Nanoscale Tribological Properties of Nanostructure Fe3Al and (Fe,Ti)3Al Compounds Fabricated by Spark Plasma Sintering Method
Next Article in Special Issue
Structural Evolution of Bulk Silver during Cold Rolling and Annealing
Previous Article in Journal
Effect of Residual Stress on Hydrogen Diffusion in Thick Butt-Welded High-Strength Steel Plates
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Metals
Volume 12
Issue 7
10.3390/met12071078
metals-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Gram-Scale Synthesis of Carbon-Supported Sub-5 nm PtNi Nanocrystals for Efficient Oxygen Reduction

by
Minli Wang
1,2,
Xu Chen
1,
Wenwen Xu
1,
Zhongfeng Wang
1,2,
Peilei He
1,2,* and
Zhiyi Lu
1,2,*
1
Key Laboratory of Advanced Fuel Cells and Electrolyzers Technology of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China
2
College of Materials Science and Opto-Electronic Technology, University of Chinese Academy of Sciences, Beijing 100049, China
*
Authors to whom correspondence should be addressed.
Metals 2022, 12(7), 1078; https://doi.org/10.3390/met12071078
Submission received: 4 May 2022 / Revised: 20 June 2022 / Accepted: 21 June 2022 / Published: 23 June 2022
(This article belongs to the Special Issue Metallic Functional Materials)
Browse Figures
Review Reports Versions Notes

Abstract

:
The preparation of a high performance and durability with low-platinum (Pt) loading oxygen reduction catalysts remains a challenge for the practical application of fuel cells. Alloying Pt with a transition metal can greatly improve the activity and durability for oxygen reduction reaction (ORR). In this work, we present a one-pot wet-chemical strategy to controllably synthesize carbon supported sub-5 nm PtNi nanocrystals with a ~3% Pt loading. The as-prepared PtNi/C-200 catalyst with a Pt/Ni atomic ratio of 2:3 shows a high oxygen reduction activity of 0.66 A mgpt−1 and outstanding durability over 10,000 potential cycles in 0.1 M KOH in a half-cell condition. The PtNi/C-200 catalyst exhibits the highest ORR activity, with an onset potential (Eonset) of 0.98 V and a half-wave potential (E1/2) of 0.84 V. The mass activity and specific activity are 3.89 times and 9.16 times those of 5% commercial Pt/C. More importantly, this strategy can be applied to the gram-scale synthesis of high-efficiency electrocatalysts. As a result, this effective synthesis strategy has a significant meaning in practical applications of full cells.

Graphical Abstract

1. Introduction

As a renewable energy source, fuel cells have been studied and developed by many researchers in recent years due to their high-energy density, environmental friendly attribute, and high efficiency [1,2,3]. For the electrodes of the fuel cells, catalysts play a crucial role in the efficiency of energy conversion, especially the sluggish kinetics of ORR at the cathode [4]. Platinum (Pt) as the cathode catalyst is generally considered as the most desirable and promising electrocatalyst to promote the ORR [5,6,7,8]. Nevertheless, to realize the large-scale commercial implementation of Pt catalysts in fuel cells, the following challenges need to be addressed: the low durability of catalysts, the high cost of Pt, and the sluggish kinetics of the ORR [9].
Recently, different strategies have been explored to reduce the platinum usage without compromising the ORR activity. First, engineering the structure of the Pt nanocrystals could tune the Pt coordination environment and exposed catalytic surface [10,11,12]. Nonetheless, some of the obtained catalysts are still suffering from a high cost and poor durability [13,14,15]. Second, alloying Pt with a less expensive 3d transition metal (Ni, Co, Cu, etc.) is a feasible method to improve the ORR intrinsic activity [16,17,18,19,20]. For example, Tian et al. reported that 1D bunched PtNi alloy nanocages with a Pt-skin structure displayed a high activity and durability for ORR [21]. Third, nonmetal element doping has been adopted to tune the electronic structure of Pt and Pd, such as boron, phosphorus, and sulfur [22,23,24,25]. However, the promoting effect of nonmetal doping is much lower than that of pure Pt or Pt-based alloy catalysts [26]. Nowadays, the strategies for improving the performance of the Pt catalyst mainly focus on Pt alloying with transition metals. However, some reported Pt alloy catalysts have too large a particle size and a low Pt utilization, which are not suitable for fuel cell applications [27,28]. Meanwhile, it is still difficult to achieve the large-scale synthesis of Pt alloy catalysts due to the harsh experimental conditions in the preparation of the alloy structure [29]. As a result, the gram-scale synthesis of Pt alloy electrocatalysts with a smaller size is highly desirable to realize the commercial viability of fuel cells.
In this work, we present a facile and gram-scale synthesis of sub-5 nm PtNi alloy nanoparticles on carbon carriers (PtNi/C) via a one-pot wet-chemical approach. The formation of the PtNi alloy induced the Pt lattice contraction and lowered the d-band center of Pt, leading to a weaker adsorption of oxygen species. Benefiting from the PtNi alloy structure, the obtained PtNi/C shows excellent ORR activity, with a mass activity of 0.66 A mgpt−1 and a specific activity of 2.13 mA cm−2 at the potential of 0.9 V vs. the reversible hydrogen electrode (RHE) in 0.1 M KOH, which are three times and nine times higher than those of 5% commercial Pt/C. The PtNi/C also shows a superior stability, with only a 5 mV negative shift after 10,000 potential cycles. This work may inspire new ideas for the gram-scale synthesis of a low-Pt electrocatalyst for the future practical application of fuel cells.

2. Materials and Methods

2.1. Chemicals and Reagents

Platinum(II) acetylacetonate (Pt(acac)2, 97%, Aladdin, Shanghai, China), nickel(II) acetylacetonate (Ni(acac)2, 95%, Aladdin, Shanghai, China), polyvinyl pyrrolidone (PVP, average MW = 8000, Aladdin, Shanghai, China), benzoic acid (C6H5COOH, ≥99.5%, Aladdin, Shanghai, China), carbon black (Vulcan XC-72, Cabot, Boston, MA, USA), benzyl alcohol (C7H8O, Aldrich, St. Louis, MO, USA), acetone (CH3COCH3, Sinopharm Chemical ReagentCo., Ltd., Shanghai, China.), ethanol (95%, Sinopharm Chemical ReagentCo., Ltd., Shanghai, China).

2.2. Electrocatalysts Synthesis

Synthesis of the PtNi/C catalysts. The PtNi/C-200 catalysts were prepared by a one-pot method. A total of 8 mg Pt(acac)2, 10.28 mg Ni(acac)2, 90 mg carbon black, 50 mg benzoic acid, 80 mg PVP, and 5 mL benzyl alcohol were added to a flask with magnetic stirring and heated to 200 °C in an oil bath with a ramp of 5 °C min−1. The temperature was held at 200 °C for 12 h. Then, the flask was naturally cooled down to room temperature. The products were collected by centrifugation and washed with an ethanol/acetone mixture three times. Finally, the products were vacuum dried for 12 h. PtNi/C-150, PtNi/C-170, and PtNi/C-190 catalysts were synthesized by adjusting the reaction temperature to 150 °C, 170 °C, and 190 °C. PtNi/C-3:1, PtNi/C-2:1, PtNi/C-1:1, and PtNi/C-1:3 catalysts were synthesized by adjusting the amounts of nickel(Ⅱ) acetylacetonate (Ni(acac)2) to 1.74, 2.61, 5.20, and 15.68 mg. For the synthesis of the PtNi nanocrystals, the procedures were the same as for the PtNi/C catalysts, except that carbon black was not added.
Gram-scale synthesis of PtNi/C catalysts. The G-PtNi/C-200 catalysts were prepared by a one-pot method. A total of 96 mg Pt(acac)2, 123.36 mg Ni(acac)2, 1080 mg carbon black, 600 mg benzoic acid, 960 mg PVP, and 60 mL benzyl alcohol were added to a flask with magnetic stirring and heated to 200 °C in an oil bath with a ramp of 5 °C min−1. The temperature was held at 200 °C for 12 h. Then, the flask was naturally cooled down to room temperature. The products were collected by centrifugation and washed with an ethanol/acetone mixture three times. Finally, the products were vacuum dried for 12 h.

2.3. Material Characterization

X-ray diffraction (XRD, D8 DISCOVER, Brukerb, Salbrucken, Germany) patterns were collected using Cu Kα radiation. Transmission electron microscopy (TEM, Talos F200x, ThemoFisher, Waltham, MA, USA) and high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM, Talos F200x, ThemoFisher, Waltham, MA, USA) were used to characterize the PtNi/C catalysts. Energy dispersive X-ray spectroscopy (EDS, Talos F200x, ThemoFisher, Waltham, MA, USA) was used to analyze the composites of PtNi/C catalysts. The valence states of the elements on the PtNi/C catalysts were determined by X-ray photoelectron spectroscopy (XPS, AXIS SUPRA, Kratos, Manchester, England). Inductively coupled plasma optical emission spectrometry (ICP-OES, SPECTRO ARCOSII, Kleve, Germany) was used to analyze the composition of the catalysts.

2.4. Electrochemical Characterization

The electrocatalytic activity and stability for the oxygen reduction reaction (ORR) were evaluated by an electrochemical workstation (CHI 760E, Shanghai ChenHua Instrument, Shanghai, China) with a classic three-electrode system. A glassy-carbon rotating disk electrode (RDE, Pine Research Instrumentation, Durham, NC, USA, diameter: 5 mm, area: 0.1963 cm2), a graphite rod, and a saturated calomel electrode were used as the working electrode, counter electrode, and reference electrode, respectively. The catalyst inks were prepared by dispersing 10 mg of the catalyst powder in 950 μL isopropanol containing 50 μL of 5 wt% Nafion solution under sonication for 30 min. A total of 5 μL of the ink was dropped onto the glassy carbon rotating disk electrode and dried in air. The Pt loading amounts of all PtNi/C catalysts on the glassy carbon rotating disk electrode were 7.64 μgPt cm−2. For comparison, the commercial Pt/C catalyst (5 wt.%, Alfa Aesar, Shanghai, China) and the commercial Pt/C catalyst (20 wt.%, TANAKA, Tokyo, Japan) were used as benchmark catalysts with Pt loading with 12.73 μgPt cm−2 and 50.94 μgPt cm−2. Cyclic voltammograms (CV) were performed at the range of 0 to 1 V (vs. RHE) at a scan rate of 50 mV s−1 in a 0.5 M H2SO4 N2-saturated solution to measure electrochemically active surface area (ECSA). Alkaline electrochemical properties were tested in 0.1 M KOH. Linear sweep voltammograms (LSV) were conducted between 0 and 1 V (vs. RHE) at a scan rate of 10 mV s−1 in 0.1 M KOH with saturated oxygen. The accelerated durability testing (ADT) was performed at room temperature by applying cyclic potential sweeps between 0.6 and 1.1 V vs. RHE at 200 mV s−1 for 10,000 cycles.

3. Results

3.1. Characterization of PtNi/C Nanostructures

Firstly, PtNi alloy nanocrystals with a particle size of approximately 5 nm were synthesized using Pt(acac)2 and Ni(acac)2 (initial ratio 1:2) as precursors in which polyvinylpyrrolidone (PVP) acted as capping agents (Figure S1). In order to further reduce the Pt loading and enhance the mass transfer capacity, the carbon-supported PtNi alloy could be obtained by introducing a carbon carrier (Vulcan XC-72) into this system. As illustrated in Figure 1, PtNi/C was synthesized by a one-pot wet-chemical method (detailed experiments can be seen in the Section 2).
PtNi/C could be synthesized at 150, 170, 190, and 200 °C to obtain the PtNi/C-T samples (T = 150, 170, 190, and 200). As shown in Figure 2, the crystal structure of the as-synthesized PtNi/C was further explored by X-ray diffraction (XRD). The diffraction peak between 20° and 30° is consistent with the Vulcan XC-72 [30] (Figure S2). Compared with the standard Pt, all of the characteristic peaks shift to a higher angle due to the Pt lattice contraction after alloying with Ni. The lattice contraction of Pt is profitable to the adsorption and dissociation of the oxygen molecule, which could result in the improvement of the ORR performance [31]. It is clearly observed that characteristic peaks become stronger and narrower as the reaction temperature increases from 150 °C to 200 °C. As the temperature increases to 200 °C, the crystallinity of the PtNi alloy is much higher, verified by the sharp characteristic peaks in the XRD patterns. These control experiments reveal that the reaction temperature contributes significantly to the structural evolution of PtNi/C-T.
To further determine the structure of the PtNi/C, the as-synthesized PtNi/C-200 was characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). As shown in Figure 3a,b, spherical nanoparticles with uniform particle size are carbon carriers. The high-resolution TEM (HRTEM) image (Figure 3c) shows that the lattice spacing is 0.216 nm, coinciding with the face-centered-cubic phase of the PtNi(111) plane. The lattice spacing of PtNi is contracted compared with Pt (Figure S3). The high-angle annular dark field scanning transmission electron microscopy (HAADF-STEM) image (Figure 3d) indicates that PtNi alloy nanoparticles are uniformly distributed on the carbon carrier. According to the size histogram in Figure 3e, more than 97% of the nanoparticles are smaller than 5 nm, and the nanoparticles in the range of 3–4 nm are predominant. The energy disperse spectroscopy (EDS) elemental mapping exhibits an even distribution of Pt and Ni elements throughout the particles, further indicating the formation of the PtNi alloy structure (Figure 3f). Furthermore, this synthesis protocol can also be realized for a 12-fold scale up, which can produce over 1 g of catalyst at one time (Figure 1). According to the XRD pattern, the product was consistent with those samples synthesized in small batches (Figure S4). Therefore, the present synthetic method allows for the synthesis of PtNi/C in a milligram-to-gram scale.
Then, inductively coupled plasma optical-emission spectrometry (ICP-OES) was used to determine the contents of Pt and Ni. The ICP-OES results indicate that the loading for Pt and Ni in the PtNi/C-200 are 3.04% and 1.29%, respectively (Table S1). The calculation results show that the atomic ratio of Pt to Ni is 2:3. The surface composition and electronic structure of the PtNi/C were investigated by X-ray photoelectron spectroscopy (XPS). As shown in Figure 4a, two major peaks at 71.3 eV and 74.7 eV are assigned to metallic Pt 4f7/2 and Pt 4f5/2. The two peaks at 72.2 eV and 76.1 eV are assigned to the oxidation state of Pt. The Ni 2p XPS spectrum (Figure 4b) indicates that the surface Ni is dominated by an oxidation state, which is consistent with the previous study [32]. The peaks at 852.8 eV and 870 eV also show that a portion of the surface Ni is in a metallic Ni(0) state. The binding energy of PtNi/C-200 at Pt 4f7/2 shows a positive shift relative to pure Pt (71.0 eV), which could be ascribed to the electron transfer from Ni to Pt, suggesting the downshift of the d-band center [26].

3.2. ORR Performance of PtNi/C

The electrocatalytic performance of PtNi/C for ORR was evaluated by the rotating disk electrode (RDE) in an O2-saturated 0.1 M KOH solution at room temperature. In the beginning, we investigated the polarization curves of PtNi/C-T synthesized at different temperatures. As shown in Figure S5, the PtNi/C-200 exhibits the highest half-wave potential in alkaline electrolytes, suggesting that alloy nanoparticles with high-crystallinity contributed to a higher ORR activity. To explore the effect of the Pt/Ni atomic ratio on the ORR performance, the PtNi/C with various initial ratios were synthesized at 200 °C, designated as PtNi/C-3:1, PtNi/C-2:1, PtNi/C-1:1, PtNi/C-1:2, and PtNi/C-1:3, respectively (Figure S6). The metal content of these samples was evaluated by ICP-OES (Table S1). Among these samples, PtNi/C-1:2 exhibits the best oxygen reduction performance (Figure S7). The typical cyclic voltammetry (CV) curves of PtNiC-200 catalysts are shown in Figure S8. The considerable difference in onset and half-wave potential between these catalysts indicates that ORR activity is also determined by the metal contents of alloy nanoparticles. In addition, carbon carriers also have a great impact on the ORR performance of alloys [33]. Therefore, different carbon carriers (Ketjen Black and Vulcan XC-72) have also been adopted to synthesize carbon-supported sub-5 nm PtNi nanocrystals. Figure S9 shows the ORR polarization curves of PtNi/C with different carbon carriers. The polarization curves indicate that the Vulcan XC-72 supported PtNi nanoparticles have the best oxygen reduction performance. Therefore, the PtNi/C mentioned in the following paper is the sample synthesized at 200 °C, using Vulcan XC-72 as a carbon carrier with an initial Pt/Ni ratio of 1:2.
Figure 5a shows the ORR polarization curves of PtNi/C, 5%, and 20% commercial Pt/C. The half-wave potential of PtNi/C with a Pt loading of 3.04% exhibits a 60 mV positive shift compared with the 5% commercial Pt/C. The ORR performance has no attenuation after amplification (Figure S10). Therefore, the existence of Ni has improved the electrocatalytic activity of PtNi/C. The main reason is that the contraction of Pt lattice spacing is more conducive to weakening the binding between O/OH and Pt sites [34], and the strong electronic interaction between Pt and Ni atoms results in the downshift of the d center of the alloyed Pt, thus improving the electrochemical performance [35]. Furthermore, the fast ORR kinetics of the PtNi/C could be indicated by its lowest Tafel slope (77.08 mv dec−1) among all of these catalysts (Figure 5b). In order to further investigate the reaction kinetics of PtNi/C, Figure 5c shows the ORR polarization curves at different rotation rates and Koutecky–Levich (K-L) plots [36]. The number of transferred electrons of PtNi/C is approximately four according to the K-L plots. This indicates that PtNi/C tends to be a four-electron oxygen reduction pathway in 0.1 M KOH.
To evaluate the intrinsic activity of different catalysts, the mass activity and specific activity were calculated by normalizing over the Pt mass and electrochemically active surface areas (ECSA) at 0.9 V vs. RHE [37]. The PtNi/C demonstrates a superior mass activity of 0.66 A mgpt−1, which is much greater than that of 5% Pt/C (0.17 A mgpt−1) and 20% Pt/C (0.22 A mgpt−1). The ECSA of the catalysts measured by underpotentially deposited hydrogen [38] is shown in Figure S11. The ECSA of PtNi/C, commercial Pt/C-5%, and commercial Pt/C-20% electrocatalysts are determined to be 31.05 m2 gPt−1, 79.24 m2 gPt−1, and 54.76 m2 gPt−1, respectively. Meanwhile, the specific activity of PtNi/C reached 2.13 mA cm−2, which is almost a tenfold higher activity than that of 5% Pt/C (0.23 mA cm−2). Obviously, the PtNi/C exhibits a higher mass activity and specific activity than the commercial Pt/C.
Furthermore, the electrochemical impedance spectroscopy (EIS) was employed to study the electrode kinetics during ORR processes, and the application of a Randles-type model was used as the equivalent circuit. Figure 5e shows the Nyquist plots of both bimetallic PtNi/C and Pt/C, featuring a depressed semi-circle shape. The smaller diameter of the semi-circle PtNi/C verifies that the PtNi/C would possess a lower charge transfer resistance RCT (25.79 Ω) and also enhanced ORR kinetics relative to the reference Pt/C (38.13 Ω), as listed in Table S2 and Figure S12.
In order to determine the ORR durability of the catalysts, we measured the ORR performance of different catalysts before and after 10,000 cycles of accelerated durability tests (ADTs). As shown in Figure 5f, PtNi/C exhibited an impressive durability, with only a 5 mV negative shift in the half-wave potential after 10,000 potential cycles in the alkaline electrolyte, which is much better than the 5% commercial Pt/C (Figure S13). A comparison of the electrochemical performance of PtNi/C and recently reported Pt-based electrocatalysts in the alkaline solutions is listed in Table S3. These findings demonstrate that the PtNi/C exhibits a greater long-term catalytic durability.

4. Conclusions

In conclusion, we report a facile method for the gram-scale synthesis of sub-5 nm PtNi nanocrystals on Vulcan XC-72 via a one-pot method to achieve a highly efficient and stable catalyst for ORR. As a result, with a much lower platinum loading of 3.04%, the obtained PtNi/C-200 exhibits an extraordinary ORR activity and outstanding durability over 10,000 potential cycles in 0.1 M KOH. Particularly, the specific activity and mass activity of the PtNi/C are 9.16 and 3.89 times those of the 5% commercial Pt/C. The superior ORR performance of the PtNi/C originated from the exposure of PtNi(111) facets and Pt lattice contraction due to the incorporation of Ni atoms into the Pt lattice. This study provides a simple strategy for the future development of the gram-scale synthesis of Pt-based electrocatalysts, which might be conducive to the future practical application of low-Pt catalysts in fuel cells.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/met12071078/s1, Figure S1: TEM images of PtNi nanocrystals; Figure S2: XRD patterns of PtNi nanocrystals and Vulcan XC-72; Figure S3: HRTEM image of the initial Pt/C; Figure S4: XRD patterns of G-PtNi/C-200 nanocrystals; Figure S5: The ORR polarization curves of PtNi/C-150, PtNi/C-170, PtNi/C-190, and PtNi/C-200 catalysts were conducted in 0.1 M KOH with saturated oxygen; Figure S6: XRD patterns of PtNi/C-3: 1, PtNi/C-2: 1, PtNi/C-1: 1, PtNi/C-1: 2, and PtNi/C-1: 3 nanocrystals; Figure S7: The ORR polarization curves of Ni/XC-72, Pt/XC-72, PtNi/C-3: 1, PtNi/C-2: 1, PtNi/C-1: 1, PtNi/C-1: 2, and PtNi/C-1: 3 catalysts were conducted in 0.1 M KOH with saturated oxygen; Figure S8: The CV curves of PtNiC-200 catalysts; Figure S9: The ORR polarization curves of PtNi/Ketjen Black and PtNi/XC-72 catalysts were conducted in 0.1 M KOH with saturated oxygen; Figure S10: The ORR polarization curves of G-PtNi/C-200, PtNi/C-200 in O2-saturated 0.1 M KOH; Figure S11: ECSA of commercial Pt/C and PtNi/C-200 at 0.9 V (vs. RHE); Figure S12: Nyquist plots of PtNi/C-200 and commercial Pt/C; Figure S13: Long-term stability of commercial Pt/C (5 wt.%) catalyst; Table S1: ICP-OES results for various PtNi/C samples; Table S2: Fitting data of EIS results of commercial Pt/C-20% and PtNi/C-200 in 0.1 M KOH; Table S3: Comparison of the alkaline ORR activity of different Pt-based catalysts. References [39,40,41,42,43,44,45,46] are cited in Supplementary Materials.

Author Contributions

Conceptualization, M.W., P.H. and Z.L.; methodology, M.W. and P.H.; software, M.W., W.X. and Z.W.; validation, M.W., P.H. and W.X.; formal analysis, M.W., P.H. and Z.L.; investigation, M.W., X.C. and P.H., data curation, M.W. and P.H.; writing—original draft preparation, M.W.; writing—review and editing, M.W. and P.H.; supervision, X.C., Z.W. and P.H.; project administration, X.C., P.H. and Z.L.; funding acquisition, M.W. and X.C. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the Hundred Talents Program in Chinese Academy of Sciences and Ningbo S&T Innovation 2025 Major Special Program (2019B10046, 2020Z059 and 2020Z107).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Staffell, I.; Scamman, D. The role of hydrogen and fuel cells in the global energy system. Energy Environ. Sci. 2019, 12, 463–491. [Google Scholar] [CrossRef] [Green Version]
  2. Kampker, A.; Ayvaz, P. Challenges towards large-scale fuel cell production: Results of an expert assessment study. Int. J. Hydrogen Energy 2020, 45, 29288–29296. [Google Scholar] [CrossRef]
  3. Wang, X.X.; Swihart, M.T. Achievements, challenges and perspectives on cathode catalysts in proton exchange membrane fuel cells for transportation. Nat. Catal. 2019, 2, 578–589. [Google Scholar] [CrossRef]
  4. Maruyama, J.; Abe, I. Formation of platinum-free fuel cell cathode catalyst with highly developed nanospace by carbonizing catalase. Chem. Mater. 2005, 17, 4660–4667. [Google Scholar] [CrossRef]
  5. Nørskov, J.K.; Rossmeisl, J. Origin of the overpotential for oxygen reduction at a fuel-cell cathode. J. Phys. Chem. B 2004, 108, 17886–17892. [Google Scholar] [CrossRef]
  6. Kulkarni, A.; Siahrostami, S. Understanding Catalytic activity trends in the oxygen reduction reaction. Chem. Rev. 2018, 118, 2302–2312. [Google Scholar] [CrossRef]
  7. Imaoka, T.; Kitazawa, H. Finding the Most catalytically active platinum clusters with low atomicity. Angew. Chem. Int. Ed. 2015, 54, 9810–9815. [Google Scholar] [CrossRef]
  8. Shao, M.; Chang, Q. Recent Advances in electrocatalysts for oxygen reduction reaction. Chem. Rev. 2016, 116, 3594–3657. [Google Scholar] [CrossRef] [Green Version]
  9. Liu, M.; Zhao, Z. Nanoscale Structure design for high-performance Pt-based ORR catalysts. Adv. Mater. 2019, 31, 1802234. [Google Scholar] [CrossRef]
  10. Li, M.; Zhao, Z. Ultrafine jagged platinum nanowires enable ultrahigh mass activity for the oxygen reduction reaction. Science 2016, 354, 1414–1419. [Google Scholar] [CrossRef] [Green Version]
  11. Liao, H.G.; Zherebetskyy, D. Facet development during platinum nanocube growth. Science 2014, 345, 916–919. [Google Scholar] [CrossRef]
  12. Gan, L.; Cui, C. Element-specific anisotropic growth of shaped platinum alloy nanocrystals. Science 2014, 346, 1502–1506. [Google Scholar] [CrossRef]
  13. Kühl, S.; Gocyla, M. Concave curvature facets benefit oxygen electroreduction catalysis on octahedral shaped PtNi nanocatalysts. J. Mater. Chem. A 2019, 7, 1149–1159. [Google Scholar] [CrossRef] [Green Version]
  14. Kim, T.S.; Kim, J. Catalytic synergy on PtNi Bimetal catalysts driven by interfacial intermediate structures. ACS Catal. 2020, 10, 10459–10467. [Google Scholar] [CrossRef]
  15. Greeley, J.; Stephens, I.E.L. Alloys of platinum and early transition metals as oxygen reduction electrocatalysts. Nat. Chem. 2009, 1, 552–556. [Google Scholar] [CrossRef]
  16. Polani, S.; MacArthur, K.E. Size and Composition dependence of oxygen reduction reaction catalytic activities of Mo-doped PtNi/C octahedral nanocrystals. ACS Catal. 2021, 11, 11407–11415. [Google Scholar] [CrossRef]
  17. Bu, L.; Guo, S. Surface engineering of hierarchical platinum-cobalt nanowires for efficient electrocatalysis. Nat. Commun. 2016, 7, 11850. [Google Scholar] [CrossRef]
  18. Lai, W.H.; Zhang, L. Activating inert surface Pt Single atoms via subsurface doping for oxygen reduction reaction. Nano Lett. 2021, 21, 7970–7978. [Google Scholar] [CrossRef]
  19. Du, X.X.; He, Y. Fine-grained and fully ordered intermetallic PtFe catalysts with largely enhanced catalytic activity and durability. Energy Environ. Sci. 2016, 9, 2623–2632. [Google Scholar] [CrossRef]
  20. Zhang, Z.; Luo, Z. One-pot synthesis of highly anisotropic five-fold-twinned PtCu nanoframes used as a bifunctional electrocatalyst for oxygen reduction and methanol oxidation. Adv. Mater. 2016, 28, 8712–8717. [Google Scholar] [CrossRef]
  21. Tian, X.; Zhao, X. Engineering bunched Pt-Ni alloy nanocages for efficient oxygen reduction in practical fuel cells. Science 2019, 366, 850–856. [Google Scholar] [CrossRef]
  22. Naveen, M.H.; Huang, Y. Enhanced electrocatalytic activities of in situ produced Pd/S/N-doped carbon in oxygen reduction and hydrogen evolution reactions. ACS Appl. Energy Mater. 2021, 4, 575–585. [Google Scholar] [CrossRef]
  23. He, T.; Wang, W. Deposition of atomically thin Pt shells on amorphous palladium phosphide cores for enhancing the electrocatalytic durability. ACS Nano 2021, 15, 7348–7356. [Google Scholar] [CrossRef] [PubMed]
  24. Yang, H.N.; Kim, W.J. Effect of boron-doping levels in Pt-B-graphene on the electrochemical properties and cell performance of high temperature proton exchange membrane fuel cells. Electrochim. Acta 2016, 209, 430–439. [Google Scholar] [CrossRef]
  25. Vinayan, B.P.; Nagar, R. Novel platinum-cobalt alloy nanoparticles dispersed on nitrogen-doped graphene as a cathode electrocatalyst for PEMFC applications. Adv. Funct. Mater. 2012, 22, 3519–3526. [Google Scholar] [CrossRef]
  26. Lu, B.A.; Shen, L.F. Structurally disordered phosphorus-doped Pt as a highly active electrocatalyst for an oxygen reduction reaction. ACS Catal. 2021, 11, 355–363. [Google Scholar] [CrossRef]
  27. Jiang, B.; Li, C. Mesoporous Pt nanospheres with designed pore surface as highly active electrocatalyst. Chem. Sci. 2016, 7, 1575–1581. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  28. Ma, L.; Wang, C. Platinum multicubes prepared by Ni2+-mediated shape evolution exhibit high electrocatalytic activity for oxygen reduction. Angew. Chem. Int. Ed. 2015, 54, 5666–5671. [Google Scholar] [CrossRef]
  29. Huang, X.; Zhao, Z. High-performance transition metal-doped Pt3Ni octahedra for oxygen reduction reaction. Science 2015, 348, 1230–1234. [Google Scholar] [CrossRef] [Green Version]
  30. Qu, R.; Tang, S. Improving Ni(OH)2/C supercapacitive performances through mixed solvents and thermal treatment of XC-72. ACS Sustain. Chem. Eng. 2018, 6, 15560–15569. [Google Scholar] [CrossRef]
  31. Xiao, W.; Lei, W. Recent advances of structurally ordered intermetallic nanoparticles for electrocatalysis. ACS Catal. 2018, 8, 3237–3256. [Google Scholar] [CrossRef]
  32. Ramos-Sanchez, G.; Praserthdam, S. Challenges of modelling real nanoparticles: Ni@Pt electrocatalysts for the oxygen reduction reaction. Phys. Chem. Chem. Phys. 2015, 17, 28286–28297. [Google Scholar] [CrossRef]
  33. Huang, X.; Zhao, Z. A rational design of carbon-supported dispersive Pt-based octahedra as efficient oxygen reduction reaction catalysts. Energy Environ. Sci. 2014, 7, 2957–2962. [Google Scholar] [CrossRef]
  34. Zhao, Y.; Wu, Y. Dependent relationship between quantitative lattice contraction and enhanced oxygen reduction activity over Pt-Cu alloy catalysts. ACS Appl. Mater. Interfaces 2017, 9, 35740–35748. [Google Scholar] [CrossRef]
  35. Chattot, R.; Asset, T. Beyond strain and ligand effects: Microstrain-induced enhancement of the oxygen reduction reaction kinetics on various PtNi/C nanostructures. ACS Catal. 2017, 7, 398–408. [Google Scholar] [CrossRef]
  36. Wang, D.; Xin, H.L. Structurally ordered intermetallic platinum-cobalt core-shell nanoparticles with enhanced activity and stability as oxygen reduction electrocatalysts. Nat. Mater. 2013, 12, 81–87. [Google Scholar] [CrossRef]
  37. Xia, Y.F.; Guo, P. How to appropriately assess the oxygen reduction reaction activity of platinum group metal catalysts with rotating disk electrode. iScience 2021, 24, 103024. [Google Scholar] [CrossRef]
  38. Wei, C.; Sun, S. Approaches for measuring the surface areas of metal oxide electrocatalysts for determining their intrinsic electrocatalytic activity. Chem. Soc. Rev. 2019, 48, 2518–2534. [Google Scholar] [CrossRef]
  39. Li, W.-Z.; Lu, B.-A. High activity and durability of carbon-supported core-shell PtP @Pt/C catalyst for oxygen reduction reaction. Chin. J. Catal. 2021, 42, 2173–2180. [Google Scholar] [CrossRef]
  40. Zhang, N.; Li, L. High Pt utilization efficiency of electrocatalysts for oxygen reduction reaction in alkaline media. Catal. Today 2019, 332, 101–108. [Google Scholar] [CrossRef]
  41. He, W.; Wu, W. Ultrasmall PtNi bimetallic nanoclusters for ultrasmall for oxygen reduction reaction in alkaline media. Int. J. Electrochem. Sci. 2018, 13, 4438–4454. [Google Scholar] [CrossRef]
  42. Zysler, M.; Shokhen, V. Bifunctional Pt–Ni Electrocatalyst Synthesis with Ultralow Platinum Seeds for Oxygen Evolution and Reduction in Alkaline Medium. ACS Appl. Energy Mater. 2022, 5, 4212–4220. [Google Scholar] [CrossRef]
  43. Wang, S.; Xiong, L. Structural and Electronic Stabilization of PtNi Concave Octahedral Nanoparticles by P Doping for Oxygen Reduction Reaction in Alkaline Electrolytes. ACS Appl. Energy Mater. 2018, 10, 27009–27018. [Google Scholar] [CrossRef] [PubMed]
  44. Wang, G.; Yang, Z. Programmable Exposure of Pt Active Facets for Efficient Oxygen Reduction. Angew. Chem. Int. Ed. Engl. 2019, 58, 15848–15854. [Google Scholar] [CrossRef] [PubMed]
  45. Chen, T.-W.; Kang, J.-X. Ultralong PtNi alloy nanowires enabled by the coordination effect with superior ORR durability. RSC Adv. 2016, 6, 71501–71506. [Google Scholar] [CrossRef]
  46. Zhang, G.-R.; Wöllner, S. Hollowed structured PtNi bifunctional electrocatalyst with record low total overpotential for oxygen reduction and oxygen evolution reactions. Appl. Catal. B Environ. 2018, 222, 26–34. [Google Scholar] [CrossRef]
Metals 12 01078 g001 550
Figure 1. Schematic illustration of the formation of PtNi/C.
Figure 1. Schematic illustration of the formation of PtNi/C.
Metals 12 01078 g001
Metals 12 01078 g002 550
Figure 2. XRD patterns of PtNi/C at different reaction temperatures.
Figure 2. XRD patterns of PtNi/C at different reaction temperatures.
Metals 12 01078 g002
Metals 12 01078 g003 550
Figure 3. Structural characterization of PtNi/C-200. (a) SEM image, (b) TEM and (c) HRTEM images, (d) HAADF-STEM image, (e) size histogram, and (f) EDS elemental mapping images of PtNi/C-200.
Figure 3. Structural characterization of PtNi/C-200. (a) SEM image, (b) TEM and (c) HRTEM images, (d) HAADF-STEM image, (e) size histogram, and (f) EDS elemental mapping images of PtNi/C-200.
Metals 12 01078 g003
Metals 12 01078 g004 550
Figure 4. XPS peaks (a) Pt 4f and (b) Ni 2p of PtNi/C.
Figure 4. XPS peaks (a) Pt 4f and (b) Ni 2p of PtNi/C.
Metals 12 01078 g004
Metals 12 01078 g005 550
Figure 5. ORR performance of PtNi/C. (a) Polarization curves of PtNi/C, 5%, and 20% commercial Pt/C in 0.1 M KOH. (b) Tafel plots of PtNi/C, 5%, and 20% commercial Pt/C. (c) Polarization curves of PtNi/C at different rotating speeds: 400, 625, 900, 1225, 1600, and 2025 rpm (insert is the corresponding K-L analysis). (d) Mass activity and specific activity of PtNi/C, 5%, and 20% commercial Pt/C at 0.9 V (vs. RHE). (e) Deviation from the Randles circuit model and the corresponding EIS. (f) Polarization curves of PtNi/C measured before and after 10,000 cycles in 0.1 M KOH.
Figure 5. ORR performance of PtNi/C. (a) Polarization curves of PtNi/C, 5%, and 20% commercial Pt/C in 0.1 M KOH. (b) Tafel plots of PtNi/C, 5%, and 20% commercial Pt/C. (c) Polarization curves of PtNi/C at different rotating speeds: 400, 625, 900, 1225, 1600, and 2025 rpm (insert is the corresponding K-L analysis). (d) Mass activity and specific activity of PtNi/C, 5%, and 20% commercial Pt/C at 0.9 V (vs. RHE). (e) Deviation from the Randles circuit model and the corresponding EIS. (f) Polarization curves of PtNi/C measured before and after 10,000 cycles in 0.1 M KOH.
Metals 12 01078 g005
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Wang, M.; Chen, X.; Xu, W.; Wang, Z.; He, P.; Lu, Z. Gram-Scale Synthesis of Carbon-Supported Sub-5 nm PtNi Nanocrystals for Efficient Oxygen Reduction. Metals 2022, 12, 1078. https://doi.org/10.3390/met12071078

AMA Style

Wang M, Chen X, Xu W, Wang Z, He P, Lu Z. Gram-Scale Synthesis of Carbon-Supported Sub-5 nm PtNi Nanocrystals for Efficient Oxygen Reduction. Metals. 2022; 12(7):1078. https://doi.org/10.3390/met12071078

Chicago/Turabian Style

Wang, Minli, Xu Chen, Wenwen Xu, Zhongfeng Wang, Peilei He, and Zhiyi Lu. 2022. "Gram-Scale Synthesis of Carbon-Supported Sub-5 nm PtNi Nanocrystals for Efficient Oxygen Reduction" Metals 12, no. 7: 1078. https://doi.org/10.3390/met12071078

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.