Abstracts

Effect of CarisolvTM gel on root surfaces

Scanning electron microscopic analysis of the effect of Carisolv^TM gel on periodontally compromised human root surfaces

Daniela Corrêa Grisi^I; Letícia Helena Theodoro^I; José Eduardo César Sampaio ^I; Márcio Fernando de Moraes Grisi^II; Sérgio Luiz de Souza Salvador^III

^IDepartment of Diagnostics and Surgery, Faculty of Dentistry of Araraquara, São Paulo State University, Araraquara, SP, Brazil

IIDepartment of Buccomaxillofacial Surgery and Traumatology and Periodontology, Faculty of Dentistry of Ribeirão Preto, University of São Paulo, Ribeirão Preto, SP, Brazil

^IIIDepartment of Clinical Analysis, Faculty of Pharmaceutical Sciences of Ribeirão Preto, University of São Paulo, Ribeirão Preto, SP, Brazil

^{Correspondence} Correspondence: Prof. Dr. José Eduardo César Sampaio Diagnóstico e Cirurgia Faculdade de Odontologia de Araraquara, UNESP Rua Humaitá, 1680, 14801-903 Araraquara, SP, Brasil Tel: +55-16-201-6369 Fax: +55-16-201-6369 e-mail: jsampaio@foar.unesp.br

ABSTRACT

The aim of this study was to analyze, under scanning electron microscopy (SEM), the morphologic characteristics of root surfaces after application of Carisolv^TM gel in association with scaling and root planing (SRP). Sixty periodontally compromised extracted human teeth were randomly assigned to 6 groups: 1) SRP alone; 2) passive topical application of Carisolv^TM + SRP; 3) active topical application of Carisolv^TM + SRP; 4) multiple applications of Carisolv^TM + SRP; 5) SRP + 24% EDTA; 6) topical application of Carisolv^TM + SRP + 24% EDTA. Carisolv^TM gel was applied to root surfaces for 30 s, followed by scaling and root planing, consisting of 50 strokes with Gracey curettes in an apical-coronal direction, parallel to the long axis of the tooth. The only exception was group 4, in which the roots were instrumented until a smooth, hard and glass-like surface was achieved. All specimens were further analyzed by SEM. The results showed that the treatment with Carisolv^TM caused significant changes in root surface morphology of periodontally compromised teeth only when the chemical agent was actively applied (burnishing technique). Carisolv^TM failed to remove the smear layer completely, especially with a single application, independently of the method of application. Multiple applications of Carisolv^TM were necessary to achieve a smear layer reduction comparable to that obtained with 24% EDTA conditioning.

Key Words: periodontal disease, scaling and root planning, Carisolv^TM, scanning electron microscopy.

RESUMO

A utilização do Carisolv^TM tem sido proposta como um método auxiliar à raspagem e ao alisamento radicular (RAR), a fim de facilitar a descontaminação da superfície da raiz. O objetivo deste estudo foi avaliar, através da microscopia eletrônica de varredura (MEV), as características das superfícies radiculares, após a aplicação do Carisolv^TM em associação à RAR. Sessenta dentes humanos extraídos devido à doença periodontal foram divididos em 6 grupos: 1) RAR ; 2) Carisolv^TM (aplicação passiva) + RAR; 3) Carisolv^TM (aplicação ativa) + RAR; 4) Carisolv^TM (aplicações múltiplas) + RAR; 5) RAR + EDTA a 24%; 6) Carisolv^TM + RAR + EDTA a 24%. Carisolv^TM foi aplicado às superfícies radiculares por 30 s, seguido de raspagem e alisamento radicular, que consistiu de 50 movimentos com curetas de Gracey no sentido corono-apical, co o instrumento paralelo ao longo eixo do dente. A única exceção foi o grupo 4, no qual as raízes foram instrumentadas até obter uma superfície lisa, dura e com aspecto vítreo. Os espécimens tratados foram preparados e examinados em MEV. Os resultados demonstraram que a associação do Carisolv^TM aos procedimentos periodontais mecânicos proporcionou modificações significativas na superfície radicular quando comparada à raspagem e ao alisamento radicular, apenas quando o Carisolv^TM foi aplicado de forma ativa. A aplicação do Carisolv^TM uma única vez, apresentou um efeito limitado na capacidade de remoção de smear layer, sendo que aplicações sucessivas apresentaram resultados comparáveis àqueles obtidos após a aplicação do EDTA.

INTRODUCTION

In periodontal disease, root surface is exposed to the subgingival environment and bacterial plaque. Exposure to crevicular fluid, as well as to enzymes and metabolites produced by subgingival plaque bacteria induces physical and chemical alterations on root cementum. Periodontitis-affected root surfaces are hypermineralized (1-3), contaminated with bacterial plaque (4) and other cytotoxic substances (5).

Traditional scaling and root planing (SRP) proce dures have relied on the mechanical removal of plaque, calculus, root-bound toxins and contaminated cementum. Although the effectiveness of scaling and root planing has been well documented, the efficacy of this treatment has been questioned. Additionally, smear layer that remains after instrumentation can impair periodontal healing (6,7).

There has been considerable interest in the use of chemical-assisted root detoxification. Chemical agents have been proposed to facilitate calculus removal (8,9), removal of smear layer and root-associated endotoxins (7,10,11), decalcifying of planed root surfaces, exposure of dentin or cementum collagen matrix, thus providing a biologically acceptable surface for regeneration of a new connective tissue attachment (12).

Different etching solutions, such as citric acid, tetracycline and EDTA, have been used as adjunctive therapies to scaling and root planing in order to overcome the limitations of these procedures.

Carisolv^TM gel (Mediteam, Sävadelen, Sweden), a chemomechanical caries removal system was developed to aid carious dentin excavation. This system consists of sodium hypochlorite and three aminoacids (lysine, leucine and glutamic acid) that are able to remove carious tissue without affecting the healthy dentin structure (13-16).

The use of chemical agents in association with mechanical treatment represents a possibility of a less traumatic procedure, preventing the excessive loss of root substance. In the field of Periodontics, the possibility of chemically dissolving calculus and contaminated root cementum in order to facilitate their mechanical removal is one of the most promising applications of Carisolv^TM gel.

Therefore, the purpose of this study was to investigate, under scanning electron microscopy (SEM), the morphologic characteristics of periodontally compromised human root surfaces after application of Carisolv^TM gel in association with scaling and root planning.

Material and Methods

Sixty periodontally compromised extracted human teeth with supra- and subgingival calculus were used. The teeth were extracted for periodontal reasons from patients treated at the Department of Diagnostics and Surgery of the Faculty of Dentistry at Araraquara, (Brazil), and were stored in saline until use. The research protocol was approved by the local Ethics in Research Committee.

Diseased tooth surfaces with adhered calculus were chosen as the treatment areas and delimited with a round bur, and the teeth were randomly assigned to 6 groups (n=10), as follows. Group 1: Scaling and root planing (SRP) alone. The root surfaces were instrumented with Gracey curettes (Hu-Friedy, Chicago, IL, USA), using 50 strokes in an apical-coronal direction, parallel to the axis of the tooth. Group 2: Passive topical application of Carisolv^TM gel + SRP. Carisolv™ gel was applied to the delimited area in each root for 30 s. Root surfaces were instrumented with Gracey curettes in the same way as described as in group 1. Group 3: Active topical application of Carisolv^TM gel + SRP: Carisolv^TM gel was burnished onto the delimited areas for 30 s, using a disposable microbrush tip. Root surfaces were instrumented with Gracey curettes, in the same way as described as in groups 1 and 2. Group 4: Multiple applications of Carisolv^TM gel + SRP. Carisolv^TM gel was applied several times interposing with SRP procedures, which were performed with Gracey curettes in order to provide a smooth, hard, glass-like surface. The teeth were instrumented with hand instruments simulating the clinical situation. Group 5: SRP + EDTA. Root surfaces were instrumented and a microbrush tip soaked in 24% EDTA gel (PrefGel; Biora HelpMed-Medical Supplies, São Paulo, SP, Brazil) was subsequently brushed onto the delimited areas for 2 min, the microbrush being resoaked every 30 s. Group 6: Carisolv^TM gel + SRP + EDTA: Prior to instrumentation, Carisolv^TM gel was applied to the delimited areas for 30 s. Root surfaces were instrumented with Gracey curettes as previously described. The instrumented root surfaces were conditioned with 24% EDTA gel.

The treated surfaces were rinsed in 20 mL saline and the crowns were removed at the cementoenamel junction. The teeth were then horizontally and vertically sectioned with a diamond circular saw, using the treated area as a reference. Each tooth section was rinsed in saline and placed in 2.5% glutaraldehyde in 0.1 M phosphate buffer (pH 7.4) for a minimum of 24 h.

The specimens were washed and dehydrated in a series of graded alcohol solutions (50, 70, 80, 95 and 100%) for 10 min each. After 2 additional 10-min washings in absolute alcohol, the specimens were dried overnight in a desiccator jar, mounted on SEM stubs and sputter-coated with gold. Specimens were examined using a scanning electron microscope (JSM-T330A; JEOL, Tokyo, Japan). Photographs of the central portion of each specimen were taken at X1000 magnification. SEM examination was performed by a single blinded examiner. The following parameters were evaluated: surface morphology (regular, irregular or flaky surface), presence or absence of smear layer and presence or absence of dentinal tubules.

Data were analyzed by MANOVA to determine statistically significant differences among the 6 treatment groups. Because MANOVA determined a statistically significant main effect for the treatments, Newman-Keuls test was used to determine differences between individual groups at 5% significance level.

RESULTS

The results of SEM analysis are presented in Table 1.

Group 1: The scaled, root-planed specimens exhibited more irregular surfaces than the specimens in groups 3, 5 and 6 (p<0.05). However, there were no statistically significant differences in regular surfaces (p>0.05) between group 1 and the other groups. All specimens were covered with smear layer. There were no statistically significant differences between the SRP specimens and the other groups with respect to the presence of smear layer (p>0.05) (Fig. 1).

Group 2: Specimens treated with topical application of Carisolv^TM plus SRP had more irregular surfaces compared to group 6 (p<0.05). In comparison to the other groups, there were no statistically significant differences in regular (p>0.05) or flaky surfaces (p>0.05). All specimens were covered with smear layer, but there were no statistically significant differences compared to the other treatments (p>0.05), except for group 4 (p<0.05) (Fig. 2).

Group 3: Specimens treated with active application of Carisolv^TM plus SRP had a regular surface, with no statistically significant differences compared to the other groups (p>0.05). In comparison to the SRP specimens, the active application of Carisolv^TM gel resulted in fewer irregular surfaces (p<0.05). There were no statistically significant differences between the treatments with respect to the formation of flaky surfaces (p>0.05). In addition, all specimens in this group were covered with smear layer, with no statistically significant differences compared to the other treatments (p>0.05), except for group 4 (p<0.05) (Fig. 3).

Group 4: Specimens exposed to multiple applications of Carisolv^TM interposed with SRP procedures had more regular surfaces, with no significant difference compared to the other groups (p>0.05). No significant differences were observed between the treatments with respect to flaky surfaces (p>0.05). Smear layer remnants were found in 6 specimens. There was a statistically significant reduction in the amount of smear layer when this group was compared to groups 2 and 3 (p<0.05) (Fig. 4).

Group 5: The scaled, planed and EDTA-treated specimens showed more regular surfaces with no statistically significant differences (p>0.05). Compared to the SRP group, the specimens in this group had fewer irregular surfaces and more smear layer-free surfaces (p<0.05). Smear layer remnants were observed in 6 specimens. This group differed statistically from group 3 with respect to the presence of smear layer (p<0.05) (Fig. 5).

Group 6: Specimens exposed to topical application of Carisolv^TM followed by SRP and conditioning with EDTA gel had more regular surfaces, although not statistically different from the other groups (p>0.05). There were no significant differences between this group and the others with respect to flaky surfaces (p>0.05). In comparison to groups 1 and 2, the specimens in this group had fewer irregular surfaces (p<0.05). Conditioning with EDTA gel for 2 min after chemomechanical therapy removed more smear layer from the root surfaces compared to SRP alone or topical application of the Carisolv^TM gel combined with SRP (p<0.05) (Fig. 6).

Although some specimens in groups 5 and 6 showed open dentinal tubules, no statistically significant differences (p<0.05) were observed among the proposed treatments with respect to tubule opening.

DISCUSSION

This study compared the morphological changes of periodontally compromised root surfaces submitted to either treatment with Carisolv^TM gel combined with mechanical instrumentation or scaling and root planing alone.

When Carisolv^TM gel was topically applied to root surfaces before scaling and root planing there were no significant changes in root surface morphology compared to mechanical treatment alone. Both treatments resulted in a higher frequency of rough surfaces and were equally ineffective in removing smear layer. The irregular appearance of root surfaces treated with SRP or SRP + Carisolv^TM were partially due to the presence of smear layer (Figs. 1 and 2).

Unlike passive application, active aplication (burnishing) of Carisolv^TM gel produced more extensive morphological changes than SRP alone. This mode of application resulted in fewer irregular surfaces, probably due to the mechanical abrading action of the microbrush soaked in Carisolv^TM gel, which also allowed this agent to be in closer contact with the root surface (Fig. 3). These results are in agreement with those of previous studies (17,18), which described considerable changes in surface morphology after burnishing with citric acid.

Although there was no statistically significant difference in root surface morphology after multiple applications of Carisolv^TM compared to scaling and root planing alone, it is interesting to note that some specimens exhibited a mosaic-like structure resembling that of healthy cementum (Fig. 7). This structure seemed to be masked to the surface coating that is often formed on root surface, due to the hypermineralization process resulting from periodontal disease (2,3). In view of this, it is reasonable to assume that if it is performed as usually done in clinical situations, the chemomechanical therapy would be able to remove the contaminated cementum layer and expose the healthy structure.

Regardless of the treatment, the surface appearance was extremely variable, ranging from irregular to regular, which may be explained by the variability in the anatomical structure of cementum and also by differences in mineralization of the surface coating or even by a combination of both.

Flaky surfaces were more frequently observed in chemomechanically treated specimens (Fig. 8). These morphological characteristics were similar to those observed by Bannerjee et al. (19). This could be due to the chemical effect of Carisolv^TM gel on root surface of periodontally compromised teeth. The main constituent of Carisolv^TM is sodium hypochlorite, which is mixed with three amino acids (lysine, leucine and glutamic acid). The resulting gel would be able to remove the organic components of root cementum or calculus, in the same way as it does with those of carious lesions. Additionally, this gel would be able to reduce smear layer formation because it is usually used simultaneously with mechanical instruments, thus acting as a lubricating gel.

In the present study, remnants of smear layer covering the root surface were still evident after the combination of Carisolv^TM gel and SRP procedures. This suggests that the chemomechanical treatment failed to reduce or eliminate the smear layer, especially with a single application of Carisolv^TM, independently of the mode of application. Other investigators have also found that Carisolv^TM failed to remove the smear layer from the dentin surface (15,20). This is not surprising because the use of Carisolv^TM gel was proposed as an adjunctive therapy to scaling and root planing for removal of calculus and contaminated cementum. Hence, it should be applied before root scaling and not after this procedure as advised for EDTA. This could explain the limited effect of a single application of Carisolv^TM gel on smear layer removal. Significant removal of smear layer was only achieved when root surfaces were etched with EDTA (Fig. 6), as observed in a previous study (15).

On the other hand, when multiple applications of Carisolv^TM were performed, there was a significant decrease in smear layer compared to a single application of the gel either passively or actively. These findings are consistent with those of Banerjee et al. (19) who observed lack of smear layer after multiple applications of Carisolv^TM gel for removal of carious dentin. It is important to note that several applications of Carisolv^TM gel caused a smear layer reduction that could be compared to that of EDTA gel (Table 1) and was also able to remove the decayed cementum layer, exposing a healthy cementum layer underneath. However, topical application of EDTA gel was the only treatment capable of reducing smear layer compared to SRP procedures. The effectiveness of EDTA gel in removing smear layer and exposing dentin or cementum collagen matrix has been previously reported (11). It may be assumed that not only active but also multiple applications of Carisolv^TM gel would be required to alter root surface morphology and enhance the smear layer removal effect of Carisolv^TM for treatment of periodontally compromised teeth.

Further studies are needed to investigate whether Carisolv^TM could improve the removal of calculus and also establish whether the morphological alterations of root surfaces produced by chemomechanical therapy might provide a biologically acceptable environment for periodontal healing.

In conclusion, the chemomechanical therapy caused significant changes in root surface morphology of periodontally compromised teeth only when Carisolv^TM was actively applied (burnishing technique). Carisolv^TM failed to remove the smear layer completely, especially with a single application, independently of the method of application. Multiple applications of Carisolv^TM were necessary to achieve a smear layer reduction comparable to that obtained with 24% EDTA conditioning.

ACKNOWLEDGEMENTS

We would like to thank Dr. Mario Taba Jr. from the Department of Buccomaxillofacial Surgery and Traumatology and Periodontology of the Faculty of Dentistry of Ribeirão Preto, University of São Paulo (Brazil) for the statistical analysis of this study.

Accepted April 5, 2006

Publication Dates