Ni-W合金電析膜の熱処理前後の構造と硬度に及ぼす下地Niめっきの影響
早田 慎一朗大上 悟高橋 武寛中野 博昭
著者情報
ジャーナル オープンアクセス HTML

2015 年 101 巻 11 号 p. 590-597

詳細
抄録

Electrodeposition of Ni-W alloys was conducted from an unagitated sulfate solution containing citric acid at pH 5 and 60 °C under coulostatic (9.0×105) and galvanostatic (100-5000 A·m–2) conditions onto steel sheets with an initial Ni plating, and the effect of initial Ni plating on the structure and hardness of deposited Ni-W alloys was investigated before and after annealing. The precipitates of Ni4W and NiW were observed in deposits obtained at all the current densities after annealing, irrespective of having undergone initial Ni plating or not. Without initial Ni plating, a lot of large precipitates occurred in the vicinity of steel substrate, while the fine precipitates occurred with initial Ni plating. Without initial Ni plating, the W content in deposits increased in the vicinity of steel substrate due to diffusion of Ni in deposits into steel substrate during annealing. With initial Ni plating, the W content in deposits in the vicinity of Ni plating decreased due to diffusion of Ni in Ni plating into deposits during annealing. Before annealing, W content in deposits was lower with initial Ni plating than that without Ni plating. With initial Ni plating, W content in deposits was lower and Ni diffused from Ni plating to deposits during annealing, as a result, the formation of large precipitates of Ni4W and NiW seems to be suppressed. The hardness of deposited Ni-W alloys after annealing increased when the precipitates of Ni4W and NiW became uniform and fine.

著者関連情報
© 2015 一般社団法人 日本鉄鋼協会

This article is licensed under a Creative Commons [Attribution-NonCommercial-NoDerivatives 4.0 International] license.
https://creativecommons.org/licenses/by-nc-nd/4.0/
前の記事 次の記事
feedback
Top