Abstract
The phase equilibria at 340°C of the Al – Ni – Zn system were investigated by combining the diffusion couple technique with the equilibrated alloys method. The samples were examined by means of optical microscopy, X-ray diffraction, scanning electron microscopy, and electron probe microanalysis. Two ternary compounds (1 and 2) were found to exist at 340°C. The solubilities of Zn in AlNi, Al3Ni2 and Al3Ni were determined to be about 20, 2 and 1 at.% Zn, respectively. The solubilities of Al in β1-NiZn and in were measured to be about 11.5 and 1 at.% Al, respectively. The solubilities of Zn in both AlNi3 and Al3Ni5 are below 1 at.% Zn.
References
[1] A.R.Marder: Progr. Mater. Sci.45 (2000) 191.10.1016/S0079-6425(98)00006-1Search in Google Scholar
[2] P.R.Sere, M.Zapponi, C.I.Elsner, A.R.Di Sarli: Corros. Sci.40 (1998) 1711.Search in Google Scholar
[3] S.M.A.Shibli, R.Manu: Surf. Coat. Technol.197 (2005) 103.Search in Google Scholar
[4] N.Dupin, I.Ansara, B.Sundman: Calphad25 (2001) 279.Search in Google Scholar
[5] X.P.Su, N.Y.Tang, J.M.Toguri: J. Phase Equilib.23 (2002) 140.Search in Google Scholar
[6] S.L.Chen, Y.A.Chang: Calphad17 (1993) 113.Search in Google Scholar
[7] S.Bhan, A.Lal, in: G.Effenberg (Ed.), “Aluminium–Nickel–Zinc”, MSIT Ternary Evaluation Program, in MSIT Workplace, MSI, Materials Science International Services GmbH, Stuttgart; Document ID: 10.16203.1.20 (1993).Search in Google Scholar
[8] V.Fuss: Z. Metallkd.16 (1924) 24.10.2307/3753457Search in Google Scholar
[9] A.Mayer: Gazz. Chim. Ital.77 (1947) 326.Search in Google Scholar
[10] G.V.Raynor, C.R.Faulkner, J.D.Noden, A.R.Harding: Acta Metall.1 (1953) 637.Search in Google Scholar
[11] V.R.Friebel, W.J.Lantz, W.P.Roe: Trans Met Soc AIME56 (1963) 90.Search in Google Scholar
[12] Y.Kuriki, S.O.Ochiai, M.Yodogawa, T.Suzuki: J. Jpn. Inst. Met.26 (1985) 213.Search in Google Scholar
[13] N.N.Kiseleva: Izv. Akad. Nauk SSSR, Metally (2) (1987) 213.Search in Google Scholar
[14] H.H.Xu, Y.Du, C.Y.Tang, Y.H.He, Z.H.Yuan, B.Y.Huang, S.T.Li: Mater. Sci. Eng. A412 (2005) 336.Search in Google Scholar
[15] H.H.Xu, Y.Du, Y.H.Tan, Y.H.He, S.T.Li, X.Zhang: J. Alloys Compd.425 (2006) 153.Search in Google Scholar
© 2008, Carl Hanser Verlag, München