Synthesis of BaTiTe3O9 Ceramics for LTCC Application and Its Dielectric Properties
Do-Kyun KWONMichael T. LANAGANThomas R. SHROUT
Author information
JOURNAL FREE ACCESS

2005 Volume 113 Issue 1315 Pages 216-219

Details
Abstract

A new tellurate, BaTiTe3O9, was found in the BaO-TiO2-TeO2 ternary system. Using conventional solid state reaction, the new single phase compound, BaTiTe3O9 phase was synthesized and sintered over the very low temperature range of only 625-700°C. In addition, different calcinations routes, including the effect of TiTe3O8 precursor in the phase formation, were examined. The dielectric properties of BaTiTe3O9 ceramics were determined in the microwave region as well as at low frequencies. The relative dielectric permittivity (εr) and the temperature coefficient of permittivity (TCε) of BaTiTe3O9 at 1 MHz were measured as 30 and 790 ppm/°C, respectively. The dielectric properties were maintained up to microwave region without degradation. The dielectric permittivity and Q×f product obtained were 29 and 1,700 GHz at 7.6 GHz, respectively. The temperature coefficient of resonance frequency (TCF) showed a large negative value of -372 ppm/°C.

Content from these authors
© 2005 The Ceramic Society of Japan
Previous article Next article
feedback
Top