Effect of Placement Techniques on Sealant Efficacy

C l i n M e d International Library Citation: Juntavee A, Juntavee N, Paleekoup J, Millstein P, Abedian B (2015) Effect of Placement Techniques on Sealant Efficacy. Int J Oral Dent Health 1:006 Received: March 10, 2015: Accepted: April 09, 2015: Published: April 11, 2015 Copyright: © 2015 Juntavee A. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited. Juntavee et al. Int J Oral Dent Health 2015, 1:2 ISSN: 2469-5734


Introduction
Fissure sealants are one of the effective preventive tools in reducing incidence of caries for children and adolescents [1][2][3][4][5][6] and their applications in the U.S. alone cover significant portion of the population across all age groups and all income levels [7].An ineffective marginal seal between the resin and the enamel is one of the most important factors causing sealant failure [8].To increase sealant success rate, most recent attempts have focused on the chemical treatments such as acid etching in the preparation step before applying the sealant [9][10][11].
Efficacy of sealants also strongly depends on their mechanical penetration and filling into occlusal areas [12].Surface depressions have restricted access: hard to clean making them more susceptible to caries, and hard to reach when applying the sealant.In an ideal application, the low-viscosity resin sealant fills all irregular occlusal areas.But penetrating deep into an occlusal area also give rise to a stronger physical bond between the sealant and the substrate which may reduce secondary caries [13], and providing longer lasting and more successful applications.Accordingly, a better marginal adaptation and deeper occlusal penetration will be key in improving the rate of success of this operation.
In present clinical practice, many sealants are often injected with a syringe onto the occlusal surfaces of teeth.For better adaptation, they are then shaped and spread around with a commercial applicator; however, upon withdrawing, the applicator leaves excess sealant which is light cured.Evidence of placement difficulty with a commercial applicator for other dental sealants has been shown previously [14].This study introduces a method of delivery that uses an oscillating applicator that momentarily thins the sealant so that it will flow more readily without sticking to the applicator.The excess sealant in the treated tooth depends on the technique by which the sealant is applied.
It's been shown that asymmetric rotating burs can provide superior marginal adaptation [15].The purpose of this study is to show that better marginal adaptations with the application of such burs ultimately can reduce microleakage, resulting in more successful sealant application.The effect of a vibrating tool to control microleakage and sealant penetration using a microvibe vibrating probe has been studied previously and no significant difference was detected [16].No physical reason was provided on how such microprobes are ineffective and no indication if such tools have better spreading ability.However, the burs that we have designed and used in this study may spread, deform and manipulate the sealant much more effectively than a conventional applicator (Figure 1) and could be more effective in dental sealant placement.
When an asymmetric rotating bur 1-3 mm in size (flow-bur) with a moderate rotational speed (100<ω<1000 rpm, with ω the rotational speed) is used to deform an adhesive material, the bur will not stick

Abstract
This in-vitro study evaluated and compared two techniques for placement of dental sealants.It is shown that sealant bondage to occlusal areas, a key factor in success and effectiveness of dental sealants, can be greatly influenced by the placement technique used in such operations.Custom-made flow-burs (Abedian and Millstein, J. Oper.Dent.2006) of different dimensions were designed, constructed and compared to a conventional applicator for sealant efficacy.A moisture-tolerant resin-based sealant was applied to occlusal surfaces of caries-free upper and lower premolars extracted teeth, and manipulated by using a conventional applicator or flow-bur.Microleakage and depth of penetration studies on sealant integrity were conducted after subjecting the treated samples to thermocycling.Image processing was conducted on the sectioned teeth for all cases and SPSS statistical analysis of the data indicated that use of flow-burs in placing dental sealants can reduce microleakage by 50% as well as 66% reduction of unfilled voids.With advantages in consistency, convenience and better marginal adaptation, the use of such flow-burs may reduce occurrence of caries after the sealant application and ultimately improve sealant clinical success.
• Page 2 of 5 • ISSN: 2469-5734 to the material as opposed to a conventional plugger [14].At such moderate speeds, the rotating bur will induce surface oscillations at high enough frequencies such that the interfacial interactions between the surface of the adhesive and the rotating bur will be minimal due to Deborah-number effects.Accordingly, the sealant may not stick to or wet the bur, as the bur deforms the sealant.The shortest times are often a Deborah number of unity, which brings about the low end of the working speeds of our flow-burs.If a non-oscillating conventional applicator is used to deform the adhesive, the material will stick to this plugger and any motion by the plugger will not result in better marginal adaptation.Induced oscillations of the dental adhesives have another beneficial effect as such materials exhibit pseudo-plastic behavior.With the application of rotating bur to deform the sealant, the sealant possesses less viscosity and might more completely wet occlusal surfaces with better adaptation of the interior surfaces.
Microleakage studies are a standard method for sealant efficacy [16][17][18][19], either in vivo or in vitro.In in vitro studies, it is possible to assess marginal leakage and overall sealant capacity to predict how such sealant operations are successful and how long they might last.Many factors influences microleakage between enamel surface and the sealant including anatomical constrictions, aprismatic enamel structure, enamel surface preparation, moisture contamination, errors in applying the sealant and temperature effects.In this study, we conducted microleakage and penetration investigation for two placement techniques with all other factors that influence adhesion and penetration remaining unchanged.
We hypothesize that using a flow bur when applying the sealant, by a dental operator who is familiar and comfortable with this technique, has several important advantages, compared to using a conventional dental applicator:

Improved penetration into occlusal areas
The present study examines the effectiveness of two techniques in applying a dental sealant on how it adapt and seal to the occlusal surfaces.To evaluate some of these advantages, we utilize a comparative microleakage and depth of penetration study for two application procedures one with a conventional applicator and the other with a set of flow-burs that is designed and constructed to conduct these tests.

Materials and Methods
Custom-made Flow-burs for this comparative study were constructed in-house by modifying the tip of commercial round cutting burs.The burs were initially sand blasted to ensure better retention of the composite at the tip.Light-cured flowable composite dental material (Esthet-Xflow) was applied on the sand blasted tip and then shaped manually by hand such that it forms asymmetrical bi-paddle-type geometry without any sharp corners, as used in previous studies [14,15].Once the desired shape was achieved, the tip material was light cured to harden with better grip on the remainder of the bur.The burs were then tested on their spreading ability of a dental adhesive on a PVC flat surface to confirm their functionality.Different size custom-made burs with maximum diagonal dimension of 1-3 mm were constructed.A flow-bur used in this study shown in Figure 2. If one follows this recipe, such burs could be made in a wellequipped dentist office.

Sample preparation
Eighty caries free upper and lower premolars, extracted for orthodontics reasons, were selected.In the post-extraction stage, the teeth were stored in 0.1% thymol solution in a dark container at room temperature.For the experiments, each specimen was embedded in a stone model and randomly divided into two groups of forty teeth each.Each group was further divided into two subgroups of twenty teeth per group.Subgroups 1and 3 were assigned to be sealed with the oscillating flow-bur application technique; subgroups 2 and 4 were assigned to be sealed using the conventional applicator.In all the experiments, the rotational speed of the handpiece was set to approximately 300 rpm.
Occlusal surfaces of the samples were thoroughly cleaned for 20 seconds with a pumice slurry in a low speed micro-motor handpiece.The surfaces were then rinsed with air-water for 10 seconds and dried.The dried teeth were subsequently etched for 15 seconds with a phosphoric etchant (Etch-Rite TM , Pulpdent), and rinsed for 10 seconds.The teeth to be sealed were air dried but not desiccated.Forty teeth (Gr1, Gr3) were sealed by the constructed flow-bur with Embrace TM Wetbond TM (Pulpdent, Watertown, MA) with an oscillating bur application technique while two groups of control (Gr2, Gr4) were sealed by using the conventional supplied cannula tip.Teeth were cured with UV light (3M™ ESPE™ Elipar™ 2500 Halogen Curing Light) for 20 second.

Processing of the samples
The teeth with sealant treatments were stored in distilled water at 37 °C for 24 hours.Subsequently, the samples were subjected to a thermocycling (SPC20, Yamatake Honeywell, HW B 332R) regimen All samples in Groups 1 and 2 were covered with sticky wax and the surface of each sample was covered with two layers of nail varnish leaving a 1-mm window around the margin of the sealant and immersed in a dye solution (methylene blue 0.5%; Merck4279, Darmstadt, Germany) for 4 hours at 37 °C.Following immersion in the dye solution, the teeth were subsequently rinsed under running tap water for 30s.All samples from Groups 1-4 were fixed and sectioned longitudinally in a bucco-lingual direction with a slow speed rotating diamond blade (Model 1000 TM ISOMET, Illinois, USA), providing two 1 mm-sections per tooth, shown in Figure 3a,3b.
The two sides of each sectioned sample were inspected by polarized light and subjected to image analysis software (Image J: NIH) (50× magnification) to measure microleakage and penetration data.Measurements, analysis, and recording were performed by the same evaluator.After calibration to a millimeter ruler, the microleakage was evaluated quantitatively by measuring the length of dye-penetration.For each tooth-section sample that was considered, the fraction of microleakage microleakage , with sa and ua the areas of the sealant and unfilled void, respectively, as shown in Figure 4B.
During a month period, a random portion of all sectioned samples were re-examined (10% of the sections).The intra-examiner reliability values of microleakage and unfilled area proportions using Cohen's kappa coefficient were 0.85 and 0.87 respectively.With SPSS Statistical Analysis, the data were primarily explored to assess the distribution.The Levene's test and a Mann-Whitney U test were used for the comparison.The level of significance was set at P<0.05.

Discussions
Sealants have gained wide acceptance by pediatric clinicians as an effective preventive method to inhibit the occurrence of caries.However, recent comprehensive studies have concluded that roughly 10% of such operations will fail [6] and indicates that failure of this operation on an annual basis can be as high as 5 million in the US alone [7].The present study indicates that the use of custom-made flow-burs that were constructed in-house for applying a sealant have much improved marginal adaptation with less unfilled fissure volume and much less microleakage compared with a conventional applicator.The use of flow-bur in this study and our statistical analysis indicate that there is a 50% reduction in microleakage for filling an occlusal area and 66% reduction of unfilled areas inside the fissures.While the authors are confident that there is a definite advantage in applying the sealant and for a more successful sealant filling operation, additional long-term studies are needed to demonstrate if such advantages may result in less failure when such flow-burs are used.
Statistical data for microleakage and penetration has another significant advantage in using a flow-bur for sealant placement,   besides their average values that we discussed above.And this has to do with consistency of the operations on a routine basis.The standard deviation of data for use of flow-bur for microleakage is 45% less than the corresponding value for a non-vibrating applicator.For penetration and adaption data, the result also show that the flow-bur data Group 3 are far less scattered than the data for group 4 that used the applicator.Accordingly, we conclude that not only use of flowbur will result in less microleakage, superior adhesion between the sealant and enamel, and deeper penetration, but also such usage will yield more consistent result with less operational errors.
Use of flow-burs for sealant placement may have another remarkable effect that has been envisioned for these operations.While we have not obtained quantitative data, it is been a general observation that the flow-bur may use less sealant material to effectively cover occlusal areas, in comparison to the standard applicator.This result would indicate that each fill can be performed even more economically and more importantly if sealant material is limited or scarce, this technique can cover multiple operations with the same amount of material that is used for a single operation.However, more studies would be needed to quantify the material use for such operations.
In a developing tooth, occlusal areas are not static but dynamic, as they continuously deformed outwardly.Thus, use of flow-bur with less adhesive in the fissure area will generate less sealant-enamelinterfacial resistance for occlusal enamel deformation and ultimately a healthier tooth.
Use of flow-burs will allow a dental practitioner to more effectively manipulate the sealant in occlusal areas for stronger sealant-dentin bonding, with superior consistency using less material for dental ISSN: 2469-5734 sealants.Such attributes will surely generate more confidence for the operator; yet, a wide clinical adaptation of this placement technique may require additional studies, before it can be fully implemented.In a future study, one can see if other dental sealants can also exhibit the similar improved penetration and marginal adaptation that we have observed with one sealant.The other concern is the longevity of these treatments.The thermocycling of the specimen is to ensure that in vitro analysis can also be applied to in vivo experience.However, to ensure the longevity of this technique a long-term clinical study should be in performed using a variety of sealants used in present day practice.
It should also be emphasized that for construction of these inhouse made flow-burs was not optimized in any form, beyond ensuring that they adhere to design principles for such burs [14] and their overall spreading functionality.Inducing an oscillation to the interface of the sealant, not only is affected by the frequency of these oscillations, but also by the amplitude of these vibrations.The amplitude of oscillations induced by the flow-burs is dependent on the asymmetricity of the tip and the aspect ratio of maximum and minimal dimensions at the bur tip.Once such optimizations for the design of the flow-burs are achieved, it is anticipated that use of flow burs can yield even better results that we reported in this paper.
The effectiveness of flow-burs that were designed and tested in this study to deform and manipulate an adhesive depends not only on the frequency and amplitude of these oscillations, but also on rheological and interfacial properties of such materials.In our studies we have shown such burs are effective for one commercial sealant.It is expected that other sealants on the market should have similar rheological properties as the one we have tested [20].Accordingly, one expects that flow burs should be successful with other sealants not considered in our studies.Nonetheless, we recommend in-vitro microleakage and penetration studies before adaptation of flow burs for other sealants.
This study has been performed exclusively for the effective placement of sealants in dental fissures.A previous study has already demonstrated that a needle vibrating tool was effective in in cleansing and etching occlusal pits and fissures [21].Accordingly, one may extend this study and show that flow-burs, constructed in a dentist office, can also be used for etching and cleaning, as well as sealant placement.

Conclusions
We have reported comparative microleakage and depth of penetration studies on dental sealants using two placement techniques.It is shown that dental sealant placement technique can have a decisive effect on occlusal adhesion and penetration.A set of flow-burs with identical tip geometry as used previously for lining of flowable composites were constructed and used to manipulate the sealant in the occlusal area of extracted healthy teeth.The results were compared with similar data using a conventional dental applicator.The comparisons indicate that the use of flow-burs resulted in 50% reduction in microleakage on average for filling a tight area and 66% reduction of unfilled voids inside the treated fissures.With superior marginal adaptation and deeper penetration, the analysis also indicated that the use of an oscillating bur as used in this study to deform the sealant was more consistent with significantly less operational errors.It is concluded that use of flow-burs may have a significant advantage in successful placements of dental sealants.

Figure 1 :Figure 2 :
Figure 1: Spreading ability of a dental adhesive (Esthet-X flow).Using a flow-burs A -before application; B -After application

FF
lengths a and c are measured interfacial length of the penetrated dye on the two sides of the cavity and b and d are the respective total length of the sealant interface with enamel, as shown in Figure 4A.The penetration ability was assessed as the proportional area of the fissure which is unfilled by sealant relative to the whole fissure area.The fraction of sealant area penetration

Figure 3a :
Figure 3a: Placement of sealants by two different techniques

Figure 4 :
Figure 4: Measuring microleakage and penetration.(A): Lengths a and c are length of microleakage, and b and d represent the length of sealant on two opposite side.(B): The fissure sealant area (sa) and unfilled area (ua).

Figure 5 :
Figure 5: Images of microleakage tests for the two placement techniques using: A -Flow-bur; B-conventional applicator.

Figure 6 :
Figure 6: Images of sealant penetration for the two placement techniques using: A -Flow-bur; B-conventional applicator.

Table 1 :
Statistial Data on Microleakage and occlusal penetration