Effect of Wood Species on the Pore Volume and Surface Area of Activated Carbon Derived From the Self Activation Process

Authors

  • Lee M Smith Department of Mechanical and Energy Engineering University of North Texas
  • Sheldon Q Shi Department of Mechanical and Energy Engineering University of North Texas
  • Jiangtao Shi College of Materials Science and Engineering Nanjing Forestry University
  • Cuicui Wang International Center for Bamboo and Rattan Beijing
  • Yulin Tan International Center for Bamboo and Rattan Beijing
  • Haiying Zhou International Center for Bamboo and Rattan Beijing

Keywords:

Activated carbon, Wood Species, BET Surface area, Pore Volume

Abstract

In this study, the effect of wood species on pore structure of activated carbon (AC) generated from a self-activation process at different dwelling times was investigated. Ten hardwood species were selected (afromosia, alder, black cherry, makore, pomelle sapele, soft maple, teak, walnut, white oak and yellow poplar) were activated at 1050OC for three dwelling times (10 h, 5 h, and 2.5 h). X-ray diffraction, Raman spectroscopy, and elemental analysis were performed on AC to analyze the carbon structure. The Brunauer-Emmett-Teller (BET) surface area, Barrett-Joyner-Halenda (BJH) pore volume, and BJH pore width of AC samples were determined. It was shown from the study that the mesopore width of AC decreased as micropores were transitioned to mesopores, leading to an increase in the pore volume and surface area. The density and porosity of the samples that underwent 2.5-h dwelling time were determined. The porosity of the wood and their resultant AC were compared. The porosity between the wood and its AC possessed a relationship when true bulk densities of the wood and carbon were compared. The porosity of wood had an impact on the bulk density of the carbon but not on the true density. No relationship was observed between the porosity and surface area of the carbon samples. 

Author Biographies

Lee M Smith, Department of Mechanical and Energy Engineering University of North Texas

Ph.D. Candidate

Sheldon Q Shi, Department of Mechanical and Energy Engineering University of North Texas

Professor

Jiangtao Shi, College of Materials Science and Engineering Nanjing Forestry University

Associate Professor

References

Bang JH, Lee HM, An KH, Kim BJ (2017) A study on optimal probe development of modified commercial activated carbons for electrode materials of supercapacitors. Appl Surf Sci 415:61-66.

Brommier C, Xu R, Wang W, Wen D, Lu J, Ji X (2015) Self activation of cellulose: A new preparation methodology for activated carbon electrodes in electrochemical capacitors. Nano Energy 13:709-717.

Caturla F, Molina-Sabio M, Rodriguez-Reinoso F (1991) Preparation of activated carbon by chemical activation with ZnCl2. Carbon 29(7):999-1007.

Chen D, Chen X, Sun J, Zheng Z, Fu K (2016) Pyrolysis polygeneration of pine nutshell: Quality of pyrolysis products and study on the preparation of activated carbon from biochar. Bioresour Technol 216:629-636.

El-Merraoui M, Aoshima M, Kaneko K (2000) Micropore size distribution of activated carbon fiber using the density functional theory and other methods. Langmuir 16(9): 4300-4304.

Gamby J, Taberna P, Simon P, Faubarque J, Chesneau M (2001) Studies and characterization of various activated carbons used for carbon/carbon supercapacitors. J Power Sources 101(1):109-116.

Girgis B, Temerk Y, Gadelrab M, Abdullah I (2007) X-ray diffraction patterns of activated carbons prepared under various conditions. Carbon Lett 8(2):95-100.

Hameed B, Din A, Ahmad A (2007) Adsorption of methylene blue onto bamboo-based activated carbon: Kinetics

and equilibrium studies. J Hazard Mater 3(22):819-825.

Kadirvelu K, Thmaraiselvi K, Namasivayam C (2001) Removal of heavy metals from industrial wastewaters by adsorption onto activated carbon prepared from an agricultural solid waste. Bioresour Technol 76(1):63-65.

Kaneko K, Ishii C, Ruike M, Kuwabara H (1992) Origin of super high surface area and microcrystalline graphitic structures of activated carbons. Carbon 30(7):1075-1088.

Li W, Yang K, Peng J, Libo Z, Guo S, Xia H (2008) Effects of carbonization temperatures on characteristics of porosity in coconut shell chars and activated carbons derived from carbonized coconut shell chars. Ind Crops Prod 28(2):190-198.

Liu Y, Xue JS, Zheng T, Dahn JR (1995) Mechanism of lithium insertion in hard carbons prepared by pyrolysis of epoxy resins. Carbon 34(2):193-200.

Meier E (2016) WOOD! Identifying and using hundreds of woods worldwide. The Wood Database.

Richter HG, Grosser D, Heinz I, Gasson PE (2004) IAWA list of microscopic features for softwood identification. IAWA J 25(1):1-70.

Rowell RM (2005) Handbook of wood chemistry and wood composites. CRC Press, Boca Raton, FL.

Shamasuddin M, Yusoff N, Sulaiman M (2016) Synthesis and characterization of activated carbon produced from kenaf core fiber using H3PO4 activation. Procedia Chem 19:558-565.

Shi SQ, Xia C (2014) Porositization process of carbon or carbonaceous materials. U.S. Patent 14/211,357, 18 9 2014.

Shi Y, Chrusciel L, Zoulalian A (2007) Production of charcoal from different wood species. In Recents progress en genie des procedes. Paris, France.

Singh G, Kim IY, Lakhi KS, Srivastava P, Naidu R, Vinu A (2017) Single step synthesis of activated bio-carbons with a high surface area and their excellent CO2 adsorption capacity. Carbon 116:448-455.

Srinivasakannan C, Bakar MZA (2004) Production of activated carbon from rubber wood sawdust. Biomass Bioenergy 27(1):89-96.

Wheeler EA, Baas P, Gasson PE (1989) IAWA list of microscopic features for hardwood identification. IAWA J 10(3):219-332.

Wigmans T (1989) Industrial aspects of production and use of activated carbon. Carbon 89(1):13-22.

Williams PT, Reed AR (2006) Development of activated carbon pore structure via physical and chemical activation of biomass fibre waste. Biomass Bioenergy 30(2):144-152.

Xia C, Shi SQ (2016a) Self-activation process to fabricate activated carbon from kenaf. Wood Fiber Sci 48:62-69.

Xia C, Shi SQ (2016b) Self-activation for activated carbon from biomass: Theory and parameters. Green Chem 18(7): 2063-2071.

Xia C, Kang C, Mumukshu PD, Cai L, Gwalani B, Banerjee R, Shi SQ, Choi W (2016) Pine wood extracted activated carbon through self-activation process for high-performance lithium-ion battery. Chem Sel 1(13):4000-4007.

Yalcin N, Sevinc V (2000) Studies of the surface area and porosity of activated carbons. Carbon 38(14):1943-1945.

Downloads

Published

2020-04-24

Issue

Vol. 52 No. 2 (2020)

Section

Research Contributions

License

The copyright of an article published in Wood and Fiber Science is transferred to the Society of Wood Science and Technology (for U. S. Government employees: to the extent transferable), effective if and when the article is accepted for publication. This transfer grants the Society of Wood Science and Technology permission to republish all or any part of the article in any form, e.g., reprints for sale, microfiche, proceedings, etc. However, the authors reserve the following as set forth in the Copyright Law:

1. All proprietary rights other than copyright, such as patent rights.

2. The right to grant or refuse permission to third parties to republish all or part of the article or translations thereof. In the case of whole articles, such third parties must obtain Society of Wood Science and Technology written permission as well. However, the Society may grant rights with respect to Journal issues as a whole.

3. The right to use all or part of this article in future works of their own, such as lectures, press releases, reviews, text books, or reprint books.