2000 Volume 12 Issue 3 Pages 343-344
Top data of magnetostrictive susceptibility was obtained at Fe-45at%Pd film. The reversible relationship was obtained between shape change and applied magnetic field from earth magnetic field to 0.2 kOe. The high magnetostrictive susceptibility at room temperature was higher than that of Tb0.3Dy0.7Fe2 thin film developed.