The investigation of applicability of the Hollomon-Jaffe equation on tempering the HSLA steel

Janjušević Zoran (The Institute of Technology of Nuclear and other Mineral Raw Materials, Belgrade)
Gulišija Zvonko (The Institute of Technology of Nuclear and other Mineral Raw Materials, Belgrade)
Mihailović Marija (The Institute of Technology of Nuclear and other Mineral Raw Materials, Belgrade)
Patarić Aleksandra (The Institute of Technology of Nuclear and other Mineral Raw Materials, Belgrade)

High strength low-alloyed (HSLA) Cr-Mn-Si steels belong to a group of steels that can reach their full mechanical properties after quenching and tempering. Those properties depend both on the temperature and time of tempering. Knowing the tempering parameters, it is possible to reach the desired properties of the treated steel. Some results on investigating the Hollomon-Jaffe equation (in parametric form) application for tempering of HSLA steel, are shown in this paper. The experiments were performed in real production conditions, using a standard material. The quenching was performed at 870°C, the heating period was always 30 min, with subsequent cooling into the oil bath. The tempering was carried out in temperature range from 480 to 680°C, while tempering time varied from 15 min to 24 h. The degree of tempering is referred through the hardness values changing. The experimental results have shown a pretty well agreement to tempering parameters, included in Hollomon-Jaffe equation, for this kind of HSLA steel.

Keywords: HSLA steel, quenching/tempering, Hollomon-Jaffe equation