Transected Tendon Treated with a New Fibrin Sealant Alone or Associated with Adipose-Derived Stem Cells

Tissue engineering and cell-based therapy combine techniques that create biocompatible materials for cell survival, which can improve tendon repair. This study seeks to use a new fibrin sealant (FS) derived from the venom of Crotalus durissus terrificus, a biodegradable three-dimensional scaffolding produced from animal components only, associated with adipose-derived stem cells (ASC) for application in tendons injuries, considered a common and serious orthopedic problem. Lewis rats had tendons distributed in five groups: normal (N), transected (T), transected and FS (FS) or ASC (ASC) or with FS and ASC (FS + ASC). The in vivo imaging showed higher quantification of transplanted PKH26-labeled ASC in tendons of FS + ASC compared to ASC on the 14th day after transection. A small number of Iba1 labeled macrophages carrying PKH26 signal, probably due to phagocytosis of dead ASC, were observed in tendons of transected groups. ASC up-regulated the Tenomodulin gene expression in the transection region when compared to N, T and FS groups and the expression of TIMP-2 and Scleraxis genes in relation to the N group. FS group presented a greater organization of collagen fibers, followed by FS + ASC and ASC in comparison to N. Tendons from ASC group presented higher hydroxyproline concentration in relation to N and the transected tendons of T, FS and FS + ASC had a higher amount of collagen I and tenomodulin in comparison to N group. Although no marked differences were observed in the other biomechanical parameters, T group had higher value of maximum load compared to the groups ASC and FS + ASC. In conclusion, the FS kept constant the number of transplanted ASC in the transected region until the 14th day after injury. Our data suggest this FS to be a good scaffold for treatment during tendon repair because it was the most effective one regarding tendon organization recovering, followed by the FS treatment associated with ASC and finally by the transplanted ASC on the 21st day. Further investigations in long-term time points of the tendon repair are needed to analyze if the higher tissue organization found with the FS scaffold will improve the biomechanics of the tendons.

Ideal biodegradable scaffolds for cells should provide them mechanical support, cells adhesion, proliferation and cellular differentiation [29]. According to James et al. [30], scaffolds for tendons should have high porosity, a large surface area and they should also mimic the native tendon ECM architecture, allowing nutrients diffusion and factors secreted by the cells, important for the stimulus of cell proliferation and synthesis of the ECM's components during tissue repair. In the present study, a new fibrin sealant (FS) derived from snake venom from Crotalus durissus terrificus was used with a biological three-dimensional scaffolding capacity of maintaining cell survival without interfering in its differentiation and with cell viability rates above 80% [29]. Gasparotto et al. [29] showed an excellent interaction of this FS with the ASC, due to its ability to induce the spontaneous adipogenic, chondrogenic and osteogenic lineages differentiation. This new FS is composed of a fibrinogen-rich cryoprecipitate extracted from the Bubalus bubalis buffalo's blood in association with a serine protease (a thrombin-like enzyme) extracted from Crotalus durissus terrificus venom [30][31][32][33]). According to Ferreira et al. [34], a thrombin-like enzyme, in the presence of calcium, acts upon the fibrinogen molecule transforming it into fibrin monomers forming a stable clot with adhesive, hemostatic and sealant effects [32,33,35].
Fibrin has been used for many years specially because it presents important characteristics like adhesive tissue or sealant to control bleeding, being used for a variety of surgical and repairing processes [29,36,37]. FS has positive effects for bone [38] and cardiac [39] tissue engineering, for peripheral nerve [40] or skin repair [41] among other applications. Still, concerns about the risk transmission of some viral diseases of commercial FS have increased researchers' interest to develop new sealants [34]. Then, the new FS used in the present study has advantages when compared to the commercially available FS products, since it is produced from animal components only, without risk of infectious diseases and lower costs of production [29].
Through the hypothesis of FS being a good scaffold for ASC, as much for tendon graft considering the FS malleability, which is important during limb movement in our model of tendon transection, the goals of this study are: (1) to evaluate the presence of ASC in the FS at the transected region of the tendons until the 21st day after injury; (2) to analyze the cells paracrine secretion through the expression of genes related to tendon remodeling; (3) to measure the organization of the collagen fibers and to quantify the total collagen content; and (4) to test the biomechanical properties of tendons.

Isolation of ASC and Ccell Culture
The procedure was done according to Yang et al. [42] with some modifications. Adipose tissue was obtained from the inguinal region of 10 male Lewis rats between 90-120 days. All surgical and experimental protocols were approved (01/12/2015) by the Institutional Committee for Ethics in Animal Research of the State University of Campinas-UNICAMP-Brazil (Protocol nº 3695-1). Adipose tissue was cut and washed in Dulbecco's modified phosphate buffered saline solution (DMPBS Flush without calcium and magnesium) containing 2% streptomycin/penicillin. Then, 0.2% collagenase (Sigma-Aldrich ® Inc., Saint Louis, MO, USA) was added to ECM degradation and the solution was maintained at 37 • C under gentle stirring for 1 h to separate the stromal cells from primary adipocytes. Dissociated tissue was filtered using cell strainers (40 µm) and the inactivation of collagenase was then done by the addition of equal volume of Dulbecco's modified Eagle's medium (DMEM) supplemented with 15% fetal bovine serum (FBS), followed by centrifugation at 1800 rpm for 10 min. The suspending portion containing lipid droplets was discarded and the pellet was resuspended in DMEM with 15% FBS and transferred to 25 cm 2 bottle. After confluence, cells were transferred to 75 cm 2 bottle (1st passage) and the cultures were maintained at 37 • C with 5% CO 2 until the 5th passage (5P). For detachment of the adherent cells, it was used 0.25% trypsin-0.02% EDTA and re-plated at a dilution of 1:3.

Fibrin Sealant (FS) Scaffold
The FS derived from serpent venom (Crotalus durissus terrificus) was kindly provided by the Center for the Study of Venoms and Venomous Animals at UNESP (CEVAP at UNESP, São Paulo State University-Brazil) and its components and instructions for use are described in its patents (registration numbers BR1020140114327 and BR1020140114360). This FS, which was developed by the researchers of CEVAP, was produced according to the proposed standardization [29,33,35,44,45]. This new sealant was produced from the thrombin-like enzyme extracted from snake venom and animal fibrinogen. The product was provided in three microtubes that were stored at −20 • C. At the time of use, the components were previously thawed, reconstituted, mixed and applied (9 µL in each transected tendon) to generate a stable clot with a dense fibrin network.

Confocal Microscope Analysis
Approximately 3.7 × 10 5 from 1 bottle of 75 cm 2 ASC on 5P (n = 3) were trypsinized and centrifuged at 1800 rpm for 10 min. The supernatant was discarded and the pellet containing ASC was fixed with 4% paraformaldehyde. ASC were labeled with phalloidin-FITC at 1.25 µg/mL for 5 min at room temperature to stain the actin cytoskeleton and incubated with DAPI (0.1 mg/mL in methanol) for 5 min at 37 • C to stain the nucleus. Then, the ASC were resuspended in 15 µL of DMPBS + 9 µL of FS and, after clot formation, were analyzed in the National Institute of Science and Technology on Photonics Applied to Cell Biology (INFABIC) at the State University of Campinas (UNICAMP), using a Zeiss LSM 780-NLO confocal on an Axio Observer Z.1 microscope (Carl Zeiss AG, Oberkochen, Germany) using a 10× objective. Images were collected using laser lines 405 nm and 488 nm for excitation DAPI and phalloidin-FITC fluorophores, respectively, with pinholes set to 1 airy unit for each channel, 1024 × 1024 image format.

Experimental Groups
A total of 110 male Lewis rats (120-day-old) kept at a constant temperature (23 ± 2 • C) and humidity (55%) under a 12/12 h light/dark cycle, with free access to food and water, were divided into 5 experimental groups: Normal (N): rats with tendons without transection; Transected (T): rats with partially transected tendons and treated with topical application of DMPBS in the transected region; Fibrin sealant (FS): rats with transected tendons and treated with FS application in the transected region; Mesenchymal stem cells derived from adipose tissue (ASC): rats with transected tendons with subsequent transplant of ASC (3.7 × 10 5 cells) in the transected region; And FS with ASC (FS + ASC): rats with transected tendons and treated with application of FS associated with ASC in the transected region. Animals were euthanized on the 21st day after transection by an overdose of anesthetic (ketamine and xylazine). Animals of the N group were euthanized at 141 days and the tendons without transection were collected for analysis.

Protocol for Partial Transection of the Achilles Tendon and Application of FS and ASC
The animals were anesthetized with intraperitoneal injection of Ketamine (90 mg/Kg) and Xylazine (12 mg/Kg) and the right lower paws submitted to antisepsis and trichotomy. To expose the calcaneus tendon, a longitudinal incision was made in the animal's skin, followed by transverse partial transection performed in the proximal tendon region (predominantly subjected to tension forces) located at a distance of 4 mm from its insertion in the calcaneus bone [11,[46][47][48][49][50][51]. Approximately 3.7 × 10 5 ASCs in the 5P were resuspended in 15 µL of DMPBS and transplanted in the transected region of tendons in the ASC group, using a pipette. In the FS + ASC group, the ASCs were resuspended in 15 µL of DMPBS + 9 µL of FS and, after clot formation; it was placed on top of the transected region. In each T-group tendon only 15 µL of DMPBS was applied and the SF group tendons received application of 15 µL of DMPBS + 9 µL FS. All applications were made in the region of the tendon where partial transection was performed. Then, the skin was sutured with nylon thread (Shalon 5-0) and needle (1.5 cm). All surgical and experimental protocols were approved (01/12/2105) by the Institutional Committee for Ethics in Animal Research of the UNICAMP-Brazil (Protocol nº 3695-1).

In Vivo Imaging
The ASC on 5P were trypsinized and centrifuged at 1800 rpm for 10 min. The supernatant was discarded and the pellet containing about 3.7 × 10 5 cells were labeled with PKH26 (Sigma) as previously described [52]. After labeling with PKH26 the pellet was resuspended in 15 µL of DMPBS and applied to the transected region of the calcaneus tendon of the ASC group. In the FS + ASC group the same procedure was repeated with the addition of 9 µL of FS. In the control rat, sham ASC were applied on the intact tendon and the negative control rat had only its tendon transected without ASC or FS application. In vivo imaging was performed on the 1st, 2nd, 3rd, 7th, 14th and 21st days after injury using the In vivo FX PRO device (BRUKER ® , Billerica, Massachusetts, USA) for identification and quantification of the intensity and area of fluorescence of the ASC labeled with PKH26. To this end, the wavelengths of 550 nm and 600 nm were applied for excitation and emission of the fluorophore, respectively, for 1 min. In addition, the animals were submitted to X-ray, aiming at the anatomical location of the marking. During the procedure, the animals of experimental groups (n = 3) were kept under anesthesia (3% isoflurane in medicinal air). In order to exclude possible nonspecific markings, negative control was also subjected to imaging. Additionally, the fur was completely removed from the area of interest and the skin was cleaned with 70% ethanol to remove any residues that could interfere with the fluorescence. The following parameters were analyzed: fluorescence area (mm 2 ) and fluorescence intensity (photons per second per square millimeter, P/s/mm 2 ).

Real-Time PCR Array
The tendons were collected carefully (n = 4), placed in stabilizing solution (RNA-later, QIAGEN ® , Hilden, Germany) and maintained at −20 • C. For total RNA extraction, the transected region (TR) of tendons were isolated and sprayed using liquid nitrogen and then homogenized in a tube containing 5 stainless steel balls (2.3 mm diameter, Biospec Products, Inc., Bartlesville, USA) by being shaken in TissueLyser LT instrument (QIAGEN ® ), with 2 repetitions (60 s) intercalated with ice cooling (2 min) between each shaking step [53]. Total RNA was in isolation from each sample using the RNeasy ® Fibrous Tissue Mini Kit (QIAGEN ® ), following the manufacturer's instructions. A spectrophotometer (NanoDrop ® ND-1000, Thermo Scientific ® , Waltham, Massachusetts, USA) was used to quantify RNA in each sample by determining the absorbance ratio at 260 and 280 nm. 0.5 µg from the total extracted RNA of each sample was used for the synthesis of cDNA, using the RT 2 First Strand Kit (QIAGEN ® ) and thermocycler Mastercycler Pro (Eppendorf ® , Hamburg, Germany), also following the manufacturer's instructions. The cDNA was frozen at −20 • C until tested. The RT-PCR array reaction was performed using the RT 2 Profiler PCR Arrays (A format) kit in combination with the RT 2 SYBR Green Mastermixes (QIAGEN ® ) on the thermocycler apparatus 7300 (ABI Applied Biosystems ® , Foster City, CA, USA), following the manufacturer's instructions. For each animal sample, three types of reaction controls were used: 1. Positive PCR control; 2. Reverse transcriptase control; 3. Control for contamination of rat genomic DNA. The Glyceraldehyde-3-phosphate dehydrogenase (Gapdh, NM_017008) was used as endogenous control for each sample. The following genes were analyzed (QIAGEN ® ): Scleraxis (Scx, NM_001130508); Tenomodulin (Tnmd, NM_022290); Tumor necrosis factor (TNF superfamily, member 2) (Tnf, NM_012675); Interleukin 1 beta (II1b, NM_031512); Transforming growth factor, beta 1 (Tgfb1, NM_021578); Matrix metallopeptidase 2 (Mmp2, NM_031054); Matrix metallopeptidase 9 (Mmp9, NM_031055); TIMP metallopeptidase inhibitor 2 (Timp2, NM_021989); Decorin (Dcn, NM_024129); Lysyl oxidase (Lox, NM_017061) e Growth differentiation factor 5 (Gdf5, XM_001066344). Reactions were made in a single cDNA pipetting for each gene including endogenous control. ∆CT values were obtained by the difference between the CT values of the target genes and the Gapdh gene. These values were normalized by subtracting the ∆CT value of the calibrator sample (N group) to obtain ∆∆CT values. For each target gene, the 2 −∆∆CT method was used to calculate the relative expression level (fold change) and the results were represented as the relative gene expression in comparison to the calibrator sample that is equal to 1.

Dosage of Hydroxyproline
Hydroxyproline was used as an indicator of total collagen amount in tendons of different groups (n = 8) used previously in the biomechanical assay. The entire tendons were cut and immersed in acetone for 48h, also followed by a solution containing chloroform: ethanol (2:1) for 48h. After dehydration, the samples were hydrolyzed in 6N HCl (1 mL/10 mg of tissue) for 4h at 130 • C according to Stegemann and Stalder [54], with some modifications. The hydrolysate was neutralized with 6N NaOH, followed by spectrophotometric quantification, according to Jorge et al. [55]. The absorbance of the samples was measured at 550 nm using a microplate reader (Expert Plus, Asys ® , Holliston, MA, USA).

Western Blotting
For protein extraction, 12 entire tendons longitudinal cryosections obtained from 4 different animals of each group were carried out using 50 µL of T-PER TM Tissue Protein Extraction Reagent. The extraction mixture was gently stirred for 30 min at 4 • C, followed by centrifugation at 10,000 rpm for 10 min. The supernatant (total extract) was used for determination of the protein concentration by the biuret method. Aliquots of the supernatant were treated with Laemmli buffer containing 100 mM DTT (Sigma). Samples containing 30 µg of protein were boiled for 5 min and loaded onto 6.5% to 10% SDS-PAGE gels. The gels were run in a Mini-Protean apparatus (Bio-Rad, Hercules, CA, USA) and transferred to PVDF membranes (Bio-Rad). The membranes were washed in basal solution (1 M Trizma base, 5 M NaCl, 0.005% Tween 20 and deionized water) and incubated in blocking solution (basal solution plus 5% Molico skim milk) for 2h. Then, the membranes were incubated with a polyclonal antibody against collagen type I (1:1000; C2456-Sigma), Tenomodulin (1:1000; SAB2108237-Sigma) and Beta-actin used as internal control (1:500; sc-47778-Santa Cruz Biotechnology, California, CA, USA), overnight at 4 • C. Specific protein bands were visualized in the PVDF (Bio-Rad ® ) membranes incubated with appropriate secondary antibodies at 1:10,000 (Santa Cruz Biotechnology, California, CA, USA) for 2h, followed by exposure to the SuperSignal West Pico Chemiluminescent Substrate kit. Membranes were developed with the Syngene G: BOX documentation system. The band intensities were quantified by optical densitometry, using the free Image J software (National Institutes of Health, Bethesda, MD, USA).

Preparation of Sections in Freezing
Tendons were placed in Tissue-Tek ® , frozen and cut in cryostat (serial longitudinal cuts of 7 µm thickness). The sections were fixed using a 4% formaldehyde solution in Millonig buffer (0.13 M sodium phosphate and 0.1 M sodium hydroxide, 7.4 pH) for 20 min and followed for birefringence and contrast analysis by differential interference and for histology and histomorphometry.

Birefringence and Contrast by Differential Interference (DIC)
For this procedure the Olympus BX-51 (Olympus America, Center Vallery, PA, USA) equipped with Q-color 5 camera (Olympus America, Center Vallery, PA, USA) was used. For visual evaluation and birefringence measurements, 3 tendons longitudinal cryosections obtained from 5 different animals of each group were carried out and Image a Pro-plus v.6.3 software for Windows™ (Media Cybernetics, Silver Spring, MD, USA) was used. Around 300 measurements were done in tendon sections of each group. With the microscope and the software it is possible to carry out analysis of DIC and anisotropic properties, both individually and in combination [56,57]. To obtain the birefringence of the fibers and collagen bundles without Walston's prism activity, these were removed from the polarized light path by turning the condenser tower to the position of a field of observation free, giving passage only to polarized light. The Nomarski prism was also removed below the analyzer. Under these conditions we simply have a polarizing microscope. In place of the Nomarski prism a Senarmont compensator of 1/4 wavelength was inserted and used for collagen bundles analysis before and after compensation. After studying the fibers morphology and collagen bundles by their birefringence of sections immersed in distilled water, birefringence was measured by captured images analysis. To do this, a standardization of the lighting source and camera sensitivity was used so that the same working conditions were always preserved. In optical terms, 40 × objective and monochromatic light with λ = 546 nm were always used. Longitudinal tendon sections of all groups were examined and measured. As standard to adjust the working conditions, sections of the ASC group were adopted as treatment from which a hypothetically ideal response was expected. The birefringence measurements were in terms of image brightness and expressed in pixels, which allowed a high sampling of measured areas, as well as the detection of the greater variability of birefringence as previously verified [58,59].

Histology and Histomorphometry
After fixing the tissue cryosections as described previously, tendons were stained with 0.025% toluidine blue (TB) in McIlvaine buffer (0.03 M citric acid, 0.04 M sodium phosphate dibasic-pH 4.0) [48] for proteoglycans observation and with hematoxylin and eosin (HE) [49] for a panoramic view of the tendon's morphology. The sections on slides were air dried and immersed in xylene, before embedding in entellan (Merck, Rio de Janeiro, Brazil). Tissue sections were analyzed for tendon morphology observation under an Olympus BX53 microscope (Center Vallery, PA, USA).
For the fibroblast count (number of fibroblasts in 10 4 µm 2 ) of the transected region, longitudinal sections of tendons stained with Harris hematoxylin were used. Three tendons sections from each different animal group (n = 3) were used, in which five samples were taken for fibroblasts count. All images were captured and scanned using the Leica DM2000 Photomicroscope. Measurements were performed on scanned images supported by the SigmaScan Pro 5.0™ program (Systat Software Inc., Chicago, USA).

Biomechanical Parameters
Tendons from experimental groups (n = 8) were collected and stored at −20 • C until tested. Before the biomechanical test, the tendons were thawed and measured with a pachymeter, considering their length, width and thickness. For the biomechanical assay, the tendons were maintained in PBS to prevent their fibers from drying out. Then, the tendons were fixed to metal claws by the myotendinous junction and by the osteotendinous junction, for a correct alignment of the equipment (Texturometer, MTS model TESTSTAR II). In each biomechanical assay tendons were subjected to a gradual increase of load at a displacement velocity of 1 mm/s by using a load 0.05 N, until the tendon ruptured. Biomechanical parameters were analyzed according to Biancalana et al. [60], such as maximum force (N) and maximum displacement (mm), which were used to calculate the maximum stress (Mpa) and maximum strain (L) of tendons from the experimental groups. The cross-sectional area of the calcaneus tendon was calculated by assuming an elliptical approximation (A = πWd/4), using measurements of width (W) and thickness (d) and values from the same [61]. The maximum stress value (MPa) was estimated by the ratio between the maximum load (N) and the cross-sectional area (mm 2 ). The maximum deformation (L) was calculated through (L = L f − L i /L i ,), where (L f ) is the value of the final length before rupture and (L i ) is the initial tendon length value.

Statistical Analysis
All results were presented in mean and standard deviation for the values with normal distribution (or interquartile range and median for the values that did not adhere to the Gaussian distribution). For the data with normal distribution, it was used the analysis of variance (ANOVA), followed by the Tukey post-hoc test for intra-group analysis (in the case of statistical significance) or the Student's T Test preceded by Levene's Test (for biomechanical parameters, dosage of hydroxyproline, in vivo imaging, histomorphometry, real-time PCR array and Western blotting). For data that did not adhere to the Gaussian distribution, it was used non-parametric test by the Kruskal-Wallis test followed by the post-hoc test of Dunn for intra-group analysis (in the case of statistical significance) or U Test of Mann-Whitney (for birefringence measurements). Statistical analysis was performed in the software Statistical Package for Social Sciences (SPSS Inc., Chicago, Illinois, USA) version 22.0 and for all the aforementioned tests the significance level α = 0.05 and power of the test of 95% were considered.

In Vitro Adipogenic, Chondrogenic and Osteogenic Differentiation of ASC and Positive ASC Markers
In vitro ASC (5P) staining with Toluidine Blue, Alizarin Red and Sudan IV showed differentiation in chondrocytes, osteoblast and adipocytes, respectively ( Figure 1A-D). In flow cytometry, CD90 positive cells (approximately 87%) and CD105 positive cells (approximately 91%) were observed. CD34 cells were not detected ( Figure 1E,F).

In Vivo Imaging for ASC Detection on Tendon
Cell migration was evaluated by in vivo imaging of animals that were injected with ASC labeled with PKH26. PKH26-labeled ASC (group ASC) or with fibrin sealant (group FS + ASC) were observed in lower limb up to 7 days ( Figure 3A-D and F-I) or 14 days ( Figure 3E and J), respectively, being not observed in any of the groups at the experiment end point (21 days, not shown). A small spot was seen in the sham group but never in the negative control, only on the 1st day (not shown), then its area was discounted from the other groups at the same day. According to our data, labeling intensity peaked at day 1 in the ASC group, decreasing on the 2nd day (1d vs. 2d, p < 0.05) with no further variation, while in the FS + ASC group it kept constant through time ( Figure 3K). Of importance, comparison of both groups revealed higher fluorescence intensity in ASC treated rats on the 1st day (p < 0.05; Figure 3K). Regarding the labeling area, it also peaked on the 1st day in the ASC group, decreasing 93.5% on the 2nd day (1d vs. 2d, p < 0.05) after when it oscillated up to 7th day, however, with no significant differences ( Figure 3L). No labeling was found on the 14th day ( Figure 3E). Variations in the labeling area were also observed in the FS + ASC group from the 1st to the 14th day, however, with no statistical differences ( Figure 3L). Comparison between both groups revealed that the labeling area is more than 10 folds higher in the absence of fibrin sealant on the 1st day (p < 0.001; Figure 3L), reinforcing its importance as a scaffold that avoids cell spreading in the tissue. No PKH26labeled ASC was observed on the 21st day after tendon transection in both ASC and FS + ASC groups (not shown).

In Vivo Imaging for ASC Detection on Tendon
Cell migration was evaluated by in vivo imaging of animals that were injected with ASC labeled with PKH26. PKH26-labeled ASC (group ASC) or with fibrin sealant (group FS + ASC) were observed in lower limb up to 7 days ( Figure 3A-D,F-I) or 14 days ( Figure 3E,J), respectively, being not observed in any of the groups at the experiment end point (21 days, not shown). A small spot was seen in the sham group but never in the negative control, only on the 1st day (not shown), then its area was discounted from the other groups at the same day. According to our data, labeling intensity peaked at day 1 in the ASC group, decreasing on the 2nd day (1d vs. 2d, p < 0.05) with no further variation, while in the FS + ASC group it kept constant through time ( Figure 3K). Of importance, comparison of both groups revealed higher fluorescence intensity in ASC treated rats on the 1st day (p < 0.05; Figure 3K). Regarding the labeling area, it also peaked on the 1st day in the ASC group, decreasing 93.5% on the 2nd day (1d vs. 2d, p < 0.05) after when it oscillated up to 7th day, however, with no significant differences ( Figure 3L). No labeling was found on the 14th day ( Figure 3E). Variations in the labeling area were also observed in the FS + ASC group from the 1st to the 14th day, however, with no statistical differences ( Figure 3L). Comparison between both groups revealed that the labeling area is more than 10 folds higher in the absence of fibrin sealant on the 1st day (p < 0.001; Figure 3L), reinforcing its importance as a scaffold that avoids cell spreading in the tissue. No PKH26-labeled ASC was observed on the 21st day after tendon transection in both ASC and FS + ASC groups (not shown).

Cell Migration Assay and Macrophages Identification
CD90+CD105+ ASC were visualized in the transected region of tendons of both ASC and FS + ASC groups (Figure 4), proving the ASC migration.

Cell Migration Assay and Macrophages Identification
CD90+CD105+ ASC were visualized in the transected region of tendons of both ASC and FS + ASC groups (Figure 4), proving the ASC migration.
A small amount of macrophages was observed in the normal ( Figure 5A,B) as well as in the transected tendons regardless the treatment ( Figure 5C-K). Of importance, in tendons that received cells it was possible to observe very few macrophages carrying PKH26 signal ( Figure 5G,H,J,K), probably due to phagocytosis of dead ASC.  A small amount of macrophages was observed in the normal ( Figure 5A, B) as well as in the transected tendons regardless the treatment ( Figure 5C-K). Of importance, in tendons that received cells it was possible to observe very few macrophages carrying PKH26 signal ( Figure 5G, H, J, K), probably due to phagocytosis of dead ASC.

Genes Expression Analysis
A higher expression level of the Tnmd gene could be observed in the ASC group in relation to T and FS groups. Trends to a greater expression of Mmp2, Timp2, Scx and Ilb1 were observed in the ASC group compared to the other transected groups. In comparison to N group, the transected groups presented higher expression of Mmp2, Mmp9, Timp2, Gdf5, Scx and Tnmd ( Figure 6).

Genes Expression Analysis
A higher expression level of the Tnmd gene could be observed in the ASC group in relation to T and FS groups. Trends to a greater expression of Mmp2, Timp2, Scx and Ilb1 were observed in the ASC group compared to the other transected groups. In comparison to N group, the transected

Genes Expression Analysis
A higher expression level of the Tnmd gene could be observed in the ASC group in relation to T and FS groups. Trends to a greater expression of Mmp2, Timp2, Scx and Ilb1 were observed in the ASC group compared to the other transected groups. In comparison to N group, the transected groups presented higher expression of Mmp2, Mmp9, Timp2, Gdf5, Scx and Tnmd (Figure 6).

Total Collagen Quantification
Higher concentration of hydroxyproline was observed in the ASC group compared to the N group (Table 1).

Total Collagen Quantification
Higher concentration of hydroxyproline was observed in the ASC group compared to the N group (Table 1). Table 1. Hydroxyproline concentration (mg/g tissue) in the entire tendon (n = 8). (*) Significant difference between N and ASC groups.

Collagen I and Tnmd quantification
The presence of collagen type I and Tnmd was observed in all groups. Densitometry analysis of the bands (pixels) showed a difference only between the normal tendon and the transected tendons, with exception of the ASC group ( Figure 7B). Table 1. Hydroxyproline concentration (mg/g tissue) in the entire tendon (n = 8). (*) Significant difference between N and ASC groups.

Collagen I and Tnmd quantification
The presence of collagen type I and Tnmd was observed in all groups. Densitometry analysis of the bands (pixels) showed a difference only between the normal tendon and the transected tendons, with exception of the ASC group ( Figure 7B).

Panoramic View of Tendons Organization and Histomorphometry
The sections stained with HE showed few fibroblasts arranged between dense and organized matrix collagen bundles and characteristics of the proximal region of a normal tendon ( Figure 7A). Higher cellularity and light staining of ECM were observed in the TR and in the regions above and below TR of transected tendons in relation to the normal tendon, indicating a strong remodeling process after lesion. The weak staining of collagen fibers by eosin shows that the reorganization of the matrix is not complete on the 21st day. Histomorphometry analysis showed no differences in the number of fibroblasts between the transected tendons. However, the N group presented a smaller number of cells compared to the T, FS, ASC and FS + ASC groups ( Table 2).  For the significant differences between the groups, see the band densitometry analysis in the graphics. The same letters (a, b, c) between the groups correspond to a significant difference between them.

Panoramic View of Tendons Organization and Histomorphometry
The sections stained with HE showed few fibroblasts arranged between dense and organized matrix collagen bundles and characteristics of the proximal region of a normal tendon ( Figure 7A). Higher cellularity and light staining of ECM were observed in the TR and in the regions above and below TR of transected tendons in relation to the normal tendon, indicating a strong remodeling process after lesion. The weak staining of collagen fibers by eosin shows that the reorganization of the matrix is not complete on the 21st day. Histomorphometry analysis showed no differences in the number of fibroblasts between the transected tendons. However, the N group presented a smaller number of cells compared to the T, FS, ASC and FS + ASC groups (Table 2). Table 2. Total number of fibroblasts: no differences were observed between the transected tendons. (*) Significant difference between the N group and the transected groups (n = 3).

Collagen Fibers Organization Measurements
The analysis of tendons of different groups, under polarizing microscopy, showed higher birefringence values in FS in relation to all groups and in FS + ASC in comparison to the ASC group, indicating difference in the collagen bundles organization (Figure 8 A-G). N group exhibited higher birefringence values in relation to all transected groups. The image analysis of tendons sections from FS groups, showed a typical crimp arrangement in the transected region ( Figure 8B). When DIC (Differential Interference Contrast) was used, which increases the contrast in unstained collagen bundles (for details see Vidal et al. [57]), it was possible to detect in the new ECM in formation, a blue color due to the presence of packed and organized collagen bundles and a background red color of unpacked or less organized collagen bundles ( Figure 8C). The frequency histograms of birefringence gray average (GA) values showed the heterogeneous data distribution, with marked low birefringence values for group T and higher values especially for the FS group.

Biomechanical Properties of Tendons
The analysis of mechanical properties of transected tendons for the maximum load (N), maximum displacement (mm), maximum strain (mm), cross-sectional area (mm 2 ) and maximum stress (MPa), showed some alterations (Figure 9). The T group had higher value of maximum load compared to the groups ASC (p = 0.011) and FS + ASC (p = 0.031). For the cross-sectional area and maximum stress, N group had lower and higher values, respectively, compared to the transected groups (p < 0.001). median between the groups. The measurements data showed in graphics (f and g) were obtained with the larger tendon axis positioned at 45° from the crossed polarizers. (*) Significant differences between the group N and groups with transected tendons. The same letters between the groups correspond to a significant difference between them. For a systematic overview table of results see Table 3. For a systematic overview table of results see Table 3.

Discussion
In the present study, the 21st day after the transection was chosen because it marks the beginning of the remodeling phase, where there is a marked decrease in cellularity and formation of fibrous tissue [49][50][51], which is the focus of our study. In order to analyze the presence of ASC in isolation or associated with FS in the transected tendon region, in vivo imaging was used, where the striking result was observed in the ASC group due a high fluorescence intensity and area on the 1st day after injury, in relation to the FS + ASC group. Fibrin sealant works as a 3D scaffold that maintains cells grouped and possibly prevents the quantification of all labeled cells, while in its absence, cells are allowed to spread in the tissue. As a consequence of initial cell spreading (accommodation), increased labeling area was observed on the 1st day in the ASC group. But, as also demonstrated by Qiao et al. [62], our data showed a substantial ASC loss, when only stem cells are transplanted, from the 1st to the 2nd day. From the 2nd to the 7th day, no differences were observed among the groups when considering the fluorescence intensity and area. It is important to observe that only the FS + ASC group showed marking on the 14th day, with similar fluorescence intensity to that observed in previous periods and a larger area of fluorescence, possibly due to the fibrin sealant being degraded and consequently releasing the ASC. Our data supports the in vivo study by Wolbank et al. [63], which subcutaneously implanted in rats, fibrin clots with fluorophore-labeled and monitored their degradation for 21 days by in vivo imaging. The study showed that much of the fibrin clot was degraded by about 14 days and after 16 days, the degradation was total. Bensaïd et al. [64], through an in vitro study, demonstrated that fibrin scaffold together with human mesenchymal stem cells, depending on the concentration of fibrinogen and thrombin, is degraded within 14 to 15 days. Also in an agreement with our data, Spejo et al. [65] showed that the mesenchymal stem cells remain at region with 28 days post injury in glial scar region in the ventral funiculus of rats, evidencing that the sealant (the same as in the present study) kept these cells protected from the phagocytic system of the organism. This sealant is produced from the blood components of buffaloes, mainly fibrinogen, resulting in a fibrin clot and because it is heterologous, its fibrinolysis is delayed, causing it to act with an excellent scaffold for cells [29].
Orsi et al. [66] did not observe cytotoxicity of FS and thrombin-like enzyme (snake venom compound), both the same as in the present study, associated to mesenchymal stem cells. No marking was detected by in vivo imaging from the 15th day. However, the presence of a small number of ASC with CD90 and CD105 positive marking was showed into the newly formed matrix of the transected region in both ASC and FS + ASC groups on the 21st day, confirming the presence of ASC in the tendon. It is important to mention that the marking detected in tendons on the 21st day corresponds to a majority of live ASC since a few macrophages carrying PKH26 signal due to phagocytosis of dead ASC, were observed in the transected region of tendons.
The literature has already reported the paracrine effects of ASC on the modulation of cellular activity [67][68][69], as well as the effects of fibroblast secreted molecules on ASC activity [70]. In our injury model, the interaction between the transplanted ASC and the cells present in the transected region is evident since the ASC with CD90 e CD105 positive marking were identified in tendon ECM on the 21st day after transection. Some in vitro studies show the capacity of tenogenic differentiation of ASC in the presence of appropriate biological stimuli, such as growth factor, stress forces [71] and when cultivated in co-culture with tenocytes [70]. Tnmd is a good phenotype marker for tendon fibroblasts and acts as a regulator of cell proliferation and differentiation [72]. Our results showed significant increase of the Tnmd gene expression in the ASC group in relation to the groups without transplanted ASC, indicating a greater differentiation in tenocytes mainly of the transplanted ASC [70,73,74]. Thus, it is concluded that the molecular signaling present in the injury environment possibly affects the differentiation of ASC in tenocytes, only in the transected region of tendons. Considering the entire tendon, no differences were observed in the Tnmd amount, in a protein level, between the transected tendons. In addition to the Tnmd, Scx is also a key molecule involved in the process of tendon development. Scx is a transcription factor responsible for the differentiation of stem cells into tenocytes and is specifically detected in precursor populations of tendon cells [70,75]. Our results showed a trend to the increase of Scx expression in the ASC group in relation to the other transected groups, suggesting its relationship with the significant increase of the Tnmd expression.
In order to analyze the effect of the treatments with ASC and FS reflecting in the entire tendon, collagen and tenomodulin, markers of tendon, were analyzed also in the entire tendons considering that the collagen fibers are also responsible for the mechanotransduction during gait, which is important for the cellular signaling in the transected region, affecting the recovery of the ECM at the site of injury. As well as it is important to consider that the molecular events in the transected region can also influence the organization and composition of the not damaged areas of tendons. In addition, collagen is the main constituent of tendons, mainly collagen type I, also being directly related to the recovery of the structure and biomechanical properties of tendons during repair process. Interestingly, the ASC group presented superior total collagen concentration, estimated by the hydroxyproline dosage, in relation to the N group. Gdf5 and Tgfb1 are related to the stimulation of collagen synthesis [26,70,[76][77][78], supporting our results in which was observed a higher Gdf5 expression in transected region of the ASC group, in comparison to N group and higher total collagen concentration in the entire tendon. However, no differences for the collagen I was observed between N and ASC groups. According to Uysal et al. [76], ASC applied on the injured calcaneus tendon of rabbits helped in tendon healing and increased the production of type I collagen.
Data from Peres [79] showed a marked increase of inflammatory infiltrate during the initial stage of healing of the skin of rats after an isolated application of either FS (the same FS used in our study) or after its association with ASC, in relation to the other sutured groups. The trend towards greater expression of II1b observed after the FS application in our study could be related to an inflammatory process with remnants still to the 21st day, considering the presence of fibrin until the 14th day in the injury region and period of its absorption [63]. Yücel et al. [80] showed that although the FS application increases inflammation on the first few days after application, the fibrin matrix helps tissue recovery.
The Yücel et al. [80] study mentioned above supports our structural data. Higher values of birefringence were detected in the FS group in comparison to all groups, followed by the FS+ASC and ASC groups in relation to T, respectively, reflecting greater organization of the collagen bundles. Considering that tissue reorganization after injury is extremely important for the recovery of the tendon functionality, our structural result is highly relevant considering the 21st day of repair, because depending on the extent of the injury, the tendon may take months for complete healing [81]. The use of FS acted as a scaffold for resident tendon cells, as well as for the interaction of ASC transplanted with resident cells of the transected region since both FS and FS + ASC groups had higher birefringence values, showing that fibrin is slowly replaced by connective tissue. A study of Tuan et al. [82] supports our structural results because demonstrated that the cultured fibroblasts together with the fibrin gel, synthesize collagen and actively reorganize the fibrin matrix which is largely replaced by collagen fibrils. Regarding the analysis of genes involved in ECM remodeling, no striking results were observed in relation to the expression of Lox, Dcn, Mmp2, Mmp9 and Timp2 in the transected tendons, suggesting the involvement of other genes in the higher collagen fibers organization observed specially in the FS, followed by FS + ASC and ASC groups In the biomechanical analysis, no differences were observed between the transected groups for the stress parameter on the 21st day, supporting no differences in the amount of collagen type I in the entire tendon, which is directly related to the resistance of tendon. Although, the literature points to the beneficial effects of FS and ASC on the biomechanics of tendons in the healing process [83]. Therefore, it is possible to conclude that the structural data did not directly reflect the biomechanics of the tendons, perhaps due to the recovery time, 21 days, which is marked by the beginning of the remodeling process. A point to be considered is that the number of crosslinks present in tendons treated with ASC and with FS isolated or in combination, reflected in the higher organization of these tendons but was not enough to warrant a more resistant tendon on the 21st day after transection. We believe that long-term time point analysis could demonstrate that transected tendon treated with FS exhibited superior strength in comparison with T group.
According to our data, transplanted ASC migrated to the transected region and consequently the ASC up-regulated the Tnmd expression suggesting a differentiation of transplanted cells in tenocytes and the ASC increased the collagen fibers organization. The application of FS alone was able to improve the molecular organization of the collagen fibers but when associated with the ASC, a higher number of cells was kept in the transected region, with the ASC protected from the phagocytic system. In conclusion, our data suggest this FS to be a good scaffold for treatment during tendon repair because it was the most effective one regarding tendon organization recovering, followed by the FS treatment associated with ASC and finally by the transplanted ASC on the 21st day. Further investigations in long-term time points of the tendon repair are needed to analyze if the higher tissue organization found with the FS scaffold will improve the biomechanics of the tendons.