Effect of Solvent Properties on the Critical Solution Temperature of Thermoresponsive Polymers

The ability of thermoresponsive polymers to respond to temperature with a reversible conformational change makes them promising ‘smart’ materials for solutions in medical and biotechnological applications. In this work, two such polymers and structural isomers were studied: poly(N-isopropyl acrylamide) (PNiPAm) and poly(2-isopropyl-2-oxazoline) (PiPOx). We compare the critical solution temperatures (CST) of these polymers in D2O and H2O in the presence of Hofmeister series salts, as results obtained under these different solvent conditions are often compared. D2O has a higher dipole moment and electronegativity than H2O, which could significantly alter the CST transition. We used two complementary methods to measure the CST, dynamic light scattering (DLS) and differential scanning calorimetry (DSC) and found that the CST decreased significantly in D2O compared to H2O. In the presence of highly concentrated kosmotropes, the CST of both polymers decreased in both solvents. The influence of the kosmotropic anions was smaller than the water isotope effect at low ionic strengths but considerably higher at physiological ionic strengths. However, the Hofmeister anion effect was quantitatively different in H2O than in D2O, with the largest relative differences observed for Cl−, where the CSTs in D2O decreased more than in H2O measured by DLS but less by DSC. PiPOx was more sensitive than PNiPAm to the presence of chaotropes. It exhibited much higher transition enthalpies and multistep transitions, especially in aqueous solutions. Our results highlight that measurements of thermoresponsive polymer properties in D2O cannot be compared directly or quantitatively to application conditions or even measurements performed in H2O.


Introduction
The ability of a material to react to external stimuli and alter its shape and functionality is a crucial characteristic of so-called 'smart' (bio)materials.In response to environmental cues like changes in pH, temperature, redox potential, or ionic strength, these structures can adapt their behavior or trigger desired reactions.This is an exciting property for novel engineering solutions in biotechnology and medicine [1][2][3].One example of such a material that has gained more and more attention since its introduction in the late 1960s is thermoresponsive polymers [4][5][6].Upon reaching a specific temperature, thermoresponsive polymers dispersed in a solvent change their conformation from an expanded, well-soluble state to a collapsed, poorly soluble globular state over a narrow temperature range [7].This process is reversible.A thermoresponsive polymer can exhibit a lower or upper critical solution temperature (LCST or UCST) and thereby decrease or increase its solvation, respectively, when the temperature is raised past its critical solution temperature (CST).The CST is concentration-and solvent-dependent.
What makes thermoresponsive polymers especially interesting for researchers is that adaptive behavior adds multifunctionality, which makes thermoresponsive polymers promising for applications in, e.g., tissue engineering, drug delivery, or catalysis [8][9][10].
The exact CST or temperature range at which the transition happens depends on the polymer and the solvent environment.Solvent polarity or changes to pH or ion concentration alter the CST of thermoresponsive polymers.For instance, intermolecular interactions in bulk deuterium oxide (D 2 O) are stronger compared to water.D 2 O molecules bind more strongly to polar groups of, e.g., polymer chains, and the resulting entropic penalty of exposed non-polar segments to the polar solvent molecules is higher [11].This is crucial because some essential analytical techniques rely on D 2 O as a measurement solvent.Prominent examples are nuclear magnetic resonance spectroscopy (NMR), small-angle neutron scattering (SANS), and neutron reflectometry (NR), which are powerful techniques for investigating polymer structures in bulk and at interfaces.However, applications are designed for biological fluids (H 2 O), where the polymer conformation and energetics could differ.A direct comparison of measurements with these techniques to complementary measurements by other techniques in normal water could be misleading.
Further, biological fluids contain high concentrations of Hofmeister series salts.The Hofmeister series describes salts according to their ability to affect the stability of proteins or polymers via their effect on the inter-water bonding network [12,13] and polar bonds of the polymer [14,15].Historically, these species were often described as 'structure-making' or 'structure-breaking' compounds because of their effect on bulk water.Regarding the stability of proteins, kosmotropes are known to promote and stabilize their defined folded conformation.Chaotropes, on the other hand, lead to the denaturation of proteins [12,16].More recent findings, notably contributed by the Cremer group, suggest that the actual mechanism behind these effects is connected to the relative ion polarizabilities and the specific ion interactions directly with the macromolecular solutes and their immediately adjacent hydration shells [14,15].Moreover, the intermolecular interactions of H 2 O or D 2 O molecules differ when such solutes are added [17][18][19].The influence of Hofmeister ions on the CST can be huge and vary depending on the polymer [20], which agrees with the results of Cremer et al.
Despite the use of D 2 O instead of H 2 O in crucial analytical techniques to study (bio)polymer conformations and their thermoresponsive properties, there is a lack of studies on the differences in the thermal solvation transition between them.Additionally, given the importance of the effect of Hofmeister ions on the solvent structure for polymer stability, there is a lack of data on how they affect structure in D 2 O.This is a severe deficiency of the current literature, given that much of the characterization of polymer properties is performed in D 2 O and not H 2 O and, further, that these investigations are performed in pure D 2 O without the presence of Hofmeister series ions.Still, such measurements are compared directly to other results obtained under physiological conditions in H 2 O to draw conclusions for designing applications.Additionally, a disproportionate amount of research on the thermal transition of polymers in water was performed on poly(Nisopropyl acrylamide) (PNiPAm).It is the most commonly investigated thermoresponsive polymer with applications in biotechnology [21][22][23].It has, e.g., been used as a surface modification to create planar substrates for cultivating cell sheets, first demonstrated by Okano et al. in 1993 [24].This success has sparked extensive research on various medical applications [25][26][27][28].Other popular thermoresponsive polymers, e.g., poly(2isopropyl-2-oxazoline) (PiPOx), are less thoroughly investigated with salts co-solved during measurements.PiPOx is a promising material for biomedical applications because PiPOx exhibits better biocompatibility than PNiPAm, reacts more strongly to environmental changes, and has a tunable CST closer to human body temperature [29,30].
Published research on thermoresponsive polymers like PNiPAm or PiPOx primarily covers specific cases, e.g., investigating these polymers crosslinked in hydrogels, grafted to surfaces, or as part of more complex copolymers [31][32][33].Our study tries to fill the gap with data connecting the CST of PNiPAm and PiPOx to solvent and co-solute properties that include D 2 O. Two complementary experimental techniques proper for both D 2 O and H 2 O were applied to investigate the CST: dynamic light scattering (DLS) and differential scanning calorimetry (DSC).DLS and DSC are two of the most frequently used techniques for determining critical solution temperatures.These techniques provide complementary information about the investigated systems, as they measure the CST in fundamentally different ways.By including data collected with both methods in this work, we aim to paint a more complete picture of the transition of thermoresponsive polymers than is available in the existing literature [20,34,35].

Effect of Polymer Concentration on the CST in H 2 O and D 2 O
CST values were extracted from DLS and DSC measurements for PNiPAm and PiPOx of 21,000 g mol −1 , respectively.DLS determines particle size from fluctuations in the scattered light intensity.The total scattered light intensity increases when aggregates are formed, which can also be measured sensitively with a DLS instrument.Once the CST has been reached, aggregates are formed.They sediment due to gravity and move in the bulk medium due to thermal convection in addition to Brownian motion.As a result, the recorded light intensity does not monotonously increase as aggregation sets in; it is susceptible to fluctuations depending on the movement of large scattering objects within the sampling volume of the DLS.In this study, DLS-derived CST values were, therefore, extracted from the initial increase in the scattering intensity as a function of temperature.A graphical illustration of the selection is shown in Figure S1 in the Supplementary Information.The selected points correspond to the temperature at which the collapsing polymer coils detectably start aggregating in response to their thermally induced reduced solvation.In contrast, DSC measures the energetics of the coil-globule transition.We recorded the temperature at the transition peak maximum as the CST.Although this point does not represent the start of the transition, it facilitates comparing the stability of polymers, as was shown in other studies [36,37].
In Figure 1, CST values of differently concentrated PNiPAm and PiPOx samples in H 2 O and D 2 O are shown (see Table S1 in the Supplementary Material for exact values).Results from DSC and DLS experiments with PiPOx correspond well, as CST values follow the same trend of decreased temperatures with increasing polymer concentration.The CST determined by DLS is approximately 4 • C lower than for DSC for low (0.1 mg mL −1 ) polymer concentrations, which decreases to 1 • C for high (10 mg mL −1 ) concentrations.These values are close to the temperature difference between the peak onsets and peak maxima of the DSC thermograms.These also vary with concentration and are approximately 4 • C lower at 0.1 mg mL −1 and 1 • C lower at 10 mg mL −1 (see Table S2).The CST decreases monotonously and quasi-linearly in the investigated concentration regime in a semi-log plot.The CST changes as a function of concentration measured by DSC are very similar in the case of all polymer and solvent combinations.The CST drops approximately 5 • C from 0.1 to 10 mg mL −1 .Measured by DLS, the CST drops by 5 • C for PiPOx but slightly more steeply for PNiPAm, with close to 10 • C in H 2 O and close to 7 • C in D 2 O, in the same concentration range.A decrease of approximately 3 • C for an increase in polymer concentration from 0.1 mg mL −1 to 1 mg mL −1 was reported by Uyama and Kobayashi in 1992 for PiPOx of comparable molecular weight (M w = 18.9 kDa) [38].Our results are in the same range as their observations, which they made visually using turbidimetry.Results reported by Pamies et al. show a CST shift of PNiPAm of about 4 • C between 0.1 and 1 mg mL −1 , which corresponds well to our findings, considering they measured PNiPAm at a lower molecular weight (M w = 13.4 kDa) [39].
Comparing H 2 O and D 2 O, the CSTs determined by DSC are lower in D 2 O for both PiPOx and PNiPAm, with, on average, 1.0 • C and 1.5 • C, respectively.The dependence of the difference as a function of concentration is moderate, with 0.72 • C difference for the 10 mg mL −1 and 1 mg mL −1 samples and 1.12 • C in the case of the 0.1 mg mL −1 sample.PiPOx shows a similar dependence on the solvent measured by DLS to that observed by DSC.The CST measured by DLS is approximately 1.0 • C lower in D 2 O.In contrast, PNiPAm has a higher CST in D 2 O than in H 2 O, as measured by DLS at higher concentrations.Only at 0.1 mg mL −1 is a higher CST in H 2 O observed.Other studies have reported higher CST values for PNiPAm in D 2 O as well, although the measured systems differ from ours: Xiaohui Wang and Chi Wu measured a 1.5 • C upwards shift of the CST in D 2 O for huge PNiPAm molecules in highly dilute dispersions (13,000 kDa, 6.3 × 10 −4 mg mL −1 ) using a combination of static and dynamic light scattering methods [40].Shirota et al. aimed to determine the CST of PNiPAm hydrogels by microscopically observing the volume phase transition and also reported a higher CST in D 2 O of approximately 1 • C [31].We note that all these studies also relied on observing the aggregation of PNiPAm at high local concentrations rather than the solvation transition directly.Comparing H2O and D2O, the CSTs determined by DSC are lower in D2O for both PiPOx and PNiPAm, with, on average, 1.0 °C and 1.5 °C, respectively.The dependence of the difference as a function of concentration is moderate, with 0.72 °C difference for the 10 mg mL −1 and 1 mg mL −1 samples and 1.12 °C in the case of the 0.1 mg mL −1 sample.PiPOx shows a similar dependence on the solvent measured by DLS to that observed by DSC.The CST measured by DLS is approximately 1.0 °C lower in D2O.In contrast, PNiPAm has a higher CST in D2O than in H2O, as measured by DLS at higher concentrations.Only at 0.1 mg mL −1 is a higher CST in H2O observed.Other studies have reported higher CST values for PNiPAm in D2O as well, although the measured systems differ from ours: Xiaohui Wang and Chi Wu measured a 1.5 °C upwards shift of the CST in D2O for huge PNiPAm molecules in highly dilute dispersions (13,000 kDa, 6.3 × 10 mg mL ) using a combination of static and dynamic light scattering methods [40].Shirota et al. aimed to determine the CST of PNiPAm hydrogels by microscopically observing the volume phase transition and also reported a higher CST in D2O of approximately 1 °C [31].We note that all these studies also relied on observing the aggregation of PNiPAm at high local concentrations rather than the solvation transition directly.
Figure 2a shows DSC thermograms of PNiPAm in H2O and D2O.The long high-temperature tails hint at a more complex process than a simple two-state transition.In contrast, the PiPOx thermograms shown in Figure 2c,d suggest that the transitions differ less between the highest and lowest concentrations than for PNiPAm.In particular, the heating curves of 10 mg mL −1 PNiPAm plotted in panels (a) and (b) of Figure 2 show more than one peak after a very sharp initial incline.Figure 2a shows DSC thermograms of PNiPAm in H 2 O and D 2 O.The long hightemperature tails hint at a more complex process than a simple two-state transition.In contrast, the PiPOx thermograms shown in Figure 2c,d suggest that the transitions differ less between the highest and lowest concentrations than for PNiPAm.In particular, the heating curves of 10 mg mL −1 PNiPAm plotted in panels (a) and (b) of Figure 2 show more than one peak after a very sharp initial incline.

Hofmeister Series Anions and Solvent Isotope Effect
Figure 3 shows the CST values of both polymers derived from DLS and DSC experiments.The CST was measured in the pure solvents, as well as in the presence of differently concentrated potassium salts of four different Hofmeister series anions: thiocyanate (SCN − ), chloride (Cl − ), hydrogen phosphate (HPO 2 − 4 ), and sulfate (SO 2 − 4 ), representing chaotropic and kosmotropic anions of the Hofmeister series.Of these, SCN − is a strong chaotrope, Cl − a weak chaotrope, and HPO 2 − 4 and SO 2 − 4 strong kosmotropes [12].It is noticeable that with increasing salt concentration, CSTs shift further away from the values in pure solvent (see also Table S3).This is true for both polymers in H 2 O and D 2 O, regardless of the measurement method.However, up to 10 mM concentration, all the salt effects are minor or negligible.For example, the CST value of PiPOx in 1 mM KSCN is the same as for 1 mM K 2 HPO 4 in H 2 O (both 41.2 • C) and even slightly lower in D 2 O (40.0 • C for 1mM KSCN compared to 40.2 • C of PiPOx in 1 mM K 2 HPO 4 ).The chaotropic properties of SCN − are not visible at the lowest concentration.These results show that significant changes to the CST, as measured by both DLS and DSC, only occur for ionic strengths in the 100 mM range.However, DLS measurements of PNiPAm or PiPOx in solutions of physiological ionic strength (160 mM potassium salts) clearly show how chaotropic and kosmotropic substances from the Hofmeister series affect polymer stability.

Hofmeister Series Anions and Solvent Isotope Effect
Figure 3 shows the CST values of both polymers derived from DLS and DSC experiments.The CST was measured in the pure solvents, as well as in the presence of differently concentrated potassium salts of four different Hofmeister series anions: thiocyanate (SCN -), chloride (Cl -), hydrogen phosphate (HPO ), and sulfate (SO ), representing chaotropic and kosmotropic anions of the Hofmeister series.Of these, SCN -is a strong chaotrope, Cl -a weak chaotrope, and HPO and SO strong kosmotropes [12].It is noticeable that with increasing salt concentration, CSTs shift further away from the values in pure solvent (see also Table S3).This is true for both polymers in H2O and D2O, regardless of the measurement method.However, up to 10 mM concentration, all the salt effects are minor or negligible.For example, the CST value of PiPOx in 1 mM KSCN is the same as for 1 mM K HPO in H2O (both 41.2 °C) and even slightly lower in D2O (40.0 °C for 1mM KSCN compared to 40.2 °C of PiPOx in 1 mM K HPO ).The chaotropic properties of SCN -are not visible at the lowest concentration.These results show that significant changes to the CST, as measured by both DLS and DSC, only occur for ionic strengths in the 100 mM range.However, DLS measurements of PNiPAm or PiPOx in solutions of physiological ionic strength (160 mM potassium salts) clearly show how chaotropic and  C. The chaotropic anion SCN − promotes hydration of the polymer chain, increasing the CST.However, the effect is not as pronounced for PNiPAm as the effect of the kosmotropic ions.In the case of PNiPAm in H 2 O, low concentrations of KSCN do not increase the CST above the value measured in pure water.The same result is observed for PiPOx samples measured with both DLS and DSC for low ionic strengths, but the chaotropic effect of KSCN is on par with the kosmotropic ions at physiological ionic strength, shifting the CST higher by about 10 • C for PiPOx.
kosmotropic substances from the Hofmeister series affect polymer stability.Figure 4 highlights these differences by comparing the CST of both polymers in a pure solvent and the presence of 160 mM salts.The kosmotropic anion concentration generally affects PiPOx in the same way in H2O and D2O.Figures 3 and 4 show how high concentrations of strong kosmotropes like SO and HPO drastically reduce the CST of both polymers in pure H2O or D2O by approximately 7-10 °C.The chaotropic anion SCN promotes hydration of the polymer chain, increasing the CST.However, the effect is not as pronounced for PNiPAm as the effect of the kosmotropic ions.In the case of PNiPAm in H2O, low concentrations of KSCN do not increase the CST above the value measured in pure water.The same result is observed for Comparing DSC peak maxima, CST shifts between H 2 O and D 2 O are generally smaller than 1 • C for PiPOx in the presence of all salt concentrations (see Table S3).The same is true for CST values determined with DLS.The DSC measurements for PNiPAm are significantly different in 160 mM ionic strength, where the change in the CST values in D 2 O is lower than in H 2 O, generally with a difference in the shift of ~2 • C. Notably, the change of the CST for the chaotropic ion SCN − is about 1.8 • C higher in D2O than in H 2 O, indicating that PNiPAm retains a higher hydration in H 2 O than in D 2 O.An outlier compared to the other ions is KCl, for which H 2 O seems to induce a lower effect on the hydration than D 2 O for both PNiPAm and PiPOx.

Transition Energetics
In Figure 2a,b, very large transition enthalpies per monomer unit are observed for PNiPAm (0.1 mg mL −1 and 1 mg mL −1 ) measured in D 2 O compared to in H 2 O.These samples require approximately twice the enthalpy per monomer unit compared to the same sample in H 2 O (11,838 J mol −1 and 11,459 J mol −1 versus 4178 J mol −1 and 5568 J mol −1 ; see Table 1).In comparison, Diab et al. reported a transition enthalpy of about 3347 J mol −1 for 1 mg mL −1 PNiPAm (13 kDa) in H 2 O [41], which is similar to our result for the same concentration.They did not, however, measure PNiPAm in D 2 O. PiPOx did not show such significant differences in transition enthalpy and had a more uniform peak shape (Figure 2c,d).In the same study, Diab et al. also measured transition enthalpies of PiPOx (5.7 kDa, 1 mg mL −1 ) of 5648 J mol −1 per monomer unit in H 2 O and 5983 J mol −1 in D 2 O.Even though the PiPOx measured in their experiments was almost four times smaller than ours, the measured transition enthalpies are in the same range.In our study, however, there seems to be a weak correlation of a moderate increase in transition enthalpy for both polymers in H 2 O.In D 2 O, there are only minor differences in transition enthalpy for PiPOx.Still, PNiPAm shows a dramatic difference in peak C p and transition enthalpy for the lower concentrations compared to the highest.Both decrease with increasing concentration (Table 1 and Figure 2).

PNiPAm
∆H monomer [J mol −1 ] c [mg mL −1     Data presented in Figure 6 shows that the multi-step conformational change of PiPOx in the presence of medium to high concentrations of KSCN requires far more heat than in the presence of other salts, with ∆H mon ranging from 7838 J mol −1 (PiPOx in a solution of 10 mM KSCN in H 2 O) to 18,000 J mol −1 (PiPOx in D 2 O + 160 mM KSCN), compared to other samples with transition enthalpies mostly between 4000 and 6000 J mol −1 .This chaotrope thereby uniquely stabilizes the solvated polymer, as also evidenced by the higher CST.Although 160 mM KCl still has a kosmotropic effect on the CST, it produces a much higher transition enthalpy, especially in H 2 O; it displays pronounced double-peaks and transition enthalpies of 9135 J mol −1 in H 2 O and 9514 J mol −1 in D 2 O at 160 mM (Figure 5e,f).In the PNiPAm samples, there seems to be no connection between CST and transition enthalpy.Values for ∆H mon vary by approximately only 12% between samples of the same salt concentration in H 2 O and D 2 O, except for PNiPAm in pure D 2 O, for which it is almost twice as high as in H 2 O or in D 2 O salt solutions (11,459 J mol −1 ; Figure 6 and Table S4).
Data presented in Figure 6 shows that the multi-step conformational change of PiPOx in the presence of medium to high concentrations of KSCN requires far more heat than in the presence of other salts, with Δ ranging from 7838 J mol −1 (PiPOx in a solution of 10 mM KSCN in H2O) to 18,000 J mol −1 (PiPOx in D2O + 160 mM KSCN), compared to other samples with transition enthalpies mostly between 4000 and 6000 J mol −1 .This chaotrope thereby uniquely stabilizes the solvated polymer, as also evidenced by the higher CST.Although 160 mM KCl still has a kosmotropic effect on the CST, it produces a much higher transition enthalpy, especially in H2O; it displays pronounced double-peaks and transition enthalpies of 9135 J mol −1 in H2O and 9514 J mol −1 in D2O at 160 mM (Figure 5e,f).In the PNiPAm samples, there seems to be no connection between CST and transition enthalpy.Values for Δ vary by approximately only 12% between samples of the same salt concentration in H2O and D2O, except for PNiPAm in pure D2O, for which it is almost twice as high as in H2O or in D2O salt solutions (11,459 J mol −1 ; Figure 6 and Table S4).

Discussion
Even though PNiPAm and PiPOx are structural isomers, they did not respond in the same way to being solvated in D2O instead of H2O.PiPOx clearly decreases its CST in D2O.D2O seems to decrease the CST for PNiPAm as well, at least when the polymer is solvated at a low concentration, but the DSC measurements reveal a possible two-step transition that becomes more accentuated in D2O and leads to a strong concentration dependence (Figure 2).Hence, the CST determined from DLS is higher in D2O than in H2O, while the CST determined from the DSC peak of the main transition is lower in D2O than in H2O.Previously published literature does not report similar features in the DSC curves, but experimental conditions differ from the measurements conducted in this study.For instance, Qiu et al., did not observe these features for PNiPAm of molecular weights between 7.6 and 44.5 kDa, and with other end-groups like hydroxyethyl, n-butyl, or isobutylsulfanylthiosulfanyl [42].To investigate this phenomenon in more detail, follow-up research would be required, especially to pinpoint if the switch from H2O to D2O influences the hydration of different hydrogen-bonding groups on the polymers differently.
Figure 2 also reveals that the phase transition is sharper for PiPOx in both H2O and D2O, especially at a high polymer concentration (10 mg mL −1 ).An in-depth study of the demixing and remixing kinetics of aqueous PiPOx solutions conducted by Zhao et al. in

Discussion
Even though PNiPAm and PiPOx are structural isomers, they did not respond in the same way to being solvated in D 2 O instead of H 2 O. PiPOx clearly decreases its CST in D 2 O. D 2 O seems to decrease the CST for PNiPAm as well, at least when the polymer is solvated at a low concentration, but the DSC measurements reveal a possible two-step transition that becomes more accentuated in D 2 O and leads to a strong concentration dependence (Figure 2).Hence, the CST determined from DLS is higher in D 2 O than in H 2 O, while the CST determined from the DSC peak of the main transition is lower in D 2 O than in H 2 O. Previously published literature does not report similar features in the DSC curves, but experimental conditions differ from the measurements conducted in this study.For instance, Qiu et al., did not observe these features for PNiPAm of molecular weights between 7.6 and 44.5 kDa, and with other end-groups like hydroxyethyl, n-butyl, or isobutylsulfanylthiosulfanyl [42].To investigate this phenomenon in more detail, follow-up research would be required, especially to pinpoint if the switch from H 2 O to D 2 O influences the hydration of different hydrogen-bonding groups on the polymers differently.
Figure 2 also reveals that the phase transition is sharper for PiPOx in both H 2 O and D 2 O, especially at a high polymer concentration (10 mg mL −1 ).An in-depth study of the demixing and remixing kinetics of aqueous PiPOx solutions conducted by Zhao et al. in 2010 attributes this to a faster thermal response of PiPOx compared to PNiPAm [43].This can be explained by PiPOx forming relatively weaker hydrogen bonds than PNiPAm in solution, as it lacks amide groups in its side chain.
Compared to the Hofmeister series ions' effects on the CST of PNiPAm and PiPOx, we observe that D 2 O has a relatively small influence.Notably, 160 mM strong kosmotropes and chaotropes solutions influenced the CSTs and the energetics of the solubility transition the most.Still, the difference between H 2 O and D 2 O was on par or larger than the effect of Hofmeister salts up to salt concentrations of 10 mM, especially for PiPOx.Both polymers significantly decrease their CST in response to strong kosmotropes (SO 2 − 4 and HPO 2 − 4 ) in D 2 O and H 2 O.
Interestingly, the relative effect of D 2 O on the CST (in particular measured by DLS) and the transition energy were most pronounced for SCN − and Cl − , which are usually classified as strong and weak chaotropes, respectively.A first explanation could be that anions like SCN − are weaker hydrated in D 2 O than water and bind closer to the polymer chain.This could lead to enhanced stabilization, i.e., a higher CST [11,44].Hence, nonkosmotropes might be more influenced by a shift from H 2 O to D 2 O.It is noteworthy that although Cl -had this similarity with the strong chaotropes SCN -and is usually classified as a weak chaotrope, its effect on the CST of both polymers was rather that of a kosmotropes, i.e., a reduction in CST (Figure 4).
Cremer et al. similarly argue that chaotropes can stabilize amide side groups of PNiPAm and increase polymer solubility [15].A schematic illustration of the proposed mechanism is shown in Figure 7. On the one hand, anions can affect the hydrogen bonding of hydrophilic structures (shown in blue in Figure 7) by polarizing the associated water molecules.They can additionally increase the interfacial tension between the hydrated structures and the cavity surrounding the apolar backbone and isopropyl side chains (indicated in yellow in Figure 7).These two effects could be responsible for destabilizing the polymers, therefore decreasing the CST.Additionally, the anions might bind directly to the amide groups, which should increase the CST.
2010 attributes this to a faster thermal response of PiPOx compared to PNiPAm [43].This can be explained by PiPOx forming relatively weaker hydrogen bonds than PNiPAm in solution, as it lacks amide groups in its side chain.
Compared to the Hofmeister series ions' effects on the CST of PNiPAm and PiPOx, we observe that D2O has a relatively small influence.Notably, 160 mM strong kosmotropes and chaotropes solutions influenced the CSTs and the energetics of the solubility transition the most.Still, the difference between H2O and D2O was on par or larger than the effect of Hofmeister salts up to salt concentrations of 10 mM, especially for PiPOx.Both polymers significantly decrease their CST in response to strong kosmotropes (SO and HPO ) in D2O and H2O.
Interestingly, the relative effect of D2O on the CST (in particular measured by DLS) and the transition energy were most pronounced for SCN -and Cl -, which are usually classified as strong and weak chaotropes, respectively.A first explanation could be that anions like SCN -are weaker hydrated in D2O than water and bind closer to the polymer chain.This could lead to enhanced stabilization, i.e., a higher CST [11,44].Hence, nonkosmotropes might be more influenced by a shift from H2O to D2O.It is noteworthy that although Cl -had this similarity with the strong chaotropes SCN -and is usually classified as a weak chaotrope, its effect on the CST of both polymers was rather that of a kosmotropes, i.e., a reduction in CST (Figure 4).
Cremer et al. similarly argue that chaotropes can stabilize amide side groups of PNiPAm and increase polymer solubility [15].A schematic illustration of the proposed mechanism is shown in Figure 7. On the one hand, anions can affect the hydrogen bonding of hydrophilic structures (shown in blue in Figure 7) by polarizing the associated water molecules.They can additionally increase the interfacial tension between the hydrated structures and the cavity surrounding the apolar backbone and isopropyl side chains (indicated in yellow in Figure 7).These two effects could be responsible for destabilizing the polymers, therefore decreasing the CST.Additionally, the anions might bind directly to the amide groups, which should increase the CST.Related to these observations, the solubility transition in the presence of chaotropic Hofmeister series salts, SCN and Cl , seems to include at least two solvation transitions following upon each other for PiPOx in H2O (Figure 5).Remarkably, only one peak is observed in D2O for the same sample.It makes determining the CST using DSC by the peak Cp value ambiguous in H2O, but it also could elucidate additional features of the Related to these observations, the solubility transition in the presence of chaotropic Hofmeister series salts, SCN − and Cl − , seems to include at least two solvation transitions following upon each other for PiPOx in H 2 O (Figure 5).Remarkably, only one peak is observed in D 2 O for the same sample.It makes determining the CST using DSC by the peak C p value ambiguous in H 2 O, but it also could elucidate additional features of the solvation transition.Tentatively, different parts of the polymer chains become dehydrated at different temperatures, reflecting preferential interactions of the anion with parts of the polymer.This could lead to significant differences between the CST determined by turbidity or DLS measurements and those determined by DSC.Unlike PNiPAm, PiPOx has an amide group in its backbone.Stronger hydration of SCN − in water than in D 2 O may allow the anion to stabilize the polymer backbone longer, leading to dehydration of the side chains first, which might cause the multiple transitions for PiPOx samples with KSCN (or KCl) solved in H 2 O as well as the higher CST than PNiPAm.
Curiously, polymer concentration greatly influenced the transition enthalpy of PNi-PAm in D 2 O.The influence of polymer concentration on the CST is well known and was observed for both polymers and solvents in our study, but this effect on the transition enthalpy stands out and could not be fully explained [43,45].Further, the observations of a two-times-higher enthalpy of the transition in D 2 O than H 2 O, which strongly decreased at a high polymer concentration, highlights that the intricate balance of several parameters of the investigated system, like intramolecular interactions and the breaking of intermolecular hydrogen bonds, must be considered if one wants to determine CST in a specific environment, in particular in D 2 O.
Our observation of multiple transitions affected by the polarity of the solvent and the presence of Hofmeister anions requires further investigation of the molecular weight dependence of these features and whether they respond to different sidechain modifications.Previous publications have shown that the CST is decreased with increasing molecular weight for PNiPAm and PiPOx [41,46] and that sidechain modifications and polymer morphology, e.g., grafting, greatly influence the CST and internal coil and coil-coil desolvation transitions [20,47,48].
Finally, in this work, we focused on differences in the solubility transitions in H 2 O and D 2 O, respectively.One could presume that mixtures of H 2 O and D 2 O would influence the solubility according to the rule of mixtures, i.e., by a simple interpolation between the responses in each individual solvent.Although such behaviors are often observed for solvent mixtures, the local activity of ions and solvents on different parts of the polymer chain and side groups indicated by our data suggest that this assumption warrants further investigation.
Synthesis was conducted by mixing 45 mL (or 1 equivalent) of 2-methylpropanenitrile (Sigma-Aldrich, St. Louis, MI, USA) with 36 mL (1.2 eq.) ethanolamine (Sigma-Aldrich, St. Louis, MI, USA).Zinc acetate dihydrate (Sigma-Aldrich, St. Louis, MI, USA) was added to catalyze the reaction (2.2038 g or 0.02 eq.).Heated to 130 • C in an oil bath and equipped with a reflux cooler, the solution was left to react in an inert atmosphere for one day.Formed ammonia was absorbed in hydrochloric acid.The product was dissolved in dichloromethane (DCM, Sigma-Aldrich, St. Louis, MI, USA) and extracted with MQ-H 2 O until the pH of the aqueous phase was neutral.The organic phase was dried with sodium sulfate (Sigma-Aldrich, St. Louis, MI, USA).The solid was removed by filtration, and the product was separated from the solvent by vacuum distillation.After adding calcium hydride (Sigma-Aldrich, St. Louis, MI, USA), the solution was stirred under inert conditions to remove residual water.Finally, the product was purified using distillation with a Vigreux column at 50 • C and 50 mbar.

Poly(2-isopropyl-2-oxazoline)
Polymerization of 2-Isopropyl-2-oxazoline followed Schroffenegger et al., who describe a cationic ring-opening polymerization (CROP) [20].Initially, 3 mL of the monomer and 9 mL N,N-dimethylacetamide anhydrous (DMA, Sigma-Aldrich, St. Louis, MI, USA) were mixed with 38 µL methyl-p-tosylate (Sigma-Aldrich, St. Louis, MI, USA) and left to react at 90 • C overnight.The reaction was quenched with sodium hydroxide and stirred for three hours at 50 • C, then at room temperature until the next day.The product was obtained by stepwise precipitation of the reaction mixture in approximately 25 mL of a 1:1 mixture of n-hexane (Sigma-Aldrich, St. Louis, MI, USA) and diethyl ether (Carl Roth, Karlsruhe, Germany).The precipitate was then dissolved in DCM and purified by distillation.

Poly(N-isopropylacrylamide)
This synthesis, described in Kurzhals et al., is an acid-terminated atomic transfer radical polymerization (ATRP) [51].First, the monomer N-isopropyl acrylamide (NiPAm, Sigma-Aldrich, St. Louis, MI, USA) is recrystallized by dissolving 2 g NiPAm in 25 mL toluene (Carl Roth) and 35 mL n-hexane and storing it at −20 • C overnight.The precipitate was then filtered and rinsed with n-hexane, followed by vacuum distillation to remove the solvent.

Polymer Characterization
The molecular weight (M W ) and the polydispersity index (PDI) of PNiPAm and PiPOx were determined with gel permeation chromatography (GPC) based on their R G against a standard of polystyrene in N,N-dimethylformamide (DMF) using a Malvern Viscotek GPC max and OmniSEC 5.12 software (Malvern Panalytical, Malvern, UK) (see Figures S6 and S10).For the measurement, 3.5 mg polymer was dissolved in 1 mL DMF containing 0.05 mol L −1 lithium bromide (Sigma-Aldrich, St. Louis, MI, USA).Then, 50 µL of sample was measured at a flow rate of 9.5 mL min −1 at 60 • C.
Successful synthesis in terms of correct chemical structure was investigated with nuclear magnetic resonance ( 1 H NMR and 13 C NMR) with a BRUKER AV III 300 MHz spectrometer (Bruker Austria GmbH, Vienna, Austria).A total of 50 mg mL −1 of either polymer was used to record the respective spectra in deuterated trichloromethane (Sigma-Aldrich, St. Louis, MI, USA).The chemical shifts (δ in ppm) were referenced to tetramethylsilane (TMS, Sigma-Aldrich, St. Louis, MI, USA); see Figures S3 and S4.
Infrared spectroscopy was performed with an FT-IR ATR spectrometer (Vertex 70, Bruker Austria GmbH, Vienna, Austria).Between 3000 cm −1 and 2800 cm −1 , the PNiPAm spectrum shows the C-H stretching region.Between 1700 and 1300 cm −1 , the fingerprint region, including the amide region with two strong peaks at approximately 1631 cm −1 and 1539 cm −1 , is found.Peaks of the C-H deformation region are visible at 1462 cm −1 and 1388 cm −1 .The PiPOx FT-IR spectrum also shows the C-H stretching region between 3000 cm −1 and 2800 cm −1 .Similarly, a strong peak at ~1620 cm −1 is attributed to the amide group.Between 1473 cm −1 and 1363 cm −1 , the C-H deformation mode is found.The respective spectra are shown in Figures S5 and S9.
The values for molecular weight and polydispersity obtained with GPC are collected in Table S5.They confirm that both polymers are of comparable size and low polydispersity. 1H NMR and 13 C NMR spectra reveal that both polymers have the desired structure.The spectra are presented in Figures S3 and S4 for PNiPAm and Figures S7 and S8 for PiPOx, respectively, and the chemical shifts are provided above.The 1 H NMR spectra show trace amounts of DCM from the synthesis.Its influence on the polymers' thermal response is expected to be marginal.Importantly, the trace amounts of DCM will be the same in D 2 O and H 2 O samples and scale stoichiometrically with the polymer concentration in all samples.Hence, all relative comparisons are unaffected.

Determination of the Critical Solution Temperature and Transition Enthalpies
Solutions of PNiPAm and PiPOx in three different concentrations were prepared in H 2 O and D 2 O (0.1 mg mL −1 , 1 mg mL −1 , and 10 mg mL −1 ).Additionally, 1 mg mL −1 solutions of each polymer were prepared in solvent containing one of four potassium salts in different concentrations (160 mM, 10 mM, or 1 mM of K 2 SO 4 (≥99.0%,Sigma-Aldrich, St. Louis, MI, USA), K 2 HPO 4 (≥99%, Riedel-de Haën, Seelze, Germany), KCl (>99.5%,Fluka BioChemika, Ronkonkoma, NY, USA) and KSCN (≥98.0%,Merck, Rahway, NJ, USA), respectively).DLS size measurements were recorded with a step size of 1 kelvin and an equilibration time of 60 s.Close to the expected CST, increments were reduced to 0.2 K, and equilibration time after each step was increased to 120 s for higher precision.At each point, three individual measurements were recorded with an automatically set number of runs and then averaged.All samples were measured with a Zetasizer Nano ZS (Malvern Panalytical, Malvern, UK) in backscatter mode.CST values were extracted at the initial increase in the recorded scattering patterns (see also Figure S1).For DSC experiments, 325 µL of each sample was scanned from 20 • C to 80 • C at a rate of 1 • C per minute with a MicroCal PEAQ-DSC Automated (Malvern Panalytical, Malvern, UK).Before starting the measurements, the system was thermally equilibrated for 5 min, and 3 purge refills of the autosampler were performed between samples.CST values were extracted from the recorded thermograms at the transition peak maximum.
Transition enthalpy values are taken directly from the MicroCal PEAQ-DSC software 1.53 and obtained by integrating the thermograms after buffer subtraction and baseline correction according to Kirchoff's law: where ∆H is the change in enthalpy, C P the heat capacity at constant pressure, and T 1 and T 2 the temperatures before and after the transition, respectively.

Conclusions
We conclude that the thermoresponsive properties of polymers quantitatively differ in D 2 O and H 2 O, but the absolute differences depend on the polymer and solution conditions.Predominantly, D 2 O decreased the CST in the pure solvent compared to H 2 O.The observed effects of changing from H 2 O to D 2 O were smaller than those of other commonly varied parameters, such as polymer concentration, molecular weight, copolymerization, or the presence of physiological concentrations of Hofmeister series ions [52][53][54].Still, they are far from negligible given that they amount to shifts of several degrees of the CST, which could increase by the addition of Hofmeister series ions, in particular the chaotropes we tested.Our results strongly imply that the effects of different environmental parameters, i.e., anion species and concentration, are not additive with a change from H 2 O to D 2 O.For instance, the dehydration of different molecular groups in a polymer can be differently affected, as well as their interactions with Hofmeister series anions, which, in turn, influence the overall thermoresponsive behavior.This was tentatively observed for the influence of amine polar bonds and chaotropic anions.These polymer-internal changes to the transition could be especially important if more complicated polymer morphologies, such as dendritic polymers or grafted polymers, are studied.Our findings regarding multiple transitions within PiPOx in the presence of chaotropes indicate the need to extend our study to a larger set of polymer side groups, molecular weights, chain ends, and topologies relevant to applications.The strong influence of physiological concentrations of Cl − , affecting the solvation transition in D 2 O in a non-additive way, highlights that care must be taken to compare results obtained by techniques relying on D 2 O and H 2 O, respectively, for conclusions regarding designs for biomedical applications.

Figure 1 .
Figure 1.Effect of solvent and polymer concentration on the CST (PiPOx and PNiPAm: 21 kDa).Black lines: CST values of PNiPAm, red lines: CST values of PiPOx; solid lines: polymers dispersed in H2O, dashed lines: polymers dispersed in D2O.(a) Measurements with DLS; (b) measurements with DSC.

Figure 1 .
Figure 1.Effect of solvent and polymer concentration on the CST (PiPOx and PNiPAm: 21 kDa).Black lines: CST values of PNiPAm, red lines: CST values of PiPOx; solid lines: polymers dispersed in H 2 O, dashed lines: polymers dispersed in D 2 O. (a) Measurements with DLS; (b) measurements with DSC.

Figure 2 .
Figure3shows the CST values of both polymers derived from DLS and DSC experiments.The CST was measured in the pure solvents, as well as in the presence of differently concentrated potassium salts of four different Hofmeister series anions: thiocyanate (SCN − ), chloride (Cl − ), hydrogen phosphate (HPO 2 − 4 ), and sulfate (SO 2 − 4 ), representing chaotropic and kosmotropic anions of the Hofmeister series.Of these, SCN − is a strong chaotrope, Cl − a weak chaotrope, and HPO 2 − 4 and SO 2 − 4 strong kosmotropes[12].It is noticeable that with increasing salt concentration, CSTs shift further away from the values in pure solvent (see also TableS3).This is true for both polymers in H 2 O and D 2 O, regardless of the measurement method.However, up to 10 mM concentration, all the salt effects are minor or negligible.For example, the CST value of PiPOx in 1 mM KSCN is the same as for 1 mM K 2 HPO 4 in H 2 O (both 41.2 • C) and even slightly lower in D 2 O (40.0 • C for 1mM KSCN compared to 40.2 • C of PiPOx in 1 mM K 2 HPO 4 ).The chaotropic properties of SCN − are not visible at the lowest concentration.These results show that significant changes to the CST, as measured by both DLS and DSC, only occur for ionic strengths in the 100 mM range.However, DLS measurements of PNiPAm or PiPOx in solutions of physiological ionic strength (160 mM potassium salts) clearly show how chaotropic and kosmotropic substances from the Hofmeister series affect polymer stability.Figure4highlights these

Figure 2 .
Figure 2. DSC recorded thermograms of PNiPAm and PiPOx (21 kDa) measured in (a,c) D 2 O and (b,d) H 2 O. Darker colors represent higher polymer concentrations.The kosmotropic anion concentration generally affects PiPOx in the same way in H 2 O and D 2 O. Figures 3 and 4 show how high concentrations of strong kosmotropes like SO 2 − 4 and HPO 2 − 4 drastically reduce the CST of both polymers in pure H 2 O or D 2 O by approximately 7-10• C. The chaotropic anion SCN − promotes hydration of the polymer chain, increasing the CST.However, the effect is not as pronounced for PNiPAm as the effect of the kosmotropic ions.In the case of PNiPAm in H 2 O, low concentrations of KSCN do not increase the CST above the value measured in pure water.The same result is observed for PiPOx samples measured with both DLS and DSC for low ionic strengths, but the chaotropic effect of KSCN is on par with the kosmotropic ions at physiological ionic strength, shifting the CST higher by about 10 • C for PiPOx.

Figure 5
Figure5presents thermograms of PiPOx in H 2 O and D 2 O co-solved with salts of increasing varying concentration.In contrast to PNiPAm, PiPOx is affected more profoundly in its transition in the presence of some salts (compare Figure5and FigureS2), as seen from the shoulders and a second peak.The most pronounced effects are observed for the strong chaotrope SCN − and the weak chaotrope Cl − in H 2 O.

Figure 6 .
Figure 6.Effect of salt concentration (1 mM, 10 mM, and 160 mM) on polymer transition enthalpies per monomer unit (∆H mon ) in H 2 O and D 2 O (PiPOx and PNiPAm: 21 kDa; 1 mg mL −1 ).Red: K 2 SO 4 , blue: K 2 HPO 4 , pink: KCl, green: KSCN; solid lines: measured in H 2 O, dashed lines: D 2 O. Plotted are ∆H mon values compared to H mon in the pure solution of (a) PNiPAm and (b) PiPOx, as a function of the concentration plotted on a logarithmic scale.

Figure 7 .
Figure 7. PNiPAm and PiPOx chemical structures with their polar and apolar regions marked.Yellow indicates exposed apolar moieties, blue polar moieties, and X − anions directly binding to the amide group.

Figure 7 .
Figure 7. PNiPAm and PiPOx chemical structures with their polar and apolar regions marked.Yellow indicates exposed apolar moieties, blue polar moieties, and X − anions directly binding to the amide group.

Table 1 .
DSC-derived transition enthalpies per monomer unit for differently concentrated PNiPAm and PiPOx dispersions (21 kDa) prepared in H 2 O and D 2 O.