Abstract

Microalloyed steels have a maximum of 2% in alloying elements and are used in the automotive and petrochemical industries. The microstructure and mechanical properties of these steels depend on chemical composition, processing and addition of molybdenum, niobium, titanium and vanadium. To evaluate the molybdenum effect in microstructure and mechanical properties, two microalloyed steels, with similar levels of niobium, titanium and vanadium, were prepared and forged. The steels have 0.056 and 0.160 percent by weight of molybdenum. The bars were homogenized, quenched and tempered. The specimens were machined for tensile and impact tests, hardness and microstructural analyzes by confocal and scanning electron microscopy. The ThermoCalc software was used to evaluate the carbides characteristics. The results show that steel with 0.160% Mo presents greater amount of bainite and austenite retained. It’s possible that formation of carbides by the secondary hardening mechanism increase in mechanical strength and a reduction in toughness.

Keywords:
Microalloyed steel; molybdenum; API steel; ThermoCalc

1. Introduction

The oil and gas industry requires the development of steels that meet API 5L (American Petroleum Institute) requirements. These steels must have an excellent combination of properties, such as high mechanical strength to withstand pressure in deep water, corrosion resistance in a marine environment, toughness and adequate weldability¹1 Gray JM, Siciliano F. High strength microalloyed linepipe: half a century of evolution. Houston: Microalloyed Steel Institute; 2009.,²2 Kumar BVR. A review on importance of microalloying in steel. Int J Mech Eng. 2014;5(2):187-93..

The conventional thermomechanical process for these steels is the controlled rolling. However, forging is used in the manufacture of parts with complex geometry, such as valves for pipelines and connections for transporting gas and oil. This process allows the manufacture of parts with a wide range of dimensions and shapes, microstructure control and an excellent combination of mechanical properties, after quenching and tempering treatments³3 Forged Components [internet]. Forging types API wellhead component manufacturing. Navasota: Forged Componentes; 2021 [cited 2021 Feb 28]. Avaiable from: https://forgedcomponents.com/forging-types-api-wellhead-component-manufacturing_2017-10/.
https://forgedcomponents.com/forging-typ... . Nowadays, several industries produce connections and accessories for use in pipelines. The forging process is also widely used in the automotive industry, as the technique produces components with adequate manufacturing cost. There is a little loss of material, as the forged product has dimensions close to the final. product⁴4 Speer JG, Matlock DK. Some recent developments in microalloyed bar and forging steels. new developments in long and forged products proceedings. Warrendale: AIST; 2006.,⁵5 Speer JG, Whitley B, Kaster S, Findley K, Matlock D, Moor E. Selected developments in Nb-microalloyed forgings for induction hardening, and pearlitic wire rod. Tecnol Metal Mater Min. 2020;17(2):164-9..

Associated with the forging process, the addition of niobium, titanium and vanadium at levels of up to 0.15% by weight promotes solid solution hardening and grain refinement. These elements favor the formation of finely dispersed carbonitrides in the matrix during the austenite-ferrite transformation and are effective in increasing mechanical strength and tenacity⁶6 Fatehi A, Calvo J, Elwazri AM, Yue S. Strengthening of HSLA steels by cool deformation. Mater Sci Eng A. 2010;527:4233-40.,⁷7 Mousavi ASH, Yue S. The effect of cooling rate, and cool deformation through strain-induced transformation, on microstructural evolution and mechanical properties of microalloyed steels. Metall Mater Trans, A Phys Metall Mater Sci. 2012;43:1140-62..

In this case, quenching and tempering heat treatments are used to control the microstructures and optimize the mechanical properties of microalloyed steels. Previous studies show that a microstructure composed of bainite, ferrite and retained austenite (M/A) is common in microalloyed steels⁸8 Mousavi ASH, Sabzi M. The Evolution of Microstructure of an High Ni HSLA X100 Forged Steel Slab by Thermomechanical Controlled Processing. In: 147th Annual Meeting & Exhibition Supplemental Proceedings; 2018 Feb 4. Cham: Springer; 2018. p. 145-56..

Regarding the molybdenum and niobium, another important effect is the reduction of the austenite-ferrite transformation temperature, which favors the formation of displactive structures, such as acicular ferrite and bainite⁸8 Mousavi ASH, Sabzi M. The Evolution of Microstructure of an High Ni HSLA X100 Forged Steel Slab by Thermomechanical Controlled Processing. In: 147th Annual Meeting & Exhibition Supplemental Proceedings; 2018 Feb 4. Cham: Springer; 2018. p. 145-56.,⁹9 Okaguchi S, Hashimoto T, Ohtani H. Effect of niobium, vanadium and titanium on transformation behavior of hsla steel in accelerated cooling. In: International Conference on Physical Metallurgy of Thermomechanical Processing of Steels and Other Metals; 1988 June 6-10; Tokyo: THERMEC; 1988. p. 330-6.. In these steels, the microstructures generally consist of a matrix with polygonal (equiaxial) ferrite grains with second phase islands that can be degenerate pearlite, bainite, martensite/retained austenite (M/A) or acicular ferrite (AF)⁶6 Fatehi A, Calvo J, Elwazri AM, Yue S. Strengthening of HSLA steels by cool deformation. Mater Sci Eng A. 2010;527:4233-40.. It is possible that molybdenum has a greater effect on the finer microstructures, while niobium on the grain refining⁷7 Mousavi ASH, Yue S. The effect of cooling rate, and cool deformation through strain-induced transformation, on microstructural evolution and mechanical properties of microalloyed steels. Metall Mater Trans, A Phys Metall Mater Sci. 2012;43:1140-62.,¹⁰10 Shang CJ, Miao CL, Subramanian SV. Austenite processing and phase transformation of niobium and molybdenum alloyed high performance structural steel. In: Fundamentals and Applications of Mo and Nb Alloying in High Performance Steels; 2014 April 24-26; Pittsburgh. Pittsburgh: CBMM, IMOA, TMS; 2014. v. 1, p. 37-61..

According to the literature, the microstructure with these constituents is interesting to meet API 5L standards⁶6 Fatehi A, Calvo J, Elwazri AM, Yue S. Strengthening of HSLA steels by cool deformation. Mater Sci Eng A. 2010;527:4233-40.,¹¹11 Huang BM, Yang JR, Huang CY. The synergistic effect of niobium-molybdenum additions on the microstructure of low- carbon bainitic steel. In: Fundamentals and Applications of Mo and Nb Alloying in High Performance Steels; 2013 April 24-26; Pittsburgh. Pittsburgh: CBMM, IMOA, TMS; 2013. v. 2, p. 29-50.

12 Li L, Xu L. Designing with High-Strength Low-Alloy Steels. In: Totten GE, Xie L, Funatani K, editors. Handbook of Mechanical Alloy Design. New York: Marcel Dekker; 2004. p. 249-320.-¹³13 API: American Petroleum Institute. Specification 5L for line pipe. 45st ed. Washington DC: API; 2013.. Previous studies showed that a steel containing 0,3 wt.% Mo produced a high volume fraction of granular bainite, with significant benefits to increase elongation after the tempering treatment¹¹11 Huang BM, Yang JR, Huang CY. The synergistic effect of niobium-molybdenum additions on the microstructure of low- carbon bainitic steel. In: Fundamentals and Applications of Mo and Nb Alloying in High Performance Steels; 2013 April 24-26; Pittsburgh. Pittsburgh: CBMM, IMOA, TMS; 2013. v. 2, p. 29-50.,¹²12 Li L, Xu L. Designing with High-Strength Low-Alloy Steels. In: Totten GE, Xie L, Funatani K, editors. Handbook of Mechanical Alloy Design. New York: Marcel Dekker; 2004. p. 249-320.. Regarding the carbides formed in the austenite-ferrite transformation and secondary hardening, they are difficult to be observed even in scanning electron microscopes¹⁴14 Isasti N, Jorge-Badiola D, Taheri ML, Uranga P. Phase transformation study in Nb-Mo microalloyed steels using dilatometry and EBSD quantification. Metall Mater Trans, A Phys Metall Mater Sci. 2013;44(8):3552-63.. In this case, computational thermodynamic simulation is an efficient tool to predict the quantity and temperature of solubilization of carbides, oxides, sulfides and nitrides¹⁵15 Han Q, Kang Y, Zhao X, Gao L, Qiu X. High-temperature properties and microstructure of Mo microalloyed ultra-high-strength steel. Int J Miner Metall Mater. 2011;18(4):407-13.,¹⁶16 Xu K, Thomas BG, O’Malley R. Equilibrium model of precipitation in microalloyed steels. Metall Mater Trans, A Phys Metall Mater Sci. 2010;42(2):524-39..

In this context, this present research aims to evaluate molybdenum effect on the microstructure, hardness, mechanical strength and Charpy impact tests of two microalloyed steels, with characteristics of the API 5L standard and similar levels of niobium, titanium and vanadium, after quenching and tempering at different temperatures. A qualitative analysis and the carbide stoichiometry were determined through thermodynamic simulations with the ThermoCalc software.

2. Experimental Procedures

Two microalloyed steels were manufactured in an induction furnace with a capacity of 300 kg at Fundição Grupo Metal, SP-Brazil. The liquid metal was poured into a cast iron ingot mold and the chemical compositions were determined by optical emission spectrometry.

Ingots were cut into three pieces with similar weights. These parts were heat treated to 1050 °C and forged with a square section of approximately 40 mm on the side and a length of 1500 mm. The last passes were made at a temperature of 850 °C to refine the grain. Afterwards, the bars were annealed at 930 °C for two hours to homogenize the microstructure. Figure 1 illustrates thermomechanical processing.

After cooling, samples cut in longitudinal orientation of 32x32x120 mm were prepared and austenitized at 900 °C in a muffle furnace for 120 minutes and cooled in water. This temperature corresponds to a fully austenitic region, above A_c3, considering the temperatures A_c1 and A_c3, calculated by Kasatkin¹⁷17 Kasatkin OG, Vinokur BB, Pilyushenko VL. Calculation models for determining the critical points of steel. Metal Sci Heat Treat. 1984;26(1):27-31..

Subsequently tempering was carried out at 150, 250, 350, 450, 550 and 600 ºC for one hour with cooling in water. On these samples, hardness measurements were obtained, according to ASTM E18, in a Rockwell B durometer, with a load of 100 kgf, to determine the tempering curves.

Specimens under tempering conditions at 450 and 600 ºC were machined for mechanical tests and microstructural analyses. These temperatures were selected according to the highest and lowest hardness values observed in the tempering curve.

After preparation by conventional metallography, the microstructures were revealed with the reagents Nital 2% (nitric acid 2% in ethyl alcohol) and Lepera (4% picric acid in ethanol and sodium metabisulfite 1% in distilled water) for 30 seconds. Microstructural analyzes were performed using confocal optical microscopy (MOC) and scanning electron microscopy (SEM) with an energy dispersive spectroscopy (EDS) system. Grain sizes were measured according to ASTM E112 standard.

Tensile tests were carried according to ASTM E8, in a universal machine with a 50 mm strain gauge, 25 mm measurable strain and 1 mm/min speed. The absorbed energy at impact was determined according to ASTM E23-16a standard using three specimens submitted to Charpy test at temperature of minus 20°C. The absorbed energy at impact was determined in accordance with ASTM E23-16a with Charpy tests at a temperature minus 20 °C. The results of the traction and impact tests correspond to the averages of three specimens for each condition.

A qualitative analysis and the carbide stoichiometry were determined through thermodynamic simulations with the ThermoCalc software, considering the percentages of chemical elements, FCC basis for an matrix and temperature in the range of 200 to 1500 °C.

3. Results and Discussion

The chemical compositions of microalloyed steels are shown in Table 1. The sum of the niobium, titanium and vanadium contents are similar and meet the API 5L standard. To facilitate presentation, steels with 0.160% Mo and 0.056% Mo are called 160-Mo and 056-Mo, respectively.

Regarding microstructures, the grain sizes were 8 ± 1 and 9 ± 1 ASTM for 160-Mo and 056-Mo steels, respectively, in the annealed condition. The smaller grain in 056-Mo steel is possibly related to the higher niobium content. Javaheriobserved the influence of niobium in the refinement of grains of two steels, even for a small difference in the element content, around 0.01%¹⁸18 Javaheri V, Khodaie N, Kaijalainen A, Porter D. Effect of niobium and phase transformation temperature on the microstructure and texture of a novel 0.40% C thermomechanically processed steel. Mater Charact. 2018;142:295-308.. Niobium forms carbides that anchor grain boundaries during austenitization and inhibit the grain growth¹⁹19 Coladas J, Masounave J, Bailon JP. The influence of niobium on the austenite processing of medium and high carbon steels. In: Balance JB, editors. The hot deformation of austenite. New York: AIME; 1977. p. 341-88.,²⁰20 Mori FY, Barbosa CA, Souze MHC, Falleiros IGS. Controle do tamanho de grão austenítico de um aço para trabalho a quente através de adição de Nb. Metalurgia ABM. 1977;33(241):743-8.. The microstructures of the steels, after quenching at 900 ºC with water cooling, are shown in Figures 2(a) and 2(b).

The bainite bundles observed in 160-Mo steel, in Figure 2(a), are elongated and may be responsible for the increase in hardness and mechanical strength⁸8 Mousavi ASH, Sabzi M. The Evolution of Microstructure of an High Ni HSLA X100 Forged Steel Slab by Thermomechanical Controlled Processing. In: 147th Annual Meeting & Exhibition Supplemental Proceedings; 2018 Feb 4. Cham: Springer; 2018. p. 145-56.. It is likely that the higher molybdenum content is responsible for the reduction in the transformation temperature and favors a greater amount of elongated bainite plates²¹21 Haijiang H, Guang X, Li W, Zhengliang X, Yulong Z, Guanghui L. The effects of Nb and Mo addition on transformation and properties in low carbono bainitic steels. Mater Des. 2015;84:95-9.. Previous studies indicate that grain size can influence bainite growth with the presence of retained austenite (M/A)²²22 Feng H, Kaiming W, Ting-Ping H, Peter H, Rodionova I, Fu-Cheng Z. The effect of microphases on elongation of nanostructured bainitic steels. Metallurgist. 2017;60(11-12):1295-300.. With the increase in grain size, there is a reduction in the boundary surface energy and greater difficulty in diffusive transformations. This favors adiffusional transformations such as bainite²³23 Bhadeshia HKDH, Edmonds DV. The bainite transformation in a silicon steel. Metall Trans, A, Phys Metall Mater Sci. 1979;10(7):895-907.. Regarding the presence of M/A, this phase acts as a microcrack initiator and can reduce the toughness of the material²⁴24 Isasti N, Jorge-Badiola D, Taheri ML, Uranga P. Microstructural features controlling mechanical properties in nb-mo microalloyed steels. Part II: impact toughness. Metall Mater Trans, A Phys Metall Mater Sci. 2014;45A:4972-82.. In Figure 2(b), the microstructure is composed of polygonal ferrite (FP) with less acicular ferrite (FAc) and bainite (B). In this case, the higher surface energy of the grain boundaries favors the formation of polygonal ferrite and limits the growth of bainite plates²¹21 Haijiang H, Guang X, Li W, Zhengliang X, Yulong Z, Guanghui L. The effects of Nb and Mo addition on transformation and properties in low carbono bainitic steels. Mater Des. 2015;84:95-9.,²³23 Bhadeshia HKDH, Edmonds DV. The bainite transformation in a silicon steel. Metall Trans, A, Phys Metall Mater Sci. 1979;10(7):895-907.,²⁵25 Bhadeshia HKDH. Bainite in steels. 2nd ed. London: Institute of Materials; 2001.,²⁶26 Shin SY, Hwang B, Lee S, Kim NJ, Ahn SS. Correlation of microstructure and charpy impact properties in API X70 and X80 line-pipe steels. Mater Sci Eng A. 2007;458:281-9..

Figure 3 shows the microstructural characteristics after quenching and tempering at 450 and 600 ºC, where FP, B and FAc represent polygonal ferrite, bainite and acicular ferrite, respectively.

In Figure 3(a), elongated bainite slabs (B) predominate in 160-Mo steel. In 056-Mo steel, Figure 3(b) shows acicular ferrite (FAc) and bainite in a polygonal ferrite (FP) matrix after tempering at 450 °C. Figures 3(c) and 3(d) show that, after tempering at 600 ºC, both steels remain with ferritic-bainitic microstructures, but with an increase in the amount of polygonal ferrite. According to literature, niobium and molybdenum favor this microstructure after tempering¹⁰10 Shang CJ, Miao CL, Subramanian SV. Austenite processing and phase transformation of niobium and molybdenum alloyed high performance structural steel. In: Fundamentals and Applications of Mo and Nb Alloying in High Performance Steels; 2014 April 24-26; Pittsburgh. Pittsburgh: CBMM, IMOA, TMS; 2014. v. 1, p. 37-61.,²⁵25 Bhadeshia HKDH. Bainite in steels. 2nd ed. London: Institute of Materials; 2001..

On the tempering curves in Figure 4, initially there is a relief of the stresses generated in the quenching. The greater hardness of 160-Mo steel is related to the higher molybdenum content and the presence of displacive constituents and elongated bainite bundles⁸8 Mousavi ASH, Sabzi M. The Evolution of Microstructure of an High Ni HSLA X100 Forged Steel Slab by Thermomechanical Controlled Processing. In: 147th Annual Meeting & Exhibition Supplemental Proceedings; 2018 Feb 4. Cham: Springer; 2018. p. 145-56.. Previous studies with Nb-Mo containing HSLA steels indicate, that the addition of Mo promotes the formation of bainite with excellent mechanical properties ⁸8 Mousavi ASH, Sabzi M. The Evolution of Microstructure of an High Ni HSLA X100 Forged Steel Slab by Thermomechanical Controlled Processing. In: 147th Annual Meeting & Exhibition Supplemental Proceedings; 2018 Feb 4. Cham: Springer; 2018. p. 145-56.,¹¹11 Huang BM, Yang JR, Huang CY. The synergistic effect of niobium-molybdenum additions on the microstructure of low- carbon bainitic steel. In: Fundamentals and Applications of Mo and Nb Alloying in High Performance Steels; 2013 April 24-26; Pittsburgh. Pittsburgh: CBMM, IMOA, TMS; 2013. v. 2, p. 29-50.. Probably the effect of secondary hardening is responsible for the increase in hardness in the range from 400 to 500 ºC²⁷27 Ma YQ, Gao HT, Liang YF, Zhang XJ. Secondary hardening during tempering of Cr-W-Mo-V high alloy medium-upper carbon steel and its hardness forecast. Adv Mat Res. 2011;415-417:813-8.. In this case, molybdenum should contribute to the precipitation mechanism of finely distributed carbides in the matrix¹⁴14 Isasti N, Jorge-Badiola D, Taheri ML, Uranga P. Phase transformation study in Nb-Mo microalloyed steels using dilatometry and EBSD quantification. Metall Mater Trans, A Phys Metall Mater Sci. 2013;44(8):3552-63.,²⁸28 Porter DA, Easterling KE, Sherif M. Phase transformations in metals and alloys. 3 ed. Londres: CRC Press; 2009.. According to Isasti, these carbides in the order of 15 nm increase the hardness and yield strength in microalloyed steels¹⁴14 Isasti N, Jorge-Badiola D, Taheri ML, Uranga P. Phase transformation study in Nb-Mo microalloyed steels using dilatometry and EBSD quantification. Metall Mater Trans, A Phys Metall Mater Sci. 2013;44(8):3552-63.. Wang et al. observed a hardening of the ferritic phase in a steel microalloyed with titanium and molybdenum and attributed the reinforcement to the nanometric precipitation of carbides. After tempering at temperatures above 500 °C the hardness gradually decreases²⁹29 Wang J, Beladi H, Pan L, Fang F, Hu J, Kong L, et al. Interphase precipitation hardening of a Ti-Mo microalloyed dual-phase steel produced by continuous cooling. Mater Sci Eng A. 2021;804:140518..

This is due to the coalescence of carbides shown in Figure 5(a) in 160-Mo steel after quenching at 900 °C and tempering at 600 °C. The EDS spectrum in Figure 5(b) indicates the particles of molybdenum carbides.

Fine particles from secondary precipitation are difficult to see by scanning electron microscopy. However, the results shown in Figure 5(a) and Table 2 indicate secondary hardening and coalescence of carbides in this temperature range. Regarding the mechanical properties of 160-Mo steel, it is possible that the effect of molybdenum is greater on the microstructure, as shown in Figure 2(a), than on secondary hardening.

According to values of mechanical properties, in Table 2, the presence of bainite plates is more important in 160-Mo steel and favors higher values of yield strength and ultimate tensile strength, and secondary hardening is negligible. However, in 056-Mo steel, there is a greater influence of the secondary hardening mechanism³⁰30 Davis JR. Alloying: understanding the basics In: Davis JR, editor. Materials park. Ohio: ASM International; 2001.,³¹31 Altuna MA, Iza-Mendia A, Gutiérrez I. Precipitation of Nb in ferrite after austenite conditioning. Part II: strengthening contribution in High-Strength Low-Alloy (HSLA) steels. Metall Mater Trans, A Phys Metall Mater Sci. 2012;43:4571-86.. In this case, molybdenum reduces the interfacial energy of the precipitates and decreases the coalescence rate of niobium carbides³²32 Abbasi E, Rainforth WM. Effect of Nb-Mo additions on precipitation behaviour in V microalloyed TRIP-assisted steels. Mater Sci Technol. 2016;32(16):1721-9..

After tempering at 600 ºC of 160-Mo steel, the lowest yield strength and the highest elongation values indicate a possible decomposition of M/A, the thickening of bainite plates and carbides coalescence. Talebi observed the beginning M/A decomposition in tempering at 350 ºC and complete decomposition at 600 ºC in bainitic steels³³33 Talebi S, Jahazi M, Melkonyan H. Retained austenite decomposition and carbide precipitation during isothermal tempering of a medium-carbon low-alloy bainitic Steel. Materials. 2018;11(8):1441..

Regarding impact resistance, the elongated bainite plates and the presence of the embrittlement microconstituent M/A, shown in Figure 2(a), justify the reduction in absorbed energy in the 160-Mo steel³⁴34 Junhua K, Lin Z, Bin G, Pinghe L, Aihua W, Chandsheng X. Influence of Mo content on microstructure and mechanical properties of high strength pipeline steel. Mater Des. 2004;25:723-8.,³⁵35 Shen YF, Qiu LN, Sun X, Zuo L, Liaw PK, Raabe D. Effects of retained austenite volume fraction, morphology, and carbon content on strength and ductility of nanostructured TRIP-assisted steels. Mater Sci Eng A. 2015;636:551-64.. However, in 056-Mo steel, the behavior is different, as, according to Figure 2(b). In this case, the amount of bainite and M/A is not significant compared to 160-Mo steel and the values of yield strength and ultimate tensile strength are lower. Thus, an increase in ductility and impact energy is possible. Another important factor, observed in the same figure, is the presence of polygonal ferrite associated with acicular ferrite and granular bainite, which contribute to toughness increasing. Experimental results show that this microstructure improves yield strength and toughness of ferrite-base steels³⁶36 Kim YM, Kim SK, Lim YJ, Kim NJ. Effect of microstructure on the yield ratio and low temperature toughness of linepipe steels. ISIJ Int. 2002;42(12):1571-7..

In 056-Mo steel, although it is not possible to confirm, the increase in yield strength and ultimate tensile strength may be related to the secondary hardening mechanism that can occur in the range of 450 to 600 °C, as seen in Figure 4.

From this perspective, the thermodynamic simulations with the ThermoCalc software in Figures 6 and 7 corroborate the results, because indicate a larger amount of complex carbides in the steels, in the range of 400 to 600 ºC. Literature shows that M₇C₃ and M₂₃C₆ carbides are mainly chromium and molybdenum. These carbides, with complex stoichiometry, form a coarse dispersion¹⁵15 Han Q, Kang Y, Zhao X, Gao L, Qiu X. High-temperature properties and microstructure of Mo microalloyed ultra-high-strength steel. Int J Miner Metall Mater. 2011;18(4):407-13.,³⁷37 Maalekian M. The effects of alloying elements on steels (I) [thesis]. Graz: Technische Universität Graz; 2007.. Dong et al. also observed different precipitates during tempering: M₃C₂ between 200 and 400 ºC, M₂C and M₂₃C₆ at 500 ºC in ultra-high strength steels³⁸38 Dong J, Zhou X, Liu Y, Li C, Liu C, Guo Q. Carbide precipitation in Nb-V-Ti microalloyed ultra-high strength steel during tempering. Mater Sci Eng A. 2017;683:215-26.. Thus, the greater amount of precipitates of M₂₃C₆ in the range of 400 to 600 ºC may indicate an increase in mechanical strength and a reduction in absorbed energy on impact in 160-Mo steel.

Finally, the API 5L standard specifications can validate the results of mechanical properties. Regarding the chemical composition and mechanical properties, according to quenching at 900 °C and tempering at 600 °C for the two steels, and using Equation 1 to calculate the elongation, the 056-Mo steel fits at PSL 2 level, while 160-Mo steel at PSL 1 level¹³13 API: American Petroleum Institute. Specification 5L for line pipe. 45st ed. Washington DC: API; 2013..

According to yield strength (σ_e) and the ultimate tensile strength (σ_t) in Table 2, the 056-Mo steel can be considered as API X65 grade, while 160-Mo steel as X70. With relation the absorbed energy, it is observed that the 056-Mo steel meets the standard value and the fracture is fully ductile. However, 160-Mo steel does not have the minimum value of 27 Joules and has a high percentage of brittle fracture.

4. Conclusions

The results show that:

• Molybdenum favors the formation of elongated plates of bainite, which increases mechanical strength and reduces toughness;

• The smallest grain size and the largest amount of polygonal ferrite increase the absorbed energy in the 056-Mo steel;

• Simulations with ThermoCalc software indicate a higher precipitation of carbides in 160-Mo steel and corroborate the results of mechanical properties;

• Qualitative analyzes of chemical composition by EDS, associated with the tempering curves, indicate the presence of the secondary hardening mechanism and carbides coalescence;

• According to API 5L standard, 056-Mo steel is similar to PSL 2, X65 grade, while 160-Mo is similar to PSL 1, X70 grade. However, the absorbed energy in the impact test for the second do not meet the minimum value required by the standard.

5. Acknowledgments

The authors thank Grupo Metal for the samples, CAPES for master’s scholarship from student Jaqueline, CBMM for niobium, LCE/UFSCar for the analysis, FAPES for the financial support, IFES by the use of equipments and MSc. Joelma Krugel for thermodynamic simulations.

6. References