Self-Assemblable Polymer Smart-Blocks for Temperature-Induced Injectable Hydrogel in Biomedical Applications

Self-assembled temperature-induced injectable hydrogels fabricated via self-assembly of polymer smart-blocks have been widely investigated as drug delivery systems and platforms for tissue regeneration. Polymer smart-blocks that can be self-assembly play an important role in fabrication of hydrogels because they can self-assemble to induce the gelation of their copolymer in aqueous solution. The self-assembly occurs in response to an external stimulus change, such as temperature, pH, glucose, ionic strength, light, magnetic field, electric field, or their combination, which results in property transformations like hydrophobicity, ionization, and conformational change. The self-assembly smart-block based copolymers exist as a solution in aqueous media at certain conditions that are suitable for mixing with bioactive molecules and/or cells. However, this solution turns into a hydrogel due to the self-assembly of the smart-blocks under exposure to an external stimulus change in vitro or injection into the living body for a controllable release of loaded bioactive molecules or serving as a biomaterial scaffold for tissue regeneration. This work reports current scenery in the development of these self-assembly smart-blocks for fabrication of temperature-induced injectable physically cross-linked hydrogels and their potential application as drug delivery systems and platforms for tissue engineering.

Hydrogel networks can be crosslinked using two main strategies, chemical and physical cross-linking (Huynh et al., 2011a;Nguyen et al., 2015;Norouzi et al., 2016;Liu et al., 2017;Yu et al., 2018;Cirillo et al., 2019). Chemically crosslinked hydrogels that normally possess high mechanical strength are fabricated by employing many different chemical reactions, such as free radical, Michael-addition, Schiff base, Click, and enzymatic reactions (Nguyen et al., 2015(Nguyen et al., , 2017Jeon et al., 2016;Liu et al., 2017;Cheng et al., 2018;Huynh et al., 2018;Yu et al., 2018). However, the requirement for implantation process after fabrication and/or the need of crosslinking agents, catalysts, light, enzymes, and/or organic solvents in some cases, which may create negative effects to the encapsulated bioactive molecules and/or cells, may reduce the potential application of these systems. In opposite, physically cross-linked hydrogels can be fabricated via non-covalently linkages, such as hydrophobic interaction, hydrogen bonding and ionic interaction between the smart-blocks in polymers (Huynh et al., 2011a;Nguyen et al., 2015;Norouzi et al., 2016;Liu et al., 2017;Yu et al., 2018;Cirillo et al., 2019). Although the physically cross-linked hydrogels possess lower mechanical strength compared to chemical crosslinked hydrogels, the physically cross-linked hydrogels offer milder conditions for hydrogel formation, and the injectability fulfills a wide range of cavity geometries to form in situ hydrogels without the need of an operation for implantation.
Hydrogels offer many advantages for biomedical applications due to their unique properties that could be used as delivery systems to control the delivery of bioactive molecules for disease therapeutics or biomaterial scaffolds to provide structural tissue integrity in tissue regeneration (Huynh et al., 2011a;Hoffman, 2012). Hydrogels possess a high loading capacity that can be used as localized drug depots for sustained release or provide a high concentration of biological or physicochemical cues for cell activity (Li and Mooney, 2016). The release kinetics of loaded bioactive molecules can be easily tailored by controlling the hydrogel property, such as the hydrophilicity, biocompatibility, degradation and swelling rate, and crosslinking density (Slaughter et al., 2009;Hoffman, 2012;Li and Mooney, 2016). In addition, the aqueous environment in the hydrogels could help protect bioactive molecules and/or cells from damage and/or degradation while maintaining the ability to transport nutrients and waste to improve cell activity. Hydrogels can also be easily injected in deep target sites in the body and act as depots to protect the loaded bioactive molecules and cells from the immune system while maintaining good bioactivity (Slaughter et al., 2009;Huynh et al., 2011a;Hoffman, 2012;Li and Mooney, 2016). Hydrogel polymer molecules can be easily functionalized with cell targeting molecules to improve the biological interactions. For example, functionalized cell adhesive ligands, such as Arg-Gly-Asp (RGD) peptide, improved cell adhesion and spreading in dextran hydrogels (Nguyen et al., 2017). Hydrogel biomaterial scaffolds are also able to provide structural integrity to regenerated tissue constructs. Therefore, hydrogel stiffness is an important factor in regulating cell behavior, the interactions between cells, extracellular matrix, and surrounding host tissues (Vedadghavami et al., 2017). It was also reported that cells exposed to stiffer hydrogels have a higher elastic modulus in their plasma membrane and cells proliferate faster when compared to those exposed to less stiff hydrogels. However, in a stiff hydrogel, the cells migrate slower than their counterparts in softer substrates (Vedadghavami et al., 2017). Therefore, the employed hydrogels should possess a similar stiffness compared to the regenerated tissues to maximize the compatibility and integrity .
Block copolymers are synthetic polymers compose at least two polymer blocks with distinct property and have been widely used for hydrogel fabrarication. Self-assembly synthetic polymer smart-blocks are segments of block copolymers that can selfassemble via property transformations, such as hydrophobicity, and ionization and conformational change, in response to the change of external environmental stimuli, including temperature, pH, glucose, ionic strength, magnetic or electric field, or their combination (Lee et al., 2001a;Hyun et al., 2007;Jiang et al., 2007;Bat et al., 2008;Dayananda et al., 2008;Kang et al., 2010;Huynh et al., 2011a,b;Yu et al., 2014aYu et al., , 2018Guo et al., 2015;Nguyen et al., 2015;Barouti et al., 2016;Chen et al., 2016a,b;Norouzi et al., 2016;Liu et al., 2017;Vidyasagar et al., 2017;Cirillo et al., 2019). These self-assembly synthetic smart-blocks play a key role in controlling the property of their copolymers in aqueous solution for fabrication of injectable self-assembled hydrogels (Huynh et al., 2011a;Nguyen et al., 2015;Norouzi et al., 2016;Yu et al., 2018;Cirillo et al., 2019). Among the stimuli signals, temperature is one of the most popular and easiest stimulus for experimentally control that has been used to induce the self-assembly of a wide range of smart-blocks and subsequently the gelation of their-derived copolymers. Injectable temperature-induced self-assembled hydrogels have been widely investigated as biomaterials for biomedical applications, especially therapeutic molecule delivery and tissue regeneration (Huynh et al., 2011a;Nguyen et al., 2015;Norouzi et al., 2016;Liu et al., 2017;Yu et al., 2018;Cirillo et al., 2019). The bioactive molecules and/or cells can be formulated with the polymer solutions prior to initiation the gelation or injection into the body without the need of an implantation procedure, to form hydrogels which serve as drug depots for sustained and localized delivery or biomaterial scaffolds for tissue regeneration (Figure 1). FIGURE 1 | Photographs of (A,B) in vitro and (C,D) in vivo gelation of 10 wt.% PLGA-PEG-PLGA hydrogel. A polymer solution exists at 5 • C (A) for formulation with bioactive molecules and/or cells before increasing temperature to physiological condition (B, 37 • C) or being injected into an SD rat (C,D) for gel formation to serve as drug depots for sustained and localized delivery or biomaterial scaffolds for tissue regeneration. Reproduced from Loh and Oren (2012) with permission from The Royal Society of Chemistry.
This review aims to provide a development progress of self-assembly synthetic smart-blocks for fabrication of temperature-induced injectable physical cross-linked hydrogels and their potential in the delivery of therapeutic molecules and tissue regeneration. The future outlook of temperatureinduced hydrogel based on these synthetic smart-blocks will also be discussed.

DESIGN OF SELF-ASSEMBLY SYNTHETIC SMART-BLOCKS FOR TEMPERATURE-INDUCED HYDROGELS
The physical properties of polymer smart-blocks play a critical role in fabrication of self-assembled injectable hydrogels because it regulates the ability to assemble their copolymers in response to the stimulation of temperature for forming hydrogels in aqueous solution (Huynh et al., 2011a;Nguyen et al., 2015;Norouzi et al., 2016;Yu et al., 2018;Cirillo et al., 2019). Temperature is one of the most popular signals that has been used to regulate the selfassembly of the smart-blocks to induce gelation. Temperature is also an easy stimulus to experimentally control to induce the self-assembled gelation of a wide range of smart-blocks both in vitro and in vivo. Temperature-responsive smart-blocks are amphiphilic blocks that can exhibit hydrophilic-hydrophobic transformation or conformational change in response to a temperature difference, which creates a change in physical state of an aqueous copolymer solution, e.g., a solution (sol) to a gel (Huynh et al., 2011a;Nguyen et al., 2015;Norouzi et al., 2016;Yu et al., 2018;Cirillo et al., 2019). For example, in aqueous solution, the polymers exist as a sol state at certain low temperature ranges that facilitates the incorporation of bioactive molecules and/or cells before transforming into a 3D hydrogel network (gel state) at physiological temperature (37 • C) for serving as a drug depot for control the delivery and/or a biomaterial scaffold for cell growth.
There are two main mechanisms for self-assembly and subsequently gelation of temperature-sensitive smart-blocks based injectable copolymer hydrogels, including micellization and conformational transitions (Huynh et al., 2011a;Nguyen et al., 2015;Zhang et al., 2015a;Norouzi et al., 2016;Yu et al., 2018;Cirillo et al., 2019). In micellization mechanism, amphiphilic smart-blocks increase their hydrophobicity in response to temperature change, and the micellization occurs due to the hydrophobic interaction between smart-blocks. The degree of micellization can be further triggered with extended temperature change that leads to the association of individual micelles (Figure 2A) or inter-molecular micelles ( Figure 2B) in polymers containing single or multiple smart-blocks in the molecules, respectively, which finally leads to the formation of 3D hydrogel networks. At low concentration, amphiphilic polymers can dissolve as individual molecules in an aqueous solution. However, polymer molecules start to interact with each other to form polymeric micelles at a specific increased polymer concentration which is defined as critical micelle concentration (CMC). The higher hydrophobicity blocks possess lower CMC values, and therefore tend to form stronger interaction micelles to FIGURE 2 | Schematic showing the sol-gel phase transition mechanisms in aqueous solution: (A) association of individual micelles from copolymers contain single amphiphilic smart-blocks, (B) association of inter-molecular micelles from copolymers contain multiple amphiphilic smart-blocks, and (C) conformational changes of peptide-based smart-blocks from random coils to packed β-sheets structure to form hydrogels. (D) A typical sol-gel phase transition of temperature-induced hydrogels, in which a polymer solution exists at low temperatures and exhibits a sol-to-gel phase transition to form a hydrogel at elevated temperatures.
trigger the gelation at lower concentration. The conformational transition gelation mechanism normally happens in peptidebased smart-blocks, which undergo transitions from random coils to packed β-sheets, and potentially further to nanofibers to form 3D hydrogel networks in response to the temperature change ( Figure 2C). In either mechanism, the sequence of the smart-blocks and topology of the copolymer molecules play a critical role in controlling the gelability and gelation mechanism of the designed hydrogels which can be used as effective tools to design a suitable hydrogel system.
A wide range of synthetic polymer smart-blocks exhibit a response to the temperature in an aqueous solution. However, only some of them could trigger the gelation of their (co)polymers in aqueous media at surrounding body conditions that showed potential in biomedical engineering applications. Some typical examples of temperature-sensitive gelable smartblocks are poly(N-isopropylacrylamide) (PNIPAAm), polyethers, e.g., PEG or PEO and poly(propylene oxide) (PPG or PPO), aliphatic polyesters, aliphatic polycarbonates, and polypeptides (Figure 3). The gelation mechanism of these temperaturesensitive smart-blocks based injectable hydrogels and their potential applications in drug delivery, therapeutic treatment and tissue engineering have been widely investigated. This section discusses about the synthesis and gelation of these smart-blocks and their temperature-induced injectable hydrogels.
Polyether Smart-Blocks PEG (Figure 3) is a hydrophilic and neutral charge synthetic polymer with a wide range of molecular weight that has been the most popular smart-block for hydrogel preparation in biomedical applications (Huynh et al., 2011a;Nguyen et al., 2015;Norouzi et al., 2016;Yu et al., 2018;Cirillo et al., 2019). Although PEG is hydrophilic and could not trigger the gelation, it can function as a bridge to induce the cross-linking density of the hydrogels. PEG has been widely used to fabricate chemically cross-linked hydrogels for a wide range of applications, such as drug delivery and tissue regeneration (Nguyen and West, 2002;Nguyen et al., 2018). In addition, the dehydration of PEG at high temperatures reported to result in a gel-to-sol phase transition . PEG is the most important smart-block for conjugation with other smart-blocks to fabricate the hydrogels that are present in most of the synthetic block copolymer hydrogels. PPG (Figure 3) exhibits amphiphilic property at low range molecular weight or when copolymerized with other hydrophilic polymers, such as PEG, and can self-assemble to form micelles in an aqueous solution (Glatter et al., 1994;Allcock et al., 2006;Loh et al., 2010;Choi et al., 2011a;Khaliq et al., 2017;Liow et al., 2017). Its copolymer with PEG in the form of PEG-PPG-PEG copolymers, known as Pluronic (BASF) or the Synperonic PE/F (Croda) or Poloxamer (ICI), are soluble in water at low temperature with a low degree of micellization due to the self-assemble properties of PPG (Huynh et al., 2011a;Khaliq et al., 2017). By increasing temperature, the degree of micellization increases which leads to the formation of associated micellar structure and subsequently results in a sol-to-gel phase transition (Mortensen and Brown, 1993;Glatter et al., 1994;Khaliq et al., 2017;Liow et al., 2017) (Figure 2A). However, when the temperature was further elevated, the dehydration of PEG blocks lead to the reduction in micellar interactions and subsequent the collapse of the 3D hydrogel network, indicated by a gel-to-sol phase transition. Pluronic hydrogels are normally non-biodegradable, short persistent, high permeability, and low mechanical strengths that may limit FIGURE 3 | Structure of some typical self-assembly smart-blocks for fabrication of temperature-induced self-assembled injectable hydrogels. their potential application (Huynh et al., 2011a;Nguyen et al., 2015;Norouzi et al., 2016;Yu et al., 2018;Cirillo et al., 2019). Scientists have modified Pluronic to adjust its critical gel concentration and sol-to-gel phase transition temperature, and improve their biodegradability, thermal and mechanical properties, and their biocompatibility (Cohn et al., 2006;Choi et al., 2011a;Loh et al., 2014;Dou et al., 2016;Wu et al., 2016a). For example, conjugating polyhedral oligosilsesquioxane (POSS) to both end of PEG-PPG-PEG copolymers via atom transfer radical polymerization (ATRP) to form POSS-PEG-PPG-PEG-POSS copolymer hydrogel could increase the solto-gel phase transition temperature from 22 to 33 • C without changing mechanical property of the formed hydrogels . In addition, PPG have also been grafted (Kim D. H. et al., 2010;Nguyen et al., 2016) into or simply mixed (Jung et al., 2017) with natural polymers, such as chitosan, heparin (HEP), hyaluronic acid (HA), and gelatin, to fabricate self-assemble temperature-induced injectable hydrogels. These inherit the biocompatibility of their natural parent polymers and the temperature responsive property of PPG, for improving hydrogel properties. For example, the addition of high molecular weight HA into PEG-PPG-PEG hydrogel could enhance the gel strength due to the co-association of HA into the intermolecular micellar packing in the hydrogel structure (Jung et al., 2017).
The first study reported the preparation of biodegradable aliphatic polyester as self-assembled polymeric injectable hydrogels for drug delivery was published in 1997 (Jeong et al., 1997). Copolymers of PLLA and PEG in the forms of PEG-PLLA diblock or PEG-PLLA-PEG triblock copolymers were synthesized via ROP, followed by urethane coupling to fabricate triblock. The gelation behavior and potential applications as drug delivery systems were investigated. In aqueous media, both PEG-PLLA and PEG-PLLA-PEG existed in the sol state at high temperatures and exhibited a sol-to-gel phase transition upon lowering down the temperature. The release of loaded-dextran, a model drug, was sustained for more than 2 weeks. Although the transition temperature can be regulated by tailoring the block length of biodegradable PLLA, hydrophobic/hydrophilic ratios, polymer end-groups, and/or stereoregularity of the PLLA (Jeong et al., 1997;Park et al., 2001;Li et al., 2007;Nagahama et al., 2008), the high temperature sol state of these hydrogels limited their application due to the potential damage of formulated bioactive molecules and/or encapsulated cells, and patients' inconvenience.
Soon after, other biodegradable aliphatic polyesters, e.g., PLGA, PCL, or PCLA, were added as self-assembly smart-blocks for temperature-induced injectable hydrogels. When the PLLA smart-block were replaced by PLGA or PCL or PCLA to generate PEG-PLGA Chiang et al., 2014;Lei et al., 2017;Shen et al., 2017), PEG-PCLA , and PEG-PCL (Kim et al., 2006a;Hyun et al., 2007;Lee et al., 2010;Kang et al., 2011) diblock or PEG-PLGA-PEG (Jeong et al., 1999b(Jeong et al., , 2000Li, 2003;Luan et al., 2017) and PEG-PCL-PEG triblock copolymers (Bae et al., 2005;Gong et al., 2009a,b;Gou et al., 2010;Hwang et al., 2010;Yin et al., 2010;Mishra et al., 2011;Zhang et al., 2017), these copolymers existed as a sol state in aqueous media at low temperatures and exhibited a sol-gel-sol phase transition upon increasing the temperature ( Figure 2D). These sol-to-gel phase transition are attributed to the micellization of hydrophobic smart-blocks, and the closed packing of individual micelles triggered by increasing temperature (Figure 2A). In addition, increasing the number of PLA smart-blocks in a single copolymer molecule, such as using two PLA blocks (e.g., PLA-PEG-PLA) (Guo et al., 2015;Shi et al., 2016), also offered a sol state window at low temperatures. The window of sol state at low temperatures offers mild conditions for formulation of bioactive molecules and/or cells before inducing the gelation or being injected into the body.
Topology of copolymers is one of the key factors that regulates the self-assembled gelation of the injectable hydrogels. Hydrogels consist of single amphiphilic aliphatic polyester smart-block in the backbone normally require higher polymer concentration to induce the gelation and the resulting hydrogels possess low mechanical properties due to their associated individual micelles triggered gelation mechanism Lee et al., 2010;Kang et al., 2011;Lei et al., 2017;Luan et al., 2017;Shen et al., 2017). In contrast, copolymers consist of multiple smartblocks in their backbone, such as PLGA-PEG-PLGA, PCGA-PEG-PCGA, PCL-PEG-PCL, PCLA-PEG-PCLA, poly(CL-co-pdioxanone) (PCLDO)-PEG-PCLDO, and (PEG-PPG-PHB) x can form hydrogels at lower polymer concentrations with higher gel strengths due to the formation of associated inter-molecular micelles ( Figure 2B; Bae et al., 2005;Loh and Oren, 2012;Li et al., 2013;Yu et al., 2014a,b;Yuan et al., 2015;Zhang L. et al., 2015;Cao et al., 2016;Wang S. J. et al., 2016;Zhang et al., 2016;Santovena et al., 2017;Wee et al., 2017). For example, 25% aqueous solutions of PEG-PLGA  and PLGA-PEG-PLGA Yu et al., 2014a,b;Yuan et al., 2015) exhibited a similar reversible sol-to-gel phase transition with increasing temperature but possessed different maximum storage moduli of ∼200 and 1,000 Pa, respectively. In aqueous solution, these multiple smart-blocks contained copolymers form bridged micelles at low temperatures and transform to the association of bridged micelles at higher temperatures due to the increase in hydrophobicity of the smart-blocks (Lee et al., 2001a;Shim et al., 2002;Huynh et al., 2011a;Nguyen et al., 2015;Norouzi et al., 2016;Yu et al., 2018;Cirillo et al., 2019). The linkages between micelles in these hydrogels act as additional bond to enhance the hydrogel mechanical properties compared to those that contain single smart-block ( Figure 2B).
The natural hydrophobicity and crystallization of aliphatic polyester smart-blocks have a strong effect on the selfassemblability and amphiphilicity of their copolymers. For example, by increasing the hydrophobicity of original monomers in smart-blocks from PGA to PDO to PLA to PVA, and to PCL, significantly increase in hydrogel strength Yu et al., 2014a;Chen et al., 2016b) and retention time of the hydrogels  or lower critical gel concentration (Jeong et al., 1999a;Chen et al., 2010Chen et al., , 2016aYu et al., 2014a) were observed due the decrease of CMC value. In addition, increasing the crystallization degree of polyester block leads to increasing its hydrophobicity that regulates the micellization of its copolymers at lower concentration and gelation at lower temperatures (Kim et al., 2006b;Gong et al., 2009b;Shi et al., 2016). The hydrophobicity of a combined smart-blocks can be regulated by changing their fraction. For example, increasing the PCL/PLA Petit et al., 2013) and PLA/PGA (Yu et al., 2007) ratio could increase the hydrophobicity of PCLA and PLGA smartblocks, respectively. Higher hydrophobicity blocks tend to form stronger micelle interactions at lower concentrations that lead to the formation of stronger hydrogels or hydrogel formation at lower polymer concentration. Moreover, increasing the length of smart-blocks also lead to the formation of stronger gels or hydrogels at lower polymer concentration (Chen et al., 2010;Shi et al., 2016;Zhang et al., 2017). Controlling the smart-block hydrophobicity is a flexible and useful tool in the design and fabrication of desired hydrogel systems for applications with specific requirements.
Many amphiphilic aliphatic polyester smart-blocks, such as PHB (Barouti et al., 2016;Wu et al., 2016b;Wee et al., 2017), PLA (Wu et al., 2016a), and PCL (Zheng et al., 2017), have been combined with PEG and PPG via urethane coupling to fabricate multiple smart-blocks contain temperatureinduced biodegradable polymer hydrogels with much lower critical gel concentration. Tailoring the hydrophobicity or ratio between smart-blocks could alter the gel region. For example, replacing PLA (Wu et al., 2016a) in (PEG-PPG-PLA) x multiblock copolymer hydrogel by more hydrophobic PBH (Wu et al., 2016b) or PCL (Zheng et al., 2017) blocks led to a significant reduction of critical gelation concentration from ∼10 to 4% (w/w). Increasing the content of hydrophobic block PPG and/or PHB or replacing the PHB with poly(4-hydroxybutyrate), a more hydrophobic block, also decreased the critical gelation concentration (Wee et al., 2017). In addition, several polyester smart-blocks have been grafted into natural polymers, such as HEP (Sim et al., 2015) and gelatin , and proteins, e.g., BSA (Giang Phan et al., 2019), to improve the property of fabricated hydrogels.
Amphiphilic PLAl and PDLAl smart-blocks can be synthesized via ROP of N-carboxyl anhydride L-alanine and D,Lalanine, respectively, using amino terminated molecules, such as PEG-amine Park et al., 2011;. Copolymers of PLAl or PDLAl with PEG, in the form of PEG-PLAl or PEG-PDLAl diblock copolymers, was first introduced in 2008 as peptide-based temperature-induced hydrogels that showed a sol-to-gel phase transition upon increasing temperature . PLAl underwent transitions from random coils to β-sheets that subsequently become packed β-sheets nanofibers as the polymer concentration increased. The preassembled β-sheet secondary structure of PLAl facilitates the sol-to-gel phase transition, occurred in the physiologically range of 20-40 • C, of PEG-PLAl upon increasing temperature due to the further packaging of the β-sheet secondary structure ( Figure 2C). However, when Dalanine stereoisomer was introduced, the β-sheet secondary structure transformation of PDLAl only happened at higher copolymer concentration, and therefore, the PEG-PDLAl could only exhibit the gelation at much higher concentration and temperature (>60 • C). Switching the arrangement of PDLAl and PLAl blocks in a copolymer molecule also leads to differences in gelation behavior. PEG-PDLAL-PLAL contain PLAl-endblock could form hydrogels at lower concentrations and lower sol-to-gel transition temperature compared to PDLAl-endblock PEG-PLAL-PDLAL hydrogel due to the formation of cylindrical bundles as well as spherical micelles of PLAl-endblock whereas only spherical micelles in PDLAl-end-block copolymer .
Hydrophobicity of peptide smart-blocks is an important and effective tool to regulate the gelation behavior and gel region of their copolymer. Replacing a small portion of L-alanine in PEG-PLAl  by more hydrophobic L-phenyl-alanine moiety , to form PEG-PLAF copolymers, could reduce critical gel concentration and sol-to-gel transition temperature. A similar trend can also be achieved by increasing the hydrophobicity from methyl to ethyl in γ-alkyl-substituted PLG in PEG-PLG hydrogels while maintaining the same repeat unit of L-glutamate (Cheng et al., 2012). In addition, increasing the length of PLAl Yeon et al., 2013;Kye et al., 2014;Patel et al., 2015) and PLAF (Kang et al., 2012a;Shinde et al., 2012) and PLG (Cheng et al., 2013a peptide smart-blocks or number of repeat unit in PLG (Cheng et al., 2012) or decreasing PEG molecular weight Kang et al., 2012a;Cheng et al., 2013a;Yeon et al., 2013;Kye et al., 2014;Hong et al., 2017) could reduce the critical gel concentration or sol-to-gel phase transition temperature. Peptide smart-blocks, such as PLAl Moon et al., 2017), PDLAl (Oh et al., 2008;Choi et al., 2010Choi et al., , 2011b, PLAF Kang et al., 2012b) and poly(L-alanineco-L-leucine) (PLAlL) , were also combined with PPG-contained or natural polymers, e.g., chitosan (Kang et al., 2012b), to prolong retention time, improve mechanical properties, biocompatibility, and degradability of the formed hydrogels for potential biomedical applications. Impressively, PEG-polytyrosine (PEG-Tyr6) could form hydrogel at low concentration (∼1.0%) at physiological temperature due to the synergistic capacity of β-sheet conformation and hydrogen bonding of phenolic groups (Huang et al., 2013).
PG with different N-substituted groups was reported to have different responses to temperature change that can be used to fabricate temperature-controlled hydrogels (Xuan et al., 2016). ABC triblock copolymers composed of poly(N-R1 glycine)poly(N-R2 glycine)-poly(N-R3 glycine), where R is a Nsubstituted groups, exhibited the sol-to-gel phase transition with increasing temperature that can be adjusted by controlling the polymer solution concentration and the hydrophobic of Nsubstituted groups. The combination of PL with PLAl, poly(Llysine) (PK) and poly(glutamic acid) (PE) were also reported to exhibit a sol-gel transition in response to temperature for tissue regeneration (Zhang et al., 2014(Zhang et al., , 2015a. Esterified-PE smart-blocks were also reported to respond to temperature change (Cheng et al., 2012(Cheng et al., , 2013aWu et al., 2017;Lv et al., 2018). Changing the block length or γ-substituted group in PE could regulate the gelation of the copolymer hydrogels. For example, increasing the hydrophobicity of γ-substituted groups from methyl or ethyl to n-propyl or butyl significantly decreased the critical gelation temperature (Cheng et al., 2012). In addition, amphiphilic poly(α/β-asparagine) derivatives, synthesized by the reaction of polysuccinimide with a combination of hydrophilic and hydrophobic amines, showed a sharp sol-gel-sol phase transition in an aqueous solution with the ability to alter the gel region via tailoring the side-chain structure of the poly(amino acid)s (Chueh et al., 2007;Takeuchi et al., 2011).

Poly(Organo-Phosphazene) Smart-Blocks
Poly(organo-phosphazene) (POPP) contains only phosphorous and nitrogen in its backbone that is degradable and easily modified with functional groups, e.g., PEG, L-isoleucine ethyl ester (IleOEt), and carboxylic acid (Figure 3), to fabricate temperature-induced hydrogels for biomedical application. In aqueous solution, these copolymers exhibited a sol-to-gel phase transition with increasing temperature with the gel region covers the physiological temperature. In the POPP smart-blocks, IleOEt group offers the temperature-sensitive property while the remaining carboxylic acid side group (Seo et al., 2017) offer the opportunity for further modification, such as conjugating with anticancer drug (Chun et al., 2009a), cell-adhesive peptide (Chun et al., 2009b), folic acid (a cell-specific targeting moiety; Kim and Song, 2014), and cationic molecules Kim et al., 2012Kim et al., , 2013Kim and Song, 2014) to improve the sustained delivery, biocompatibility, and affinity with bioactive molecules.

Aliphatic Polycarbonate-Based Smart-Blocks
Aliphatic polycarbonate-based smart-blocks (Figure 3) have also attracted the attention from scientists due to its ease of preparation, biocompatibility, low degradation rate, and mechanical properties. PEG-PTMC diblock copolymers exhibited a sol-to-gel-to-sol transition in aqueous solution upon increasing temperature due to the amphiphilic property of PTMC mart-blocks . The sol-to-gel transition temperature could be controlled by tailoring concentration, molecular weight, and composition of the polymer. However, PTMC smart-block has difficulty in regulating the gelation of its copolymer. The gelation of PTMC-PEG-PTMC triblock copolymers could only be achieved with high molecular weight PEG and the sol-state at low temperature was not observed (Bat et al., 2008;Park et al., 2008). When PCL, a more hydrophobic block, was added to PTMC, the resulted triblock copolymer exhibited a sol-gel-sol phase transition with increase temperature (Park et al., 2008). Multi-block copolymers fabricated by coupling of PTMC with PPG and PEG [(PEG-PPG-PTMC) x ] via urethane addition reaction exhibited a temperature-induced sol-to-gel phase transition at much lower polymer concentration (<2%) . Copolymerization of poly(polytetrahydrofuran carbonate) (PTHC) with Pluronic F127 (Loh et al., 2014) or PPG and PEG (Chan et al., 2018) [(PEG-PPG-PEG-PTHC) x ] or [(PEG-PPG-PTHC) x ] via urethane reaction were reported for regulating the gel window and hydrogel property with much lower critical gelation concentration.

Poly(N-Isopropyl Acrylamide) Smart-Blocks
PNIPAAm (Figure 3) is a wildly used temperature-sensitive smart-block for hydrogel preparation. However, there is very limited reports of using PNIPAAm for fabricating injectable temperature-induced physically cross-linked hydrogels for biomedical application due to its low critical transition temperature (∼32 • C), which is much lower than physiological temperature. PNIPAAm can be combined with other smartblock to regulate the gelation of their copolymers upon heating due to the trigger of hydrogen bond between amide groups. For example, in aqueous solution, copolymer of PNIPAAm with poly(2-hydroxyl ethyl methacrylate) (PHEMA) and poly(methacrylate-PLA) (pMAPLA) in the form of poly(NIPAAm-co-HEMA-co-MAPLA) existed as a sol at low temperature (<10 • C) and exhibited a sol-to-gel phase transition when temperature was increased to body condition (Ma et al., 2010). However, the gel shrunk after a day. When PNIPAAm was copolymerized with poly(acrylic acid) (PAAc) and poly(trimethylene carbonate) to form poly(NIPAAmco-AAc-co-PTMC), the formed hydrogel was stable both in vitro and in vivo due to the additional crosslinking between PTMC smart-blocks, which enhanced the stability of the formed hydrogel (Fujimoto et al., 2009). Conjugating of PNIPAAm via ATRP of NIPAAm into 2-bromoisobutyryl bromide functionalized un-gellable PCL-PEG-PCL triblock copolymer could trigger the gelation of formed PNIPAAm-PCL-PEG-PCL-PNIPAAm pentablock copolymers (Abandansari et al., 2013). Grafting PNIPAAm into natural polymer is also a potential strategy to fabricate PNIPAAm-based injectable hydrogel. PNIPAAm-grafted chondroitin sulfate underwent a sol-to-gel phase transition with increasing temperature from room temperature to body condition (Lü et al., 2011).

Other Synthetic Smart-Blocks
Many less popular smart-blocks have been reported to trigger the gelation of their copolymers in aqueous solution upon changing temperature for fabricating injectable hydrogels with highly potential for biomedical applications. These smart-blocks include poly(ethylene/butylene) (Nguyen et al., 2011), poly(propylene fumarate) (Chapanian et al., 2009), polyorthoester (Schacht et al., 2006).

SELF-ASSEMBLY SMART-BLOCKS FOR BOTH TEMPERATURE-AND PH-INDUCED HYDROGELS
pH is an important parameter of a living body that may vary between the body fluid, specific organs and disease tissues. Although this work aims to discuss synthetic smart-blocks for temperature-induced gelation, some smart-blocks that are able to trigger a sol-gel phase transition of their copolymers in response to both temperature and pH change for fabrication selfassembled injectable hydrogel are briefly mentioned (Figure 4) (Dayananda et al., 2008;Nguyen et al., 2009;Huynh et al., 2010Huynh et al., , 2011b. Temperature and pH-sensitive smart-blocks are polymers with functional groups that can be ionized and deionized in response to pH change, including sulfonamide groups and amino group, and also show the self-assemblability in response to temperature. These smart-blocks are soluble at acidic or basic pH (e.g., pH < 6.0 or pH > 8.5, respectively) due to the protonation of pH-sensitive moiety and convert to amphiphilic blocks at physiological pH (pH = 7.4) due to the deprotonation (Dayananda et al., 2008;Nguyen et al., 2009;Huynh et al., 2010Huynh et al., , 2011b. Their amphiphilic property can further trigger the gelation of their copolymers upon increasing temperature at physiological pH to form a hydrogel. There are two main categories of pH-sensitive smart-blocks that can trigger the gelation of their copolymer in different direction. Cationic smart-blocks are amino-contained polymers, including non-degradable PAU (Dayananda et al., 2008;Huynh et al., 2010;Manokruang et al., 2014), poly(amino carbonate urethane) (PACU) (Phan et al., 2016a), poly(amido amine) (PAA) (Nguyen et al., 2009;Nguyen and Lee, 2010) and biodegradable PAEU (Huynh et al., 2011b), which are soluble at acidic pH (e.g., pH < 6.0), have amphiphilic property at physiological pH (pH = 7.4) for trigger the gelation upon increasing temperature. For example, cationic PAU smart-blocks, which was synthesized via urethane polyaddition between hydroxyl groups FIGURE 4 | Structure of some smart-blocks for both temperature-and pH-induced self-assemble to fabricate injectable hydrogels.
Frontiers in Chemistry | www.frontiersin.org FIGURE 5 | Schematic showing mechanism of sol-gel phase transition upon changing of temperature and pH of temperature-and pH-induced hydrogels. The copolymer contains both temperature-sensitive and pH-sensitive smart-blocks, e.g., (PCL-PEG-PCL-PAU) x . Copolymer exists as a solution in aqueous solution at low temperatures and acidic pH (A) retains its sol state with solely increasing of temperature (B) or pH (C) but changes to a gel when both temperature and pH are increasing (D). Generated based on the idea from Dayananda et al. (2008). in 1,4-bis(hydroxyethyl) piperazine and isocyanate groups in HDI, is soluble at acidic pH = 6.0 due to the ionization of amino groups. At physiological pH, deionized PAU regulated the sol-to-gel transition of its copolymers, PEG(-PAU) 4  or (PEG-PAU) x -grafted-BSA (Manokruang et al., 2014) or (PCL-PEG-PCL-PAU) x (Dayananda et al., 2008), upon increasing temperature from low (e.g., 5 • C) to body temperature ( Figure 5). In addition, low molecular weight biodegradable PAEU, synthesized using similar urethane polyaddition reaction, could trigger the its sol-to-gel phase transition upon increasing temperature at physiological pH (Huynh et al., 2011b). In opposite manner, poly(sulfamethazine ester urethane) (PSMEU) anionic smart-blocks, which was synthesized via urethane polyaddition, could trigger the gelation of its (PEG-PSMEU) x multiblock copolymers upon the increasing temperature at physiological pH (Le et al., 2018(Le et al., , 2019. These temperature and pH-sensitive smart-blocks can also be combined with other mentioned temperature-sensitive smartblocks to trigger the gelation of their copolymers. For example, copolymers of PAU, PCL and PEG, (PCL-PEG-PCL-PAU) x , exhibited the gelation upon increasing pH and/or temperature with the existence of a gel at the physiological condition (Dayananda et al., 2008). In addition, many other pH-sensitive smart-blocks that could not trigger the sol-to-gel phase transition upon increasing temperature at physiological pH but can be combined with other temperature-sensitive smart-bocks to triggered the gelation of their copolymers upon changing pH or increasing the temperature. Those include oligosulfamethazine (OSM) in OSM-PCLA-PEG-PCLA-OSM pentablock copolymers (Shim et al., 2007), and poly(amino ester) (PAE) in PAE-PCL-PEG-PCL-PAE pentablock (Huynh et al., 2008) or (PAEg-PCL)-PEG-(PAE-g-PCL) triblock copolymers (Zheng et al., 2010). Interestingly, end-capping Pluronic F127 with polyamine could trigger a closed-loop sol-gel-sol phase transition as upon increasing pH and/or temperature . Amphotectic poly(SM amino urethane) (PSMAU) contains both anionic and cationic moiety in its structure that could trigger the gelation of its copolymer, (PCLA-PEG-PCLA-PSMAU) x multiblock copolymers, to form a closed-loop sol-gel-sol phase transition upon increasing pH and/or temperature due to its solubility at either acidic and basic pH (Huynh et al., 2012).

Anticancer Drugs Model Systems
A wide range of bioactive molecules has been used as a model drug for testing the release behavior from hydrogel systems. Among those, anticancer drugs are one of the most interested molecular types because hydrogels can be easily injected into the tumor site or deeper sites in the body, which advances their potential application in cancer therapy. These temperature-induced hydrogels exhibited the sustained release of many anticancer drugs, such as doxorubicin (DOX) (Xun et al., 2009;Huynh et al., 2011b;Manokruang et al., 2014;Guo et al., 2015;Wee et al., 2017;Zhang et al., 2017), paclitacxel (PTX) (Elstad and Fowers, 2009), chlorambucil , honokiol (Gong et al., 2009a,b;Gou et al., 2010), and leuprorelin acetate (Rao et al., 2018) with multiple options to adjust the release behavior. The release of the loaded anticancer drugs can be regulated via controlling the property of smart-blocks in the hydrogels. For example, in vitro experiments showed that DOX was released from PCLA-PEG-PCLA hydrogels in the course of 2 weeks while further  attachment of KRGDKK (Lys-Arg-Gly-Asp-Lys-Lys) peptide at both end of copolymer could increase the sustained release up to 5 weeks (Xun et al., 2009). However, DOX was released in from PLA-PEG-PLA hydrogels in only 1 week (Guo et al., 2015) due to the faster degradation of PLA compared to PCLA. Introducing stimuli-triggered degradation groups into the middle of smart-blocks offers the ability of using stimuli to control the degradation of hydrogels and subsequently the release of loaded bioactive molecules (Zhang et al., 2017). For example, introducing a diselenide linkage at the middle of PCL block in PEG-PCL-PEG copolymers could offer reducing-agentregulated release of loaded DOX with faster DOX release rate due to hydrogel degradation in the presence of a reducing agent (Zhang et al., 2017). PEG-PCL-PEG hydrogels were also reported to control the release of honokiol over the course of 2-3 weeks (Gong et al., 2009a,b;Gou et al., 2010). Increasing the hydrophobicity of smart-blocks not only triggered the gelation at lower polymer concentrations, but also offered more sustained released of loaded anticancer drugs Wee et al., 2017). The hydrogels contain smart-blocks that response to both temperature and pH also exhibited sustained release of DOX (Huynh et al., , 2011bManokruang et al., 2014).

Proteins in Model Systems
Therapeutic and model proteins, such as insulin (Qiao et al., 2007), human growth hormone (hGH) Huynh et al., 2012;Shinde et al., 2012Shinde et al., , 2015Phan et al., 2016a) and bovine serum albumin (BSA) (Jeong et al., 1997;Hyun et al., 2007;Moon et al., 2011) are among the molecules served as model drugs for testing the controlled release ability of hydrogel systems. Peptide-based smart-block hydrogels have showed potential in control the release of hGH with sustained release for 1-2 weeks in vitro and 4 days in a rat model from PEG-PLAF hydrogels (Shinde et al., 2012. The improvement in sustained release of hGH was not observed in cationic smart-block contained hydrogels, such as (PEG-PACU)x (Phan et al., 2016a), (PCLA-PEG-PCLA-PSMAU) x (Huynh et al., 2012), protamine-modified POPP . Short release courses of hGH from all these hydrogels was attributed to its naturally hydrophilicity. In addition, hydrogels with faster degradation rate offered shorter controlled release course while hydrogels contained peptide block could offer more sustained protein release due to the addition of hydrogen bonds between protein and peptide segments in the hydrogels. For example, BSA was released from PEG-PLLA hydrogel in 10 day (Jeong et al., 1997) while it was sustained for 3 and 4 weeks from PEG-PCL (Hyun et al., 2007) and PLAlL-PPG-PEG-PPG-PLAlL  hydrogels, respectively.

Controlled Release of Bioactive Molecules for Therapeutics
Cancer Therapeutics There are enormous number of studies that reported the used of smart-block based temperature-induced self-assembled hydrogels for delivery of anticancer drugs and other bioactive molecules for controlling the tumor growth or clearance tumor in animal models (Table 1). Many designed systems with tunable release behavior and high bioactive efficacy have been developed. PPG-based hydrogels exhibited the sustained release of DOX (Khaliq et al., 2017;Liow et al., 2017;Chan et al., 2018) and PTX (Wu et al., 2016a,b;Zheng et al., 2017) for suppression tumor growth from 1 to 4 weeks. The release of anticancer drugs and resultant tumor suppressing ability could be controlled via changing the designed structure of polymer hydrogels. For example, PTX-loaded (PEG-PPG-PHB) x hydrogels (Wu et al., 2016b) could suppress the tumor growth for 4 weeks while PTX-loaded (PEG-PPG-PLA) x hydrogels (Wu et al., 2016a) were reported to show the control tumor growth in 1 week due to the faster degradation of PLA smart-blocks. Many aliphatic polyester smart-blocks hydrogels have been used for delivery of anticancer drugs and other bioactive molecules to control tumor growth in animal models (Zentner et al., 2001;Samlowski et al., 2006;Bagley et al., 2007;Matthes et al., 2007;Yu et al., 2008;Chang et al., 2011;Gao et al., 2011;Ci et al., 2014;Ma et al., 2014Ma et al., , 2015Phan et al., 2016b) and even in human patients (Vukelja et al., 2007). Among these, PLGA-based hydrogels are the most popular for cancer therapy. PCLA-PEG-PCLA hydrogels were reported to deliver anticancer drugs, such as gemcitabine (GEM) (Phan et al., 2016b), irinotecan (IRN) (Ci et al., 2014), camptothecin (CPT) Chang et al., 2011), docetaxel (DTX) (Gao et al., 2011), cisplatin (CDDP) and methotraxate (MTX) (Ma et al., 2015), DOX (Ma et al., 2014(Ma et al., , 2015, and PTX (Zentner et al., 2001;Bagley et al., 2007;Matthes et al., 2007;Vukelja et al., 2007), immunotherapy agent, e.g., interleukin-2 (IL-2) (Samlowski et al., 2006), and RNA molecule, e.g., polo-like kinase 1 shRNA (PLK1-shRNA) (Ma et al., 2014) for controlling tumor growth ( Table 1). For example, GEM was sustained release from montmorillonite-functionalized PCLA-PEG-PCLA hydrogels for more than 1 week in vitro and could suppressed tumor growth in pancreatic tumor-bearing mice for more than 6 weeks (Phan et al., 2016b). Co-delivery of DOX, CDDP, and MTX from PCLA-PEG-PCLA hydrogels could increase efficacy in suppressing tumor growth in tumorbearing nude mice compared to groups treated with single or dual drugs (Figure 6) (Ma et al., 2015). Co-delivery of PLK1-shRNA and DOX was also reported to provide the synergistic effect in treatment of cancer in nude mice due to the antitumor effect of DOX and ability of PLK1-shRNA to silence PLK1 expression for higher apoptosis effect (Ma et al., 2014). Other PLGA-based hydrogel, e.g., PLGA(-PEG) 4 , PEG-PLGA , and aliphatic ester smart-block based hydrogels, e.g., PEG-PCL Kang et al., 2011) and PCL-PEG-PCL (Peng C. L. et al., 2013) also showed promise in control the release of anticancer drugs for suppressing tumor growth. Importantly, encapsulation of therapeutic radionuclide ( 188 Re-Tin colloid) into PCL-PEG-PCL (Peng C. L. et al., 2013) could inhibit the tumor growth for 32 days. The antitumor effect was significantly enhanced when DOX and 188 Re-Tin colloid were co-delivered, which showed the tumor disappear in 75% animal after 31 days treatment (Peng C. L. et al., 2013). Figure 7 is reproduced from ref (Peng C. L. et al., 2013) showing a schematic represent a copolymer solution loaded with Lipo-DOX and 188 Re-Tin colloid at 4 • C in a syringe that forms a gel at 37 • C or after being injected to the tumor site for control tumor growth.
Peptide smart-block hydrogels exhibited excellent ability in controlling the release of bioactive molecules, including anticancer drugs (Cheng et al., 2013a;Wei et al., 2017;Wu et al., 2017;Lv et al., 2018), and immunotherapy agent Lv et al., 2018) for subduing tumor growth in animal models. PTX loaded PLG-PEG-PLG hydrogels could sustained the release of PTX and efficiently suppressed the tumor growth in BALB/c nude mice for up to 21 days (Cheng et al., 2013a). Co-delivery of anticancer drugs and immunotherapy agents from peptidebased hydrogels was reported to provide synergistic effect in subduing tumor growth that has significantly higher efficacy compared to the delivery of single molecule Wu et al., 2017;Lv et al., 2018). For example, co-delivery of DOX and combretastatin A4 (CA4) from PEG-PLAF hydrogels could inhibit the tumor growth in BALB/c mouse for up to 28 days with much smaller tumor volume compared to single molecule treatment . FIGURE 6 | Schematic illustration the localized, sustained co-delivery of multiple anticancer drugs (DOX, CDDP, and MTX) from injectable hydrogels for obtaining the synergistic tumor suppression. Reproduced from Ma et al. (2015) with permission from American Chemical Society.

FIGURE 7 | Schematic represents a PCL-PEG-PCL solution loaded with
Lipo-DOX and 188 Re-Tin colloid at 4 • C before injecting and a formed hydrogel at 37 • C or after being injected to the tumor site for control tumor growth. Reproduced from (Peng C. L. et al., 2013) with permission from American Chemical Society.
POPP possess abundant pendent functional groups that can be easily modified to improve the retention of loaded bioactive molecules. POPP modified with protamine  or PEI (Kim et al., 2012;Kim and Song, 2014) could provide the sustained delivery of siRNA against vascular endothelial growth factor (siVEGF) Kim and Song, 2014) or siRNA against cyclin B1(siCyclin B1) (Kim et al., 2012) for suppressing the tumor growth in mice. For example, siVEGF loaded in protamine-conjugated POPP was sustained released and limited the growth of tumor for 4 weeks . PEI-conjugated POPP can form cationic interaction with RNA to provide the sustained presentation of siRNA at tumor site (Figure 8) to enhance the long-term RNAimediated tumor inhibition via target gene silencing (Kim et al., 2012). When protamine was replaced by PEI and folic acid, a cancer cell targeted molecule, the siVEGF loaded hydrogels could completely inhibited the tumor growth Balb/c nude mice for 30 days (Kim and Song, 2014). In addition, POPP was also able to sustain the delivery of chemically conjugated PTX that suppressed tumor growth for more than 30 days (Chun et al., 2009a).

Diabetic Treatment
Smart-block hydrogels have been widely used for delivery bioactive molecules, such as insulin Choi and Kim, 2003;Qiao et al., 2007;Huynh et al., 2008Huynh et al., , 2009, liraglutide (Lira) (Chen et al., 2016a,b), exenatide (EXT) Yu et al., 2013), and incretin hormone glucagon-like peptide-1 (GLP-1) (Choi et al., 2004), to control glucose level in diabetic animal models. PLGA-PEG-PLGA hydrogels were reported to provide the sustained delivery of insulin over the course of 2 weeks in vitro and 10-15 days in rat models Choi and Kim, 2003;Qiao et al., 2007). Peptide-based smart-block hydrogels (PEG-PLAF) offered longer insulin sustained release with 18 days in vitro, and an injection of insulin-loaded hydrogel could reduce glucose level in diabetic mice for 18 days . However, glucose level in treatment group was higher than that in normal mice from day 4. Adding cationic moiety to the hydrogel could prolong the sustained release of insulin both in vitro and in vivo. Insulin was released from PAE-PCL-PEG-PCL-PAE hydrogels in 30 days in vitro and ∼20 days in vivo that maintained low blood glucose in diabetic rats for more than 12 days (Huynh et al., 2008(Huynh et al., , 2009. PLGA-PEG-PLGA hydrogels also sustained the in vitro release of EXT for 1 week and the subcutaneous injected EXT-loaded hydrogels could maintain blood glucose level of type-II diabetic db/db and ICR mice in the normal range for up to 7 days Yu et al., 2013). Lira, an antidiabetic polypeptide, was sustained released from PLGA-PEG-PLGA hydrogels for more than 10 days (Chen et al., 2016a,b). A single injection of Lira-loaded hydrogels in diabetic db/db mice showed hypoglycemic efficacy for up to 1 week. In addition, the sustained FIGURE 8 | (A) Schematic showing the concept of PEI-conjugated POPP injectable hydrogel for localized and long-term delivery of siRNA. By simply mixing (1), the polyplexes (2) form by ionic interactions between conjugated PEI and siRNAs, and their aqueous solution transforms to a gel (3) after being injected into tumor site for sustained siRNA delivery (4) and long-term RNAi therapy via target gene silencing. (B) In vivo sustained siRNA retention of fluorescent cy5.5-tagged si(Cyclin B1) at tumor site after injection of siRNA-loaded hydrogel. Reproduced from Kim et al. (2012) with permission from American Chemical Society.
release of GLP-1 from PLGA-PEG-PLGA hydrogels more than 10 days after single subcutaneous injection in to diabetic rats that led to stimulation of insulin secretion to improve glucose tolerance for more than 1 week (Choi et al., 2004).

Chronic Pain Relief
PLGA-PEG-PLGA hydrogels also showed great potential in locally sustained drug delivery for chronic pain control (Petit et al., 2014(Petit et al., , 2015Tellegen et al., 2018). Celecoxib was sustained released from the hydrogels for more than 3 months in vitro and more than 8 weeks in knee joints of healthy Wistar rats without cytotoxicity after a single injection of celecoxibloaded hydrogels (Petit et al., 2014). Locally sustained release of celecoxib for 4 weeks was also observed with a single injection of celecoxib-loaded hydrogels into the right middle carpal joint healthy horses (Petit et al., 2015). The formulation was also reported as a safe and effective approach to control back pain in dog with significantly pain reduction for up to 6 months (Tellegen et al., 2018).

Other Therapeutics
VEGF-conjugated PVL-PEG-PVL hydrogels showed potential for myocardial and functional recovery stabilizing myocardial infarct and inducing angiogenesis in myocardial infarction SD rats (Wu et al., 2011). PCLA-PEG-PCLA grafted BSA hydrogels provide the sustained release of polyplex-pDNA for more than 10 days in mice. The release polyplex-pDNA activated a robust antigen-specific immune response, which might be potential for the formulation of vaccine against Alzheimer's disease (Giang Phan et al., 2019).

Bone Regeneration
Although injectable self-assembled hydrogels possess low mechanical property that may limits their potential application in bone regeneration, some hydrogel systems have been reported to deliver bioactive molecules and/or cells to enhance the regeneration of bone ( Table 2). For example, PEG-PCL and RGD-conjugated POPP hydrogels were reported as injectable scaffolds for delivery of rat bone marrow stromal cells (rBMSCs) and DEX (Kim et al., 2006a), and rabbit MSCs (Chun et al., 2009b) to enhance the ectopic bone formation. Delivery of simvastatin (SIM) from PCLA-PEG-PCLA hydrogels to femur bone defects of Wistar rats were reported to significant enhance bone formation (Yan et al., 2015). PCLA-PEG-PCLA hydrogels could also sustain the delivery of bone morphogenetic protein 2 (BMP-2) in SD rats for 9 days (Santovena et al., 2017). Loading bare polystyrene microspheres (MSs) or MSs functionalized with phosphate or carboxylate group into PEG-PLAL hydrogels could guide the osteogenesis of co-encapsulated tonsil-tissue-derived mesenchymal stem cells (TMSCs) (Kye et al., 2014). Importantly, POPP modified with -COOH side-groups were reported to provide the sustained release of BMP-2 for 1-3 months. Injection BMP-2-loaded POPP hydrogels with/with-out biphasic calcium phosphate ceramic (BCP) submicron particles into 5 mm critical-sized bone defects in C57BL/6 mice could significantly enhance the healing rate (Seo et al., 2017).

Cartilage Regeneration
Temperature-induced self-assembled hydrogels have showed their potential in cartilage regeneration by supporting the 3D culture of chondrocytes (CHONs) or enhancing the chrondrogenesis of encapsulated MSCs ( Table 2). BMSCs encapsulated in PLGA-PEG-PLGA hydrogels underwent the chondrogenic differentiation in vitro, demonstrated by upregulating expression of chondrogenic markers and increasing glycosaminoglycan (GAG) content (Wang S. J. et al., 2016). PEG-PLGA hydrogels were also reported as platforms for CHON 3D culture with high cell viability and strong chondrogenic activity  or supporting chondrogenesis of encapsulated synovial fluid mesenchymal stem cells (SFMSCs) (Chiang et al., 2014). PEG-PLGA hydrogels encapsulated with SFMSCs and platelet-rich plasma (PRP) could induce the chondrogenesis of SFMSCs and increase cell growth and maturation of CHONs to significantly enhance the cartilage focal defects in pig model (Chiang et al., 2014).
Peptide smart-block based hydrogels were reported as good candidates for cartilage regeneration. TMSCs were reported to preferentially undergo chondrogenesis with high expressions of type II collagen and sulfated glycosaminoglycan when being encapsulated in PEG-PLAF hydrogels and cultured in induction media supplemented with adipogenic, osteogenic, or chondrogenic factors . PEG-PLAl hydrogels exhibited the capability to regulate the chondrogenesis of encapsulated adipose-tissue-derived stem cells (ADSCs) (Yeon et al., 2013), BMSCs , and TMSCs (Kye et al., 2014). Subcutaneous injection PEG-PLAl aqueous solution loaded with BMSCs  or ADSCs (Yeon et al., 2013) in mice led to the chondrogenesis of encapsulated cells with excellent expressions of early chondrogenic biomarkers. PDLAl-PPG-PEG-PPG-PDLAl (Choi et al., , 2011b and poly(α/β-asparagine)-based (Chueh et al., 2007) hydrogels can also be used as platforms for CHON 3D culture in vitro with high cell viability and strong chondrogenic activity. PG-based ABC triblock copolymer hydrogels could induce chondrogenesis of encapsulated human ADSCs demonstrated by upregulating the expressing of chondrogenic marker (Xuan et al., 2016).

Neuron Regeneration
Peptide smart-block based hydrogels possess same stiffness with brain tissue that have been injected into mouse forebrain with minimal detectable toxicity in the central nervous system (CNS) and good integration with brain tissue . The PL-based hydrogels served as depots for localized and sustained release of bioactive nerve growth factor (NGF) in the CNS that maintained hypertrophy of local forebrain cholinergic neurons for at least 4 weeks . The hydrogels were also reported to deliver hydrophobic molecules that alter gene expression of CNS cells in a locally restricted area in the forebrain (Zhang et al., 2014), or to deliver neural stem cells (NSCs) into an injured CNS (Zhang et al., 2015b). Delivered NSC distributed in non-neural lesion cores and integrated with surrounding healthy neural cells to supported regenerate the host nerve fibers (Zhang et al., 2015b). PEG-PLAL hydrogels encapsulated with NGF and brain derived neurotropic growth factor (BDNF) loaded alginate MSs could sustained the release growth factors from 12 to 18 days (Patel et al., 2015). Cultured TMSCs in growth factors loaded hydrogels exhibited shape change from spherical shape to multipolar elongation with significantly higher expressions of the neuronal biomarkers. A summary is presented in Table 2.

Liver Regeneration
Peptide smart-block based hydrogels showed their potential in liver regeneration due to their similar stiffness compared to liver tissue ( Table 2). Encapsulation of hepatogenic growth factors (HGF) alone  or in combination with tauroursodeoxycholic acid (TUDCA) and fibroblast growth factor 4 (FGF-4) (Hong et al., 2017) could provide the sustain delivery of growth factors for guiding the hepatogenic differentiation of co-encapsulated TMSCs, demonstrated by expression of hepatogenic biomarker and hepatocyte-specific biofunctions. Conjugation of lactobionic acid (LB) to PLAl-PPG-PEG-PPG hydrogels could also improve the hepatogenic differentiation of the encapsulated TMSCs (Moon et al., 2017).

Wound Healing and Scar Prevention
Hydrogels are good platforms to deliver bioactive molecules and/or cells to improve the wound healing rate ( Table 2). PEG-PLAl hydrogels have been reported for encapsulation of fibroblasts to improve the wound healing on incisions of rat skin with significantly better wound closure and skin tissue regeneration compared to groups treated with cell-free gels or PBS (Yun et al., 2012). Release of polyplex-DNA loaded in the (PEG-PSMEU) x hydrogels accelerated the wound healing process in mice, demonstrated by effectively sealing the ruptured skin, absorbing wound exudates, and promoting the tissue regeneration in the wounded area (Le et al., 2018). Bare PCLA-PEG-PCLA-grafted gelatin hydrogels could not only adhere on skin tissues and effectively sealed the wounds, accelerated cutaneous wound healing, and promoted tissue regeneration in the wound area .
Preventing scar and post-operative abdominal adhesions is very important in medical operation. Cyclosporine A (CsA), an anti-fibrotic drug to inhibit post-operative scarring, was sustained release from PLGA-PEG-PLGA hydrogels for over 2 months in vitro. The sustained delivery of CsA from hydrogels inhibited post-surgical scar formation and promoted bleb survival in rabbits after glaucoma filtration surgery (Figure 9) (Sun et al., 2017). PLGA-PEG-PLGA hydrogels also sustained the release of 5-fluorouracil (5-Fu) to prevent post-operative abdominal adhesions in sutured Achilles tendon model of rats (Yuan et al., 2015). Bare hydrogels based on PLGA, PCLA and PLA were also reported to reduce the post-operative abdominal adhesions in animal models (Zhang et al., 2011;Yu et al., 2014a;Shi et al., 2016;Lei et al., 2017;.

CONCLUSION AND FUTURE OUTLOOK OF SELF-ASSEMBLY SMART-BLOCK BASED TEMPERATURE-INDUCED INJECTABLE HYDROGELS
A summary in development of self-assembly smart-block for fabrication of temperature-induced injectable physically crosslinked hydrogels and their potential biomedical applications have been conducted. The development and achievement in biomedical applications of these smart-block based hydrogels have showed remarkable progress in over the last 20 years. These injectable hydrogels offer many advantages such as cytocompatibility, non-invasive administration, tunable mechanical properties, highly permeability, controllable degradability, injectability, and capacity to deliver bioactive molecules and/or cells for a wide range of biomedical applications. These hydrogel systems have confirmed their potential application as drug delivery systems, cancer and disease therapeutics, and delivery of bioactive molecules and cells for tissue regeneration.
Although these self-assembled injectable hydrogels have offered many advantages and potential, several important challenges still remain and need to be carefully considered in designing the future approaches. The challenges include: • First, the majority of biodegradable hydrogels are ester based polymers with carboxylic acid bearing degraded byproducts, which might cause a decreasing of local pH and/or inflammation to the surrounding tissues, and damage of loaded bioactive molecules. • Second, the hydrogel degradation rate is an important factor to control the release of therapeutic molecules; therefore, the balance between hydrogel bulk degradation and surface degradation should be considered for sustaining the delivery of these molecules. • Third, controlling the initial burst release of loaded bioactive molecules, especially for proteins, growth factors and RNA molecules, from these delivery systems is crucial as it may reduce the serving period of these carrier systems. Loading bioactive molecules into nanoparticles (NPs) or MSs followed by encapsulation of these NPs/MSs in the hydrogels (Giang Phan et al., 2019) or directly tethering them to the network  for prolong the sustained delivery should be put in mind. • Fourth, several reports have proved that the combination of multiple drugs and/or molecules can enhance effects in disease or cancer therapeutics (Peng C. L. et al., 2013;Ma et al., 2014;Wei et al., 2017;Lv et al., 2018); therefore, this direction should be further investigated to maximize their synergistic therapeutic effect with minimal side effects. • Fifth, the difference between animal models and human patients is the most difficult challenge that cause a huge delay in potential clinicalization and commercializing of developed approach that may have significantly impact in improving human health.
In summary, clearly understanding the polymer structureproperty relationship should allow designing of self-assembly smart-blocks and their hydrogel systems with desired performance. Important properties of smart-blocks include assembability, degradability, property of their degraded byproducts, mechanical property of their formed hydrogels, gelation time, interaction between smart-blocks with bioactive molecules (proteins, DNAs, RNAs), and ability to covalently conjugate bioactive molecules to the network. In addition, the nature property and availability of bioactive molecules, and the availability of cell sources and developed technologies are among important factors to achieve an ideal hydrogel system.
Furthermore, pre-clinical pilot animal studies need to be moving forward for developing clinical trial approaches to further enhance human health.

AUTHOR CONTRIBUTIONS
TH, LS, DN, DH, and CH summarized the information and prepared the manuscript. CH supervised the whole process.