Abstract
Mechanism for the hardening of two-phase Ni3Al-Ni3V intermetallic alloy to which 2 at.% Ta was added in different substitution manners for Ni, Al and V was presented, based on the microstructural observation, alloying behavior and lattice properties of the additive in the constituent phases. The hardening behavior was explained in terms of solid solution hardening in which the mixture rule in the volume fraction of the two constituent phases and the atomic size misfit evaluated from the changes of the lattice parameters were incorporated. Consequently, the hardening for the alloys in which the additives were substituted for Ni and V was attributed to solid solution hardening. On the other hand, the hardening for the alloy in which the additive was substituted for Al was attributed to the hardening due to microstructural refining in addition to the solid solution hardening.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
S. Kobayashi, K. Sato, E. Hayashi, T. Osaka, T.J. Konno, Y. Kaneno and T. Takasugi, Intermetallics 23, 68 (2012).
S. Semboshi, H. Tsuda, Y. Kanano, A. Iwase and T. Takasugi, Intermetallics 59, 1 (2015).
Y. Nunomura, Y. Kaneno, H. Tsuda and T. Takasugi, Acta Mater. 54, 851 (2006).
S. Shibuya, Y. Kaneno, M. Yoshida and T. Takasugi, Acta Mater. 54, 861 (2006).
S. Shibuya, Y. Kaneno, H. Tsuda and T. Takasugi, Intermetallics 15, 338 (2007).
T. Moronaga, Y. Kaneno, S. Semboshi and T. Takasugi, Phil. Mag. 95, 3859 (2015).
T. Takeshita, Y. Murata, N. Miura, Y. Kondo, Y. Tsukada and T. Koyama, J. Japan Inst. Met. Mater. 79, 203 (2015).
W.C. Johnson and J.K. Lee, Metall. Trans. A 10, 1141 (1979).
T. Miyazaki, H. Imamura, H. Mori and T. Kozakai, J. Mater. Sci. 16, 1197 (1981).
A. Kelly and R.B. Nicholson, Prog. Mater. Sci. 10, 151 (1963).
M. Doi, T. Miyazaki and T. Wakatsuki, Mater. Sci. Eng. 67, 247 (1984).
L.A. Gypen and A. Deruyttere, J. Mater. Sci. 12, 1028 (1977).
R.W. Guard and J.H. Westbrook, Trans. Met. Soc. AIME 215, 807 (1959).
R.D. Rawlings and A.E. Staton-Bevan, J. Mate. Sci. 10, 505 (1975).
Y. Mishima, S. Ochiai, N. Hamao, M. Yodogawa and T. Suzuki, Trans JIM 27, 648 (1986).
T. Moronaga, Y. Kaneno, H. Tsuda and T. Takasugi, Mater. Sci. Forum 706–709, 1077–1082 (2012).
K. Hagihara, M. Mori, T. Kishimoto and Y. Umakoshi, Mater. Sci. Forum 638–642, 1318–1323 (2010).
H. Yasuda, T. Takasugi and M. Koiwa, Acta Metall. Mater. 40, 381 (1992).
Y. Zhao, L. Qi, Y. Jin, K. Wang, J. Tian and P. Han, J. Alloys Compounds 647, 1104 (2015).
F.R.N. Nabarro, Phil. Mag. 35, 613 (1977).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ioroi, K., Kaneno, Y. & Takasugi, T. Effect of Ta addition on microstructure and mechanical properties of dual two-phase Ni3Al-Ni3V intermetallic alloy. MRS Advances 4, 1509–1514 (2019). https://doi.org/10.1557/adv.2019.140
Published:
Issue Date:
DOI: https://doi.org/10.1557/adv.2019.140