific surface area, adsorption performance and degradation ability of the lattice are enhanced [26][27][28]. Compared with the absorbance curve of T/M, the absorption range of ultraviolet light by Fe-T/M and Ce-T/M is extended to 300-500 nm, indicating the enhanced absorption capacity of UV light. The absorption wavelength range of ultraviolet light was clearly enlarged after being doped by Cu. Ce-T/M has a good absorption effect on ultraviolet light in a wavelength range of 300-600 nm and can still maintain better absorption capacity in the wavelength range of 600-1000 nm. Different metal doped TiO 2 pillared montmorillonite has a wider ultraviolet absorption wavelength range than T/M, and the optical absorption ranges are extended from ultraviolet to visible light. The metal doped TiO 2 pillared montmorillonite has a better photocatalytic ability, especially for Cu-T/M [29,30]. The morphology of Ce-T/M was analyzed by TEM image (Figure 3a). The typical parallel structure of montmorillonite with a 1 μm in diameter was observed. The dark particles in the Ce-MMT is concluded to be the Ce-TiO2 on the surface or in the layer of MMT. FM was carried out on the 5 wt % Ce-T/M modified bitumen to observe the distribution of the Ce-TiO2 nano powder in the bitumen (Figure 3b). The bitumen of the image is displayed as black with a continuous phase, and the Ce-TiO2 nano powder is shown as green bright spots by adjusting the brightness.

High Temperature Rheological Properties of Modified Bitumen
The high temperature rheological properties of the metal doped modified bitumen were tested by DSR. The content of the three modifiers in the bitumen were 4 wt %, 5 wt %, and 6 wt %; the modified bitumen with a 5 wt % T/M was selected as a contrast (Figure 4). The G*/sinδ of the bitumen is obviously improved after being modified with Cu-T/M, Fe-T/M, and Ce-T/M. The exfoliation structure was formed after adding montmorillonite to the bitumen, and the modifier was uniformly dispersed in the bitumen. Large numbers of bitumen particles entered the montmorillonite layer, and the compatibility between the modifier and asphalt increased, resulting in improved high temperature rheological properties for the asphalt [31]. It can be found that the G*/sinδ of the 5 wt % Cu-T/M and Ce-T/M modified bitumen is bigger than that of the 5 wt % T/M modified bitumen. However, the G*/sinδ of the Fe-T/M modified bitumen is less than that of that of the 5 wt % T/M modified bitumen. It was proven that the high temperature rheological properties of The morphology of Ce-T/M was analyzed by TEM image (Figure 3a). The typical parallel structure of montmorillonite with a 1 µm in diameter was observed. The dark particles in the Ce-MMT is concluded to be the Ce-TiO 2 on the surface or in the layer of MMT. FM was carried out on the 5 wt % Ce-T/M modified bitumen to observe the distribution of the Ce-TiO 2 nano powder in the bitumen (Figure 3b). The bitumen of the image is displayed as black with a continuous phase, and the Ce-TiO 2 nano powder is shown as green bright spots by adjusting the brightness. The morphology of Ce-T/M was analyzed by TEM image (Figure 3a). The typical parallel structure of montmorillonite with a 1 μm in diameter was observed. The dark particles in the Ce-MMT is concluded to be the Ce-TiO2 on the surface or in the layer of MMT. FM was carried out on the 5 wt % Ce-T/M modified bitumen to observe the distribution of the Ce-TiO2 nano powder in the bitumen (Figure 3b). The bitumen of the image is displayed as black with a continuous phase, and the Ce-TiO2 nano powder is shown as green bright spots by adjusting the brightness.

High Temperature Rheological Properties of Modified Bitumen
The high temperature rheological properties of the metal doped modified bitumen were tested by DSR. The content of the three modifiers in the bitumen were 4 wt %, 5 wt %, and 6 wt %; the modified bitumen with a 5 wt % T/M was selected as a contrast (Figure 4). The G*/sinδ of the bitumen is obviously improved after being modified with Cu-T/M, Fe-T/M, and Ce-T/M. The exfoliation structure was formed after adding montmorillonite to the bitumen, and the modifier was uniformly dispersed in the bitumen. Large numbers of bitumen particles entered the montmorillonite layer, and the compatibility between the modifier and asphalt increased, resulting in improved high temperature rheological properties for the asphalt [31]. It can be found that the G*/sinδ of the 5 wt % Cu-T/M and Ce-T/M modified bitumen is bigger than that of the 5 wt % T/M modified bitumen. However, the G*/sinδ of the Fe-T/M modified bitumen is less than that of that of the 5 wt % T/M modified bitumen. It was proven that the high temperature rheological properties of

High Temperature Rheological Properties of Modified Bitumen
The high temperature rheological properties of the metal doped modified bitumen were tested by DSR. The content of the three modifiers in the bitumen were 4 wt %, 5 wt %, and 6 wt %; the modified bitumen with a 5 wt % T/M was selected as a contrast (Figure 4). The G*/sinδ of the bitumen is obviously improved after being modified with Cu-T/M, Fe-T/M, and Ce-T/M. The exfoliation structure was formed after adding montmorillonite to the bitumen, and the modifier was uniformly dispersed in the bitumen. Large numbers of bitumen particles entered the montmorillonite layer, and the compatibility between the modifier and asphalt increased, resulting in improved high temperature rheological properties for the asphalt [31]. It can be found that the G*/sinδ of the 5 wt % Cu-T/M and Ce-T/M modified bitumen is bigger than that of the 5 wt % T/M modified bitumen. However, the G*/sinδ of the Fe-T/M modified bitumen is less than that of that of the 5 wt % T/M modified bitumen. It was proven that the high temperature rheological properties of the T/M modified bitumen can be further improved by being doped with two metal ions of Ce and Cu, but the effect of Fe ion is not obvious. A lateral comparison of the curves in Figure 4a-c show that the G*/sinδ of the Ce-T/M modified bitumen at different temperatures is higher than that of the Cu-T/M and Fe-T/M modified bitumen with the same content, which proves that the high temperature performance of the Ce-T/M modified bitumen is obviously improved. The rutting factor G*/sinδ of the modified bitumen increased significantly with an increase of nano-metal oxides, which means that the viscous properties of the bitumen are weakened, and the high temperature resistance to permanent deformation is significantly enhanced [32].  Figure 4a-c show that the G*/sinδ of the Ce-T/M modified bitumen at different temperatures is higher than that of the Cu-T/M and Fe-T/M modified bitumen with the same content, which proves that the high temperature performance of the Ce-T/M modified bitumen is obviously improved. The rutting factor G*/sinδ of the modified bitumen increased significantly with an increase of nano-metal oxides, which means that the viscous properties of the bitumen are weakened, and the high temperature resistance to permanent deformation is significantly enhanced [32].

UV Aging of Modified Bitumen
The optimum dosage and effects of different modifiers on UV aging resistance were investigated by UV aging tests. After UV aging, the residual bitumen samples were analyzed by

UV Aging of Modified Bitumen
The optimum dosage and effects of different modifiers on UV aging resistance were investigated by UV aging tests. After UV aging, the residual bitumen samples were analyzed by DSR. Then  Figure 6. The AI value of the Ce-T/M modified bitumen at different temperatures is lower than the other two, which is closer to 1. This analysis indicated that the degree of UV aging is lower after being modified with 5 wt % Ce-T/M, and the effect of improving the UV aging resistance of bitumen is the best. According to the analysis shown in Figures 2 and 4, Ce-T/M has the best UV shielding ability and high temperature rheological properties, so the UV aging resistance ability of the Ce-T/M modified asphalt is the most obvious. Compared with T/M, the UV absorption capacities of Fe-T/M and Cu-T/M were enhanced, but the high temperature rheological properties of the Fe-T/M and Cu-T/M modified asphalt were degraded, so the UV aging resistance of the Fe-T/M and Cu-T/M modified asphalts did not improve [25,33]. bitumen at different temperatures is lower than the other two, which is closer to 1. This analysis indicated that the degree of UV aging is lower after being modified with 5 wt % Ce-T/M, and the effect of improving the UV aging resistance of bitumen is the best. According to the analysis shown in Figures 2 and 4, Ce-T/M has the best UV shielding ability and high temperature rheological properties, so the UV aging resistance ability of the Ce-T/M modified asphalt is the most obvious. Compared with T/M, the UV absorption capacities of Fe-T/M and Cu-T/M were enhanced, but the high temperature rheological properties of the Fe-T/M and Cu-T/M modified asphalt were degraded, so the UV aging resistance of the Fe-T/M and Cu-T/M modified asphalts did not improve [25,33].

Photocatalytic Degradation of Tail Gas Test
In the experiment of degradation exhaust gases, the blank control groups were set up firstly. Because the original bitumen did not possess the photocatalytic capability to calculate the bare degradation rate, the degradation rates of the exhaust gases catalyzed by the original bitumen were first measured at the same experimental time and temperature. The degradation rates of the exhaust gases catalyzed by the metal doped TiO2 pillared montmorillonite minus the blank control groups values were measured to obtain the bare degradation rates. Figure 7 shows the NO degradation curve after subtracting the blank group. The maximum degradation rate (η) of the 6 wt % Cu-T/M, Ce-T/M, and Fe-T/M modified bitumen reached 82.99%, 71.30%, and 69.20% after 90 min, respectively, while that of the T/M modified bitumen at 90 min was 54.63% for the NO. Cu-T/M modified bitumen had the strongest degradation ability among NO gases. Compared to the T/M modified bitumen, the Fe-T/M modified bitumen showed no obviously increased degradation for the NO gas. Doping Cu, Ce can efficiently enhance the degradation for NO gases of TiO2. The η growth of the four kinds of modified bitumen is faster at 0-30 min, and becomes slower at 30-90

Photocatalytic Degradation of Tail Gas Test
In the experiment of degradation exhaust gases, the blank control groups were set up firstly. Because the original bitumen did not possess the photocatalytic capability to calculate the bare degradation rate, the degradation rates of the exhaust gases catalyzed by the original bitumen were first measured at the same experimental time and temperature. The degradation rates of the exhaust gases catalyzed by the metal doped TiO 2 pillared montmorillonite minus the blank control groups values were measured to obtain the bare degradation rates. Figure 7 shows the NO degradation curve after subtracting the blank group. The maximum degradation rate (η) of the 6 wt % Cu-T/M, Ce-T/M, and Fe-T/M modified bitumen reached 82.99%, 71.30%, and 69.20% after 90 min, respectively, while that of the T/M modified bitumen at 90 min was 54.63% for the NO. Cu-T/M modified bitumen had the strongest degradation ability among NO gases. Compared to the T/M modified bitumen, the Fe-T/M modified bitumen showed no obviously increased degradation for the NO gas. Doping Cu, Ce can efficiently enhance the degradation for NO gases of TiO 2 . The η growth of the four kinds of modified bitumen is faster at 0-30 min, and becomes slower at 30-90 min. The degradation ability of the T/M modified bitumen was saturated after 55 min, but the Cu-T/M and Ce-T/M modified bitumen maintained a high growth rate in the 30-90 min period. The degradation rate of the Cu-T/M modified bitumen was faster, indicating the stronger catalytic degradation of the NO gas [25,35].
min. The degradation ability of the T/M modified bitumen was saturated after 55 min, but the Cu-T/M and Ce-T/M modified bitumen maintained a high growth rate in the 30-90 min period. The degradation rate of the Cu-T/M modified bitumen was faster, indicating the stronger catalytic degradation of the NO gas [25,35].         Compared to the T/M modified bitumen, the Cu-T/M, Fe-T/M, and Ce-T/M modified bitumen exhibited obvious improvement in UV aging resistance and photocatalytic activity to HC and NO gases after doping TiO 2 with Ce, Cu, and Fe. This was mainly due to the obvious red shift of the optical absorption edge of the three kinds of modified bitumen, which made the optical absorption range extend from an ultraviolet region to a visible region. The red shift of Cu-T/M, Fe-T/M, and Ce-T/M is attributed to the charge transfer transition between the three metal ion electrons of Ce, Cu, and Fe, and the conduction band or valence band of TiO 2 , resulting in a decrease in the band gap energy of TiO 2 . After doping Ce, Cu, and Fe into T/M, the unit cell expanded, and the lattice became distorted. The positive and negative charges moved to the center, the degenerate orbit decreased, and the number of excited electrons increased, which promoted the capture of photogenerated electrons, and then the electron-hole pairs increased. All these phenomena resulted in the improved photocatalytic capacity of Cu-T/M, Fe-T/M, and Ce-T/M modified bitumen [37]. Cu-T/M displayed superior photocatalytic capacity for NO and HC, which may be due to the similar atomic radius for Cu 2+ (0.073 nm) and Ti 4+ (0.068 nm). Compared with Ce 4+ (0.102 nm) and Fe 2+ (0.078 nm), Cu 2+ can easily enter the lattice of TiO 2 , which induces more electron-hole pairs and better catalytic performance. Metal oxides with high activity, such as Cu, can achieve similar catalytic effects to rare metals at normal temperatures. Moreover, Cu could be widely applied because of its lower cost, and because it has practical road engineering applications, which provide a new research direction for the metal doped catalytic degradation of automobile exhaust [23,38].

Conclusions
This work mainly studies the effects of metal doped TiO 2 pillared montmorillonite on bitumen, including a physical characterization of the modifiers, high temperature properties, and UV aging resistance of modified bitumen. Furthermore, the photocatalytic degradation of tail gas properties by modified bitumen was investigated. Several major conclusions are as follows:

Conflicts of Interest:
The authors declare no conflict of interest.