Durable Nanoﬁber-Based Membrane with Efﬁcient and Consistent Performance for Oil/Saltwater Separation

: There is a large amount of oil-contaminated wastewater caused by oil/gas production and marine oil spills. It is still a major challenge for the development of oil/water separating membranes that have excellent separation efﬁciency, can withstand saline environments, and have long-term durability. We present a new membrane made of ultralong titanate nanoﬁbers (TNF) (with diameter of 200 nm and length of 60 µ m) and carbon nanoﬁbers (CNF) (with a diameter of 150 nm and length of 50 µ m) for efﬁcient and consistent oil/saltwater separation. The intertwined structure of titanate and carbon nanoﬁbers is critical to ensuring a high mechanical strength and durability for the new membrane. The carbon nanoﬁber works as a scaffold in this membrane to maintain mechanical integrity during multiple cycles of reuses, which is an important merit for its practical applications. The ultralong titanate nanoﬁbers work as functional component to provide high hydrophilicity of the membrane. The new membrane has an oil/water separation efﬁciency of more than 99%, an oil content in treated efﬂuent that is lower than US environmental discharge standards (42 ppm), and a high water ﬂux of 1520 LMH/bar, due to its excellent superhydrophilicity and inter-connected pore structure. The new membrane also exhibits outstanding durability in a variety of salinity environments, as well as good resistance to oil fouling. This new type of membrane has a high potential for industrial application in treating oily wastewater due to its excellent environmental durability, oil-fouling resistance, high separation efﬁciency, and easy scalability.


Introduction
Due to the enormous amounts of oily and salty wastewater produced by frequent maritime oil spill accidents as well as oil mining, production, and refinery activities, oil pollution is a serious issue on a global scale [1]. The opportunities for treating produced water are therefore increasing and driven mainly by reuse demand and regulation. The US Environmental Protection Agency (EPA) has enacted regulations that limit the amount of oil released into effluents to no more than 42 mg/L [2]. As a result, creating efficient and sustainable methods to treat wastewater that has been contaminated by oil is in high demand in order to meet stringent regulations as well as to protect the environment. Traditional oil/water separation techniques, such as hydrocyclones and air floatation, have some disadvantages, such as low separation efficiency or high operating costs [3].
Membrane techniques that operate with a "size-sieving" effect, such as nanofiltration (NF), ultrafiltration (UF), and microfiltration (MF), have been frequently utilized to purify water [4]. MF and UF membranes have limitations in terms of the size of oil droplet removal. These membranes may remove oil droplets that have micrometer size. In addition to that, MF and UF membranes can be effective in removing oil from a stable oil emulation.
The membrane presented in this paper is made of nanofibers with interconnected porous structure with high separation efficiency for oil/saltwater emulsions and with oil residuals in the filtrates lower than environmental discharge standards (42 ppm). The high durability and performance of this nanofiber-based membrane are ensured by carbon nanofiber as mechanical scaffold and titanate nanofiber as functional materials. Meanwhile, due to its superhydrophilicity, the membrane has excellent antifouling properties. Most importantly, this new membrane has good durability in harsh environments while maintaining consistent water flux and separation efficiency. The new membrane has a small pore size that does not allow the passage of the emulsified oil through the membrane. This new membrane has a high potential for practical industrial applications due to its excellent oil/water separation efficiency, durability, fouling resistance, and low cost of fabrication. The properties of the new ultralong titanate nanofiber and carbon nanofiber membrane are described in Figure 1. Appl. Sci. 2023, 13, x FOR PEER REVIEW 3 of 14 and long-term preservation for reuse [15]. Superoleophobic membranes for oil/water separation with high separation efficiency, superior oil-fouling resistance, and high environmental durability have been used sparingly in industry up to now. The membrane presented in this paper is made of nanofibers with interconnected porous structure with high separation efficiency for oil/saltwater emulsions and with oil residuals in the filtrates lower than environmental discharge standards (42 ppm). The high durability and performance of this nanofiber-based membrane are ensured by carbon nanofiber as mechanical scaffold and titanate nanofiber as functional materials. Meanwhile, due to its superhydrophilicity, the membrane has excellent antifouling properties. Most importantly, this new membrane has good durability in harsh environments while maintaining consistent water flux and separation efficiency. The new membrane has a small pore size that does not allow the passage of the emulsified oil through the membrane. This new membrane has a high potential for practical industrial applications due to its excellent oil/water separation efficiency, durability, fouling resistance, and low cost of fabrication. The properties of the new ultralong titanate nanofiber and carbon nanofiber membrane are described in Figure 1. The technology that will be developed in this research can find numerous application opportunities such as the produced water treatment and oil spill cleanup in the sea.

•
The produced water refers to the water that is returned to the surface through a well borehole. The quantity of produced water is increasing with increased volumes of global oil/gas production. This project will examine the feasibility of the synthesized membrane to treat produced water.

•
Oil spills can occur in the sea and cause a negative impact on the ocean and marine life. The major human activities that cause oil spills are land drainage and waste disposal, offshore drilling, and spills from ships or tankers. These practices form a saline oily wastewater that requires a treatment process. This work will examine the feasibility of the synthesized membrane to treat saline oily water.

Materials
The chemicals used in this study are (Titanium dioxide (P25) (TiO2), n-hexane C6H14, and n-Octane C8H18 and were purchased from Sigma Aldrich (St. Louis, MO, USA). Carbon nanofibers were purchased from ACS Material (No. 308063-67-4) with a diameter of 150 nm and length of 50 µm. The dye of Oil Red EGN was purchased from Sigma Aldrich and was used to stain the solution to highlight the oil removing performance. In addition to that, DI water was used. The technology that will be developed in this research can find numerous application opportunities such as the produced water treatment and oil spill cleanup in the sea.

•
The produced water refers to the water that is returned to the surface through a well borehole. The quantity of produced water is increasing with increased volumes of global oil/gas production. This project will examine the feasibility of the synthesized membrane to treat produced water.

•
Oil spills can occur in the sea and cause a negative impact on the ocean and marine life. The major human activities that cause oil spills are land drainage and waste disposal, offshore drilling, and spills from ships or tankers. These practices form a saline oily wastewater that requires a treatment process. This work will examine the feasibility of the synthesized membrane to treat saline oily water.

Materials
The chemicals used in this study are (Titanium dioxide (P25) (TiO 2 ), n-hexane C6H14, and n-Octane C 8 H 18 and were purchased from Sigma Aldrich (St. Louis, MO, USA). Carbon nanofibers were purchased from ACS Material (No. 308063-67-4) with a diameter of 150 nm and length of 50 µm. The dye of Oil Red EGN was purchased from Sigma Aldrich and was used to stain the solution to highlight the oil removing performance. In addition to that, DI water was used.

Emulsion Preparation
A stable oil-in-water emulsion was prepared using the sonication technique [16]. In this technique, an ultrasonic water bath was used to sonicate 1 mL of oil in of deionized water of 45 mL for 5 min. A total of 100 mL of oil-in-water emulsion of 1% v/v was obtained then by diluting the emulsion with deionized water [17].
Different types of oils were used in this study to prepare the emulsion, which are sunflower oil, diesel, gasoline, n-octane, and n-hexane. To control the level of salinity content of the feed emulsion, sodium chloride was added to the emulsion to obtain salinity concentration between 2500 ppm to 45,000 ppm.

Titanium Nanofiber Synthesis
The hydrothermal method was used to fabricate titanate (Ti) nanofibers [18]. To prepare 7.5 mg/mL of TiO 2 nanoparticle (anatase P25) in 10 M NaOH solution, 0.375 g of TiO 2 nanoparticles were added and mixed for 30 min in 50 mL of a10M NaOH solution. After that, the solution was moved into an autoclave. A mechanical convection oven was set at 220 • C, and the autoclave was left in the oven for four days. Titanate nanofibers hydrogels were then formed as a result of the hydrothermal reaction between TiO 2 particles and the basic solution. After cooling the titanate nanofibers (TNF) to room temperature, the pH of the nanofibers was neutralized by washing the nanofibers with deionized water several times. Following that, the titanate nanofibers were filtered using vacuum filtration. The obtained TNF material was then allowed to dry at room temperature for 24 h prior to using the material in the membrane fabrication process. The optimization process for the deposition of different nanomaterials with 15 different compositions was shown in Figure S1.

Carbon Nanofiber Solution
To prepare a carbon nanofiber (CNF) solution, 10 mg of CNFs was added to 50 mL of 1% SDS solution. Probe sonication was used for 10 min to disperse the CNFs in the SDS solution. The homogenized solution was then centrifuged at 4500× g for 10 min to remove impurities such as graphitic particles and amorphous carbon.

Membrane Preparation
To construct TNF/CNF membrane, a pre-mixed solution containing titanium nanofibers and carbon nanofibers was applied to a cellulose substrate under low vacuum using a vacuum filtration device as presented in Figure 2.

Emulsion Preparation
A stable oil-in-water emulsion was prepared using the sonication technique [16]. In this technique, an ultrasonic water bath was used to sonicate 1 mL of oil in of deionized water of 45 mL for 5 min. A total of 100 mL of oil-in-water emulsion of 1% v/v was obtained then by diluting the emulsion with deionized water [17].
Different types of oils were used in this study to prepare the emulsion, which are sunflower oil, diesel, gasoline, n-octane, and n-hexane. To control the level of salinity content of the feed emulsion, sodium chloride was added to the emulsion to obtain salinity concentration between 2500 ppm to 45,000 ppm.

Titanium Nanofiber Synthesis
The hydrothermal method was used to fabricate titanate (Ti) nanofibers [18]. To prepare 7.5 mg/mL of TiO2 nanoparticle (anatase P25) in 10 M NaOH solution, 0.375 g of TiO2 nanoparticles were added and mixed for 30 min in 50 mL of a10M NaOH solution. After that, the solution was moved into an autoclave. A mechanical convection oven was set at 220 °C, and the autoclave was left in the oven for four days. Titanate nanofibers hydrogels were then formed as a result of the hydrothermal reaction between TiO2 particles and the basic solution. After cooling the titanate nanofibers (TNF) to room temperature, the pH of the nanofibers was neutralized by washing the nanofibers with deionized water several times. Following that, the titanate nanofibers were filtered using vacuum filtration. The obtained TNF material was then allowed to dry at room temperature for 24 h prior to using the material in the membrane fabrication process. The optimization process for the deposition of different nanomaterials with 15 different compositions was shown in Figure  S1.

Carbon Nanofiber Solution
To prepare a carbon nanofiber (CNF) solution, 10 mg of CNFs was added to 50 mL of 1% SDS solution. Probe sonication was used for 10 min to disperse the CNFs in the SDS solution. The homogenized solution was then centrifuged at 4500× g for 10 min to remove impurities such as graphitic particles and amorphous carbon.

Membrane Preparation
To construct TNF/CNF membrane, a pre-mixed solution containing titanium nanofibers and carbon nanofibers was applied to a cellulose substrate under low vacuum using a vacuum filtration device as presented in Figure 2.  To create the premixed solution, 0.08 g of TNF was mixed in 40 mL of deionized water and 1 mL of CNF. Then, the premixed solution was probe-sonicated for five minutes prior to deposition in order to homogenize the nanoparticle dispersion. The homogeneous solution was then deposited on the cellulose substrate under low vacuum using vacuum filtration. Deionized water was used to wash the deposited nanoparticles multiple times. Then, the new TNF/CNF membrane was dried at room temperature for 24 h prior to using the membrane in the performance test.

Instruments and Characterization
The water contact angle and the oil contact angle were measured to study the hydrophilicity and hydrophobicity of the membranes by using an advanced goniometer (Rame-hart A100, Arden, NC, USA). The contact angles of 5 spots on the membrane surface were measured, and the average were calculated. The surface morphology of the membrane was examined using a scanning electron microscopy (SEM, FEI Corp., Hillsboro, OR, USA) with Bruker Quantx400 EDS for microanalysis. The total organic carbon (TOC) was measured in the feed and filtrate samples using a TOC analyzer (Shimadzu, TOC-L, Tokyo, Japan). A Visual Process analyzer (JORIN-ViPA) was use to measure the size and distribution of oil droplets in the feed. The membrane material's crystal structure was investigated using an X-ray diffraction instrument (XRD, Bruker D8 Advance, Bruker-AXS, Germany).

Performance Test
The oil/water separation efficiency of the fabricated new membranes was evaluated by a filtration device (Nalgene 300-4050, Rochester, NY, USA) with its effective membrane area of 11.3 cm 2 . The device was operated under vacuum filtration condition. The fabricated TNF/CNF membrane was placed in the vacuum filtration apparatus. The separation of oil and water was conducted in the dead-end filtration mode. In the filtering device, 100 mL of the prepared oil-in-water emulsions or oil-in-saline water mixtures was poured. The oil emulsion was then allowed to pass through the TNF/CNF membrane using vacuum pressure. The operating vacuum pressure throughout all the experiments was −30 KPa.
2.6. Calculation Procedure 2.6.1. Flux Calculation Equation (1) was used to determine the fluxes through TNF/CNF membrane.
where t is the testing period, P is the applied pressure, S is the membrane's surface area, and V is the volume of water permeate.

Oil Rejection
Equation (2) was used to determine the oil rejection when using TNF/CNF membrane.
where Cf is the feed concentration, Cp is the permeate concentration, and R is the rejection percentage. Oil concentration in the samples of feed (Cf ) and of permeate (Cp) was measured using a TOC analyzer.

Oil Rejection
The membrane reusability was examined with ten filtration cycles. After each filtration cycle, the membrane was washed with distilled water and reused again for the next cycle. Oil concentration in the permeate was measured after each reuse cycle, and the rejection rate was calculated using Equation (2). The flux after each cycle was calculated using Equation (1).

Results and Discussion
We present a new nanofiber-based membrane for oil/saltwater separation in this paper. Ultralong titanate nanofiber and carbon nanofiber make up the new membrane as presented in Figure 3. jection rate was calculated using Equation (2). The flux after each cycle was calculated using Equation (1).

Results and Discussion
We present a new nanofiber-based membrane for oil/saltwater separation in this paper. Ultralong titanate nanofiber and carbon nanofiber make up the new membrane as presented in Figure 3.  Figure 4 represents optical SEM image of the prepared membrane. As seen in Figure  4, the long titanate nanofibers (TNF) are intertwined with the carbon nanofibers (CNF). The length and the diameter of the lab-synthesized TNFs are 60 µm and 200 nm, while the length and the diameter of the CNFs are 50 µm and 150 nm, respectively. The ultralong length of both TNF and CNF ensures the sound mechanical strength and flexibility of the membrane. The interconnected pore structure of the membrane is favorable for high permeation flux, which can be proved in the following performance tests.   Figure 4 represents optical SEM image of the prepared membrane. As seen in Figure 4, the long titanate nanofibers (TNF) are intertwined with the carbon nanofibers (CNF). The length and the diameter of the lab-synthesized TNFs are 60 µm and 200 nm, while the length and the diameter of the CNFs are 50 µm and 150 nm, respectively. The ultralong length of both TNF and CNF ensures the sound mechanical strength and flexibility of the membrane. The interconnected pore structure of the membrane is favorable for high permeation flux, which can be proved in the following performance tests. jection rate was calculated using Equation (2). The flux after each cycle was calculated using Equation (1).

Results and Discussion
We present a new nanofiber-based membrane for oil/saltwater separation in this paper. Ultralong titanate nanofiber and carbon nanofiber make up the new membrane as presented in Figure 3.  Figure 4 represents optical SEM image of the prepared membrane. As seen in Figure  4, the long titanate nanofibers (TNF) are intertwined with the carbon nanofibers (CNF). The length and the diameter of the lab-synthesized TNFs are 60 µm and 200 nm, while the length and the diameter of the CNFs are 50 µm and 150 nm, respectively. The ultralong length of both TNF and CNF ensures the sound mechanical strength and flexibility of the membrane. The interconnected pore structure of the membrane is favorable for high permeation flux, which can be proved in the following performance tests.  The porosity of the membrane was investigated by analyzing the SEM image of the membrane using Image J software [19]. As presented in Table 1, the average size of pores is 0.071 µm, and the area of the pores counts for 21.4% of the membrane area. The average pore size of the membrane is lower than the size of the emulsified oil droplet (d90 = 5.27 µm); thus, the oil cannot penetrate through the membrane, which can be proved by the following performance tests with high oil rejection rates.

XRD and EDS
TiO 2 amorphous structure can be crystalized by calcination at high temperature [20]. Figure 5a represents the XRD of TNF that made up the membrane material. The peaks are marked as R for the rutile structure and A for the anatase structure as identified in the literature [21,22]. The anatase structure peaks are (101), (004), (200), and (105) which correspond to 2 theta degrees of 25.19, 38.4, 48.35, and 52.39, respectively, whereas the rutile structure peaks are (101) and (110), which correspond to 2 theta degrees of 29.4 and 35.08, respectively. The XRD of TNF matches that in the literature which proves the formation of the TNF structure from its precursor [20]. Figure 5b represents the EDS analysis of the membrane, showing the chemical elements (Ti, C, and O) of the new membranes that are made of titanate and carbon nanofibers. µm); thus, the oil cannot penetrate through the membrane, which can be proved b following performance tests with high oil rejection rates.

XRD and EDS
TiO2 amorphous structure can be crystalized by calcination at high temperature Figure 5a represents the XRD of TNF that made up the membrane material. The peak marked as R for the rutile structure and A for the anatase structure as identified i literature [21,22]. The anatase structure peaks are (101), (004), (200), and (105) which respond to 2 theta degrees of 25.19, 38.4, 48.35, and 52.39, respectively, whereas the structure peaks are (101) and (110), which correspond to 2 theta degrees of 29.4 and 3 respectively. The XRD of TNF matches that in the literature which proves the form of the TNF structure from its precursor [20]. Figure

AFM
The purpose of performing AFM analysis of the membrane is to measure its ro ness. The roughness parameters are surface kurtosis (Rku), average roughness (Ra) root mean square roughness (Rq). Figure 6 represents the surface topography o TNF/CNF membrane using AFM analysis. Roughness parameters of the membrane determined from the topography image of a scanning area of 10 × 10 µm. The valu Rku, Rq, and Ra were 3.12, 5.3 nm, and 4.05 nm, respectively. The roughness param values were relatively low, because the relatively fine and long nanofibers were bonded together, which results in a lower valley region in the membrane surface [23] stacking of fine and interpenetrated nanofibers renders the membrane with smooth faces. The link between surface roughness and membrane fouling during membran tration processes has been established [24]. The smoother the membrane surface i less pollutants block the valleys of the membranes, which results in less membrane fo

AFM
The purpose of performing AFM analysis of the membrane is to measure its roughness. The roughness parameters are surface kurtosis (Rku), average roughness (Ra), and root mean square roughness (Rq). Figure 6 represents the surface topography of the TNF/CNF membrane using AFM analysis. Roughness parameters of the membrane were determined from the topography image of a scanning area of 10 × 10 µm. The values of Rku, Rq, and Ra were 3.12, 5.3 nm, and 4.05 nm, respectively. The roughness parameters values were relatively low, because the relatively fine and long nanofibers were well bonded together, which results in a lower valley region in the membrane surface [23]. The stacking of fine and interpenetrated nanofibers renders the membrane with smooth surfaces. The link between surface roughness and membrane fouling during membrane filtration processes has been established [24]. The smoother the membrane surface is, the less pollutants block the valleys of the membranes, which results in less membrane fouling [25,26]. The observation of the contact angle in Figure 7 also supports the low fouling tendency, as a thin hydration layer was assumed to form on the membrane surface owing to the high hydrophilicity of the membrane, which will repel the oil pollutants from the membrane surface, as illustrated in Figure 3.  [25,26]. The observation of the contact angle in Figure 7 also supports the low fouling tendency, as a thin hydration layer was assumed to form on the membrane surface owing to the high hydrophilicity of the membrane, which will repel the oil pollutants from the membrane surface, as illustrated in Figure 3.

Contact Angles for Membrane Wettability
The hydrophilicity of the membrane was identified by studying water contact angle (WCA) and oil contact angle (OCA) [27]. The dynamic water contact angle of the water droplet on the membrane surface was assisted within milliseconds. As represented in Figure 7, the water contact angle (WCA) of the TNF/CNF membrane is 0°, which implies that the membrane is superhydrophilic. Contrariwise, as represented Figure 7, the underwater oil contact angle (OCA) is 161 ± 1.5°, which indicates that the membrane is superoleophobic underwater [28]. While oil and organic substances can cause fouling on a membrane surface, the superhydrophilicity and the underwater superoleophobicity can significantly reduce the fouling of the TNF/CNF membrane. The surface free energy of the CNF/TNF membrane was investigated by using the contact angle [29]. The surface free energy of the membrane was determined to be 72.4 mN/m. The value of surface free energy is high relatively, indicating high surface polarity [29].   [25,26]. The observation of the contact angle in Figure 7 also supports the low fouling tendency, as a thin hydration layer was assumed to form on the membrane surface owing to the high hydrophilicity of the membrane, which will repel the oil pollutants from the membrane surface, as illustrated in Figure 3.

Contact Angles for Membrane Wettability
The hydrophilicity of the membrane was identified by studying water contact angle (WCA) and oil contact angle (OCA) [27]. The dynamic water contact angle of the water droplet on the membrane surface was assisted within milliseconds. As represented in Figure 7, the water contact angle (WCA) of the TNF/CNF membrane is 0°, which implies that the membrane is superhydrophilic. Contrariwise, as represented Figure 7, the underwater oil contact angle (OCA) is 161 ± 1.5°, which indicates that the membrane is superoleophobic underwater [28]. While oil and organic substances can cause fouling on a membrane surface, the superhydrophilicity and the underwater superoleophobicity can significantly reduce the fouling of the TNF/CNF membrane. The surface free energy of the CNF/TNF membrane was investigated by using the contact angle [29]. The surface free energy of the membrane was determined to be 72.4 mN/m. The value of surface free energy is high relatively, indicating high surface polarity [29].

Contact Angles for Membrane Wettability
The hydrophilicity of the membrane was identified by studying water contact angle (WCA) and oil contact angle (OCA) [27]. The dynamic water contact angle of the water droplet on the membrane surface was assisted within milliseconds. As represented in Figure 7, the water contact angle (WCA) of the TNF/CNF membrane is 0 • , which implies that the membrane is superhydrophilic. Contrariwise, as represented Figure 7, the underwater oil contact angle (OCA) is 161 ± 1.5 • , which indicates that the membrane is superoleophobic underwater [28]. While oil and organic substances can cause fouling on a membrane surface, the superhydrophilicity and the underwater superoleophobicity can significantly reduce the fouling of the TNF/CNF membrane. The surface free energy of the CNF/TNF membrane was investigated by using the contact angle [29]. The surface free energy of the membrane was determined to be 72.4 mN/m. The value of surface free energy is high relatively, indicating high surface polarity [29].

Oil on Water Emulsion
One phase of oil in water emulsion is prepared prior to being used in the experiments as seen in Figure 8. The emulsified oil is characterized using ViPA. The mean size of the oil drops is 3.35 µm with d10, d50, and d90 sizes of 2.04 µm, 2.83 µm, and 5.27 µm, respectively, Appl. Sci. 2023, 13, 6792 9 of 14 as presented in Table 2. The particle mean size of the oil emulsion shows that the particle produced by the bath sonication method produces a small oil particle size that is below 20 µm.

Oil on Water Emulsion
One phase of oil in water emulsion is prepared prior to being used in the experiments as seen in Figure 8. The emulsified oil is characterized using ViPA. The mean size of the oil drops is 3.35 µm with d10, d50, and d90 sizes of 2.04 µm, 2.83 µm, and 5.27 µm, respectively, as presented in Table 2. The particle mean size of the oil emulsion shows that the particle produced by the bath sonication method produces a small oil particle size that is below 20 µm.   Figure 9 displays VIPA microscopic photograph of the oil droplets in the feed emulsion and permeate solutions. To visualize the oil emulsion in water, the oil emulsion was dyed with Oil Red EGN. Prior to filtration, the VIPA microscopic picture of the filtration exhibits the presence of oil droplets in the emulsion as observed in Figure 9a. As demonstrated in Figure 9d, oil droplets are not visible in the VIPA microscopic image after filtration, which indicates TNF/CNF membrane has removed the emulsified oil droplet from the feed.   3.5.2. Image Characterization of the Water/Oil Solutions before and after Treatment Figure 9 displays VIPA microscopic photograph of the oil droplets in the feed emulsion and permeate solutions. To visualize the oil emulsion in water, the oil emulsion was dyed with Oil Red EGN. Prior to filtration, the VIPA microscopic picture of the filtration exhibits the presence of oil droplets in the emulsion as observed in Figure 9a. As demonstrated in Figure 9d, oil droplets are not visible in the VIPA microscopic image after filtration, which indicates TNF/CNF membrane has removed the emulsified oil droplet from the feed.

Oil on Water Emulsion
One phase of oil in water emulsion is prepared prior to being used in the experiments as seen in Figure 8. The emulsified oil is characterized using ViPA. The mean size of the oil drops is 3.35 µm with d10, d50, and d90 sizes of 2.04 µm, 2.83 µm, and 5.27 µm, respectively, as presented in Table 2. The particle mean size of the oil emulsion shows that the particle produced by the bath sonication method produces a small oil particle size that is below 20 µm.   Figure 9 displays VIPA microscopic photograph of the oil droplets in the feed emulsion and permeate solutions. To visualize the oil emulsion in water, the oil emulsion was dyed with Oil Red EGN. Prior to filtration, the VIPA microscopic picture of the filtration exhibits the presence of oil droplets in the emulsion as observed in Figure 9a. As demonstrated in Figure 9d, oil droplets are not visible in the VIPA microscopic image after filtration, which indicates TNF/CNF membrane has removed the emulsified oil droplet from the feed.

Performance Tests with Different Oils
The performance of the new titanate nanofiber/carbon nanofiber (TNF/CNF) membrane was assisted using different oils in water emulsion in the feed which are vegetable oil, gasoline, engine oil, n-octane, and n-hexane. As represented in Figure 10a, the oil rejection rate exceeds 99% for the different types of oil emulsion. The oil concentration in the permeate was less than US EPA discharge limit (42 mg/L) as presented in Figure 10b. The oil rejection rate for the different types of oil ranges between 1520 LMH/bar and 1600 LMH/bar as represented in Figure 10a.

Performance Tests with Different Oils
The performance of the new titanate nanofiber/carbon nanofiber (TNF/CNF) membrane was assisted using different oils in water emulsion in the feed which are vegetable oil, gasoline, engine oil, n-octane, and n-hexane. As represented in Figure 10a, the oil rejection rate exceeds 99% for the different types of oil emulsion. The oil concentration in the permeate was less than US EPA discharge limit (42 mg/L) as presented in Figure 10b. The oil rejection rate for the different types of oil ranges between 1520 LMH/bar and 1600 LMH/bar as represented in Figure 10a.  Table 3 presents some reported data from literature of different membranes and their performance for oil/water separation. TNF/CNF membranes present a high rejection rate and water flux while having low operating pressure relatively.   Table 3 presents some reported data from literature of different membranes and their performance for oil/water separation. TNF/CNF membranes present a high rejection rate and water flux while having low operating pressure relatively.

Performance Tests with Different Salty Environments
The content of produced water and offshore oil spills has high salinity; for this reason, the performance test of TNF/CNF membrane was conducted under different saline environments. Figure 11 presents the outcome of the high salinity emulsion treatment using a TNF/CNF membrane. The percentage of oil removal was above 99% for different salty environments as represented in Figure 11a, and the oil concentration in the permeate was below 11 ppm as shown in Figure 11b, which is lower than the discharge limit of EPA regulations. High oil rejection rate was maintained at high saline environment as presented in Figure 11a. As salts only can be dissolved in water rather than oil and the new membrane has a high separation rate between oil and water as evidenced in Figure 11, therefore there was no significant differences in terms of oil rejection rates between different salty environments. This is an indication that the membrane can function well under high saline environment. Figure S2 shows the water fluxes using TNF/CNF membrane using different loading of TNF and CNF and the percentages of oil rejection using TNF/CNF membrane using different loading of TNF and CNF.

Performance Tests with Different Salty Environments
The content of produced water and offshore oil spills has high salinity; for this reason, the performance test of TNF/CNF membrane was conducted under different saline environments. Figure 11 presents the outcome of the high salinity emulsion treatment using a TNF/CNF membrane. The percentage of oil removal was above 99% for different salty environments as represented in Figure 11a, and the oil concentration in the permeate was below 11 ppm as shown in Figure 11b, which is lower than the discharge limit of EPA regulations. High oil rejection rate was maintained at high saline environment as presented in Figure 11a. As salts only can be dissolved in water rather than oil and the new membrane has a high separation rate between oil and water as evidenced in Figure 11, therefore there was no significant differences in terms of oil rejection rates between different salty environments. This is an indication that the membrane can function well under high saline environment. Figure S2 shows the water fluxes using TNF/CNF membrane using different loading of TNF and CNF and the percentages of oil rejection using TNF/CNF membrane using different loading of TNF and CNF. 3.5.5. Reusability Test for the Membranes TNF/CNF membrane reusability was examined using ten filtration cycles. After each filtration cycle, the membrane was washed with distilled water and reused again for the next cycle. Oil concentration in the permeate was measured after each reuse cycle. As seen in Figure 12, throughout the 10 operating cycles, oil rejection rates were over 99% for all cycles. The permeate's oil content was consistently below the US EPA's oil disposal limit of 42 ppm. These findings show that the TNF/CNF nanocomposite membranes have excellent durability. It is worth noting that for the membrane washing, there is no need for 3.5.5. Reusability Test for the Membranes TNF/CNF membrane reusability was examined using ten filtration cycles. After each filtration cycle, the membrane was washed with distilled water and reused again for the next cycle. Oil concentration in the permeate was measured after each reuse cycle. As seen in Figure 12, throughout the 10 operating cycles, oil rejection rates were over 99% for all cycles. The permeate's oil content was consistently below the US EPA's oil disposal limit of 42 ppm. These findings show that the TNF/CNF nanocomposite membranes have excellent durability. It is worth noting that for the membrane washing, there is no need for any chemicals to be used (only distilled water used), which strongly suggests the good fouling-resistance of the membranes. The TNF/CNF membranes' superhydrophilic and oil-repellent surface can be consistently preserved. Figure S3 shows the long-term stability tests under acidic environment. Figure S4 shows the long-term stability tests under basic environment. any chemicals to be used (only distilled water used), which strongly suggests the good fouling-resistance of the membranes. The TNF/CNF membranes' superhydrophilic and oil-repellent surface can be consistently preserved. Figure S3 shows the long-term stability tests under acidic environment. Figure S4 shows the long-term stability tests under basic environment.

Conclusions
For effective and reliable oil/saltwater separation, a novel type of nanostructured TNF/CNF membrane was presented in this study. The novel membranes were made of ultralong titanate and carbon nanofibers. The membranes show high hydrophilicity and high oil repellence, which render the excellent anti-oil-fouling property. The membranes feature an interconnected porous structure, which enables the high water permeation flux (1520 LMH/bar) at low operating pressure. The novel TNF/CNF membrane exhibits high oil removal above 99.1%, oil content in the permeate below the US environmental discharge limit (42 ppm). Most importantly, even after multiple cycles of reuse in environments with various salinities, the performance with oil rejection rate and water flux can be well maintained. This new membrane has great potential to treat oil/gas field production water and marine oil spills due to its durability, separation efficiency, fouling resistance, and inexpensive fabrication. The future work for this research may focus on the prototyping of the new membranes at a larger scale to further demonstrate its industrial applicability.

Conclusions
For effective and reliable oil/saltwater separation, a novel type of nanostructured TNF/CNF membrane was presented in this study. The novel membranes were made of ultralong titanate and carbon nanofibers. The membranes show high hydrophilicity and high oil repellence, which render the excellent anti-oil-fouling property. The membranes feature an interconnected porous structure, which enables the high water permeation flux (1520 LMH/bar) at low operating pressure. The novel TNF/CNF membrane exhibits high oil removal above 99.1%, oil content in the permeate below the US environmental discharge limit (42 ppm). Most importantly, even after multiple cycles of reuse in environments with various salinities, the performance with oil rejection rate and water flux can be well maintained. This new membrane has great potential to treat oil/gas field production water and marine oil spills due to its durability, separation efficiency, fouling resistance, and inexpensive fabrication. The future work for this research may focus on the prototyping of the new membranes at a larger scale to further demonstrate its industrial applicability.