Preparation of Nanocomposite Heteropoly Metalate Based Graphene Oxide : Insight into Cadmium Adsorption

How to cite this article Fakhri H, Mahjoub A. R, Aghayan H. Preparation of Nanocomposite Heteropoly Metalate Based Graphene Oxide: Insight into Cadmium Adsorption. J Nanostruct, 2017; 7(3):223-235. DOI: 10.22052/jns.2017.03.009 We developed a facile strategy for preparation of heteropoly metalate/ graphene oxide nanocomposite as a new ion exchanger for cadmium ion removal from aqueous solution. The synthesized nanocomposite was characterized by X-ray powder diffraction (XRD), UV-Vis spectroscopy, FT-IR spectroscopy and Raman spectroscopy. Our findings indicated that the combination of heteropoly metalate nanoparticles with graphene oxide results in an excellent performance for cadmium ions removal of aqueous solution. The experimental data demonstrated that the adsorption isotherm fitted well by Langmuir model with maximum sorption capacity of 47.85 mg/g. The removal behavior of this compound was evaluated by various parameters such as contact time, concentration of metal ion, pH of solution and temperature. In addition, the effect of interfering cations on the cadmium adsorption is investigated. Dubinin–Radushkevich model represented physical sorption occurred as bold mechanism that is confirmed by thermodynamic parameters. Also, the obtained data of the recycling experiment presented excellent stability after 4 consecutive cycles. This study indicated heteropoly metalate supported graphene oxide with good performance for removal of cadmium can be used for treating polluted solution by other heavy metal.


INTRODUCTION
Water contamination by heavy metals has become a serious subject of worldwide concerns.Discharge of these heavy metals from various sources like mining, Ni-Cd batteries, oil refineries, smelting operations and pigments quickly are increasing in the recent years [1].So, the removal of these toxic pollutions from aqueous waste is nowadays considered as a hot issues being investigated.Cadmium (Cd) as a component of heavy metals group attracted notable attention due to high toxicity, tendency to accumulation in liver and kidney [2], non-biodegradable and also has bad effects on ecosystem [3,4].The World Health Organization (WHO) is considered cadmium as one of the most dangerous heavy metals and a drastic human carcinogen [5].Several methods such as chemical precipitation, reverse osmosis and solvent extraction [6,7] are employed for treatment of polluted solution.However, these methods are unsuitable due to incomplete removal of the heavy metal and so additional treatment is required.Other methods such as ultrafiltration and electrochemical deposition are used in developed industrial but high cost and complexity of process limited their usage [8].Many of research studies is introduced ion exchange as an effective method for treating contaminated solution, particularly ion exchange process by inorganic materials that have in nurture ion exchange properties like heteropoly acids (HPAs).HPAs nanoparticles are made of particular combination of hydrogen and oxygen with certain metals and non-metals.Nowadays, Keggin structure of HPAs ( with overall formula [XM 12 O 40 ] n− , where X is the heteroatom (eg P 5+ , Si 4+ , or B 3+ ) and M is the addenda atom (most common are molybdenum and tungsten)) is attracted more attention in this area.Potential acidic properties is one of the excellent properties of keggin structure that it enable as ion exchanger to remove metals ion [9,10].This ability comes back to the interaction of metal ions in solution with an oxygen end-atom and a release of exchangeable protons in the HPAs structure.So they can act as cation-exchange materials.However, low surface area and high solubility in aqueous media limited its usage as ion exchanger.The formation of salt of these compounds leads to increase their surface area and insolubility in aqueous solution.Siddiqui et al. reported the synthesis of Zirconium (IV) tungsto iodo phosphate and used it for the separation of Pb 2+ from other metal ions [11].Mittal et al. synthesized zirconium antimono phosphate and zirconium phosphor tungstate as inorganic ion exchanger and reported that these have good ion exchange capacity for Fe 2+ , Fe 3+ , Pb 2+ and Ba 2+ [12].However, their separation and filtration even under conditions of high speed centrifugation still is confined their practical applications.Recently, many researches focused on fabrication of nanocomposite by inserting the nanoparticles on the various supports such as silica [13], multi walled carbon [14] and carbon nanotubes [15] that is an important study for the exploration of their properties and applications.Graphene oxide (Go) with layer structure is the most attractive and the newest member of carbon family that has various functional groups such as carboxyl, hydroxyl and epoxy.Layer structure and also presence of different functional groups introduced it as desirable support.Composites of decorated Go sheets by nanoparticles with oxidative and acidic properties such as HPAs are developed [16,17].As an evident point from the literature, the immobilization of HPAs on the graphene based surfaces produces new nanocomposite materials which have potential importance in the areas such as optics, electronics, catalysis and sensors [18][19][20].Anyway, there is a little evaluation of heteropoly metalate supported graphene oxide.In the present study, tin (IV) molybdo tangsto phosphate, donated as TMTP, supported Go was prepared via a simple strategy and in the first time, its application for removal of Cd ions was studied.Finally adsorption experiments directed to examine effective parameters such as metal ion concentration, pH of solution, temperature and presence of alkaline metal ions.

Materials
All of the materials were used in this research work purchased from Merck and Aldrich without further purification.

Characterization
FT-IR analyses of materials were performed using a Shimadzu-8400S spectrometer in the range of 400-4000 cm -1 .The crystalline structure of products were recorded by powder X-ray diffraction (XRD) on philips X-pert X-ray diffractometer using Cu Kα radiation (wavelength, λ = 1.5418 ˚A).The morphology of various samples was obtained with scanning electron microscopy (SEM, Philips XL-300 instrument).Inductively Coupled Plasma (ICP, Varian vista-PRO) was employed to evaluate the cadmium value.The Raman spectra of samples were recorded by the Almega Thermo Nicolet Dispersive Raman Spectrometer (Laser second harmonic @532 nm of a Nd: YLF laser).UV-Vis spectra were achieved with Shimadzu-UV-2550-8030 spectrophotometer in the range of 200-800 nm at room temperature.[21].Briefly, Na 2 HPO 4 (2.23 gr) and desired amount of sodium molybdate were dissolved in distilled water.So, the solution was stirred at 90 ˚C.After being stirred for 30 min, aqueous solution of Na 2 WO 4 .2H 2 O was added to the above heated solution.Subsequently, aqueous sulfuric acid solution was added dropwise until the solution pH value reached 1.5-2.In the following, the mixture was heated at 90 ˚C and then final product was extracted by diethyl ether and following was recrystallized.ICP analysis indicated that the atomic ratio of P/Mo/W were: 1/ 3.86/ 7.69 that this product, 4-molybdo-8-tangsto phosphoric acid, is symbolized as MTP.

Preparation of TMTP/Go composites
Go was prepared by a modified procedure according to the literature [22].TMTP supported Go, donated as TMTP/Go, was synthesized as follows: First, 1gr Go was dispersed in 40 ml water.So 3 gr MTP added to it and was stirred at 300 ˚C until the solvent was completely volatilized.Subsequently, the collected precipitate was calcined at 300 ˚C for 3 h.Acidic solution of SnCl 4 .5H 2 O (0.31 gr SnCl 4 •5H 2 O dissolved in 10 ml HCl) was added to above precipitate and was stirred at the room temperature.The sample was filtered and washed with distilled water and ethanol and dried in an oven at 60 ˚C for 18 h.ICP elemental analysis indicated that 20% of TMTP species was loaded on the Go support that indicated as 20%TMTP/Go.This procedure was used for preparation of other loading of TMTP on the support.

Adsorption experiment
Batch technique was employed to determine the adsorption capacities of Cd ions.For this purpose, 0.1 gr of adsorbent was mixed in a 20 mL of preselected concentration of metal ion solution.The mixture was continuously shaken by the mechanical shaker at 150 rpm and 25 ºC.The desired pH of the solution was adjusted using negligible volumes of 0.1 M nitric acid and sodium hydroxide solution.At the end of adsorption experiments, the solid phase was collected by centrifuged at 6000 rpm for 10 min and the residual concentration of Cd in aqueous solution was determined by ICP-OES elemental analysis.Also the effect of different conditions such as pH, contact time, concentration of metal ions and temperature of solutions on adsorption efficiency were investigated.In order to examine influence of interfering cations containing Ca 2+ and Mg 2+ on adsorption process, Cd solution with initial concentration 200 ppm was added to various concentration of interfering cations ( 80, 160 and 240 ppm).The equilibrium adsorption capacity was calculated according to Eq. 1 where C 0 and C e are the initial and equilibrium concentration of the metal ions (mg.L -1 ), v is the volume of the liquid phase (ml) and W is the mass of the adsorbent (gr).

Adsorbent characterization
The morphology and texture of produced samples were investigated by SEM and TEM analysis.As seen in Fig. 1a, the smooth and silk-like sheets were observed for Go sample.It is found from Fig. 1b and TEM images in Fig. 1c , d that surfaces of supports (Go) were randomly covered by lots of TMTP nanoparticles which suggesting a strong interaction between TMTP nanoparticles and Go.The purity phase of synthesized products examined with XRD analyses as shown in Fig. 2. The diffraction peak at 2θ= 8.9˚ correspond to the (001) reflection of Go (Fig. 2a) [23].As shown in fig.2b, XRD patterns of MTP sample are in good agreement with its reported patterns in previous study indicating phase purity and good crystalline of it [21].In the long-range ordered XRD pattern of TMTP/Go (Fig. 2c) the absence of any diffraction peaks related to TMTP in composite diagram implies the high dispersion of TMTP on the Go support [24].The FT-IR spectrum of Go (Fig. 3a) indicated peaks at 1056 cm-1 , 1226 cm -1 , 1622 cm -1 and 1732 cm -1 that correspond to alkoxy C-OH stretching vibrations, epoxy C-O-C stretching vibrations, aromatic C C stretching vibrations and C = O stretching vibrations of the -COOH groups, respectively [25].The broad peak corresponded to the hydroxyl groups and the adsorbed water on surface is located at 3381 cm −1 [26].Fig. 3b showed four characteristic peaks belonging to MTP at 1051 cm -1 (ν P-O ), 951 cm -1 (ν m=o ), 877 cm -1 (ν Mo-O-Mo ) and 741 cm -1 (ν Mo-O-Mo ) [21].FT-IR spectra of TMTP/ Go demonstrated that the structure of TMTP is remained in composition sample (Fig. 3c) and confirmed the presence of both Go and TMTP in the nanocomposite.TMTP interact with functional groups such as carbonyl, carboxyl and other group of Go.Especially, in aqueous solution the carboxyl group is weakly acidic but when it is bonded with TMTP that have a lower pH value; it alters to a weak base by changing to a positive charge.So, electrostatic bonding between positively charged carboxyl groups and negatively charged TMTP anions improved interaction TMTP with surface of Go [27].In comparing between the Go and TMTP/ Go spectra, red shift of C=O peak was observed from 955 cm -1 to 941 cm -1 that this may be referred to electrostatic bonding between TMTP and Go.UV-Vis spectroscopy was applied to evaluate the ligand-to-metal charge transfer (LMCT) band of the pure MTP in 200-800 nm regions.The adsorption edge MTP was measured using the first derivative of the absorption spectrum.The calculated band gap (Fig. 4a) in the case of the pure MTP is 2.25 eV (edge wavelength 551 nm).This value shifted to 2.88 eV for TMTP/Go sample.This shift in the band gap clearly associated with the changed energy levels of MTP owing to electron transfer from MTP to Go [28].These results were supported by Raman spectroscopy.Interaction between Go and TMTP can be investigated by the changes of the degree of disorder in crystalline structure carbon materials using Raman spectroscopy.The Raman spectrum of Go exhibited two peaks at 1360 cm -1 and 1650 cm -1 which are attributed to existing disorder in the carbon structure (D band) and E 2 g mode of sp 2 bonds of carbon framework (G band) respectively.The obtained I D /I G ratio for Go and TMTP/Go are 0.94, 1.04 respectively (Fig. 4b).The increased ratio indicated the anchoring of TMTP onto Go resulted in increased defect of the sp 2 domain which can be assumed as a good evidence for successful formation TMTP/Go.

Adsorption tests Effect of amount of loading on removal efficiency
The dependence of Cd 2+ removal to the presence of TMTP /Go composite shown in Fig. 5.It is clear that only 27% of Cd +2 removed by pure Go.When TMTP/Go is used as adsorbent, removal efficiency was enhanced with the increase of loading amount.The efficiency reaches the maximum when the TMTP loading increase up to 30%.The fall of removal efficiency with the further increasing of loading was corresponded to aggregation of TMTP species on surface of TMTP/Go composite.

Effect of pH solution
The initial pH of solution plays important role in determining adsorption nature of adsorbent.The different cadmium species exist in aqueous solution such as Cd +2 , Cd(OH) + , Cd(ІІ)(OH) 2 , Cd(OH) 2 (s), [Cd(OH) 3 ] -and [Cd(OH) 4 ] 2-that concentration of each of them depends on pH of solution.Cd +2 is dominant species at pH 8 [29].Hence, the considered value range of pH is adjusted between 2-8.Results of Zeta potential for 30%TMTP/Go nanocomposite demonstrated in Fig. 6a.It is seen, this nanocomposite is negatively charged at the entire mentioned range pH (2pH8).As shown in Fig. 6b, the removal of metal ion increases along with increasing the pH from 2 until 8.In the lower values of pH, competition of Cd 2+ ions with H + or H 3 O + for adsorption on negative surface adsorbent increase and so decrease of Cd removal is expected.For a higher pH, it is seen that adsorption efficiency is reached to maximum value at pH=8 that attributed to decline of protons concentration resulting enhancement of Cd 2+ removal.

Effect of contact time
In particular, adsorption kinetics is important character for fast treatment water.The adsorption of Cd +2 from aqueous solution at initial concentration of 10 ppm on the adsorbent as a function of contact time is represented in Fig. 7a.As shown, the adsorption process is rapid within the first 60 min and reached equilibrium within 180 min.The initial rapid adsorption can be ascribed to expanded access to active sites due to plane layer structure of Go unlike other supports such as SBA-15 or carbon nanotube that lead easy migrate of Cd +2 ions to the external active site of TMTP/Go nanocomposite and Subsequently, the slow diffusion rate of Cd +2 ions into the internal site of adsorbent.
In the present work, three models of kinetic reaction including pseudo-first-order, pseudo- Where q e (mg/g) and q t (mg/g) are the sorption amounts per unit mass at equilibrium and at time t; k 1 is the pseudo-first-order rate constant, k 2 is pseudo-second-order rate constant, k d is diffusion rate constant and c is the intercept that corresponded to the thickness of the boundary layer.The fitting parameters and the correlation factors (R 2 ) of the pseudo-first-order and pseudosecond-order kinetic models are depicted in Fig. 7b, c and Table 1.The high correlation factor and good accordance between the experimental q e value and calculated value of pseudo-secondorder kinetic model indicated that the adsorption dynamics obey pseudo-second-order model (R 2 = 0.9945).
For the better identify of diffusion mechanism, the Weber-Morris intraparticle diffusion model log(  −   ) =   −  1 2.303 (2) was then used [32].This model can be ascribed the mass transfer steps in the Cd +2 ions adsorption onto adsorbent.The plots of q t versus t 1/2 (Fig. 7d) in the range of the studied adsorption give nonlinear curve and did not pass through the origin (C≠0) that described intraparticle diffusion was not the only rate-controlling step.The initial portion can be assigned to the boundary layer diffusion (film diffusion) and the second portion with lower slop reflected to the slow adsorption step where the intraparticle diffusion is involved in adsorption process but not the only rate controlling step (fig.7d, Table 2).The initial portion with larger slop has a faster rate than second portion.This rapid rate is due to the significant availability to active adsorption sites on sheets of Go and on the other hand, the lower slope of second portion resulted a low adsorption rate owing to decreased concentration of ion is spent long time to diffuse.Effect of the initial metal ion concentration Fig. 8 shows the adsorption isotherm of Cd +2 ions by 30%TMTP/Go nanocomposite at the initial concentration range of 10-200 mg.L −1 .Adsorption isotherm can represent the significant parameters for designing a favorable adsorption system.The isotherm data were simulated to the Langmiur (Fig. 8b), Freundlich (Fig. 8c) and Dubinin-Radushkevich (D-R) models (Fig. 8d).
The obtained parameters of these models can be employed to evaluation of surface properties and affinity of the adsorbent toward metal ions.The Langmuir model assumes that metal ions are adsorbed as monolayer coverage without any interaction between adsorbed species [33].The linear form of this model is shown in the following relation; where Q 0 (mg.g -1 ) is the required amount of metal to form a monolayer and b (L.mg -1 ) is the constant that referred to energy of adsorption.The equilibrium parameter or separation factor (R L ) is other important parameters that obtained of Langmuir plot by the following equation; where C 0 (mg.L -1 ) is the highest initial concentration in the solution.The R L reflect the type of isotherm to be favorable (0 < R L < 1) or unfavorable (R L > 1).
The Freundlich model assumes multilayer adsorption onto heterogeneous surface [34].The linearized form of this equation is represented as; where k f is the Freundlich constant related to the multilayer adsorption of the adsorbent and n is linearity index related to the adsorption intensity.
The Dubinin-Radushkevich (D-R) isotherm model is usually applied to determine the type sorption process (chemical or physical sorption) which were expressed in the following equation; where q DR is the monolayer capacity (mmol.g -1 ), B DR (mol 2 .J -2 ) is referred to adsorption energy and ε is the Polanyi potential which is calculated by; where R is the gas universal constant (8.314J. mol. - K -1 ) and T is the absolute temperature (K).The value of E (kJ.mol -1 ) is mainly parameters of (D-R) equation for estimation the type of sorption process.This parameter can be obtained according to the below equation [34]: If value of E was less than 8 kJ.mol -1 , the physical sorption mainly will occur and if value of E was 8-16 kJ.mol -1 the chemical sorption will be expected.The fitted results investigated in this work are tabulated in Table 3 and 4. As can be seen in Table 3, The sorption isotherm of Cd +2 could be fitted better by Langmuir than Freundlich model with high correlation coefficient values (R 2 > 0.98) that is described Cd +2 ion is adsorbed as a monolayer coverage onto specific sites of 30%TMTP/Go composite.Also, q m of this composite measured from the Langmuir isotherm is 47.85 mg/g.It can be seen from Table 3, the value of R L is 0.42, implied favorable adsorption as it places in 0 to 1 range.It is also seen, the value of n (1.54) is lied between 1 and 10, resulted that the sorption is favorable under desired condition.The values of E were between 1 and 8 (Table 4) indicating that physical attraction can be affected on Cd +2 ions sorption.Table 5 revealed some adsorption capacity by different adsorbents that reported previously.As can be seen, TMTP/Go nanocomposite with desirable adsorption capacity has excellent adsorption performance.

Adsorption thermodynamics
The relations among temperature and Cd 2+ ions adsorption described by the following formulas: where the ∆G˚ is the change in Gibbs free energy  bigger steric hindrance and so its negative effect on adsorption is stronger [47].Since concentration of Ca 2+ and Mg 2+ in fresh water is approximately between 10-80 ppm, so the presence of these cations with these levels of concentration have not significant effect on Cd 2+ adsorption.

Reusability
Reusability is considered a particular parameter for evaluation the economy and applicability of

Fig. 10 .
Fig. 10.The effect of interfering cations on adsorption efficiency

Table 1 .
kinetic adsorption parameters of pseudo-first-order and pseudo-second-order models

Table 5 .
Comparison of adsorption capacity of Cd2+ by various adsorbent